Highly conductive and transparent laser ablated nanostructured Al: ZnO thin films

Al doped ZnO thin films are prepared by pulsed laser deposition on quartz substrate at substrate temperature 873 K under a background oxygen pressure of 0.02 mbar. The films are systematically analyzed using X-ray diffraction, atomic force microscopy, micro-Raman spectroscopy, UV-vis spectroscopy, photoluminescence spectroscopy, z-scan and temperature-dependent electrical resistivity measurements in the temperature range 70-300 K. XRD patterns show that all the films are well crystallized with hexagonal wurtzite structure with preferred orientation along (0 0 2) plane. Particle size calculations based on XRD analysis show that all the films are nanocrystalline in nature with the size of the quantum dots ranging from 8 to 17 nm. The presence of high frequency E₂ mode and longitudinal optical A₁ (LO) modes in the Raman spectra suggest a hexagonal wurtzite structure for the films. AFM analysis reveals the agglomerated growth mode in the doped films and it reduces the nucleation barrier of ZnO by Al doping. The 1% Al doped ZnO film presents high transmittance of ∼75% in the visible and near infrared region and low dc electrical resistivity of 5.94 × 10⁻⁶ Ω m. PL spectra show emissions corresponding to the near band edge (NBE) ultra violet emission and deep level emission in the visible region. Nonlinear optical measurements using the z-scan technique shows optical limiting behavior for the 5% Al doped ZnO film.     

Transparent conductive ZnO:Al films grown by atomic layer deposition for Si-wire-based solar cells

Structural, electrical, and optical properties of atomic layer-controlled Al-doped ZnO (ZnO:Al) films grown by atomic layer deposition (ALD) on glass substrates were characterized at various growth temperatures for use as transparent electrodes. The Al atomic content in ZnO:Al films increased due to the reduced ZnO film growth rate with increasing temperature. The preferred orientation of ZnO:Al films was changed, and the optimum condition for best crystallinity was identified by varying the growth temperature. Furthermore, the carrier concentration of free electron was increased by substituting the Zn sites with Al atoms in the crystal, resulting from monolayer growth based on alternate self-limiting surface chemical reactions. The electrical resistivity of ZnO:Al film grown by ALD at 225 °C reached the lowest value of 8.45 × 10⁻⁴ Ω cm, with a carrier mobility of 9.00 cm² V⁻¹ s⁻¹ and optical transmittance of ∼93%. This result demonstrates that ZnO:Al films grown by ALD possess excellent potential for applications in electronic devices and displays as transparent electrodes and surface passivation layers.     

Investigation of p-type behavior in Ag-doped ZnO thin films by E-beam evaporation

Ag-doped ZnO (ZnO:Ag) thin films were grown on glass substrates by E-beam evaporation technique. The structural, electrical and optical properties of the films were investigated as a function of annealing temperature. The films were subjected to post annealing at different temperatures in the range of 350-650 °C in an air ambient. All the as grown and annealed films at temperature of 350 °C showed p-type conduction. The films lost p-type conduction after post annealing treatment temperature of above 350 °C, suggesting a narrow post annealing temperature window for the fabrication of p-type ZnO:Ag films. ZnO:Ag film annealed at 350 °C revealed lowest resistivity of 7.25 × 10⁻² Ω cm with hole concentration and mobility of 5.09 × 10¹⁹ cm⁻³ and 1.69 cm²/V s, respectively. Observation of a free-to-neutral-acceptor (e,A^o) and donor-acceptor-pair (DAP) emissions in the low temperature photoluminescence measurement confirms p-type conduction in the ZnO:Ag films.     

The influence of titanium on the properties of zinc oxide films deposited by radio frequency magnetron sputtering

TiO₂-doped zinc oxide thin films were deposited on glass substrates by radio frequency (RF) magnetron sputtering with TiO₂-doped ZnO targets in an argon atmosphere. The structural properties of TiO₂-doped ZnO films doped with different TiO₂ contents were investigated. The experimental results show that polycrystalline TiO₂-doped ZnO films had the (0 0 2) preferred orientation. The deposition parameters such as the working pressure and substrate temperature of TiO₂-doped ZnO films were also investigated. The crystalline structure of the TiO₂-doped ZnO films gradually improved as the working pressure was lowered and the substrate temperature was raised. The lowest electrical resistivity for the TiO₂-doped ZnO films was obtained when the Ti addition was 1.34 wt%; its value was 2.50 × 10⁻³ Ω cm, smaller than that found in previous studies. The transmittance of the TiO₂-doped ZnO films in the visible wavelength range was more than 80%. The optical energy gap was related to the carrier concentration, and was in the range of 3.30-3.48 eV.     

Growth of Ga-doped ZnO films with ZnO buffer layer by sputtering at room temperature

Gallium-doped zinc oxide films have been grown on glass substrates with and without ZnO buffer layers by r.f. magnetron sputtering at room temperature. In this approach, the grey relational Taguchi method analysis is adopted to solve the coating process with multiple deposition qualities. Optimal coating parameters can then be determined by using the gray relational grade as a performance index. The GZO coating parameters (r.f. power, sputtering pressure, O₂/(Ar+O₂) flow-rate ratios, and deposition time) are optimized, by taking into account the multiple performance characteristics (structural, morphological, deposition rate, electrical resistivity, and optical transmittance). The results indicate that with the grey relational Taguchi method, the electrical resistivity of GZO films is reduced from 9.23×10⁻³ to 5.77×10⁻³ Ω cm and optical transmittance increases from 79.42% to 82.95%, respectively. The ZnO buffer layer can reduce the electrical resistivity of GZO films from 5.77×10⁻³ to 2.38×10⁻³ Ω cm. It can be anticipated that room temperature deposition enables film deposition onto polymeric substrates for flexible optoelectronic devices.     

