Comparison of media properties between hard/soft stacked composite and capping layer perpendicular recording media

The effect of soft layer thickness (t_Soft) of CoTaZr–SiO₂ and low Pt-containing CoCrPtO layers on media properties in hard/soft (H/S) stacked media is compared to media properties in conventional capping layer (CL) media. Coercivity and coercivity squareness in H/S stacked media continuously decrease with increasing t_Soft, while they increase in CL media. H/S stacked media with CoTaZr–SiO₂ layers having higher saturation magnetization and in-plane magnetic anisotropy constant exhibit stronger demagnetization effect. Compared to CL media, H/S stacked media with CoCrPtO soft layers improve signal-to-noise ratio and magnetic write width. However, the use of a relatively soft layer deteriorates adjacent track erasure and does not improve media writeability due to compensation effect between softer and harder layers to be used. These phenomena can be understood as undesirable side effects of a soft layer: higher demagnetization field and larger lattice mismatch.     

Anisotropy dispersion in (CoCrPt)1−x(SiO2)x perpendicular recording media

The distribution of easy axis orientation in perpendicular media is of technological importance because it affects the value of S^* (see Fig. 1), which quantifies the switching field distribution (SFD) and hence partially determines the data density achievable on a given medium. The distribution is controlled by the crystallographic orientation of grains and factors such as intergranular exchange and dipolar coupling. Due to strong demagnetising fields in the perpendicular orientation, traditional measurements of remanence as a function of angle are difficult to interpret and have required the use of large-scale computational models. In this work we have utilised the variation of coercivity H_C with angle, which has the advantage that at H_C the global demagnetising field is zero. Additionally, since such materials follow essentially the Stoner–Wohlfarth mode of reversal, the variation of H_C with angle, H_C(θ), is much greater than that for the remanence. We find that for (CoCrPt)_1−x(SiO₂)_x, where the level of exchange coupling is controlled, the distribution of magnetic easy axes is narrower when the exchange coupling is reduced, but dipolar coupling between the grains is strong and affects the magnetisation reversal significantly.     

Magnetic properties and microstructure study of high coercivity Au/FePt/Au trilayer thin films

High-coercivity Au(60 nm)/FePt(δ nm)/Au(60 nm) trilayer samples were prepared by sputtering at room temperature, followed by post annealing at different temperatures. For the sample with δ=60 nm, L1₀ ordering transformation occurs at 500 °C. Coercivity (H_c) is increased with the annealing temperature in the studied range 400–800 °C. The H_c value of the trilayer films is also varied with thickness of FePt intermediate layer (δ), from 27 kOe for δ=60 nm to a maximum value of 33.5 kOe for δ=20 nm. X-ray diffraction data indicate that the diffusion of Au atoms into the FePt L1₀ lattice is negligible even after a high-temperature (800 °C) annealing process. Furthermore, ordering parameter is almost unchanged as δ is reduced from 60 to 15 nm. Transmission electron microscope (TEM) photos indicate that small FePt Ll₀ particles are dispersed amid the large-grained Au. We believe that the high coercivity of the trilayer sample is attributed to the small and uniform grain sizes of the highly ordered FePt particles which have perfect phase separation with Au matrix.     

Preparation and recording characteristics of granular-type perpendicular magnetic recording media with thin intermediate layer

Granular-type media with thin Ru intermediate layer were prepared on a highly oriented high-B_s FeCo soft underlayer (SUL). A CoPt–TiO₂ recording layer on a Ru intermediate layer of only 2 nm had high-crystal orientation, high H_c of 6.5 kOe, and a high squareness ratio (SQ) of 0.99. The magnetic property of the SUL was also good. The recording performance was measured for the media with different Ru intermediate thicknesses by using a single-pole-type (SPT) head. The media had large reproduced output even for the Ru intermediate layer thickness of 2 nm.     

L12 phase formation and giant exchange anisotropy in Mn3Ir/Co–Fe bilayers

The degree of order S of Mn–Ir layers and the exchange anisotropy of Mn–Ir/Co–Fe bilayers were investigated for various chemical compositions of Mn–Ir layers, underlayer materials, and underlayer thicknesses. It was found that: (1) The compositional range over which L1₂-phase Mn₃Ir could be formed is 22–32 at% Ir and giant exchange anisotropy is obtained in this range. (2) Ru is favorable as an underlayer material for avoiding interdiffusion with the Mn–Ir layer during deposition on the temperature elevated substrate. (3) The underlayer thickness could be reduced to 5 nm while maintaining a giant exchange anisotropy in excess of 1 erg/cm².     

