钨酸铋量子点和纳米片修饰石墨相氮化碳复合催化剂的制备及其可见光催化活性增强

利用超声-水热法、使用油酸钠辅助合成钨酸铋(Bi₂WO₆)量子点/纳米片修饰的石墨相氮化碳(g-C₃N₄)(Bi₂WO₆/g-C₃N₄)复合光催化剂。 通过X射线粉末衍射(XRD)、透射电子显微镜(TEM)、傅里叶变换红外光谱(FT-IR)、紫外可见漫反射光谱(UV-Vis DRS)、N₂吸附-脱附等技术手段获得Bi₂WO₆/g-C₃N₄催化剂的组成、结构和光吸收性能,分析合成机理。 以罗丹明B(RhB)水溶液为模拟污染物,考察Bi₂WO₆/g-C₃N₄复合催化剂的可见光催化活性。 结果表明:g-C₃N₄和Bi₂WO₆的质量比为3:7的Bi₂WO₆/g-C₃N₄-30具有最有效的异质界面,电化学阻抗和光电流测试结果显示该催化剂的光生载流子传输速率快、复合率低,可见光照射120 min对RhB的降解率达到95.8%;通过活性物质捕捉实验获知光生空穴是光催化反应中的主要活性物质,分析异质界面对光催化活性的影响,进而提出光催化反应机理。     

三元金属硫化物-石墨相氮化碳异质结催化剂的制备及光催化性能

以双氰胺、醋酸锌、钼酸铵、醋酸镉和硫化钠为原料,采用水热法合成了一系列Zn-Mo共掺杂CdS(Zn-Mo-CdS),并与g-C₃N₄组成异质结催化剂(Zn-Mo-CdS/g-C₃N₄)。采用X射线衍射光谱(XRD)、紫外-可见(UV-Vis)光谱、电感耦合等离子体-原子发射光谱(ICP-AES)、电化学阻抗谱(EIS)、X光电子能谱(XPS)等分析手段对制备的催化剂进行了表征。结果表明, Zn-Mo-CdS与g-C₃N₄之间紧密结合并形成异质结,促进界面电荷迁移,抑制光生电子-空穴对的复合。以可见光下降解染料罗丹明B (RhB)为探针反应考察了催化剂性能。结果表明, Zn-Mo-CdS/g-C₃N₄异质结催化剂的光催化性能与单纯g-C₃N₄、Zn-Mo-CdS及双金属硫化物/g-C₃N₄异质结催化剂相比均有大幅度提高,质量比m(Zn-Mo-CdS)/m(g-C₃N₄) = 4 : 1时制备的异质结催化剂表现出最大的降解速率常数,是单纯g-C₃N₄和Zn-Mo-CdS的30倍和10倍。不仅Zn-Mo-CdS,其他三元金属复合硫化物如Mo-Ni-CdS和Ni-Sn-CdS与g-C₃N₄之间也能有效构筑异质结,促进电子-空穴对的分离和催化性能提升。     

碳自掺杂g-C3N4光催化性能的原位光微量热-荧光光谱研究

通过在尿素前驱体中添加单宁酸, 原位缩聚形成碳自掺杂石墨相氮化碳(g-C₃N₄). 利用X射线光电子能谱(XPS)、 场发射扫描电子显微镜(FESEM)、 X射线衍射(XRD)仪和同步热分析(TG-DSC)等方法对碳自掺杂 g-C₃N₄的形貌、 物相结构和能带价态组分进行表征分析, 结合紫外-可见吸收光谱(UV-Vis)和原位光微量热-荧光光谱联用仪获得碳自掺杂g-C₃N₄降解罗丹明B的原位热/动力学信息和三维荧光光谱信息, 探讨了光催化降解罗丹明B的微观机制. 结果表明, 单宁酸浓度≤10 mg/mL时, 碳会取代七嗪单元结构的氮原子形成g-C₃N₄骨架碳自掺杂; 单宁酸浓度≥ 20 mg/mL时, 碳以无定形形式沉积负载在g-C₃N₄表面上形成无定形碳自掺杂. 骨架碳自掺杂g-C₃N₄形成的π电子有效缩短了禁带宽度, 减小了光生电子-空穴复合几率, 比无定形C掺杂g-C₃N₄显示出更优异的光催化性能, 催化主要活性物种为h⁺和·O{}_{\mathrm{2}}^{-}. 碳自掺杂g-C₃N₄光催化降解过程可分为光响应吸热、 降解污染物放热平衡过程和稳定放热3个过程. 其中骨架碳自掺杂g-C₃N₄(C/N摩尔比为0.844)在光照1000 s内, 三维荧光光谱检测的RhB降解率锐减, 光照1000 s后, 其RhB降解率为87.6%, 分别是原始g-C₃N₄和无定形碳自掺杂g-C₃N₄的3.13倍和1.95倍. 光照1000 s后, 光微量热计显示以矿化和降解非荧光发色中间产物为主, 并保持以热变速率为(0.9799±0.5356) μJ/s稳定放热, 为拟零级反应过程, 是光催化反应的决速步骤.     

