负载型镍基非晶态催化剂催化氯代硝基苯加氢合成氯代苯胺

分别以碳纳米管(CNTs), SiO_2, TiO_2, γ-Al_2O_3, TiO_2-SiO_2和活性炭(AC)为载体(M),以Ni和B为活性组分,采用浸渍-化学还原法制备了一系列负载型Ni-B非晶态合金催化剂(Ni-B/M).采用电感耦合等离子体光谱(ICP), XRD, TEM和DSC研究了Ni-B/CNTs的非晶性质,Ni的担载量及其热稳定性.将Ni-B/M用于催化三种氯代硝基苯液相加氢合成氯代苯胺的反应.结果表明,Ni-B/M在反应中表现出较高的活性和良好的选择性,其中Ni-B/CNTs可使三种氯代硝基苯的转化率均高于99.8%,加氢脱氯率小于3%.讨论了CNTs和Ni-B之间的相互作用对催化剂性能的影响.     

Ni-Co-B非晶态合金催化剂用于氯代硝基苯液相加氢制氯代苯胺

 用化学还原法制备了 Ni-Co-B 非晶态合金催化剂,并采用透射电子显微镜、扫描电子显微镜、选区电子衍射、X射线衍射、X射线能谱和差热-热重分析等表征手段研究了催化剂的非晶性质和原子组成等. 将此催化剂用于邻氯硝基苯和 3,4-二氯硝基苯的液相催化加氢反应,结果表明,当Co/(Co+Ni)=0.5 (摩尔比)时, Ni-Co-B 催化剂具有较好的加氢性能和较高的抑制脱卤性能. 在不加脱卤抑制剂的情况下,两种氯代硝基苯的转化率均接近100%, 脱卤率分别为1.12%和0.42%, 优于使用 Ni-B 和 Co-B 非晶态合金催化剂时的结果. 还讨论了将Co引入到 Ni-B 非晶态合金催化剂时对其性能的影响.     

卤代苯和卤代萘用三氧化硫进行的磺化反应

本文研究 了在非极性溶剂二氯甲烷中卤代苯和卤代萘用SO~3进行的磺化反应. 卤代苯最初开始磺化反应的产物是4-磺酸, 2-卤代萘的产物是8-磺酸. 当用过量的SO~3长时间反应时, 磺化反应得到三取代产物.     

水溶性含钌-铂双金属催化剂催化卤代芳香硝基化合物选择性加氢

考察了水溶性Ru/Pt-TPPTS双金属催化剂催化卤代芳香硝基化合物的加氢性能.实验结果表明,在Ru-TPPTS中添加铂或钯后,反应活性明显提高,尤其是Ru/Pt-TPPTS双金属催化剂更表现出显著的双金属协同效应.在pH2=1.0MPa,70℃,反应2h的条件下,双金属催化剂0.50Ru/0.50Pt-TPPTS催化对-氯硝基苯加氢生成对-氯苯胺的反应转化率达到100%.对于取代基和取代位置不同的一些卤代硝基苯加氢,该双金属催化剂也表现出很高的催化活性和生成卤代苯胺的选择性,脱卤反应的程度很小.     

Ni-Ce-P非晶态合金催化剂用于氯代硝基苯液相加氢制氯代苯胺

 采用化学还原法制备了Ni-Ce-P非晶态合金催化剂,用X射线能谱、 X射线衍射、 选区电子衍射、 透射电子显微镜和差热分析等方法对催化剂的组成、结构、形貌及热稳定性进行了表征,讨论了Ni-Ce-P非晶态合金催化剂的催化性能和结构的关系,并以氯代硝基苯液相加氢合成氯代苯胺为探针反应考察了所制备催化剂的加氢性能. 研究结果表明,在不加脱卤抑制剂的情况下,在110 ℃下反应时所选4种反应物的转化率均可达99.8%, 脱卤率小于1.8%, 且Ni-Ce-P非晶态合金的活性为Ni-P非晶态合金催化剂的2倍,表现出较高的加氢性能和抑制脱卤性能.     

