微波辐射对浆态床合成甲醇CuO/ZnO/Al2O3催化剂前驱体晶相转变的影响

在微波辐射条件下,对CuO/ZnO/Al2O3催化剂的沉淀母液进行老化,通过XRD、TG、H2-TPR,FTIR、HR-TEM和XPS对前驱体及催化剂微观结构的进行表征,探讨了CuO/ZnO/Al2O3催化剂前驱体晶相转变过程中微波辐射的作用。结果表明,微波辐射有利于Cu2+取代Zn5(CO3)2(OH)6中Zn2+的同晶取代反应。微波辐射的老化过程中,首先发生Cu2+取代Zn5(CO3)2(OH)6中Zn2+生成(Cu,Zn)5(CO3)2(OH)6的同晶取代反应,并于1.0 h内基本完成;随着老化时间继续延长,主要进行Zn2+取代Cu2(CO3)(OH)2中Cu2+生成(Cu,Zn)2(CO3)(OH)2的同晶取代反应,同时(Cu,Zn)5(CO3)2(OH)6进一步结晶。与常规老化1 h制备的前驱体相比,微波辐射老化1.0 h制备的前驱体含有较多的(Cu,Zn)5(CO3)2(OH)6物相,有助于增强焙烧后CuO/ZnO/Al2O3催化剂中CuO-ZnO协同作用,提高表面铜含量,进而提高CuO/ZnO/Al2O3催化剂在浆态床合成甲醇的催化活性和稳定性,在400 h浆态床合成甲醇评价期间,甲醇时空收率最大达318.9 g.kg-1.h-1,失活率仅为0.11%.d-1。     

以类水滑石CuZnAl为前驱体制备的催化剂对C—N交叉偶联反应的性能研究

以类水滑石Cu Zn Al为前驱体,经600℃焙烧制备了一系列不同Cu/Zn/Al摩尔比的催化剂.对催化剂进行了XRD、BET、AAS及XPS等表征,并测定了该催化剂催化碘苯与咪唑C—N交叉偶联合成1-苯基咪唑的催化性能.结果表明,当Cu/Zn/Al摩尔比为2∶1∶1时,其活性组分Cu分散均匀且催化性能达到最佳.在130℃空气气氛中,KOH存在的条件下,反应24 h,1-苯基咪唑的产率可达到85.8%,实现了C—N偶联反应在多相催化体系中进行.催化剂可回收不产生环境污染,经5次重复使用其催化性能下降不明显.     

有氧气氛中碱金属改性CuAl复合氧化物催化分解N2O的活性

合成了Cu/Al原子比分别为2.0、3.1、4.1的CuAl类水滑石样品,焙烧得到CuAl复合氧化物。在Cu/Al原子比为3.1的CuAl氧化物表面浸渍碱金属盐溶液,制备改性CuAl复合氧化物,用AES、XRD、FT-IR、BET、H₂-TPR、XPS等技术对催化剂进行了结构表征,考察了CuAl复合氧化物组成、碱金属助剂类型和K的前驱物对改性催化剂在有氧气氛中催化分解N₂O活性的影响。结果表明,Na、K、Cs改性CuAl复合氧化物均提高了催化剂活性,但K助剂的增强效应最显著;钾的不同前驱物改性CuAl复合氧化物的催化活性有显著差异,加入碳酸钾、草酸钾提高了催化剂的活性,而加入醋酸钾、硝酸钾反而降低了催化剂活性。优化出的K改性CuAl复合氧化物催化剂在含氧含水气氛的N₂O分解反应中表现出了较高的活性。     

焙烧温度对K-Cu/Zn/La/ZrO2催化剂上异丁醇合成的影响

采用共沉淀法制备了Cu/Zn/La/ZrO₂催化剂,并浸渍K对其进行改性.以合成气合成异丁醇为探针反应,考察了焙烧温度对K-Cu/Zn/La/ZrO₂催化剂合成反应的影响.采用XRD、TG、BET、NH₃-TPD、H₂-TPR、Raman及XPS等手段表征了催化剂的结构和表面性质.结果表明,催化剂体相结构、比表面积与其催化活性没有直接关系;催化剂表面强酸中心的存在不利于异丁醇的生成;Cu-Zn-Zr活性组分间协同作用对催化剂活性影响很大,450 ℃焙烧温度下,Cu-Zn-Zr活性组分间协同作用最强,CuO最容易还原,催化活性最高,此时CO的转化率(物质的量)达到69.47%,醇中异丁醇的选择性(质量分数)为19.09%,甲醇+异丁醇的选择性(质量分数)为95.02%.     

