硼硫共掺杂TiO2的光催化性能及掺杂机理

采用水热法制备了硼硫共掺杂的TiO2光催化剂(TiO2-B-S),并用其光催化降解甲基橙.结果表明,在240℃下水热反应12h时制得的TiO2-B-S具有较高的催化活性,紫外光照射50min和太阳光照射230min时对甲基橙的降解率分别达99.8%和81%.X射线粉末衍射、紫外-可见漫反射光谱和X射线光电子能谱等研究表明,TiO2-B-S为锐钛矿晶型,硫硼掺杂能抑制TiO2粒径的生长;TiO2-B-S同时具有较高的紫外光和可见光活性的原因可能是掺杂的硼以B3 进入晶格中,导致TiO2晶格畸变,带隙变窄.掺杂的硼和硫还提高了TiO2的表面酸度和对可见光的吸收.     

B掺杂TiO2/AC光催化剂的制备及活性

以硼酸和钛酸丁酯为主要原料，以活性炭(AC)为载体。用溶胶-凝胶法制备了B掺杂TiO2／AC光催化剂．用X射线衍射(XRD)、紫外可见漫反射吸收光谱(UV—VIS)对制得的光催化剂进行了表征．以甲基橙水溶液的光催化脱色反应和氧化乐果水溶液的光催化降解反应。考查了不同B掺杂TiO2／AC光催化剂的活性．结果表明，所有B掺杂TiO2／AC光催化剂均为锐钛矿晶相．B的掺杂未导致TiO2／AC光催化剂的吸收带边发生明显的移动．当B-TiO2质量分数分别为2．0％和2．5％时，TiO2／AC光催化剂的活性有明显的提高．B-TiO2质量分数2．0％时活性最高．但是，当B-TiO2质量分数分别为1．5％和3．0％时。TiO2／AC光催化剂的活性降低．B的缺电子特性可能改变了TiO2能带中的电子密度，使光催化反应中光生电子和空穴的俘获方式发生变化；同时。B的缺电子特性也会使光催化剂表面的Lewis酸强度增强，导致表面吸附OH-数量和目标反应物的吸附方式发生变化．这些可能是B-TiO2／AC光催化剂活性发生变化的主要原因．     

ZSM-5 晶粒度对其负载的 TiO2 光催化剂性能的影响

 采用透射电子显微镜、扫描电子显微镜、X 射线荧光分析、X 射线光电子能谱、紫外-可见漫反射光谱和吡啶吸附傅里叶变换红外光谱等表征方法以及偶氮染料甲基橙的吸附和光降解反应, 研究了 ZSM-5 晶粒度对 TiO2/ZSM-5 光催化剂性能的影响. 结果表明, TiO2 主要负载于 ZSM-5 沸石外表面, 因而减小载体晶粒度有利于提高 TiO2 的负载量和分散性. 纳米 ZSM-5 沸石负载的 TiO2 催化剂具有较高的甲基橙吸附量, 且吸附发生在 ZSM-5 外表面的酸中心上, 催化剂良好的吸附能力促进了甲基橙的光降解.     

Sm掺杂对TiO2薄膜光催化性能的影响

 采用溶胶-凝胶法、浸渍-提拉法制备了不同形式和不同含量Sm掺杂的锐钛矿晶型TiO2的光催化剂薄膜. 采用X射线衍射、UV-Vis光谱及电化学实验对所制得的TiO2光催化剂薄膜进行了表征,并通过甲基橙溶液的光催化降解实验评价了其光催化活性. 结果表明,与未掺杂的TiO2薄膜相比,Sm掺杂的TiO2薄膜的UV-Vis吸收光波长向长波方向移动,并且光照开路电压也相应提高; 适量Sm掺杂可以明显提高TiO2薄膜的光催化活性,最佳Sm掺杂量为x(Sm3+)=0.5%; 在各种掺杂形式中以表层Sm掺杂的Sm-TiO2(S)薄膜的光催化活性最好. 讨论了Sm掺杂提高TiO2薄膜光催化活性的机理.     

