 共查询到20条相似文献,搜索用时 171 毫秒
1.
Dy改性SnO2 / Sb电催化电极的制备及表征   总被引:13,自引:0,他引:13  
为改进钛基SnO2/Sb电极的电催化性能,采用高温热氧化法制备了稀土Dy改性钛基SnO2/Sb电极。以苯酚为目标有机物,考察了所制备电极的电催化活性,并采用SEM、EDS、XRD等分析方法表征了电极的形貌、组成及结构。对制备温度和Dy添加量进行了详细的实验研究,确定了适宜的制备条件为热处理温度650℃、Dy添加量1%左右。研究表明,结晶良好的掺杂SnO2晶粒有助于苯酚的快速彻底分解。Dy掺杂后,半径较大的Dy^3 可能取代半径较小的Sn^4 ,导致SnO2晶胞膨胀。引入Dy可提高SnO2晶粒的形核与长大速率之比,使SnO2的平均粒径变小,有利于电极催化性能的改善。但同时Dy掺杂使杂质原子Sb、Dy在电极表层富集,高含量的Dy会降低电极的性能。  相似文献   

2.
制备了Ti/SnO2+Sb2O3/Fe-PbO2阳极,采用SEM、XRD和ICP对电极的表面形貌和组成进行了表征.为了考察电极的电催化活性,以苯酚为目标污染物,进行了电催化降解实验.研究结果表明Ti/SnO2+Sb2O3/Fe-PbO2电极电催化降解苯酚模拟废水的最佳工艺条件为:电流密度10mA/cm2、支持电解质Na2SO4浓度0.05 mol/L、温度25℃.在25℃时苯酚的电催化氧化降解反应遵循一级反应动力学规律,并且苯酚的电催化氧化主要是·OH参与的间接氧化,反应过程中电极表面产生的羟基自由基对苯酚的氧化去除起着主要作用.  相似文献   

3.
丁海洋  冯玉杰  吕江维  刘峻峰 《分析化学》2007,35(10):1395-1399
采用浸渍-热分解方法制备了钛基二氧化钌(Ti/RuO2)和钛基二氧化锡(Ti/SnO2)两类尺寸稳定阳极电极。以扫描电子显微镜(SEM)和X射线衍射(XRD)对电极结构进行了表征。用循环伏安法(CV)比较研究了Ti/RuO2和Ti/SnO2电极直接电催化氧化苯酚性能,表明苯酚在Ti/RuO2和Ti/SnO2电极上均可发生直接电氧化反应,两种电极上氧化峰电位分别为0.96和1.43 V(vs.Ag/AgC l)。以对苯二甲酸为捕获剂,利用荧光光谱法进行了羟基自由基(.OH)检测。Ti/SnO2电极在电解过程中能够产生.OH;而Ti/RuO2电极.OH的生成极其微弱。Ti/SnO2电极电解过程中生成.OH是其具有高电催化活性的主要原因,也表明了用荧光法进行羟基自由基检测方便、灵敏,可以用于电催化过程羟基自由基的检测。  相似文献   

4.
甲醇在铂修饰的氧化钛电极上电催化氧化行为的研究   总被引:8,自引:0,他引:8  
运用电化学方法评价了电化学阴极还原-阳极氧化两步法制得的以钛为基体的铂修饰的钛氧化物电极对甲醇电催化氧化的性能,结果表明,制得的修饰电极对甲醇氧化呈现了很高的电催化活性和好的稳定性。  相似文献   

5.
Ti/Sb2O5-SnO2/PbO2电极电催化氧化对氨基苯酚   总被引:2,自引:0,他引:2  
以电沉积法制备的Ti/Sb2O5-SnO2/PbO2电极作阳极,恒电流电解水溶液中的对氨基苯酚(PAP),利用紫外光谱探讨了对氨基苯酚电催化氧化的反应历程,系统地考察了电解时间、反应温度,pH值、电流密度以及对氨基苯酚初始浓度对COD去除率的影响,提出了电催化氧化对氨基苯酚的最佳条件.结果表明,对氨基苯酚电催化反应为逐级氧化历程,主要中间产物为苯醌、丁烯二酸和草酸,最终产物为CO2和水.20℃,对初始浓度10mg/L的对氨基苯酚水溶液(pH=6),恒定电流密度100mA/cm^2,电解1h,COD去除率可达98.5%.该方法作为废水中对氨基苯酚的最小化处理.具有良好的应用前景.  相似文献   

