不同MgO担体对Ba-Ru/MgO氨合成催化剂物化性质和反应性能的影响

采用不同沉淀剂制备了MgO材料,以其为载体制备了Ba-Ru/MgO氨合成催化剂,考察了沉淀剂种类和BaO助剂对其氨合成性能的影响.通过X射线衍射(XRD)、N2物理吸附、X射线荧光光谱(XRF)、透射电镜(TEM)、H2程序升温还原(H2-TPR)、CO2程序升温脱附(CO2-TPD)、H2程序升温脱附(H2-TPD)和N2程序升温脱附(N2-TPD)表征手段,对不同沉淀剂影响Ba-Ru/MgO催化剂氨合成性能的原因进行了探索.结果表明:采用(NH4)2CO3作沉淀剂制备的Ba-Ru/MgO催化剂表面Ru物种易于在低温下还原,催化剂表面在低温区具有较多数量的弱碱性吸附位,在450℃、5.0 MPa和5 000 h-1条件下,由(NH4)2CO3做沉淀剂制备的Ba-Ru/MgO催化剂活性最高,出口氨浓度为3.74%.BaO助剂的加入大大减少了Ba-Ru/MgO催化剂表面吸附氢的数量,增大表面脱附氮的数量,从而易于N2解离吸附,提高氨合成反应速率.     

氧化镁载体和氧化钡助剂对钌基氨合成催化剂结构和性能的影响

采用不同来源氧化镁(市售MgO-1,合成MgO-2)作为钌基氨合成催化剂载体,浸渍法制备了添加不同BaO助剂含量的Ba-Ru/MgO催化剂,通过X射线衍射(XRD)、热重-量热扫描分析(TG/DSC)、N2-低温物理吸附、透射电镜(TEM)、H2程序升温还原(H2-TPR)和CO2程序升温脱附(CO2-TPD)等手段对其进行了表征,考察了不同来源的MgO和BaO助剂含量对负载型钌基氨合成催化剂的物相结构、织构性质、微观形貌、Ru物种的还原性质和体系酸碱性质以及催化剂的氨合成活性等方面的影响。结果表明,MgO的理化性质对所制备的钌基氨合成催化剂的结构以及氨合成活性有较大影响。MgO-2比表面较大,总碱性位数量较多,负载在其表面的Ru粒子粒径在2 nm左右,nBa∶nRu为1.0时,Ba-Ru(1∶1)/MgO-2催化剂表面的Ru物种易于还原,表面存在的弱碱性位极大地促进了氨合成活性,在400°C时活性达到15.40 L.g-1Ru.h-1(3.0 MPa,5 000 h-1),在相同反应条件下比Ba-Ru/MgO-1催化剂活性更高。     

特定碱性MgO纳米晶暴露晶面上铁基催化剂及其费-托合成反应的研究

本研究采用等量浸渍法、化学沉淀法和超声浸渍法合成了一系列具有良好外露晶面的Fe/MgO催化剂。采用X射线粉末衍射、高分辨透射电子显微镜、CO₂程序升温脱附、H₂程序升温还原、X射线光谱学和N₂物理吸附等物理化学方法对催化剂进行了表征。MgO纳米晶载体的碱性会影响费-托合成产物的选择性。在超声浸渍过程中,MgO纳米晶载体的碱性得到了保持。研究结果显示,Fe/MgO催化剂的碱性会提高CO解离速率和产物中烯烃的选择性。此外,相比于MgO（100）晶面,MgO（111）晶面负载铁基催化剂具有更高的活性（TOF）和烯烃选择性。MgO（111）晶面上更有利于CO的吸附,抑制二次加氢反应,提高产物中烯烃的收率。     

不同MgO载体对合成低碳烯烃用铁锰基催化剂的影响

采用共沉淀法、硝酸盐热分解法制备的MgO和商品MgO为载体,使用共浸渍法制备了系列FeMn/MgO催化剂,以CO加氢合成低碳烯烃为模型反应,对不同催化剂的反应性能进行了考察,采用X射线光电子能谱、N2物理吸附、X射线物相分析、程序升温还原等表征技术对催化剂的结构和性能进行了表征。结果表明,采用共沉淀法制备的MgO载体比表面积最大,达到203.5m²/g,以此为载体制备的催化剂取得了最优的CO加氢合成低碳烯烃性能。在340℃、2.0MPa、1600h^-1的反应条件下,CO转化率达到91.36%,C₂⁼～C₄⁼选择性为58.48%。催化剂的比表面积大,活性组分分布均匀且在表面含量高及低温还原性能的明显改善是其具有优异的催化性能的重要原因。     