氮硫共掺杂TiO_2的光电荷分离效应及其光催化性能研究

以硫脲为掺杂剂,采用溶胶-凝胶法制备了氮硫共掺杂TiO2(N,S-TiO2)。用比表面孔隙仪(BET)、X射线衍射仪(XRD)、紫外-可见漫反射(UV-Vis DRS)和X射线光电子能谱(XPS)对制备的光催化剂进行了表征,用表面光电压仪(SPS)和捕获剂研究了光催化剂的光生电荷分离效应。以甲基橙为模拟污染物,在模拟自然光照射下考察了样品的光催化性能。结果表明:硫脲/Ti的摩尔比为30%所制备氮硫共掺杂TiO2具有较高的光催化活性,光催化活性是纯TiO2的5倍。氮硫共掺杂使TiO2具有更高的比表面和光生电荷分离效应,从而有利于提高光催化活性。     

N掺杂TiO_2纳米粒子表面光生电荷特性与光催化活性

以尿素为氮源,采用水热法制备了不同N掺杂量的TiO2(N-TiO2)光催化剂.利用X射线衍射(XRD),紫外-可见漫反射光谱(UV-Vis DRS),X射线光电子能谱(XPS)及荧光(PL)光谱等技术对其进行了系统的表征.以罗丹明B(RhB)和甲基橙(MO)溶液的脱色降解为模型反应,分别考察了N-TiO2光催化剂在紫外和可见光区的光催化活性.利用表面光伏(SPV)和瞬态光伏(TPV)技术研究了N-TiO2纳米粒子表面光生电荷的产生和传输机制,并探讨了光生电荷与光催化活性之间的关系.结果显示,随着N含量的增大,TiO2表面光伏响应阈值红移,可见光部分光电压响应强度逐渐增强,瞬态光伏响应达到最大值的时间亦有着不同程度的延迟.这表明适量的N掺杂能够提高TiO2纳米粒子中光生载流子的分离效率,相应地延长载流子的传输时间,增加光生电荷的寿命,从而促进其光催化活性;而过量的N掺杂则增加了TiO2纳米粒子中光生载流子的复合中心,抑制其光催化活性.     

Sm2O3掺杂TiO2光催化剂的制备和性能

 采用溶胶-凝胶法制备了Sm2O3掺杂TiO2光催化剂,通过X射线衍射、程序升温脱附和漫反射紫外-可见光谱等手段对催化剂进行了表征,并以苯酚为光催化降解反应模型化合物考察了光催化剂的活性,测定了苯酚在TiO2和Sm2O3掺杂TiO2光催化剂上的吸附常数. 结果表明,Sm2O3掺杂TiO2光催化剂具有较强的紫外光吸收性能. Sm2O3掺杂使TiO2粒径减小,比表面积增大,同时导致氧脱附温度提高及脱氧量增大. Sm2O3掺杂有利于反应底物在催化剂表面的吸附,Sm2O3的最佳掺入量为Sm/Ti摩尔比=0.8%.     

TiO2/Mo-TiO2 的制备、表征和光催化活性

 采用溶胶-凝胶法制备了掺 Mo 的 TiO2 粉末, 再由其制得 TiO2/Mo-TiO2 复合物光催化剂. 使用 X 射线光电子能谱、X 射线衍射、透射电镜、N2 吸附-脱附、紫外-可见漫反射光谱和荧光光谱等手段对催化剂进行了表征. 在紫外光照射下, 以甲基橙溶液降解为探针反应, 研究了 Mo 掺杂量对样品光催化活性的影响. 结果表明, Mo-TiO2 催化剂的活性不如纯 TiO2, 这是因为 Mo 离子促进了光生载流子的复合; 而带有 n-n 异质结半导体结构的 TiO2/Mo-TiO2 复合催化剂具有比纯 TiO2 和 Mo-TiO2 催化剂更高的光催化活性. 当 Mo 掺杂摩尔分数为 2%, TiO2:Mo-TiO2 质量比为 10:1 时, 活性是纯 TiO2 的 1.57 倍.     

