纤维素纳米晶模板法制备多级孔炭材料及其电化学性能

以纤维素纳米晶(CNC)为模板,酚醛树脂为碳源,KOH为活化剂,通过高温碳化制备了多级孔炭材料.采用透射电子显微镜(TEM)、扫描电子显微镜(SEM)和X射线光电子能谱仪(XPS)等手段对合成的一系列炭材料进行了表征.结果表明,前驱体中CNC的降解会形成与CNC直径相当的介孔,KOH活化则会导致炭材料产生大量的微孔和大孔,以及部分4 nm左右较小尺度的介孔,所制备炭材料呈现明显的多级孔特性,其比表面积达554.7 m²/g,总孔体积为0.323 cm³/g.以CNC为模板,KOH活化的炭材料作为电极材料时,在1.0 A/g电流密度下其比电容达202.8 F/g,当电流密度升高至40.0 A/g时,其电容保持率仍达69%,表明该炭材料具有优异的倍率性能;由该电极材料组装的超级电容器在10000次充放电循环后,电容保持率达95%以上,具有良好的循环稳定性.     

Hierarchical Activated Mesoporous Phenolic‐Resin‐Based Carbons for Supercapacitors

A series of hierarchical activated mesoporous carbons (AMCs) were prepared by the activation of highly ordered, body‐centered cubic mesoporous phenolic‐resin‐based carbon with KOH. The effect of the KOH/carbon‐weight ratio on the textural properties and capacitive performance of the AMCs was investigated in detail. An AMC prepared with a KOH/carbon‐weight ratio of 6:1 possessed the largest specific surface area (1118 m² g^?1), with retention of the ordered mesoporous structure, and exhibited the highest specific capacitance of 260 F g^?1 at a current density of 0.1 A g^?1 in 1 M H₂SO₄ aqueous electrolyte. This material also showed excellent rate capability (163 F g^?1 retained at 20 A g^?1) and good long‐term electrochemical stability. This superior capacitive performance could be attributed to a large specific surface area and an optimized micro‐mesopore structure, which not only increased the effective specific surface area for charge storage but also provided a favorable pathway for efficient ion transport.     

Hierarchical porous carbon derived from coal-based carbon foam for high-performance supercapacitors

Hierarchical porous carbon (HPC) from bituminous coal was designed and synthesized through pyrolysis foaming and KOH activation. The obtained HPC (NCF-KOH) were characterized by a high specific surface area (S_BET) of 3472.41 m²/g, appropriate mesopores with V_mes/V_total of 57%, and a proper amount of surface oxygen content (10.03%). This NCF-KOH exhibited a high specific capacitance of 487 F/g at 1.0 A/g and a rate capability of 400 F/g at 50 A/g based on the three-electrode configuration. As an electrode for a symmetric capacitor, a specific capacitance of 299 F/g at 0.5 A/g was exhibited, and the specific capacitance retained 96% of the initial capacity at 5 A/g after 10,000 cycles. Furthermore, under the power density of 249.6 W/kg in 6 mol/L KOH, a high energy density of 10.34 Wh/kg was obtained. The excellent charge storage capability benefited from its interconnected hierarchical pore structure with high accessible surface area and the suitable amount of oxygen-containing functional groups. Thus, an effective strategy to synthesize HPC for high-performance supercapacitors serves as a promising way of converting coal into advanced carbon materials.     

Comprehensive utilization of dairy manure to produce glucose and hierarchical porous carbon for supercapacitors

Dairy manure, one of the most abundant agricultural wastes generated in livestock farming, was pretreated with KOH aqueous solution to relieve the constraint of lignin, thus facilitating cellulose hydrolysis. The generated black liquor waste was used to prepare porous carbon. Glucose yield of 261 g/kg was obtained from dairy manure pretreated in 0.73 wt% HCl aqueous solution, much higher than that obtained from crude dairy manure (116 g/kg). The generated black liquor, mainly containing lignin and KOH, was employed to prepare porous carbon via a self-templating method. The obtained material had a three-dimensional (3D) hierarchical structure and was applied for supercapacitors. Good capacitance of 202 F/g was obtained in a two-electrode system with 6 M KOH electrolyte. The porous carbon-based electrode showed excellent cycling stability with retention of 100% after 3000 galvanostatic charge–discharge (GCD) cycles. This work provides a scalable strategy for comprehensive utilization of lignocellulosic biomass resources.     

