Characterization,crystallization kinetics,and melting behavior of poly(ethylene succinate) copolyester containing 10 mol % butylene succinate

Copolyester was synthesized and characterized as having 89.9 mol % ethylene succinate units and 10.1 mol % butylene succinate units in a random sequence, as revealed by NMR. Isothermal crystallization kinetics was studied in the temperature range (T_c) from 30 to 73 °C using differential scanning calorimetry (DSC). The melting behavior after isothermal crystallization was investigated using DSC by varying the T_c, the heating rate and the crystallization time. DSC curves showed triple melting peaks. The melting behavior indicates that the upper melting peaks are associated primarily with the melting of lamellar crystals with various stabilities. As the T_c increases, the contribution of recrystallization slowly decreases and finally disappears. A Hoffman‐Weeks linear plot gives an equilibrium melting temperature of 107.0 °C. The spherulite growth of this copolyester from 80 to 20 °C at a cooling rate of 2 or 4 °C/min was monitored and recorded using an optical microscope equipped with a CCD camera. Continuous growth rates between melting and glass transition temperatures can be obtained after curve‐fitting procedures. These data fit well with those data points measured in the isothermal experiments. These data were analyzed with the Hoffman and Lauritzen theory. A regime II → III transition was detected at around 52 °C. © 2008 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 46: 2431–2442, 2008     

New insights into the multiple melting behaviors of the semicrystalline ethylene‐hexene copolymer: Origins of quintuple melting peaks

A semicrystalline ethylene‐hexene copolymer (PEH) was subjected to a simple thermal treatment procedure as follows: the sample was isothermally crystallized at a certain isothermal crystallization temperature from melt, and then was quenched in liquid nitrogen. Quintuple melting peaks could be observed in heating scan of the sample by using differential scanning calorimeter (DSC). Particularly, an intriguing endothermic peak (termed as Peak 0) was found to locate at about 45 °C. The multiple melting behaviors for this semicrystalline ethylene‐hexene copolymer were investigated in details by using DSC. Wide‐angle X‐ray diffraction (WAXD) technique was applied to examine the crystal forms to provide complementary information for interpreting the multiple melting behaviors. Convincing results indicated that Peak 0 was due to the melting of crystals formed at room temperature from the much highly branched ethylene sequences. Direct heating scans from isothermal crystallization temperature (T_c, 104–118 °C) were examined for comparison, which indicated that the multiple melting behaviors depended on isothermal crystallization temperature and time. A triple melting behavior could be observed after a relatively short isothermal crystallization time at a low T_c (104–112 °C), which could be attributed to a combination of melting of two coexistent lamellar stack populations with different lamellar thicknesses and the melting‐recrystallization‐remelting (mrr) event. A dual melting behavior could be observed for isothermal crystallization with both a long enough time at a low T_c and a short or long time at an intermediate T_c (114 °C), which was ascribed to two different crystal populations. At a high T_c (116–118 °C), crystallizable ethylene sequences were so few that only one single broad melting peak could be observed. © 2008 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 46: 2100–2115, 2008     

Thermal analysis of poly(2-methylpentamethylene terephthalamide)

Poly(2-methylpentamethylene terephthalamide) (Nylon M5T) is a new high temperature aromatic polyamide developed by Hoechst Celanese. In this paper thermal properties of Nylon M5T chips, as well as as-spun and drawn fibers were studied by DSC, DMA, hot stage microscopy and WAXS.T _g of the fully amorphous Nylon M5T is 143°C when measured by DSC;T _g increases with crystallinity to 151°C. The temperature dependence of the solid and melt specific heat capacities has also been determined. The heat capacity increase at the glass transition of the amorphous polymer is 103.9 J °C^–1 mol^–1.T _g by DMA for the as-spun fiber is 155°C, for a drawn fiber is 180°C. Three secondary transitions were observed by DMA in addition to the glass transition. These correspond to a local mode relaxation of the methylene groups at –120°C, onset of rotation of the amide-groups at –65°C and the onset of the rotation of the phenylenegroups (at 63°C). The crystallinity of Nylon M5T strongly depends on the rate of cooling from the melt. The isothermal crystallization data are melt temperature dependent: two-dimensional crystallization takes place when the samples are crystallized from higher melt temperatures, and this phase changes into a spherulitic structure during cooling to room temperature. Spherulitic crystallization occurs when lower melt temperatures are used. This polymer has three crystal forms as indicated by DSC, DMA and WAXS data. The crystal to crystal transitions are clearly visible when amorphous samples are heated in the DSC, or the DMA curves of as-spun fibers are recorded. It is experimentally shown that a considerable melting of the lower temperature crystal forms takes place during the crystal to crystal transitions. The equilibrium melting point as measured by the Hoffman-Weeks method, has been determined to be 339°C.Dedicated to Professor Bernhard Wunderlich on the occasion of his 65th birthday     

