Morphology and thermal properties of polyhedral oligomeric silsesquioxane/polybutadiene nanocomposites prepared by anionic polymerization

The morphology and thermal properties of Allylisobutyl Polyhedral Oligomeric Silsesquioxane (POSS)/Polybutadiene (PB) nanocomposites prepared through anionic polymerization technique were investigated by X-ray diffraction (XRD), scanning electron microscopy (SEM), transmission electron microscopy (TEM), differential scanning calorimetry (DSC) and thermogravimetric analysis (TGA). The results of XRD, SEM and TEM showed that the aggregation of POSS in PB matrix occurred obviously, forming crystalline domains and the size of POSS particles increased with increasing POSS content. The DSC and TGA results indicated that the glass transition temperature (T _g) of the nanocomposites was significantly increased and the maximum degradation temperature (T _dmax) of nanocomposites was slightly increased compared with pure PB, implying an increase in thermal stability.     

聚乳酸/氧化锌柱撑皂石纳米复合材料制备与性能及结构表征

通过微波水解法制备了ZnO柱撑皂石,并以其为加工助剂制备了聚乳酸(PLA)/ZnO柱撑皂石纳米复合材料.通过X射线衍射(XRD)、扫描电子显微镜(SEM)、透射电子显微镜(TEM)、对ZnO柱撑皂石及PLA/ZnO柱撑皂石纳米复合材料的结构进行了表征,并对其力学性能和热稳定性能进行了测试.微观结构分析表明,ZnO柱撑皂石呈现剥离状,并均匀分散在PLA基质中.力学性能研究表明0.3%ZnO柱撑皂石的加入有助于改善PLA复合材料的断裂伸长率.SEM分析表明PLA复合材料的断面发生明显改变,表现良好韧性;DSC结果显示纳米ZnO柱撑皂石可以降低复合材料的玻璃化转变温度、结晶温度,有助于提高PLA复合材料的结晶度,与XRD分析相吻合;热重分析表明ZnO柱撑皂石可以提高PLA复合材料的热稳定性.测试结果表明,ZnO柱撑皂石在PLA基质中起到了异相成核的作用,促进了PLA基质的结晶.     

Preparation and characterization of novel polyimide/functionalized ZnO bionanocomposite for gas separation and study of their antibacterial activity

In the present investigation novel Polyimide/functionalized ZnO (PI/ZnO) bionanocomposites containing amino acid (Methionine) and benzimidazole pendent groups with different amounts of modified ZnO nanoparticles (ZnO NPs) were successfully prepared through ultrasonic irradiation technique. Due to the high surface energy and tendency for agglomeration, the surface ZnO NPs was modified by a coupling agent as 3- methacryloxypropyl-trimethoxysilane (MPS) to form MPS-ZnO nanoparticles. The ultrasonic irradiation effectively changes the rheology and the glass transition temperature and the crystallinity of the composite polymer. PI/ZnO nanocomposites were characterized by Fourier transform infrared spectroscopy (FTIR), X-ray diffraction (XRD), scanning electron microscopy (SEM) and transmission electron microscope (TEM). TEM analysis showed that the modified ZnO nanoparticles were homogeneously dispersed in polymer matrix. The TGA results of PI/ZnO nanocomposites showed that the thermal stability is obviously improved the presence of MPS-ZnO NPs in comparison with the pure PI and that this increase is higher when the NP content increases. The permeabilities of pure H₂, CH₄, O₂, and N₂ gases through prepared membranes were determined at room temperature (25 °C) and 20 bar feed pressure. The membranes having 20% ZnO showed higher values of H₂ permeability, and H₂/CH₄ and H₂/N₂ ideal selectivities (the ratio of pair gas permeabilities) compared with other membranes. The antibacterial activity of bionanocomposite films was tested against gram-positive bacteria (Staphylococcus aureus and Bacillus subtilis) and gram-negative bacteria (Escherichia coli and Pseudomonas aeruginosa). Further, it was observed that antibacterial activity of the resulting hybrid biofilms showed somewhat higher for gram-positive bacteria compared to gram-negative bacteria.     

