Preparation of a highly active nanocrystalline TiO2 photocatalyst from titanium oxo cluster precursor

Nanocrystalline TiO₂ (sample S1) was prepared from a titanium oxo cluster (Ti₇O₄(OEt)₂₀) precursor via a sol-gel route. This photocatalyst showed a higher photocatalytic activity than the TiO₂ (sample S2) obtained from titanium tetraisopropoxide. The samples were characterized by thermal analysis (TGA/DSC), X-ray diffraction, micro-Raman spectroscopy, transmission electron microscopy, N₂ adsorption (BET surface area), infrared absorption spectroscopy (FT-IR) and X-ray photoelectron spectroscopy. The characterization results show that both samples are anatase nanocrystals with particle sizes of about 12 nm, but the more photocatalytically active sample S1 has more surface hydroxyl groups and larger surface area and pore volume than sample S2.     

Sonochemical fabrication of fluorinated mesoporous titanium dioxide microspheres

A sonochemical-hydrothermal method for preparing fluorinated mesoporous TiO₂ microspheres was developed. Formation of mesoporous TiO₂ and doping of fluorine was achieved by sonication and then hydrothermal treatment of a solution containing titanium isopropoxide, template, and sodium fluoride. The as-synthesized TiO₂ microspheres were characterized by X-ray diffraction (XRD), Fourier translation infrared spectroscopy (FT-IR), X-ray photoelectron spectroscopy (XPS), scanning electron microscopy (SEM), transmission electron microscopy (TEM), energy-dispersive X-ray (EDX) spectroscopy, photoluminescence spectroscopy (PL), and BET surface areas. The P123 template was removed completely during the hydrothermal and washing steps, which was different from the conventional calcination treatment. The as- synthesized TiO₂ microspheres had good crystallinity and high stability. Results from the photocatalytic degradation of methylene blue (MB) showed that fluorination could remarkably improve the photocatalytic activity of titanium dioxide.     

Rapid Synthesis of Nanocrystalline TiO2/SnO2 Binary Oxides and Their Photoinduced Decomposition of Methyl Orange

A rapid and simple method, the so-called stearic acid method (SAM) was developed to prepare nanostructured TiO₂/SnO₂ binary oxides by combustion of stearic acid precursors. The preparative process was studied by Fourier transform infrared spectroscopy (FT-IR). During the preparative process, metal precursors were dispersed in stearic acid at molecular level. Microstructure of the samples was investigated by X-ray diffraction (XRD), transmission electron microscopy (TEM), BET specific surface area measurement and the results were compared with those obtained by conventional sol-gel method. The photocatalytic decomposition of methyl orange was used as a model system to determine the relative influences of the preparation method and the concentration of SnO₂ on the photocatalytic activities. It was found that preparative methods affected the crystalline structure of TiO₂/SnO₂ powders and the anatase phase of TiO₂ was stabilized by the addition of SnO₂ in SAM. The samples prepared by SAM showed better dispersity, larger specific surface area and the TiO₂/SnO₂ (r=0.15, SAM) catalyst showed higher photocatalytic activity than Degussa P25.     

Template‐free Fabrication of Hierarchical Macro‐/mesoporous N‐doped TiO2/graphene Oxide Composites with Enhanced Visible‐light Photocatalytic Activity

Hierarchical macro‐/mesoporous N‐doped TiO₂/graphene oxide (N‐TiO₂/GO) composites were prepared without using templates by the simple dropwise addition mixed solution of tetrabutyl titanate and ethanol containg graphene oxide (GO) to the ammonia solution, and then calcined at 350 °C. The as‐prepared samples were characterized by scanning electron microscopy (SEM), Brunauer‐Emmett‐Teller (BET) surface area, X‐ray diffraction (XRD), Raman spectroscopy, X‐ray photoelectron spectroscopy (XPS), and UV‐Vis absorption spectroscopy. The photocatalytic activity was evaluated by the photocatalytic degradation of methyl orange in an aqueous solution under visible‐light irradiation. The results show that N‐TiO₂/GO composites exhibited enhanced photocatalytic activity. GO content exhibited an obvious influence on photocatalytic performance, and the optimal GO addition content was 1 wt%. The enhanced photocatalytic activity could be attributed to the synergetic effects of three factors including the improved visible light absorption, the hierarchical macro‐mesoporous structure, and the efficient charge separation by GO.     