One-step synthesis of biomass derived O,N-codoped hierarchical porous carbon with high surface area for supercapacitors

We report a convenient method to synthesize O, N-codoped hierarchical porous carbon by one-step carbonization of the mixture of KHCO₃, urea and alginic acid. Benefiting from KHCO₃ and urea synergistic effect, the obtained O, N-codoped hierarchical porous carbon (NPC-700) material has a well-developed interconnected porous framework with ultrahigh specific surface area (2846 m²/g) and massive heteroatoms functional groups. Consequence, such porous carbon displays high specific capacitance (324 F/g at 1 A/g), excellent rate performance (212 F/g at 30 A/g) and good electrochemical stabilization in 6 mol/L KOH solution. More importantly, the assembled NPC-700//NPC-700 symmetrical supercapacitor can achieve a high energy density of 18.8 Wh/kg and good electrochemical stabilization in 1 mol/L Na₂SO₄ solution. This process opens up a new way to design heteroatoms-doped hierarchical porous carbon derived from biomass materials for supercapacitors.     

基于聚多巴胺的氮掺杂碳材料的制备及其电化学性能

多孔碳材料由于高的比表面积、优异的电子传导率、良好的化学稳定性等优点在超级电容器电极材料领域被广泛研究。 碳材料的组成及表面孔结构直接影响其电化学性能,为进一步提高碳材料的电容性能,本文首次以聚多巴胺球为前体,KOH为活化剂,通过高温碳化成功制备了良好电化学性能的氮掺杂多孔碳材料。 通过扫描电子显微镜(SEM)、透射电子显微镜(TEM)、 X射线粉末衍射(XRD)、傅里叶变换红外光谱(FT-IR)、X射线光电子能谱(XPS)和Raman光谱等对所制备的氮掺杂多孔碳材料进行了形貌及结构组成的表征。 在6 mol/L KOH电解液中, 采用循环伏安、恒电流充放电对多孔碳材料的电化学性能进行了研究。 结果表明,由于双电层电容和赝电容的协同作用,在电流密度为1 A/g时,材料的比电容可达269 F/g,充放电循环1000圈后电容仍可保留初始值的93.5%。     

Core–Shell Carbon‐Coated CuO Nanocomposites: A Highly Stable Electrode Material for Supercapacitors and Lithium‐Ion Batteries

Herein we present a simple method for fabricating core–shell mesostructured CuO@C nanocomposites by utilizing humic acid (HA) as a biomass carbon source. The electrochemical performances of CuO@C nanocomposites were evaluated as an electrode material for supercapacitors and lithium‐ion batteries. CuO@C exhibits an excellent capacitance of 207.2 F g^?1 at a current density of 1 A g^?1 within a potential window of 0–0.46 V in 6 M KOH solution. Significantly, CuO electrode materials achieve remarkable capacitance retentions of approximately 205.8 F g^?1 after 1000 cycles of charge/discharge testing. The CuO@C was further applied as an anode material for lithium‐ion batteries, and a high initial capacity of 1143.7 mA h g^?1 was achieved at a current density of 0.1 C. This work provides a facile and general approach to synthesize carbon‐based materials for application in large‐scale energy‐storage systems.     

Excellent Capacitive Performance of a Three‐Dimensional Hierarchical Porous Graphene/Carbon Composite with a Superhigh Surface Area

Three‐dimensional hierarchical porous graphene/carbon composite was successfully synthesized from a solution of graphene oxide and a phenolic resin by using a facile and efficient method. The morphology, structure, and surface property of the composite were investigated intensively by a variety of means such as scanning electron microscopy (SEM), transmission electron microscopy (TEM), N₂ adsorption, Raman spectroscopy, and Fourier transform infrared spectroscopy (FTIR). It is found that graphene serves as a scaffold to form a hierarchical pore texture in the composite, resulting in its superhigh surface area of 2034 m²g^?1, thin macropore wall, and high conductivity (152 S m^?1). As evidenced by electrochemical measurements in both EMImBF₄ ionic liquid and KOH electrolyte, the composite exhibits ideal capacitive behavior, high capacitance, and excellent rate performance due to its unique structure. In EMImBF₄, the composite has a high energy density of up to 50.1 Wh kg^?1 and also possesses quite stable cycling stability at 100 °C, suggesting its promising application in high‐temperature supercapacitors. In KOH electrolyte, the specific capacitance of this composite can reach up to an unprecedented value of 186.5 F g^?1, even at a very high current density of 50 A g^?1, suggesting its prosperous application in high‐power applications.     

