Influence of substrate temperature on structures and dielectric properties of pyrochlore Bi1.5Zn1.0Nb1.5O7 thin films prepared by pulsed laser deposition

The influence of substrate temperature on structural and dielectric properties of cubic pyrochlore Bi_1.5Zn_1.0Nb_1.5O₇ (BZN) thin films prepared by pulsed laser deposition process has been investigated. BZN thin films were deposited on Pt/Ti/SiO₂/Si(1 0 0) substrate and in situ annealed at 700 °C. The results indicate that the substrate temperature has a significant effect on the structural and dielectric properties of BZN thin films. The films exhibit a cubic pyrochlore structure in the substrate temperature range from 550 °C to 700 °C and at the annealing temperature of 700 °C. With further increase of substrate temperature to 750 °C, the phases of Bi₂O₃, BiNbO₄ and Bi₅Nb₃O₁₅ can be detected in the XRD pattern due to the Zn loss. The dielectric constant and loss tangent of the films deposited at 650 °C are 192 and 6 × 10⁻⁴ at 10 kHz, respectively. The tunability is 10% at a dc bias field of 0.9 MV/cm.     

Structural and optical properties of Er, Yb co-doped Y2O3 thin films

Thin Er³⁺, Yb³⁺ co-doped Y₂O₃ films were grown on (1 0 0) YAG substrates by pulsed laser deposition. Ceramic targets having different active ion concentration were used for ablation. The influence of the rare-earth content and oxygen pressure applied during the deposition on the structural, morphological and optical properties of the films were investigated. The films deposited at the lower pressure, 1 Pa, and at 1/10 Er to Yb doping ratio are highly textured along the (1 1 1) direction of the Y₂O₃ cubic phase. In addition to the crystalline structure, these films possess smoother surface compared to those prepared at the higher pressure, 10 Pa. All other films are polycrystalline, consisting of cubic and monoclinic phases of Y₂O₃. The rougher surface of the films produced at the higher-pressure leads to higher scattering losses and different behavior of the reflectivity spectra. Optical anisotropy in the films of less than 0.004 was measured regardless of the monoclinic structure obtained. Waveguide losses of about 1 dB/cm at 633 nm were obtained for the films produced at the lower oxygen pressure.     

RHEED study of titanium dioxide with pulsed laser deposition

Reflection high-energy electron diffraction (RHEED) operated at high pressure has been used to monitor the growth of thin films of titanium dioxide (TiO₂) on (1 0 0) magnesium oxide (MgO) substrates by pulsed laser deposition (PLD). The deposition is performed with a synthetic rutile TiO₂ target at low fluence. The topography and structure of the deposited layers are characterized using in situ high pressure RHEED and atomic force microscope (AFM). Based on these observations the growth mode of the films is discussed. The results will be compared to earlier results obtained for the growth of TiN films on (1 0 0) MgO.     

Effects of depositing temperatures on structure and optical properties of TiO2 film deposited by ion beam assisted electron beam evaporation

TiO₂, which is high in refractive index and dielectric constant, plays an important role in the fields of optics and electronics. In this work, TiO₂ films were prepared on glass substrates by the technique of ion beam assisted electron beam evaporation. The films were deposited at 50, 150 and 300 °C, respectively. Then the as-deposited TiO₂ films were annealed at 450 °C for 1 h in vacuum atmosphere. Structures and optical properties of TiO₂ films were characterized by XRD, SEM, ellipsometry and spectrophotometer. As a result, the structure and the refractive index of films were improved by both the annealing and the increasing of the deposition temperature. The UV-vis transmittance spectra also confirmed that the deposition temperature has a significant effect on the transparency of the thin films. The highest transparency over the visible wavelength region of spectra was obtained at the deposition temperature of 300 °C. The allowed direct band gap at the deposition temperature ranging from 50 to 300 °C was estimated to be in the range from 3.81 to 3.92 eV.     