Parameters controlling the photocatalytic performance of ZnO/Hombikat TiO2 composites

Commercial TiO₂ (Hombikat, UV-100) was impregnated with different loadings of zinc nitrate solution and subsequently calcined at different temperatures in order to obtain a stable homogeneous solid composite of ZnO/TiO₂. The prepared samples were characterized by X-ray powder diffraction (XRD), scanning electron microscopy (SEM), high resolution transmission electron microscopy (HR-TEM), UV-vis and Raman spectroscopy, inductively coupled plasma mass spectroscopy (ICP), X-ray photoelectron spectroscopy (XPS) as well as N₂ adsorption and desorption measurements. Results show that ZnO was incorporated within the TiO₂ crystals and did not form a separate bulky phase or metallic zinc. Moreover, the calcination temperature dramatically modifies the texture properties of the prepared samples compared with original Hombikat TiO₂. The photocatalytic performance of the prepared samples was evaluated by monitoring the degradation of methyl orange dye under black light illumination. Three main parameters were studied; ZnO loading, surface area and initial pH of the methyl orange solution. The variation in ZnO loading appears to have less influence on the catalytic activity than either the surface area or the pH.     

Solvothermal preparation of copper(II) porphyrin-sensitized mesoporous TiO<Subscript>2</Subscript> composites: enhanced photocatalytic activity and stability in degradation of 4-nitrophenol

Four new copper(II) porphyrins CuPp(1, 2, 3, 4) with a different number of peripheral ester groups were synthesized and used to sensitize the mesoporous TiO₂ under solvothermal condition, and accordingly, four mesoporous CuPp(1, 2, 3, 4)/TiO₂ composites were obtained. These composites were characterized by X-ray diffraction, scanning electron microscopy, transmission electron microscopy, BET nitrogen adsorption–desorption isotherms (BET), UV–vis diffuse reflectance spectroscopy (UV–vis-DRS), and Fourier-transform infrared spectroscopy (FT-IR). The results showed the crystal structure and morphology of mesoporous TiO₂ were not affected by the porphyrin existence on its surface. The photocatalysis properties of mesoporous TiO₂ and CuPp(1, 2, 3, 4)/TiO₂ have been evaluated by conducting the photocatalytic degradation of 4-nitrophenol (4-NP) under visible-light irradiation, and the result showed their higher photocatalytic activities and the order is: CuPp(4)/TiO₂ > CuPp(3)/TiO₂ > CuPp(2)/TiO₂ > CuPp(1)/TiO₂ ? TiO₂. The probable reasons are their large surface area and different number of peripheral groups in CuPp, which separate electron–hole pairs efficiently. The repetition test of CuPp(1, 2, 3, 4)/TiO₂ composites demonstrated that they still maintained superior photocatalytic activity over six recycles.     

Synthesis and photocatalytic activity of co-doped mesoporous TiO2 on Brij98/CTAB composite surfactant template

Using composite surfactant templates, polyoxyethylene (20) oleyl ether (Brij98) and cetyl trimethyl ammonium bromide (CTAB), as structure-directing agents, N and La co-doped mesoporous TiO₂ complex photocatalysts were synthesized successfully. The micromorphology of co-doped mesoporous TiO₂ samples was characterized by X-ray diffraction (XRD), transmission electron microscopy (TEM), Fourier transformed infrared spectroscopy (FT-IR), energy-dispersive X-ray spectrometer (EDS) and N₂ adsorption-desorption measurements. The results indicated that the complex photocatalyst prepared with a molar ratio of Brij98:CTAB=1:1 showed a uniform pore size of ca. 7 nm and a high specific surface area (S_BET) of 279.0 m² g⁻¹, and exhibited the highest photocatalytic activity for degradation of papermaking wastewater under ultra-violet light irradiation. The chemical oxygen demand (CODc_r) percent degradation was about 73% in 12 h and chroma percent degradation was 100% in 8 h.     