Heteroatom‐Doped Porous Carbon Nanosheets: General Preparation and Enhanced Capacitive Properties

High‐performance electrical double‐layer capacitors (EDLCs) require carbon electrode materials with high specific surface area, short ion‐diffusion pathways, and outstanding electrical conductivity. Herein, a general approach combing the molten‐salt method and chemical activation to prepare N‐doped carbon nanosheets with high surface area (654 m² g^?1) and adjustable porous structure is presented. Owing to their structural features, the N‐doped carbon nanosheets exhibited superior capacitive performance, demonstrated by a maximum capacitance of 243 F g^?1 (area‐normalized capacitance up to 37 μF cm^?2) at a current density of 0.5 A g^?1 in aqueous electrolyte, high rate capability (179 F g^?1 at 20 A g^?1), and excellent cycle stability. This method provides a new route to prepare porous and heteroatom‐doped carbon nanosheets for high‐performance EDLCs, which could also be extended to other polymer precursors and even waste biomass.     

A hierarchical porous carbon membrane from polyacrylonitrile/polyvinylpyrrolidone blending membranes: Preparation,characterization and electrochemical capacitive performance

Novel hierarchical porous carbon membranes were fabricated through a simple carbonization procedure of well-defined blending polymer membrane precursors containing the source of carbon polyacrylonitrile (PAN) and an additive of polyvinylpyrrolidone (PVP), which was prepared using phase inversion method. The as-fabricated materials were further used as the active electrode materials for supercapacitors. The effects of PVP concentration in the casting solution on structure feature and electrochemical capacitive performance of the as-prepared carbon membranes were also studied in detail. As the electrode material for supercapacitor, a high specific capacitance of 278.0 F/g could be attained at a current of 5 mA/cm² and about 92.90% capacity retention could be maintained after 2000 charge/discharge cycles in 2 mol/L KOH solution with a PVP concentration of 0.3 wt% in the casting solution. The facile hierarchical pore structure preparation method and the good electrochemical capacitive performance make the prepared carbon membrane particularly promising for use in supercapacitor.     

A hierarchical porous carbon membrane from polyacrylonitrile/polyvinylpyrrolidone blending membranes:Preparation,characterization and electrochemical capacitive performance

Novel hierarchical porous carbon membranes were fabricated through a simple carbonization procedure of well-defined blending polymer membrane precursors containing the source of carbon polyacrylonitrile （PAN） and an additive of polyvinylpyrrolidone （PVP）, which was prepared using phase inversion method. The as-fabricated materials were further used as the active electrode materials for supercapacitors. The effects of PVP concentration in the casting solution on structure feature and electrochemical capacitive performance of the as-prepared carbon membranes were also studied in detail. As the electrode material for supercapacitor, a high specific capacitance of 278.0 F/g could be attained at a current of 5 mA/cm2 and about 92.90% capacity retention could be maintained after 2000 charge/discharge cycles in 2 mol/L KOH solution with a PVP concentration of 0.3 wt% in the casting solution. The facile hierarchical pore structure preparation method and the good electrochemical capacitive performance make the prepared carbon membrane particularly promising for use in supercapacitor.     