高活性Pd/MgO催化剂的制备及其CO氧化偶联制草酸二甲酯催化反应

利用溶液法结合高温煅烧处理合成MgO载体,通过浸渍法制备Pd/MgO催化剂并对其进行CO氧化偶联制草酸二甲酯催化性能研究。通过X射线粉末衍射、CO2程序升温脱附、比表面仪、热重分析、扫描电镜、透射电镜和微型催化评价装置对合成的样品进行结构和性能表征。结果表明,合成的MgO载体是一种Lewis碱性很强的纳米片结构,Pd纳米颗粒高度分散在MgO载体上,粒径小且分布均一。此MgO纳米片作为载体制备的Pd/MgO催化剂在较低的Pd负载量(0.5%)下表现出优异的CO氧化偶联催化性能,在反应温度130℃时CO单程转化率高达65%,草酸二甲酯选择性96%,稳定性超过100 h,明显越于工业催化剂(Pd/α-Al2O3),具有潜在的工业应用前景。     

MgO负载Cu2O催化剂的制备及其催化环己醇脱氢

 以MgO为载体,水合肼为还原剂,采用浸渍还原法制备了Cu2O/MgO催化剂,考察了不同制备条件对其催化环己醇脱氢性能的影响,并采用N2物理吸附、 X射线衍射、透射电镜、 X射线光电子能谱、俄歇电子能谱和程序升温还原等手段对催化剂进行了表征. 实验结果表明,当Cu2+∶N2H4·H2O∶NaOH摩尔比为1∶1∶2时催化剂的活性最高. 与传统的Cu/MgO催化剂相比, Cu2O/MgO催化剂对环己醇脱氢反应具有很高的催化活性.     

特定碱性MgO纳米晶暴露晶面上铁基催化剂及其费-托合成反应的研究（英文）

本研究采用等量浸渍法、化学沉淀法和超声浸渍法合成了一系列具有良好外露晶面的Fe/MgO催化剂。采用X射线粉末衍射、高分辨透射电子显微镜、CO2程序升温脱附、H_2程序升温还原、X射线光谱学和N_2物理吸附等物理化学方法对催化剂进行了表征。MgO纳米晶载体的碱性会影响费-托合成产物的选择性。在超声浸渍过程中,MgO纳米晶载体的碱性得到了保持。研究结果显示,Fe/MgO催化剂的碱性会提高CO解离速率和产物中烯烃的选择性。此外,相比于MgO(100)晶面,MgO(111)晶面负载铁基催化剂具有更高的活性(TOF)和烯烃选择性。MgO(111)晶面上更有利于CO的吸附,抑制二次加氢反应,提高产物中烯烃的收率。     

氧化铝载体和氧化钡助剂对钌基氨合成催化剂结构和性能的影响

采用不同来源γ-Al2O3(市售Al2O3-1,合成Al2O3-2)作为钌基氨合成催化剂载体,利用浸渍法制备了一系列添加不同BaO助剂含量的Ba-Ru/Al2O3催化剂.通过X射线衍射(XRD)、N2-低温物理吸附、X射线荧光光谱(XRF)、透射电镜(TEM)、H2程序升温还原(H2-TPR)、NH3程序升温脱附(NH3-TPD)和X射线光电子能谱(XPS)等方法研究了不同来源的Al2O3以及BaO助剂含量对负载型钌基催化剂的物相结构、织构性质、微观形貌、表面性质和催化剂的氨合成活性等方面的影响.结果表明,载体的物理化学性质对制备的钌基氨合成催化剂的结构以及活性有较大影响.BaO助剂对催化剂的影响主要表现在两个方面:添加量不同导致BaO与γ-Al2O3的作用力不同,从而进一步影响催化体系的比表面积和孔结构性质;BaO助剂会对体系的Ru物种还原性质以及催化剂表面酸碱性质进行调节,适量BaO的加入能够极大提高反应活性,而这种最佳量与载体性质密切相关.     