Effect of polyaniline as a surface modifier of TiO2 nanoparticles on the properties of polyvinyl chloride/TiO2 nanocomposites

Surface of TiO2 nanoparticles was modified with the in situ chemical oxidative polymerization of aniline. Polyaniline modified TiO2 nanoparticles (PANI-TiO2 ) were characterized with the FT-IR, XRD, SEM and TEM techniques. Results confirmed that PANI was grafted successfully on the surface of TiO2 nanoparticles, therefore agglomeration of nanoparticles decreased dramatically. Polyvinyl chloride nanocomposites filled with 1 wt% 5 wt% of PANI-TiO2 and TiO2 nanoparticles were prepared via the solution blending method. PVC nanocomposites were analyzed with FT-IR, XRD, SEM, TG/DTA, DSC and tensile test techniques. Effect of PANI as surface modifier of nanoparticles was discussed according to the final properties of PVC nanocomposites. Results demonstrated that deposition of PANI on the surface of TiO2 nanoparticles improved the interfacial adhesion between the constituents of nanocomposites, which resulted in better dispersion of nanoparticles in the PVC matrix. Also PVC/PANI-TiO2 nanocomposites showed higher thermal resistance, tensile strength and Young’s modulus compared to those of unfilled PVC and PVC/TiO2 nanocomposites.     

Investigation of thermally stimulated charge relaxation mechanism in SiO<Subscript>2</Subscript> filled polycarbonate nanocomposites

The thermally stimulated charge relaxation properties of polycarbonate (PC) filled with SiO₂ nanofiller were studied by means of thermally stimulated discharge current (TSDC). The nanocomposite samples were further characterized by UV–vis spectroscopy, scanning electron microscopy, energy dispersive X-ray spectra, and differential scanning calorimetry (DSC) techniques to investigate the dispersion of nanofillers in polymer matrix and glass transition temperature. All pristine and nanocomposites samples of thickness about 25 μm were prepared using solution mixing method. The suitable weight percentage of SiO₂ nanofillers has been chosen to prevent the nonuniform dispersion. TSDC measurement of PC (Pristine) and PC+ (7% SiO₂) shows the single peak, while TSDC characteristic of other nanocomposites are showing two peaks. The higher temperature TSDC peak of pristine and nanocomposites samples is originated due to the charge relaxation from shallower and deeper trapping sites, however, low temperature peak is caused by dipolar relaxation of charge carriers. Since the position of higher temperature TSDC peak is generally an analysis of glass transition temperature of polymer/polymer nanocomposites. The authors have observed that the temperature of this peak is almost same as the T _g measured by DSC with 0 to ±5% variation. This article presents the deeper understanding of charge relaxation mechanism caused by SiO₂ nanofillers in polycarbonate.     

Effects of organophilic montmorillonite on hydrogen bonding, free volume and glass transition temperature of epoxy resin/polyurethane interpenetrating polymer networks

Epoxy resin nanocomposites containing organophilic montmorillonite (oM) and polyurethane were prepared by adding oM to interpenetrating polymer networks (IPNs) of epoxy resin and polyurethane (EP/PU). The dispersion degree of oM in EP/PU matrix was characterized by X-ray diffraction (XRD) and transmission electron microscopy (TEM). Fourier transform infrared spectrometry (FT-IR) showed that strong interactions existed between oM and EP/PU matrix, and oM had some effect on hydrogen bonding of these EP/PU IPNs nanocomposites. Positron annihilation spectroscopy (PALS) and differential scanning calorimetry (DSC) measurements were used to investigate the effect of oM and PU contents on free volume and glass transition temperature (T_g) of these nanocomposites. The PALS and DSC results clearly showed that the presence of oM led to a decrease in the total fractional free volume, which was consistent with increasing T_g upon addition of oM, ascribed to increasing hydrogen bonding in interfacial regions of oM and EP/PU matrix and enhancing the miscibility between EP phase and PU phase. In addition, with increasing PU content, the total fractional free volume increased, corresponding to decreasing T_g.     

Microcalorimetric study of the effect of manganese on the growth and metabolism in a heterogeneously expressing manganese-dependent superoxide dismutase (Mn-SOD) strain

