几种吸附树脂对五氯酚钠吸附性能的研究

研究了几种树脂对五氯酚钠的吸附能力,其中戊二醛交联的壳聚糖树脂不仅有较好的吸附效果,动态吸附容量为187.5mg/g干树脂,而且易洗脱,洗脱率高达90%以上。     

交联壳聚糖微球及其接枝精氨酸树脂吸附性质的比较研究

研究了交联壳聚糖接枝精氨酸阴离子吸附树脂及交联壳聚糖微球吸附L-谷氨酸、β-内酰胺抗生素(青霉素G及氨苄青霉素)、尿素及Zn2+的动态吸附时间进程曲线及吸附容量。实验结果表明,交联壳聚糖接枝精氨酸阴离子吸附树脂对L-谷氨酸、青霉素G、氨苄青霉素、尿素及Zn2+的动态吸附平衡时间分别为120min、60min、75min、90min及50min,比交联壳聚糖微球分别缩短15min、15min、45min、45min、30min;对L-谷氨酸、青霉素G、氨苄青霉素、尿素及Zn2+的动态吸附容量分别是214.95mg/g干树脂、78.56mg/g干树脂、67.91mg/g干树脂、530mg/g干树脂及85.01mg/g干树脂,分别比交联壳聚糖微球提高了2.35倍、2.26倍、2.41倍、3.64倍和2.37倍。     

铜模板交联壳聚糖对金属离子的吸附性能研究

研究了壳聚糖对CuSO4、Cu(Ac)2、Cu（NO3)2和CuCl2溶液中铜离子的吸附性能，并以各种铜盐为模板合成了戊二醛交联树脂，考察该树脂了对金属离子的选择吸附性能．结果表明，交联树脂对铜离子有较强的“记忆”功能，且以硫酸铜为模板的壳聚糖较其它盐的模板有更高的吸附量和选择性．     

丝氨酸改性壳聚糖的合成及其对铀的吸附研究

本文利用丝氨酸对壳聚糖进行改性,再用戊二醛对改性壳聚糖进行交联,合成了丝氨酸改性壳聚糖树脂.研究了该树脂对铀的吸附等温线,吸附动力学,去除率和重复性.结果表明,该树脂对铀具有很好的吸附性能,当铀浓度在80 μg/ml 时该树脂对铀的吸附在3h达到平衡,吸附量达55.87 mg/g,去除率达90%以上,重复性能良好,是较好的吸附废水中铀的吸附剂.     

聚（对乙烯基苄基脲）大孔吸附树脂对银杏叶黄酮的吸附性能

通过静态吸附平衡和动态柱吸附试验,研究了自制大孔交联聚（对乙烯基苄基脲）树脂（简称PMVBU树脂）对银杏叶黄酮的吸附性能．结果表明,在pH=5．00时,该树脂对银杏叶黄酮有较好的吸附性能;PMVBU树脂对黄酮的吸附等温线符合Langmuir吸附等温方程,相关系数R^2〉0．99．308K时,PMVBU干树脂对黄酮的静态饱和吸附量达293．3mg／g．298K时,干树脂的动态吸附穿透容量为180mg／g．用75％的乙醇溶液对吸附在PMVBU树脂上的黄酮可进行有效洗脱．银杏叶提取液经过该树脂吸附柱吸附纯化后,黄酮纯度提高了18．6％,且树脂具有良好的重复使用性．     

基于壳聚糖及其衍生物的金属离子吸附剂的研究进展

综述了近年来以壳聚糖和壳聚糖衍生物为原料的金属离子吸附剂的研究进展．重点介绍了壳聚糖及其衍生物的交联和功能化反应，以及交联后的树脂对多种金属离子的吸附情况．常用的交联剂包括戊二醛、甲醛及环氧氟丙烷，(聚)乙二醇双缩水甘油醚等，壳聚糖树脂的功能化主要包括向其中引入冠醚、羧甲基等功能团，其中羧甲基化是最常用最有效的方法．另外，还介绍了金属离子模板壳聚糖树脂以及基于壳聚糖衍生物的蛇笼树脂的合成。     

壳聚糖涂层亲和层析介质合成的研究

研究了壳聚糖涂层亲和层析介质的制备工艺。采用合适的涂层条件，壳聚糖在玻璃珠上一次涂层量可达34mg／g介质。采用二氯化物交联剂可提高壳聚糖涂层介质的稳定性。当pH＞4．3时，交联壳聚糖涂层介质对Cu2＋的吸附容量达13．6mgCu2＋／g壳聚糖。在本介质的膨胀床中，最大液体流速可达1m／h。     

