Diagram of the PbF<Subscript>2</Subscript>–SnF<Subscript>2</Subscript> system

A phase diagram of the PbF₂–SnF₂ system has been studied by differential thermal analysis and X-ray powder diffraction. The system forms Pb_1–хSn_хF₂ (х ≤ 0.33) solid solution and three compounds. Pb₂SnF₆ decomposes in solid state by a peritectoid reaction at 350°С; Pb₃Sn₂F₁₀ and PbSnF₄ melt by peritectic reactions at 565 and 380°С, respectively. The eutectic coordinates are 180°С, 90 mol % SnF₂.     

State of active components on the surface of the PdCl<Subscript>2</Subscript>-CuCl<Subscript>2</Subscript>/γ-Al<Subscript>2</Subscript>O<Subscript>3</Subscript> catalyst for the low-temperature oxidation of carbon monoxide

The state of the active constituents of the freshly prepared PdCl₂-CuCl₂/γ-Al₂O₃ catalyst for the low-temperature oxidation of the carbon monoxide by molecular oxygen was studied by X-ray absorption spectroscopy (XAS), powder X-ray diffraction (XRD), scanning electron microscopy (SEM), and diffuse reflectance IR Fourier transform spectroscopy (DRIFTS). It was shown that copper in the form of a crystalline phase of Cu₂Cl(OH)₃ with the structure of the mineral paratacamite and palladium chloride in an amorphous state occurred on the surface of γ-Al₂O₃. According to XAS data, the local environment of palladium consisted of four chlorine atoms, which formed a flat square with an increased distance between palladium and one of the chlorine atoms. The evolution of the local environments of copper and palladium upon a transition from the initial salts to the impregnating solutions and chlorides on the surface of γ-Al₂O₃ was considered. The role of γ-Al₂O₃ in the formation of the Cu₂Cl(OH)₃ phase was discussed. It was found by the DRIFTS method that linear (2114 cm⁻¹) and bridging (1990 and 1928 cm⁻¹) forms of coordinated carbon monoxide were formed upon the adsorption of CO on the catalyst surface. The formation of CO₂ upon the interaction of coordinated CO with atmospheric oxygen was detected. Active sites including copper and palladium were absent from the surface of the freshly prepared catalyst.     

Crystal structure of Ba<Subscript>3</Subscript>[UO<Subscript>2</Subscript>(C<Subscript>2</Subscript>O<Subscript>4</Subscript>)<Subscript>2</Subscript>(NCS)]<Subscript>2</Subscript> · 9H<Subscript>2</Subscript>O

Single crystals of Ba₃[UO₂(C₂O₄)₂(NCS)]₂ · 9H₂O are synthesized and studied by X-ray diffraction. The crystals are orthorhombic, space group Fddd, Z = 16, and the unit cell parameters are a = 16.253(3) Å, b = 22.245(3) Å, c = 39.031(6) Å. The main crystal structural units are mononuclear complex groups [UO₂(C₂O₄)₂NCS]^3? of the crystal-chemical family (AB ₂ ⁰¹ M¹ (A = UO ₂ ²⁺ , B⁰¹ = C₂O ₄ ^2? , M¹ = NCS^?) of the uranyl complexes linked into a three-dimensional framework by electrostatic interactions and hydrogen bonds involving oxalate ions and water molecules.     

Crystal structure of Cs[(UO<Subscript>2</Subscript>)<Subscript>2</Subscript>(C<Subscript>2</Subscript>O<Subscript>4</Subscript>)<Subscript>2</Subscript>(OH)] · H<Subscript>2</Subscript>O

Single crystals of Cs[(UO₂)₂(C₂O₄)₂(OH)] · H₂O were synthesized and structurally studied using X-ray diffraction. The compound crystallizes in monoclinic space group P2₁/m, Z = 2, with the unit cell parameters a = 5.5032(4) Å, b = 13.5577(8) Å, c = 9.5859(8) Å, β = 97.012(3)°, V = 709.86(9) ų, R = 0.0444. The main building units of crystals are [(UO₂)₂(C₂O₄)₂(OH)]^? layers of the A₂K ₂ ⁰² M² (A = UO ₂ ²⁺ , K⁰² = C₂O ₄ ^2? , and M² = OH^?) crystal-chemical family. Uranium-containing layers are linked into a three-dimensional framework via electrostatic interactions with outer-sphere cations and hydrogen bonds with water molecules.     

