Ag/TiO2纳米材料的制备和光致变色性能研究

 采用光催化还原法在不同温度热处理的TiO2薄膜表面沉积Ag纳米颗粒,制备了Ag/TiO2纳米薄膜材料。通过UV-Vis吸收光谱表征对比了不同温度热处理的TiO2对Ag粒子光催化沉积的影响,发现500℃退火处理TiO2薄膜较利于Ag纳米粒子的光催化沉积;在650 nm红色激光照射下,500℃退火处理的Ag/TiO2样品具有明显的光致变色现象,对此变色过程中涉及的机理进行了讨论,且发现随着Ag纳米颗粒光催化沉积时间的增长,Ag/TiO2薄膜光致变色的响应速率提高,但Ag纳米颗粒过多会抑制Ag/TiO2薄膜的变色响应速率。     

Ti(SO4)2水热法制纳米SO2-4/TiO2光催化剂的光谱研究

以Ti(SO4) 2 水溶液为前驱物 ,尿素为沉淀剂 ,采用水热沉淀 加热分解 浸渍烧结法制备纳米SO2 -4/TiO2 固体超强酸光催化剂 ,并用XRD ,BET ,FTIR ,DRS和FS等对中间态粒子和产物进行表征 ,以光催化降解罗丹明B为模型反应 ,筛选制备SO2 -4/TiO2 光催化剂的优化条件。结果表明 ,用Ti(SO4) 2 为前驱物 ,水热法能在较低的温度、弱碱性介质中 ,得到纳米锐钛矿型TiO2 晶体 ;在 30 0℃下控制焙烧 4h ,基本能使水热反应副产物 (NH4) 2 SO4等分解 ,又避免H2 SO4大量的流失 ;SO2 -4负载量和烧结时间是影响SO2 -4/TiO2 光催化活性的主要因素 ,当SO2 -4负载量 11%、烧结温度 4 5 0℃时 ,制备的SO2 -4/TiO2 光催化剂活性较高 ,达P 2 5光催化剂的水平     

纳米金红石TiO2光催化剂的水解合成及其性能

采用水解法在323K制备了比表面积较大的纳米金红石TiO2光催化剂,并通过X射线衍射(XRD)、BET比表面积测试法、紫外-可见吸收光谱(UV-Vis)、红外光谱(IR)和光电化学(PEC)测量对纳米光催化剂进行了表征。以甲基橙为光催化反应的模型化合物,在比表面积相近的条件下,对纳米金红石和锐钛矿TiO2光催化剂的光催化活性进行了评价。光催化实验结果表明:比表面积为～95m2.g-1时,比表面积相近的金红石和锐钛矿的紫外光催化活性相当,但金红石的可见光催化活性明显高于锐钛矿的可见光催化活性。光电化学实验表明:在紫外光照射下催化剂的光电流密度从弱到强的顺序与其紫外光催化活性从低到高的次序一致。     

纳米复合材料TiO2-ZrO2光催化降解可溶性染料的研究

采用溶胶-凝胶方法将光催化剂TiO2和ZrO2复合,再经700℃灼烧5h后获得了纳米复合光催化材料TiO2-ZrO2.该材料经XRD检测具有光催化活性良好的晶型结构.TEM测定结果显示产物的平均粒径约为20nm.通过对可溶性染料刚果红等的光催化降解实验证明,该复合材料具有较高的光催化活性.     

TiO2/5A光催化降解水中CN-的催化活性

采用溶胶-凝胶-浸渍法制备TiO2/5A型催化剂,以其对水样中CN-降解率的大小来评价催化剂的光催化活性,并与P25型纳米TiO2催化效果作比较,从而探讨5A型分子筛负载纳米TiO2的百分含量、催化剂加入量、水样的pH值及CN-初始浓度对TiO2/5A光催化降解水中CN-催化活性的影响.结果表明:5A型分子筛负载纳米TiO2的量为20％、加入量为1.5g/L、pH=10、CN-初始浓度为50mg/L,反应时间为3h时,降解率达88.64％,且优于P25型纳米TiO2的降解效果.     

