聚乙烯吡咯烷酮(PVP)功能化的聚苯乙烯(PS)粒子在SiO2包覆的同时被乙醇/氨水介质溶解, 得到了单分散空心SiO2纳米微球. 该空心SiO2纳米微球的尺寸和形态可以通过PVP, NH4OH和正硅酸乙酯(TEOS)的用量来调节. PVP用量增加导致PS粒子变小, 从而得到较小的空心SiO2纳米微球; NH4OH用量增加, 空心SiO2纳米微球表面变得粗糙; TEOS用量增加, 空心SiO2纳米微球的壳层厚度增加. 包覆(溶解)温度是控制空心SiO2纳米微球形成的最有效手段. 在70 ℃的包覆(溶解)温度下可以获得全部空心的SiO2纳米微球.     

中空SiO_2纳米微球的制备与表征

在乙醇/氨水介质中,将SiO2包覆在聚乙烯吡咯烷酮(PVP)功能化的聚苯乙烯(PS)微粒表面,利用一步法得到了中空纳米二氧化硅微球;研究了影响中空纳米二氧化硅微球形成的主要因素,并探讨了中空纳米SiO2微球的可能形成机理.结果表明,在一定的反应时间下,当氨水用量为0.6 mL、温度为70℃时,可以获得空心结构的SiO2纳米微球;通过控制四乙基原硅酸盐(TEOS)的量可以调节微球的包覆层厚度.     

反应介质pH值和前驱体用量对PSt/TiO_2复合微球结构形态及TiO_2空心微球形貌的影响

首先用聚乙烯亚胺(PEI)对粒径为360 nm的单分散无皂聚苯乙烯(PSt)乳胶粒进行修饰,得到表面荷正电的PSt种子乳液,然后将其滴加到溶有钛酸正丁酯(TBT)的乙醇与水的混合介质中,通过溶胶-凝胶(sol-gel)法制备出了核壳结构PSt/TiO2复合微球,系统研究了体系pH和TBT用量对复合微球结构形态的影响.研究表明,酸性条件不利于核壳结构PSt/TiO2复合微球的形成;当体系pH值为7.2时,可得到包覆完整、TiO2壳层厚度均一的PSt/TiO2复合微球,此后随着体系pH值的升高,包覆厚度逐渐提高;当pH值升高到11.0时,壳层厚度达到最大,但出现了包覆层不完整的复合微球.在固定聚合体系pH为8.5,EtOH/H2O质量比为100/6,表面修饰PSt种子乳液用量为0.5 g(固含量为4%)的条件下,随着TBT用量从0.01 g增加到0.16 g,复合微球壳层厚度从约0 nm逐渐增加到60 nm;当TBT用量增加到0.32 g时,壳层厚度迅速降至12nm,微球表面变得粗糙,并出现大量未包覆微粒;此后随着TBT用量的增加,包覆层厚度逐渐减少,未包覆微球逐渐增多.结果显示,当复合微球中TiO2包覆层达到一定厚度时,经煅烧后才能得到形貌完整的TiO2中空微球.     

种子表面改性法制备核壳结构PSt/SiO_2复合微球

首先采用无皂乳液聚合法合成了表面带负电荷、粒径为360nm的单分散聚苯乙烯(PSt)种子乳液,并以EtOH/H2O混合物为分散介质,利用γ-氨丙基三乙氧基硅烷(KH-550)在25℃下对PSt微球表面进行改性,得到了表面硅烷化并带有正电荷的改性PSt种子乳液,然后在碱性条件下加入原硅酸乙酯(TEOS)使其和微球进行共水解与共缩聚,制备出了核壳结构PSt/SiO2复合微球,并利用电镜对复合微球的结构形态进行了表征.研究表明,PSt种子乳液改性时体系的zeta电位随着KH-550用量的增加而升高,当KH-550用量为PSt种子重量的1/3时,体系的zeta电位从原来的-34.5mV升高到了38mV,达到对PSt微球表面改性的最佳值;在制备PSt/SiO2复合微球时,TEOS水解缩聚形成的SiO2包覆到改性微球上的量随着反应时间的延长而增加,反应24h时达到97.9%的最大值;随介质中水含量的增加,吸附到复合微球表面上的SiO2纳米颗粒逐渐减少,复合微球表面逐渐变得光滑,当EtOH/H2O质量比降低到60/28.5时,得到结构均一、壳层厚度为35nm的核壳结构PSt/SiO2复合微球。     