DSC, SEM–EDS, XRD and high-temperature XRD analysis was used to study thermal and crystallization behaviour of yttrium aluminate glasses prepared in the form of microspheres. The glasses YA-E (eutectic composition from the pseudo-binary system Al₂O₃–Y₃Al₅O₁₂) and YA-G (a composition identical to the stoichiometric Y₃Al₅O₁₂ (YAG) phase) were prepared by combination of the Pechini method with flame synthesis. The resulting microspheres were largely amorphous, but contained traces of yttrium–aluminium garnet as the main crystalline phase embedded in the yttrium aluminate glass matrix. Crystallization of the YAG phase was observed as the dominant exothermic process on DSC curves. From the DSC records, the basic thermal characteristics of the matrix glass, i.e. T _g (glass transition temperature), T _x (onset of crystallization peak temperature), T _f (temperature of the inflection point of the crystallization peak) and T _p (maximum of crystallization peak temperature), were determined. HT XRD experiments in the temperature interval 750–1200 °C and isothermal HT XRD experiments at 932, 998 and 1200 °C with 6-h holding time were also performed. Crystallization experiments at lower temperatures 932 °C (YA-E) and 915 °C (YA-G) were conducted to study phase development in a low-temperature region. Crystallization experiments at higher temperatures (1000, 1300 and 1500 °C) with maximum holding time of 6 h were performed to study crystallization of α-Al₂O₃ in the eutectic system. The SEM and SEM–EDS examination of polished cross sections of crystallized microspheres revealed slow volume crystallization of the YAG phase in the AY-E glass. Eventually, polycrystalline microspheres with fine-grained microstructure were prepared after 6-h treatment at 1500 °C.     

Synthesis and characterization of poly(ɛ-caprolactone)/Fe3o4 nanocomposites by in situ polymerization

A series of magnetic nanocomposites based on poly(?-caprolactone) (PCL) and Fe₃O₄ nanoparticles were prepared using a facile in situ polymerization method. The chemical structures of the PCL/Fe₃O₄ nanocomposites were characterized by Fourier transform infrared (FTIR) spectroscopy. Results of wide-angle X-ray diffraction (WAXD) showed that the incorporation of the Fe₃O₄ nanoparticles did not affect the crystallization structure of the PCL. Both scanning electron microscopy (SEM) and transmission electron microscopy (TEM) were used to characterize the morphology and dispersion of the Fe₃O₄ nanoparticles within the as-synthesized nanocomposites. Results of differential scanning calorimetry (DSC) and polarizing optical microscopy (POM) showed that the crystallization temperature was raised and the spherulites size decreased by the presence of Fe₃O₄ nanoparticles in the nanocomposites due to the heterogeneous nucleation effect. The thermal stability of the PCL was depressed by incorporation of Fe₃O₄ nanoparticles from thermogravimetric analysis (TGA). The superparamagnetic behavior of the PCL/Fe₃O₄ nanocomposites was testified by the superconducting quantum interference device (SQUID) magnetometer analysis. The obtained biodegradable nanocomposites will have a great potential in magnetic resonance imaging contrast and targeted drug delivery.     

Characterization of polypropylene/layered silicate nanocomposites prepared by single-step method

The extent of organo-modified clay (C93A) platelets dispersion in polymer matrix and crystallization and melting behavior of iPP-based nanocomposites prepared by a single-step melt-mixing method were investigated by wide-angle X-ray diffraction (WAXD), transmission (TEM), scanning electron microscopy (SEM), and differential scanning calorimetry (DSC). WAXD patterns revealed exfoliated structure of nanocomposites containing 1 wt% clay, and mixed intercalated/exfoliated structure at higher concentration of nanoclay. The isothermal crystallization proceeds faster in the matrix polymer (iPP/PP-g-MA) than in nanocomposite samples. The results obtained for T _m ^o suggest that the presence of nanoclay has induced a perfection of the formed crystals. The presence of C93A particles in PP leads to increase in crystallization peak temperature implying nucleating ability of clay particles, which was more pronounced in exfoliated than in mixed intercalated/exfoliated system.     

Toughening of ethylene-propylene random copolymer/clay nanocomposites: Comparison of different compatibilizers

Ethylene/propylene-random-copolymer(PPR)/clay nanocomposites were prepared by two-stage melt blending. Four types of compatibilizers,including an ethylene-octene copolymer grafted maleic anhydride(POE-g-MA) and three maleic-anhydride-grafted polypropylenes(PP-g-MA) with different melt flow indexes(MFI),were used to improve the dispersion of organic clay in matrix.On the other hand,the effects of organic montmorillonite(OMMT) content on the nanocomposite structure in terms of clay dispersion in PPR matrix,thermal behavior and tensile properties were also studied. The X-ray diffraction(XRD) and transmission electron microscopy(TEM) results show that the organic clay layers are mainly intercalated and partially exfoliated in the nanocomposites.Moreover,a PP-g-MA compatibilizer(compatibilizer B) having high MFI can greatly increase the interlayer spacing of the clay as compared with other compatibilizers.With the introduction of compatibilizer D(POE-g-MA),most of the clays are dispersed into the POE phase,and the shape of the dispersed OMMT appears elliptic,which differs from the strip of PP-g-MA.Compared with virgin PPR,the Young’s modulus of the nanocomposite evidently increases when a compatibilizer C(PP-g-MA) with medium MFI is used.For the nanocomposites with compatibilizer B and C,their crystallinities(X_c) increase as compared with that of the virgin PPR. Furthermore,the increase of OMMT loadings presents little effect on the melt temperature(T_m) of the PPR/OMMT nanocomposites,and slight effect on their crystallization temperature(T_c).Only compatibilizer B can lead to a marked increases in crystallinity and T_c of the nanocomposite when the OMMT content is 2 wt%.     