Synthesis and structure of the complex [Mo<Subscript>3</Subscript>(μ<Subscript>3</Subscript>-S)(μ<Subscript>2</Subscript>-S<Subscript>2</Subscript>)<Subscript>3</Subscript>(Et<Subscript>2</Subscript>NCS<Subscript>2</Subscript>)<Subscript>3</Subscript>]I

The structure of tri-μ₂-disulfido-μ₃-thiotris(diethyldithiocarbamato)-S,S′-triangle-trimolybdenum iodide [Mo₃(μ₃-S)(μ₂-S₂)₃(Et₂NCS₂)₃]I was determined. The compound was characterized by differential thermal analysis and IR, Raman, and X-ray electronic spectroscopy.     

Oxidation of Adamantane with H<Subscript>2</Subscript>O<Subscript>2</Subscript>–CF<Subscript>3</Subscript>COCF<Subscript>3</Subscript> · 1.5 H<Subscript>2</Subscript>O in the Presence of VO(acac)<Subscript>2</Subscript>

The system hydrogen peroxide–hexafluoroacetone sesquihydrate effectively oxidizes adamantane in the presence of VO(acac)₂ to afford 64% of adamantan-1-ol in tert-butyl alcohol or 76% of adamantan-2-one in a mixture of acetic acid with pyridine.     

Synthesis and structure of the [Co(NioxH)<Subscript>2</Subscript>(Thio)<Subscript>2</Subscript>]<Subscript>2</Subscript>SO<Subscript>4</Subscript>·2H<Subscript>2</Subscript>O complex compound

A new Co(III) complex of 1,2-cyclohexanedionedioxime and thiocarbamide with an SO ₄ ^2? anion and solvation water molecules in the outer sphere has been synthesized and its structure has been defined. Orthorhombic crystals, a = 11.659(2) Å, b = 26.448(5) Å, c = 30.142(6) Å, V = 9295(3) Å ³, Z = 8, d_calc = 1.599 g/cm³, space group Pbca; final R index is 0.0578 for 8221 reflections with I > 2σ(I). In the octahedral Co(III) complex, two 1,2-cyclohexanedionedioxime residues lie in the equatorial plane, while two thiocarbamide molecules are in the axial plane. Intramolecular bonds: N-H…O and O-H…O type hydrogen bonds and π-π interactions that stabilize the complex cations. In crystal, the components are linked by N-H…O and O-H…O hydrogen bonds into a 3D framework.     

Neutron diffraction study of Rb<Subscript>2</Subscript>UO<Subscript>2</Subscript>(SeO<Subscript>4</Subscript>)<Subscript>2</Subscript> · 2D<Subscript>2</Subscript>O

A powder of deuterated rubidium diselenatouranylate dihydrate Rb₂UO₂(SeO₄)₂ · 2D₂O has been studied by neutron diffraction. The compound is orthorhombic, space group Pna2₁, with the following unit cell parameters: a = 13.654(2) Å, b = 11.863(2) Å, c = 7.625(1) Å, Z = 4, R _F = 3.77, R _I = 6.12, and χ² = 2.21. Basic structure units are [UO₂(SeO₄)₂ · D₂O]^2? layers belonging to the AB ₂ ² M¹ crystal-chemical group (A = UO ₂ ²⁺ , B² = SeO ₄ ^2? , M¹ = D₂O) of uranyl complexes. The hydrogen atoms if the water molecules involved in the layer form intralayer hydrogen bonds with the terminal oxygen atoms of selenate ions. The outer-sphere water molecules are coordinated to the rubidium ions and are involved in hydrogen bonding with oxygen atoms of neighboring [UO₂(SeO₄)₂ · D₂O]^2? layers.     

Thermogravimetric analysis of wheatleyite Na<Subscript>2</Subscript>Cu<Superscript>2+</Superscript>(C<Subscript>2</Subscript>O<Subscript>4</Subscript>)<Subscript>2</Subscript>·2H<Subscript>2</Subscript>O

Evidence for the existence of primitive life forms such as lichens and fungi can be based upon the formation of oxalates. These oxalates form as a film like deposit on rocks and other host matrices. The anhydrous oxalate mineral moolooite CuC₂O₄ as the natural copper(II) oxalate mineral is a classic example. Another example of a natural oxalate is the mineral wheatleyite Na₂Cu²⁺(C₂O₄)₂·2H₂O. High resolution thermogravimetry coupled to evolved gas mass spectrometry shows decomposition of wheatleyite at 255°C. Two higher temperature mass losses are observed at 324 and 349°C. Higher temperature mass losses are observed at 819, 833 and 857°C. These mass losses as confirmed by mass spectrometry are attributed to the decomposition of tennerite CuO. In comparison the thermal decomposition of moolooite takes place at 260°C. Evolved gas mass spectrometry for moolooite shows the gas lost at this temperature is carbon dioxide. No water evolution was observed, thus indicating the moolooite is the anhydrous copper(II) oxalate as compared to the synthetic compound which is the dihydrate.     