以类水滑石为前驱体的Cu/Zn/Al/(Zr)/(Y)催化剂制备及其催化CO_2加氢合成甲醇的性能

采用共沉淀法合成了Cu:Zn:Al:Zr:Y原子比分别为2:1:1:0:0、2:1:0.8:0.2:0、2:1:0.8:0:0.2和2:1:0.8:0.1:0.1的Cu/Zn/Al/(Zr)/(Y)类水滑石化合物.将前驱体材料在空气中500°C焙烧后得到复合金属氧化物,并将其用于CO2加氢合成甲醇反应.采用X射线衍射(XRD)、热重(TG)分析、N2吸附、氧化亚氮(N2O)反应吸附、氢气程序升温还原(H2-TPR)和H2/CO2程序升温脱附(H2/CO2-TPD)技术对所制备的样品进行表征.结果表明,Zr和Y的引入使得催化剂BET比表面积大幅增加,金属铜的比表面积和分散度均按以下顺序依次增加:Cu/Zn/AlCu/Zn/Al/ZrCu/Zn/Al/YCu/Zn/Al/Zr/Y,然而,强碱位数目占总碱位数目的比例的变化顺序为:Cu/Zn/AlCu/Zn/Al/YCu/Zn/Al/Zr/YCu/Zn/Al/Zr.活性评价结果揭示CO2转化率取决于金属铜的比表面积,甲醇选择性则随强碱位比例的增加而线性增加.因而,Zr和Y的引入有利于甲醇的合成,Cu/Zn/Al/Zr/Y催化剂上的甲醇收率最高.     

溶剂极性对微波辐射老化制备前驱体及CuO/ZnO/Al2O3催化剂结构的影响

在制备CuO/ZnO/Al2O3催化剂的老化过程中,采用微波辐射老化技术,着重研究了溶剂极性对前躯体物相组成,烧后CuO/ZnO/Al2O3催化剂结构及其在浆态床合成甲醇工艺中催化性能的影响。通过XRD、DTG、H2-TPR,FTIR、HR-TEM和XPS对前驱体及催化剂表征表明,沉淀母液在微波辐射条件下进行老化,溶剂的极性对前躯体物相组成及催化剂结构影响显著。随着溶剂极性的增大,Zn2+/Cu2+取代Cu2(CO3)(OH)2/Zn5(CO3)2(OH)6中Cu2+/Zn2+的取代反应增强,使得前躯体中(Cu,Zn)5(CO3)2(OH)6和(Cu,Zn)2(CO3)(OH)2物相的含量增多,结晶度提高,导致烧后CuO/ZnO/Al2O3催化剂中CuO-ZnO协同作用增强,且CuO晶粒减小,表面Cu含量增加,催化剂活性和稳定性提高。水溶剂的极性最大,制备的催化剂活性和稳定性最好,甲醇的时空收率(STY)和平均失活率分别为320 mg.g-1.h-1和0.11%.d-1。     

Ni-Al类水滑石的制备及其Ni/Al2O3加氢脱硫研究

采用共沉淀方法合成了不同Ni/Al比的镍铝类水滑石,将其作为催化剂前驱体,制备了Ni/Al2O3加氢脱硫催化剂.通过X射线衍射法(XRD),程序升温还原(H2-TPR),热重分析(TG),傅里叶变换红外光谱(FT-IR)等技术对催化剂进行了表征.利用10 mL固定床装置在不同温度,压力,体积空速和氢油比条件下对Ni/Al2O3催化剂的加氢脱硫活性进行了评价.结果表明,XRD图和FT-IR图中均出现了Ni-Al类水滑石的特征峰,TG图呈现出两个明显阶段的失重,在Ni-Al2O3-HT的XRD图中最强的衍射角对应单质金属Ni粒子的(111)晶面.脱硫结果显示Ni-Al类水滑石作为前驱体在适当的条件下,FCC汽油的硫含量降至10 ppm以下.类水滑石作为前驱体的Ni/Al2O3加氢脱硫活性很好,说明类水滑石作为前驱体在加氢脱硫领域有好的应用前景.     

Cu/Zn比对微波辐射老化制备CuO/ZnO/Al2O3催化剂结构和活性的影响

在微波辐射条件下,对共沉淀法制备合成甲醇CuO/ZnO/A12O3催化剂前驱体的母液进行老化,通过改变Cu/Zn比,研究了微波辐射对催化剂性能的影响,并结合XRD,FTIR,DTG,H2-TPR,XPS等表征手段,探讨了微波辐射对前驱体物相组成及催化剂微观结构的影响.结果表明:在微波辐射老化条件下,Cu/Zn比对催化剂...     