Magnetic properties of CoPt–SiNx/Ag nanocomposite films

When the thickness of Ag under layer is 25 nm, the CoPt/Ag film has maximum out-of-plane squareness (S_⊥), minimum in-plane squareness (S_∥), and the largest out-of-plane coercivity (H_c⊥), they are 0.95, 0.35, and 15 kOe, respectively. Different volume percent of SiN_x ceramic materials were co-sputtered with Co₅₀Pt₅₀ films on the Ag under layer to reduce the grain size of the CoPt film. Comparing the X-ray diffraction pattern of CoPt-SiN_x/Ag films without annealing with that of the films which annealed at 600 and 700 °C, it is found that the intensities of CoPt (0 0 1) and CoPt (0 0 2) superlattice lines were reduced after annealing. As the SiN_x content is raised to 50 vol%, the particle size of CoPt is reduced to be about 9 nm.     

Exchange coupling and remanence enhancement in nanocomposite Nd–Fe–B/FeCo multilayer films

Nd–Fe–B-type hard phase single layer films and nanocomposite Nd₂₈Fe₆₆B₆/Fe₅₀Co₅₀ multilayer films with Mo underlayers and overlayers have been fabricated on Si substrates by rf sputtering. The hysteresis loops of all films indicated simple single loops for fixed Nd–Fe–B layer thickness (10 nm) and different FeCo layer thickness (d_FeCo=1–50 nm). The remanence of these films is found to increase with increasing d_FeCo and the coercivity decrease with increasing d_FeCo. It is shown that high remanence is achieved in the nanocomposite multilayer films consisting of the hard magnetic Nd–Fe–B-type phase and soft magnetic phase FeCo with 20 nm?d_FeCo?3 nm. The sample of maximum energy product is 27 MG Oe for d_FeCo=5 nm at room temperature. The enhancement of the remanence and energy products in nanocomposite multilayer films is attributed to the exchange coupling between the magnetically soft and hard phases.     

Microstructure and switching mechanism of stacked CoCrPt–SiO2 perpendicular recording media

Perpendicular magnetic recording media consisting of two stacked CoCrPt–SiO₂ recording layers incorporating different O₂ content in each layer were studied. The samples used Ru intermediate layers. With increasing O₂ levels in the lower recording layer, the samples exhibited marginal change in the crystallographic texture, and superior overall magnetic properties such as higher coercivity and improved exchange decoupling. However, the media grain size remained unchanged. Investigations into the switching mechanism by means of virgin and isothermal remanence magnetization measurements showed the predominance of Stoner–Wohlfarth coherent reversal modes in all samples. The thermal stability dropped slightly. A model that describes the evolution of the microstructure in stacked perpendicular recording media is presented to understand these observations.     

Low-temperature ordering of L10 FePt phase in FePt thin film with AgCu underlayer

FePt (20 nm) films with AgCu (20 nm) underlayer were prepared on thermally oxidized Si (0 0 1) substrates at room temperature by using dc magnetron sputtering, and the films annealed at different temperature to examine the disorder–order transformation of the FePt films. It is found that the ordered L1₀ FePt phase can form at low annealing temperature. Even after annealing at 300 °C, the in-plane coercivity of 5.2 kOe can be obtained in the film. With increase in annealing temperature, both the ordering degree and coercivity of the films increase. The low-temperature ordering of the films may result from the dynamic stress produced by phase separation in AgCu underlayer and Cu diffusion into FePt phase during annealing.     

Magneto-transport properties of [Co/Bi]n wire structures

The present study examines the artificial control of grain-boundary resistance and its contribution to the magneto-transport properties of [Co(1 nm)/Bi(2.5 nm)]_n (n=10 or 20) line structures on the Si(0 0 1)/SiN_x substrate. Conventional patterning and deposition processes are applied for the fabrication of a device that consists of five-line structures with a line width of 2 μm. A ΔR/R=80% ratio was observed in the five-line structure of [Co(1 nm)/Bi(2.5 nm)]₁₀ multilayers at 10 K. Our measurements indicate that grain-boundary effects can be associated with the large ΔR/R ratio of transverse magnetoresistance.     

Microfabrication and magnetoelectric properties of amorphous magnetic-tunnel-junctions with Co–Fe–B/Al–O/Co–Fe–B hardcore structure

Both single-barrier magnetic tunnel junctions (SBMTJs) and double-barrier magnetic tunnel junctions (DBMTJs) with an amorphous hardcore structure of Co₆₀Fe₂₀B₂₀/Al–O/Co₆₀Fe₂₀B₂₀ were microfabricated. A high TMR ratio of 102.2% at 4.2 K was observed in the SBMTJs after annealing at 265 °C for 1 h. High TMR ratio of 56.2%, low junction resistance-area product RS of 4.6 kΩ μm², small coercivity H_C=25 Oe, and relatively large bias-voltage-at-half-maximum TMR with the value V_1/2 greater than 500 mV at room temperature (RT) had been achieved in such Co–Fe–B SBMTJs. Whereas, high TMR ratio of 60% at RT and 89% at 30 K, low junction resistance-area product RS of 7.8 kΩ μm² at RT and 8.3 kΩ μm² at 30 K, low coercivity H_C=8.5 Oe at RT and H_C=14 Oe at 30 K, and relatively large bias-voltage-at-half-maximum TMR with the value V_1/2 greater than 1150 mV at RT had been achieved in the Co–Fe–B DBMTJs. Temperature dependence of the TMR ratio, resistance, and coercivity from 4.2 K to RT, and applied voltage dependence of the TMR ratio and resistance at RT for such amorphous MTJs were also investigated.     