Reversible and irreversible heat capacity of poly(trimethylene terephthalate) analyzed by temperature‐modulated differential scanning calorimetry

The heat capacity of poly(trimethylene terephthalate) (PTT) has been analyzed using temperature‐modulated differential scanning calorimetry (TMDSC) and compared with results obtained earlier from adiabatic calorimetry and standard differential scanning calorimetry (DSC). Using quasi‐isothermal TMDSC, the apparent reversing and nonreversing heat capacities were determined from 220 to 540 K, including glass and melting transitions. Truly reversible and time‐dependent irreversible heat effects were separated. The extrapolated vibrational heat capacity of the solid and the total heat capacity of the liquid served as baselines for the analysis. As one approaches the melting region from lower temperature, semicrystalline PTT shows a reversing heat capacity, which is larger than that of the liquid, an observation that is common also for other polymers. This higher heat capacity is interpreted as a reversible surface or bulk melting and crystallization, which does not need to undergo molecular nucleation. Additional time‐dependent, reversing contributions, dominating at temperatures even closer to the melting peak, are linked to reorganization and recrystallization (annealing), while the major melting is fully irreversible (nonreversing contribution). © 2000 John Wiley & Sons, Inc. J Polym Sci B: Polym Phys 38: 622–631, 2000     

Crystallization behavior and morphology of poly(ethylene‐co‐trimethylene terephthalate)s

The melt crystallization behaviors and crystalline structures of poly(ethylene terephthalate) (PET), poly(trimethylene terephthalate), and poly(ethylene‐co‐trimethylene terephthalate) (PETT) were investigated with differential scanning calorimetry (DSC), polarized optical microscopy (POM), and X‐ray diffraction at various crystallization temperatures (T_cs). The PETT copolymers were synthesized via the polycondensation of terephthalate with ethylene glycol and trimethylene glycol (TG) in various compositions. The copolymers with 69.0 mol % or more TG or 31.0 mol % or less TG were crystallizable, but the other copolymers containing 34–56 mol % TG were amorphous. The DSC isothermal results revealed that the addition of a small amount of flexible TG (up to 21 mol %) to the PET structure slightly reduced the formation of three‐dimensional spherulites. A greater TG concentration (91–100%) in the copolyesters changed the crystal growth from two‐dimensional to three‐dimensional. The DSC heating scans after the completion of isothermal crystallization at various T_cs showed three melting endotherms for PET, PETT‐88, PETT‐84, and PETT‐79 and four melting endotherms for PETT‐9 and PETT. The presence of an additional melting endotherm could be attributed to the melting of thinner and imperfect copolyester crystallites. Analyses of the Lauritzen–Hoffman equation demonstrated that PETT‐88 had the highest values of the product of the lateral and folding surface free energies, and this suggested that the addition of small amounts of flexible trimethylene terephthalate segments to PET disturbed chain regularity, thus increasing molecular chain mobility. © 2004 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 42: 4255–4271, 2004     