石墨相氮化碳/蒙脱石复合材料的制备及其可见光催化性能

为提高石墨相氮化碳(g-C₃N₄)对可见光的利用率及光催化效率,采用热聚合与直接负载等方法,将g-C₃N₄负载于蒙脱石表面,制备了g-C₃N₄/蒙脱石复合光催化材料,其结构经SEM, FT-IR及XRD表征。以罗丹明B(RhB)为目标污染物,研究了不同负载量g-C₃N₄/蒙脱石复合光催化剂的可见光催化性能。并分别以对苯醌、碘化钾和异丙醇为自由基捕获剂,研究了复合材料的光催化机理。结果表明：当g-C₃N₄的质量分数为83%(CN/M-83%)时,RhB经可见光照射1 h后,降解率达到99.2%。光催化速率常数为纯g-C₃N₄光催化速率常数的3.2倍。     

质子化g-C3N4/β-SiC复合材料的制备及光催化降解茜素红性能

分别采用热解法和溶胶-凝胶-碳热还原法合成了石墨相氮化碳(g-C₃N₄)和纳米级碳化硅(β-SiC), 通过浸渍-热处理法将两者复合并通过浓盐酸质子化, 分别制备了g-C₃N₄/β-SiC和质子化g-C₃N₄/β-SiC(P-g-C₃N₄/β-SiC)复合光催化剂. 利用X射线衍射(XRD)、 扫描电子显微镜(SEM)、 高分辨透射电子显微镜(HRTEM)、 傅里叶变换红外光谱(FTIR)、 X射线光电子能谱(XPS)、 紫外-可见漫反射光谱(UV-Vis-DRS)和光致发光光谱(PL)等对样品进行了表征. 结果表明, P-g-C₃N₄/β-SiC复合材料的比表面积增大, 光生电子-空穴对的复合几率降低, 光催化性能明显提高. 在光催化降解染料茜素红(ARS)研究中, 样品的可见光催化活性顺序为P-g-C₃N₄/β-SiC>g-C₃N₄/β-SiC>P-g-C₃N₄>g-C₃N₄>β-SiC. 其中P-g-C₃N₄/β-SiC在60 min内对ARS的降解效率高达99.9%, 符合准一阶动力学模型, 速率常数为0.0967 min ^-1, 且循环使用9次后, 光催化降解效率仍保持97.5%以上.     

g-C3N4/BiVO4复合催化剂的制备及应用于光催化还原CO2的性能

用简单的超声分散法合成了具有可见光响应的类石墨氮化碳(g-C₃N₄)/BiVO₄复合光催化剂. 采用X射线衍射(XRD), X射线光电子能谱(XPS), 扫描电子显微镜(SEM), 透射电子显微镜(TEM), 紫外-可见(UV-Vis)分光光谱, 傅里叶红外变换(FTIR)光谱, 荧光发射谱(PL)和光电流响应等技术对所制备催化剂进行相关表征. 通过可见光下(λ> 420 nm)光催化还原CO₂的性能来评价样品的光催化活性, 发现不同复合比的催化剂中, 含40% (w) g-C₃N₄的复合催化剂表现出最高的光催化活性, 其催化活性分别为纯g-C₃N₄纳米片和纯BiVO₄的催化活性的2倍和4倍.光催化活性增加的主要原因是g-C₃N₄和BiVO₄之间形成了异质结, 且相互间能级匹配, 有利于光生电子和空穴的分离.     

