以共沉淀法合成的Mg2ZnAl-CO3水滑石为前体,采用离子交换插层组装方法制备了Mg2ZnAl-EDTA柱撑水滑石,并用XRD和IR进行表征。以水滑石前体和柱撑水滑石为吸附剂,用于废水中Pb2+的吸附。柱撑水滑石的吸附容量明显大于水滑石前体,柱撑水滑石的最佳吸附条件为:温度45℃,pH 5.5,吸附时间150min,Pb2+初始浓度100 mg·L-1。在最佳吸附条件下,柱撑水滑石对废水中Pb2+的饱和吸附量为183.51 mg/g。     

有机硅修饰的剥层水滑石及其对废水中金属离子的吸附

对剥层的镁铝硝酸根水滑石(Mg2Al-NO3-LDHs)片表面进行了有机硅化合物(N-(2-Aminoethyl)-3-aminopropyl)tris-(2-ethoxy)silane(KH-791)修饰,并研究了修饰后的水滑石片对废水中Pb2+,Cu2+和Zn2+离子的吸附行为。结果表明:在相同的温度和金属离子浓度条件下,被修饰的水滑石片对Pb2+吸附容量最大,达到378.0 mg.g-1;在以上几种金属离子的混合溶液中,修饰主体材料表现出对Pb2+高度的选择性吸附,对Pb2+吸附容量为85 mg.g-1,而对Zn2+和Cu2+的吸附容量只有30 mg.g-1左右。     

焙烧态镁铝水滑石对诺氟沙星的吸附行为研究

采用共沉淀法合成镁铝水滑石(LDH),用X-射线衍射(XRD)、扫描电镜(SEM)等表征了产物,研究了400℃焙烧后LDH(LDO)的结构、成分及吸附率的变化,通过静态吸附实验考察了LDO对诺氟沙星的吸附性能。结果表明,在固液比1∶500、pH=5.0、吸附温度25℃、离子强度0.1 mol/L的条件下吸附1 h对诺氟沙星(20 mg/L)的吸附率达91.25%。吸附过程符合Langmuir等温线方程,理论平衡吸附量达到32.05 mg/g,推断焙烧态镁铝水滑石对诺氟沙星的吸附是以表面吸附为主的自发反应。     

Ce/Zr/Al类水滑石的合成、表征及其吸附性能研究

本研究对Ce/Zr/Al三元类水滑石材料去除微囊藻毒素(MC)的潜在应用进行了探索。采用共沉淀法合成了碳酸根型Ce/Zr/Al三元类水滑石,通过XRD、IR等手段对样品进行了测试和表征。合成的类水滑石用于吸附MC,并详细研究了其对MC的吸附性能。结果显示,控制反应条件为温度80℃,M3+/M4+摩尔投料比为1∶1,pH为8.5,合成的Ce/Zr/Al三元类水滑石对MC具有较高的吸附性能,对微囊藻毒素LR(MC-LR)最大吸附量可达178μg/g,对MC-LR和微囊藻毒素RR(MC-RR)的吸附效率均大于70%,吸附性能明显高于硅胶等常用吸附剂。这些研究数据表明Ce/Zr/Al三元类水滑石对去除水体中微囊藻毒素具有潜在的应用价值。     

镁铝类水滑石对阳离子染料中性红的吸附及机理研究

研究了镁铝类水滑石对中性红的吸附及其作用机理,考察了时间、pH、温度、电解质浓度等因素对吸附作用的影响。结果表明,镁铝类水滑石对中性红的吸附动力学符合准二级动力学方程,热力学符合Langmuir吸附等温式。在实验范围内,吸附量随溶液pH的增大而增加,随温度的升高而降低,随电解质浓度的增加先增加后降低。吸附过程是放热、熵减小的自发过程。镁铝类水滑石对中性红的吸附缘于为类水滑石与中性红分子中π电子的较强静电吸引作用。     