6.
采用循环伏安与Tafel曲线比较不同阳极的电催化性能   总被引:1,自引:0,他引:1  
采用循环伏安和Tafel曲线两种方法评价了Pt电极、钛基二氧化钌电极(Ti/RuO2)及钛基二氧化锡电极(Ti/SnO2)的电催化氧化性能.结果表明,在500 mg/L的苯酚溶液中,Pt,Ti/RuO2和Ti/SnO2电极氧化苯酚的峰电位依次为0.93,0.95和1.40 V(vsAg/AgCl).Tafel曲线表明,三种电极析氧过电位的顺序依次是Ti/RuO2相似文献   

7.
钕改性钛基SnO2/Sb电催化电极的制备及表征   总被引:2,自引:0,他引:2  
为改善钛基SnO2/Sb电极的电催化性能,采用浸渍法制备了Nd改性钛基SnO2/Sb电极。以活性艳红X-3B为目标有机物,考察电极的电催化性能,对制备温度和Nd掺杂量进行了研究,确定了适宜的制备条件为:热处理温度550℃,Nd掺杂量1.0%。采用SEN,EDS,XRD及XPS等分析方法对所制备电极的表面形貌、元素组成及结构进行分析,发现掺杂Nd可使SnO2粒径变小,有利于电极电催化性能的改善,同时Nd元素的引入可使杂质元素sb,Nd在电极表面涂层富集。Nd改性钛基SnO2/Sb电极表面主要是四方相金红石结构的SnO2晶体,掺杂的sb和Nd分别以Sb^5+和Nd^3+的形式存在。电极动电位扫描测试结果表明,Nd改性钛基SnO2/Sb电极具有较高的阳极析氧电位,有利于有机物的阳极氧化降解。  相似文献   

8.
以纳米TiN粉体和氯铱酸的混合液为涂液,采用浸渍-热分解法制备了含IrOx-TiO2中间层的钛基氧化铱电极.利用扫描电镜、X射线能谱和X射线衍射技术并结合电化学方法考察了中间层的组成和焙烧温度对电极的电催化性能和使用寿命的影响.结果表明,IrOx-TiO2中间层的加入没有改变传统的钛基氧化铱电极的形貌特征和组成,并使电极具有相同的电催化响应特性,同时大大提高了钛基氧化铱电极的使用寿命.制备钛基氧化铱电极的最优条件为焙烧温度450℃,中间层中Ir/Ti摩尔比为1.5。  相似文献   

9.
通过循环伏安的电化学方法在金属钛基体上先后进行苯胺的聚合和金属铂的电化学沉积,得到以金属钛为基体的聚苯胺载铂电极(Pt/PAn/Ti),并通过扫描电镜和循环伏安法对该电极进行了表征。通过研究甲醛在该电极上的电催化氧化行为,考察了载铂量对甲醛氧化效果的影响及PAn在电催化氧化甲醛的过程中所起的作用。结果表明,载铂量与甲醛的氧化有一定的关系,PAn的存在使得铂微粒分散程度更好,有效面积更大,与相同铂沉积量的Pt/Ti电极相比,甲醛在其上的正向扫描氧化峰电流密度增加了2.3倍,电位负移了40mV;反向扫描氧化峰电流密度增加了5倍,电位负移了30mV。同时,PAn的存在也增强了电极的抗中毒能力。  相似文献   

10.
采用水热法制备了钛基纳米金微粒修饰电极(Au/Ti)。扫描电镜图表明纳米金颗粒粒径大约为300 nm,在钛基体表面构成三维多孔网状结构。运用循环伏安,电位阶跃和交流阻抗等电化学技术研究了碱性介质中甲醛在Au/Ti电极上的电氧化行为。循环伏安图显示,甲醛在Au/Ti上的起始氧化电位在-0.90 V左右,相对于多晶金电极提前大约0.2 V,交流阻抗测试表明,甲醛在Au/Ti电极上电氧化表现出低的电荷传递电阻。研究结果表明钛基纳米金微粒修饰电极对甲醛氧化具有良好的电催化活性。  相似文献   