Cu/Co/Fe水滑石衍生的复合氧化物催化高氯酸铵热分解的研究

以Cu/Co/Fe水滑石(Cu/Co/Fe-LDHs)为前驱体经过焙烧制备了Cu/Co/Fe复合氧化物(Cu/Co/Fe-MOs)。利用DTA和TG-MS研究了Cu/Co/Fe-MOs作为新型催化剂对高氯酸铵热分解的催化性能。结果表明,Cu/Co/Fe-MOs呈现为CuFe2O4和(CoFe2)O4晶相,具有70~110 m2.g-1的比表面积。晶粒大小均匀,尺寸在20~30 nm。添加4wt%的400℃焙烧得到的Cu/Co/Fe-MOs催化剂使高氯酸铵热分解反应的温度降低了139℃。Cu/Co/Fe-MOs是通过吸附在金属氧化物表面的超氧离子(O2-)来加速高氯酸铵热分解的。     

含钯类水滑石衍生复合氧化物Pd/M3AlO(M=Mg,Co, Ni,Cu, Zn)催化剂上氯苯的催化氧化

采用共沉淀法制备了系列含Pd类水滑石材料, 类水滑石基体为M3Al-HT (M=Mg, Co, Ni, Cu, Zn), 经焙烧制备出含Pd类水滑石衍生复合氧化物催化剂. 通过X射线衍射(XRD), 热重-差热分析(TG-DTG), H2程序升温还原(H2-TPR), O2程序升温脱附(O2-TPD)和N2吸脱附等表征技术手段研究了不同二价金属元素对含Pd类水滑石衍生复合氧化物催化剂物理化学性质及其对挥发性有机污染物氯苯催化氧化性能的影响. XRD和TG-DTG结果表明, 不同二价金属元素, 除Cu外, 都能形成类水滑石层状结构, Pd在不同类水滑石前驱物中均能良好分散. 不同的二价金属元素对催化剂性能的影响不同, 其中Pd/Co3AlO催化剂表现出最高的氯苯催化氧化活性, 其起燃温度和全转化温度分别为182和283 ℃. H2-TPR和O2-TPD测试表明, Pd和类水滑石衍生复合氧化物存在着协同作用, Pd的引入促进了复合氧化物的还原, 从而影响氧化物的氧化还原性能. Pd/M3AlO系列催化剂的活性主要受催化剂的氧化还原性能及其表面活性氧物种的影响.     

并流淤浆混合法制备铜基甲醇合成催化剂及助剂Al2O3的作用研究

采用并流淤浆混合法制备了一系列具有不同铜锌铝比的铜基甲醇合成催化剂CuO/ZnO/Al2O3，测试了其催化性能(甲醇收率和CO转化率)及物相结构，并对该制备方法进行评价。Cu∶Zn∶Al摩尔比为4∶5∶1 的铜基催化剂显示了最好的催化活性。通过对催化剂前驱物煅烧过程进行DTA分析及对前驱物进行XRD分析表明， 催化剂前驱物的物相与Al2O3的量有关。当Al2O3的量较低时，前驱物的物相以(Cu0.3 Zn0.7)5(CO3)2(OH)6为主；当Al2O3的量较高时，前驱物中物相(Cu0.3Zn0.7)5(CO3)2(OH)6的量下降，而物相Cu2CO3(OH)2的量增加。物相(Cu0.3 Zn0.7)5(CO3)2(OH)6对终态催化剂的活性是十分有利的 。     

Controlling the Catalytic Properties of Copper-Containing Oxide Catalysts

The results of a systematic study of the formation of Cu–Zn, Cu–Zn–Al, Cu–Zn–Cr, Cu–Zn–Si, Cu–Cr, and Cu–Si oxide catalysts with a widely varied ratio between their components are generalized within the chemical approach developed by G.K. Boreskov to establish the quantitative relation between their chemical composition and catalytic activity. Simultaneously, their catalytic properties, such as selectivity and activity, are measured under the same conditions in the methanol synthesis and dehydrogenation and water gas shift reactions, whose common feature is a reductive reaction medium. The activity of Cu–Zn–Al–Cr— Si-oxide catalysts in all the studied reactions is governed by the Cu⁰ nanoparticles formed on their surface in the process of reductive activation. Nanoparticles of different catalysts have similar sizes (3–8 nm). However, the ratios between the catalytic activities per unit of the copper surface area for catalysts with various structures of their oxide support (spinel, wurtzite, zincsilite, or silica type) are appreciably different in each reaction. The relation between the chemical composition of a catalyst and its catalytic activity in a certain reaction is established by the chemical composition of its precursor representing a hydroxo compound, i.e., the nature of the selected cations and the quantitative ratio between them. The decomposition of hydroxo compounds to oxides (and the further activation of oxides) should be performed at medium temperatures, providing the incomplete elimination of ОН^– and CO₃^2- anions, i.e., the formation of anion-modified oxides. The structure of the latter and the type of interaction between Cu⁰ nanoparticles and an oxide support are governed by the structure of the hydroxo precursor compound.     

