 共查询到10条相似文献,搜索用时 15 毫秒
1.
Europium-doped yttrium-silicon-oxide-nitride phosphors are synthesized by carbothermal reduction and nitridation method. The crystal structure of the phosphors changed gradually from oxide Y2Si2O7 to nitride YSi3N5 state with increasing dosage of Si3N4 and carbon powder. The Y2Si2O7:Eu phosphor shows a blue emission at 465 nm with 300 nm excitation and a characteristic red emission of Eu^3+ at 612 nm with 230 nm excitation. The YSi3N5:EU phosphor shows a broad emission band centred at 595nm with some sharp peaks of Eu^3+ with 325nm excitation. The absorption of the studied phosphors increases from 450 to 700hm with an increment in nitrogen content. Blue-to-orange tunable luminescence is observed with 390 nm excitation.  相似文献   

2.
A 0.1 mol.% CoF_2-doped Na_5Lu_9F_(32)single crystal with high quality in the size of ~φ10 mm×100 mm was grown by the Bridgman method. Three peaks located at 504, 544, and 688 nm and a broad band in the range of 1200–1600 nm centered at 1472 nm were observed in the absorption spectra. The absorption peak position suggests cobalt ions in the divalent state in the grown crystal. Moreover, the cobalt ions are confirmed to locate in the distorted cubic crystal structure. Upon excitation of 500 nm light, a sharp emission peak at 747 nm ascribed to the ~2T_2(H_1) →~4A_2(F) transition was observed for the crystal. The Co~(2+)-doped Na_5Lu_9F_(32)crystal shows a potentially promising material for the application of a passively Q-switched laser operating in the near-infrared range.  相似文献   

3.
The absorption and emission spectra of the YVO4 single crystal co-doped with 1 at.% Nd^3+ and 1 at.% Yb^3+ are investigated. The efficient Nd^3+ → Yb^3+ energy transfer and the back transfer (Yb^3+ → Nd^3+) are observed at room temperature. The fluorescence lifetime of the 4F3/2 level of Nd^3+ in Nd,Yb:YVO4 is measured under 808 nm laser light excitation. The efficiency of Nd^3+ → Yb^3+ energy transfer in YVO4 is determined to be about 34%.  相似文献   

4.
The optical reflectance by a metallic plate arranged with array consisting of subwavelength periodic square hole is investigated by using the three-dimensional finite-difference time-domain method (3D-FDTD). There are dips in the reflectivity spectra, which indicate the absorption peaks. The absorption peaks behave differently according to the ratio of hole width and the period of the hole array. Combined with the near fields of the absorption peaks, it is found that the surface plasmon (SP) resonance on the surface of plate and localized SP in the hole play a major role for the two absorptions.  相似文献   

5.
The possible defect models of Y^3+:PbWO4 crystals are discussed by defect chemistry and the most possible substituting positions of the impurity Y^3+ ions are studied by using the general utility lattice program (GULP). The calculated results indicate that in the lightly doped Y^3+ :PWO crystal, the main compensating mechanism is [2Ypb^+ + VPb^2-], and in the heavily doped Y^3+ :PWO crystal, it will bring interstitial oxygen ions to compensate the positive electricity caused by YPb^+, forming defect clusters of [2Ypb^+ +Oi^2-] in the crystal. The electronic structures of Y3+ :PWO with different defect models are calculated using the DV-Xα method. It can be concluded from the electronic structures that, for lightly doped cases, the energy gap of the crystal would be broadened and the 420nm absorption band will be restricted; for heavily doped cases, because of the existence of interstitial oxygen ions, it can bring a new absorption band and reduce the radiation hardness of the crystal.  相似文献   

6.
A theoretical model to simulate an end-pumped CW Nd^3+:GdVO4 laser at 1063 nm is presented. Its essence is to use the propagation equations to demonstrate the spatial evolutions of the pump and the laser powers in the cavity, hence it is applicable to both low and high gain lasers. The simulation results obtained by this model are in good agreement with the experimental observations reported in the literature for a Ti:sapphlre-pumped Nd^3+:GdVO4 laser. Moreover, some parameters, such as the reflectivity of output coupler, the spot size of laser beam and the crystal length, are discussed with a view to optimizing the laser performance.  相似文献   

