Crystal growth, structural characterization and magnetic properties of Ca3CuRhO6, Ca3Co1.34Rh0.66O6 and Ca3FeRhO6

Single crystals of Ca₃CuRhO₆, Ca₃Co_1.34Rh_0.66O₆ and Ca₃FeRhO₆ were synthesized by high temperature flux growth in molten K₂CO₃ and structurally characterized by single crystal X-ray diffraction. While Ca₃Co_1.34Rh_0.66O₆ and Ca₃FeRhO₆ crystallize with trigonal (rhombohedral) symmetry in the space group , Z=6: Ca₃Co_1.34Rh_0.66O₆a=9.161(1) Å, c=10.601(2) Å; Ca₃FeRhO₆a=9.1884(3) Å, c=10.7750(4) Å; Ca₃CuRhO₆ adopts a monoclinic distortion of the K₄CdCl₆ structure in the space group C2/c, Z=4: a=9.004(2) Å, b=9.218(2) Å, c=6.453(1) Å, β=91.672(5). All crystals of Ca₃CuRhO₆ examined were twinned by pseudo-merohedry. Ca₃CuRhO₆, Ca₃Co_1.34Rh_0.66O₆, and Ca₃FeRhO₆ are structurally related and contain infinite one-dimensional chains of alternating face-sharing RhO₆ octahedra and MO₆ trigonal prisms. In the monoclinic modification, the copper atoms are displaced from the center of the trigonal prism toward one of the rectangular faces adopting a pseudo-square planar configuration. The magnetic properties of Ca₃CuRhO₆, Ca₃Co_1.34Rh_0.66O₆, and Ca₃FeRhO₆ are discussed.     

Crystallographic and magnetic characterisation of the brownmillerite Sr2Co2O5

Sr₂Co₂O₅ with the perovskite-related brownmillerite structure has been synthesised via quenching, with the orthorhombic unit cell parameters a=5.4639(3) Å, b=15.6486(8) Å and c=5.5667(3) Å based on refinement of neutron powder diffraction data collected at 4 K. Electron microscopy revealed L-R-L-R-intralayer ordering of chain orientations, which require a doubling of the unit cell along the c-parameter, consistent with the assignment of the space group Pcmb. However, on the length scale pertinent to NPD, no long-range order is observed and the disordered space group Imma appears more appropriate. The magnetic structure corresponds to G-type order with a moment of 3.00(4) μ_B directed along [1 0 0].     

Crystal structure of BaMg2Si2O7 and Eu luminescence

Crystal structure of BaMg₂Si₂O₇ was determined and refined by a combined powder X-ray and neutron Rietveld method (monoclinic, C2/c, no. 15, Z=8, a=7.24553(8) Å, b=12.71376(14) Å, c=13.74813(15) Å, β=90.2107(8)°, V=1266.44(2) Å³; R_p/R_wp=3.38%/4.77%). The structure contains a single crystallographic type of Ba atom coordinated to eight O atoms with C₁ (1) site symmetry. Under 325-nm excitation Ba_0.98Eu_0.02Mg₂Si₂O₇ exhibits an asymmetric emission band around 402 nm. The asymmetric shape of the emission band is likely associated with a small electron-phonon coupling in BaMg₂Si₂O₇. The integrated intensity of the emission band was observed to remain constant over the temperature range 4.2-300 K.     

The non-centrosymmetric borate oxides, MBi2B2O7 (M=Ca, Sr)

Two novel noncentrosymmetric borates oxides, MBi₂B₂O₇ or MBi₂O(BO₃)₂ (MCa, Sr), have been synthesized by solid-state reactions in air at temperatures in the 600-700 °C range. Their crystal structures have been determined ab initio and refined using powder neutron diffraction data. CaBi₂B₂O₇ crystallizes in the orthorhombic Pna2₁ space group with a=8.9371(5) Å, b=5.4771(3) Å, c=12.5912(7) Å, Z=4, R_wp=0.118, χ²=2.30. SrBi₂B₂O₇ crystallizes in the hexagonal P6₃ space group with a=9.1404(4) Å, c=13.0808(6) Å, Z=6, R_wp=0.115, χ²=4.15. Large displacement parameters suggest the presence of disorder in SrBi₂B₂O₇ as also revealed by diffuse 2×a superstructure reflections in electron diffraction patterns. Both structures are built of identical (001) neutral layers of corner-sharing BO₃ triangles and MO₆ trigonal prisms forming six-membered rings in which Bi₂O groups are located. Adjacent layers are stacked in a staggered configuration and connected through weak Bi-O bonds. A moderate efficiency for second harmonic generation (SHG) has been measured for a powder sample of CaBi₂B₂O₇ (d_eff=2d_eff(KDP)).     