KOH‐Activated Porous Carbons Derived from Chestnut Shell with Superior Capacitive Performance

Porous carbons (PC) were prepared from a waste biomass named chestnut shell via a two‐step method involving carbonization and KOH activation. The morphology, pore structure and surface chemical properties were investigated by scanning electron microscopy (SEM), N₂ sorption, Raman spectroscopy, X‐ray diffraction (XRD) and X‐ray photoelectron spectroscopy (XPS). The carbons have been evaluated as the electrode materials for supercapacitors by a two‐electrode system in 6 mol/L KOH electrolyte. Benefiting from the porous texture, high surface area and high oxygen content, the PCs derived from chestnut shell have exhibited high specific capacitance of 198.2 (PC‐1), 217.2 (PC‐2) and 238.2 F·g^?1 (PC‐3) at a current density of 0.1 A·g^?1, good rate capability of 55.7%, 56.6% and 54.9% in a range of 0.1–20 A·g^?1 and high energy density of 5.6, 6.1 and 6.7 Wh·kg^?1, respectively. This is believed to be due to electric double layer capacitance induced by the abundant micropores and extra pseudo‐capacitance generated by oxygen‐containing groups. At a power density of 9000 Wh·kg^?1, the energy density is 3.1, 3.5 and 3.7 Wh·kg^?1 for PC‐1, PC‐2 and PC‐3, respectively, demonstrating the potential of the carbons derived from chestnut shells in energy storage devices.     

From interpenetrating polymer networks to hierarchical porous carbons for advanced supercapacitor electrodes

A novel and effective strategy to fabricate hierarchical porous carbons for supercapacitors is developed via in-situ activation of interpenetrating polymer networks obtained from simultaneous polymerization of the monomers for two polymeric networks.     

Preparation of nitrogen doped clews-like carbon materials and their application as the electrode in supercapacitor

Nitrogen doped clews-like hierarchical porous carbon materials, fabricated by means of a one-pot hydrothermal reaction and post treatment, exhibit superior supercapacitive performances.     

Synthesis of Nanoporous Carbon–Cobalt‐Oxide Hybrid Electrocatalysts by Thermal Conversion of Metal–Organic Frameworks

Nanoporous carbon–cobalt‐oxide hybrid materials are prepared by a simple, two‐step, thermal conversion of a cobalt‐based metal–organic framework (zeolitic imidazolate framework‐9, ZIF‐9). ZIF‐9 is carbonized in an inert atmosphere to form nanoporous carbon–metallic‐cobalt materials, followed by the subsequent thermal oxidation in air, yielding nanoporous carbon–cobalt‐oxide hybrids. The resulting hybrid materials are evaluated as electrocatalysts for the oxygen‐reduction reaction (ORR) and the oxygen‐evolution reaction (OER) in a KOH electrolyte solution. The hybrid materials exhibit similar catalytic activity in the ORR to the benchmark, commercial, Pt/carbon black catalyst, and show better catalytic activity for the OER than the Pt‐based catalyst.     

Sub-nanopores-containing N,O-codoped porous carbon from molecular-scale networked polymer hydrogel for solid-state supercapacitor

A template-free carbonization-activation route is developed to fabricate sub-nanopore-containing porous carbon by using a novel polypyrrole(PPy) hydrogel as a precursor.This design of PPy hydrogel precursor containing molecular-scale grids(diameter～2.0 nm) allows for homogeneous N,O-codoping into the porous carbon scaffold during the pyrolysis process.A subsequent activation step produces activated porous carbons(APCs) with tailored pore structures,which renders the APCs abundant subnanopores on their surface to increase the specific capacitance as extra capacitance sites.Coupled with large specific surface area and abundant heteroatoms,the optimized APC4/1 displays excellent specific capacitance of 379 F/g for liquid-state supercapacitor and 230 F/g for solid-state supercapacitor.The solid-state supercapacitor shows a high energy density of 22.99 Wh/kg at power density of 420 W/kg,which is higher than most reported porous carbon materials and satisfy the urgent requirements of elementary power source for electric vehicles.Moreover,this method can be easily modified to fabricate sub-nanopore-containing porous carbons with preferred structures and compositions for many applications.     