Chemical synthesis of spinel nickel ferrite (NiFe2O4) nano-sheets

The present investigation is related to the deposition of single-phase nano-sheets spinel nickel ferrite (NiFe₂O₄) thin films onto glass substrates using a chemical method. Nano-sheets nickel ferrite films were deposited from an alkaline bath containing Ni²⁺ and Fe²⁺ ions. The films were characterized for their structural, surface morphological and electrical properties by means of X-ray diffraction (XRD), transmission electron microscope (TEM), Fourier transform infrared spectroscopy (FT-IR), scanning electron microscopy (SEM), and two-point probe electrical resistivity techniques. The X-ray diffraction pattern showed that NiFe₂O₄ nano-sheets are oriented along (3 1 1) plane. The FT-IR spectra of NiFe₂O₄ films showed strong absorption peaks around 600 and 400 cm⁻¹ which are typical for cubic spinel crystal structure. Microstructural study of NiFe₂O₄ film revealed nano-sheet like morphology with average sheet thickness of 30 nm. The room temperature electrical resistivity of the NiFe₂O₄ nano-sheets was 10⁷ Ω cm.     

Electrochemical behaviour of sputtered c-V2O5 and LiCoO2 thin films for solid state lithium microbatteries

Here are reported for the first time electrochemical data on all-solid-state lithium microbatteries using crystalline sputtered V₂O₅ thin films as cathode materials and LiPON as solid electrolyte. The stable specific capacity of 30 µAh/cm² found with a 2.4 µm thick film competes very well with the best values obtained for solid state microbatteries using amorphous films. With the challenge of decreasing the temperature of heat treatment for sputtered LiCoO₂ thin films, we show that a temperature of 500 °C combined with an optimized bias sputtering (-50 V) allows to get highly crystalline deposits, to minimize the presence of Co₃O₄ and to suppress any trace of the cubic phase. At the same time the theoretical specific capacity is reached in the 4.2 V-3 V range and a good cycling behaviour is achieved with a high capacity of 50 µAh/cm²/µm after 140 cycles at 10 µA.cm².     

Investigation of thermal annealing effects on microstructural and optical properties of HfO2 thin films

In the present paper, we investigate the effect of thermal annealing on optical and microstructural properties of HfO₂ thin films (from 20 to 190 nm) obtained by plasma ion assisted deposition (PIAD). After deposition, the HfO₂ films were annealed in N₂ ambient for 3 h at 300, 350, 450, 500 and 750 °C. Several characterisation techniques including X-ray reflectometry (XRR), X-ray diffraction (XRD), spectroscopic ellipsometry (SE), UV Raman and FTIR were used for the physical characterisation of the as-deposited and annealed HfO₂ thin films. The results indicate that as-deposited PIAD HfO₂ films are mainly amorphous and a transition to a crystalline phase occurs at a temperature higher than 450 °C depending on the layer thickness. The crystalline grains consist of cubic and monoclinic phases already classified in literature but this work provides the first evidence of amorphous-cubic phase transition at a temperature as low as 500 °C. According to SE, XRR and FTIR results, an increase in the interfacial layer thickness can be observed only for high temperature annealing. The SE results show that the amorphous phase of HfO₂ (in 20 nm thick samples) has an optical bandgap of 5.51 eV. Following its transition to a crystalline phase upon annealing at 750 °C, the optical bandgap increases to 5.85 eV.     

Effects of co-substitution on the electrical properties of BiFeO3 thin films prepared by chemical solution deposition

Ferroelectric BiFeO₃ thin films with Nd-Cr (or Sm-Cr) co-substitution (denoted by BNdFCr and BSmFCr, respectively) were deposited on the Pt(2 0 0)/TiO₂/SiO₂/Si(1 0 0) substrates by a chemical solution deposition method. X-ray diffraction patterns revealed the formation of BNdFCr and BSmFCr thin films without any secondary phases. The co-substituted BNdFCr (or BSmFCr) thin films, which were annealed at 550 °C for 30 min in N₂ atmosphere, exhibited enhanced electrical properties compared to BFO thin films with the remanent polarization (2P_r) and coercive electric field (2E_c) of 196, 188 μC/cm² and 600, 570 kV/cm with the electric field of 800 kV/cm, respectively. The leakage current densities of BNdFCr and BSmFCr thin films measured at room temperature were approximately three orders of magnitude lower than that of BFO thin film, and the leakage current at room temperature of the thin films exhibited three distinctive conduction behaviors. Furthermore, the values of pulse polarizations [i.e., +(P*-P^{^}) or −(P*-P^{^})] of BNdFCr and BSmFCr thin films were reasonably unchanged up to 1.4 × 10¹⁰ switching cycles.     