Phase equilibria in the Nb<Subscript>2</Subscript>O<Subscript>5</Subscript>–CdO system and the thermal stability of Cd<Subscript>2</Subscript>Nb<Subscript>2</Subscript>O<Subscript>7</Subscript> and CdNb<Subscript>2</Subscript>O<Subscript>6</Subscript>

Phase equilibria were studied in the Nb₂O₅–CdO system in the Nb₂O₅-rich region including CdNb₂O₆ and Cd₂Nb₂O₇. It was determined that CdNb₂O₆ and Cd₂Nb₂O₇ in air are stable to 1150 and 1120°C, respectively, and that, above these temperatures, there is solid-phase decomposition of niobates with CdO release in the gas phase. Along with the cadmium oxide evaporation, the Cd₂Nb₂O₇ decomposition is accompanied by the formation of cadmium metaniobate CdNb₂O₆ and the CdNb₂O₆ decomposition results in the formation of niobium oxide Nb₂O₅. No thermal events were observed in the differential thermal analysis curve for a 1: 1 CdNb₂O₆–Cd₂Nb₂O₇ mixture heated to 1100°C in air, which suggests that there are neither phase transformations in cadmium niobates, nor a eutectic within this temperature and concentration ranges. A study of the morphology of compacted samples of niobates determined specific conditions for producing dense composite ceramics, a mixture of niobates, that is suitable for using as a dielectric material.     

Formation of solid solutions of multiferroics in the Bi<Subscript>2</Subscript>O<Subscript>3</Subscript>–Nd<Subscript>2</Subscript>O<Subscript>3</Subscript>–Fe<Subscript>2</Subscript>O<Subscript>3</Subscript> system

The sequence of phases appearance during the formation of Bi_1–xNd_xFeO₃ solid solutions in powder oxides mixtures of bismuth, neodymium, and iron has been determined. It has been shown that the closeness of the reaction mixture composition to that of the individual compound (BiFeO₃ or NdFeO₃) is essential for the realization of the series of phase transformations yielding solid solutions of multiferroics Bi_1–xNd_xFeO₃ as the final product, due to the prevalence of various interphase contacts in the starting reaction zone.     

Synthesis and crystal structure of Rb<Subscript>2</Subscript>[(UO<Subscript>2</Subscript>)<Subscript>2</Subscript>(C<Subscript>2</Subscript>O<Subscript>4</Subscript>)<Subscript>2</Subscript>(SeO<Subscript>4</Subscript>)] · 1.33H<Subscript>2</Subscript>O

The single crystals of Rb₂[(UO₂)₂(C₂O₄)₂(SeO₄)] · 1.33H₂O were synthesized and studied by X-ray diffraction. The crystals are monoclinic, space group P2₁/m, Z= 2, the unit cell parameters: a = 5.6537(8), b = 18.736(3), c = 9.4535(15) Å, β = 98.440(5)°, V = 990.6(3) ų, R ₁ = 0.0506. The main structural units of the crystal are infinite layers of [(UO₂)₂(C₂O₄)₂(SeO₄)]^2?, corresponding to the crystal chemical group A₂K ₂ ⁰² B² (A = UO ₂ ²⁺ , K⁰² = C₂O ₄ ^2? , B² = SeO ₄ ^2? ) of uranyl complexes. The uranium-containing layers are united into a three-dimensional framework through the electrostatic interactions with the outer-sphere rubidium ions and the hydrogen bonding system involving the outer-sphere water molecules.     

Crystal structure of Na<Subscript>4</Subscript>[Na<Subscript>2</Subscript>Cr<Subscript>2</Subscript>(C<Subscript>2</Subscript>O<Subscript>4</Subscript>)<Subscript>6</Subscript>] · 10H<Subscript>2</Subscript>O

Single crystals of the Na₄[Na₂Cr₂(C₂O₄)₆] · 10H₂O complex were synthesized for the first time. The structure of the complex was determined by X-ray diffraction analysis. The compound crystallizes in the monoclinic crystal system with the unit cell parameters a = 17.290(4) Å, b = 12.521(3) Å, c = 15.149(3) Å, β = 100.45(3)°, Z = 4, space group Cc. Anionic layers [NaCr(C₂O₄)₃] _2n ^4n? can be distinguished in the crystal structure of the complex. The Na⁺ cations and water molecules, involved in the formation of a hydrogen bond network, are located between the anionic layers.     