载体对负载型Ni-B催化剂催化2-乙基蒽醌加氢制H2O2反应性能的影响

采用还原剂浸渍法将Ni-B非晶态合金负载到SiO2,γ-Al2O3和活性炭(AC)上,以2-乙基蒽醌选择加氧制H2O2为探针反应,系统研究了载体对Ni-B非晶态合金催化剂结构、热稳定性和催化性能的影响.结果表明,将Ni-B负载到载体上后,其晶化温度显著提高,各催化剂热稳定性依次为Ni-B/AC＞Ni-B/SiO2＞Ni...     

用卤代乙酸酯与酰卤的格氏偶合反应合成新戊酰乙酸乙酯

卤代乙酸酯与Mg反应形成格氏试剂后,易与酯基发生自身偶合,格氏试剂难以分离,因而很少应用于合成。M0riwake报道用卤代乙酸的叔丁酯代替乙酯,并与酮一起加入到Mg/     

卤代苯和卤代萘用三氧化硫进行的磺化反应

前文报道了各种甲氧基萘用三甲硅基氯磺酸酯在非极性溶剂中进行的磺化反应。本文研究了四种卤代苯和六种卤代萘用三氧化硫在非极性溶剂中进行的磺化反应。卤代芳香化合物用氯磺酸,浓硫酸及发烟硫酸进行的磺化反应已有报道。在芳香化合物的亲电取代反应中,卤素的定位效应取决于以下两个因素。首先,负的诱导效应体现为F>Cl>Br>I,且对邻位的影响远大于对位的影响。而正的共轭效应亦体现为F>Cl>Br>I,对对位的影响最大。单取代卤苯在浓硫酸中进行磺化反应,几乎专一地发生在4—位上。说明尽管卤素降低了芳香环上的电子云密度,但仍为邻对位定位基。三氧化硫(SO_3)是最剧烈的磺化剂,溶于非极性溶剂二氯甲烷中,既减少了付反应,又可在室温下进行高效率的磺化反应。     

氧化铁负载铂纳米簇催化卤代硝基苯本体氢化性质研究

复相金属催化剂中的载体效应研究具有重要意义。我们以结构不同的氧化铁载体吸附"非保护型"Pt金属纳米簇制备了具有相同Pt纳米簇的Pt/Fe_3O_4、Pt/γ-Fe_2O_3和Pt/α-Fe_2O_3催化剂,考察了其在无溶剂条件下(本体条件)催化邻氯硝基苯(o-CNB)选择性氢化反应的性能,发现三种铂/氧化铁催化剂的催化选择性远高于商购铂/碳催化剂,Pt/γ-Fe_2O_3和Pt/α-Fe_2O_3的催化选择性明显高于Pt/Fe_3O_4,而Pt/Fe_3O_4的催化活性较Pt/α-Fe_2O_3高50%。铂/氧化铁对不同卤代硝基苯的本体选择性氢化反应表现出优良的催化性能,相应卤代苯胺产物的选择性均可达到99%以上。考察了温度、氢气压力对Pt/Fe_3O_4催化o-CNB本体氢化性能的影响。本工作为理解氧化铁负载金属纳米簇催化剂的特殊催化性质,进而发展高效金属纳米簇基催化体系提供了新的基础。     

卤代异羟肟酸钴（Ⅱ）配合物催化氧化二甲苯的研究

以空气为氧源,一系列卤代异羟肟酸钴(Ⅱ)配合物(CoL21～CoL29)为催化剂,研究了其液相氧化对二甲苯生成对甲苯甲酸的性能和规律,比较了配合物中引入卤原子的种类与位置对催化剂催化活性的影响,考察了氯代异羟肟酸钴(Ⅱ)配合物CoL23催化氧化不同配比的混合二甲苯的选择性.结果表明:在反应温度为110℃、催化剂浓度为1.0 mmol/L、空气流速为2.4 L/L/min的条件下,1.5 h内二氯代异羟肟酸配体的钴(Ⅱ)配合物的催化活性顺序是CoL23＞CoL24＞CoL27＞CoL25＞CoL26,1.5～4 h的催化活性顺序是CoL23＞CoL24＞COL24＞CoL25＞CoL26单卤代异羟肟酸配体的钴(Ⅱ)配合物催化活性顺序是CoL29＞CoL28＞CoL21.当混合二甲苯中各异构体比例为5:3:2(对:邻:间)时,反应有较高的选择性,并能析出纯度达96.7%的对甲苯甲酸固体.     

