Conversion of covalent to ionic character of V2O5–CeO2–PbO–B2O3 glasses for solid state ionic devices

xV₂O₅–xCeO₂–(30−x)PbO–(70−x) B₂O₃ glasses are synthesized by using the melt quench technique. The number of studies such as XRD, density, molar volume, optical band gap, refractive index and FTIR spectroscopy are employed to characterize the glasses. The band gap decreases from 2.20 to 1.78 eV and density increases from 3.49 to 4.25 g/cm³. FTIR spectroscopy reveals that incorporation of V₂O₅ in glass network helps to convert the structural units of [BO₃] into [BO₄]. At higher concentration of vanadium, VO vibration of [VO₅] structural units and V–O–V vibration are present. The bond ionicity of glasses increases with incorporation of V₂O₅ contents.     

Modification in structural and optical properties of ZnO, CeO2 doped Al2O3-PbO-B2O3 glasses

The structural and optical analysis of glasses is carried out by XRD, FTIR, density and UV visible spectroscopic measurement techniques. XRD results have confirmed the glassy nature of the samples. The FTIR spectral analysis reveals that with the combined presence of ZnO and CeO₂ contents in Al₂O₃-PbO-B₂O₃ glasses, more BO₃ groups are transformed into BO₄. The optical analysis reveals that optical band gap energy decreases more for CeO₂-ZnO-Al₂O₃-PbO-B₂O₃ glasses (from 2.28 to 1.84 eV). The presence of CeO₂ and ZnO in the glass samples causes more compaction of the borate network due to the formation of more BO₄ groups and the presence of ZnO₄ groups, which results an increase in density, refractive index and decrease of molar volume.     

Role of WO3 in structural and optical properties of WO3-Al2O3-PbO-B2O3 glasses

Glass samples of composition xAl₂O₃-20PbO-(80−x)B₂O₃ and xWO₃-xAl₂O₃-20PbO-(80−2x)B₂O₃ with x varying from 0% to 10% mole fraction are prepared by melt quench technique. The optical band gap decreases (from 3.21 to 2.37 eV) more for WO₃-Al₂O₃-PbO-B₂O₃ glasses with an addition of WO₃ content. The FTIR spectral studies have pointed out the conversion of structural units of BO₃ to BO₄ and WO₄ to WO₆ in these glasses. The increase in density from 4.51 to 5.80 g cm⁻³ for WO₃-Al₂O₃-PbO-B₂O₃ glasses is observed with an increase in WO₃ content. This is observed that the atomic structure changes more with the incorporation of WO₃. This is due to the formation of WO₆, WO₄ and BO₄ units.     

Effect of WO3 on structural and optical properties of CeO2-PbO-B2O3 glasses

Pure and WO₃ doped CeO₂-PbO-B₂O₃ glasses are prepared by the melt-quench technique. The structural and optical analyses of glasses are carried out by XRD, FTIR, density and UV-vis spectroscopic measurement techniques. FTIR analysis indicates the transformation of structural units of BO₃ into BO₄ with W-O-W vibration and the presence of WO₄ and WO₆ units observed with increase in WO₃ contents. Decrease in band gap for CeO₂-PbO-B₂O₃ glasses from 2.89 to 2.30 eV and for WO₃ doped glasses from 2.89 to 1.95 eV has been observed and discussed. This decrease in band gap with WO₃ doping approaches to semiconductor behavior. It shows that the presence of WO₃ in the glass samples causes more compaction of the borate network due to the formation of BO₄ groups and the presence of WO₄ and WO₆ groups, which result in a decrease in the optical band gap energy and increase in the density.     

Investigation of structural,physical and optical properties of CeO2–Bi2O3–B2O3 glasses

xCeO₂–30Bi₂O₃–(70−x) B₂O₃ glasses are synthesized by using the melt quench technique. A number of studies such as XRD, density, molar volume, optical band gap, refractive index and FTIR spectroscopy are employed to characterize the glasses. The band gap decreases from 2.15 to 1.61 eV, refractive index increases from 2.67 to 2.93 and density increases from 4.151 to 4.633 g/cm³. The decrease in band gap with CeO₂ doping approaches the semiconductor behavior. FTIR spectroscopy reveals that incorporation of CeO₂ into glass network helps to convert the structural units of [BO₃] into [BO₄] and results in Bi–O bond vibration of [BiO₆].     

