VPO超微粒子的制备和表征

以Ｖ２Ｏ５和浓Ｈ３ＰＯ４为原料,浓ＨＣｌ和柠檬酸作还原剂,以含量不同金属离子为助剂,采用超临界流干燥法制备了ＶＰＯ超微粒子,应用ＢＥＴ、ＸＲＤ、ＴＥＭ及ＸＰＳ等手段考察了ＶＰＯ超微粒子的物性、结构及助剂对其物性的影响,实验结果表明,超临界流体干燥法可显著增大样品的比表面积,一可使粒子大小达到纳米尺度,实验发现,超微样品的晶相结构为一种尚未鉴定的未知物相,而表面Ｖ离子价态则基本上为＋４价。     

合成低碳醇超细Mo-Co-K催化剂的制备及其表征

采用类凝胶法和超临界流体干燥技术制备超细Ｍｏ－Ｃｏ－Ｋ催化剂。通过ＢＥＴ,ＴＥＭ,ＸＲＤ和ＴＰＲ等表征手段比较分析了不同制备参数尤其是Ｃｏ／Ｍｏ比对超细Ｍｏ－Ｃｏ－Ｋ催化剂性能的影响。结果表明,制得的催化剂为大比表面积、小粒径、大孔超细粒子。     

VPO催化剂的制备及其表征

采用ＢＥＴ、ＸＲＤ等测试手段，考察了由四种不同方法和条件下制备的ＶＰＯ催化剂的比表面积和晶体结构。实验结果表明：还原剂、溶剂、Ｐ／Ｖ、干燥条件及焙烧温度都对ＶＰＯ催化剂的物理性质有影响。水相法制备，获较复杂的晶相，且随着焙烧温度的提高样品的比表面积减小，晶相强度增加。有机相法制备，可获得较单一、活性好的晶相，且焙烧温度提高对样品的比表面积影响不大，但超临界条件下干燥，可使催化剂比表面积成倍地增大     

纳米级TiO_2粉体的制备研究Ⅰ.pH值的影响

采用无机盐作为前驱物，利用溶胶凝胶超临界流体干燥（ＳＣＦＤ）法，制备出大孔、高比表面纳米级ＴｉＯ２超细粉。详细考察了初始水凝胶ｐＨ值对ＴｉＯ２超细粉形貌、晶相、颗粒大小、比表面积及孔结构等的影响。实验结果发现：当在酸性环境中，所制得的ＴｉＯ２超细粉的比表面积随着ｐＨ值的减小而增大；而在碱性环境中，则随着ｐＨ值的增大而增大。ＴｉＯ２超细粉的比表面积和孔体积由ｐＨ为６．５时的ＳＢＥＴ＝１４２．２ｍ２·ｇ１，ＶＰＮ＝０．４５ｃｍ３·ｇ１，增大到ｐＨ值为１３．０时的ＳＢＥＴ＝４２５．６ｍ２·ｇ１，ＶＰＮ＝１．７９ｃｍ３·ｇ１，且颗粒分布均匀狭窄，颗粒间的三维网络织构更为规整清晰。     

不同制法镁铝尖晶石在环己酮双聚中的应用

用共沉淀法，溶胶－凝胶法，超临界干燥技术和脲燃烧法制备了一系列镁铝尖晶石，并将其用于环己酮双聚合成环己烯环己酮（ＣＨＣＨ）的反应中。借助于ＴＥＭ、ＸＲＤ、ＢＥＴ和ＣＯ＿２－ＴＰＤ等手段考察了不同制备方法对催化剂性质及性能的影响。     

不同制法镁铝尖晶石在环已酮双聚中的应用

用共沉淀法，溶胶－凝胶法，超临界干燥技术和脲燃烧法制备了一系列镁铝尖晶石，并将其用于环已酮双聚合成环已烯环已酮（ＣＨＣＨ）的反应中。借助于ＴＥＭ、ＸＲＤ、ＢＥＴ和ＣＯ２－ＴＰＤ等手段考察了不同制备方法对催化剂性质及性能的影响。     

