不同磷含量对NiMoP/Al2O3加氢处理催化剂的影响

采用NiMoP浸渍液浸渍载体γ Al₂O₃制备了不同磷含量的NiMoP/Al₂O₃加氢处理催化剂。为了研究磷对该系列催化剂活性相结构的影响,用二苯并噻吩（DBT）和喹啉为模型化合物,考察了催化剂的加氢脱硫（HDS）和加氢脱氮（HDN）性能。结果表明,添加适当的磷能够提高催化剂的HDS和HDN活性,但是高含量的磷能显著的降低催化剂的催化性能。通过对催化剂进行XRD和HRTEM表征发现,添加磷能够增加MoS2的堆积层数以及Ⅱ型“Ni-Mo-S”相的相对含量,这是因为在制备过程中添加磷降低了活性组分与载体之间的相互作用。     

助剂对Co/Al2O3催化剂浆态床费托合成反应性能影响

考察了ZrO₂、Ru或Pt助剂对Co/Al₂O₃催化剂结构及浆态床费托合成反应性能的影响。实验结果表明,添加ZrO₂助剂可阻止或降低难还原铝酸钴的形成、促进催化剂的还原、提高Co/Al₂O₃催化剂对费托合成反应的催化活性、降低甲烷选择性并提高C₅₊烃选择性。H₂-TPR表征结果表明,少量Ru或Pt助剂均能降低Co-ZrO₂/Al₂O₃催化剂中钴物种还原温度(Co₃O₄→CoO和CoO→Co⁰),提高催化剂的还原度,催化剂呈现出良好的CO加氢反应活性。此外,催化剂组分间浸渍次序对费托合成反应性能有重要影响,载体γ-Al₂O₃先浸渍Zr组分,可有效抑制难还原化合物形成;Co、Ru组分共浸渍加强了Co和Ru组分密切接触程度,更利于钴物种的还原;Co、Pt组分依次浸渍更利于活性组分的均匀分布,催化剂具有最佳的费托合成反应性能。     

CoAl2O4/Al2O3载体对钴基费托催化剂反应性能影响的研究

通过浸渍和高温焙烧,制得表面附着CoAl₂O₄微晶颗粒的改性Al₂O₃载体,并采用等体积浸渍法制备负载型Co基催化剂。结合 N₂物理吸附、XRD、H₂-TPR、XPS及H₂化学吸附等表征手段,研究改性载体及其负载钴基催化剂的织构特征;采用费托合成反应评价其催化性能。结果表明,Al₂O₃改性后,表面CoAl₂O₄的存在有效减少了载体与活性组分Co的相互作用,显著提高了催化剂的还原度和催化活性。载体的改性量在20%左右达到最佳值,继续增加,催化剂还原度和活性基本不再升高。载体改性促使催化剂CH₄选择性有所降低,C₅₊选择性略有提高。     

添加钒对Pd/Al2O3-TiO2 催化剂上醇醛催化氧化性能及表面特性的影响

采用浸渍法分别制备了Pd/Al₂O₃-TiO₂、V/Al₂O₃-TiO₂和不同钒含量的V-Pd/Al₂O₃-TiO₂催化剂,并对乙醇、乙醛的完全催化氧化性能进行了测试。结果表明,添加适量的钒组分(1%~3%)能够有效地提高催化剂的深度氧化活性。采用XRD、NH₃-TPD、N₂吸附等技术分析研究催化剂的表面特性与催化活性之间的关系,发现Pd/Al₂O₃-TiO₂催化剂添加适量钒组分后,调变了催化剂的表面酸性、比表面积和孔容,使得V组分和Pd组分与载体之间产生较强的相互作用,双金属组分的协同效应提高了催化剂对乙醇、乙醛的深度氧化活性。     