Melting behavior of isotactic polystyrene

The melting behavior of isotactic polystyrene, crystallized from the melt and from dilute solutions in trans-decalin, has been studied by differential scanning calorimetry and solubility measurements. The melting curves show 1, 2, or 3 melting endotherms. At large supercooling, crystallization from the melt produces a small melting endotherm just above the crystallization temperature T_c. This peak originates from secondary crystallization of melt trapped within the spherulites. The next melting endotherm is related to the normal primary crystallization process. Its peak temperature increases linearly with T_c, yielding an extrapolated value for the equilibrium melting temperature T_c° of 242 ± 1°C as found before. By self-seeding, crystallization from the melt could be performed at much higher temperature to obtain melting temperatures as high as 243°C, giving rise to doubt about the value of T_c° found by extrapolation. For normal values of T_c and heating rate, an extra endotherm appears on the melting curve. Its peak temperature is the same for both melt-crystallized and solution-crystallized samples, and independent of T_c, but rises with decreasing heating rate. From the effects of heating rate and partial scanning on the ratio of peak areas and of previous heat treatment on dissolution temperature, it is concluded that this peak arises from the second one by continuous melting and recrystallization during the scan.     

Oxygen‐barrier properties of cold‐crystallized and melt‐crystallized poly(ethylene terephthalate‐co‐4,4′‐bibenzoate)

This study examined the oxygen‐transport properties of poly(ethylene terephthalate‐co‐bibenzoate) (PETBB55) crystallized from the melt (melt crystallization) or quenched to glass and subsequently isothermally crystallized by heating above the glass‐transition temperature (cold crystallization). The gauche–trans conformation of the glycol linkage was determined by infrared analysis, and the crystalline morphology was examined by atomic force microscopy. Oxygen solubility decreased linearly with volume fraction crystallinity. For melt‐crystallized PETBB55, extrapolation to zero solubility corresponded to an impermeable crystal with 100% trans glycol conformations, a density of 1.396 g cm^?3, and a heat of melting of 83 J g^?1. From the melt, PETBB55 crystallized as space‐filling spherulites with loosely organized lamellae and pronounced secondary crystallization. The morphological observations provided a structural model for permeability consisting of impermeable platelets randomly dispersed in a permeable matrix. In contrast, cold‐crystallized PETBB55 retained the granular texture of the quenched polymer despite the high level of crystallinity, as measured by the density and heat of melting. Oxygen solubility decreased linearly with volume fraction crystallinity, but zero solubility corresponded to an impermeable defective crystal with a trans fraction of 0.83 and a density of 1.381 g cm^?3. © 2002 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 40: 2489–2503, 2002     

Analysis of a symmetric neopolyol ester

Quantitative thermal analysis was carried out for tetra[methyleneoxycarbonyl(2,4,4-trimethyl)pentyl]methane. The ester has a glass transition temperature of 219 K and a melting temperature of 304 K. The heat of fusion is 51.3 kJ mol^?1, and the increase in heat capacity at the glass transition is 250 J K^?1 mol^?1. The measured and calculated heat capacities of the solid and liquid states from 130 to 420 K are reported and a discussion of the glass and melting transitions is presented. The computation of the heat capacity made use of the Advanced Thermal Analysis System, ATHAS, using an approximate group-vibration spectrum and a Tarasov treatment of the skeletal vibrations. The experimental and calculated heat capacities of the solid ester were compared over the whole temperature range to detect changes in order and the presence of large-amplitude motion. An addition scheme for heat capacities of this and related esters was developed and used for the extrapolation of the heat capacity of the liquid state for this ester. The liquid heat capacity for the title ester is well represented by 691.1+1.668T [J K^?1 mol^?1]. A deficit in the entropy and enthalpy of fusion was observed relative to values estimated from empirical addition schemes, but no gradual disordering was noted outside the transition region. The final interpretation of this deficit of conformational entropy needs structure and mobility analysis by solid state¹³C NMR and X-ray diffraction. These analyses are reported in part II of this investigation.     