以混合模板剂合成TS—1分子筛及其性能研究

以四丁基溴化铵（ＴＢＡＢｒ）＋四乙基氢氧化铵（ＴＥＡＯＨ，ｎ（ＴＢＡ＾＋）／ｎ（ＴＥＡ＾＋）＝１）或以四丙基溴化铵（ＴＰＡＢｒ）＋ＴＥＡＯＨ为模板剂，钛酸四丁酯和正硅酸乙酯为原料，于１７０℃水热合成出ＴＳ－１分子筛。对合成的ＴＳ－１样品进行了ＸＲＤ，ＦＴ－ＩＲ，ＳＥＭ和ＢＥＴ比表面积分析，证实了样品中钛已进入Ｓｉｌｉｃａｌｉｔｅ－１骨架。选择戊烷氧化为探针反应，考察了ＴＳ－１的催化活性。结果表明以     

超临界条件下合成晶型骨架的介孔氧化锆

采用聚氧乙烯型非离子表面活性剂（ＰＥＯ）为模板剂,超临界乙醇为介质,在不同条件下（各种ＰＥＯ,不同ＰＨ值和络合剂）合成了类似于ＭＳＵ的介孔氧化锆。ＸＲＤ,Ｎ２物理脱吸附曲线,ＴＥＭ及选区电子衍射证明该介氧化锆骨架为四方晶型;改变表面活性剂类型、络合剂及ＰＨ可调变介孔氧化锆的ＢＥＴ表面积与孔分布。     

无铬CO高温变换催化剂的研究 Ⅰ.氧化铬对CO高变催化剂结构与性能的影响 W

通过ＸＲＤ，ＢＥＴ和ＸＰＳ表征及反应活性测定表明，ＣＯ高温变换催化剂中加入的助剂ＣｒＯ３在制备及还原过程中，能进入Ｆｅ３Ｏ４晶格，使晶胞参数增大，晶粒度变小，分散度提高，比表面积和孔容积增大，孔结构改善而提高催化剂活性和稳定性。     

以混合模板剂合成TS-1分子筛及其性能研究

以四丁基溴化铵（ＴＢＡＢｒ）＋四乙基氢氧化铵（ＴＥＡＯＨ，ｎ（ＴＢＡ＋）／ｎ（ＴＥＡ＋）＝１）或以四丙基溴化铵（ＴＰＡＢｒ）＋ＴＥＡＯＨ为模板剂，钛酸四丁酯和正硅酸乙酯为原料，于１７０℃水热合成出ＴＳ１分子筛．对合成的ＴＳ１样品进行了ＸＲＤ，ＦＴＩＲ，ＳＥＭ和ＢＥＴ比表面积分析，证实了样品中钛已进入Ｓｉｌｉｃａｌｉｔｅ１骨架．选择戊烷氧化为探针反应，考察了ＴＳ１的催化活性．结果表明以ＴＥＡＯＨ为碱，合成的样品晶粒较大，达到４～１０μｍ，用氨水和ＴＥＡＯＨ调节反应液的碱度，对晶体的生长和形貌的影响各不相同．文中还就ＴＥＡＯＨ引入的作用进行了讨论．     

制备方法对负载型纳米ZrO2/Al2O3复合载体性能的影响

采用浸渍-沉淀法制备了负载型纳米ZrO2/Al2O3复合载体.采用X射线衍射、N2物理吸附、差示扫描量热(DSC)和程序升温脱附等技术考察了浸渍方式和干燥方法对复合载体的表面性能、热稳定性和晶相结构的影响.结果表明,ZrO2/Al2O3复合载体中没有生成ZrO2-Al2O3复合氧化物或固溶体,纳米ZrO2仅负载在Al2O3的表面.微波干燥法制备的ZrO2/Al2O3复合载体的比表面积(158.7 m2/g)较大,最可几孔径为19.4 nm,ZrO2的粒度为4.2 nm,晶相结构为四方相ZrO2.微波诱导作用使ZrO2/Al2O3复合载体表面产生了新的酸碱中心,微波干燥法制备的ZrO2/Al2O3复合载体具有较强的热稳定性,在873~1 073 K范围内DSC曲线没有出现吸热峰,而其它干燥方法制备的复合载体在903~1 023 K范围内出现了较明显的吸热峰,表明复合载体表面的部分四方相ZrO2转变为单斜相ZrO2(m-ZrO2).对超声波处理过的复合载体进行微波干燥能进一步提高纳米ZrO2与Al2O3之间的相互作用,纳米粒子的粒度(3.4 nm)更小,分布更均匀,但没有改变ZrO2的晶相结构.     