Preparation,Characterization and Photocatalytic Activity of Lanthanum Doped Mesoporous Titanium Dioxide

Lanthanum doped mesoporous titanium dioxide photocatalysts with different La content were synthesized by template method using tetrabutyltitanate (Ti(OC₄H₉)₄) as precursor and Pluronic P123 as template. The catalysts were characterized by thermogravimetric dif-ferential thermal analysis, N₂ adsorption-desorption measurements, X-ray diffraction, and UV-Vis adsorption spectroscopy. The effect of La³⁺ doping concentration from 0.1% to 1% on the photocatalytic activity of mesoporous TiO₂ was investigated. The characterizations indicated that the photocatalysts possessed a homogeneous pore diameter of about 10 nm with high surface area of 165 m²/g. X-ray photoelectron spectroscopy measurements in-dicated the presence of C in the doped samples in addition to La. Compared with pure mesoporous TiO₂, the La-doped samples extended the photoabsorption edge into the visible light region. The results of phenol photodecomposition showed that La-doped mesoporous TiO₂ exhibited higher photocatalytic activities than pure mesoporous TiO₂ under UV and visible light irradiation.     

不同氮源溶剂热合成N-TiO2纳米颗粒及其光催化降解气相苯（英文）

采用三种不同的氮源溶剂热合成了锐钛矿-板钛矿混晶的N-TiO2催化剂.采用X射线衍射、N2吸附-脱附、X射线光电子能谱和透射电子显微镜等手段对催化剂进行了表征.重点研究了不同氮源对催化剂的相组成、晶粒尺寸、微观结构以及比表面积的影响.采用紫外光降解气相苯测试了合成材料的催化活性.结果表明,以水合肼为氮源合成的N-TiO2表现出最优的光催化活性,其活性明显高于P25,且能够循环使用15次以上.采用气相色谱-质谱技术分析了光降解过程的中间产物,基于此提出了相应的降解机理.     

Study of photocatalytic activity of Cd-doped mesoporous nanocrystalline TiO2 prepared at low temperature

Mesoporous nanocrystalline Cd-doped titania was firstly prepared at low temperature by a modified sol–gel method, using dodecylamine as a template. The template could be easily removed by refluxing samples in nitric acid ethanol solution. The Fourier transform infrared spectrometer (FT-IR), low-angle and wide-angle X-ray diffraction (XRD), N₂ adsorption–desorption, transmission electron microscopy (TEM), X-ray photoelectron spectra (XPS), and UV–visible diffuse reflectance spectroscopy were used for the characterization of catalysts. The characteristic results clearly showed that Cd²⁺ ions were doped into the titania lattice, and the mesoporous architecture of Cd-doped TiO₂ was composed of mixed-phase crystal textures of anatase and brookite. The samples displayed high visible-light photocatalytic activity for photodegradating 2,4-dichlorophenol (2,4-DCP) solution. The high activities of samples were attributed to the bicrystalline framework, large BET surface area, small crystallite size, and Cd-doping.     

N,B, Si-tridoped mesoporous TiO<Subscript>2</Subscript> with high surface area and excellent visible-light photocatalytic activity

N, B, Si-tridoped mesoporous TiO₂, together with N-doped, N, B-codoped and N, Si-codoped TiO₂, was prepared by a modified sol–gel method. The samples were characterized by wide-angle X-ray diffraction (WAXRD), N₂ adsorption–desorption, transmission electron microscopy (TEM), Fourier transform infrared (FT-IR) spectroscopy, UV–visible adsorbance spectra (UV–vis) and X-ray photoelectron spectra (XPS). The N, B, Si-tridoped mesoporous TiO₂ showed small crystallite size, large specific surface area (350 m²/g), uniform pore distribution (3.2 nm) and strong absorption in the visible light region. The photocatalytic activities of the samples were evaluated by the photodegradation of 2,4-dichlorophenol (2,4-DCP) aqueous solution. The N, B, Si-tridoping sample exhibited much higher photocatalytic activity compared with other synthesized photocatalysts. The high activity could be attributed to the strong absorption in the visible light region, large specific surface area, small crystallite size, large amount of surface hydroxyl groups, and mesoporosity.     

