相似文献
 共查询到10条相似文献,搜索用时 95 毫秒
1.
Abstract

Helium clustering in alpha irradiated copper has been investigated by positron annihilation spectroscopy. Pure copper samples have been homogeneously helium implanted using a cyclotron, yielding helium concentrations of 100 appm and 400 appm. Post-implantation positron lifetime and Doppler broadened annihilation lineshape measurements have been carried out on these Cu samples as a function of isochronal annealing temperature. An annealing stage observed in the isochronal annealing curve viz., a marked reduction in the resolved lifetime τ2 and an increase of its intensity I 2, is explained as due to the formation of helium bubble embryos. At higher annealing temperatures, τ2 corresponding to helium bubbles increases and saturates while its intensity I 2 decreases, indicating an increase in the size of the bubble with a concomitant decrease in the bubble concentration. This stage is interpreted to be the bubble growth stage. From an analysis of positron lifetime parameters in the growth stage, helium stom density, bubble size and bubble concentration have been deduced at various annealing temperatures. The bubble characteristics are found to be affected by the helium dose. The present results on direct helium implanted Cu are compared with those of our earlier study on n-irradiated Cu-B, where helium was introduced using 10B(n, α)7 Li reaction.  相似文献   

2.
181Ta time differential perturbed angular correlation (TDPAC) and positron lifetime measurements were carried out on homogeneously α-implanted CuHf samples. TDPAC measurements indicate the trapping of vacancy clusters and helium associated defect complexes by Hf atoms. The presence of helium-vacancy complexes and helium stabilised voids has been identified by positron lifetime measurements. Further the nucleation and growth stages of helium bubbles have been identified. TDPAC and positron lifetime measurements indicate that Hf atoms act as heterogeneous nucleating centers for helium bubbles. Hf atoms are found to suppress the bubble growth in CuHf as indicated by the results of positron lifetime measurements.  相似文献   

3.
本文介绍应用正电子湮没寿命和多普勒加宽方法研究60%形变铁等时退火各阶段中缺陷的恢复行为,实验结果说明正电子湮没平均寿命τ及多普勒加宽的S参数都是退火温度的函数,完整晶体中湮没寿命τf=111±lPS,缺陷中湮没寿命τd=162±lps,本文还根据捕获模型计算了正电子的捕获速率及τ1,结果证明与理论预期的完全一致,经计算得出捕获正电于的相对缺陷浓度的范围为10-7-10-4数量级。 关键词:  相似文献   

4.
Corrosion-related defects of pure iron were investigated by measuring Doppler broadening energy spectra (DBES) of positron annihilation and positron annihilation lifetime (PAL). Defect profiles of the S-parameter from DBES as a function of positron incident energy up to 30 keV (i.e. ∼1 μm depth) were analyzed. The DBES data show that S-parameter increases as a function of positron incident energy (mean depth) after corrosion, and the increase in the S-parameter is larger near the surface than in the bulk due to corrosion. Furthermore, information on defect size from PAL data as a function of positron incident energy up to 10 keV (i.e. ∼0.2 μm depth) was analyzed. In the two-state trapping model, the lifetime τ2 = 500 ps is ascribed to annihilation of positrons in voids with a size of the order of nanometer. τ1, which decreases with depth from the surface to the bulk, is ascribed to the annihilation of positrons in dislocations and three-dimensional vacancy clusters. The corroded samples show a significant increase in τ1 and the intensity I2, and near the surface the corroded iron introduces both voids and large-size three-dimensional vacancy clusters. The size of vacancy clusters decreases with depth.  相似文献   

5.

