Characterization of Alumina Gel Catalysts by Emanation Thermal Analysis (ETA)

Alumina gels made from the metal alkoxide is known to have high catalyst activity for the selective reduction of NO _x by hydrocarbons. It is also reported that the fine structure of the gels effects the activity. In this study, the effect of the preparation method on the fine structure and catalyst activity of the gels was investigated. Monolithic gels were obtained by hydrolysis of Al(sec-C₄H₉O)₃. The wet gels were dried at 90°C (xerogels), supercritically dried (aerogels), or dried after immersion in an ethanol solution of methyltrimethoxysilane (modified xerogels). The changes in the microstructure during heating were discussed using the results of TG-DTA, ETA and N₂ adsorption. The ETA curves show the ²²⁰Rn-release rate, E, of the samples, previously labelled with ²²⁸Th and ²²⁴Ra, during heating. The decrease in E of the xerogel at temperatures higher than 400°C indicates a gradual decrease in the surface area and porosity. A remarkable decrease in the BET surface area of the xerogel was found after heat-treating at 500°C. On the other hand, constant E of the aerogels and modified xerogels above 450°C suggests high thermal stability. The pore radii, estimated by BJH method, and the catalyst activities at 500°C of the aerogels and the modified xerogels were higher than those of the xerogels. The temperature range in which the alumina gels are applicable as catalysts was determined.     

Surface Area Study of High Area Cobalt Aluminate Particles Prepared by the Sol-Gel Method

Cobalt aluminate particles were prepared by the sol-gel method, starting from aluminum sec-butoxide and cobalt salts with a Co:Al ratio of 1:3. Samples with the same composition were also prepared by the citrate-gel method from cobalt and aluminum nitrates and citric acid. The particles were calcined to temperatures between 400 and 1000°C, for the formation of the mixed oxide having spinel structure. The surface properties of the different samples (BET surface area and pore size distribution) were measured. The highest BET surface area obtained (about 339 m²/g) corresponds to a sample prepared by cobalt acetate and aluminum sec-butoxide, calcined at 400°C. The surface area of the sample is reduced progressively as the sample is calcined to higher temperatures (to about 65 m²/g at 1000°C). Narrow pore size distributions were observed with average pore radius ranging from 17–20 Å, for samples heated to 400°C, to about 55–65 Å, for samples heated to 1000°C. The different surface areas and porosities obtained for particles prepared by different methods, different precursors or calcination temperatures, are discussed.     

Silica–titania aerogel monoliths with large pore volume and surface area by ambient pressure drying

Ambient pressure drying has been carried out for the synthesis of silica–titania aerogel monoliths. The prepared aerogels show densities in the range 0.34–0.38 g/cm³. The surface area and pore volume of these mixed oxide aerogels are comparable to those of the supercritically dried ones. The surface area for 5wt% titania aerogel has been found to be as high as 685 m²/g with a pore volume of 2.34 cm³/g and the 10wt% titania aerogel has a surface area of 620 m²/g with a pore volume of 2.36 cm³/g. Some gels were also made hydrophobic by a surface treatment with methyltrimethoxysilane and trimethylchlorosilane. The surface modified aerogels possess high surface areas in the range of 540–640 m²/g, and are thermally stable in terms of retaining hydrophobicity up to a temperature of 520 °C. The pore size distribution of the aerogels clearly indicates the preservation of the aerogel structure. High Resolution Transmission Electron microscopy has been employed to characterise the aerogels and Fourier Transform infrared spectroscopy to study the effect of titania addition to silica and the surface modification. X-ray diffraction patterns were recorded to verify the molecular homogeneity of the aerogel.     

Surface Energy Changes of Heat Treated TEOS Derived Silica Xerogels

The surface energy of monolithic silica xerogels was examined by measuring the interaction of organic probes with xerogels heated at temperatures close to the gel-to-glass transition temperature. Values of the dispersive component of the surface energy, , between 60 and 80 mJ m^-2 have been observed using n-alkanes for silica xerogels heated at 700, 800 and 900°C. At 1000°C, decreases to 8.37 mJ · m^-2. Also the differential heat of adsorption, variation of standard free energy and entropy of adsorption decrease when the silica xerogel is heated at 1000°C, showing a lower interaction potential of the organic probes with the silica surface. For the silica xerogels heated between 700 and 900°C, the acid character varies in accordance with the variation of the chemical nature of the silica. Upon heating at 1000°C, both acid and base characters are very close in accordance with a neutral surface. Within the experimental conditions used in this work, the surface of the obtained monolithic silica xerogels behaves as a glass surface when the treating temperature is 1000°C.     