氮缺陷石墨相氮化碳的制备及其光催化降解环境有机污染物性能

通过在三聚氰胺热分解过程中加入NaHCO₃制备出具有氮缺陷的石墨相氮化碳（g-C₃N₄）,利用X射线衍射（XRD）、傅里叶变换红外光谱（FT-IR）、N₂吸附-脱附、X射线光电子能谱（XPS）、紫外-可见漫反射光谱（UV-vis DRS）和固体荧光光谱（PL）等方法对其进行表征,并在可见光（λ> 420nm）照射下,以水相中罗丹明B（RhB）的降解为模型反应,研究了该氮缺陷g-C₃N₄对有机污染物降解的光催化活性。结果表明,引入氮缺陷可以提高g-C₃N₄对可见光的吸收以及电子-空穴对的分离效率,进而提高g-C₃N₄的可见光催化活性。催化剂CNK0.005、CNK0.01和CNK0.05在30min内对RhB的降解率分别为79.8%、100.0%和87.6%;而在相同条件下,没有氮缺陷的g-C₃N₄对RhB的降解率仅为59.8%。     

Ni-P@g-C3N4复合材料的合成与可见光催化性能

以三聚氰胺为前驱体,采用两步热聚合法,制备了一系列石墨相氮化碳(g-C₃N₄)基光催化复合材料。通过X-射线衍射光谱(XRD)、扫描电子显微镜(SEM)、N₂吸附、光致荧光光谱(PL)、傅里叶变换红外光谱(FT-IR)和电化学阻抗谱(EIS)等表征了其结构与光电特性。结果发现,Ni-P共掺杂可以有效改善g-C₃N₄的可见光吸收性能,减小其电化学阻抗,抑制光生载流子的复合。以可见光条件下降解亚甲基蓝(MB)溶液为探针反应研究了Ni-P@g-C₃N₄复合材料的光催化降解性能。结果表明,照射120分钟1.5%Ni/P-CN复合材料对MB的降解率为61.7%,速率常数为0.00785 min^-1,是纯g-C₃N₄的两倍。反应体系的主要活性物种为超氧自由基(·O₂^-)。经过简单处理催化剂可重复使用3次以上且活性保持稳定。     

ZnIn2S4/g-C3N4复合材料的制备及可见光催化制氢性能

采用水热方法制备了ZnIn₂S₄/g-C₃N₄复合材料, 并通过X射线衍射(XRD)、 傅里叶变换红外光谱(FTIR)、 紫外-可见漫反射光谱(UV-Vis DRS)、 透射电子显微镜(TEM)和荧光光谱(PL)等手段对其结构和性能进行表征. 结果表明, 当ZnIn₂S₄的负载量为20%(质量分数)时, 复合材料表现出最佳的光催化制氢性能, 制氢速率可达到637.08 μmol·g^-1·h^-1, 分别为纯ZnIn₂S₄和纯g-C₃N₄的4倍和37倍. 其原因在于ZnIn₂S₄和g-C₃N₄之间具有紧密的异质结结构, 两者有效的结合改善了组分的能带匹配和界面电荷转移, 从而大幅增强了载流子的分离和迁移, 进而提高光催化的性能.     

金属相1T´ MoS2增强类石墨相C3N4的可见光催化性能

通过煅烧和静电自组装的方法制备了1T′ MoS₂超薄纳米片和类石墨烯相氮化碳(g-C₃N₄)纳米片的复合材料. 该材料在光催化实验中展现出6.24 μmol?g^?1?h^?1的产氢速率, 优于贵金属铂修饰的g-C₃N₄纳米片的性能(4.64 μmol?g^?1?h^?1). 此外, 该复合材料在光催化降解有机染料甲基橙的实验中表现出0.19 min^?1的催化速率, 而纯g-C₃N₄纳米片只有0.053 min^?1的催化速率. 材料光催化性能的提升可归结于1T′MoS₂ 和g-C₃N₄之间的协同效应, 包括光吸收的增强以及因1T′MoS₂优异电子导电性而得到的高效电荷分离.     