7.
A high-quality Cr 3+:CdWO4 single crystal at a size of approximatelyΦ25×80 mm is grown using the Bridgman method with CdO,WO3,and Cr2O3 as raw materials and their molar ratio of 100:100:0.5.The temperature gradient of solid-liquid interface at growth is approximately 50?C/cm and the growth rate is 0.05 mm/h.The X-ray diffraction(XRD),absorption,excitation,and emission spectra of different parts of the as-grown and O2-annealed crystals are investigated.Two strong broad optical absorption bands of about 472 and 708 nm are observed,and they are associated with the transitions 4 A2→ 4 T1 and 4 A2→ 4 T2.The weak 4 T2→ 2 E transition(the R-line)at 632 nm is also observed.The crystal-field parameter Dq and the Racah parameters B and C are estimated to be 1 412.4,776.8,and 3 427.6 cm? 1,respectively,according to the absorption spectra and crystal-splitting theory.A broadband fluorescence at about 1 000 nm due to 4 T2→ 4 A2 transition is produced by exciting the samples at 675 nm.After being annealed in an O2 atmosphere,the crystals become more transparent,while the effective light absorption of Cr 3+ ions is evidently enhanced and the emission intensity is also strengthened due to the reduction of oxygen vacancies in the CdWO4 crystal after annealing.  相似文献   

8.
Rare earth europium(Eu(3+))-doped lithium tetraborate(Eu:Li_2B_4O_7) crystal is grown from its stoichiometric melt by microtube Czochralski pulling technique(μT-Cz) for the first time. The grown crystals are subjected to powder x-ray diffraction(PXRD) analysis which reveals the tetragonal crystal structure of the crystals. UV–vis–NIR spectral analysis is carried out to study the optical characteristics of the grown crystals. The crystal is transparent in the entire visible region, and the lower cutoff is observed to be at 304 nm. The existence of BO_3 and BO_4 bonding structure and the molecular associations are analyzed by Fourier transform infrared(FTIR) spectroscopy. The results of excitation and emission-photoluminescence spectra of europium ion incorporated in lithium tetraborate(LTB) single crystal reveal that the observations of peaks at 258,297, and 318 nm in the excitation spectra and peaks at 579, 591, 597, 613, and 651 nm are observed in the emission spectra.The chromaticity coordinates are calculated from the emission spectra, and the emission intensity of the grown crystal is characterized through a CIE 1931(Commission International d'Eclairage) color chromaticity diagram.  相似文献   

9.
Novel Dy^3+-doped GdPO4 white light phosphors with a monoclinic system are successfully synthesized by the hydrothermal method at 240℃. The strong absorption at around 147nm in the excitation spectrum is assigned to the host absorption. It is suggested that the vacuum ultraviolet excited energy is transferred from the host to the Dy^3+ ions. The f - d transition of the Dy^3+ ion is observed to be located at 182nm, which is consistent with the calculated value using Dorenbos's expression. Under 147nm excitation, Gd0.92PO4:0.08Dy^3+ phosphor exhibits two emission bands located at 572 nm (yellow) and 478 nm (blue), which correspond to the hypersensitive transitions ^4 F9/2-^6 H13/2 and ^4 F9/2-^6 H15/2. The two emission bands lead to the white light. Because of the strong absorption at about 147nm, Gd0.92PO4:0.08Dy^3+ under vacuum ultraviolet excitation is an effective white light phosphor, and has promising applications to mercury-free lamps.  相似文献   

10.
LiLuF4 single crystals co-doped with thulium (5%) and holmium (0.5%), having large size, intact shape, and high optical quality, are successfully grown by the Czochralski technique. Absorption and fluorescence spectra of the crystal are measured. The absorption spectrum shows that the main absorption band locates at near 686 and 792 nm and the fluorescence spectrum peaks at 2.05 um. At room temperature, the as-grown Tin, Ho: LiLuF4 single crystals are end-pumped by a fiber-coupled laser diode system with pumping wavelength of 795 nm under CW operations. A power of 50 mw contin- uous laser outout at 2.05-um wavelength is achieved. Meanwhile an obvious green light is detected.  相似文献   