LiF掺杂TiO2的制备及其光催化性能

采用溶胶-凝胶法制备了LiF掺杂的TiO2光催化剂,并采用X射线衍射、X射线光电子能谱和光致发光光谱等技术对样品进行了表征.以亚甲基蓝的光催化降解为反应模型,考察了LiF掺杂量、退火温度和溶液pH值对催化剂光催化性能的影响.结果表明,LiF的掺杂降低了金红石相的形成温度,同时在TiO2表面引入大量羟基氧并提高了TiO2表面氧空穴浓度,因此提高了TiO2的光催化性能.在LiF掺杂量为8%,退火温度为500℃和反应液pH值为6.6的条件下,LiF掺杂的TiO2的光催化活性是未掺杂TiO2的6倍.     

酸法纳米纤维素模板剂合成介孔TiO2及光催化活性

以生物可再生资源的酸法纳米纤维素为模板剂,四氯化钛为钛源,采用液相水解-沉淀法制备了具有介孔结构的TiO2光催化剂。采用低温N2物理吸附-脱附、透射电镜(TEM)、X射线衍射(XRD)、热重-量热扫描(TG/DSC)、傅里叶变换红外(FTIR)、X射线光电子能谱(XPS)等对介孔TiO2进行了表征,并以甲基橙为模型物,考察了介孔TiO2光催化活性。结果表明,以酸法纳米纤维素为模板剂合成的TiO2光催化活性显著提高,且具有良好的孔隙结构,平均孔径5.03 nm、总孔容积0.35 cm3.g-1、比表面积192m2.g-1;纤维素模板剂合成的TiO2表面羟基数量降低;纤维素长链分子结构之间的羟基与TiO2表面羟基的键合,可有效限制TiO2前驱体的生长和团聚,并抑制锐钛矿相TiO2向金红石相转变。     

Dichroism of absorption and polarization of phosphorescence of molecules of the closed form of nitrobenzospirothiopyran

The spectral-polarization characteristics of absorption and phosphorescence of molecules of the initial form of nitro-substituted indolinospirobenzothiopyran were studied in oriented polyethylene films and in solutions with different polarity. An oscillator model of the electron transitions responsible for the formation of absorption and luminescence spectra was suggested. It was established that the principal differences in the spectral and photophysical properties of the compound studied and its oxygen-containing analog are associated with the fact that the electronegativity of the S atom is lower than that of the O atom. Translated fromIzvestiya Akademii Nauk. Seriya Khimicheskaya, No. 6, pp. 1143–1146, June, 1997.     

非那雄胺合成工艺改进

非那雄胺能抑制5α-还原酶的活性,明显降低二氢睾酮水平,是一种治疗良性前列腺增生的有效药品。该合成工艺以甾烯酮酸为原料,将其与氯化亚砜反应,无须分离即与叔丁胺反应得17β-酰胺化合物,再氧化开环,环合,氢化,脱氢合成了非那雄胺。经元素分析、IR、1HNMR、13CNMR、MS分析表征了其结构。该法无须使用昂贵的2,2-二吡啶二硫化物和剧毒药品苯亚硒酸酐,且以乙酸铵代替氨气,降低了对设备的要求和腐蚀,更适用于工业生产。     

Synthesis of phenolic components of Grains of Paradise

Two vanilloids, (5E)-8-(4-hydroxy-3-methoxyphenyl)oct-5-en-4-one (1) and 4-[3-hydroxydecyl]-2-methoxyphenol (2), isolated from the dried seeds of Grains of Paradise (Aframomum melegueta), were synthesized; the latter compound was made as the S-enantiomer and the material derived from the seeds was found to be a 1:1.7 mixture of the R and S isomers. The synthetic route used should allow the preparation of analogs having extended alkyl chains and consequently different lipophilicity, and 3, a homolog of 2, was also prepared.     