溶剂热法制备Ag/TiO2纳米材料及其光催化性能

以乙醇为溶剂, 钛酸四丁酯为前驱体, 用溶剂热法制备了Ag表面修饰的负载型纳米二氧化钛光催化剂. 利用X射线衍射(XRD)、N₂吸附-脱附(BET)、透射电子显微镜(TEM)、X射线光电子能谱(XPS)、紫外-可见(UV-Vis)光谱等技术对其进行了系统的表征, 以亚甲基蓝(MB)溶液的脱色降解为模型反应, 考察了不同Ag含量样品的光催化性能. 结果表明: 用溶剂热法制备的样品中TiO₂皆为锐钛矿相, 金属Ag颗粒沉积在TiO₂表面, 粒径为2 nm左右, 比表面积较溶胶凝胶法制备的样品大大增加, 最高可达151.44 m²·g^-1; UV-Vis光谱和光催化实验表明: Ag修饰使TiO₂对光的吸收能力大大增强, 吸收带边红移至可见光区, 亚甲基蓝在该复合材料上的光催化降解反应遵循一级反应动力学模型; 溶剂热法制备样品的光催化性能明显好于溶胶凝胶法制备的样品, 在紫外光和可见光下, Ag摩尔分数为5%的样品表现出最佳的光催化活性.     

溶剂热法制备Ag/TiO2纳米材料及其光催化性能

以乙醇为溶剂, 钛酸四丁酯为前驱体, 用溶剂热法制备了Ag表面修饰的负载型纳米二氧化钛光催化剂. 利用X射线衍射(XRD)、N₂吸附-脱附(BET)、透射电子显微镜(TEM)、X射线光电子能谱(XPS)、紫外-可见(UV-Vis)光谱等技术对其进行了系统的表征, 以亚甲基蓝(MB)溶液的脱色降解为模型反应, 考察了不同Ag含量样品的光催化性能. 结果表明: 用溶剂热法制备的样品中TiO₂皆为锐钛矿相, 金属Ag颗粒沉积在TiO₂表面, 粒径为2 nm左右, 比表面积较溶胶凝胶法制备的样品大大增加, 最高可达151.44 m²·g^-1; UV-Vis光谱和光催化实验表明: Ag修饰使TiO₂对光的吸收能力大大增强, 吸收带边红移至可见光区, 亚甲基蓝在该复合材料上的光催化降解反应遵循一级反应动力学模型; 溶剂热法制备样品的光催化性能明显好于溶胶凝胶法制备的样品, 在紫外光和可见光下, Ag摩尔分数为5%的样品表现出最佳的光催化活性.     

溶剂热法制备Ag/TiO2纳米材料及其光催化性能

以乙醇为溶剂, 钛酸四丁酯为前驱体, 用溶剂热法制备了Ag表面修饰的负载型纳米二氧化钛光催化剂. 利用X射线衍射(XRD)、N₂吸附-脱附(BET)、透射电子显微镜(TEM)、X射线光电子能谱(XPS)、紫外-可见(UV-Vis)光谱等技术对其进行了系统的表征, 以亚甲基蓝(MB)溶液的脱色降解为模型反应, 考察了不同Ag含量样品的光催化性能. 结果表明: 用溶剂热法制备的样品中TiO₂皆为锐钛矿相, 金属Ag颗粒沉积在TiO₂表面, 粒径为2 nm左右, 比表面积较溶胶凝胶法制备的样品大大增加, 最高可达151.44 m²·g^-1; UV-Vis光谱和光催化实验表明: Ag修饰使TiO₂对光的吸收能力大大增强, 吸收带边红移至可见光区, 亚甲基蓝在该复合材料上的光催化降解反应遵循一级反应动力学模型; 溶剂热法制备样品的光催化性能明显好于溶胶凝胶法制备的样品, 在紫外光和可见光下, Ag摩尔分数为5%的样品表现出最佳的光催化活性.     