Ternary semiconductor compounds CuInS2 (CIS) thin films synthesized by electrochemical atomic layer deposition (EC-ALD)

In this paper the formation and characterization of the I-III-VI₂ semiconductor compound CuInS₂ (CIS) on gold substrate at room temperature by electrochemical atomic layer deposition (EC-ALD) method are reported. Optimum deposition potentials for each element are determined using cyclic voltammetry (CV) technique and Amperometric I-t method is used to prepare the semiconductor compound. These thin films were characterized by X-ray diffraction (XRD), X-ray photoelectron spectroscopy (XPS), field emission scanning electron microscopy (FE-SEM) and Fourier transform infrared spectroscopy (FT-IR). XRD results indicate that the CIS thin films have a (1 1 2) preferred orientation. The XPS analyses of the films reveal that Cu, In and S are present in an atomic ratio of approximately 1:1:2. And their semiconductor band gaps are found to be 1.50 eV by FT-IR.     

Growth and characterization of Y2O3 thin films

Y₂O₃ thin films were grown on silicon (1 0 0) substrates by pulsed-laser deposition at different substrate temperatures and O₂ pressures. The structure and composition of films are studied by using X-ray diffraction (XRD) and X-ray photoelectron spectroscopy (XPS). The Y₂O₃ thin films deposited in vacuum strongly oriented their [1 1 1] axis of the cubic structure and the film quality depended on the substrate temperature. The magnitude of O₂ pressure obviously influences the film structure and quality. Due to the silicon diffusion and interface reaction during the deposition, yttrium silicate and SiO₂ were formed. The strong relationship between composition and growth condition was discussed.     

Effect of oxygen pressure on structure and properties of Bi1.5Zn1.0Nb1.5O7 pyrochlore thin films prepared by pulsed laser deposition

The Bi₂O₃-ZnO-Nb₂O₅ (BZN) cubic pyrochlore thin films were prepared on Pt/TiO₂/SiO₂/Si(1 0 0) substrates by using pulsed laser deposition process. The oxygen pressure was varied in the range of 5-50 Pa to investigate its effect on the structure and dielectric properties of BZN thin films. It is found that oxygen pressure during deposition plays an important role on structure and other properties of BZN films. The BZN films deposited at temperature of 650 °C and at O₂ pressure of 5 Pa have an amorphous BZN and Nb₂O₅ phases but exhibits a cubic pyrochlore structure with a preferential (2 2 2) orientation when the oxygen pressure increases to 10 Pa. Dielectric constant and loss tangent of the films deposited at 10 Pa are 185 and 0.0008 at 10 kHz, respectively. The dielectric tunability is about 10% at a dc bias field of 0.9 MV/cm.     

Deposition and characterization of layer-by-layer sputtered AgGaSe2 thin films

Sputtering technique has been used for the deposition of AgGaSe₂ thin films onto soda-lime glass substrates using sequential layer-by-layer deposition of GaSe and Ag thin films. The analysis of energy dispersive analysis of X-ray (EDXA) indicated a Ga-rich composition for as-grown samples and there was a pronounce effect of post-annealing on chemical composition of AgGaSe₂ thin film. X-ray diffraction (XRD) measurements revealed that Ag metallic phase exists in the amorphous AgGaSe₂ structure up to annealing temperature 450 °C and then the structure turned to the single phase AgGaSe₂ with the preferred orientation along (1 1 2) direction with the annealing temperature at 600 °C. The surface morphology of the samples was analyzed by scanning electron microscopy (SEM) measurements. The structural parameters related to chalcopyrite compounds have been calculated. Optical properties of AgGaSe₂ thin films were studied by carrying out transmittance and reflectance measurements in the wavelength range of 325-1100 nm at room temperature. The absorption coefficient and the band gap values for as-grown and annealed samples were evaluated as 1.55 and 1.77 eV, respectively. The crystal-field and spin-orbit splitting levels were resolved. These levels (2.03 and 2.30 eV) were also detected from the photoresponse measurements almost at the same energy values. As a result of the temperature dependent resistivity and mobility measurements in the temperature range of 100-430 K, it was found that the decrease in mobility and the increase in carrier concentration following to the increasing annealing temperature attributed to the structural defects (tetragonal distortion, vacancies and interstitials).     