不同锌铝比水滑石的合成及吸附脱除水中邻苯二甲酸性能的研究

采用共沉淀法合成一系列具有不同锌铝比的水滑石,并利用X射线衍射（XRD）、扫描电镜（SEM）、热重（TG）、氮气吸脱附及电感耦合等离子体质谱（ICP-MS）等表征手段对其结构与组成进行了测试。将上述水滑石材料用于吸附脱除水中邻苯二甲酸污染物,考察了不同锌铝比水滑石吸附邻苯二甲酸性能的差异。结果表明,在较低锌铝比时,随着水滑石锌铝比的增加,其对邻苯二甲酸的吸附量逐渐增大;当锌铝比较大时（>6）,随着锌铝比的增加,水滑石的吸附量基本保持不变。进一步选取锌铝比为6的水滑石,分别对其吸附邻苯二甲酸的动力学和热力学进行了研究,发现其吸附等温线和吸附动力学数据分别符合Freundlich等温吸附模型和准二级动力学模型,且循环吸附性能较好。     

制备方法对NiCoPrLa类水滑石及其衍生复合氧化物结构及催化性能的影响

用微波法,水热法和微波水热法合成NiCoPrLa类水滑石,并用XRD,TG,TPO,TPR,TPD和FT-IR等对NiCoPrLa类水滑石的晶相结构、热稳定性及相应的衍生复合氧化物的晶相结构、还原性能、吸附性能和抗积碳性能等进行了表征,同时以乙醇水蒸气重整制氢为探针反应考察了制备方法对NiCoPrLa类水滑石的衍生复合氧化物的初活性和选择性的影响.结果表明,制备方法影响类水滑石的结构和热稳定性,水热法制备的类水滑石结晶度较好,微波水热法制备的类水滑石具有较好热稳定性,其中微波水热法所制备的类水滑石衍生复合氧化物具有较好的催化活性和抗积炭性能,在350℃温度下乙醇转化率达到86%.     

Mg/Al-NO_3 LDH吸附诺氟沙星的热力学和动力学研究

采用平衡吸附实验,研究了诺氟沙星在自制焙烧态镁铝水滑石(Mg/Al-NO_3 LDH)上的吸附热力学和动力学行为。结果表明,在固液比1∶500、p H=5.0、吸附温度25℃、离子强度0.1 mol/L的条件下,吸附1 h对诺氟沙星(20 mg/L)的吸附过程符合Langmuir等温线方程和准二级动力学,理论平衡吸附量达到32.05 mg/g。其热力学参数ΔG0 KJ/mol,ΔH0 KJ/mol,由此推断焙烧态镁铝水滑石对诺氟沙星的吸附是自发放热反应。     

不同锌铝比水滑石的合成及其吸附脱除水中邻苯二甲酸性能

采用共沉淀法合成一系列具有不同锌铝比的水滑石,并利用X射线衍射(XRD)、扫描电镜(SEM)、热重(TG)、氮气吸脱附及电感耦合等离子体质谱(ICP-MS)等表征手段对其结构与组成进行了测试。将上述水滑石材料用于吸附脱除水中邻苯二甲酸污染物,考察了不同锌铝比水滑石吸附邻苯二甲酸性能的差异。结果表明,在较低锌铝比时,随着水滑石锌铝比的增加,其对邻苯二甲酸的吸附量逐渐增大;当锌铝比较大时(6),随着锌铝比的增加,水滑石的吸附量基本保持不变。进一步选取锌铝比为6的水滑石,分别对其吸附邻苯二甲酸的动力学和热力学进行了研究,发现其吸附等温线和吸附动力学数据分别符合Freundlich等温吸附模型和准二级动力学模型,且循环吸附性能较好。     

二氧化硅负载镍铝水滑石的制备及其催化合成安息香乙醚的研究

采用共沉淀法制备了以二氧化硅为载体,表面包覆镍铝水滑石的NiAl-LDHs/SiO2复合物,借助XRD、IR及N2吸附-脱附等手段对合成物进行了表征,并将其应用于苯甲醛与乙醇反应生成安息香乙醚反应中进行活性评价。结果表明,复合物中镍铝水滑石与二氧化硅以稳定的Si-O-Al和Si-O-Ni键结合,镍铝水滑石均匀分布于二氧化硅表面,且生成的复合物比表面积较大;当镍铝水滑石负载量为20%时,在反应温度为70℃﹑反应时间为60 min条件下,NiAl-LDHs/SiO2催化苯甲醛与乙醇反应的苯甲醛转化率为61.8%,安息香乙醚选择性接近100%,其催化效果明显优于单一的NiAl-LDHs。     

Textural and chemical characterizations of adsorbent prepared from palm shell by potassium hydroxide impregnation at different stages