溶剂热法制备Ag/TiO2纳米材料及其光催化性能

以乙醇为溶剂, 钛酸四丁酯为前驱体, 用溶剂热法制备了Ag表面修饰的负载型纳米二氧化钛光催化剂. 利用X射线衍射(XRD)、N₂吸附-脱附(BET)、透射电子显微镜(TEM)、X射线光电子能谱(XPS)、紫外-可见(UV-Vis)光谱等技术对其进行了系统的表征, 以亚甲基蓝(MB)溶液的脱色降解为模型反应, 考察了不同Ag含量样品的光催化性能. 结果表明: 用溶剂热法制备的样品中TiO₂皆为锐钛矿相, 金属Ag颗粒沉积在TiO₂表面, 粒径为2 nm左右, 比表面积较溶胶凝胶法制备的样品大大增加, 最高可达151.44 m²·g^-1; UV-Vis光谱和光催化实验表明: Ag修饰使TiO₂对光的吸收能力大大增强, 吸收带边红移至可见光区, 亚甲基蓝在该复合材料上的光催化降解反应遵循一级反应动力学模型; 溶剂热法制备样品的光催化性能明显好于溶胶凝胶法制备的样品, 在紫外光和可见光下, Ag摩尔分数为5%的样品表现出最佳的光催化活性.     

溶剂热法制备Ag/TiO2纳米材料及其光催化性能

以乙醇为溶剂, 钛酸四丁酯为前驱体, 用溶剂热法制备了Ag表面修饰的负载型纳米二氧化钛光催化剂. 利用X射线衍射(XRD)、N₂吸附-脱附(BET)、透射电子显微镜(TEM)、X射线光电子能谱(XPS)、紫外-可见(UV-Vis)光谱等技术对其进行了系统的表征, 以亚甲基蓝(MB)溶液的脱色降解为模型反应, 考察了不同Ag含量样品的光催化性能. 结果表明: 用溶剂热法制备的样品中TiO₂皆为锐钛矿相, 金属Ag颗粒沉积在TiO₂表面, 粒径为2 nm左右, 比表面积较溶胶凝胶法制备的样品大大增加, 最高可达151.44 m²·g^-1; UV-Vis光谱和光催化实验表明: Ag修饰使TiO₂对光的吸收能力大大增强, 吸收带边红移至可见光区, 亚甲基蓝在该复合材料上的光催化降解反应遵循一级反应动力学模型; 溶剂热法制备样品的光催化性能明显好于溶胶凝胶法制备的样品, 在紫外光和可见光下, Ag摩尔分数为5%的样品表现出最佳的光催化活性.     

溶剂热法制备Ag/TiO2纳米材料及其光催化性能

以乙醇为溶剂, 钛酸四丁酯为前驱体, 用溶剂热法制备了Ag表面修饰的负载型纳米二氧化钛光催化剂. 利用X射线衍射(XRD)、N₂吸附-脱附(BET)、透射电子显微镜(TEM)、X射线光电子能谱(XPS)、紫外-可见(UV-Vis)光谱等技术对其进行了系统的表征, 以亚甲基蓝(MB)溶液的脱色降解为模型反应, 考察了不同Ag含量样品的光催化性能. 结果表明: 用溶剂热法制备的样品中TiO₂皆为锐钛矿相, 金属Ag颗粒沉积在TiO₂表面, 粒径为2 nm左右, 比表面积较溶胶凝胶法制备的样品大大增加, 最高可达151.44 m²·g^-1; UV-Vis光谱和光催化实验表明: Ag修饰使TiO₂对光的吸收能力大大增强, 吸收带边红移至可见光区, 亚甲基蓝在该复合材料上的光催化降解反应遵循一级反应动力学模型; 溶剂热法制备样品的光催化性能明显好于溶胶凝胶法制备的样品, 在紫外光和可见光下, Ag摩尔分数为5%的样品表现出最佳的光催化活性.     