11.
陈野  赵文丽  温青 《电化学》2011,(2):199-203
应用阳极电沉积法制备钛基二氧化锰(Ti/MnO2)电极.采用X射线衍射(XRD)、扫描电子显微镜(SEM)及能谱(EDS)表征电极结构、形貌.据V~logi曲线及苯酚降解实验优化电极制备工艺参数:在电流密度4mA·cm-2、Mn2+离子浓度0.5 mol·L-1及温度70℃条件下阳极电沉积Ti/MnO2电极.以苯酚为目...  相似文献   

12.
应用电化学阳极氧化法在纯Ti基底上制备高度有序的TiO2纳米管阵列,考察了Ti/TiO2光阳极的光电化学响应.以苯酚溶液为目标污染物,研究Ti/TiO2电极的光电催化性能,并与光催化性能进行比较.结果表明,该电极光电催化性能优于光催化性能.施加0.6 V电压时,光电催化性能最好.电化学阻抗谱分析显示,光电催化和光催化降解过程的速控步骤均为表面反应步骤,外加偏压减小了界面电荷转移阻抗,提高了光生载流子的分离效率.  相似文献   

13.
Ag/TiO2对含酚废水的光电催化降解   总被引:5,自引:0,他引:5  
Ag/TiO2对含酚废水的光电催化降解;Ag/TiO2; 光电催化; 苯酚;电解质  相似文献   

14.
Lead dioxide electrodes on Ti substrates were prepared by thermal-deposition or electro-deposition. The amount of hydroxyl radicals generated at the electrodes prepared by the above-mentioned two methods was compared with that at the electrodes mingled with Bi or La prepared by electro-deposition. The experimental results indicate that the highest concentration of hydroxyl radicals generated by thermal-deposition, electro-deposition mingled with nothing, electro-deposition mingled with Bi or La was 0.781, 1.048, 1.838 or 2.044 μmol/L, respectively. When phenol was electrolyzed on the four electrodes at a current density of 30 mA/cm2, the removal efficiency of phenol after electrolysis for 1.5 h was 87.30%, 93.55%, 97.95% or 98.70%, TOC removal efficiency after electrolysis for 5 h was 86.76%, 94.26%, 98.53% or 99.60%, respectively. Through the degradation experiments of phenol, the amount of hydroxyl radicals was responsible for the removal efficiency of phenol. The electro-catalytic characteristics were investigated by SEM, the generation amount of hydroxyl radicals, the degradation degree of phenol and the stability and conductivity of the electrodes were also investigated. The experimental results indicate that the four electrodes all show good electro-catalytic characteristics; the electro-catalytic characteristics of the electrode mingled with La were superior to those of the other three ones, and the electrochemical degradation of phenol followed one-step reaction dynamics.  相似文献   

15.
The widely utilization of phenol and its derivatives such as 3-nitrophenol (3-NP) has led to the worldwide pollution in the environment. In this study, Ti/TiO2 photoelectrode was prepared with anodic oxidation of Ti foil electrode and then the photoelectrocatalytic (PEC) degradation of 3-NP was performed via this electrode, comparing with photocatalytic (PC), electrooxidation and direct photolysis by ultraviolet light. A significant photoelectrochemical synergetic effect in 3-NP degradation was observed on the Ti/TiO2 electrode and rate constant for the PEC process of Ti/TiO2 electrode was about three times as high as its PC degradation process. 3-NP concentration monitoring was carried out with differential pulse voltammetry. Results showed that PEC degradation has highest effect on concentration decreasing of 3-NP at solution and degraded it about 38 %, while other processes degradation efficiencies were about 4, 7, and 12 % for electrooxidation, direct photolysis and photocatalytic degradation, respectively. Finally, effects of solution pH and applied potential on degradation efficiency were studied and results showed that optimum pH for degradation is equal 4.00 and optimum potential is 1.2 V vs. Ag|AgCl|KCl (3M) reference electrode.  相似文献   