CuZn/Al2O3催化γ-戊内酯加氢制1,4-戊二醇

生物质利用是缓解能源及环境危机的有效途径。 本文利用共沉积法制备了一系列CuZn/Al₂O₃催化剂,通过电感耦合等离子光谱(ICP)、X射线粉末衍射(XRD)、透射电子显微镜(TEM)、二氧化碳程序升温脱附(CO₂-TPD)等表征技术对催化剂的结构及性质进行了表征。 重点讨论了还原温度对CuZn/Al₂O₃催化γ-戊内酯加氢反应催化性能的影响,研究发现还原温度显著影响催化剂的活性和选择性。 高温还原有利于γ-戊内酯加氢生成1,4-戊二醇,440 ℃还原的CuZn/Al₂O₃催化剂对1,4-戊二醇的选择性可高可达98%;而200 ℃还原的催化剂,在相似的转化率下1,4-戊二醇选择性仅为71%。 结合催化剂的结构分析,高温有利于ZnO的还原,促使催化剂表面生成新的活性位点,并改变了催化剂表面的酸碱性,促进了1,4-戊二醇的生成。     

活性金属不同浸渍顺序对Mo-Ni/Al2O3催化剂硫醚化反应性能的影响

针对硫醚化反应过程使用的Mo-Ni/Al₂O₃催化剂,考察了不同浸渍方法对其催化性能和表面结构性质的影响。结果表明,通过同步浸渍和分步浸渍方法制得Mo-Ni/Al₂O₃催化剂的活性顺序为：先浸渍Mo后浸渍Ni的催化剂（SI-mn）≈Ni和Mo共同浸渍的催化剂（MN）>先浸渍Ni后浸渍Mo的催化剂（SI-nm）。对于SI-mn催化剂,先负载Mo后减弱了二次浸渍的Ni金属与载体间的相互作用,有利于负载金属的活化,并在二次浸渍后焙烧过程显现出显著的电子效应,形成新的Mo-Ni前体物种,有利于在预硫化过程形成适宜硫醚化和二烯烃选择性加氢的活性中心相,促进硫醚化反应和二烯烃选择性加氢。对于共同浸渍的MN催化剂也有类似的性质,因而也具有较好的催化性能。     

不同载体Ni基负载型催化剂对甲烷部分氧化制合成气催化行为研究

采用浸渍法制备了单一载体(Al₂O₃、ZrO₂、CeO₂)和ZrO₂、CeO₂改性的Al₂O₃复合载体的Ni催化剂,考察了在甲烷部分氧化制备合成气反应中的催化性能。通过N₂-物理吸附、H₂程序升温还原、X射线衍射、NH₃程序升温脱附和程序升温氧化等技术对催化剂进行了表征。结果表明,在单一载体催化剂中,Ni/Al₂O₃具有较大的比表面积,其初始反应活性较高,但该催化剂表面易形成大量的积炭而快速失活。Ni/ZrO₂和Ni/CeO₂催化剂比表面积较小,活性金属Ni在其表面分散性差,催化剂具有较低的CH₄转化率。而CeO₂和ZrO₂改性的Al₂O₃复合载体催化剂,具有较大的比表面积,反应活性明显高于单一载体催化剂。CeO₂-Al₂O₃复合载体催化剂具有最高的反应活性和较好的反应稳定性。同时表明,含CeO₂催化剂反应后表面积炭较少,CeO₂的储放氧功能增强了催化剂对O₂的活化,提高催化剂活性的同时,可以抑制积炭的生成。     

等离子体技术对CO2甲烷化用Ni/SiO2催化剂的改性作用

采用浸渍法制备了Ni/SiO₂催化剂,应用等离子体技术对催化剂进行改性处理。以CO₂甲烷化为模型反应对催化剂进行活性评价,通过H₂程序升温还原(H₂-TPR)和CO₂程序升温脱附(CO₂-TPD)技术对催化剂进行表征。研究了等离子体技术强化处理对催化剂吸附性能和还原性能的影响。结果表明,与常规焙烧的催化剂相比,等离子体技术改性处理提高了催化剂活性组分的分散度,增加反应活性位并调变了活性位对吸附物种的吸附强度,改进了催化剂的还原性能,CO₂甲烷化反应活性和甲烷的时空产率显著提高。     