MgO海/泡石复合载体负载Cu催化剂催化环己醇脱氢

采用浸渍沉淀法制备了不同比例的MgO/海泡石(Sep)复合载体负载Cu催化剂,并考察了其对环己醇脱氢反应的催化性能。采用N2气物理吸附、X射线衍射(XRD)、红外光谱(IR)、氨气程序升温脱附(NH3-TPD)、程序升温还原(TPR)等测试技术对催化剂进行了表征。结果表明,海泡石的引入有助于催化剂比表面积的增加,但当载体中海泡石的比例太高时,会导致催化剂酸性以及活性组分Cu状态的变化,从而降低催化剂的活性和选择性。当复合载体中海泡石质量分数为40%时,催化剂的活性最高,选择性也较好。     

柠檬酸络合法制备Ba促进ZrO_2负载Ru催化剂上氨合成反应性能

采用柠檬酸络合法制备了一系列不同含量Ba掺杂的ZrO2,再用浸渍法制备了K-Ru/Ba-ZrO2催化剂并将其用于氨合成反应.采用X射线衍射和CO2程序升温脱附技术考察了Ba含量对催化剂结构与性能的影响.结果表明,Ba掺入ZrO2后形成的BaZrO3有助于其负载的Ru催化剂氨合成活性的显著提高.在5.0MPa,10000h–1,425oC时,Ru/Ba-ZrO2(Ba:Zr摩尔比为1:1)催化剂活性最高,出口氨浓度和反应速率分别达9.24%和29.77mmol/(g·h).这主要归因于载体的强电子传导性能和碱性提高.     

Cover Picture

The cover picture shows an arrangement of ruthenium atoms representing the active site of ruthenium catalysts for ammonia synthesis. This B(5)-type active site consists of three ruthenium atoms in one layer (blue spheres) and two ruthenium atoms in the layer directly above this (red spheres). This arrangement is energetically preferred, because none of the ruthenium atoms is in contact with both of the nitrogen atoms (green spheres) of the adsorbed N(2) molecule. Based on knowledge of this active site a number of catalysts were prepared by using [Ru(3)(CO)(12)] (upper green sphere) as a precursor. These catalysts were characterized (left red sphere and TEM micrograph in the background), tested using a parallel screening procedure (left and lower blue spheres), and kinetically analyzed (right blue sphere). The resulting barium-promoted Ru/MgO catalyst is the most active catalyst for ammonia synthesis to be described (right red sphere). It can be concluded that the B(5)-type site also dominates the activity of the promoted catalysts (lower green sphere). The enormous catalytic potential of Ba-Ru/MgO is described by Muhler et al. on pp. 1061 ff.     

Pt/MOx-SiO2 (M=Ce,Zr, Al)催化剂对CO和C3H8氧化性能的影响

采用共沉淀法制备质量比为1:1的MOx-SiO2(M=Ce,Zr,Al)复合氧化物,以此为载体采用浸渍法制备了铂基氧化型催化剂.考察了该系列催化剂在模拟柴油车尾气条件下,经SO2硫化前后对C3H8和CO的氧化性能.用X射线衍射(XRD)、低温N2吸附-脱附、氨气/氧气/二氧化碳程序升温脱附(NH3/O2/CO2-TPD)和X射线光电子能谱(XPS)等手段进行了表征.NH3-TPD证实催化剂表面存在多种酸中心,硫化后催化剂表面中强酸中心增多.O2-TPD证实催化剂表面存在α和β氧物种,硫化后催化剂表面氧脱附量减少.其中Pt/Al2O3-SiO2表面酸性最弱和表面氧脱附量最大.XPS结果表明新鲜催化剂经硫化后会使催化剂表面Pt的结合能降低.活性测试结果表明,三种催化剂对CO和C3H8的催化氧化活性均较好,其中Pt/ZrO2-SiO2抗SO2中毒性能最佳,具有良好的应用前景.     