Structural and optical properties of WO3-ZnO-PbO-B2O3 glasses

Glass samples of compositions 20PbO-80B₂O₃ and xWO₃—(20−x) ZnO-20PbO-60B₂O₃ with x varying from 0% to 10% mole fraction are prepared by the melt quench technique. Decrease in the band gap from 2.86 to 2.16 eV for ZnO-PbO-B₂O₃ glasses with an increase in the WO₃ content has been observed and discussed. The FTIR spectral studies have pointed out the conversion of structural units of BO₃ to BO₄ and WO₄ to WO₆ with the presence of W-O-W vibration of tungsten and incorporation of ZnO₄ structural units of zinc in these glasses. The increase in density from 2.75 to 4.03 gcm⁻³ for ZnO-PbO-B₂O₃ glasses is observed with an increase in WO₃ content. Due to the formation of WO₆, WO₄ and BO₄ units, changes in the atomic structure with WO₃ composition are observed and discussed.     

Bioactivity of SiO2-CaO-P2O5-Na2O glasses containing zinc-iron oxide

Glasses with composition x(ZnO,Fe₂O₃)(65 − x)SiO₂20(CaO,P₂O₅)15Na₂O (6 ≤ x ≤ 21 mol%) were prepared by melt-quenching technique. Bioactivity of the glasses was investigated in vitro by examining apatite formation on the surface of glasses treated in acellular simulated body fluid (SBF) with ion concentrations nearly equal to those in human blood plasma. Formation of bioactive apatite layer on the samples treated in SBF was confirmed by using Fourier transform infrared reflection (FTIR) spectroscopy, grazing incidence X-ray diffraction (GI-XRD) and scanning electron microscope (SEM) equipped with energy dispersive X-ray spectrometer. Development of an apatite structure on the surface of the SBF treated glass samples as functions of composition and time could be established using the GI-XRD data. FTIR spectra of the glasses treated in SBF show features at characteristic vibration frequencies of apatite after 1-day of immersion in SBF. SEM observations revealed that the spherical particles formed on the glass surface were made of calcium and phosphorus with the Ca/P molar ratio being close to 1.67, corresponding to the value in crystalline apatite. Increase in bioactivity with increasing zinc-iron oxide content was observed. The results have been used to understand the evolution of the apatite surface layer as a function of glass composition and immersion time in SBF.     

Structural investigation of xAg2O·(100−x)·[2B2O3·As2O3] glasses doped with manganese ions

Structural analysis of x[(100−y)Ag₂O·yMnO]·(100−x)[2B₂O₃·As₂O₃] glasses, with x=10 mol% and 0≤y≤10 mol%, was performed by means of FT-IR and FT-Raman spectroscopies. The purpose of this work is to investigate the structural changes that appear in the xAg₂O·(100−x)·[2B₂O₃·As₂O₃] glasses with the addition and increase in manganese ions content. FT-IR measurements revealed the presence of pyro-, ortho-, di-, tri-, tetra- and penta-borate groups and structural units characteristic to As₂O₃ in the structure of the studied glasses. FT-IR spectroscopy measurements also show that BO₃ units are the main structural units of the glass system. The presence of structural units characteristic to Ag₂O were not directly evidenced by FT-IR spectroscopy. In addtition, the FT-Raman analysis evidenced the presence of boroxol rings in the structure of the studied glasses.     

Crystallization kinetics of Li2O-PbO-V2O5 glasses

Lead vanadate glasses of the system 5Li₂O−(45−x) PbO−(50+x) V₂O₅, with x=0, 5, 10, and 15 mol% have been prepared and studied by differential scanning calorimetry (DSC). The crystallization kinetics of the glasses were investigated under non-isothermal conditions applying the formal theory of transformations for heterogeneous nucleation to the experimental data obtained by DSC using continuous-heating techniques. In addition, from dependence of the glass-transition temperature (T_g) on the heating rate, the activation energy for the glass transition was derived. Similarly the activation energy of the crystallization process was determined and the crystallization mechanism was characterized. The results reveal the increase of the activation energy for glass transition which was attributed to the increase in the rigidity, the cross-link density and the packing density of these glasses. The phases into which the glass crystallizes have been identified by X-ray diffraction. Diffractograms of the transformed material indicate the presence of microcrystallites of Li_0.30V₂O₅, Li_0.67O₅V₂, LiV₆O₁₅, Li₄O₄Pb, and O₇Pb₂V₂ in a remaining amorphous matrix.     