Conversion of p-type to n-type conductivity in undoped ZnO films by increasing operating temperature

ZnO thin films with the thickness of about 15 nm on (0 0 0 1) sapphire substrates were prepared by pulsed laser deposition. X-ray photoelectron spectroscopy indicated that both as-grown and post-annealed ZnO thin films were oxygen-rich. H₂ sensing measurements of the films indicated that the conductivity type of both the unannealed and annealed ZnO films converted from p-type to n-type in process of increasing the operating temperature. However, the two films showed different conversion temperatures. The origin of the p-type conductivity in the unannealed and annealed ZnO films should be attributed to oxygen related defects and zinc vacancies related defects, respectively. The conversion of the conductivity type was due to the annealing out of the correlated defects. Moreover, p-type ZnO films can work at lower temperature than n-type ZnO films without obvious sensitivity loss.     

Influence of deposition conditions on the optical properties of erbium-doped yttrium oxide films grown by aerosol-UV assisted MOCVD

Erbium-doped Y₂O₃ films were prepared by aerosol-UV assisted metal-organic chemical vapour deposition (MOCVD) at 410 °C. The effects of humidity of carrier gas and UV-assistance on their structure and optical properties were investigated on the as-deposited and thermal annealed films using infrared spectroscopy, X-ray diffraction and transmission electron microscopy. It was found that the as-deposited Er:Y₂O₃ films crystallise in the Y₂O₃ cubic structure and present a very low organic contamination when the deposition takes place under high air humidity and, even better, with UV-assistance. After annealing, two different structural phases are observed corresponding to the cubic and the monoclinic structures of Y₂O₃. The Er³⁺ luminescence analysed in the visible and IR regions, shows the classical green transitions. The best optical properties were obtained with as-deposited and annealed Er:Y₂O₃ films grown under high air humidity with UV-assistance. Under such deposition conditions, ⁴I_13/2 lifetimes was found to be 3.07 and 6.1 ms for films annealed at 800 and 1000 °C, respectively, and up-conversion phenomena were underlined. This indicates that the deposition conditions, in particular air humidity, play an important role in the luminescent properties even after annealing.     

Deposition and growth kinetics studies of thin zirconium dioxide films by UVILS-CVD

We report the deposition of thin zirconium dioxide films on Si(1 0 0) by a technique of ultraviolet-assisted injection liquid source chemical vapor deposition (UVILS-CVD) by using ultraviolet with 222 nm radiation. The alkoxide zirconium(IV) tert-butoxide (Zr[OC(CH₃)₃]₄) was used as precursor while nitrous oxide was driven into the reaction chamber as an oxidizing agent. The ZrO₂ films were deposited under various conditions and characterized by ellipsometry, Fourier transform infrared spectroscopy, X-ray photoelectron spectroscopy, X-ray diffraction and scanning electron microscopy. The growth rate decreased with the increasing of substrate temperatures from 200 to 400 °C. Deposition rate of 20 nm/min was observed at a substrate temperature of 350 °C. There was a liner relation between the thicknesses of the films and deposition times. As a result the thicknesses can be accurately controlled by changing the number of drops of precursor introduced by the injection liquid source. The growth rate increased with the increasing concentrations of the precursor, nevertheless the trend stopped when the concentration exceeded 8.5%. The growth kinetics were also studied and the results were fit to a three-step kinetic model involving a photo chemical reaction, a reversible precursor absorption process and a following irreversible deposition reaction.     

Structure and photoluminescence properties of epitaxial SnO2 films grown on α-Al2O3 (0 1 2) by MOCVD

SnO₂ thin films have been successfully deposited on α-Al₂O₃ (0 1 2) substrates by metalorganic chemical vapor deposition (MOCVD) in the temperature range 500-700 °C. The films were epitaxially grown in the tetragonal SnO₂ phase and were (1 0 1) oriented. In-plane orientation relationship [0 1 0]SnO₂||[1 0 0]Al₂O₃ and [1 0 1?]SnO₂||[1? 2? 1]Al₂O₃ was determined between the film and substrate. Photoluminescence (PL) spectra measured at room temperature revealed that the film grown at 700 °C showed an intense ultra-violet (UV) PL peak at 333 nm, which was a band-edge emission peak in SnO₂ films. At a temperature of 13 K, a new broad PL band centered at about 480 nm was observed. The corresponding PL mechanisms are discussed in detail.     

