Structural and electrical properties of crystalline (1−x)Ta2O5−xTiO2 thin films fabricated by metalorganic decomposition

Polycrystalline (1−x)Ta₂O₅−xTiO₂ thin films were formed on Si by metalorganic decomposition (MOD) and annealed at various temperatures. As-deposited films were in the amorphous state and were completely transformed to crystalline after annealing above 600 °C. During crystallization, a thin interfacial SiO₂ layer was formed at the (1−x)Ta₂O₅−xTiO₂/Si interface. Thin films with 0.92Ta₂O₅–0.08TiO₂ composition exhibited superior insulating properties. The measured dielectric constant and dissipation factor at 1 MHz were 9 and 0.015, respectively, for films annealed at 900 °C. The interface trap density was 2.5×10¹¹ cm⁻² eV⁻¹, and flatband voltage was −0.38 V. A charge storage density of 22.8 fC/μm² was obtained at an applied electric field of 3 MV/cm. The leakage current density was lower than 4×10⁻⁹ A/cm² up to an applied electric field of 6 MV/cm.     

Side‐chain crystallization behavior of graft copolymers consisting of an amorphous main chain and crystalline side chains. II. Poly(n‐hexyl methacrylate)‐graft‐poly(ethylene glycol)

The phase behavior and crystallization of graft copolymers consisting of poly(n‐hexyl methacrylate) (PHMA) as an amorphous main chain and poly(ethylene glycol) (PEG) as crystallizable side chains (HMAx with 15 ≤ x ≤ 73, where x represents the weight percentage of PEG) were investigated. Small‐angle X‐ray scattering profiles measured above the melting temperature of PEG suggested that a microdomain structure with segregated PHMA and PEG domains was formed in HMA40 and HMA46. This phase behavior was qualitatively described by a calculated phase diagram based on the mean‐field theory. Because of the segregation of PEG into microdomains, the crystallization temperature of the PEG side chains in HMAx was higher than that in poly(methyl acrylate)‐graft‐poly(ethylene glycol) having a similar value of x, which was considered to be in a disordered state above the melting temperature. In HMAx with x ≤ 40, PEG crystallization was strongly restricted, probably because the PEG microdomains were isolated in the PHMA matrix. As a result, the growth of PEG spherulite was not observed because the PEG crystallization occurred after vitrification of the PHMA segregated domains. © 2006 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 45: 129–137, 2007     

Intrinsic field theory of chemical reactions

An intrinsic principle of least action is presented for the intrinsic dynamism of chemical reactions. Then, as the stationary trajectory, a meta-IRC (intrinsic reaction coordinate) draws a geodesic curve in a rigged Riemannian space. This establishes a geodesic law for the intrinsic dynamism. Moreover, a diagrammatic perturbation theory is formulated for the intrinsic dynamism, and a dynamical interaction between a chemically reacting system and a background system is investigated. Then, the structural stability of the system is discussed using a new concept of the dynamical potential field. An example is given in order to elucidate the present theory.Dedicated to Prof. Hermann Hartmann on the occasion of his 65th birthday.     

Thermolysis of reactive oligo(p-phenylene sulfide) containing disulfide bond

Oligo(phenylene sulfide) (OPS) containing one disulfide bond at the end of the chain, which was obtained by the oxidative polymerization of diphenyl disulfide, had a relatively low Td_10%(temperature for 10% weight loss) of 412 °C because of degradation of the disulfide bond. But this thermal cleavage of the disulfide bond promoted the curing reaction through thiophenoxy radical formation. OPS was allowed to react with diiodobenzene at 220 °C. The thermal stability of OPS was improved through the consumption of the disulfide bond and the coupling of the chain.     

The chemical synthesis of a cyclic oligosaccharide derivative with branching

A cyclic oligosaccharide derivative was synthesized by cationic ring-opening polymerization of an anhydrodisaccharide derivative under high vacuum in dichloromethane with 20 mol% of PF₅ as initiator. Analysis of the spectral results showed that the oligomer chain is composed of only 3 glucose units connected by -1,6 linkages with a glucopyranosyl branching unit at C-4 of each sugar residue in the main chain.     

Intramolecular photoreactions of 6-(ω-alkenyl)-4-methoxy-2-pyrones

6-(ω-Alkenyl)-2-pyrones 3a-c and 8a, b were prepared and the photochemical reactions were investigated. Photosensitized reactions of 3b, c gave intramolecular [2+2]-cycloadducts 11b, c as tricyclic lactones, site-and regio-specifically. They are not frontier-orbital-controlled adducts. On the other hand, 3a, 8a, b afforded cyclobutenecarboxylic acids, 10a, 14a, b , respectively. The end-ester group at the side-chain is thought not to be effective for the intramolecular phptoaddition.