Optical properties of Er in MoO3-Bi2O3-TeO2 glasses

Erbium-doped MoO₃−Bi₂O₃−TeO₂ (MBT) glasses suitable for broadband optical amplifier applications have been fabricated and characterized optically. The maximum phonon band of undoped glasses is at 915 cm⁻¹, and the emission from the Er³⁺: ⁴I_13/2 → ⁴I_15/2 transition locates around 1.53 μm with a full width at half maximum (FWHM) of ∼80 nm. The lifetime and quantum efficiency of the ⁴I_13/2 level are 2.13 ms and ∼90%, respectively. Under the same measurement condition, the upconversion emission intensities at 550 nm in Er³⁺-doped MBT glasses is about 30 times weaker than that in Er³⁺-doped Na₂O−ZnO−TeO₂ (NZT) glasses.     

Reactivity and XAFS study on (1−x)CeO2-xNiO (x=0.025-0.3) system in the two-step water-splitting reaction for solar H2 production

The redox reaction of Ce⁴⁺-Ce³⁺ promoted by the catalytic function of nickel ions in a (1−x)CeO₂-xNiO solid solution was investigated for solar H₂ production by the two-step water-splitting reaction. By irradiation using an infrared imaging lamp as a solar simulator, the O₂-releasing reaction with (1−x)CeO₂-xNiO solid solution proceeded at 1673-1873 K, and its reduced form was produced. The amounts of H₂ gas evolved by the reduced form were 1.2-2.5 cm³/g and the evolved gases amounts ratio of H₂/O₂ was nearly 2, which is equal to the stoichiometric value of the water-splitting reaction (H₂O=H₂+1/2O₂). The maximum amounts of evolved H₂ and O₂ gases were obtained at the Ce:Ni mole ratio of 0.95:0.05 (x=0.05) in the (1−x)CeO₂-xNiO system. The X-ray absorption fine structure (XAFS) measurement showed that the O₂-releasing and H₂-generation reactions with (1−x)CeO₂-xNiO solid solution were repeatable with the redox system of Ce⁴⁺-Ce³⁺, which was enhanced by the catalytic function of Ni²⁺-Ni⁰.     

Optical absorption and thermoluminescence studies on LiF-Sb2O3-B2O3 glasses doped with Ni ions

20LiF-(30−x)Sb₂O₃-50B₂O₃:xNiO glasses with the value of x (ranging from 0 to 1.0 mol% in steps of 0.2) were prepared. A number of studies, viz. differential scanning calorimetry, optical absorption, magnetic susceptibility and thermoluminescence, on these glasses were carried out as a function of nickel ion concentration. An anomaly has been observed in all the properties of these glasses when NiO concentration is about 0.6 mol%. The results of these studies were analysed in the light of different environments of nickel ions in the glass network.     

Influence of B2O3 to the inhomogeneous broadening and spectroscopic properties of Er/Yb codoped fluorophosphate glasses

In a three-components fluorophosphate glass system, the introduction of H₃BO₃ brings some valuable influence to the spectroscopic and thermal properties of the glasses. With H₃BO₃ increases from 2 to 20 mol%, Ω₆, S_ed4I13/2, FWHM, T_g and fluorescence lifetime change from 3.21×10⁻²⁰ cm², 1.77×10⁻²⁰ cm², 45 nm, 480 °C and 8.8 ms to 4.66×10⁻²⁰ cm², 2.11×10⁻²⁰ cm², 50 nm, 541 °C and 7.4 ms, respectively. σ_abs, σ_emi, FWHM×τ_f×σ_emi has a maximum when H₃BO₃ is 11 mol%. T_g and T_x−T_g increases with H₃BO₃ introduction. Results showed that in fluorophosphate glasses, proper amount of B₂O₃ can be used as a modifier to suppress upconversion and improve spectroscopic properties, broadband property and crystallization stability of the glasses while keeps the fluorescence lifetime relatively high.     