戊二醛交联壳聚糖树脂的制备及其血液相容性研究

以戊二醛为交联剂制备了交联壳聚糖树脂,讨论了合成过程中的诸多影响因素,得到了制备的最佳条件。对交联树脂的血要容性进行了研究。结果表明,树脂对人血清白蛋白的吸附量较低;经过处理后,其血液相容性得到一定程度的改善。     

交联壳聚糖吸附氯乙酸和三氯乙酸的热力学研究

利用静态吸附实验方法，研究了交联壳聚糖(氨基含量为2．414mmol／g)吸附氯乙酸和三氯乙酸的热力学性质．结果发现其对低浓度的氯乙酸和三氯乙酸的吸附均属于Langmiur型吸附，随着温度的升高，对氯乙酸的吸附量逐渐减少，而对三氯乙酸的吸附量则逐渐增加．其热力学性质表明，该交联壳聚糖对氯乙酸的吸附过程是放热过程，而对三氯乙酸的吸附过程则是吸热过程．     

交联壳聚糖树脂对部分尿毒症毒物的吸附性能研究

用反向悬浮的方法制备了戊二醛交联壳聚糖树脂吸附剂,并对制得的球形吸附剂用NaBH4进行了氢化还原处理,以提高其在使用环境下的化学稳定性。扫描电子显微镜(SEM)分析表明,吸附剂的表面形态构成了吸附的微观基础。通过对部分尿毒症毒性物质的吸附研究发现,本文研制的壳聚糖吸附剂对这些目标物均产生了一定的吸附作用,吸附平衡时间符合临床要求,其对3种小分子尿毒症毒性物质的吸附能力依肌酐、尿酸、尿素的次序递增,而对促皮质素(ACTH)的吸附量则达到了13.04mg/g,显示了该类吸附剂应用于临床治疗的潜在价值     

ADSORPTION SELECTIVITY FOR Cu~(2 ),Ni~(2 ),Co~(2 )IONS USING CROSSLINKING CHITOSAN RESINS IMPRINTED BY METAL IONS

1introductionChitosan,adeacetylatedderivativeofchitin,isnatUralpolysaccharideswithfreeaminogroups.Itcanactasanexcellentadsorbenttoadsorbnotonlyvariousorganiccompoundsincludingpolychlorinatedbiphenyls,proteinsandnucleicacids,butalsometalions[1~sl.ChitosanhasbeenwidelyemployedasaneffectivecoagulatingagentinactivatedsludgeplantSandfoodprocessingfactories,andalsoinpreparation,concentTationandpurificationofmetalionsinhydrometallurgy.Chitosanbehavesasanaturalchelatingpolymer.Chitosanundergoeschela…     

外加盐对壳聚糖树脂吸附游离酸的影响

利用电化实验技术,跟踪观察交联壳聚糖树脂在不同环境体系吸附低浓度游离酸的行为。讨论了在三元体系（酸 水 盐）和四元体系（酸 水 有机物 盐）中,交联壳聚糖树脂吸附游离酸的规律。利用固-液相互作用方程,求取吸附剂-吸附质相互作用能。实验结果表明,交联壳聚糖树脂在三元体系和四元体系中吸附游离酸,表观吸附速率常数（k)随着外加盐浓度的增大而减小。发现表观吸附速率常数（k)与吸附剂-吸附质相互作用能（U）存在线性关系。     

氨基酸修饰壳聚糖对胆固醇的吸附作用

通过将不同脱乙酰度的壳聚糖粉末与戊二醛交联,再经苯丙氨酸和色氨酸修饰,得到了两种珠状壳聚糖吸附剂,并进而研究了有关吸附剂对胆因醇的吸附性能。实验表明,交联壳聚糖珠对ＣＨＯ的吸附能力比壳聚糖粉末降低,而经不同氨基酸修饰后的壳聚糖珠对ＣＨＯ吸附能力提高,用Ｐｈｅ修饰比用Ｔｒｙ修饰的珠吸附性能更好些。     

ADSORPTION SELECTIVITY FOR Cu^2＋,Ni^2＋,Co^2＋IONS USING CROSSLINKING CHITOSAN RESINS IMPRINTED BY METAL IONS

Metal ion-imprintedly crosslinked chitosan resin 1 and resin 2 were prepared by the use of Cu^2+ and Ni^2+ as template ions and glutaraldehyde as crosslinking agent,respectively,Through investigation on the adsorption capacties and binding constants for Cu^2+,Ni^2+ and Co^2+ ions on chitosan resins,resin 1 and resin 2 exhibit the adsorption selectivity for the mixture solution of 1L1 Cu^2+ and Ni^2+ ions.The adsorption selectivity of metal ion-imprinted resins for their template ions in much higher than that of uncrosslinked chitosan resin.     