Nanoparticles of cobalt ferrite prepared by the co-precipitation method with crystallite size varying from 4.7 to 41 nm have been characterized by positron annihilation lifetime spectroscopy. Three lifetime components are fitted to the lifetime data. The shortest lifetime component is attributed to the delocalized positron lifetime shortened by defect trapping. The intermediate lifetime is assigned to the positron annihilation in diffuse vacancy clusters or microvoids at the grain boundaries and at the grain-boundary triple points. The longest component corresponds to the pick-off annihilation of ortho-positronium formed at the larger voids. The variations in these lifetimes and their relative intensities with annealing temperature and crystallite size have been studied in detail.  相似文献   

6.
Abstract

A pseudo-potential technique has been applied to calculate the annihilation rates for positrons in bubbles of helium gas in gold and silver. The positron pseudo-wavefunction in each case was found to be in a surface state of the metal, the exact form of which displayed a slight dependance on the density of the helium gas. The annihilation rate of the positron was the sum of a nearly constant surface rate and a strongly density dependant annihilation rate with the helium electrons. There is a trend for annihilation with the helium to be greater in metals with low free electron densities, the helium in such metals resting closer to the metal surface thus increasing the overlap of the positron wavefunction with the helium.  相似文献   

7.
C. He  T. Yoshiie  Q. Xu  K. Sato  S. Peneva 《哲学杂志》2013,93(14):1183-1195
Hydrogen in nano-voids in neutron-irradiated nickel has been detected using positron annihilation lifetime spectroscopy (PALS). As positron lifetime is greatly affected by nano-voids bound with hydrogen, special attention was paid to the analysis. The positron lifetime of neutron-irradiated nickel at higher irradiation doses increased with the dose, which is an indicator for vacancy cluster (nano-void) formation in the lattice. The introduction of hydrogen in well-annealed nickel by electrical charging also resulted in an increase in positron lifetime due to vacancy formation. In neutron-irradiated nickel specimens, hydrogen charging shortened the positron lifetime from 456 to 334 ps (irradiation dose: 3 × 10?3 dpa). Isochronal annealing behaviour of hydrogen-charged nickel and neutron-irradiated nickel was also studied. Positron trapping rate was calculated using a simple trapping model. Thermal desorption spectroscopy was used for the investigation of hydrogen behaviour in non-irradiated hydrogen-charged nickel.  相似文献   

8.
钨合金中钾的掺杂会引入大量的缺陷,如尺寸几十纳米的钾泡、高密度的位错以及微米量级的晶粒带来的晶界等,这些缺陷的浓度和分布直接影响合金的服役性能.本文运用正电子湮没谱学方法研究钾掺杂钨合金中的缺陷信息,首先模拟计算了合金中各种缺陷的正电子湮没寿命,发现钾的嵌入对空位团、位错、晶界等缺陷的寿命影响很小;然后测量了不同钾含量掺杂钨合金样品的正电子湮没寿命谱,建立三态捕获模型,发现样品中有高的位错密度和低的空位团簇浓度,验证了钾对位错的钉扎作用,阐述了在钾泡形成初期是钾元素与空位团簇结合并逐渐长大的过程;最后使用慢正电子多普勒展宽谱技术表征了样品中缺陷随深度的均匀分布和大量存在,通过扩散长度的比较肯定了钾泡、晶界等缺陷的存在.  相似文献   

9.
通过分子动力学模拟研究了在相同冲击加载强度下单晶铝中氦泡和孔洞的塑性变形特征,结果发现氦泡和孔洞的塌缩是由发射剪切型位错环引起的,而没有观测到棱锥型位错环发射. 氦泡和孔洞周围的位错优先成核位置基本一致,但是氦泡周围发射的位错环数目比孔洞多,位错环发射速度明显比孔洞快. 且氦泡和孔洞被冲击波先扫过部分比后扫过部分发射位错困难. 通过滑移面上的分解应力分析发现,氦泡和孔洞周围塑性特征的差别是由于氦泡内压引起最大分解应力分布改变造成的. 氦泡和孔洞被冲击波先后扫过部分塑性不对称是因为冲击波扫过时引起形状变化, 关键词: 分子动力学 冲击波 氦泡 孔洞  相似文献   

10.
Theoretical Hartree-Fock calculation are summarized for the [X=e+] systems with X = O, S, Se, and Te which establish the stability of bound states for the system. The two-photon annihilation lifetime, τ, and angular correlation, N(θ), are calculated and positron annihilation from alkaline earth oxides is discussed.  相似文献   