Study of hydration of two cements of different strengths

Main hydration products of two cement pastes, i.e. CSH-gel, portlandite (P) (and specific surface S) were studied by static heating, and by SEM, TEM and XRD, as a function of cement strength (C-33 and C-43) hydration time (th) and subsequent hydration in water vapour.Total change in mass on hydration and air drying, M_o, increased with strength of cement paste and with hydration time. Content of water escaping at 110 to 220°C, defined as water bound with low energy, mainly interlayer and hydrate water, was independent on cement strength but its content increased with (th). Content of chemically bound (zeolitic) water in CSH-gel, escaping at 220-400°C, was slightly dependent on strength and increased with (th). It was possibly derived from the dehydroxylation of CSH-gel and AFm phase. Portlandite water, escaping at 400-500°C, was independent on cement strength and was higher on longer hydration. Large P crystals were formed in the weaker cement paste C-33. Smaller crystals were formed in C-43 but they increased with (th). Carbonate formated on contact with air (calcite, vaterite and aragonite), decomposed in cement at 600-700^oC. It was high in pastes C-33(1 month) and C-43(1 month), i.e. 5.7 and 3.3%, respectively; it was less than 1% after 6 hydration months (low sensitivity to carbonation) in agreement with the XRD study showing carbonates in the air dry paste (1month), and its absence on prolonged hydration (6 months) and on acetone treatment. Water vapour treatment of (6 months) pastes or wetting-drying increased this sensitivity.Nanosized P-crystals, detected by TEM, could contribute to the cement strength; carbonate was observed on the rims of gel clusters.This revised version was published online in November 2005 with corrections to the Cover Date.     

Acid hydrolysis of carboxymethylcellulose of low degree of substitution

Cotton cellulose was swollen in a sodium hydroxide solution and carboxymethylated by a two-bath method for different periods of time for each process. The kinetics of acid hydrolysis and the crystallinity of the swollen and carboxymethylated samples were measured. The proportion of broken bonds, rate constants for hydrolysis, and permeability of cellulose to hydrolyzing agents were calculated. The susceptibility of glycosidic linkages to acid hydrolysis was improved by carboxymethylation more than by swelling in alkali. The increased accessibility of carboxymethylcellulose to acid was regarded as a consequence of increased intra-and intercrystalline swelling and of the glycosidic bonds' weakness caused by the electron-attracting carboxymethyl group on the C-6 position.     

氯氧化镁生成热的研究

用氧化镁氯化镁水溶液制备了8水合氯氧化镁[nMg(OH)2·MgCl2·8H2O], 并测定了其在盐酸中的溶解热, 实验结果表明, 氯氧化镁溶解热与n值呈线性关系, 根据溶解热求出5Mg(OH)2·MgCl2·8H2O和3Mg(OH)2·MgCl2·8H2O的生成热分别为-7727.1和5888.1kJ·mol^1^-。     

Determination of heats of detonation and influence of components of composite explosives on heats of detonation of high explosives

The heats of detonation of 20 simple high explosives and explosive mixtures were determined by means of an adiabatic detonation calorimeter designed by the authors. The results indicated that the performance of the instrument was reliable and the experimental data were very accurate. For explosive mixtures, there was a linear accumulative relationship between the heats of detonation of the explosive mixture and its components. Accordingly, the heats of detonation of explosive mixtures could be calculated directly from the heats of detonation of simple explosives and the characteristic heats of other components. The experiments showed that the gold or brass shell of the cylindrical charge could be substituted by a thick-walled porcelain shell, which had the advantage of cheapness.

     

Estimation of Kinetic Parameters of Thermal Oxidation of Ilmenite

The aim of the presented work was the investigation of thermal oxidation of ilmenite in static air atmosphere. The investigations were carried out by use of a derivatograph (MOM, Hungary). The changes of crystallographic structure of investigated samples were identified by X-ray diffractometry on Philips PW-1710 diffractometer. In temperature above 500°C appears structure of hematite Fe₂O₃. On the basis of the thermogravimetric measurements, the contracting area and contracting volume models were found as the best fitting experimental data. This revised version was published online in August 2006 with corrections to the Cover Date.     

Mechanism of action of base-catalyzed oxygenation of phenol derivatives

Cyclopropyl derivative of 2,6-di-tert-butylphenol is synthesized as a probe to investigate the mechanism of base-catalyzed autooxidation of phenol derivatives. Our study indicates that one electron reduction of molecular oxygen from phenolate gives phenoxyl radical 3, a key intermediate of autooxidation. The coupling of phenoxyl radical and superoxide radical gives peroxylate anion 4 and produces the final epoxy alcohol adduct 6.