Generation of highly stable amidate anion in anionic polymerization of 3‐(triethylsilyl)propyl isocyanate

To study living anionic polymerization, 3‐(triethylsilyl)propyl isocyanate (TEtSPI) monomer was synthesized by hydrosilylation of allylamine with triethylsilane and treatment of the resulting amine with triphosgene. The polymerization of TEtSPI was performed with sodium naphthalenide (Na‐Naph) as an initiator and in the absence and presence of sodium tetraphenylborate (NaBPh₄) as an additive in tetrahydrofuran (THF) at ?78 and at ?98 °C. A highly stabilized amidate anion for living polymerization of isocyanates was generated for the first time with the combined effect of the bulky substituent and the shielding action of the additive NaBPh₄, extending the living character at least up to 120 min at ?98 °C. Even the anion could exist at ?78 °C for 10 min. A block copolymer, poly(n‐hexyl isocyanate)‐b‐poly[(3‐triethylsilyl)propyl isocyanate]‐b‐poly(n‐hexyl isocyanate), was synthesized with quantitative yields and controlled molecular weights via living anionic polymerization in THF at ?78 °C for TEtSPI and ?98 °C for n‐hexyl isocyanate, respectively, with Na‐Naph with three times of NaBPh₄ as a common ion salt. © 2004 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 42: 933–940, 2004     

Preparation and characterization of acrylic‐based black particles of poly(methyl methacrylate‐co‐ethylene glycol dimethacrylate) by dispersion polymerization for electrophoretic displays

Ultrafine black particles, ranging in diameter from 1 to 3 μm, were prepared by dispersion polymerization in a methanol/water mixture with vinyl monomers, nonpolymerizable Sudan black B dyes, and fluorescein isothiocyanate labeled charge control additives. Both the ratio of the methanol to the water dispersion medium and the polymeric stabilizer concentration had significant effects on the particle size. The important role of the stabilizer concentration lay in the particle formation step, during which it determined the particle stability and final particle size. These could affect the extent of the aggregation of nuclei by changing the adsorption rate of the stabilizer and the viscosity of the dispersion medium, resulting in smaller particles. The fluorescent‐labeled charge control additives strongly affected the electrophoretic mobility. A small concentration of fluorescent‐labeled charge control additives increased the electrophoretic mobility. However, a further addition reduced the electrophoretic mobility of the polymer particles. The concentration dependence of the fluorescent‐labeled charge control additives on the deposition behavior in the polymer particles was successfully imaged and thereafter quantified by image analysis. © 2004 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 42: 5608–5616, 2004     

Synthesis and characterization of new segmented polyurethanes with side‐chain,liquid‐crystalline chain extenders

Liquid‐crystalline, segmented polyurethanes with methoxy–biphenyl mesogens pendant on the chain extender were synthesized by the conventional prepolymer technique and esterification reaction. Two, side‐chain, liquid‐crystalline (SCLC) polyurethanes with mesogens having spacers of six and eight methylene units were prepared. The structures of the mesogenic units and SCLC polyurethanes were confirmed by Fourier transform infrared spectroscopy and ¹H NMR. Polymer properties were also examined by solubility tests, water uptakes, and inherent viscosity measurements. Differential scanning calorimetry studies indicated that the transition temperature of the isotropic to the liquid‐crystalline phase decreased with increasing spacer length. Wide‐angle X‐ray diffraction (WAXD) studies revealed the existence of liquid‐crystalline phases for both SCLC polyurethanes. Polarized optical microscopic investigations further confirmed the thermotropic liquid‐crystalline behaviors and nematic mesophases of both samples. Thermogravimetric analysis displayed better thermal stabilities for both SCLC polymers and indicated that the presence of mesogenic side chains may increase the thermal stability of segmented polyurethanes. © 2003 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 42: 290–302, 2004     

Dendrimers as scaffolds for multifunctional reversible addition–fragmentation chain transfer agents: Syntheses and polymerization