PREPARATION AND ADSORPTION OF THIOUREA MODIFIED GLUTARALDEHYDE-CROSSLINKED CHITOSAN RESINS

The preparation and adsorption of thiourea modified glutaraldehyde-crosslinked chitosan resin (Thio-chitosan) using cyanuric chloride as activator was studied. The adsorptive capacity of thio-chitosan with 15% apparent degree of crosslinking (DC, mass ration of glutaraldehyde to chitosan) to Cu(Ⅱ) was 160mg/g (dry weight). The adsorption of Cu(Ⅱ) was correlated with Freundlich and Langmuir isotherm equation. Cu(Ⅱ) adsorbed on thio-chitosan column ( 1 cm×10 cm)was eluted with 0.5mol/L H2SO4, 6mol/L HCl and 3% thiourea solution with the recovery of 88.3%,86.1% and 95.3%, respectively. The thio-chitosan resin can be applied to the separation and recovery of metal ions.     

流动注射分光光度法研究壳聚糖树脂吸附阴离子染料

利用流动注射分光光度法技术，跟踪观察交联壳聚糖树脂吸附阴离子染料的行为，讨论了外加氯化钠或甲醇以及温度等因素对吸附的影响。利用固－液相互作用方程，求取了吸附剂－吸附质相互作用能。实验结果表明，交联壳聚糖树脂吸附 子染料，其表观吸附速率常数随体系中氯化钠浓度或甲醇含量的增大而减小，随温度的升高而增大；交联壳聚糖树脂吸附酸性铬蓝K染料的表观活化能力26.095kJ/mol。     

尿毒症中分子毒物吸附剂的研究(Ⅰ)——戊二醛交联壳聚糖吸附剂

长期以来 ,血液净化疗法一直是临床上处理各种血液中毒的基本手段[1～ 3] .对尿毒症患者 ,目前普遍采用的治疗措施是对其进行定期的血液或腹膜透析 [1] 缓解病情 ;然而单纯血液透析疗法难以清除患者体内的中分子毒物 ,以致血液透析的患者体内 ,中分子毒物的积累会达到很高的程度 .因此 ,通过研制高效的中分子吸附剂 ,以血液灌流的方式清除中分子毒物 ,对于控制和治疗尿毒症具有重要意义 .据文献报道 ,体内蓄积的中分子毒物中肽类物质占了一定的比例[4～ 9] ,患者的许多顽固临床症状与这些毒物的体内蓄积密切相关 [1,10 ] .本课题组的研究结…     

电化法研究壳聚糖树脂与游离酸的相互作用

利用电化实验技术，跟踪观察交联壳聚糖树脂吸附低浓度游离酸的行为，讨论了酸和甲醇浓度等因素对吸附的影响，利用固-液相互作用方程，求取吸附剂一吸附质相互作用能。实验结果表明，交联壳聚糖树脂吸附低浓度游离酸的过程是遵循单分子层机制进行的，表观吸附速率常数随着吸附质浓度和外加甲醇含量的增大而减小，表观吸附速率常数与吸附剂一吸附质相互作用能（U）存在线性相关。     

Synthesis of cross-linked chitosan modified with the glycine moiety for the collection/concentration of bismuth in aquatic samples for ICP-MS determination.

A chelating resin, cross-linked chitosan modified with the glycine moiety (glycine-type chitosan resin), was developed for the collection and concentration of bismuth in aquatic samples for ICP-MS measurements. The adsorption behavior of bismuth and 55 elements on glycine-type chitosan resin was systematically examined by passing a sample solution containing 56 elements through a mini-column packed with the resin (wet volume; 1 ml). After eluting the elements adsorbed on the resin with nitric acid, the eluates were measured by ICP-MS. The glycine-type chitosan resin could adsorb several cations by a chelating mechanism and several oxoanions by an anion-exchange mechanism. Especially, the resin could adsorb almost 100% Bi(III) over a wide pH region from pH 2 to 6. Bismuth could be strongly adsorbed at pH 3, and eluted quantitatively with 10 ml of 3 M nitric acid. A column pretreatment method with the glycine-type chitosan resin was used prior to removal of high concentrations of matrices in a seawater sample and the preconcentration of trace bismuth in river water samples for ICP-MS measurements. The column pretreatment method was also applied to the determination of bismuth in real samples by ICP-MS. The LOD of bismuth was 0.1 pg ml(-1) by 10-fold column preconcentration for ICP-MS measurements. The analytical results for bismuth in sea and river water samples by ICP-MS were 22.9 +/- 0.5 pg ml(-1) (RSD, 2.2%) and 2.08 +/- 0.05 pg ml(-1) (RSD, 2.4%), respectively.