N-doped honeycomb-like porous carbon towards high-performance supercapacitor

Biomass-derived porous carbon with developed pore structure is critical to achieving high performance electrode materials. In this work, we report a grape-based honeycomb-like porous carbon (GHPC) prepared by KOH activation and carbonization, followed by N-doping (NGHPC). The obtained NGHPC exhibits a unique honeycomb-like structure with hierarchically interconnected micro/mesopores, and high specific surface area of 1268 m²/g. As a supercapacitor electrode, the NGPHC electrode exhibits a remarkable specific capacitance of 275 F/g at 0.5 A/g in a three-electrode cell. Moreover, the NGHPC//NGHPC symmetric supercapacitor displays a high energy density of 12.6 Wh/kg, and excellent cycling stability of approximately 95.2% capacitance retention after 5000 cycles at 5 A/g. The excellent electrochemical performance of NGHPC is ascribed to its high specific surface area, honeycomb-like structure and high-content of pyrodinic-N (36.29%). It is believed that grape-based carbon materials show great potential as advanced electrode materials for supercapacitors.     

Effect of surface area and heteroatom of porous carbon materials on electrochemical capacitance in aqueous and organic electrolytes

A series of porous carbon materials with wide range of specific surface areas and different heteroatom contents had been prepared using polyaniline as carbon precursor and KOH as an activating agent. Effect of surface area and heteroatom of porous carbon materials on specific capacitance was investigated thoroughly in two typical aqueous KOH and organic 1-butyl-3- methylimidazolium tetrafluoroborate/acetonitirle electrolytes. The different trends of capacitance performance were observed in these two electrolytes. Electrochemical analyses suggested that the presence of faradaic interactions on heteroatom-enriched carbon materials in organic environment is less significant than that observed in aqueous electrolytes. Thus, in aqueous electrolyte, a balance between surface area and heteroatom content of activated porous carbon would be found to develop a supercapacitor with high energy density. In organic electrolyte, the capacitance performance of porous carbon is strongly dependent on the surface area. The results may be useful for the design of porous carbon-based supercapacitor with the desired capacitive performance in aqueous and organic electrolytes.     

Synthesis of High‐Surface‐Area Nitrogen‐Doped Porous Carbon Microflowers and Their Efficient Carbon Dioxide Capture Performance

Sustainable carbon materials have received particular attention in CO₂ capture and storage owing to their abundant pore structures and controllable pore parameters. Here, we report high‐surface‐area hierarchically porous N‐doped carbon microflowers, which were assembled from porous nanosheets by a three‐step route: soft‐template‐assisted self‐assembly, thermal decomposition, and KOH activation. The hydrazine hydrate used in our experiment serves as not only a nitrogen source, but also a structure‐directing agent. The activation process was carried out under low (KOH/carbon=2), mild (KOH/carbon=4) and severe (KOH/carbon=6) activation conditions. The mild activated N‐doped carbon microflowers (A‐NCF‐4) have a hierarchically porous structure, high specific surface area (2309 m² g^?1), desirable micropore size below 1 nm, and importantly large micropore volume (0.95 cm³ g^?1). The remarkably high CO₂ adsorption capacities of 6.52 and 19.32 mmol g^?1 were achieved with this sample at 0 °C (273 K) and two pressures, 1 bar and 20 bar, respectively. Furthermore, this sample also exhibits excellent stability during cyclic operations and good separation selectivity for CO₂ over N₂.     

Anchoring Iron‐EDTA Complex on Graphene toward the Synthesis of Highly Efficient Fe‐N‐C Oxygen Reduction Electrocatalyst for Fuel Cells

Developing nonprecious carbon electrocatalysts as alternatives to platinum for cathodic oxygen reduction reaction in fuel cells is of significance. Herein, an efficient precursor‐controlled synthesis strategy based on extremely rapid nucleation and deposition process assisted by the liquid nitrogen freeze drying method is explored to anchor cheap iron‐EDTA complex evenly dispersed on graphene to realize microstructural homogeneity of the derived Fe‐N‐C oxygen reduction electrocatalyst. The prepared electrocatalyst possesses excellent performance including high activity with more positive onset and half‐wave potential, such long‐term stability, and anti‐poisoning effect compared to commercial Pt/C. The activity correlates well with the unique sheet‐shaped morphology, high surface area, hierarchical porous structure, and the introduction of Fe‐Nx/C species. Especially, both the assembled practical alkaline and acid fuel cells based on the synthesized cathode catalysts reveal excellent performance with high open‐circuit voltage and power density.