Preparation and characterization of activated carbon from palm shell, a carbonaceous agricultural solid waste, by potassium hydroxide treatment at different stages were studied. The effects of activation temperature and chemical to sample ratio on the characteristics of the activated carbon were investigated. Fixed-bed adsorption of sulfur dioxide (SO(2)) gas was carried out to evaluate the adsorptive capacity of the samples. Desorption tests were conducted to verify the occurrence of chemisorption due to some surface functional groups or of chemical reaction between SO(2) and KOH. It was found that pre-impregnation of raw palm shell was involved in replacement of some hydrogen ions with potassium ions to form cross-linked complexes, which retarded the tar formation during carbonization, resulting in a relatively high yield. Moreover, these potassium ions accelerated the reaction as catalysts during gasification of chars by carbon dioxide. For chars with mid-impregnation, potassium hydroxide acted in two ways: (i) formation of metallic potassium by dehydration and (ii) conversion into potassium carbonate. Metallic potassium intercalated to the carbon matrix accounted for pore development and potassium carbonate layer prevented the sample from over burn-off. Post-impregnation of final products modified the textural characteristics of the sample as some pore entrances were blocked by chemicals. However, potassium hydroxide enhanced the amount of SO(2) uptaken via formation of potassium sulfite.     

K/CeO2催化剂上碳黑催化燃烧性能及稳定性（英文）

采用不同的钾盐前体制备了一系列K/CeO2催化剂,利用热重和程序升温氧化(TPO)等技术考察了其催化性能及稳定性.结果表明,K/CeO2催化剂可使碳黑完全燃烧温度降低近200oC.钾盐前体对催化活性和稳定性具有较大影响,由于硝酸钾熔点低,金属在载体上的流动性强,有利于催化剂与碳黑的有效接触,因而表现了较高的活性,三次TPO循环试验中催化活性稳定.碳酸钾的熔点高且碱性较强,使碳黑燃烧生成的CO2不可逆吸附在其表面,导致反应活性低,TPO循环实验表明其反应速率降低,失活明显.     

碳酸钾在糠醛PERKIN反应中的催化作用初探

ａ-呋喃丙烯酸是合成ａ一呋喃丙烯酸酯类的必要原料,而后者作为多种食用香精的调香原料和性能较为理想的紫外线吸收剂,在食品和防晒护肤类化妆品中广泛应用［１］。ａ－呋喃丙烯酸的合成是以粮醛和乙酐为原料经ＰＥＲＫＩＮ反应制备,通常以ＣＨ３ＣＯＯＮａ为催化剂,但一般反应时间长,温度高,产率不稳定,糠醛的电子云密度高,活性强,在高温下易氧化和聚合。我们采用碳酸钾作为该反应的催化剂,取得了较好的效果［２］。．ｆｉ４’＝－ＯｒｔＰＩｇｔ习业１．１试剂糠醛ＡＲ（使用前经重蒸馏处理）,乙酸ＡＲ（使用前经重蒸馏处理）…     

燃烧-色谱法测定催化剂上碳含量标准物质的确定

利用燃烧-色谱法测定催化剂上碳含量采用外标法定量时,需要确定一种标准物作为定量的基础.在自主开发的燃烧-色谱高温定碳仪上,详细研究了草酸、碳酸钙和碱式碳酸镁3种物质的分解温度,根据3种物质的定碳常数测定了同一催化剂上的碳含量,并与化学法的测定结果进行了比较.结果表明,碳酸钙是测定催化剂上碳含量最合适的标准物质.     

酚酞型聚芳醚砜(Ⅶ):K_2C0_3存在下PP/DCDPS体系聚合反应机理的研究

利用~(13)C-NMR方法研究了弱碱K_2CO_3存在下酚酞成盐反应及其与活性双卤砜亲核缩聚反应过程中的结构特征。对一系列碱性条件下酚酞(PP)与4,4'-二氯二苯砜(DCDPS)的缩聚反应的研究表明任何影响内酯结构酚酞盐生成的因素都会严重阻碍聚合反应的进行。对模型化合物存在下K_2CO_3在极性非质子溶剂中的溶解/解离行为的研究结果表明酚酞类Card。双酚与固体K_2CO_3之间可能存在着一种特殊的络合作用。基于我们系列研究结果,本文中总结提出了弱碱K_2CO_3存在下酚酞的反应机理。     