Nonisothermal crystallization and morphology of poly(butylene succinate)/layered double hydroxide nanocomposites

Biodegradable poly(butylene succinate) (PBS) and layered double hydroxide (LDH) nanocomposites were prepared via melt blending in a twin-screw extruder. The morphology and dispersion of LDH nanoparticles within PBS matrix were characterized by transmission electron microscopy (TEM), which showed that LDH nanoparticles were found to be well distributed at the nanometer level. The nonisothermal crystallization behavior of nanocomposites was extensively studied using differential scanning calorimetry (DSC) technique at various cooling rates. The crystallization rate of PBS was accelerated by the addition of LDH due to its heterogeneous nucleation effect; however, the crystallization mechanism and crystal structure of PBS remained almost unchanged. In kinetics analysis of nonisothermal crystallization, the Ozawa approach failed to describe the crystallization behavior of PBS/LDH nanocomposites, whereas both the modified Avrami model and the Mo method well represented the crystallization behavior of nanocomposites. The effective activation energy was estimated as a function of the relative degree of crystallinity using the isoconversional analysis. The subsequent melting behavior of PBS and PBS/LDH nanocomposites was observed to be dependent on the cooling rate. The POM showed that the small and less perfect crystals were formed in nanocomposites.     

Influence of calcination temperature on structural and magnetic properties of nanocomposites formed by Co-ferrite dispersed in sol-gel silica matrix using tetrakis(2-hydroxyethyl) orthosilicate as precursor

Effects of calcination temperatures varying from 400 to 1000°C on structural and magnetic properties of nanocomposites formed by Co-ferrite dispersed in the sol-gel silica matrix using tetrakis(2-hydroxyethyl) orthosilicate (THEOS) as water-soluble silica precursor have been investigated. Studies carried out using XRD, FT-IR, TEM, STA (TG-DTG-DTA) and VSM techniques. Results indicated that magnetic properties of samples such as superparamagnetism and ferromagnetism showed great dependence on the variation of the crystallinity and particle size caused by the calcination temperature. The crystallization, saturation magnetization M_s and remenant magnetization M_r increased as the calcination temperature increased. But the variation of coercivity H_c was not in accordance with that of M_s and M_r, indicating that H_c is not determined only by the crystallinity and size of CoFe₂O₄ nanoparticles. TEM images showed spherical nanoparticles dispersed in the silica network with sizes of 10-30 nm. Results showed that the well-established silica network provided nucleation locations for CoFe₂O₄ nanoparticles to confinement the coarsening and aggregation of nanoparticles. THEOS as silica matrix network provides an ideal nucleation environment to disperse CoFe₂O₄ nanoparticles and thus to confine them to aggregate and coarsen. By using THEOS as water-soluble silica precursor over the currently used TEOS and TMOS, the organic solvents are not needed owing to the complete solubility of THEOS in water. Synthesized nanocomposites with adjustable particle sizes and controllable magnetic properties make the applicability of Co-ferrite even more versatile.     

The glass transition

This work deals with a comparison of data obtained from differential scanning calorimetry (DSC) and thermally stimulated depolarization current (TSDC) investigations. Measurements were performed on various poly(ethylene terephthalate) films: a wholly amorphous, a thermally crystallized and drawn samples. For each specimen, the TSDC complex spectra, resolved into elementary ones, led to the determination of the classical compensation temperature (T _c ). The glass transition temperature (T _g) and the fictive equilibrium temperature (T _f) were determined by means of DSC. It appears thatT _c is different fromT _g and very close toT _f.     