Physical Properties of Silica Aerogels Prepared with Polyethoxydisiloxanes

Silica aerogels were made by sol-gel techniques using industrial silicon derivatives (polyethoxydisiloxanes, E-40), followed by supercritical drying with ethanol. The morphology and microstructure of the silica aerogels were investigated by using specific surface area, S_BET, SEM, TEM and the pore size distribution techniques. The thermal conductivity was also measured as a function of air pressure. The results show that the diameter of the silica particles is about 13 nm and the pore size of the silica aerogels is 20–80 nm. The specific surface area of the silica aerogel is about 470 m²/g and the thermal conductivity of the silica aerogel prepared with E-40 is 0.014 w m^–1 K^–1 at room temperature and 1 atm.     

Ambient pressure dried tetrapropoxysilane-based silica aerogels with high specific surface area

In the present paper, we report the synthesis of tetrapropoxysilane (TPOS)-based silica aerogels with high surface area and large pore volume. The silica aerogels were prepared by a two-step sol-gel process followed by surface modification via a simple ambient pressure drying approach. In order to minimize drying shrinkage and obtain hydrophobic aerogels, the surface of the alcogels was modified using trichloromethylsilane as a silylating agent. The effect of the sol-gel compositional parameters on the polymerization of aerogels prepared by TPOS, one of the precursors belonging to the Si(OR)₄ family, was reported for the first time. The oxalic acid and NH₄OH concentrations were adjusted to achieve good-quality aerogels with high surface area, low density, and high transparency. Controlling the hydrolysis and condensation reactions of the TPOS precursor turned out to be the most important factor to determine the pore characteristics of the aerogel. Highly transparent aerogels with high specific surface area (938 m²/g) and low density (0.047 g/cm³) could be obtained using an optimized TPOS/MeOH molar ratio with appropriate concentrations of oxalic acid and NH₄OH.     

Preparation of Porous Cordierite with Thermally Stable Pore Structure

A cordierite ceramic with a thermally stable pore structure was prepared by a simple modification of a sol-gel reaction of alkoxide precursors, synthesized from Mg metal or Mg acetate, Al(i-OPr)₃, and partially prehydrolyzed Si(OEt)₄. For aging and drying, wet cordierite gel was treated with water vapor at 150°C to strengthen the gel network through enhanced hydrolysis and condensation reactions. The cordierite xerogels showed BET surface areas between 220–410 m²/g, depending on the catalyst and treatment conditions used. In particular, water vapor treated xerogel displayed comparatively thermally stable pore characteristics, which exhibited only a 4–17% decrease in BET surface area up to 700°C, while samples prepared using the conventional sol-gel method showed a 55–91% reduction. Both the DTA and XRD patterns showed that crystallization began at 900°C leading to the -Cordierite phase and the subsequent phase transition to -cordierite at temperatures between 1050 to 1250°C.     

Synthesis and characterization of silica xerogels obtained via fast sol–gel process

The synthesis and physical properties of high surface area silica xerogels obtained by a two-step sol–gel process in the absence of supercritical conditions are reported. The hydrolysis and condensation reactions were followed by infrared spectroscopy. The increment in the bands corresponding to silanol and hydroxyl groups suggests that the hydrolysis reaction was complete during the first 30 min. The effect on surface area and global reaction time under various reaction conditions, such as type of alkaline catalyst and solvents, water–monomer and solvent–monomer molar ratios, was also studied. The obtained results suggest that surface area was increased using 3-aminopropyltriethoxysilane as catalyst. The use of isopropyl alcohol as solvent promotes the reduction of the capillary stress, giving a well-structured xerogel. As a conclusion, with H₂O/i-PrOH/TEOS in a molar ratio of 10:4:1, it was possible to obtain silica xerogels with surface areas about 1,240 m²/g. Such surface areas are comparable with those obtained under supercritical conditions (aerogels), and higher than those xerogels conventionally obtained under normal condition (500–800 m²/g).     

Application of ZrO2-Al2O3 Aerogels to Catalysts

ZrO2-Al2O3 aerogels were prepared by hydrolysis of metal alkoxides in alcoholic solutions and supercritical drying in order to obtain an improved de-NOx catalyst with high activity in a wide temperature range. The aerogels have about 20–50% higher activity than the xerogels in the range 300–600°C. The higher activity of aerogels may be attributed to the higher effective gas diffusivity in them, estimated to be about 20–60 times higher than that of the xerogels, because of their high porosity and large pore size. The catalytic activity of aerogels containing 4–10 mol% ZrO2 is more than 20% higher than that of Al2O3 aerogels at temperatures <450°C.     