掺加Nd和K改性对Co3O4催化分解N2O活性的影响

用水热法和共沉淀法分别制备了Nd-Co₃O₄催化剂，催化分解N₂O。其中，水热法制备的Nd-Co₃O₄催化活性较高。在不同组成的Nd-Co₃O₄中，优化出了较高活性的0.01Nd-Co₃O₄催化剂，在其表面浸渍K₂CO₃溶液制备K改性催化剂（K/Nd-Co₃O₄）。用X射线衍射（XRD）、N₂物理吸附、扫描电镜（SEM）、X射线光电子谱（XPS）、程序升温还原（H₂-TPR）、O₂程序升温脱附（O₂-TPD）等技术表征催化剂结构。结果表明，Nd-Co₃O₄和K改性催化剂均为尖晶石结构；K改性弱化了催化剂表面Co-O键，有利于表面氧的脱除，提高了催化剂活性。有氧有水气氛350 ℃连续反应40 h，K/Nd-Co₃O₄催化剂上的N₂O分解率超过90%，稳定性较好。     

CoMo/ZrO2-Al2O3催化剂的制备及其加氢脱氧性能

以ZrOCl₂·6H₂O和Al₂(SO₄)₃为原料,采用超声波共沉淀法制得一系列不同ZrO₂质量分数的ZrO₂- Al₂O₃复合氧化物载体;并以该复合氧化物为载体,采用等体积浸渍法制得Co和Mo质量分数分别为6.0%和16.0%的CoMo/ZrO₂-Al₂O₃催化剂。BET、XRD、H₂-TPR和NH₃-TPD等表征结果表明,ZrO₂-Al₂O₃复合氧化物载体具有较高的比表面积与较大的孔容、孔径,随着复合载体中ZrO₂质量分数的增加,复合载体比表面积逐渐减小。ZrO₂-Al₂O₃复合载体能高度分散活性组分,钴钼负载量接近其在载体上的单层分散阈值。相比于CoMo/Al₂O₃,CoMo/ZrO₂-Al₂O₃催化剂具有较高的还原性能和较多的表面酸性活性中心,由此导致其在苯酚加氢脱氧(HDO)反应中,具有较高的加氢脱氧活性和苯选择性。
     

柠檬酸添加方式对Mo-Ni-P/Al_2O_3催化剂加氢活性的影响

以Mo、Ni为活性组分,Al_2O_3为载体,采用不同柠檬酸添加方法制备了Mo-Ni-P/Al_2O_3催化剂.通过氢气程序升温还原(H2-TPR)、X射线衍射(XRD),透射扫描电镜(TEM)、XPS等表征方法研究催化剂的物化性质.结果表明:催化剂经柠檬酸的后处理,改善了载体氧化铝表面羟基基团的分布,促使Mo物种以八面体配位多核聚钼酸的形态存在,有效地减弱了载体与活性金属之间的强相互作用,提高了Mo物种的分散度与硫化度,使得催化剂形成更多"Mo-Ni-S"加氢活性相,提高了催化剂的加氢活性.与其他处理方法相比,柠檬酸后处理的催化剂对VGO具有更高的加氢脱硫、脱氮与芳烃饱和性能.     

M/Al2O3-CeO2（M=Pt-Ru，Ru，Pt）催化剂在甲胺催化湿式氧化中的活性与选择性

采用浸渍法制备了M/Al₂O₃-CeO₂（M=Pt-Ru,Ru,Pt）催化剂,并将其用于甲胺的催化湿式氧化反应（CWAO）.结果表明,Pt-Ru/Al₂O₃-CeO₂具有最佳活性和选择性.运用程序升温还原、X射线光电子能谱、X射线衍射、透射电子显微镜、N₂吸附和CO化学吸附等技术对催化剂的物化性质进行了表征.Pt组分的引入可有效提高双金属催化剂活性组分的分散度,从而明显提高了其催化性能.升降温过程中总有机碳（TOC）转化率与N₂选择性迟滞效应表明,甲胺CWAO遵循化学吸附-脱附机理.     

