(111)择优取向的Pb(Zr0.52Ti0.48)O3铁电薄膜的制备及研究

选用不同浓度的Pb(Zr_0.52Ti_0.48)O₃溶胶，用Sol-gel法在Pt/Ti/SiO₂/Si基片上沉积一层厚度不同的Pb(Zr_0.52Ti_0.48)O₃ (PZT52)过渡层，经400℃烘烤、550℃退火等程序后，再用Sol-gel法在PZT52过渡层上沉积Pb(Zr_0.52Ti_0.48)O _{关键词： PZT铁电薄膜 择优取向 过渡层 剩余极化强度}     

Au/PZT/BIT/p-Si异质结的制备与性能研究

采用脉冲激光沉积(PLD)工艺,制备了以Bi₄Ti₃O₁₂(BIT)为过渡阻挡层的Au/PZT/BIT/p-Si异质结.研究了BIT铁电层对Pb(Zr_0.52Ti_0.48)O₃(PZT)薄膜晶相结构、铁电及介电性能的影响,对Au/PZT/BIT/p-Si异质结的导电机制进行了讨论.氧气氛530℃淀积的PZT为多晶铁电薄膜,与直接淀积在Si基片上相比,加入BIT铁电层后PZT铁 关键词： 铁电薄膜 异质结构 脉冲激光沉积(PLD)     

Pb(Zr0.3Ti0.7)O3铁电薄膜激光感生电压效应

采用脉冲激光沉积(PLD)技术在LaSrAlTaO₃(LSATO),LaAlO₃(LAO)和SrTiO₃(STO)的单晶倾斜衬底上成功制备了Pb(Zr_0.3Ti_0.7)O₃(PZT)薄膜,在三种倾斜衬底上生长的PZT薄膜中都首次发现了LIV效应.对PZT/LSATO薄膜在a,c轴两种不同取向择优生长下的LIV效应做了研究,发现在薄膜c轴取向择优生长 关键词： 激光感生电压效应 铁电薄膜 薄膜生长取向 原子层热电堆     

用改进的sol-gel法制备锆钛酸铅薄膜及其物相转化的研究

利用改进的solgel法,在Pt/Ti/SiO2/Si衬底上制备了PbZr0.5Ti0.5O3(PZT50/50)薄膜.采用了一种新的方式,从同一前驱体溶液得到了厚度各异的单一退火层.研究了薄膜的结构和性质随单层退火厚度的改变而发生的变化,发现随着单一退火层厚度的降低,薄膜(111)取向的程度增大,同时薄膜的剩余极化和介电常量也逐渐增高.当单一退火层厚度降低到约为40nm时,可得到高度(111)择优取向的PZT薄膜.从薄膜成核机理的基础上讨论了薄膜结构变化的内在因素,认为随单一退火层厚度的增加薄膜由单一的 关键词：     

Co:BaTiO3/Si(100)纳米复合薄膜制备、微结构及其紫外光电子能谱研究

采用脉冲激光气相沉积(PLD)方法,在Si(100)晶面上制备了Co:BaTiO₃纳米复合薄膜.采用X射线衍射(XRD)结合透射电镜(TEM)方法研究了两种厚度Co:BaTiO₃纳米复合薄膜的晶体结构,当薄膜厚度约为30 nm时,薄膜为单一择优取向;当薄膜厚度约为100nm时,薄膜呈多晶结构.原子力显微镜(AFM)分析表明,当膜厚为30nm时,薄膜呈现明显的方形晶粒.采用紫外光电子能谱(UPS)研究了Co的价态和Co:BaTiO₃纳米复合薄 关键词： 3')" href="#">BaTiO₃ 纳米复合薄膜 紫外光电子能谱     

PbTiO3/PbZr0.3Ti0.7O3/PbTiO3夹心结构铁电薄膜子晶层的优化

用Sol-Gel法制备了Pb_(1+x)TiO₃/PbZr_03Ti_07O₃/Pb_(1+x)TiO₃(PT/PZT/PT)夹心结构及PZT铁电薄膜,为了获得高质量的PT/PZT/PT夹心结构铁电薄膜,使用不同过量Pb配比(x)的PbTiO₃ (PT)层进行制备,以获得优化的PT子晶层.X射线 关键词： PT/PZT/PT 夹心结构 子晶 铁电薄膜     