Crystallization of poly(ethylene terephthalate–co–isophthalate)

Melt crystallization behaviors of poly(ethylene terephthalate) (PET) and poly(ethylene terephthalate‐co‐isophthalate) (PETI) containing 2 and 12 mol % of noncrystallizable isophthalate components were investigated. Differential scanning calorimetry (DSC) isothermal results revealed that the introduction of 2 mol % isophthalate into PET caused a change of the crystal growth process from a two‐dimensional to a three‐dimensional spherulitic growth. The addition of more isophthalate up to 12 mol % into the PET structure induced a change in the crystal growth from a three‐dimensional to a two‐dimensional crystal growth. DSC heating scans after completion of isothermal crystallization at various T_c's showed three melting endotherms for PET and four melting endotherms for PETI‐2 and PETI‐12. The presence of an additional melting endotherm is attributed to the melting of copolyester crystallite composed of ethylene glycol, tere‐phthalate, and isophthalate (IPA) or the melting of molecular chains near IPA formed by melting the secondary crystallite T_m (I) and then recrystallizing during heating. Analyses of both Avrami and Lauritzen‐Hoffman equations revealed that PETI containing 2 mol % of isophthalate had the highest Avrami exponent n, growth rate constant G_o, and product of lateral and end surface free energies σσ_e. © 2000 John Wiley & Sons, Inc. J Polym Sci B: Polym Phys 38: 2515–2524, 2000     

Reversible and irreversible heat capacity of poly[carbonyl(ethylene‐co‐propylene)] by temperature‐modulated calorimetry

The heat capacity of poly[carbonyl(ethylene‐co‐propylene)] with 95 mol % C₂H₄? CO? (Carilon EP®) was measured with standard differential scanning calorimetry (DSC) and temperature‐modulated DSC (TMDSC). The integral functions of enthalpy, entropy, and free enthalpy were derived. With quasi‐isothermal TMDSC, the apparent reversing heat capacity was determined from 220 to 570 K, including the glass‐ and melting‐transition regions. The vibrational heat capacity of the solid and the heat capacity of the liquid served as baselines for the quantitative analysis. A small amount of apparent reversing latent heat was found in the melting range, just as for other polymers similarly analyzed. With an analysis of the heat‐flow rates in the time domain, information was collected about latent heat contributions due to annealing, melting, and crystallization. The latent heat decreased with time to an even smaller but truly reversible latent heat contribution. The main melting was fully irreversible. All contributions are discussed in the framework of a suggested scheme of six physical contributions to the apparent heat capacity. © 2001 John Wiley & Sons, Inc. J Polym Sci Part B: Polym Phys 39: 1565–1577, 2001     

Study of formation of nano-quasicrystals and crystallization kinetics of Zr-Al-Ni-Cu metallic glass

The formation of nano-quasicrystals on isothermal annealing of melt-spun ribbons of Zr_69.5Al_7.5Ni₁₁Cu₁₂ metallic glass has been investigated using transmission electron microscopy (TEM). The crystallization study of this metallic glass has been carried out using differential scanning calorimetry (DSC) in non-isothermal (linear heating) mode. It exhibits two-stage crystallization where the first stage corresponds to the precipitation of icosohedral nano-quasicrystalline phase. This has been confirmed with the help of TEM investigations. The crystallization parameters like the activation energy (E _c) and frequency factor (k ₀) have been derived using the Kissinger peak shift analysis. The activation energies for the first and second crystallization peak are found to be 278 and 295 kJ mol^–1, respectively. The frequency factors obtained for the two peaks are respectively 7.16·10¹⁹ and 1.42·10²⁰ s^–1. E _c, k ₀ and the Avrami exponent (n) have also been derived by fitting the Johnson-Mehl-Avrami-Kolmogorov (JMAK) equation for the transformed volume fraction (x) to the crystallization data. JMAK results of E _c for the first and second crystallization peak turn out to be 270 and 290 kJ mol^–1 respectively. However, k ₀ and n are found to be heating rate dependent as reported in similar studies. The values of n for the first crystallization stage ranges between 1.66 and 2.57 indicating diffusion-controlled transformation in agreement with earlier reports.     