金属离子对纳米TiO2悬浊液的光催化性能影响的光谱研究

以钛氧有机物为前驱体,利用微乳液法制备了纳米TiO2微晶。用X射线衍射(XRD)和红外光谱(FTIR)等测试技术对产物进行了表征,并就纳米TiO2悬浊液中加入金属离子后光催化降解甲基橙溶液进行了初步的研究。光谱分析表明,纳米TiO2悬浊液中加入Bi3 离子后对甲基橙溶液的光催化降解有很大的促进作用,Bi3 与TiO2质量比为1∶8及TiO2的浓度为1.6g·L-1时光催化活性最佳。     

La-Ce-TiO_2纳米光催化剂的溶胶-微波法合成、谱学表征及其活性研究

以钛酸四丁酯为原料,采用溶胶-微波法(Sol-Microwave Method)合成了镧和铈共掺型纳米TiO2粉体(La-Ce-TiO2),借助XRD、XPS和UV-Vis等测试手段对其进行了表征,并以甲基橙为模型污染物考察了掺杂量对样品光催化活性的影响规律.XRD分析表明,所得粉体均为锐钛矿相纳米TiO2,且稀土元素镧和铈掺杂后纳米TiO2特征衍射峰宽化,强度降低;XPS分析表明,镧和铈掺杂后样品表面存在大量的氧缺位;UV-Vis吸收光谱表明,所得粉体在400 nm以下均有连续宽化的吸收带,且La和Ce掺杂后样品对光的吸收显著增强,这足由于La(Ⅲ)-O荷移跃迁以及Ce(Ⅳ)f→d跃迁和Ce(Ⅳ)-O荷移跃迁所致;光催化实验表明,La和Ce共掺杂能显著提高纳米TiO2的光催化活性,其中当La(Ⅲ)和Ce(Ⅳ)掺杂量分别为2%和0.04%时,纳米TiO2光催化剂具有较高的催化活性,自然光照射下光催化氧化处理卷烟厂蒸叶车间废水,效果较好,废水COD去除率达到86.11%.     

TiO2薄膜的制备及甲醛的光催化降解

以钛酸四丁酯为前驱体，采用溶胶一凝胶一超声波法制备得到了纳米TiO2溶胶，在单面抛光的硅片上采用旋转涂膜法涂上TiO2溶胶，快速烘干，再经烧结得到TiO2薄膜，并利用XRD，XPS与AFM对其结构性能进行表征，结果表明，膜厚度大约可控在3-5nm，膜表面颗粒大小约20nM，膜的组成主要为锐钛矿型TiO2和少量有机碳化物。在制备TiO2薄膜时，发现膜层随着镀膜次数变化显示不同的颜色差异，并有着良好的对应关系。以此现象入手研究不同颜色的TiO2薄膜在同一光催化条件下甲醛的降解分析，实验结果发现呈蓝色光的TiO2薄膜表现良好的光催化效果，其原因可能是蓝色光对光的吸收较好。     

Ag负载WO3/TiO2光催化剂的合成及其催化性能

以钛酸丁酯、无水乙醇、钨酸铵为原料,采用溶胶-凝胶法合成了WO3/TiO2复合光催化剂;采用光还原技术制备了Ag负载WO3/TiO2光催化剂,借助X射线粉末衍射(XRD)和UV-Vis光谱等技术对样品的组成和光吸收性能进行了表征,并以罗丹明B为模型污染物考察样品的光催化活性。XRD分析表明,所得粉体均为锐钛矿型纳米TiO2,且与WO3复合后,纳米TiO2特征衍射峰宽化,强度降低;UV-Vis光谱分析表明,载银使得催化剂在400—700nm的可见光区域对光响应,且在紫外光区吸收显著增强,对光具有更高的利用率;以罗丹明B为降解物的光催化实验表明,WO3复合对纳米TiO2光催化活性有显著的影响,而载Ag后其光催化活性进一步提高,将该光催化剂用于炼油厂废水的处理,效果较好。     

掺Fe~(3+)对载Ag纳米TiO_2光催化性能的改良

为研究掺杂不同mol分数的Ag+,Fe3+对TiO2薄膜光催化性能的影响,采用溶胶-凝胶法分别制备了掺杂不同质量分数的Ag+,Fe3+及其共掺杂的纳米TiO2光催化杀菌膜。以大肠杆菌为光催化抗菌的反应模型,对TiO2薄膜光催化性能进行了评价。进而采用XRD,Uv-Vis对复合掺杂薄膜的特性进行了测试,以分析Ag+,Fe3+对影响TiO2薄膜的光催化杀菌性能的内在机理。结果表明:在荧光灯照射下,以Ag+,Fe3+各自最佳掺杂量Ag/Ti+=0.05%,Fe/Ti=0.1%,共同掺入TiO2中时,共掺杂杀菌率最高,并且共掺杂有良好的光催化分解能力。所得TiO2晶型基本为锐钛矿型,通过Uv-Vis可以看出共掺杂在可见光区具有良好的吸收性能。Fe3+是由于拓展了TiO2的吸收范围,而Ag+是由于正离子有效地抑制光生电子空穴的复合,它们二者共同合作从而提高了TiO2薄膜的光催化性能。共掺杂相对于单掺杂有着更优异的性能,是进一步的研究方向。     