微波辐射紫茎泽兰制备优质活性炭的研究

以紫茎泽兰为原料,碳酸钾为活化剂,采用超声波浸渍,微波辐射法制备活性炭.研究了浸渍方式与时间、微波功率、微波辐射时间、剂料比对活性炭吸附性能和得率的影响.得到了本实验条件下的优化工艺条件:超声波浸渍20min、120℃脱水2h,微波功率700W、微波辐射时间12min、剂料比1.25∶1.优化工艺条件下制备的活性炭碘吸附值为1470.27mg/g,亚甲基蓝吸附值为300mL/g,得率为16.35%.浸渍时间极大的缩短,微波辐射时间只有传统法活化时间的1/15左右,活性炭的吸附指标超过了国标GB/T 13803.1-1999和GB/T 13803.2-1999一级品的标准,其中碘吸附值是国家一级标准的1.47倍,亚甲基蓝吸附值是国家一级标准的2.73倍.同时,测定了该活性炭氮吸附,其BET比表面积为1540.97m2/g,总孔容为0.7393mL/g,并通过DFT表征了活性炭的孔径分布,结果表明该活性炭为微孔型活性炭.     

水蒸气气化条件下碳酸钾对煤灰烧结和矿物质演化的影响

在水蒸气气化气氛（水蒸气-氢气-一氧化碳-二氧化碳混合气氛）下考察了反应压力对负载碳酸钾煤灰烧结温度的影响，建立了包含煤的灰分、煤灰化学组成、催化剂负载量及反应压力因素的煤灰烧结温度预测关系式，预测结果与实测烧结温度的误差在±15℃（2%）范围内。利用X射线衍射仪和FactSage热力学计算软件对不同气氛和压力下煤灰中的矿物组成及含量的变化规律进行了分析。结果表明，碳酸钾与煤灰中的硬石膏、方解石反应生成硫酸钾和碳酸钾钙；水蒸气气化气氛下硫酸钾和赤铁矿被还原，碳酸钾钙的分解温度随反应压力的增大而升高；负载催化剂煤灰中氢氧化钾的量随温度和压力的提高而增加，不同压力下煤灰的最低烧结温度与氢氧化钾的含量有关，当氢氧化钾的含量达到一定值时，不同压力下对应的温度与实验测得的煤灰烧结温度接近。     

酚酞型聚芳醚砜(Ⅶ):K2C03存在下PP/DCDPS体系聚合反应机理的研究

 利用¹³C-NMR方法研究了弱碱K₂CO₃存在下酚酞成盐反应及其与活性双卤砜亲核缩聚反应过程中的结构特征。对一系列碱性条件下酚酞(PP)与4,4'-二氯二苯砜(DCDPS)的缩聚反应的研究表明任何影响内酯结构酚酞盐生成的因素都会严重阻碍聚合反应的进行。对模型化合物存在下K₂CO₃在极性非质子溶剂中的溶解/解离行为的研究结果表明酚酞类Card。双酚与固体K₂CO₃之间可能存在着一种特殊的络合作用。基于我们系列研究结果,本文中总结提出了弱碱K₂CO₃存在下酚酞的反应机理。     

氧弹燃烧-离子色谱法测定海藻酸钠中的氯离子和硫酸根离子

采用氧弹燃烧法对海藻酸钠样品进行燃烧,用碳酸钠作为吸收液进行吸收,建立了离子色谱-抑制电导法检测海藻酸钠中阴离子的方法.实验采用SH-AC-1型离子交换色谱柱,最佳色谱条件:以3.6 mmol/L碳酸钠为淋洗液,柱温45℃,流速0.7 mL/min.在此条件下,可同时分离Cl-、SO42-离子,且色谱峰型对称,所测C1...     

腐植酸接枝共聚物对赤红壤K~+吸附与解吸的影响

本文研究了经施用硝基腐植酸与丙烯酸、丙烯酰胺三元接枝共聚物的赤红壤中钾离子的吸附和解吸的影响。实验结果表明,施用共聚物的土壤可减少土壤对中钾离子的吸附,增加土壤对钾离子的解吸,提高钾离子的抗淋溶。改良后的土壤可减少土壤钾的损失,提高钾肥的利用率。