制备方法对模板法制备SiO_2中空微球形貌的影响

模板法是制备无机中空微球的重要方法之一.首先通过苯乙烯和甲基丙烯酸的无皂乳液聚合法制得表面含羧基、粒径为360nm的单分散聚苯乙烯(PSt)乳胶粒,并以此为模板,分别采用表面改性-前驱体水解法(PHC)和SiO2纳米颗粒层层自组装法(LBL),制备出了不同壳层厚度的PSt/SiO2核壳结构复合微球,然后经500℃煅烧4h,得到SiO2中空微球.利用透射电镜和扫描电镜对微球结构形态进行了表征.研究表明,首先利用γ-氨丙基三乙氧基硅烷(KH-550)对PSt模板微球进行表面改性、然后再在乙醇-水混合介质中进行原硅酸乙酯(TEOS)水解与缩合反应的PHC法,是制备PSt/SiO2核壳结构复合微球的简便方法,复合微球经煅烧可制得表面均匀、结构致密、壳层厚度和形貌可控的SiO2中空微球;而LBL法制备PSt/SiO2核壳结构复合微球的工艺复杂,煅烧后所得SiO2中空微球结构疏松,易于破碎.     

N掺杂空心TiO2微球的合成与表征

采用无皂乳液聚合合成的聚苯乙烯(PS)微球为模板、氨水/三乙醇胺为催化体系, 通过溶胶-凝胶方法合成了PS/TiO₂(核/壳)复合微球, 然后通过煅烧制备了N掺杂、锐钛型空心TiO₂微球. 在反应体系中三乙醇胺扮演双重角色, 既是TiO₂生成及包覆过程的抑制剂又是空心TiO₂微球的N掺杂剂. 改变氨水、三乙醇胺和钛酸正丁酯用量可控制TiO₂壳的形态和尺寸. 氨水用量增加, PS/TiO₂复合微球的壳表面变得粗糙|三乙醇胺用量增加, 壳表面变得光滑|钛酸正丁酯用量提高导致壳层变厚. 改变三乙醇胺用量可调节空心TiO₂微球中的N掺杂量|N掺杂空心TiO₂微球具有可见光响应和光催化作用.     

磁性SiO2/PSt中空复合微球的细乳液法制备及表征

采用双原位细乳液聚合工艺,将疏水改性的磁性纳米粒子(MNP)加入到细乳液反应体系的油相中,利用增长的聚合物和单体TEOS之间的相分离原理,实现了聚合物的生成和TEOS的水解缩合同步进行,一步获得了磁性SiO2/PSt中空复合微球.通过红外光谱(FTIR)、透射电镜(TEM)、热重差热分析(TGA/DSC)和振动磁强计(VSM)对中空复合微球进行了表征.结果表明,制备的SiO2/PSt中空复合微球的尺寸范围为300～600 nm,当加入磁性纳米粒子后,得到的磁性SiO2/PSt中空微球保持了原来的中空结构,中空复合微球内腔的大小可以通过改变单体TEOS的加入量来控制.SiO2/PSt中空微球对磁性纳米粒子的包封率达到了86%.磁性SiO2/PSt中空复合微球具有超顺磁性,饱和磁强度值为14.7 emu/g.     

介孔SiO_2/Fe_3O_4中空磁性复合微球的制备与表征

采用多步包覆法在自制的240nm的单分散SiO2微球表面进行β-FeOOH的包覆,在5wt%的NaOH溶液中去除核心SiO2后,得到β-FeOOH纳米结构空心微球。将单分散的β-FeOOH空心球作为内核,十六烷基三甲基溴化铵(CTAB)为模板剂,正硅酸乙酯(TEOS)为硅源,经水解缩聚反应得到空心核壳复合微球。在空气中焙烧(500℃,5h)对样品去除模板剂,并在还原气氛(5%H2/95%Ar,350℃,3h)下焙烧得到介孔SiO2/Fe3O4中空磁性复合微球。结果表明,所制得的介孔SiO2/Fe3O4中空磁性复合微球中的Fe3O4层厚度约60nm,是由Fe3O4纳米棒搭接而成的三维网络结构,复合微球的整体平均直径为390nm,比表面积较高约693m2·g-1,孔体积为0.63cm3·g-1,平均孔径为3.6nm,其饱和磁化强度可达13.6emu·g-1,同时较低的矫顽力(50Oe)有利于颗粒的再分散。     