Reaction of water with Ce-Au(1 1 1) and CeOx/Au(1 1 1) surfaces: Photoemission and STM studies

This article reports photoemission and STM studies for the adsorption and dissociation of water on Ce-Au(1 1 1) alloys and CeO_x/Au(1 1 1) surfaces. In general, the adsorption of water at 300 K on disordered Ce-Au(1 1 1) alloys led to O-H bond breaking and the formation of Ce(OH)_x species. Heating to 500-600 K induced the decomposition or disproportionation of the adsorbed OH groups, with the evolution of H₂ and H₂O into gas phase and the formation of Ce₂O₃ islands on the gold substrate. The intrinsic Ce ↔ H₂O interactions were explored by depositing Ce atoms on water multilayers supported on Au(1 1 1). After adsorbing Ce on ice layers at 100 K, the admetal was oxidized immediately to yield Ce³⁺. Heating to room temperature produced finger-like islands of Ce(OH)_x on the gold substrate. The hydroxyl groups dissociated upon additional heating to 500-600 K, leaving Ce₂O₃ particles over the surface. On these systems, water was not able to fully oxidize Ce into CeO₂ under UHV conditions. A complete Ce₂O₃ → CeO₂ transformation was seen upon reaction with O₂. The particles of CeO₂ dispersed on Au(1 1 1) did not interact with water at 300 K or higher temperatures. In this respect, they exhibited the same reactivity as does a periodic CeO₂(1 1 1) surface. On the other hand, the Ce₂O₃/Au(1 1 1) and CeO_2−x/Au(1 1 1) surfaces readily dissociated H₂O at 300-500 K. These systems showed an interesting reactivity for H₂O decomposition. Water decomposed into OH groups on Ce₂O₃/Au(1 1 1) or CeO_2−x/Au(1 1 1) without completely oxidizing Ce³⁺ into Ce⁴⁺. Annealing over 500 K removed the hydroxyl groups leaving behind CeO_2−x/Au(1 1 1) surfaces. In other words, the activity of CeO_x/Au(1 1 1) for water dissociation can be easily recovered. The behavior of gold-ceria catalysts during the water-gas shift reaction is discussed in light of these results.     

EPR and magnetic susceptibility studies of iron ions in ZnO-Fe2O3-SiO2-CaO-P2O5-Na2O glasses

Room temperature electron paramagnetic resonance (EPR) spectra and temperature dependent magnetic susceptibility data have been obtained on bulk x(ZnO,Fe₂O₃)(65−x)SiO₂20(CaO, P₂O₅)15Na₂O (6≤x≤21 mole%) glasses prepared by melt quenching method. EPR spectra of the glasses revealed absorptions centered at g≈2.1 and 4.3. The variations of the intensity and line width of these absorption lines with composition have been interpreted in terms of the variation in the concentration of the Fe²⁺ and Fe³⁺ ions in the glass and the interaction between the iron ions. EPR and magnetic susceptibility data of the glasses reveal that both Fe²⁺ and Fe³⁺ ions are present in the glasses, with their relative concentration being dependent on the glass composition. The studies reveal superexchange type interactions in these glasses, which are strongly dependent on their iron content.     

Low energy Ar-ion bombardment effects on the CeO2 surface

The structure and electronic properties of epitaxial grown CeO₂(1 1 1) thin films before and after Ar⁺ bombardment have been comprehensively studied with synchrotron radiation photoemission spectroscopy (SRPES). Ar⁺ bombardment of the surface causes a new emission appearing at 1.6 eV above the Fermi edge which is related to the localized Ce 4f¹ orbital in the reduced oxidation state Ce³⁺. Under the condition of the energy of Ar ions being 1 keV and a constant current density of 0.5 μA/cm², the intensity of the reduced state Ce³⁺ increases with increasing time of sputtering and reaches a constant value after 15 min sputtering, which corresponds to the surface being exposed to 2.8 × 10¹⁵ ions/cm². The reduction of CeO₂ is attributed to a preferential sputtering of oxygen from the surface. As a result, Ar⁺ bombardment leads to a gradual buildup of an, approximately 0.69 nm thick, sputtering altered layer. Our studies have demonstrated that Ar⁺ bombardment is an effective method for reducing CeO₂ to CeO_2−x and the degree of the reduction is related to the energy and amount of Ar ions been exposed to the CeO₂ surface.     