Ni-B非晶态合金催化苯丙酮酸加氢合成苯丙氨酸

通过化学还原法制备了纳米非晶态Ni-B合金催化剂,考察了其对苯丙酮酸胺化加氢合成苯丙氨酸的催化性能.结果表明,相对于传统雷尼镍和漆原镍催化剂,非晶态合金催化剂表现出更为优异的活性和选择性,并且当非晶态Ni-B合金负载在SiO2载体上时,其活性和选择性均得到较大提高(高达97.67%).非晶态合金催化剂对苯丙氨酸合成反应表现出较好活性和选择性的原因主要是硼提供部分电子给镍的效应以及非晶态合金颗粒的纳米尺寸效应.     

Hydrogenation of phenylpyruvic acid to phenylalanine catalyzed by Ni-B/SiO2

Phenylalanine （Phe） is a significant amino acid that cannot be synthesized by human themselves but must be taken from environment. It was initially found that the nanosized amorphous Ni-B/SiO2 alloy prepared by the chemical reduction method was an effective catalyst for the preparation of Phe from phenylpyruvic acid （PPA） by amination and hydrogenation. It has been found that the amorphous Ni-B/SiO2 alloy catalyst exhibits superior activity and selectivity to the traditional catalysts Raney Ni and Urushibara nickel. The effects of reaction time, amounts of catalysts and ammonia solution, reaction temperature, and H2 pressure on the reaction have been investigated systematically. The results indicated that the yield of Phe was 97.9%, and the selectivity for Phe reached 98.9% when the reaction was carried out for 3 h at 333 K and 2.0 MPa of H2 with m（Cat.） ： m（PPA） = 0.6 ： 1.0 and n（NH3） ： n（PPA） = 3 ： 1. The catalysts were characterized by XRD, AAS, XPS, BET, and TEM, and the relationship between the catalyst structure and the catalytic activity was discussed in detail. It was found that the reason why Ni-B/SiO2 amorphous alloy catalyst was much more active for the preparation of Phe could be accounted for by the presence of electron-rich Ni due to electron donation from alloying B; the smaller size of Ni-B particles, the larger specific surface area of Ni-B/SiO2.     

Preparation of Uniform Ni-B Amorphous Alloy Catalyst on CNTs and its Performance for Acetylene Selective Hydrogenation

Carbon nanotubes (CNTs) are severely bundled and essentially insoluble in solvent. These properties are generally considered as a significant barrier toward the practical uses of CNTs. Therefore, the functionalization and solubilization of CNTs have recei…     

微波辅助Ni-B/SiO2非晶态催化剂的制备及其在硝基苯加氢中催化性能的研究

采用微波辐射干燥浸渍法获得的Ni2 /SiO2,再由液相KBH4还原制备Ni-B/SiO2非晶态催化剂,在液相硝基苯加氢反应中,该催化剂对苯胺的选择性为100%,催化活性显著高于由传统加热法制备的Ni-B/SiO2.根据XRD、XPS、SEM和氢吸附等表征,两种催化剂具有相似的活性中心本质,催化性能的不同主要归因于分散度的区别.与传统加热法相比,微波加热具有受热均匀以及增强Ni2 与载体SiO2相互结合力的特点,导致Ni-B/SiO2(MW)分散度增加,并能减少催化反应过程中活性相的脱落流失,延长催化剂使用寿命.     