La0.3Sr0.7TiO3模板层对Pb(Zr0.5Ti0.5)O3薄膜的铁电性能增强效应的研究

通过sol-gel法在Si (111) 基片上分别制备了LaNiO₃(LNO)底电极和LaNiO₃/La_0.3Sr_0.7TiO₃ (LNO/LSTO)底电极.然后采用sol-gel 方法，在两种衬底上分别制备了Pb (Zr_0.5Ti_0.5)O₃ (PZT)铁电薄膜.XRD分析表明，两种PZT薄膜均具有钙钛矿结构，且在LNO底电极上的PZT薄膜呈(100) 择优取向，而在LNO/LSTO底电极上的PZT薄膜呈随机取向.铁电性能测试表明，相对LNO衬底上制备的PZT薄膜，在LNO/LSTO底电极上制备的PZT薄膜的剩余极化强度得到了有效的增强，同时矫顽场也增大.介电常数和漏电流的测试表明，LNO/LSTO底电极上制备的PZT薄膜具有大的介电常数和漏电流. 关键词： PZT薄膜 铁电性 漏电流 0.3Sr_0.7TiO₃')" href="#">La_0.3Sr_0.7TiO₃     

Nd-Fe-B/FeCo多层纳米复合膜的结构和磁性

制备了Nd₂₈Fe₆₆B₆/Fe₅₀Co₅₀多层纳米复合磁性薄膜，对溅射态和650℃退火处理15 min试样的相成分分析和微结构的观察显示，溅射态薄膜呈非晶态，经650℃退火处理15 min后，薄膜主要相成分为硬磁性Nd₂Fe₁₄B相和软磁性相FeCo(110)相.Nd₂Fe₁₄B相呈柱状，其易磁化c轴垂直于膜面，尺寸约10 nm.在硬磁性相和软磁性相之间存在少量富Nd相和非晶态，富Nd相大小约7 nm.磁性测量和分析表明，1)该系列薄膜退火态具有垂直于膜面的磁晶各向异性.2)对于固定厚度(10 nm)层Nd-Fe-B和不同厚度(t_FeCo=1—100 nm)层FeCo多层纳米复合膜,剩磁随软磁相FeCo 厚度的增加快速增加，而矫顽力则减小.当t_FeCo=5 nm时，最大磁能积达到200 kJ/m³. 3)硬磁相Nd-Fe-B层和软磁相FeCo层之间交换耦合导致剩磁和磁能积增强. 关键词： Nd-Fe-B/FeCo多层纳米复合膜 交换耦合 磁各向异性     

非晶钛酸锶钡薄膜的金属有机分解法制备及其光学性能

本文采用2-辛酸钡(Ba(C₈H₁₅O₂)₂)和3-甲基丁基醋酸盐(CH₃COOC₂H₄CH(CH₃)₂-)为基的特殊前驱体溶液,在硅和石英基片上低温制备Ba_0.7Sr_0.3TiO₃ (BST0.7)薄膜.性能测试结果表明,厚度约为214 nm的非晶BST0.7薄膜的光学带隙能和折射率分别为4.27 eV和n=1.94.薄膜在可见光和近红外区域的消光系数远远低于多晶BST薄膜,约为10^-3数量级.激发波长为450 nm时,在室温环境下非晶BST0.7薄膜在波长520—610 nm处发出强烈的可见光,峰值为540—570 nm,而结晶态的BST0.7薄膜则无发光现象. 关键词： 钛酸锶钡 非晶薄膜 金属有机分解法 光学性能     

AlN/Si3N4纳米多层膜的外延生长与力学性能

采用射频磁控溅射方法制备单层AlN, Si₃N₄薄膜和不同调制周期的AlN/Si₃N₄纳米多层膜.采用X射线衍射仪、高分辨透射电子显微镜和纳米压痕仪对薄膜进行表征.结果发现,多层膜中Si₃N₄层的晶体结构和多层膜的硬度依赖于Si₃N₄层的厚度.当AlN层厚度为4.0nm、 Si₃N₄层厚度 关键词： 3N₄纳米多层膜')" href="#">AlN/Si₃N₄纳米多层膜 外延生长 应力场 超硬效应     

The effect of microwave annealing on the electrical characteristics of lanthanum doped bismuth titanate films obtained by the polymeric precursor method

Lanthanum doped bismuth titanate thin films (Bi_3.25La_0.75Ti₃O₁₂ - BLT) were produced by the polymeric precursor method and crystallized in a domestic microwave oven and in conventional furnace. Using platinum coated silicon substrates configuration, ferroelectric properties of the films were determined with remanent polarization P_r and a coercive field E_c of 3.9 μC/cm² and 70 kV/cm for the film annealed in the microwave oven and 20 μC/cm² and 52 kV/cm for the film annealed in conventional furnace, respectively. The films annealed in conventional furnace exhibited excellent retention-free characteristics at low infant periods indicating that BLT thin films can be a promise material for use in non-volatile memories. On the other hand, the pinning of domains wall causes a strong decay at low infant periods for the films annealed in the microwave furnace which makes undesireable the application for future FeRAMS memories.     