单分散α-Fe_2O_3纳米结构空心亚微球的制备及表征

采用一种新的溶液生长法结合多步包覆法在自制的不同粒径SiO2单分散亚微球表面包覆不同厚度的β-FeOOH涂层,得到单分散β-FeOOH/SiO2核壳结构亚微球.实验结果表明,SiO2核心颗粒尺寸对表面涂层的形态和包覆均匀性有很大影响.当SiO2核心颗粒的平均粒径为250 nm左右时,β-FeOOH表面涂层均匀,颗粒间团聚较少,一次包覆后涂层厚度约为35 nm.涂层中β-FeOOH纳米棒的尺寸随着所选SiO2核心颗粒粒径的增大而相应增大.经多次包覆能够显著提高涂层的厚度,3次包覆后β-FeOOH表面涂层厚约100 nm.β-FeOOH/SiO2核壳结构亚微球与质量分数5%的NaOH溶液反应后,于600℃焙烧2 h得到了单分散α-Fe2O3空心微球.单分散α-Fe2O3空心亚微球表层是由α-Fe2O3纳米棒搭建而成的三维网络结构,α-Fe2O3纳米棒的尺寸与核壳结构中β-FeOOH纳米棒的尺寸基本一致.     

静电层层自组装制备聚苯乙烯微球(核)/MCM-41纳米粒子(壳)阶层结构复合微粒

采用聚苯乙烯磺酸钠(PSS)和聚二烯丙基二甲基氯化铵(PDDA)两种聚电解质, 通过静电层层自组装成功地将MCM-41介孔二氧化硅纳米粒子包覆到聚苯乙烯(PS)微球表面. 实验结果表明, 当以尺寸为1.4 μm的PS微球为核时, 包覆了两个聚电解质双层(PDDA/PSS)2的PS(PDDA/PSS)2(PDDA/MCM-41)复合结构微粒与包覆了一个聚电解质双层(PDDA/PSS)的PS(PDDA/PSS)(PDDA/MCM-41)复合结构微粒相比, 复合结构微粒之间的交联程度降低, 但是MCM-41纳米粒子在聚苯乙烯微球表面的包覆都比较松散, 且产物中存在大量杂质. 而当以尺寸为5 μm的聚苯乙烯微球为核时, MCM-41纳米粒子紧密地包覆在聚苯乙烯微球表面, 复合结构微粒之间只有少量桥连物, 且产物中杂质很少.     

PS/TiO2复合纳米微球的制备和结构表征

无机纳米微粒具有特殊的物理化学性能 ,近年来在摩擦学领域中受到越来越多的重视 .由于无机纳米微粒难以分散于润滑基础油中 ,故其作为润滑材料主要用作聚合物填料和润滑脂添加剂 .为了改善其在基础油中的分散性 ,需要对无机纳米微粒进行表面改性 ,制备成有机无机复合纳米微粒 ,从而使它们能够用作润滑油添加剂 .目前有机小分子表面修饰无机纳米微粒的摩擦学性能已有报导 [1－ 3],但是聚合物修饰无机纳米微粒的研究较少 ,并且大多是采用高分子（如 PVK,PVA等）直接包埋的方法 ,用这种方法制得的微粒 ,粒径差别较大,性能不太稳定 .　　本…     

Fabrication of Fluorescent Porphyrin/Polystyrene Composite Nanospheres by Electrospinning

Fluorescent polystyrene(PS)/porphyrin(TPPA) composite nanospheres were successfully fabricated by electrospinning. The SEM images clearly show that owing to adding TPPA in PS, the averaged diameter of the composite nanospheres became smaller, from 1500 to 580 nm. Fourier-transform infrared(FTIR) spectra determined the chemical composition of the resulting PS/TPPA composite nanospheres. The photoluminescent(PL) spectral analysis indicates that the peak position of the composite nanospheres in either solid st...     

Development of high magnetization Fe3O4/polystyrene/silica nanospheres via combined miniemulsion/emulsion polymerization

Monodispersed, hydrophilic, superparamagnetic magnetic nanospheres with a high fraction of magnetite were synthesized by combining modified miniemulsion/emulsion polymerization and sol-gel technique for the first time. The surface of the nanospheres was coated by a silica layer with controlled thickness. Transmission electron microscopy experimental results showed well-proportioned, equal-sized, magnetite/polystyrene (Fe3O4/PS) nanospheres with a thin silica shell. Based on the TGA data, the fraction of magnetite in the Fe3O4/PS nanospheres core was estimated to be 80 wt %. Magnetization measurements indicated that the superparamagnetic nature of the nanospheres had high saturation magnetization of 40 emu/g at 300 K. The procedures of the novel synthesis are described in detail. Also discussed are the mechanisms of the novel combined miniemulsion/emulsion polymerization processes.     