Crystallization kinetics,morphology, and mechanical properties of novel poly(ethylene succinate-co-octamethylene succinate)

The crystallization kinetics, morphology and mechanical properties of a novel poly(ethylene succinate-co-octamethylene succinate) (PEOS) copolyester with 82 mol% ethylene succinate (ES) units and 18 mol% octamethylene succinate (OS) units, and its homopolymer poly(ethylene succinate) (PES) were extensively investigated. The glass transition temperature, cold crystallization peak temperature and melting point of PEOS are around −24, 47.5, and 80.5 °C, respectively. The Avrami equation was used to analyze the isothermal melt crystallization kinetics of PEOS and PES. They display the same crystallization mechanism, and PEOS crystallizes slower than PES at the same degree of supercooling. The spherulitic growth rates of PEOS and PES exhibit a bell shape within the investigated crystallization temperature range, with the crystallization regime transition temperature of PEOS being lower than that of PES. In addition, PEOS has high thermal stability and good mechanical properties.     

CRYSTALLIZATION AND MULTI-MELTING BEHAVIOR OF POLY (ETHYLENE TEREPHTHALATE) MODIFIED BY SODIUM SALT OF 5-SULPHO-ISOPHTHALIC ACID

The crystallization kinetics of the copolyester, poly(ethylene terephthalate) (PET) modified by sodium salt of 5-sulpho-isophthalic acid(SIPM), was investigated by means of differential scanning calorimeter. The experimental results and polari-microscopy observation all showed that the introduction of SIPM did not affect the nucleation of crystallization. Within the temperature range between their glass transition temperature T_θand melting point T_m, the crystallization rate of the copolyester sample decreased with increasing content of SIPM. The relative crystallization rate constant Z of SIPM/DMT (dimethyl terephthalate) 4mol % sample was about 1% pure PET's Z value. For isothermal crystallized copolyester samples, DSC heating curves displayed multi-melting behavior. This was interpreted by molecular weight fractionation during crystallization and premelting-recrystallization mechanism. This interpretation showed why the second melting point T_(m2) will change according to Hoffman-Weeks(H-W) equation and the first melting point T_(m1) will increase with increasing SIPM. The principal cause of these phenomena is the high temperature crystallization rate decreases rapidly with increasing SIPM.     

CRYSTALLIZATION SEGREGATION DSC STUDIES OF PP/PE COPOLYMERS

 The structural analysis of two PP/PE copolymer samples, I and 2, was conducted by using ¹³C-NMR, GPC and crystallization segregation DSC (CSDSC) techniques. A pure polypropylene sample was also used for comparison. It was found that the two copolymer samples are very close in composition (the ethylene mol content is 4.3% and 4.5%,respectively), stereoregularity (96% and 97%) and molecular weight (M_w, = 7.0 x 10⁴ and 7.3x10⁴; M_w/M_n = 5.0 and 6.1,respectively). While the CSDSC thermograms of the two samples are quite different from each other. Sample 1 shows a higher average melting temperature and a broader distribution of its thermogram. These phenomena were explained as an indication of a less uniform distribution of ethylene units along the PP chains for sample 1. It was noted that CSDSC is a very sensitive and convenient technique for structural studies of copolymers.     

Heat capacity of poly(butylene terephthalate)

The low‐temperature heat capacity of poly(butylene terephthalate) (PBT) was measured from 5 to 330 K. The experimental heat capacity of solid PBT, below the glass transition, was linked to its approximate group and skeletal vibrational spectrum. The 21 skeletal vibrations were estimated with a general Tarasov equation with the parameters Θ₁ = 530 K and Θ₂ = Θ₃ = 55 K. The calculated and experimental heat capacities of solid PBT agreed within better than ±3% between 5 and 200 K. The newly calculated vibrational heat capacity of the solid from this study and the liquid heat capacity from the ATHAS Data Bank were applied as reference values for a quantitative thermal analysis of the apparent heat capacity of semicrystalline PBT between the glass and melting transitions as obtained by differential scanning calorimetry. From these results, the integral thermodynamic functions (enthalpy, entropy, and Gibbs function) of crystalline and amorphous PBT were calculated. Finally, the changes in the crystallinity with the temperature were analyzed. With the crystallinity, a baseline was constructed that separated the thermodynamic heat capacity from cold crystallization, reorganization, annealing, and melting effects contained in the apparent heat capacity. For semicrystalline PBT samples, the mobile‐amorphous and rigid‐amorphous fractions were estimated to complete the thermal analysis. © 2004 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 42: 4401–4411, 2004     