Synthesis of Z-scheme g-C3N4 nanosheets/Ag3PO4 photocatalysts with enhanced visible-light photocatalytic performance for the degradation of tetracycline and dye

Graphene-like C3N4/Ag3PO4 photocatalysts are synthesized by calcination and solutions precipitating method.The obtained g-C3N4/Ag3PO4 composites display excellent photocatalytic activity for the degradation of methylene orange(MO),rhodamine B(RhB)and tetracycline(TC)under visible light irradiation.The solutions containing RhB(10 mg/L)and MO(10 mg/L)can be efficiently degraded within15 min and 30 min.Especially,nearly 80%of TC(50 mg/L)is degraded within 20 min.which are much better than those of pure g-C3N4 nanosheets and Ag3PO4,implying that strong interaction and reasonable energy band alignment in the contact interface can effectively transfer the carries.Furthermore,the g-C3N4/Ag3PO4 composites exhibit the improved stability,and only a slight decrease is observed after three recycling runs.Moreover,the impact of inorganic ions and PH values on the degradation performance is rather small.The Z-scheme photocatalytic mechanism of the g-C3N4/Ag3PO4 composites based on the active species trapping experimental is proposed.This work demonstrates the promising applications of the g-C3N4/Ag3PO4 composites in environmental issues.     

Cu2+改性g-C3N4光催化剂的光催化性能

Photocatalytic technology can effectively solve the problem of increasingly serious water pollution, the core of which is the design and synthesis of highly efficient photocatalytic materials. Semiconductor photocatalysts are currently the most widely used photocatalysts. Among these is graphitic carbon nitride (g-C₃N₄), which has great potential in environment management and the development of new energy owing to its low cost, easy availability, unique band structure, and good thermal stability. However, the photocatalytic activity of g-C₃N₄ remains low because of problems such as wide bandgap, weakly absorb visible light, and the high recombination rate of photogenerated carriers. Among various modification strategies, doping modification is an effective and simple method used to improve the photocatalytic performance of materials. In this work, Cu/g-C₃N₄ photocatalysts were successfully prepared by incorporating Cu²⁺ into g-C₃N₄ to further optimize photocatalytic performance. At the same time, the structure, morphology, and optical and photoelectric properties of Cu/g-C₃N₄ photocatalysts were analyzed by X-ray diffraction (XRD), X-ray photoelectron spectroscopy (XPS), scanning electron microscopy, UV-Vis diffuse reflectance spectroscopy (DRS), and photoelectric tests. XRD and XPS were used to ensure that the prepared photocatalysts were Cu/g-C₃N₄ and the valence state of Cu was in the form of Cu²⁺. Under visible light irradiation, the photocatalytic activity of Cu/g-C₃N₄ and pure g-C₃N₄ photocatalysts were investigated in terms of the degradation of RhB and CIP by comparing the amount of introduced copper ions. The experimental results showed that the degradation ability of Cu/g-C₃N₄ photocatalysts was stronger than that of pure g-C₃N₄. The N₂ adsorption-desorption isotherms of g-C₃N₄ and Cu/g-C₃N₄ demonstrated that the introduction of copper had little effect on the microstructure of g-C₃N₄. The small difference in specific surface area indicates that the enhanced photocatalytic activity may be attributed to the effective separation of photogenerated carriers. Therefore, the enhanced photocatalytic degradation of RhB and CIP over Cu/g-C₃N₄ may be due to the reduction of carrier recombination rate by copper. The photoelectric test showed that the incorporation of Cu²⁺ into g-C₃N₄ could reduce the electron-hole recombination rate of g-C₃N₄ and accelerate the separation of electron-hole pairs, thus enhancing the photocatalytic activity of Cu/g-C₃N₄. Free radical trapping experiments and electron spin resonance indicated that the synergistic effect of superoxide radicals (O₂^•−), hydroxyl radicals (•OH) and holes could increase the photocatalytic activity of Cu/g-C₃N₄ materials.     