Effects of Fe<Subscript>2</Subscript>O<Subscript>3</Subscript> on the crystallization and structure of CaO–Fe<Subscript>2</Subscript>O<Subscript>3</Subscript>–SiO<Subscript>2</Subscript> glass ceramics

Radiation-induced degradation of the weakly and strongly 4-vinylpyridine basic ion exchange resins by gamma radiolysis was investigated in the presence of air and liquid water. This study is focused on evaluating the radiolytic gases (H₂, CO, CO₂ and CH₄) and liquid products (water-solute TOC and NH₄ ⁺). The weakly basic resin yielded lower amounts of H₂ and CO and higher amounts of CO₂ than those of the strongly basic resin. Moreover, the strong basic resin tended to yield greater amounts of NH₄ ⁺. Resins were characterized by the FTIR spectroscopy technique and the results showed that the resins structures are relatively stable.     

Modifying additives affect the properties of Y<Subscript>2</Subscript>O<Subscript>3</Subscript>–Al<Subscript>2</Subscript>O<Subscript>3</Subscript>–SiO<Subscript>2</Subscript> system

The effects caused by modifying additives, namely nonionic surfactants (Tween 80 and Neonol AF 9-6) and oxides (B₂O₃ and HfO₂), on the rheology, film formation, and phase formation in the yttrium aluminum silicate system prepared by sol–gel technology were studied. The effect of 1 wt % HfO₂ additions on the activation energy of crystallization was studied.     

Study of the kinetic aspects of formation of calcium monosilicate in the model system CaSO<Subscript>4</Subscript>·2H<Subscript>2</Subscript>O-Na<Subscript>2</Subscript>O·SiO<Subscript>2</Subscript>

The possibility and kinetic aspects of formation of X-ray amorphous calcium monosilicate in the model system CaSO₄·2H₂O-Na₂O·SiO₂ at room temperature were studied.     

Crystal structure and thermal properties of [Au(en)<Subscript>2</Subscript>]<Subscript>2</Subscript>[Cu(C<Subscript>2</Subscript>O<Subscript>4</Subscript>)<Subscript>2</Subscript>]<Subscript>3</Subscript>·8H<Subscript>2</Subscript>O

The crystal structure of a double complex salt of the composition [Au(en)₂]₂[Cu(C₂O₄)₂]₃·8H₂O (en = ethylenediamine) at 150 K is determined by single crystal X-ray diffraction. The crystal data for C₂₀H₄₈Au₂Cu₃N₈O₃₂ are: a = 9.1761(3) Å, b = 16.9749(6) Å, c = 13.4475(5) Å, β = 104.333(1)°, V = 2029.43(12) ų, P2₁/c space group, Z = 2, d _x = 2.450 g/cm³. It is demonstrated that the thermal decomposition of the double complex salt in a helium or hydrogen atmosphere affords the solid solution Au_0.4Cu_0.6.     

Balance,uniformity, and asymmetry of the structure of volborthite Cu<Subscript>3</Subscript>(OH)<Subscript>2</Subscript>(V<Subscript>2</Subscript>O<Subscript>7</Subscript>)·2H<Subscript>2</Subscript>O

Four structural models of volborthite Cu₃(OH)₂(V₂O₇)·2H₂O (a = 10.646(2) Å, b = 5.867(1) Å, c = 14.432(2) Å, β = 95.19(1)°, V = 897.7(5) ų, Z = 4, R/R _w = 0.038/0.046) calculated in the space groups determined from the systematic absences are compared. Based on the structure balance and the similarity of constituting polyhedra, values of the R factor, and isotropic thermal parameters, the space group Ia is found to be preferable, which is the only possible asymmetric and uniform variant. Hydrogen atoms of OH-groups, oxygen atoms and, partially, hydrogen atoms of water are localized.     

Crystal structure of Na<Subscript>3</Subscript>(NH<Subscript>4</Subscript>)<Subscript>2</Subscript>[Ir(SO<Subscript>3</Subscript>)<Subscript>2</Subscript>Cl<Subscript>4</Subscript>]·4H<Subscript>2</Subscript>O

The complex Na₃(NH₄)₂[Ir(SO₃)₂Cl₄]·4H₂O was examined with single crystal X-ray diffraction and IR spectroscopy. Crystal data: a = 7.3144(4) Å, b = 10.0698(5) Å, c = 12.3748(6) Å, β = 106.203(1)°, V = 875.26(8) ų, space group P2₁/c, Z = 2, d _calc = 2.547 g/cm³. In the complex anion two trans SO ₃ ^2? groups are coordinated to iridium through the S atom. The splitting of O-H bending vibrations of crystallization water molecules and N-H ones of the ammonium cation is considered in the context of different types of interactions with the closest neighbors in the structure.