Characterization and activity of visible-light-driven TiO2 photocatalyst codoped with lanthanum and iodine

The novel visible-light-activated La/I/TiO₂ nanocomposition photocatalyst was successfully synthesized using precipitation-dipping method, and characterized by X-ray powder diffraction (XRD), the Brunauer-Emmett-Teller (BET) method, transmission electron microscopy (TEM), thermogravimetry-differential scanning calorimetry (TG-DSC) and UV-vis diffuse reflectance spectroscopy (UV-vis DRS). The photocatalytic activity of La/I/TiO₂ was evaluated by studying photodegradation of reactive blue 19 as a probe reaction under simulated sunlight irradiation. Photocatalytic experiment results showed that the maximum specific photocatalytic activity of the La/I/TiO₂ photocatalyst appeared when the molar ratio of La/Ti was 2.0 at%, calcined at 350 °C for 2 h, due to the sample with good crystallization, high BET surface area and small crystal size. Under simulated sunlight irradiation, the degradation of reactive blue 19 aqueous solution reached 98.6% in 80 min, which showed La/I/TiO₂ photocatalyst to be much higher photocatalytic activity compared to standard Degussa P25 photocatalyst. The higher visible light activity is due to the codoping of lanthanum and iodine.     

Synthesis of nanometer Bi2WO6 synthesized by sol-gel method and its visible-light photocatalytic activity for degradation of 4BS

Nanometer Bi₂WO₆ catalyst with visible-light responsive was prepared by a sol-gel method in the presence of EDTA. The as-prepared samples were characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM), transmission electron microscopy (TEM), UV-vis diffuse reflectance spectrum, Fourier transform infrared (FTIR) spectrum, Brunauer-Emmet-Teller (BET). The UV-vis diffuse reflectance spectrum of the as-prepared sample shows a markedly blue-shift as compared to that of the sample obtained by a solid-state reaction. The as-prepared samples exhibited higher activities than that synthesized by the solid-state reaction for 4BS photodegradation under visible-light irradiation (λ>400 nm) and the sample prepared at 450 °C exhibited the highest photocatalytic activity.     

The crossing of N2 adsorption isotherms on CdCl2

The adsorption of N₂ at 77.7, 83.3 and 90.1 K has been obtained on a sample of CdCl₂ previously treated in vacuum at 150°C for 40 h. All adsorption isotherms, when plotted versus relative pressure, cross at a point near $\text{P}\text{P}{}_0$ = 0.15. The volume adsorbed at the crossing point is near the BET or point B monolayer volume. The crossing of the isotherms is related to the high surface homogeneity of the sample.     

Preparation and photocatalytic property of CeO2 lamellar

A novel room temperature solid-state chemical synthesis was introduced to successfully fabricate CeO₂ samples, coupled by a polyethylene glycol 400 (PEG 400)/cetyl trimethylammonium bromide (CTAB)/sodium dodecyl sulfate (SDS). The as-prepared products were characterized by XRD, TEM, SEM, BET and UV. A study of photocatalytic degradation of the methylene blue MB under UV illumination has been carried out. It is indicated that the samples exhibit excellent photocatalytic activity. Besides, the samples assisted with surfactants possess higher photocatalytic activity than the sample without any surfactants, wherein the sample with SDS as an additive shows the highest photocatalytic activity, which is able to reach 89.6% MB degradation ratio within 60 min illumination. Moreover, the effects of important operational parameters such as initial MB concentration, catalyst loading and pH were also investigated. The above sample under the optimum conditions obtained the maximum MB degradation ratio up to 96.5%, which is higher than that of the commercial TiO₂ P25 under the same conditions. It can be concluded that CeO₂ will be a potential photocatalyst in the application of organic pollutant.     

Preparation and characterization of iodine-doped mesoporous TiO2 by hydrothermal method

Iodine-doped mesoporous TiO₂ (I/TiO₂) was prepared by hydrothermal method, using tetrabutyl titanate as precursor, potassium iodate as iodine sources. The as-prepared I/TiO₂ catalysts were characterized by UV-vis, XRD, TEM, BET, TG/DTA, XPS and photoluminescence (PL) spectroscopy. Production of OH radicals on the I/TiO₂ surface was detected by the PL technique using terephthalic acid as a probe molecule. The effects of hydrothermal reaction temperature, calcination temperature and iodine doping content on the structure and properties of the catalysts were investigated. The results showed that iodine-doped TiO₂ calcinated at 300 °C have good anatase crystal. The optimal hydrothermal conditions have been determined to be that reaction temperature 120 °C, calcinated temperature 300 °C and added 1.16 mmol iodine dopants. The average particle size of I/TiO₂ synthesized under optimal condition (I-3 sample) is about 3.9 nm. The I-3 photocatalyst contains 100% anatase crystalline phase of TiO₂. BET specific surface area of I-3 sample is184.8 m² g⁻¹ and is 3.67 times that of pure TiO₂ (50.37 m² g⁻¹). Iodine in I/TiO₂ catalyst mainly exists in the form of I₂, and photoactivity of I/TiO₂ catalyst in visible light comes from photosensitize of I₂. I/TiO₂ catalysis shows very high efficiency for the degradation of phenol under visible light.     