TiO2-Al2O3载体的制备方法对其负载的磷化镍催化剂加氢脱氮反应性能的影响

采用共沉淀法和原位溶胶-凝胶法制备了TiO₂-Al₂O₃复合载体,其负载的磷化镍催化剂采用等体积浸渍法和H₂原位还原法制备. 通过N₂吸附（BET）、X射线衍射（XRD）、透射电镜（TEM）、程序升温还原（TPR）,X射线光电子能谱（XPS）和等离子体发射光谱（ICP-AES）表征技术对催化剂进行了表征,并通过喹啉的加氢脱氮反应评价了催化剂的加氢脱氮性能. 结果表明,原位溶胶-凝胶法制成的复合载体基本保留了原有的γ-Al₂O₃的孔特征,具有较大的比表面积和较宽的孔分布,TiO₂主要以表面富集的形式分散在管状的γ-Al₂O₃表面,其负载的磷化镍催化剂还原后所形成的活性相为Ni₂P和Ni₁₂P₅;而共沉淀法制成的复合载体比表面积较小,孔径分布更加集中,TiO₂趋于在块状的Al₂O₃表面均匀分散,其负载的磷化镍催化剂具有更好的可还原性,还原后所形成的活性相为Ni₂P. 不同的载体制备方法和不同的钛铝比对催化剂加氢脱氮性能影响较大,当n（Ti）/n（Al）=1/8时,共沉淀法载体负载的催化剂表现出最佳的加氢脱氮性能,在340 ℃,3 MPa,氢油体积比500,液时空速3 h^-1的反应条件下,喹啉的脱氮率可以达到91.3%.     

Dependence of the catalytic activity of Ag/Al2O3 on the silver concentration in the selective reduction of NOx with n-hexane in the presence of H2

The activity of 0.25–5% Ag/Al₂O₃ catalysts in the selective catalytic reduction of nitrogen oxides with n-hexane under the conditions of promotion with a small amount of H₂ was studied. It was found that, upon the introduction of ∼1000 ppm of H₂ into the reaction mixture, the Ag/Al₂O₃ samples containing 1–2% Ag exhibited optimum activity and selectivity. It was established that, in the presence of 1000 ppm of H₂, the rate of the selective catalytic reduction of NO _x was higher by a factor of 10–13, and the onset temperature of the reaction was lower by approximately 100°C. It was found by X-ray photoelectron spectroscopy, temperature-programmed reduction, and UV spectroscopy that the high activity of 1–2% Ag/Al₂O₃ catalysts was due to the presence of small Ag _n ^δ+ and Ag _m ⁰ clusters on their surface. A decrease in the concentration of Ag below the optimum value resulted in the predominance of an inactive ionic form on the catalyst surfaces. As the concentration of Ag was increased (>2%), large particles of Ag₂O and Ag⁰, which facilitate the oxidation of n-C₆H₁₄, were formed to lead to a decrease in selectivity and in the degree of reduction of nitrogen oxides.     

Effect of Mo content in MoO3/g-Al2O3 on the catalytic activity for transesterification of dimethyl oxalate with phenol

The influence of molybdenum content on the catalytic performance in the transesterification of dimethyl oxalate (DMO) with phenol to methyl phenyl oxalate (MPO) and diphenyl oxalate (DPO) was investigated. The results indicated that the MoO₃/Al₂O₃ catalyst with 14 wt% Mo content gave maximal DPO yield with 6.1% and 75.1% DMO conversion. The component, structure and phase of MoO₃/Al₂O₃ catalysts were characterized by means of X-ray diffraction (XRD), BET specific surface area, temperature-programmed desorption of ammonia (NH₃-TPD), and FTIR analysis of adsorbed pyridine. This revised version was published online in June 2006 with corrections to the Cover Date.     