Ethanol Washing Effect on Textural Properties of the Sodium Silicate-Derived Silica Xerogel

This study deals with the use of ethanol as washing solvent in the preparation of the silica gels from sodium silicate in order to enhance the textural properties, especially surface area. We here examined the effect of ethanol-washing on surface area, micro- and mesopore volume, and average pore size. The silica xerogels prepared from sodium silicate solution exhibited an extremely high surface area of 1139 m2/g by washing their hydrogels with ethanol. Compared to water-washed xerogels, ethanol-washed xerogels showed higher surface areas, total pore volumes, and larger average pore sizes. Unlike the surface area of water-washed xerogel, that of the ethanol-washed xerogel was not affected by the silica concentration of initial solution. This study indicates that the textural properties of sodium silicate-derived xerogels are further enhanced by using ethanol as washing solvent.     

Characterization of Hydrophobic SiO2 Powders Prepared by Surface Modification on Wet Gel

Hydrophobic porous silica has been prepared by surface modification of TEOS (tetraethylorthosilicate) wet gel with 6 and 12 vol.% of TMCS (trimethylchlorosilane). We characterized the products by using FT-IR, TGA, DTA, N₂ adsorption/desorption, contact angle and SEM. Surface silanol groups of the gel were widely replaced by–Si(CH₃)₃ to result in a hydrophobic SiO₂ powder as confirmed by contact angle measurements with H₂O, 1-butanol and ethanol. The modified dried gels had a surface area of 950–1000 m²/g (average pore size 120 Å), compared to the non-modified surface which had a surface area of 690 m²/g (average pore size 36 Å). The adsorption/desorption isotherm curves indicated they had similar pore characteristics as aerogels prepared by the supercritical drying process.     

Microporous Silica Particles Prepared by the Salt-Catalytic Sol-Gel Process with Extremely Low Content of Water

Microporous silica was synthesized by the salt catalytic sol-gel process with extremely low content of water to tetramethoxysilane. Silica particles were precipitated even when the extent of hydrolysis was very low, since ammonium carbonate as a salt catalyst made the polycondensation faster than an acid catalyst. Microporous silica with a high surface area (680 m² g^–1) was obtained by combustion of methoxy groups at 450°C. The methoxy groups can be removed by the post-hydrolysis before heating. A high specific surface area (>750 m²g^–1) of microporous silica was obtained with pore diameter between 1.2 and 2.0 nm.     

Surfactant Templated Silica Xerogels as Adsorbents for Rhodamine 6G

A series of silica xerogels was synthesized by using TEOS as the silica precursor and a non ionic surfactant Triton X100 (TX100) and a cationic surfactant Hexadecyltrimethylammonium Bromide (CTAB) as templates. The xerogels were synthesized through 2‐way catalysis using ultrasonic radiations for homogeneous mixing of the precursors and template. The surfactant template was later removed through calcination at 550 °C. It was found out that gels having CTAB as the template had higher surface area (612.08 m²/g) than the gels templated by TX100 (539.6 m²/g). High surface area xerogels were used in adsorption experiments for aqueous solutions of Rhodamine 6G (R6G). UV visible spectroscopy was used to find out the concentrations of dye solutions. The adsorption data of both the types of xerogels was found to follow Freundlich's adsorption model pointing towards the possibility of adsorption of the dye molecules on the heterogeneous surface of the adsorbent.     

Silica-zirconia monoliths from gels

Zirconium propoxide and tetraethylorthosilicate were hydrolyzed in methoxyethanol which acts as stabilizer of zirconium and in presence of formamide or dimethylformamide as Drying Control Chemical Additives in order to obtain zirconia silica gels. The gels were dried at 70°C to get monolithic xerogels. The influence of zirconium content and DCCA on texture was determined. The evolution of these xerogels was investigated as a function of temperature between 70°C and 1000°C by thermogravimetry, differential scanning calorimetry, I.R. spectroscopy and R.X. diffractometry.     

Gels dried under supercritical and ambient conditions: a comparative study and their subsequent conversion to silica–carbon composite aerogels

In present work, we have prepared gels with various compositions of methyltrimethoxysilane—3-(2,3-epoxypropoxy) propyltrimethoxysilane (MTMS-GPTMS) using a two-step acid base sol–gel process. To make a comparative study between the two common drying routes, we prepared gels under supercritical and also under ambient conditions. The density of the supercritically dried hybrid aerogels lies between 0.18 and 0.31 gcm^?3, while the density of the ambient dried ones ranges between 0.35 and 0.42 gcm^?3. The surface area of MTMS-0.25 GPTMS aerogel dried under supercritical conditions, has been found to be 464 m² g^?1 with a pore volume and average pore diameter of 1.24 cm³ g^?1 and 11 nm respectively. The same composition dried under ambient conditions is found to have similar properties i.e. a BET surface area of 439 m² g^?1, pore volume of 1.22 cm³ g^?1 and average pore diameter of 11 nm. The aerogels were later pyrolyzed yielding silica/carbon composite aerogels. The pyrolized aerogels possessed a surface area as high as 207 m² g^?1 with a total pore volume of 0.98 cm³ g^?1. The pyrolysed aerogels were also calcined to yield carbon free materials.     