Structure and electron density analysis of electrochemically and chemically delithiated LiCoO2 single crystals

Single crystals of Li_0.68CoO₂, Li_0.48CoO₂, and Li_0.35CoO₂ were successfully synthesized for the first time by means of electrochemical and chemical delithiation processes using LiCoO₂ single crystals as a parent compound. A single-crystal X-ray diffraction study confirmed the trigonal R3¯m space group and the hexagonal lattice parameters a=2.8107(5) Å, c=14.2235(6) Å, and c/a=5.060 for Li_0.68CoO₂; a=2.8090(15) Å, c=14.3890(17) Å, and c/a=5.122 for Li_0.48CoO₂; and a=2.8070(12) Å, c=14.4359(14) Å, and c/a=5.143 for Li_0.35CoO₂. The crystal structures were refined to the conventional values R=1.99% and wR=1.88% for Li_0.68CoO₂; R=2.40% and wR=2.58% for Li_0.48CoO₂; and R=2.63% and wR=2.56% for Li_0.35CoO₂. The oxygen-oxygen contact distance in the CoO₆ octahedron was determined to be shortened by the delithiation from 2.6180(9) Å in LiCoO₂ to 2.5385(15) Å in Li_0.35CoO₂. The electron density distributions of these Li_xCoO₂ crystals were analyzed by the maximum entropy method (MEM) using the present single-crystal X-ray diffraction data at 300 K. From the results of the single-crystal MEM, strong covalent bonding was clearly visible between the Co and O atoms, while no bonding was found around the Li atoms in these compounds. The gradual decrease in the electron density at the Li site upon delithiation could be precisely analyzed.     

K2Mo4O13 phases prepared by hydrothermal synthesis

Hydrothermal synthesis in the K-Mo oxide system was investigated as a function of the pH of the reaction medium. Four compounds were formed, including two K₂Mo₄O₁₃ phases. One is a new low-temperature polymorph, which crystallizes in the orthorhombic, space group Pbca, with Z=8 and unit cell dimensions a=7.544(1) Å, b=15.394(2) Å, c=18.568(3) Å. The other is the known triclinic K₂Mo₄O₁₃, whose structure was re-determined from single crystal data; its cell parameters were determined as a=7.976(2) Å, b=8.345(2) Å, c=10.017(2) Å, α=107.104(3)°, β=102.885(3)°, γ=109.760(3)°, which are the standard settings of the crystal lattice. The orthorhombic phase converts endothermically into triclinic phase at ca. 730 K with a heat of transition of 8.31 kJ/mol.     

Subsolidus phase relations and crystal structures of the mixed-oxide phases in the In2O3-WO3 system

Subsolidus phase relationships in the In₂O₃-WO₃ system at 800-1400°C were investigated using X-ray diffraction. Two binary-oxide phases—In₆WO₁₂ and In₂(WO₄)₃—were found to be stable over the range 800-1200°C. Heating the binary-oxide phases above 1200°C resulted in the preferential volatilization of WO₃. Rietveld refinement was performed on three structures using X-ray diffraction data from nominally phase-pure In₆WO₁₂ at room temperature and from nominally phase-pure In₂(WO₄)₃ at 225°C and 310°C. The indium-rich phase, In₆WO₁₂, is rhombohedral, space group (rhombohedral), with Z=1, a=6.22390(4) Å, α=99.0338(2)° [hexagonal axes: a_H=9.48298(6) Å, c=8.94276(6) Å, a_H/c=0.9430(9)]. In₆WO₁₂ can be viewed as an anion-deficient fluorite structure in which 1/7 of the fluorite anion sites are vacant. Indium tungstate, In₂(WO₄)₃, undergoes a monoclinic-orthorhombic transition around 250°C. The high-temperature polymorph is orthorhombic, space group Pnca, with a=9.7126(5) Å, b=13.3824(7) Å, c=9.6141(5) Å, and Z=4. The low-temperature polymorph is monoclinic, space group P2₁/a, with a=16.406(2) Å, b=9.9663(1) Å, c=19.099(2) Å, β=125.411(2)°, and Z=8. The structures of the two In₂(WO₄)₃ polymorphs are similar, consisting of a network of corner sharing InO₆ octahedra and WO₄ tetrahedra.     