(111)取向(Pb,La)TiO3铁电薄膜中90°纳米带状畴与热释电性能的研究

采用射频磁控溅射技术在Pt/Ti/SiO₂/Si(100)衬底上生长了掺镧钛酸铅(PLT)铁电薄膜.用X射线衍射技术(XRD)研究了PLT薄膜结晶性能，结果表明PLT薄膜为 (111)择优取向钙钛矿相织构.使用原子力显微镜(AFM)和压电响应力显微镜(PFM) 分别观察了PLT薄膜的表面形貌和对应区域的电畴结构.PFM观察显示PLT薄膜中存在90°纳米带状畴，电畴的极化为首尾相接的低能量的排列方式，带状畴的宽度为20—60nm.研究了PLT10铁电薄膜的制备条件与性能之间的关系.发现在优化条件下制备的PLT10铁电薄膜的介电常数ε_r为365、介电损耗tgδ为0.02，热释电系数γ为2.18×10^-8C·(cm²·K)^-1，可以满足制备非制冷红外探测器的需要. 关键词： PLT薄膜 电畴 PFM 极化     

Lead-free ferroelectric BaTiO3 doped-(Na0.5Bi0.5)TiO3 thin films processed by pulsed laser deposition technique

The difficulties in synthesizing phase pure BaTiO₃ doped-(Na_0.5Bi_0.5)TiO₃ are known. In this work, we reporting the optimized pulsed laser deposition (PLD) conditions for obtaining pure phase 0.92(Na_0.5Bi_0.5)TiO₃-0.08BaTiO₃, (BNT-BT_0.08), thin films. Dielectric, ferroelectric and piezoelectric properties of BNT-BT_0.08, thin films deposited by PLD on Pt/TiO₂/SiO₂/Si substrates are investigated in this paper. Perovskite structure of BNT-BT_0.08 thin films with random orientation of nanocrystallites has been obtained by deposition at 600 °C. The relative dielectric constant and loss tangent at 100 kHz, of BNT-BT_0.08 thin film with 530 nm thickness, were 820 and 0.13, respectively. Ferroelectric hysteresis measurements indicated a remnant polarization value of 22 μC/cm² and a coercive field of 120 kV/cm. The piezoresponse force microscopy (PFM) data showed that most of the grains seem to be constituted of single ferroelectric domain. The as-deposited BNT-BT_0.08 thin film is ferroelectric at the nanoscale level and piezoelectric.     

Nd掺杂对Bi4Ti3O12铁电薄膜的微结构和铁电性能的影响

利用溶胶-凝胶法在Pt/Ti/SiO₂/Si(100)衬底上制备了Nd掺杂Bi₄Ti₃O₁₂(Bi_4-xNd_xTi₃O₁₂, x=0.00,0.30,0.45,0.75,0.85,1.00,1.50)铁电薄膜样品.研究了Nd掺杂对Bi₄Ti₃O₁₂薄膜的微结构和铁电性能的影响.研究结果表明:Nd掺杂未改变Bi₄Ti₃O₁₂薄膜的基本晶体结构.在掺杂量x<0.45时,Nd³⁺只取代类钙钛矿层中的A位Bi³⁺.当x=0.45时,样品剩余极化强度达最大值,在270kV·cm^-1的电场下为32.7μC·cm^-2.掺杂量进一步增加时,结构无序度开始明显增大,Nd³⁺开始进入(Bi₂O₂)²⁺层,削弱其绝缘层和空间电荷库的作用,导致材料剩余极化逐渐下降.当掺杂量x达到1.50时,掺杂离子最终破坏(Bi₂O₂)²⁺层的结构,材料发生铁电-顺电相变.     