Synergistic effects of potassium promoter and carbon fibers on direct synthesis of isobutanol from syngas over Cu/ZnO/Al2O3 catalysts obtained from hydrotalcite-like compounds

The Cu/ZnO/Al₂O₃ catalysts (CuZnAl) can be utilized to directly synthesize higher alcohols from syngas under mild conditions. Carbon fibers (CFs) are widely used as a catalyst supporter, and potassium is usually used as a good electron assistant for charge transfer to the active phase of the catalyst. However, little is known about the combined effects of CFs and potassium on Cu/ZnO/Al₂O₃ catalysts. In this work, the CuZnAl catalysts supported on activated carbon fibers (ACFs) were prepared by a co-precipitation method, and then the catalysts were modified by potassium. The catalytic performances of K-modified CuZnAl and composites containing ACFs and CuZnAl were evaluated. Addition of ACFs and/or potassium increased CO conversion and selectivity for isobutanol compared with pure CuZnAl. All the samples were characterized by BET, XRD, SEM–EDS, CO–TPD, and Raman spectroscopy to further disclose the reason for better catalytic performance of the catalysts with ACFs and/or potassium. We found that addition of ACFs or potassium promotes moderate CO adsorption and formation of the active phase (CuO/ZnO solid solution) during alcohol synthesis, which facilitates synthesis of higher alcohols and CO conversion. As a result, ACFs and potassium exhibited synergistic effects on improvement of CO conversion and selectivity for isobutanol.     

液相还原法制备Cu/Zn/Al/Zr催化剂用于CO2加氢合成甲醇

近年来,由于大气CO2浓度增加引起的温室效应正日益威胁着人类的生存与发展,CO2的捕获与利用是有望解决温室效应和能源危机的有效途径.CO2催化转化为甲醇成为众多研究者关注的焦点,这是因为甲醇不仅是一种重要的基本化工原料,也是一种洁净的绿色燃料和能源载体.Cu基催化剂广泛应用于CO2加氢合成甲醇反应,并表现出良好的催化性能.通常,金属催化剂的制备是采用H2对金属氧化物进行还原.然而,传统的气相还原过程伴随着强烈的热效应,且需要在高温(473-573 K)下进行,会引起表面铜颗粒长大并加速其聚集烧结,使得活性组分利用率下降.近年来,以NaBH4为还原剂的液相还原法逐渐受到人们的重视,该方法操作简单、快捷且条件可控,反应在低温下进行,放出的热量可在液相环境中迅速得到转移,大大抑制了铜颗粒的聚集.因此,液相还原法可制备出高铜分散度、高活性的催化剂.焙烧温度对铜基催化剂结构和催化性能的影响已得到广泛探究,但这仅限于含二价铜物种催化剂,焙烧温度对含多种铜价态催化剂的影响未见报道.由于液相还原法制备的催化剂含有还原态的铜物种(Cu0和Cu+),它们比Cu2+具有更强的流动性,因此在后续的焙烧过程中催化剂更容易发生烧结和聚集.本文采用液相还原法合成了Cu/Zn/Al/Zr催化剂,分别于423,573,723和873 K焙烧后用于CO2加氢合成甲醇反应,考察了焙烧温度对制备的铜基催化剂结构性质和催化性能的影响,并与传统共沉淀法制备的催化剂进行了对比.结果显示,随着焙烧温度升高,铜物种聚集作用增强,金属铜颗粒尺寸增大,873 K时烧结出现显著增强.由于比表面积随焙烧温度升高而减小,高温度焙烧的催化剂具有小的表面碱性位数目.焙烧温度会影响催化剂中铜物种与其它组分的相互作用,进而影响催化剂的还原.随着焙烧温度的升高,催化剂的还原温度逐渐降低,表面Cu+/Cu0的比例先增后减.CO2加氢活性评价显示,液相还原法制备的催化剂具有更高的催化活性,尤其是甲醇选择性;随着焙烧温度升高,催化剂的CO2转化率和甲醇选择性先增后减,CZAZ-573催化剂具有最高活性,且在1000 h长周期活性测试中表现稳定.CO2转化率与催化剂暴露金属铜的比表面积密切相关.相比Cu0,产物甲醇更容易在Cu+表面催化生成,催化剂表面的Cu+/Cu0比与甲醇选择性的变化规律一致.通过调控焙烧温度可得到高Cu比表面积以及高Cu+/Cu0比的催化剂,有利于CO2加氢生成甲醇.     