Pt/CeO2-ZrO2/Al2O3催化剂的光谱表征

利用拉曼光谱表征了不同方法添加ＣｅＯ２－ＺｒＯ２混合氧化物对Ｐｔ／Ａｌ２Ｏ３催化剂的影响,并采用了ＸＲＤ,Ｈ２化学吸附,ＢＥＴ表征了相应的分散度影响。结果表明：Ｃｅ、Ｚｒ、与金属Ｐｔ存在着强的相互作用,而ＣｅＯ２－ＺｒＯ２以盐的形式加入时,高度分散在Ａｌ２Ｏ３载体上,提高贵金属Ｐｔ的分散度,进而提高了反应的活性。     

Mechano‐Chemical Changes of Nano Sized α‐Al2O3 During Wet Dispersion in Stirred Ball Mills

The mechano‐chemical changes in synthetic α‐Al₂O₃ during wet dispersion in a stirred ball mill, are studied. It is shown that a second phase is generated which can be identified as an aluminum hydroxide (Bayerite) by use of dynamic scanning calorimetry (DSC), X‐ray diffraction (XRD), thermogravimetry (TG), Fourier transformed infrared (FTIR) spectroscopy and transmission electron microscopy (TEM). The amount of the Bayerite phase produced increases with milling time. A comparison of the evaluated amounts from TG‐ and DSC‐measurements are in reasonable agreement. Furthermore, the measured BET surface area shows a strong dependence on the temperature of sample preparation. Depending on the temperature, the bayerite phase is seen to convert to the α‐phase again and also forms meso‐ and possibly micro‐pores, leading to a high BET surface area. In this paper, we highlight the necessity for using different methods to characterize the dispersion process, and for a correct interpretation of the measurement results.     

触发电压对±100 kV多级多通道开关性能的影响

研制了一种用于快脉冲直线型脉冲变压器的±100 kV多级多通道火花开关,研究了触发电压极性、幅值对多级多通道火花开关触发性能的影响,分析了不同触发电压下开关各部分延时及抖动。研究结果表明:触发电压的极性对双极性多级多通道火花开关触发性能影响较小;开关的触发放电延时和抖动随着触发电压的增大而减小。进一步分析了多级多通道火花开关的触发击穿模式以及影响开关击穿延时和抖动的主要因素,提出了减小开关触发击穿延时及抖动的技术途径。     

Synthesis of a magnetically separable composite photocatalyst with high photocatalytic activity under sunlight

A novel magnetically separable composite photocatalyst (N-doped titania-coated γ-Fe₂O₃ magnetic activated carbon) was prepared. It consists of N-doped titania, activated carbon and γ-Fe₂O₃. The whole processes were carried out under low temperature. The prepared sample was characterized by XRD, DRS, SEM, BET and vibrating sample magnetometer (VSM). The photocatalytic activity was determined by degradation of Reactive Brilliant Red X-3B in an aqueous solution under solar irradiation. Results showed that this as-prepared composite photocatalyst exhibited much higher photocatalytic activity than Degussa P25. Furthermore, the photocatalyst can be separated easily by an external magnetic field. Thus, the photocatalyst can be recycled without mass losing, and the degradation percent of X-3B decreased less than 2% after six cycles.     

Enhanced adsorption and visible-light-induced photocatalytic activity of hydroxyapatite modified Ag-TiO2 powders

In order to get a kind of materials with enhanced adsorption and photocatalytic performance, hydroxyapatite modified Ag-TiO₂ powders (Ag-TiO₂-HAP) were prepared by a facile wet chemical strategy. The powders were characterized by X-ray diffraction (XRD), X-ray photoelectron spectroscopy (XPS), UV-vis absorption spectroscopy, N₂ adsorption-desorption measurement (BET), photoluminescence spectroscopy (PL), etc. The photocatalytic activities were evaluated by photocatalytic oxidation decomposition of acetone in air under visible-light illumination. The results showed that the coupled system indicated a highest photocatalytic activity and photochemical stability under visible-light irradiation than all the other catalysts. The intensively improved visible-light-induced photocatalytic activity of the Ag-TiO₂-HAP hybrids could be attributed to its strong absorption in the visible-light region, low recombination rate of the electron-hole pair and large BET specific surface area.