费-托合成Co/ZrO2-Al2O3催化剂反应性能的研究

以ZrOCl2·6H2O和AlCl3为原料，采用共沉淀方法制得一系列不同ZrO2质量分数的ZrO2-Al2O3混合氧化物载体；并以该混合氧化物为载体，采用初湿浸渍法制得钴质量分数为12％的Co/ZrO2-Al2O3催化剂。XRD、NH3-TPD、TPR和原位IR等表征结果表明，随着混合载体中ZrO2质量分数的增加，载体比表面积先增加后减少，混合载体的平均孔径则小于单一氧化物ZrO2和Al2O3的平均孔径。ZrO2和Al2O3载体混合后会导致氧化物的比表面积和酸性增大并且有新的物相生成。当混合氧化物用作载体时，能够抑制载体表面金属钴的分散，改变催化剂的还原行为，降低催化剂对CO物种的吸附能力。CO加氢反应表明，与单一金属氧化物相比，钴负载ZrO2-Al2O3混合氧化物催化剂的加氢活性和重质烃选择性有所降低。     

稀土添加剂对超细ZrO2织构、结构的影响

Pure zirconia and zirconia containing Y or Ce were prepared by Supercritical Drying Method (SCD) followed by calcination in air at temperature up to 700℃. It was found that the zirconia containing Y or Ce possessed much higher specific surface area and larger pore volume than that of pure zirconia. The BET surface area of 3.4Y2O3-96.6ZrO2 without calcination and that calcined at 700℃ were 376.2 m2﹒g-1 and 80.0 m2﹒g-1 respectively, while the corresponding values of pure zirconia were 248.0 m2 ﹒g-1 and 47.8 m2﹒g-1 respectively. It was postulated that the better textural properties of zirconia containing Y or Ce were resulted from preventing zirconia particles sintering in the presence of Y or Ce additive. All of these samples made by SCD had a well-developed mesoporous texture.     

Study of a Ru-La/Zr02 Catalyst Prepared by Precipitation Method for Selective Hydrogenation of Benzene to Cyclohexene

A Ru-La/ZrO2 catalyst was prepared by the precipitation method, in which Ru was an active component, La was a promoter and ZrO2 was a dispersant. Comparing with the catalyst prepared by the chemical reduction method, the Ru-La/ZrO2 exhibited higher activity and better selectivity. At 140 ℃ and hydrogen pressure of 5 MPa, the C6H10 selectivity reached 70% at a C6H6 conversion of 35% for a reaction time was 5 min and the total La/Ru loading was 10%. Textural parameters of the catalyst were obtained by physical adsorption, BET surface area and specific pore volume measurements. The catalyst sample gave a BET area of 41 m2/g and a specific pore volume of 1.1 cm^3/g, and the most probable pore distribution was located at 5 to 10 nm. H2-TPR measurements showed that ruthenium oxide could be reduced to its metallic state at about 403 K. XRD determinations indicated that ruthenium and lanthanum were highly dispersed on the zirconia. A significant advantage of the Ru-La/ZrO2 catalyst is that it can be used directly in its unreduced state for the selective hydrogenation of benzene.     