非负载镍催化剂的2-乙基蒽醌加氢活性及其氢吸脱附性质

 分别制备了金属镍粉、兰尼镍、Ni-B非晶态合金及镧掺杂的Ni-B非晶态合金(Ni-B-La)催化剂,研究了催化剂的氢吸附和脱附性质以及对2-乙基蒽醌加氢反应的催化性能. 结果表明,金属镍粉、兰尼镍和Ni-B催化剂表面均具有两种氢吸附位: 弱吸附位和强吸附位. Ni-B-La催化剂表面只有氢的强吸附位,其强吸附氢量与兰尼镍相当. 推测只有氢的强吸附位是2-乙基蒽醌加氢反应的活性中心,并且Ni-B-La催化剂上的强吸附氢较兰尼镍上的更活泼,因而Ni-B-La非晶态合金催化剂对加氢反应的催化活性高于兰尼镍.     

Ni-B/SiO2非晶态催化剂应用于硝基苯液相加氢制苯胺

 考察了Ni－B／SiO2非晶态催化剂在高压液相硝基苯加氢制苯胺反应中的催化活性和选择性．研究表明,该催化剂不仅具有很高的催化活性,而且对苯胺的选择性较高,优于RaneyNi以及其它Ni基催化剂．晶化导致催化剂失活．载体的存在不仅能提高催化剂的分散度,而且能对非晶态结构起稳定化作用;将催化剂保存在乙醇中可保持其活性不变．结合催化剂的表征,讨论了Ni－B／SiO2非晶态催化剂的催化性能与其结构的关系．     

糠醛液相加氢用Mo改性Ni-B/TiO2-Al2O3(S)非晶态合金催化剂

以溶胶-凝胶法制备复合载体TiO2-Al2O3(S)负载非晶态Ni-B合金用于催化糠醛液相加氢反应, 并研究了Mo对催化剂的改性作用. 采用ICP(等离子发射光谱)、DSC(差示扫描量热)、N2吸附、TPR(程序升温还原)和TPD(程序升温脱附)等技术对催化剂进行了表征. 研究结果表明, 与单一氧化铝载体相比, 复合载体负载的Ni-B合金催化性能明显提高, 这是由于在同样的制备条件下, 复合载体负载的Ni-B中Ni含量更高, 同时TiO2分散到了γ-Al2O3的孔中, 堵住了部分细孔, 有利于产物糠醇扩散出来, 防止深度加氢. Mo能提高Ni-B/TiO2-Al2O3(S)的热稳定性, 增大Ni的负载量, 使部分氧化态物种变得易于被还原, 表面出现新的加氢活性中心, 并增加化学吸附中心数, 减弱吸氢强度, 因而显著提高了Ni-B/TiO2-Al2O3(S)的活性; Mo添加使Ni-B/TiO2-Al2O3(S)的平均孔径及总孔容均增大, 有利于产物糠醇扩散出来, 还能使糠醇更易从催化剂的表面脱附, 防止其深度加氢, 因而提高了糠醇的选择性. 当Mo含量为1.25%时, 糠醛转化率、糠醇选择性都达到了100%.     

Liquid phase glucose hydrogenation to -glucitol over an ultrafine Ru-B amorphous alloy catalyst

A Ru-B amorphous alloy catalyst in the form of ultrafine particles was prepared by chemical reduction of RuCl₃ with borohydride in aqueous solution, whose amorphous structure was confirmed by XRD, DSC, and SAED. Heating pretreatment resulted in the rapid crystallization and the deep decomposition of the Ru-B amorphous alloy as well as the abrupt decrease in the surface area due to the gathering of small particles at high temperature. XPS spectra revealed that partial electrons transferred from the alloying B to the metallic Ru in the as-prepared Ru-B sample. In comparison with other catalysts, the as-prepared Ru-B amorphous catalyst exhibited excellent activity and perfect selectivity to -glucitol as well as superior lifetime during the liquid phase glucose hydrogenation, showing its potential application in industrial process. The higher activity of the Ru-based catalysts than that of other metal catalysts, such as Co-B and Ni-B amorphous catalysts as well as Raney Ni catalysts, demonstrated that the metallic Ru was more active than both metallic Ni and Co for the glucose hydrogenation. Meanwhile, the Ru-B amorphous catalyst exhibited higher activity than its corresponding crystallized Ru-B and pure Ru powder catalysts, showing the promoting effects of both the amorphous structure and the electronic interaction between the metallic Ru and the alloying B, which was briefly discussed based on the kinetic studies and various characterizations.