沉淀方式对氧化还原共沉淀制备Ru/CeO2氨合成催化剂结构与性能的影响

采用氧化还原共沉淀法制备了Ru/CeO2氨合成催化剂,并运用N2物理吸附、X射线衍射(XRD)、场发射扫描电镜(FE-SEM)、CO吸附和H2程序升温还原(H2-TPR)等技术对其进行了表征,考察了沉淀时反应液的并流、反加、正加对所制备的Ru/CeO2催化剂氨合成性能的影响.结果表明,不同沉淀方式所得到的催化剂,催化剂的表面织构和金属钌的分散度都存在明显的差别,最终影响了催化剂的氨合成活性,其中采用反加法制备的催化剂上钌的分散度(45.6%)和还原性最好,比表面积最大(120 m2/g),因而催化活性最高,在10 MPa,10000 h?1,425℃反应时,出口NH3浓度达到12.6%.     

Characterization and Catalytic Behavior of Nano Pt/MgO Catalysts

"Pt/MgO catalysts were prepared by using wet impregnation method. X-ray diffraction, transmission electron microcopy (TEM), electron spectroscopy for chemical analysis, and temperature programmed surface reaction (TPSR) were used to characterize the calcined and used catalysts. Partial Oxidation of Methane (POM) to synthesis gas was carried out in a fixed bed micro-reactor to test the catalytic activity. TEM images revealed that Pt particles have the size of less than 10 nm, the size of the support MgO is about 50-200 nm. At 800 oC, the Pt/MgO catalyst exhibited a very high activity and stability for POM reaction. Both the conversion of methane and selectivities to CO and H2 remained almost constant up to 120 h. The dispersed Pt existed in the metallic state. The state and the dispersion of active Pt and the structure of support MgO were very stable, together with the high ability to resist carbon deposition, made the catalysts show a very high stability for POM under stoichiometric reaction conditions."     

沉淀方法对Ru/CeO_2氨合成催化剂催化性能的影响

采用沉淀法制备了Ru/CeO_2氨合成催化剂,并运用N_2物理吸附、X射线衍射、X射线荧光光谱、CO吸附和H2程序升温还原等技术对其进行了表征,考察了沉淀时反应液的并流、反加、正加以及沉积一沉淀对所制备的Ru/CeO_2催化剂氨合成性能的影响.结果表明,不同制备方法所得到的催化剂,其氯残留量和载体的还原性能都存在明显的差别,最终影响了催化剂的氨合成活性,其中采用正加法制备的催化剂上氯残留量少,载体易还原,因而催化活性最高,在10MPa,10 000h~(-1),450℃反应时,NH_3浓度达到11.9%.     

Li-Mn/WO_(3)/TiO_(2)固体酸催化剂的制备及其甲烷氧化偶联催化性能研究北大核心CSCD

Li-Mn/WO_(3)/TiO_(2)催化剂具有良好的低温OCM催化性能,采用浸渍法制备Li-Mn/WO_(3)/TiO_(2)催化剂,并详细考察WO_(3)对催化剂物理化学性质及催化性能的影响.利用X射线衍射(XRD)、CO_(2)程序升温脱附(CO_(2)-TPD)、O_(2)程序升温脱附(O_(2)-TPD)、H_(2)程序升温还原(H_(2)-TPR)、拉曼光谱(Raman)和X射线光电子能谱(XPS)等表征技术对催化剂进行了研究,发现WO_(3)的添加提高了C_(2)选择性,并有效抑制了深度氧化.XRD与CO_(2)-TPD结果表明,WO_(3)的添加不仅有利于金红石型TiO_(2)的形成而且能够中和催化剂表面的强碱位,从而抑制了深度氧化反应.O_(2)-TPD和H_(2)-TPR结果表明,WO_(3)的添加降低了晶格氧(O^(2-))移动性,进而提高了反应的C_(2)选择性.此外,WO_(3)的添加促使了低温氧化偶联活性物种MnTiO_(3)的形成并提高了活性物种的分散性,因此提高了催化剂甲烷氧化偶联的反应活性和选择性.所有Li-Mn/x%WO_(3)/TiO_(2)催化剂中,Li-Mn/5%WO_(3)/TiO_(2)催化剂显示出最佳的OCM反应性能.在750℃,CH_(4)∶O_(2)∶N_(2)=10∶4∶5,GHSV=2280 mL·g^(-1)·h^(-1)条件下,最高的C_(2)产物收率可达16.3%.