Study of a Ru-La/ZrO_2 Catalyst Prepared by Precipitation Method for Selective Hydrogenation of Benzene to Cyclohexene

1. Introduction Cyclohexene as an important intermediate prod- uct is widely used in chemical productions. The process of selective hydrogenation of benzene to cyclo- hexene has been an important research topic in green chemistry owing to its atomic economy and clean production [1]. In order to attain greater economic benefits, researchers are searching for a new catalytic system that is high in activity and selectivity, simple in technology, and low in cost. In this respect, some progresses h…     

Re组分及ZrO_2载体制备方法对Ru-Re/ZrO_2催化丙三醇氢解反应的影响

分别采用沉淀法、水热合成法和不同气氛下焙烧的方式制备了ZrO2载体,采用浸渍法负载Ru及Ru-Re组分制备了Ru/ZrO2和Ru-Re/ZrO2催化剂.利用氮气吸附-脱附、X射线衍射、透射电镜及程序升温还原等方法对样品的比表面积、孔容、平均孔径、晶体结构、形貌及还原特性等进行了表征.考察了Re组分及ZrO2载体制备方法对催化剂在丙三醇氢解制丙二醇反应中的催化性能的影响.结果表明,不同方法制备的ZrO2载体对负载型Ru催化剂的催化性能有一定影响,其中以沉淀法在空气中焙烧制得ZrO2负载活性组分后得到的催化剂的活件相对较低(转化率18.7%),而以沉淀法在氮气中焙烧以及水热合成法制备的ZrO2负载活性组分后得到的催化剂的活性相对较高(转化率25.8%).Re组分的引入对Ru/ZrO2系列催化剂的催化性能有明显的促进作用.     

氧化铝基表层ZrO2的相结构、孔结构及性能研究

近年来，双组份氧化物的性质和作用越来越受到人们的重视，国内外学者对TIOZ／A1203，Ceo。／AI。oa＊，MgO／AI。osRI等作了大量的研究．Zro。既可以做工业催化剂的载体，又可作添加剂或活性组份，它具有酸、碱、氧化和还原四种化学性质，在一氧化碳加氢合成甲醇中更具有重要作用·本文通过改变在7－AI。O3表面上Zro：负载量，研究了Zro。－AI。Oa体系的相结构及孔结构，并以CO氧化为模型反应，结合TPD－MS等实验技术研究并考察了添加Zroz对Alzoa基催化氧化及表面氧性能的影响，探讨Zroz的助催化作用·1实验部分（1）实验样…     

Super critical drying applied on severely corroded buried glasses

The corrosion of buried glass leads to the formation of a hydrated surface which is silica rich, porous and multilayered. Following the excavation of the glass, water evaporates causing important stresses due to surface tension forces. Severe damages such as surface deformation, shrinkage then occur or even destruction of the item. In order to eliminate these stresses, we performed a Super Critical Drying (SCD). We have compared the results obtained by ethanol and acetone extraction to those obtained by conventional drying, on some freshly excavated carolingian glasses (10 centuries burying time). The SCD method seems to be suitable to preserve the morphology of the alteration profile as well as the coherence of the altered layer-glass interface.     

中孔分子筛负载钴催化剂制备及其在费-托合成中的催化性能

 以HMS,MCM－41,AlHMS和ZrO2／HMS等中孔分子筛为载体,采用孔体积浸渍法制备了系列负载型钴催化剂．XRD测定结果表明,Co氧化物完全分散于分子筛内表面,载体仍保持中孔分子筛的特征;低温N2吸附测定结果表明,表面负载金属钴后,分子筛的比表面积和孔体积下降,孔径减小,孔壁增厚．比较了不同中孔分子筛负载Co催化剂在F－T反应中的催化性能,以短程六角对称的HMS为载体,有利于F－T反应中的链增长,烃类产物主要为微晶蜡;以ZrO2／HMS为载体可抑制CH4的生成,提高C5＋的选择性．     

负载型纳米ZrO2/Al2O3复合载体的制备和表征及其Ni/ZrO2/Al2O3催化性能的研究

以大孔Al2O3为基载体，采用沉积-沉淀法和溶胶-沉积法制备了负载型纳米ZrO2/Al2O3复合载体．用XRD、TEM和比表面与孔径测定等手段对载体进行了表征．结果表明，负载型纳米ZrO2/Al2O3复合载体具有较大的比表面积和适宜的孔径分布，纳米ZrO2在载体上呈单层均匀分布．以CH4-CO2重整制合成气为探针反应，考察了Ni/ZrO2/Al2O3催化剂的活性和选择性．