The microstructure and magnetic properties of electrodeposited Co–Pt thin films on Ru buffer layer

For high-density magnetic recording media, this study examined the crystal structure and the texture of electrodeposited cobalt–platinum (Co–Pt) films on Ru buffer layer. A 15-nm-thick Co–Pt film exhibited very high out-of-plane coercivity and squareness, which were 6248 Oe and 0.89, respectively. The coercivity, H_c, of Co–Pt films grown on Ru buffer layer decreased significantly with increasing thickness, possibly due to the lattice misfit of 5.4% between Co–Pt and Ru, leading to the decrease of perpendicular magnetic anisotropy (PMA) of Co–Pt films as indicated by the observed hexagonal-closed-packed (HCP) (1 1¯ 0 1) plane of Co–Pt films. According to nano beam diffraction pattern (NBDP), however, Co–Pt film grown on Ru layer of HCP exhibited mixed HCP and FCC phases. Also, cross-sectional TEM image suggests that the high PMA may result from the columnar structure of physically isolated Co–Pt grains with the c-axis perpendicular to the film plane.     

Evolution of phase,texture, microstructure and magnetic properties of Fe–Cr–Co–Mo–Ti permanent magnets

Magnetic phase evolution, crystallographic texture, microstructure and magnetic properties of Fe–28Cr–15Co–3.5Mo–1.8Ti alloy have been investigated by X-ray diffractometry, scanning transmission electron microscopy and magnetometry techniques as a function of processing conditions. Heat treatment conditions for obtaining optimum textural, microstructural and magnetic properties have been established by the experimentations. The Goss {110}〈001〉 and cube type {001}〈010〉 textures have been developed in an optimal treated Fe–28Cr–15Co–3.5Mo–1.8Ti magnets. The coercive force in Fe–28Cr–15Co–3.5Mo–1.8Ti magnets depends critically on the shape anisotropy of rod-like Fe Co Ti-rich α₁ particles and remanence on the alignment and elongation of α₁ particles parallel to applied magnetic field 〈100〉 directions. The optimum magnetic properties obtained in Fe–28Cr–15Co–3.5Mo–1.8Ti alloy are intrinsic coercive force, _iH_c, of 78.8 kA/m (990 Oe), remanence, B_r of 1.12 T (11.2 kG) and energy product, (BH)_max of 52.5 kJ/m³ (6.5 MGOe). The development of Fe–28Cr–15Co–3.5Mo–1.8Ti magnets as well as characterization of texture, microstructural and magnetic properties in the current study would be helpful in designing the new Fe–Cr–Co–Mo based magnets suitable for scientific and technological applications.     

Magnetic properties of anisotropic Sm–Fe–N bulk magnets produced by spark plasma sintering method

Sm–Fe–N powders were consolidated into bulk materials by the spark plasma sintering (SPS) method. Although partial decomposition of the Sm₂Fe₁₇N₃ phase was noted in the magnets, the decomposition was reduced by the addition of a small amount of Zn powder to the Sm–Fe–N powder. The anisotropic Sm–Fe–N magnet obtained from a mixture of Sm–Fe–N and Zn powders exhibited a high remanence of 0.90 T with a coercivity of 0.54 MA m⁻¹.     

Thickness measurement of a thin hetero-oxide film with an interfacial oxide layer by X-ray photoelectron spectroscopy

The general equation T_ove = L cos  θ ln(R_exp/R₀ + 1) for the thickness measurement of thin oxide films by X-ray photoelectron spectroscopy (XPS) was applied to a HfO₂/SiO₂/Si(1 0 0) as a thin hetero-oxide film system with an interfacial oxide layer. The contribution of the thick interfacial SiO₂ layer to the thickness of the HfO₂ overlayer was counterbalanced by multiplying the ratio between the intensity of Si⁴⁺ from a thick SiO₂ film and that of Si⁰ from a Si(1 0 0) substrate to the intensity of Si⁴⁺ from the HfO₂/SiO₂/Si(1 0 0) film. With this approximation, the thickness levels of the HfO₂ overlayers showed a small standard deviation of 0.03 nm in a series of HfO₂ (2 nm)/SiO₂ (2-6 nm)/Si(1 0 0) films. Mutual calibration with XPS and transmission electron microscopy (TEM) was used to verify the thickness of HfO₂ overlayers in a series of HfO₂ (1-4 nm)/SiO₂ (3 nm)/Si(1 0 0) films. From the linear relation between the thickness values derived from XPS and TEM, the effective attenuation length of the photoelectrons and the thickness of the HfO₂ overlayer could be determined.     