The synthesis and characterization of novel first‐ and second‐generation true dendritic reversible addition–fragmentation chain transfer (RAFT) agents carrying 6 or 12 pendant 3‐benzylsulfanylthiocarbonylsulfanylpropionic acid RAFT end groups with Z‐group architecture based on 1,1,1‐hydroxyphenyl ethane and trimethylolpropane cores are described in detail. The multifunctional dendritic RAFT agents have been used to prepare star polymers of poly(butyl acrylate) (PBA) and polystyrene (PS) of narrow polydispersities (1.4 < polydispersity index < 1.1 for PBA and 1.5 < polydispersity index < 1.3 for PS) via bulk free‐radical polymerization at 60 °C. The novel dendrimer‐based multifunctional RAFT agents effect an efficient living polymerization process, as evidenced by the linear evolution of the number‐average molecular weight (M_n) with the monomer–polymer conversion, yielding star polymers with molecular weights of up to M_n = 160,000 g mol^?1 for PBA (based on a linear PBA calibration) and up to M_n = 70,000 g mol^?1 for PS (based on a linear PS calibration). A structural change in the chemical nature of the dendritic core (i.e., 1,1,1‐hydroxyphenyl ethane vs trimethylolpropane) has no influence on the observed molecular weight distributions. The star‐shaped structure of the generated polymers has been confirmed through the cleavage of the pendant arms off the core of the star‐shaped polymeric materials. © 2004 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 42: 5877–5890, 2004     

Intramolecular energy transferable (2,2‐diphenylvinyl)phenyl substituted poly(p‐phenylenevinylene) derivative with efficient photoluminescence and electroluminescence

A poly(p‐phenylenevinylene) (PPV) derivative containing a bulky (2,2‐diphenylvinyl)phenyl group in the side chain, EHDVP‐PPV, was synthesized by Gilch route. The reduced tolane‐bisbenzyl (TBB) defects, as well as the structure of the polymer, was confirmed by various spectroscopic methods. The intramolecular energy transfer from the (2,2‐diphenylvinyl)phenyl side group to the PPV backbone was studied by UV‐vis and photoluminescence (PL) of the obtained polymer and model compound. The polymer film showed maximum absorption and emission peaks at 454 and 546 nm, respectively, and high PL efficiency of 57%. A yellow electroluminescence (λ_max = 548 nm) was obtained with intensities of 6479 cd/m² when the light‐emitting diodes of ITO/PEDOT/EHDVP‐PPV/LiF/Al were fabricated. The maximum power efficiency of the devices was 0.729 lm/W with a turn‐on voltage of 3.6 V. © 2004 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 42: 5636–5646, 2004     

Controlled synthesis of amphiphilic biodegradable polylactide‐grafted dextran copolymers

The whole controlled synthesis of novel amphiphilic polylactide (PLA)‐grafted dextran copolymers was achieved. The control of the architecture of such biodegradable and potentially biocompatible copolymers has required a three‐step synthesis based on the “grafting from” concept. The first step consisted of the partial silylation of the dextran hydroxyl groups. This protection step was followed by the ring‐opening polymerization of D ,L ‐lactide initiated from the remaining OH functions of the partially silylated polysaccharide. The third step involved the silylether group deprotection under very mild conditions. Based on previous studies, in which the control of the first step was achieved, this study is focused on the last two steps. Experimental conditions were investigated to ensure a controlled polymerization of D ,L ‐lactide, in terms of grafting efficiency, graft length, and transesterification limitation. After polymerization, the final step was studied in order to avoid degradation of both polysaccharide backbone and polyester grafts. The chemical stability of dextran backbone was checked throughout each step of the synthesis. PLA‐grafted dextrans and PLA‐grafted (silylated dextrans) were proved to adopt a core‐shell conformation in various solvents. Furthermore, preliminary experiments on the potential use of these amphiphilic grafted copolymers as liquid/liquid interface stabilizers were performed. © 2004 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 42: 2577–2588, 2004     

Novel,organosoluble, light‐colored fluorinated polyimides based on 2,2′‐bis(4‐amino‐2‐trifluoromethylphenoxy)biphenyl or 2,2′‐bis(4‐amino‐2‐trifluoromethylphenoxy)‐1,1′‐binaphthyl