Thermal and structural investigation of random ethylene/1-hexene copolymers with high 1-hexene content

Random ethylene/1-hexene copolymers with the 1-hexene content in the range from 2 to 28 mol% were produced with a novel post-metallocene catalyst and analyzed by three techniques, FTIR, ¹³C NMR, and DSC. The 1-hexene content and the sequence distribution in the copolymers were determined by means of FTIR-M and ¹³C NMR. The crystallization behavior of the copolymers was studied by DSC under dynamic and isothermal conditions; the Avrami model was used to analyze the crystallization kinetics. It was found that both the 1-hexene content and the crystallization temperature affect the relative crystallinity. The bulk crystallization rate decreases with the 1-hexene content and reduces exponentially with an increase of T _c. The melting behavior of isothermally crystallized samples was also investigated and it was found that the melting temperatures of the copolymers under equilibrium conditions were related to the composition.     

Multiple melting behavior of poly(butylene succinate). II. Thermal analysis of isothermal crystallization and melting process

The multiple melting behavior of poly(butylene succinate) (PBSu) was studied with differential scanning calorimetry (DSC). Three different PBSu resins, with molecular weights (MWs) of 1.1 × 10⁵, 1.8 × 10⁵, and 2.5 × 10⁵, were isothermally crystallized at various crystallization temperatures (T_c) ranging from 70 to 97.5 °C. The T_c dependence of crystallization half‐time (τ) was obtained. DSC melting curves for the isothermally crystallized samples were obtained at a heating rate of 10 K min⁻¹. Three endothermic peaks, an annealing peak, a low‐temperature peak L, and a high‐temperature peak H, and an exothermic peak located between peaks L and H clearly appeared in the DSC curve. In addition, an endothermic small peak S appeared at a lower temperature of peak H. Peak L increased with increasing T_c, whereas peak H decreased. The T_c dependence of the peak melting temperatures [T_m(L) and T_m(H)], recrystallization temperature (T_re), and heat of fusion (ΔH) was obtained. Their fitting curves were obtained as functions of T_c. T_m(L), T_re, and ΔH increased almost linearly with T_c, whereas T_m(H) was almost constant. The maximum rate of recrystallization occurred immediately after the melting. The mechanism of the multiple melting behavior is explained by the melt‐recrystallization model. The high MW samples showed similar T_c dependence of τ, and τ for the lowest MW sample was longer than that for the others. Peak L increased with MW, whereas peak H decreased. In spite of the difference of MW, T_m(L), T_m(H), and T_re almost coincided with each other at the same T_c. The ΔH values, that is crystallinity, for the highest MW sample were smaller than those for the other samples at the same T_c. © 2005 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 43: 2039–2047, 2005     

A study of phase separation of crystalline and miscible polymer blends. Poly(ε-caprolactone)/poly(styrene-co-acrylonitrile)

The phase separation of a crystalline and miscible polymer blend, poly(ε-caprolactone) /poly(styrene-co-acrylonitrile) (PCL/SAN), has been studied by differential scanning calorimetry (DSC), using a SAN containing 28.3% of acrylonitrile units. Several phenomena can be associated with the occurrence of phase separation depending upon the composition of the mixture. Following annealing at high temperatures, below and above the phase separation temperature T_c, three cases can be distinguished. In Case I, there is no sign of crystallization during quenching and DSC scanning, but a melting peak is observed at T_c, and above. In Case II, there is no crystallization on quenching but it does occur during the DSC run; the shift of the crystallization peak can then be related to T_c. In Case III, there is crystallization on quenching, and additional crystallization during the DSC run; the change of area of the crystallization peak is indicative of T_c. From these observations, the phase diagram of the system was determined. © 1993 John Wiley & Sons, Inc.     