Effective preparation of crack-free silica aerogels via ambient drying

Effective ambient-drying techniques for synthesizing crack-free silica aerogel bulks from the industrial waterglass have been developed. Silica wet gels were obtained from aqueous colloidal silica sols prepared by ion-exchange of waterglass solution (4–10 wt% SiO₂). Crack-free monolithic silica aerogel disks (diameter of 22 mm and thickness of 7 mm) were produced via solvent exchange/surface modification of the wet gels using isopropanol/trimethylchlorosilane/n-Hexane solution, followed by ambient drying. The effects of the silica content in sol and the molar ratio of trimethylchlorosilane/pore water on the morphology and property of final aerogel products were also investigated. The porosity, density, and specific surface area of silica aerogels were in the range of 92–94%, 0.13–0.16 g/cm³, and ∼675 m²/g, respectively. The degree of springback during the ambient drying processing of modified silica gels was 94%.     

Application of Alumina Aerogels as Catalysts

Al₂O₃ gels prepared by hydrolysis of Al-alkoxide were applied as catalysts for NO reduction by hydrocarbon. Xerogels were obtained by drying at 90°C, for 24 h, in air. Aerogels were prepared by supercritical drying of the wet gels in ethanol, using an autoclave. The catalyst activity of the gels for NO reduction with C₃H₆ as determined at 200–600°C in a fixed bed flow reactor. NO conversion to N₂ was about 60% at 550°C with both catalysts, and at 600°C it was better with the aerogel than with the xerogel. The specific surface area of the xerogel, which was larger than that of the aerogel as-dried, decreased to 1/3 by annealing at >500°C. However, the surface area of the aerogel hardly changed by annealing at temperatures up to 700°C. The bimodal pore size distribution of the aerogel hardly changed by annealing, too. The microstructure of the aerogels is stable at high temperatures, and they are better catalysts at high temperatures.     

Preparation of octadecyl modified column gels using heat-treated silicas and their retention behaviour in high-performance liquid chromatography

Summary The effect of silanol groups on three types of octadecylmodified column gels using heat-treated silicas by calcination has been studied by high-performance liquid chromatography. After heat-treating at 180°C, 500°C and 950°C, the silicas treated with octadecyldimethylchlorosilane were used for the measurement of physical and chemical analysis. From elemental carbon analysis data, the reactive silanol group concentrations, _OH(s), were determined to be 2.0 in the 180°C treated silica, 2.1 in the 500°C treated silica and 1.6 in the 950°C treated silica, respectively (original silica: mean pore diameter 116 Å, specific surface area 298 m²/g, pore volume 1.22 ml/g, particle size 5.0 m). The separation factors, , of pyridine versus phenol were measured to be 0.79 on 180°C treated silica, 0.91 on 500°C treated silica and 1.98 on 950°C treated silica, using acetonitrile-water mixtures as the eluent. And then, on the basis of the physico-chemical and chromatographic data, the three types of octadecyl modified column gels using heat-treated silicas by calcination have been compared.     

Raman Spectroscopic Investigations of the Effects of Ag+ and Ce3 + Doping on the Densification of Nanoporous Silica Xerogels

Doped and undoped 50 Å porous silica xerogels were heat-treated at various annealing temperatures ranging from 800°C to 1150°C. The heating was performed in air for 1 hour at each temperature. Raman spectroscopy was used to follow the structural changes occurring at various stages of the gel-to-glass transformation, as well as to investigate the effects of metal ions on the densification of these nanoporous silica xerogels. Raman data and density measurements showed that while densification is completely achieved at 1050°C for undoped xerogels, it occurs at 950°C for Ag⁺-doped samples. On the other hand, Ce^{3 +} doping was found to slow down the densification process, with complete densification occurring at 1100°C.     

Preparation and characterization of silica aerogels from diatomite via ambient pressure drying

The silica aerogels were successfully fabricated under ambient pressure from diatomite. The influence of different dilution ratios of diatomite filtrate on physical properties of aerogels were studied. The microstructure, surface functional groups, thermal stability, morphology and mechanical properties of silica aerogels based on diatomite were investigated by BET adsorption, FT-IR, DTA-TG, FESEM, TEM, and nanoindentation methods. The results indicate that the filtrate diluted with distilled water in a proportion of 1: 2 could give silica aerogels in the largest size with highest transparency. The obtained aerogels with density of 0.122–0.203 g/m³ and specific surface area of 655.5–790.7 m²/g are crack free amorphous solids and exhibited a sponge-like structure. Moreover, the peak pore size resided at 9 nm. The initial aerogels were hydrophobic, when being heat-treated around 400°C, the aerogels were transformed into hydrophilic ones. The obtained aerogel has good mechanical properties.