悬浮液气-液界面二元胶体颗粒的漂浮组装机理

提出一种在悬浮液气-液界面漂浮组装亚微米单分散聚苯乙烯(PS)微球和纳米SiO2颗粒二元胶粒晶体的新方法, 并系统研究了漂浮组装机理. 研究表明, 聚苯乙烯微球和二氧化硅两种胶体颗粒在悬浮液气-液界面的漂浮组装是以PS微球的组装为主导的. 在一定PS微球相浓度范围内, 悬浮液中PS 微球与SiO2颗粒的初始体积配比基本不影响PS微球有序组装的形成. PS微球粒径在150-500 nm时易于形成有序排列, 较小或较大粒径的PS微球难以形成有序排列. SiO2颗粒的组装是一种以PS微球为“基底”的沉积过程. 二元胶粒晶体中SiO2颗粒的体积分数由其在混合悬浮液中的相浓度所决定.     

聚苯乙烯球模板法制备二氧化钛纳米环

TiO2 nanorings were synthesized using the polystyrene nanospheres of 85 nm prepared by micro-emulsion polymerization as template. The result TiO2 nanorings were characterized by FE-SEM and XRD. Results showed that the inner diameter of the TiO2 nanorings matched size of the polystyrene nanospheres used, and the thickness with nanometer size depended on that of the TiO2 gel coated on the PS surface.     

A novel method to synthesize polystyrene nanospheres immobilized with silver nanoparticles by using compressed CO2

In this work, a novel route to synthesize polymer/metal composite nanospheres has been proposed. This method combines the advantages that the polymer chains collapse and entangle in the presence of compressed CO(2), which acts as antisolvent, and the metal nanoparticles and polymers can be precipitated simultaneously from micellar solutions by the easy control of CO(2) pressure. Ag/polystyrene (PS) nanocomposites have been successfully prepared using this method. The transmission electronic micrographs (TEM) of the obtained nanocomposites show that the smaller Ag nanoparticles are immobilized by PS nanospheres of about 50 nm; the phase structure was characterized by X-ray diffraction (XRD). The Ag/PS nanocomposites show absorption properties at a wavelength of approximately 417 nm. The results of X-ray photoelectron spectra (XPS) and FT-IR spectra indicate that there is no chemical linkage or strong interaction between PS and Ag nanoparticles in the resultant products. This method has many potential advantages for applications and may easily be applied to the preparation of a range of inorganic/ polymer composite nanoparticles.     

H4SiW12O40/TiO2/SiO2复合光催化剂的制备及性能研究

溶胶-凝胶法制备了TiO2/S iO2光催化剂,利用所得TiO2/S iO2光催化剂为基体,浸渍烧结法制备了H4S iW12O40/TiO2/S iO2表面负载修饰型复合光催化剂。TG-DSC、XRD、SEM、BET对催化剂的物化结构进行了表征,分析了TiO2和H4S iW12O40催化活性组分在S iO2载体表面上的键联机理。光催化性能测试是以低浓度酸性品红染料的水溶液为降解目标物,试验结果表明H4S iW12O40的负载修饰可以改进TiO2/S iO2光催化剂的催化活性,酸性品红的降解效率最高可以增加45%。     

Size‐controlled/Surface‐Functionalized Polystyrene Nanospheres with Good Biocompatibility and High Encapsulation Efficiency of Cyclosporin A via Miniemulsion Polymerization in One Step

In this paper, size‐controlled and surface‐functionalized RhB‐labeled and Cyclosporin A (CsA)‐loaded polystyrene (PS) nanospheres were successfully synthesized via miniemulsion polymerization. The biophysical properties of PEG functionalized PS nanospheres from protein adsorption, blood compatibility, cell compatibility and cell penetrability showed the nanoparticles with high biocompatibility. These results indicated that PEG modified PS nanospheres showed outstanding properties as low size distribution (0.164), high encapsulation efficiency (98.3%), long re‐calcification time (50% than positive control), low hemolysis ratio (3.19%) and high cell viability (95.3%). This work could be used as a good drug delivery system for CsA.