Structural and thermal properties of polysulfone-ZnO nanocomposites

Polymer nanocomposite thin film of polysulfone with different concentration of ZnO was prepared by solution grown technique. This paper presents a study on the structural and thermal properties of ZnO filled Polysulfone (PSF) nanocomposites. The structural morphology of the resulting nanocomposites was investigated by X-ray diffraction (XRD), Scanning electron microcopy (SEM), and Atomic force microscopy (AFM). Thermal properties of PSF nanocomposites samples were investigated by Differential thermal analysis, Thermal gravimetric, and Differential thermal gravimetric. Structural result shows that the ZnO nanofiller with different mass% in polymer matrix cause the significant variation of lattice spacing, crystallite size, and percentage crystallinity. XRD result shows that the amorphous behavior of PSF (Pristine) is increasing with incorporation of ZnO nanoparticle in PSF matrix. The SEM and AFM images show the change in structural morphology of PSF due to incorporation of ZnO nanoparticles. The thermal analysis result shows that the significant thermal degradation of polysulfone nanocomposites due to catalytic behavior of ZnO nanoparticles.     

Properties of biodegradable poly(butylene carbonate) (PBC) composites with fumed silica nanoparticles

Biodegradable poly(butylene carbonate)/fumed silica (PBC/SiO₂) nanocomposites were prepared by melt compounding. The PBC/SiO₂ nanocomposites exhibited a good dispersion of aggregates of SiO₂ in the PBC matrix, and an improvement in mechanical properties. Nanoparticles affect, also, the thermal properties of PBC and especially the crystallization rate, which in all nanocomposites is faster than that of pure PBC. Due to ongoing crystallization and the crystal perfection during heating process, the melting peak of PBC shifted to higher temperature when heating from amorphous state with decreasing heating rate. With increasing cooling rate, the non-isothermal crystallization exotherms became wider and shifted to lower temperature. At a given cooling rate, the crystallization peak temperature of neat PBC was lower than that of its nanocomposite. Non-isothermal crystallization kinetic procedure, the method of Ozawa, was applied to the first deconvoluted DSC peak only by processing the data related to DSC peak. The average value of Ozawa exponent m of pure PBC is 3.04, while the one of its nanocomposite is about 2.98. Moreover, the thermal stability of the nanocomposites was increased. The T _d enhancement of the nanocomposite was remarkable.     

The disorderly exfoliated LDHs/PMMA nanocomposites synthesized by in situ bulk polymerization: The effects of LDH-U on thermal and mechanical properties

The disorderly exfoliated layered double hydroxides/poly(methyl methacrylate) (LDHs/PMMA) nanocomposites were obtained in a two-stage process by the in situ bulk polymerization of methyl methacrylate (MMA) in the presence of 10-undecenoate intercalated LDH (LDH-U). The dispersed behavior of the LDH-U in the PMMA matrix was identified by using X-ray diffraction (XRD), transmission electron microscopy (TEM), and UV/visible transmission spectroscopy. All these nanocomposites showed significantly enhancement of glass transition temperature (T_g) and the decomposition temperatures compared to pristine PMMA, as identified in differential scanning calorimetry (DSC) and thermogravimetric (TGA) analysis. The tensile modulus of these nanocomposites was also enhanced by incorporating the LDH-U into the PMMA matrix and increased as the amount of LDH-U increased. According to the analytical method of Ozawa-Flynn, the degradation activation energies of these nanocomposites are higher than that of pristine PMMA.     

Effect of nanoclay and barium sulfate nanoparticles on the thermal and morphological properties of polyvinylidene fluoride nanocomposites