16.
苯酚在热氧化法制备的SnO2/Ti电极上的电氧化研究   总被引:7,自引:0,他引:7  
张清松 《电化学》1999,5(4):401-405
以热氧化法制备的SnO2/Ti电极作为阳极用于含苯酚酸性溶液的恒电流电解,测定了苯酚浓度、溶液中化学需氧量(COD)以及瞬时电流效率等随电解时间的变化。结果表明,用SnO2/Ti电极代替铂作为阳极可使相同氧化电量下的COD明显下降,而平均电流效率提高了3倍,讨论了两种电极上苯酚氧化的反应机理。  相似文献   

17.
Despite of the hazardous risk of Pb2+leakage,lead dioxide has been attributed as a quasi-ideal anode material with high oxygen evolution potential,excellent conductivity,good stability and low cost in electrochemical oxidation wastewater treatment technique.In this study,a novel Ti/PbO2 anode was fabricated by embedding raw materials that are readily and cheaply available,i.e.,hairs.The structure-activity relationship of the new electrode was firstly revealed by material an...  相似文献   

18.
采用电化学沉积法在Ti基底上制备了复合电极Ti/α-PbO2/β-PbO2,扫描电镜结果表明电极呈现由β-PbO2小晶体组成的菜花状微观形貌.所制电极在电化学降解环境污染物2-氯酚时表现出较高的电催化效率、较好的电极稳定性和较长的电极寿命.用正交实验优化了电化学降解2-氯酚的实验条件.在最优的实验条件(2-氯酚初始浓度50 mg/L,电解质0.1 mol/L Na2SO4,温度35oC,阳极电流密度20 mA/cm2)下电化学降解180 min后,2-氯酚的去除率达100%.动力学结果表明, Ti/α-PbO2/β-PbO2电极上2-氯酚的电化学氧化符合准一级动力学过程.  相似文献   

19.
董艳杰  林海波  刘小波  任秀彬  姜梅 《化学学报》2007,65(20):2257-2260
用循环伏安法研究了Ti/PbO2电极在苯酚硫酸溶液中的电催化作用. 结果表明, 在硫酸溶液中, Ti/PbO2阳极对苯酚具有电催化氧化作用. 如果苯酚浓度较低, 产生的吸附态羟基自由基可以将苯酚氧化, 直至完全矿化. 当苯酚浓度较高或产生的羟基自由基量相对较小时, 苯酚或中间产物可吸附在电极表面, 降低电极的真实表面积, 减少电极的活性点, 阻止反应物接近电极表面, 抑制苯酚的进一步氧化. 随着电解时间的延长, 这些吸附物由于逐渐被氧化, 电极活性恢复.  相似文献   

20.
以钛网为基底,采用电沉积法制备了Ni-Fe/Ti析氧电极,然后将得到的Ni-Fe/Ti电极通过固相硫化制备了Ni-Fe-S/Ti析氢电极. 分别考察了电沉积液中Ni 2+/Fe 3+离子摩尔浓度比和硫脲加入量对Ni-Fe/Ti和Ni-Fe-S/Ti结构和电化学性能的影响. 结果表明,随着电沉积液中Ni 2+含量的增加,Ni-Fe/Ti电极析氧性能先增强后减弱,Ni9Fe1/Ti电极具有最好的析氧性能;随着硫脲加入量的增加,Ni-Fe-S/Ti电极析氢性能呈现先增强后减弱的趋势,Ni9Fe1S0.25/Ti电极具有最好的析氢性能. 在50 mA·cm -2下,Ni9Fe1/Ti电极的析氧过电位为280 mV,Ni9Fe1S0.25/Ti电极的析氢过电位为269 mV,且均具有很好的稳定性. 将Ni9Fe1/Ti与Ni9Fe1S0.25/Ti分别作为阳极和阴极进行电催化全水分解,电流密度达到50 mA·cm -2所需电势仅1.69 V,表现出很好的全水解催化性能.  相似文献   