Dynamic DSC,SAXS and WAXS on homogeneous ethylene-propylene and ethylene-octene copolymers with high comonomer contents

Ethylene-propylene (EP) and ethylene-octene (EO) copolymers polymerized with the aid of homogeneous vanadium and metallocene catalysts were compared by DSC and time-resolved simultaneous SAXS-WAXS-DSC at scanning rates of 10 and 20°C min^?1 using synchrotron radiation. An EP copolymer with a density of 896 kg m^?3 (about 89 mol % ethylene) after compression moulding gave orthorhombic WAXS reflections. The crystallinity as a function of temperature [w ^c (T)] calculated from these reflections using the two-phase model was in good agreement withw ^c (T) calculated fromc _p measurements using DSC. Thec _p measurements also enabled calculation of the baselinec _p and the excessc _p. The SAXS measurements revealed a strong change in the long period in cooling and in heating. The SAXS invariant as a function of temperature showed a maximum in both cooling and heating, which could be explained from the opposing influences of the crystallinity and the electron density difference between the two phases. Two EO copolymers with densities of about 871 kg m^?3 (about 87 mol% ethylene) no longer showed any clear WAXS reflections, although DSC and SAXS measurements showed that these copolymers did crystallize. The similarity between the results led to the conclusion that the copolymers, though based on different catalyst systems — vanadium and metallocene — did not have strongly different sets of propagation probabilities of chain growth during polymerization. On the basis of a Monte Carlo simulation model of crystallization and morphology, based on detailed knowledge of the microchain structure, the difference between WAXS on the one hand and DSC and SAXS on the other could be explained as being due to loosely packed crystallized ethylene sequences in clusters. These do cause the density and the electron density of the cluster to increase (which is measurable by SAXS) and the enthalpy to decrease (which is measurable by DSC) but the clusters are too small and/or too imperfect to give constructive interference in the case of WAXS. Of an EP copolymer with an even lower ethylene content (about 69 mol %), the crystallization and melting processes could still be readily measured by DSC and SAXS, which proves that these techniques are eminently suitable for investigating the crystallization and melting behaviour of the copolymers studied.     

Effects of carbon nanotubes on crystallization and melting behavior of poly(L‐lactide) via DSC and TMDSC studies

In this work, multiwalled carbon nanotubes (MWNTs) were surface‐modified and grafted with poly(L ‐lactide) to obtain poly(L ‐lactide)‐grafted MWNTs (i.e. MWNTs‐g‐PLLA). Films of the PLLA/MWNTs‐g‐PLLA nanocomposites were then prepared by a solution casting method to investigate the effects of the MWNTs‐g‐PLLA on nonisothermal and isothermal melt‐crystallizations of the PLLA matrix using DSC and TMDSC. DSC data found that MWNTs significantly enhanced the nonisothermal melt‐crystallization from the melt and the cold‐crystallization rates of PLLA on the subsequent heating. Temperature‐modulated differential scanning calorimetry (TMDSC) analysis on the quenched PLLA nanocomposites found that, in addition to an exothermic cold‐crystallization peak in the range of 80–120 °C, an exothermic peak in the range of 150–165 °C, attributed to recrystallization, appeared before the main melting peak in the total and nonreversing heat flow curves. The presence of the recrystallization peak signified the ongoing process of crystal perfection and, if any, the formation of secondary crystals during the heating scan. Double melting endotherms appeared for the isothermally melt‐crystallized PLLA samples at 110 °C. TMDSC analysis found that the double lamellar thickness model, other than the melting‐recrystallization model, was responsible for the double melting peaks in PLLA nanocomposites. Polarized optical microscopy images found that the nucleation rate of PLLA was enhanced by MWNTs. TMDSC analysis found that the incorporation of MWNTs caused PLLA to decrease the heat‐capacity increase (namely, ΔC_p) and the C_p at glass transition temperature. © 2007 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 45: 1870–1881, 2007