Catalytic Gas‐phase Fluorination of Hexachlorobutadiene to 1,2‐Dichlorotetrafluorocyclobutene over Cr/Zn‐based Catalysts

In this paper, the gas‐phase fluorination of hexachlorobutadiene (HCBD) to synthesize 1,2‐dichlorotetrafluorocyclobutene (DTB) was carried out over a series of Cr/M/Zn catalysts (M = Ni, Co, Cu, In, Al). The influence of prefluorination by different fluorinating agents (HF, 95%HF + 5%Cl₂, 95%HF + 5%O₂, CF₂O, CF₂Cl₂) on catalytic performance of Cr/Co/Zn sample was also investigated. The addition of prompters to the Cr/Zn catalyst improved remarkably its catalytic properties. The Cr/Ni/Zn catalyst exhibited the best catalytic activity (1.318 mmol/h/g) at 390 °C and the Cr/Co/Zn catalyst showed the best DTB selectivity (42.5%) at 350 °C. Compared to that of gaseous HF, the catalytic performance of the Cr/Co/Zn catalyst after treatment by HF + O₂ and CF₂O increased considerably, whereas for HF + Cl₂ and CF₂Cl₂ it showed little effect. In order to identify the different species (Cr─O, Cr─F, CrO _xF _y) present on catalysts’ surface and determine their exact role, these catalysts before and after the reaction were characterized by X‐ray photoelectron spectroscopy. It was found that the concentration of the various species was responsible for the activity and lifetime of catalysts. Moreover, a possible reaction route is proposed based upon the product distribution. The most feasible formation pathway of DTB proceeded via the cyclization of C₄Cl₄F₂ or C₄Cl₃F₃ to yield c‐C₄Cl₄F₂ and c‐C₄Cl₃F₃ followed by further the Cl/F exchange.     

负载型CuO/TiO2催化剂催化CO2加氢制甲醇

采用浸渍法制备了CuO/TiO_2负载型催化剂,并将其用于CO2加氢制甲醇反应。重点考察了铜的负载量对催化剂性能的影响,并对其物化性能和催化性能之间的关系进行了讨论。结果发现,随着铜负载量的增加,催化剂中金属铜的比表面先增加后减小,当铜的负载量为10%(质量百分数)时达到最大值。催化剂的表面碱性位数量随铜含量的增加持续减小,中等碱位和强碱位的强度下降。当铜的负载量不高于10%时,CO2的转化率与铜的比表面积呈线性关系。甲醇选择性与催化剂的表面碱位性质有关,过强的碱性位会降低甲醇选择性。     

Characterization and performance of Cu/ZnO/Al_2O_3 catalysts prepared via decomposition of M(Cu,Zn)-ammonia complexes under sub-atmospheric pressure for methanol synthesis from H_2 and CO_2

Methanol synthesis from hydrogenation of CO2 is investigated over Cu/ZnO/Al2O3 catalysts prepared by decomposition of M(Cu,Zn)-ammonia complexes (DMAC) at various temperatures.The catalysts were characterized in detail,including X-ray diffraction,N2 adsorption-desorption,N2O chemisorption,temperature-programmed reduction and evolved gas analyses.The influences of DMAC temperature,reaction temperature and specific Cu surface area on catalytic performance are investigated.It is considered that the aurichalcite phase in the precursor plays a key role in improving the physiochemical properties and activities of the final catalysts.The catalyst from rich-aurichalcite precursor exhibits large specific Cu surface area and high space time yield of methanol (212 g/(Lcat·h);T=513 K,p=3MPa,SV=12000 h-1).     

负载型CuO/TiO2催化剂催化CO2加氢制甲醇

采用浸渍法制备了CuO/TiO₂负载型催化剂,并将其用于CO₂加氢制甲醇反应。重点考察了铜的负载量对催化剂性能的影响,并对其物化性能和催化性能之间的关系进行了讨论。结果发现,随着铜负载量的增加,催化剂中金属铜的比表面先增加后减小,当铜的负载量为10%（质量百分数）时达到最大值。催化剂的表面碱性位数量随铜含量的增加持续减小,中等碱位和强碱位的强度下降。当铜的负载量不高于10%时,CO₂的转化率与铜的比表面积呈线性关系。甲醇选择性与催化剂的表面碱位性质有关,过强的碱性位会降低甲醇选择性。