The crystal chemistry of Bi6TP2O15+x, T=Fe, Ni, Zn: Isomorphism and polymorphism, structural relationship to Bi6TiP2O16

The crystal structures of compounds with nominal compositions Bi₆FeP₂O_15+x (I), Bi₆NiP₂O_15+x (II) and Bi₆ZnP₂O_15+x (III) were determined from single-crystal X-ray diffraction data. They are monoclinic, space group I2, Z=2. The lattice parameters for (I) are a=11.2644(7), b=5.4380(3), c=11.1440(5) Å, β=96.154(4)°; for (II) a=11.259(7), b=5.461(4), c=11.109(7) Å, β=96.65(1)°; for (III) a=19.7271(5), b=5.4376(2), c=16.9730(6) Å, β=131.932(1)°. Least squares refinements on F² converged for (I) to R1=0.0554, wR₂=0.1408; for (II) R₁=0.0647, wR₂=0.1697; for (III) R₁=0.0385, wR₂=0.1023. The crystals are complexly twinned by 2-fold rotation about , by inversion and by mirror reflection. The structures consist of edge-sharing articulations of OBi₄ tetrahedra forming layers in the a-c plane that then continue by edge-sharing parallel to the b-axis. The three-dimensional networks are bridged by Fe and Ni octahedra in (I) and (II) and by Zn trigonal bipyramids in (III) as well as by oxygen atoms of the PO₄ moieties. Bi also randomly occupies the octahedral sites. Oxygen vacancies exist in the structures of the three compounds due to required charge balances and they occur in the octahedral coordination polyhedron of the transition metal. In compound (III), no positional disorder in atomic sites is present. The Bi-O coordination polyhedra are trigonal prisms with one, two or three faces capped. Magnetic susceptibility data for compound (I) were obtained between 4.2 and 350 K. Between 4.2 and 250 K it is paramagnetic, μ_eff=6.1 μ_B; a magnetic transition occurs above 250 K.     

Synthesis, structure and physical properties of the new uranium ternary phase U3Co2Ge7

A new ternary compound, U₃Co₂Ge₇, has been synthesized from the corresponding elements by a high temperature reaction using molten tin flux. It crystallizes in the orthorhombic La₃Co₂Sn₇-type (Pearson's symbol oC24, space group Cmmm, No. 65) with lattice parameters determined from single-crystal X-ray diffraction as follows: a=4.145(2) Å; b=24.920(7); c=4.136(2) Å, V=427.2(3) Å³. Structure refinements confirm an ordered structure having two crystallographically inequivalent uranium atoms, occupying sites with dissimilar coordination. U₃Co₂Ge₇ orders ferromagnetically below 40 K and undergoes a consecutive magnetic transition at 20 K. These results have been obtained from temperature- and field-dependent magnetization, resistivity and heat-capacity measurements. The estimated Sommerfeld coefficient γ=87 mJ/mol-U K² suggests U₃Co₂Ge₇ to be a moderately heavy-fermion material.     

The mercury chromates Hg6Cr2O9 and Hg6Cr2O10—Preparation and crystal structures, and thermal behaviour of Hg6Cr2O9

The basic mercury(I) chromate(VI), Hg₆Cr₂O₉ (=2Hg₂CrO₄·Hg₂O), has been obtained under hydrothermal conditions (200 °C, 5 days) in the form of orange needles as a by-product from reacting elemental mercury and K₂Cr₂O₇. Hydrothermal treatment of microcrystalline Hg₆Cr₂O₉ in demineralised water at 200 °C for 3 days led to crystal growth of red crystals of the basic mercury(I, II) chromate(VI), Hg₆Cr₂O₁₀ (=2Hg₂CrO₄·2HgO). The crystal structures were solved and refined from single crystal X-ray data sets. Hg₆Cr₂O₉: space group P2₁2₁2₁, Z=4, a=7.3573(12), b=8.0336(13), , 3492 structure factors, 109 parameters, R[F²>2σ(F²)]=0.0371, wR(F² all)=0.0517; Hg₆Cr₂O₁₀: space group Pca2₁, Z=4, a=11.4745(15), b=9.4359(12), , 3249 structure factors, 114 parameters, R[F²>2σ(F²)]=0.0398, wR(F² all)=0.0625. Both crystal structures are made up of an intricate mercury-oxygen network, subdivided into single building blocks [O-Hg-Hg-O] for the mercurous compound, and [O-Hg-Hg-O] and [O-Hg-O] for the mixed-valent compound. Hg₆Cr₂O₉ contains three different Hg₂²⁺ dumbbells, whereas Hg₆Cr₂O₁₀ contains two different Hg₂²⁺ dumbbells and two Hg²⁺ cations. The Hg^I-Hg^I distances are characteristic and range between 2.5031(15) and 2.5286(9) Å. All Hg₂²⁺ groups exhibit an unsymmetrical oxygen environment. The oxygen coordination of the Hg²⁺ cations is nearly linear with two tightly bonded O atoms at distances around 2.07 Å. For both structures, the chromate(VI) anions reside in the vacancies of the Hg-O network and deviate only slightly from the ideal tetrahedral geometry with average Cr-O distances of ca. 1.66 Å. Upon heating at temperatures above 385 °C, Hg₆Cr₂O₉ decomposes in a four-step mechanism with Cr₂O₃ as the end-product at temperatures above 620 °C.