The thermal, morphological and optical studies of BaSO₄ and MMT (nanoclay) embedded in PVDF were investigated. Nanocomposites samples of PVDF–BaSO₄–MMT were prepared by varying the loadings (1–4 mass%) in case of BaSO₄ and MMT nanomaterials, respectively. Polyvinylidene fluoride–barium sulfate-montmorillonite (PVDF–BaSO₄–MMT) nanocomposites were prepared by solvent-mixing technique. Nanoparticles were synthesized by in situ deposition technique with the help of nonionic polymeric surfactant, and the particle size of nanoparticles was recognized by scanning electron microscopy (SEM) analysis which confirms that the particle has diameter of 80–90 nm. As prepared, nanocomposites films (thickness, 25 μm) were characterized by Fourier transform infrared microscopy (FTIR), SEM and electron diffraction spectroscopy (EDS). FTIR shows that all the chemical constituents were present in the nanocomposites, whereas SEM analysis suggested that the nanofillers dispersed well in polymer matrix and EDS showed the elemental composition of nanocomposite samples. Thermal properties of nanocomposites were studied by using TG/DTA/DTG. TG/DTA studies showed decomposition temperature of pure PVDF is 473.5 °C. The decomposition temperature (T _d) of nanocomposites was increased by 93 °C in case of nanocomposites with addition of both BaSO₄ and MMT nanomaterials. The difference in the thermal degradation temperature was found to be 1.2% higher in case of addition of BaSO₄ nanoparticle as compared to nanoclay. The obtained transparent nanocomposite films were characterized by using UV–Vis spectrophotometer which shows that transparencies of nanocomposites are maintained in visible region, the intensity of absorption band in UV region is increased with the addition of BaSO₄ nanoparticles, while in case of addition of nanoclay the UV region does not show drastic changes. Addition of both nanoparticle and nanoclay shows higher absorption in comparison with the individual samples. But further, doubling the amount of nanoparticle and nanoclay shows decrease in UV absorption. Overall, the results of thermal studies show that the incorporation of BaSO₄ and MMT could significantly improve the thermal properties of nanocomposites.     

Synthesis, characterization and thermal properties of novel PMDA-PAPD/silica hybrid network polymers

Novel PMDA-PAPD/silica hybrid polymers were synthesized by the sol-gel process. Fourier transform infrared spectroscopy and ²⁹Si nuclear magnetic resonance spectroscopy were used to characterize the structure of the hybrids, (condensed siloxane bonds designated as Q¹, Q², Q³, Q⁴, wth 3-aminopropyltriethoxysilane having mono-, di-, tri-, tetra-substituted siloxane bonds is designated as T¹, T² and T³). The results revealed that Q³, Q⁴ and T³ are the major microstructure elements in forming a network structure. The surface morphology, particle size, crystallinity and the thermal stability of the hybrids were investigated using Scanning electron microscopy (SEM), Transmission Electron Microscopy (TEM), X-ray diffraction (XRD), Thermogravimetric analysis (TGA) and Differential Scanning Calorimetry (DSC). SEM and TEM revealed that the hybrids were nanocomposites. The XRD indicated that covalent bonding (Si-O-Si) between the organic and inorganic components enhanced miscibility. DSC and TGA results showed that these hybrid materials had excellent thermal stability. The heat capacities of some materials were reported for the temperature range 273 K and 363 K as no thermal anomaly was found in this temperature range.     

Intercalated poly(vinylidene fluoride)/clay nanocomposites: Structure and properties

The preparation and characterization of melt‐intercalated poly(vinylidene fluoride) (PVDF)/clay nanocomposites are reported. Organophilic clay (clay treated with dimethyl dihydrogenated tallow quaternary ammonium chloride) was used for the nanocomposite preparation. The composites were characterized with X‐ray diffraction (XRD), differential scanning calorimetry (DSC), and dynamic mechanical analysis (DMA). XRD results indicated the intercalation of the polymer in the interlayer spacing. The incorporation of clay in PVDF resulted in the β form of PVDF. DSC nonisothermal curves showed an increase in the melting and crystallization temperatures along with a decrease in crystallinity. Isothermal crystallization studies show an enhanced rate of crystallization with the addition of clay. DMA indicated significant improvements in the storage modulus over a temperature range of ?100 to 150 °C. © 2002 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 41: 31–38, 2003     

Morphological structures of poly(vinylidene fluoride)/montmorillonite nanocomposites

Poly(vinylidene fluoride) (PVDF)/montmorillonite (MMT) nanocomposites were prepared by melt blen- ding a kind of organically modified montmorillonite with PVDF. The morphological structures of the nanocomposites were studied using X-ray diffraction (XRD), transmission electron microscopy (TEM), Fourier transform infrared (FTIR) spectroscopy, and differential scanning calorimetry (DSC). The re- sults indicate that organically modified montmorillonites are in the form of intercalation, exfoliation, and fragments in the PVDF matrix. For the composites, the (001) peak position of MMT was found to shift to a lower angle in XRD patterns, and some MMT fragments could be observed under TEM. MMT loading was favorable to producing the piezoelectric β phase in the PVDF matrix and caused internal stress in α crystals. At the same time, the crystallinity and spherulite size of PVDF decreased with the MMT content. MMT induced β phase is stable even at high temperatures (160℃). For these changes in morphological structures, some possible explanations were proposed based on the experimental re- sults.