溶剂热法制备Ag/TiO2纳米材料及其光催化性能

以乙醇为溶剂, 钛酸四丁酯为前驱体, 用溶剂热法制备了Ag表面修饰的负载型纳米二氧化钛光催化剂. 利用X射线衍射(XRD)、N₂吸附-脱附(BET)、透射电子显微镜(TEM)、X射线光电子能谱(XPS)、紫外-可见(UV-Vis)光谱等技术对其进行了系统的表征, 以亚甲基蓝(MB)溶液的脱色降解为模型反应, 考察了不同Ag含量样品的光催化性能. 结果表明: 用溶剂热法制备的样品中TiO₂皆为锐钛矿相, 金属Ag颗粒沉积在TiO₂表面, 粒径为2 nm左右, 比表面积较溶胶凝胶法制备的样品大大增加, 最高可达151.44 m²·g^-1; UV-Vis光谱和光催化实验表明: Ag修饰使TiO₂对光的吸收能力大大增强, 吸收带边红移至可见光区, 亚甲基蓝在该复合材料上的光催化降解反应遵循一级反应动力学模型; 溶剂热法制备样品的光催化性能明显好于溶胶凝胶法制备的样品, 在紫外光和可见光下, Ag摩尔分数为5%的样品表现出最佳的光催化活性.     

溶剂热法制备Ag/TiO2纳米材料及其光催化性能

以乙醇为溶剂, 钛酸四丁酯为前驱体, 用溶剂热法制备了Ag表面修饰的负载型纳米二氧化钛光催化剂. 利用X射线衍射(XRD)、N₂吸附-脱附(BET)、透射电子显微镜(TEM)、X射线光电子能谱(XPS)、紫外-可见(UV-Vis)光谱等技术对其进行了系统的表征, 以亚甲基蓝(MB)溶液的脱色降解为模型反应, 考察了不同Ag含量样品的光催化性能. 结果表明: 用溶剂热法制备的样品中TiO₂皆为锐钛矿相, 金属Ag颗粒沉积在TiO₂表面, 粒径为2 nm左右, 比表面积较溶胶凝胶法制备的样品大大增加, 最高可达151.44 m²·g^-1; UV-Vis光谱和光催化实验表明: Ag修饰使TiO₂对光的吸收能力大大增强, 吸收带边红移至可见光区, 亚甲基蓝在该复合材料上的光催化降解反应遵循一级反应动力学模型; 溶剂热法制备样品的光催化性能明显好于溶胶凝胶法制备的样品, 在紫外光和可见光下, Ag摩尔分数为5%的样品表现出最佳的光催化活性.     

溶剂热法制备Ag/TiO2纳米材料及其光催化性能

以乙醇为溶剂, 钛酸四丁酯为前驱体, 用溶剂热法制备了Ag表面修饰的负载型纳米二氧化钛光催化剂. 利用X射线衍射(XRD)、N₂吸附-脱附(BET)、透射电子显微镜(TEM)、X射线光电子能谱(XPS)、紫外-可见(UV-Vis)光谱等技术对其进行了系统的表征, 以亚甲基蓝(MB)溶液的脱色降解为模型反应, 考察了不同Ag含量样品的光催化性能. 结果表明: 用溶剂热法制备的样品中TiO₂皆为锐钛矿相, 金属Ag颗粒沉积在TiO₂表面, 粒径为2 nm左右, 比表面积较溶胶凝胶法制备的样品大大增加, 最高可达151.44 m²·g^-1; UV-Vis光谱和光催化实验表明: Ag修饰使TiO₂对光的吸收能力大大增强, 吸收带边红移至可见光区, 亚甲基蓝在该复合材料上的光催化降解反应遵循一级反应动力学模型; 溶剂热法制备样品的光催化性能明显好于溶胶凝胶法制备的样品, 在紫外光和可见光下, Ag摩尔分数为5%的样品表现出最佳的光催化活性.