Highly active Ce1−xCuxO2 nanocomposite catalysts for the low temperature oxidation of CO

A series of Ce_1−xCu_xO₂ nanocomposite catalysts with various copper contents were synthesized by a simple hydrothermal method at low temperature without any surfactants, using mixed solutions of Cu(II) and Ce(III) nitrates as metal sources. These bimetal oxide nanocomposites were characterized by means of XRD, TEM, HRTEM, EDS, N₂ adsorption, H₂-TPR and XPS. The influence of Cu loading (5-25 mol%) and calcination temperature on the surface area, particle size and catalytic behavior of the nanocomposites have been discussed. The catalytic activity of Ce_1−xCu_xO₂ nanocomposites was investigated using the test of CO oxidation reaction. The optimized performance was achieved for the Ce_0.80Cu_0.20O₂ nanocomposite catalyst, which exhibited superior reaction rate of 11.2 × 10⁻⁴ mmol g⁻¹ s⁻¹ and high turnover frequency of 7.53 × 10⁻² s⁻¹ (1% CO balanced with air at a rate of 40 mL min⁻¹, at 90 °C). No obvious deactivation was observed after six times of catalytic reactions for Ce_0.80Cu_0.20O₂ nanocomposite catalyst.     

Characterization of Pd-CeOx interaction on α-Al2O3 support

The Pd-Ce interaction was studied over CeO₂ (0.3-2.5 wt.%)-Pd (1 wt.%)/α-Al₂O₃ catalysts used in the reforming reaction of CH₄ with CO₂. The samples were characterized by using high resolution transmission electron microscopy (HRTEM) and X-ray photoelectron spectroscopy (XPS). The activity and selectivity behavior was in good agreement with that of other supported metal catalysts (Ni and Pd) modified with different promoters. The preliminary results of HRTEM would indicate that the CeO_x forms small crystallites around the Pd particle. The XPS analysis for the regions of Ce 3d and Pd 3d, gives an account of Ce being present mostly as Ce³⁺ and a high binding energy for Pd 3d_5/2 (335.3 eV), an evidence of Pd-Ce chemical interaction. The Pd/Al XPS intensity ratios vs. the Pd average particle size, determined by TEM, show an excellent correlation for fresh and used catalyst. These results indicate that the diminution of the Pd/Al ratios was due to Pd sintering. Consequently, the small amounts of CeO_x species do not cover the Pd particle, in agreement with the HRTEM results. The overall results stand for the promoter action mechanism of the CeO_x for the reforming reaction with CO₂.     

Crystal structure and photoluminescence of (Y1−xCex)2Si3O3N4

Oxonitridosilicate phosphors with compositions of (Y_1−xCe_x)₂Si₃O₃N₄ (x=0−0.2) have been synthesized by solid state reaction method. The structures and photoluminescence properties have been investigated. Ce³⁺ ions have substituted for Y³⁺ ions in the lattice. The emission and excitation spectra of these phosphors show the characteristic photoluminescence spectra of Ce³⁺ ions. Based on the analyses of the diffuse reflection spectra and the PL spectra, a systematic energy diagram of Ce³⁺ ion in the forbidden band of sample with x=0.02 is given. The best doping Ce content in these phosphors is ∼2 mol%. The quenching temperature is ∼405 K for the 2 mol% Ce content sample. The luminescence decay properties were investigated. The primary studies indicate that these phosphors are potential candidates for application in three-phosphor-converted white LEDs.     

Thermoluminescence of B2O3-Li2O glass system doped with MgO

Lithium borate (LiB) glasses in the system (100−x)B₂O₃-xLi₂O with x=20, 30, 40, 50, 60 and 70 mol% were prepared. The glasses were doped with different concentrations of the order of 10⁻¹, 10⁻², 10⁻³, 10⁻⁴ and 10⁻⁵ of MgO and their thermoluminescent (TL) response was investigated. The irradiations were performed using γ rays from a ⁶⁰Co source in the dose range from 0.1 to 25 kGy. The material displayed good sensitivity for γ-rays and intensity of TL signals is dependent on γ-ray dose and Li₂O content. For each dose level and investigated temperature range (50-350 °C), exactly single isolated glow peak appears in the temperature range of 165-205 °C depending on both Li₂O concentrations and time of exposure. The shape of the glow peak has altered significantly with increase in the gamma ray dose or Li₂O concentrations. The glass composition with x=50 mol% doped with 10⁻³ mol% of MgO presented the best TL response. The results of the present study indicated that the recorded single and isolated high temperature peak is a good candidate for TL dosimetric investigations. This indicates that 50 B₂O₃-50Li₂O-doped with 10⁻³ mol% of MgO is possibly used as materials for radiation dosimetry in the dose range of 0.1-20 kGy.