退火气压对Bi3.25La0.75Ti3O12铁电薄膜的微观结构和铁电性能的影响

采用sol-gel法在Pt/TiO₂/SiO₂/p-Si(100)衬底上制备了Bi_3.25La_0.75Ti₃O₁₂(BLT)铁电薄膜,研究了在750 ℃时不同退火气压(p_{O2:10^-4—3 atm)对薄膜微观结构和电学性能的影响.XRD和拉曼光谱结果表明在10^-4和3 atm氧气压下退火 关键词： 3.25}La_0.75Ti₃O₁₂')" href="#">Bi_3.25La_0.75Ti₃O₁₂ 铁电性能 sol-gel法 正交化度     

Effect of buffer layers on the property of Pb(Zr,Ti)O3-Pb(Mn,W,Sb,Nb)O3 thin films grown by pulsed laser deposition

New ferroelectric Pb(Zr,Ti)O₃-Pb(Mn,W,Sb,Nb)O₃ (PZT-PMWSN) thin film has been deposited on a Pt/Ti/SiO₂/Si substrate by pulsed laser deposition. Buffer layer was adopted between film and substrate to improve the ferroelectric properties of PZT-PMWSN films. Effect of a Pb(Zr_0.52Ti_0.48)O₃ (PZT) and (Pb_0.72La_0.28)Ti_0.93O₃ (PLT) buffer layers on the stabilization of perovskite phase and the suppression of pyrochlore phase has been examined. Role of buffer layers was investigated depending on different types of buffer layer and thickness. The PZT-PMWSN thin films with buffer layer have higher remnant polarization and switching polarization values by suppressing pyrochlore phase formation. The remnant polarization, saturation polarization, coercive field and relative dielectric constant of 10-nm-thick PLT buffered PZT-PMWSN thin film with no pyrochlore phase were observed to be about 18.523 μC/cm², 47.538 μC/cm², 63.901 kV/cm and 854, respectively.     

溶胶-凝胶法制备Sr2Bi4Ti5O18薄膜及其铁电性能研究

采用溶胶-凝胶法,在氧气氛中和层层晶化的工艺条件下,成功地制备了沉积在Pt/Ti/SiO₂/Si(100)衬底上的铁电性能优良的Sr₂Bi₄Ti₅O₁₈ (SBTi)薄膜,并研究了SBTi薄膜的微结构、表面形貌、铁电性能和疲劳特性.研究表明：薄膜具有单一的层状钙钛矿结构，且为随机取向；薄膜表面光滑，无裂纹，厚度约为725nm；铁电性能测试显示较饱和、方形的电滞回线，当外电场强度为275kV/cm时 关键词： 溶胶-凝胶法 铁电薄膜 2Bi₄Ti₅O₁₈')" href="#">Sr₂Bi₄Ti₅O₁₈     

SrBi2Ta2O9铁电薄膜微结构及其抗疲劳等铁电特性的研究

在低温Pt/Ti/SiO₂/Si衬底上用脉冲准分子激光沉积技术结合氧气氛下700℃退火获得高质量的SBT薄膜，其择优取向为（008）和（115）．薄膜厚度约为200nm．铁电性能测试显示较饱和的、方形的电滞回线，其剩余极化和矫顽电场分别为10μC/cm²和57kV/cm，在10¹⁰次开关极化后没有显示任何疲劳，在5V直流电压下的漏电流密度约为4×10^-8A/cm²，直流击穿电场约为250kV/cm 关键词：     

Effect of internal strain fields on the controllability of nanodimensional ferroelectric films in a plane capacitor

Nanodimensional ferroelectric heteroepitaxial Ba_0.8Sr_0.2TiO₃ films grown by the layer-by-layer mechanism on MgO(100) substrates are examined by the X-ray diffraction and transmission electron microscopy methods. It is established that, when the thickness of the film changes, the stress relaxation proceeds via generation of misfit dislocations at the film-substrate interface. There exists a critical thickness (≈40 nm) of the film below and above which the film possesses tensile and compression stresses, respectively. Examples of how the stresses influence the insulating properties of the films are given.     

Magnetic, electric, and optical functionalities of (PLZT)x(BiFeO3)1−x ferroelectric-ferromagnetic thin films

We have prepared a series of (PLZT)_x(BiFeO₃)_1−x transparent thin films with thickness of 300 nm by a thermal pyrolysis method. Only films with x≦0.10 formed a single phase of perovskite structure. The film where x=0.10 exhibited both ferromagnetic and ferroelectric properties at room temperature with spontaneous magnetization and coercive magnetic fields of 0.0027μ_B and 5500 G, respectively. The remanent electric polarization and coercive electric field for the film where x=0.10 were 3.0 μC/cm² and 24 kV/cm, respectively. Additionally, films with 0.02≦x≦0.10 showed both magneto-optical effects and the second harmonic generation of transmitted light.