Effect of substrate temperature on properties of multilayer thin film based on ZnO and Mo-doped indium oxide

Zinc oxide/molybdenum-doped indium oxide/zinc oxide (ZnO/IMO/ZnO) multilayer thin films are grown using pulsed laser deposition technique. The effect of substrate temperature on structural, optical, and electrical properties of multilayer films is studied. It is observed that films grown at high substrate temperature are oriented along (0 0 2) and (2 2 2) direction for ZnO and IMO respectively. The crystallinity of these films increases with increase in substrate temperature. It is also seen that conductivity, carrier concentration, and mobility increase with increase in temperature. The multilayer film grown at 500 °C has low resistivity (7.67 × 10⁻⁵ Ω cm), high carrier concentration (3.90 × 10²⁰ cm⁻³), and high mobility (209 cm²/Vs).     

Optical and electrical properties of nanocrystal zinc oxide films prepared by dc magnetron sputtering at different sputtering pressures

The nanocrystal thin films of zinc oxide doped by Al (ZnO:Al) were deposited by dc reactive magnetron sputtering on the glass substrates, in the pressure range of 33-51 Pa. From the X-ray diffraction patterns, the nanocrystalline structure of ZnO:Al films and the grain size were determined. The optical transmission spectra depend from the sputtering pressure, but their average value was 90% in the range from 33 Pa to 47 Pa. Also, the sputtering pressure changes the optical band gap of ZnO:Al films, which is highest for films deposited at 37 Pa, 40 Pa and 47 Pa. The obtained films at room temperature have a sheet resistance of 190 Ω/cm² which increases with time, but the films annealed at temperature of 400 °C have constant resistance. The surface morphology of the films was studied by Scanning electron microscopy. XPS spectra showed that the peak of O1s of the as-deposited films is smaller than the peak of the annealed ZnO:Al films.     

Room temperature soft chemical route for nanofibrous wurtzite ZnO thin film synthesis

Room temperature soft chemical deposition route has been utilized to grow thin films of ZnO on glass substrate. Annealing at 673 K removed zinc hydroxide phase and nanofibrous ZnO films with wurtzite crystal structure were obtained. Decrease in the room temperature electrical resistivity from 10⁷ to 10⁴ Ω cm was observed after annealing. The nanofibrous ZnO thin films were sensitive to the explosive liquefied petroleum gas (LPG) and the maximum response of 17% at 698 K under the exposure of 6500 ppm of LPG was obtained.     

Preparation and characterization of ZnO thin films prepared by thermal oxidation of evaporated Zn thin films

In this paper, the experimental results regarding some structural, electrical and optical properties of ZnO thin films prepared by thermal oxidation of metallic Zn thin films are presented.Zn thin films (d=200–400 nm) were deposited by thermal evaporation under vacuum, onto unheated glass substrates, using the quasi-closed volume technique. In order to obtain ZnO films, zinc-coated glass substrates were isochronally heated in air in the 300–660 K temperature range, for thermal oxidation.X-ray diffraction (XRD) studies revealed that the ZnO films obtained present a randomly oriented hexagonal nanocrystalline structure. Depending on the heating temperature of the Zn films, the optical transmittance of the ZnO films in the visible wavelength range varied from 85% to 95%. The optical band gap of the ZnO films was found to be about 3.2 eV. By in situ studying of the temperature dependence of the electrical conductivity during the oxidation process, the value of about 2×10⁻² Ω⁻¹ m⁻¹ was found for the conductivity of completely oxidized ZnO films.     

Characterization of ZnO-SnO2 thin film composites prepared by pulsed laser deposition

Thin films of ZnO-SnO₂ composites have been deposited on Si(1 0 0) and glass substrates at 500 °C by pulsed laser ablation using different composite targets with ZnO amount varying between 1 and 50 wt%. The effect of increasing ZnO-content on electrical, optical and structural properties of the ZnO-SnO₂ films has been investigated. X-ray diffraction analysis indicates that the as-deposited ZnO-SnO₂ films can be both crystalline (for ZnO <1 wt%) and amorphous (for ZnO ≥ 10 wt%) in nature. Atomic force microscopy studies of the as-prepared composite films indicate that the surfaces are fairly smooth with rms roughness varying between 3.07 and 2.04 nm. The average optical transmittance of the as-deposited films in the visible range (400-800 nm), decreases from 90% to 72% for increasing ZnO concentration in the film. The band gap energy (E_g) seems to depend on the amount of ZnO addition, with the maximum obtained at 1 wt% ZnO. Assuming that the interband electron transition is direct, the optical band gap has been found to be in the range 3.24-3.69 eV for as-deposited composite films. The lowest electrical resistivity of 7.6 × 10⁻³ Ω cm has been achieved with the 25 wt% ZnO composite film deposited at 500 °C. The photoluminescence spectrum of the composite films shows a decrease in PL intensity with increasing ZnO concentration.