Two series of fluorinated polyimides were prepared from 2,2′‐bis(4‐amino‐2‐trifluoromethylphenoxy)biphenyl ( 2 ) and 2,2′‐bis(4‐amino‐2‐trifluoromethylphenoxy)‐1,1′‐binaphthyl ( 4 ) with various aromatic dianhydrides via a conventional, two‐step procedure that included a ring‐opening polyaddition to give poly(amic acid)s, followed by chemical or thermal cyclodehydration. The inherent viscosities of the polyimides ranged from 0.54 to 0.73 and 0.19 to 0.36 dL/g, respectively. All the fluorinated polyimides were soluble in many polar organic solvents, such as N,N‐dimethylacetamide and N‐methylpyrrolidone, and afforded transparent and light‐colored films via solution‐casting. These polyimides showed glass‐transition temperatures in the ranges of 222–280 and 257–351 °C by DSC, softening temperatures in the range of 264–301 °C by thermomechanical analysis, and a decomposition temperature for 10% weight loss above 520 °C both in nitrogen and air atmospheres. The polyimides had low moisture absorptions of 0.23–0.58%, low dielectric constants of 2.84–3.61 at 10 kHz, and an ultraviolet–visible absorption cutoff wavelength at 351–434 nm. Copolyimides derived from the same dianhydrides with an equimolar mixture of 4,4′‐oxydianiline and diamine 2 or 4 were also prepared and characterized. © 2004 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 42: 2416–2431, 2004     

Synthesis,characterization, and curing kinetics of novel ladder‐like polysilsesquioxanes containing side‐chain maleimide groups

Two ladder‐like polysilsesquioxanes (LPS) containing side‐chain maleimide groups have been synthesized successfully by reacting N‐(4‐hydroxyphenyl)maleimide (HPM) with LPS containing 100 mol % of chloropropyl groups (Ladder A ) and 50 mol % of each methyl and chloropropyl group (Ladder B ). HPM was synthesized by reacting maleic anhydride with 4‐aminophenol, and the resulting amic acid was imidized using p‐toluenesulfonic acid as a catalyst (Scheme 1 ). The LPSs were characterized by Fourier transform infrared (FTIR), ¹H nuclear magnetic resonance (NMR), proton‐decoupled ¹³C NMR, ²⁹Si NMR, wide‐angle X‐ray diffraction (WAXD), differential scanning calorimetry (DSC), and thermogravimetric analysis (TGA). Characterization indicated that these polymers had ordered ladder‐like structures with possible defects. These polymers were soluble in common solvents at ambient temperature, which suggested that they were not crosslinked. Both the polymers and the HPM were cured, and their kinetics were followed by dynamic DSC. The Ozawa and Kissinger methods were used to calculate activation energies for curing. Curing increased the temperature at which both 5% weight loss and maximum rate of weight loss were observed. © 2004 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 42: 4036–4046, 2004     

Synthesis and characterization of well‐defined diblock and triblock copolymers of poly(N‐isopropylacrylamide) and poly(ethylene oxide)

Well‐defined diblock and triblock copolymers composed of poly(N‐isopropylacrylamide) (PNIPAM) and poly(ethylene oxide) (PEO) were successfully synthesized through the reversible addition–fragmentation chain transfer polymerization of N‐isopropylacrylamide (NIPAM) with PEO capped with one or two dithiobenzoyl groups as a macrotransfer agent. ¹H NMR, Fourier transform infrared, and gel permeation chromatography instruments were used to characterize the block copolymers obtained. The results showed that the diblock and triblock copolymers had well‐defined structures and narrow molecular weight distributions (weight‐average molecular weight/number‐average molecular weight < 1.2), and the molecular weight of the PNIPAM block in the diblock and triblock copolymers could be controlled by the initial molar ratio of NIPAM to dithiobenzoate‐terminated PEO and the NIPAM conversion. © 2004 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 42: 4873–4881, 2004