二硫化钼量子点/还原氧化石墨烯复合材料的制备及其光催化降解有机染料、四环素和Cr（VI）

以钼酸钠、L-半胱氨酸和氧化石墨烯为原料,采用一锅溶剂热还原法制备了二硫化钼量子点/还原氧化石墨烯（MoS₂ QDs/rGO）复合材料,分别以罗丹明B、亚甲基蓝、四环素和Cr（VI）为目标污染物,研究了复合材料的可见光响应光催化降解性能。结果显示,MoS₂ QDs/rGO对两种染料和Cr（VI）的光催化降解率均可达97%以上,对四环素的光催化降解率为69%;循环使用10次,对目标染料的降解率均保持在90%以上。说明MoS₂ QDs/rGO具有良好的催化活性和稳定性。在降解体系中分别加入异丙醇、对苯醌和乙二胺四乙酸二钠捕获剂,结果显示,超氧自由基（?O₂^-）是MoS₂ QDs/rGO光催化反应的主要活性物种。     

Fe掺杂g-C_3N_4的制备及其可见光催化性能

以硝酸铁和三聚氰胺为原料制备不同含铁量的Fe掺杂石墨氮化碳(g-C3N4).采用X射线衍射光谱(XRD)、紫外-可见(UV-Vis)光谱、傅里叶变换红外(FT-IR)光谱、电感耦合等离子体-原子发射光谱(ICP-AES)、荧光(PL)光谱、X光电子能谱(XPS)等分析手段对制备的催化剂进行了表征.结果表明,铁以离子形式镶嵌在gC3N4的结构单元中,影响了g-C3N4的能带结构,增加了g-C3N4对可见光的吸收,降低了光生电子-空穴对的复合几率.以染料罗丹明B的降解为探针反应系统研究了不同含铁量对g-C3N4在可见光下催化性能的影响.结果表明,m(Fe)/m(g-C3N4)=0.14%时,制备的Fe掺杂g-C3N4表现出最佳的光催化性能,120 min内罗丹明B的降解率高达99.7%,速率常数达到0.026 min-1,是纯g-C3N4的3.2倍.以叔丁醇、对苯醌、乙二胺四乙酸二钠为自由基(·OH)、自由基(O2-·)和空穴(h+VB)的捕获剂,研究了光催化反应机理.     

Ag/Ag_3PO_4/g-C_3N_4复合光催化剂的合成与再生及其可见光下的光催化性能(英文)

研究了用离子交换沉淀法制备的Ag/Ag3PO4/g-C3N4的可见光光催化性能及再生方法.通过X射线衍射(XRD)、场发射扫描电子显微镜(FESEM)、紫外-可见(UV-Vis)吸收光谱及X射线光电子能谱(XPS)对其进行了结构特性分析.XRD结果显示再生后催化剂的结构未发生改变.FESEM及UV-Vis分析结果说明催化剂由Ag3PO4与g-C3N4复合而成.XPS分析结果表明催化剂表面出现少量的银单质.利用可见光(λ420nm)照射下的苯酚降解实验评价了样品的光催化活性,并通过活性物种及能带结构的分析对催化剂的光催化机理进行了推测.研究表明,Ag/Ag3PO4/g-C3N4的光催化活性明显高于纯Ag3PO4及纯g-C3N4,主要原因归结为单质银、Ag3PO4及g-C3N4的协同效应.经过氧化氢和磷酸氢铵钠(NaNH4HPO4)的再生可完全恢复催化剂的活性,这表明该绿色环保的再生方法可实现Ag/Ag3PO4/g-C3N4催化剂在环境中的实际应用.     

g-C_3N_4/BiOBr异质结光催化剂的制备与可见光催化活性

以三聚氰胺作为合成g-C_3N_4纳米片的前躯体,以Bi(NO3)3·5H2O和KBr作为合成BiOBr的原料,采用水热法构建g-C_3N_4/Bi OBr二维异质结可见光催化剂,有效的晶面复合和合适的能带组合有助于增强g-C_3N_4和BiOBr的可见光催化活性。利用X射线衍射(XRD)、透射电镜(TEM)、X射线光电子能谱(XPS)、光致发光光谱(PL)和紫外-可见漫反射光谱(UVvis DRS)等方法表征其结构、光学性质以及组成结构。在可见光(λ420 nm)下以光催化降解RhB来评价合成催化剂的光催化活性,结果表明,g-C_3N_4/BiOBr光催化降解罗丹明B(Rh B)的效率高于单体g-C_3N_4和BiOBr,并对g-C_3N_4/BiOBr增强可见光催化RhB机理进行解释。