The electrical and magnetic properties of epitaxial orthorhombic YMnO3 thin films grown under various oxygen pressures

Orthorhombic YMnO₃ thin films were epitaxially grown on bare and LaNiO₃ buffered (0 0 1)-SrTiO₃ substrates by pulsed laser deposition under various oxygen pressures from 5 to 30 Pa. The crystal structure and microstructure of these films have been characterized by both X-ray diffractions and transmission electron microscopy. The leakage current, modeled as the space charge limited current (SCLC) mechanism, decreased significantly with the increase of oxygen content. It is further found that the magnetic property of films is greatly enhanced in YMnO₃ films grown under high oxygen pressure, which can be explained decreased oxygen vacancies. In addition, bipolar switching behavior was obtained only in the films grown under 30 Pa oxygen pressure, which is attributed to the decrease of voltage-driven oxygen vacancy migration.     

Surface characterization and luminescent properties of SrAl2O4:Eu,Dy nano thin films

SrAl₂O₄:Eu²⁺, Dy³⁺ thin films were grown on Si (1 0 0) substrates in different atmospheres using the pulsed laser deposition (PLD) technique. The effects of vacuum, oxygen (O₂) and argon (Ar) deposition atmospheres on the structural, morphological and photoluminescence (PL) properties of the films were investigated. The films were ablated using a 248 nm KrF excimer laser. Improved PL intensities were obtained from the unannealed films prepared in Ar and O₂ atmospheres compared to those prepared in vacuum. A stable green emission peak at 520 nm, attributed to 4f⁶5d¹→4f⁷ Eu²⁺ transitions was obtained. After annealing the films prepared in vacuum at 800 °C for 2 h, the intensity of the green emission (520 nm) of the thin film increased considerably. The amorphous thin film was crystalline after the annealing process. The diffusion of adventitious C into the nanostructured layers deposited in the Ar and O₂ atmospheres was most probably responsible for the quenching of the PL intensity after annealing.     

Effect of deposition temperature on orientation and electrical properties of (K0.5Na0.5)NbO3 thin films by pulsed laser deposition

Lead-free ferroelectric K_0.5Na_0.5NbO₃ (KNN) thin films have been prepared on Pt/TiO₂/SiO₂/Si substrates by pulsed laser deposition process. The structures, crystal orientations and electrical properties of thin films have been investigated as a function of deposition temperature from 680 °C to 760 °C. It is found that the deposition temperature plays an important role in the structures, crystal orientations and electrical properties of thin films. The crystallization of thin films improves with increasing deposition temperature. The thin film deposited at 760 °C exhibits strong (0 0 1) preferential orientation, large dielectric constant of 930 and the remnant polarization of 8.54 μC/cm².     

Two routes to polycrystalline CoSi2 thin films by co-sputtering Co and Si

Two processes for the fabrication of polycrystalline CoSi₂ thin films based on the codeposition of Co and Si by sputtering were studied and compared. The first process involved “annealing after deposition”, where Co and Si are codeposited at ambient temperature and then crystallized by annealing. This process yielded randomly oriented plate-like CoSi₂ grains with a grain size that is governed by the nanostructure of the as-deposited film. Polycrystalline CoSi₂ thin films were obtained at a process temperature of 170 °C, which was much lower than the annealing temperature of 500 °C needed for Co/Si bilayers. The second process involved “heating during deposition”, where Co and Si are codeposited on heated substrates. This process yielded CoSi₂ grains with a columnar structure, and the grain size and degree of (1 1 1) orientation are temperature dependent. The sheet resistance of the resulting films was determined by the preparation temperature regardless of the deposition process used, i.e. “annealing after deposition” or “heating during deposition”. Temperatures of 500 °C and higher were needed to achieve CoSi₂ resistivity of 40 μΩ cm or lower for both processes.