Exchange coupling in CoO–Co bilayer

In this work, exchange bias and coercivity enhancement in ferromagnet (FM)–antiferromagnet (AFM) bilayer have been investigated. CoO film (50 nm) was deposited by sputtering with a relatively high oxygen partial pressure. The deposited films were subsequently annealed at varied temperature up to 973 K in the air atmosphere. The CoO film shows a disordered structure in the as-deposited state and an increase of crystallinity after annealing characterized by XRD and Raman spectra. A 40-nm Co film was deposited on the as-deposited CoO and annealed films. The Co–CoO bilayer shows a large exchange bias up to 1600 Oe and relatively high coercivity up to 3200 Oe (H_C−) at 5 K, which is much larger than that of crystalline Co–CoO bilayer films without any treatment. The spin glass behavior combined with increasing crystallinity, surface roughness of CoO after annealing may be attributed to the large exchange bias and high coercivity.     

Effects of Nb substitution for Zr on the phases,microstructure and magnetic properties of Co80Zr18−xNbxB2 melt-spun ribbons

The phases, microstructure, and magnetic properties of Co₈₀Zr_18−xNb_xB₂ (x=1, 2, 3, and 4) melt-spun ribbons were investigated. The small substitution of Nb for Zr in the Co–Zr–B melt-spun ribbons resulted in the improvement of magnetic properties, especially the coercivity. The main effect of added Nb on the coercovity of Co–Zr–Nb–B melt-spun ribbons, originated from modification of the grain size of Co₁₁Zr₂ phase. The coercivity of the Co–Zr–Nb–B melt-spun ribbons depends on the annealing temperature. The optimal magnetic properties of H_c=5.1 kOe, and (BH)_max=3.4 MGOe were obtained in the Co₈₀Zr₁₅Nb₃B₂ melt-spun ribbons annealed at 600 °C for 3 min.     

Coercivity enhancement of anisotropic Dy-free Nd–Fe–B powders by conventional HDDR process

Coercivity enhancement of Dy-free Nd–Fe–Co–B–Ga–Zr powders was studied using the conventional hydrogenation–decomposition–desorption–recombination (HDDR) process. It was found that the addition of Al together with the proper Nd content and the slow hydrogen desorption of the HDDR treatment can induce high coercivity in the powder. For example, the 14.0 at% Nd–2.0 at% Al powder exhibits H_cJ of 1560 kA/m, B_r of 1.22 T, and (BH)_max of 257 kJ/m³. The high coercivity inducement of the powder is thought to be attributed to the formation of Nd-rich phase, which continuously surrounds fine Nd₂Fe₁₄B grains.     

Enhanced ferroelectric property of (Pb0.95Ca0.05)(Nb0.02Zr0.80Ti0.20)O3 thin films prepared by RF magnetron sputtering

(Pb_0.95Ca_0.05)(Nb_0.02Zr_0.80Ti_0.20)O₃ [PCNZT] thin films were deposited on the Pt(1 1 1)/Ti/SiO₂/Si(1 0 0) substrates by RF magnetron sputtering with and without a LaNiO₃ [LNO] buffer layer. Ca and Nb elements in PZT films enhance the ferroelectric property, LaNiO₃ buffer layer improves the crystal quality of the PCNZT thin films. PCNZT thin films possess better ferroelectric property than that of PZT films for Ca and Nb ion substitution, moreover, PCNZT thin films with a LNO buffer layer possess (1 0 0) orientation and good ferroelectric properties with high remnant polarization (P_r = 38.1 μC/cm²), and low coercive field (E_c = 65 kV/cm), which is also better than that of PCNZT thin films without a LNO buffer layer (P_r = 27.9 μC/cm², E_c = 74 kV/cm). The result shows that enhanced ferroelectric property of PZT films can be obtained by ion substitution and buffer layer.     

Resin-bonded permanent magnetic films with out-of-plane magnetization for MEMS applications

Resin-bonded permanent magnets with out-of-plain direction of magnetization and improved magnetic properties for magnetic MEMS actuator have been created. The material investigated consists of magnetically anisotropic strontium ferrite particles embedded into epoxy resin matrix upto a volume loading of 80%. Intrinsic coercivity H_ci of 6000 Oe (480 kA/m), residual magnetic flux density B_r up to 4000 G (0.4 T) and maximum energy product (BH)_max of 3.0 MG Oe (23.6 kJ/m³) have been attained due to magnetic-field-induced alignment of the ferrite particles during curing process.