Catalytic Performance of Re/Ga2O3/WO3/ZrO2 Catalyst for n-Hexane Isomerization

A series of Re/Ga₂O₃/WO₃/ZrO₂ catalysts were prepared by the impregnation method. The crystalline structure, redox, and acid site distribution of the catalysts were characterized by X-ray powder diffraction, temperature-programmed reduction of H₂, and temperature-programmed desorption of NH₃. Their catalytic performance for n-hexane isomerization was studied. The results showed that the addition of Re greatly affected the redox properties and the acid site distribution of the catalysts. Owing to the presence of Re, n-hexane isomerization was catalyzed by metal and acid sites, and thus the conversion of n-hexane and the selectivity for 2,2-dimethylbutane were significantly increased. Under the conditions of 195 °C, 1.0 MPa, LHSV = 1.0 h⁻¹, and n(H₂)/n(C₆) = 2.0, the conversion of n-hexane over 1.0%Re/1.0%Ga₂O₃/WO₃/ZrO₂ is 84.8%, and the selectivities for 2,2-dimethylbutane, i-hexane, and cracking products (C_5-) are 20%, 97.7%, and 2.1%, respectively. The catalyst is stable during 150 h operation.     

Al含量对Pt-SO2-4 /ZrO2-Al2O3固体超强酸催化

通过向SO^2-₄ /ZrO₂催化剂中同时引入适量的Pt和Al₂O₃, 制备出了具有较高催化性能和稳定性的Pt-SO^2-₄ /ZrO₂-Al₂O₃型固体超强酸催化剂. 以正戊烷异构化反应为探针, 考察了Al含量对催化剂性能的影响; 并采用X射线衍射(XRD)、比表面积测定(BET)、红外(IR)光谱、程序升温还原(TPR)、热重-差热分析(TG-DTA)和氨-程序升温脱附(NH₃-TPD)手段对催化剂进行了表征. 结果表明, Al能够提高ZrO₂的晶化温度, 抑制硫的分解, 增加催化剂的比表面积, 增强硫氧键的结合, 提高催化剂的还原性能, 增加催化剂的酸强度和酸总量. 当Al₂O₃含量(质量分数, w)为5.0%时, Pt-SO^2-₄ /ZrO₂-Al₂O₃固体超强酸催化剂的催化活性最好, 在100 h内异戊烷收率可稳定在52.0%以上, 选择性在98.2%以上.     

乙烷氧化脱氢用Ni/Al2O3催化剂中活性镍物种前驱体（英文）

Ni/Al2O3 catalysts for oxidative dehydrogenation(ODH) of ethane were prepared by impregnation of Al2O3 with nickel acetate or nickel nitrate,and by mechanical mixing of NiO and Al2O3.The Ni-based catalysts were characterized by N2 adsorption-desorption,X-ray diffraction,diffuse reflectance UV-visible diffuse reflectance spectroscopy,and temperature-programmed reduction of hydrogen.The results showed that formation of crystalline NiO particles with a size of < 8 nm and/or non-stoichiometric NiO species in the Ni/Al2O3 catalysts led to more active species in ODH of ethane under the investigated reaction conditions.In contrast,tetrahedral Ni species present in the catalysts led to higher selectivity for ethene.Formation of large crystalline NiO particles(22-32 nm) over Ni/Al2O3 catalysts decreased the selectivity for ethene.     

Plasma treatment of Ni and Pt catalysts for partial oxidation of methane

Summary In this work DBD (dielectric barrier discharge) plasma treatments of 10%Ni/Al₂O₃and 1%Pt/Al₂O₃catalysts have been conducted to study the principles of plasma treatment of supported catalysts. It was found that 10%Ni/Al₂O₃and 1%Pt/Al₂O₃catalysts treated by plasma exhibit a higher catalytic activity and a better stability than the catalysts prepared without plasma treatment. Methane conversion over the plasma treated catalyst is 3-5% higher than on untreated catalysts. The metal species dispersion also increased after plasma treatment, which leads to improvement of the interaction between active species and supports, the catalytic activities and the resistance to carbon deposition.</o:p>