ZnS:Ag的ESR及结构相变研究

ESR实验表明Ag在ZnS微晶中是以Ag⁺离子的形式存在,没有测到Ag²⁺离子的信号.以Mn²⁺为探针的ESR和X射线衍射分析研究发现,在ZnS微晶由立方点阵(β相)变为六角点阵(α相)的结构相变中,Ag⁺离子对相变的影响与掺杂浓度和煅烧温度有关,当掺Ag量为5×10^-4g/g时相变在1100~1200℃出现逆转现象.由Mn²⁺的ESR谱得出α相的朗德因子g为2.006,越精细常数a为6.76mT,β相的g为2.002,a为6.81mT.     

SrB4O7：Pr3+,Mn2+中的Pr→Mn能量传递

从能量传递的角度出发,利用同步辐射光源(德国HASYLAB实验室的SUPERLUMI实验站)对Pr³⁺和Mn²⁺掺杂的SrB₄O₇粉末样品进行了光谱研究.206nm激发下,在SrB₄O₇:Pr³⁺(0.1%,摩尔分数)样品中观察到了来自Pr³⁺离子1S0能级的光子级联发射.SrB₄O₇:Pr³⁺样品的发射谱与SrB₄O₇:Mn²⁺样品监测Mn²⁺离子640nm发射的激发谱在330~430nm的波长范围里存在显著的光谱重叠.这个光谱重叠有利于Pr³⁺→Mn²⁺的能量传递发生,从而将Pr³⁺离子级联发射中第一步不实用的紫外或近紫外光子转换为Mn²⁺的红光发射.双掺杂样品SrB₄O₇:Pr³⁺,Mn²⁺与单掺杂样品SrB₄O₇:Pr³⁺的发射谱比较揭示出Pr³⁺→Mn²⁺的能量传递的确存在,并且提供了一种传递效率的估算方法,表明通过“Pr³⁺-Mn²⁺”组合有可能获得量子效率大于1的高效真空紫外激发发光材料.     

Ba2SiO4:Ce3+,Mn2+荧光粉的制备与光谱性质

用高温固相反应法合成了Ba₂SiO₄:xCe³⁺,yMn²⁺(x=0~0.2, y=0~0.15)荧光粉,研究了荧光粉的晶体结构和发光性质。在紫外光激发下,Ba₂SiO₄:xCe³⁺的发射光谱为位于384 nm附近的宽带。Ba₂SiO₄:Mn²⁺样品的发射光谱位于376 nm的宽带较强,红光发射极弱。在Ce³⁺和Mn²⁺共掺的Ba₂SiO₄:xCe³⁺,yMn²⁺样品中,位于606 nm附近的红光发射较强,来源于Mn²⁺的⁴T₁(⁴G)-⁶A₁(⁶S)跃迁。这说明Ce³⁺离子将部分能量传递给了Mn²⁺离子,有效地敏化了Mn²⁺离子的发光。当Ce³⁺的摩尔分数为0.2、Mn²⁺的摩尔分数为0.075时,Ba₂SiO₄:xCe³⁺,yMn²⁺荧光粉位于606 nm的Mn²⁺的发射峰最强。     

玻璃基质中ZnS纳米晶Mn2+的EPR谱

用融熔法制备分散有ZnS:Mn²⁺纳米晶的纳硼硅(Na₂O-B₂O₃-SiO₂)玻璃在不同温度、时间对样品进行退火处理,得到不同尺寸的纳米晶.研究了玻璃基质中ZnS:Mn²⁺纳米晶的EPR谱、微波功率饱和EPR谱及发射光谱,发现Mn²⁺有二种组态,即替位组态和间隙位组态.分析结果表明替位组态Mn²⁺及周围立方晶场的畸变程度直接影响光学发光特性.     

Li2O-P205O-V2O5系统非晶材料电学性质与磁共振研究

本文对Li₂O-P₂O₅-V₂O₅系统非晶态中的几组试样进行了电导率、核磁共振及顺磁共振测试。实验分析表明非晶态的log(σΤ)-1/Τ曲线都是由两个直线段构成。电导率在转变温度以后的“晶化前期”异常增大,这归因于该阶段非晶态结构有序化程度增加所致,利用ESR实验结果对非晶态进行钒离子价态分析表明,该系统非晶态中钒离子仅以V⁴⁺和V⁵⁺状态存在。固定P< 关键词：     

天然方解石的定代和顺磁共振研究

用ESR分析了天然方解石(CaCO₃)中的杂质Mn²⁺离子和天然顺磁缺陷的性质。有关谱的理论计算基本和实验结果一致.解释了热处理和辐照样品出现的一些实验现象,最后提出了如何克服干扰解决含有一些杂质Mn²⁺离子样品的定代问题。     

Y-型沸石上VO(H2O)42+的ESR波谱研究

本文报道了VO²⁺在Y型沸石上用不同温度灼烧处理之后测得的两种不同的ESR波谱。提出了VO(H₂O)₄²⁺离子在沸石笼中的两种可能结构,随着灼烧温度的升高,结构(Ⅰ)减少。到灼烧温度高于600。C时则结构(Ⅰ)完全消失,而对应于结构(Ⅱ)的A_⊥也渐渐变小,说明未偶电子离域性增大以致失去电子,V⁴⁺则被氧化成V⁵⁺。本文利用波谱参数计算了键参数和约化能级。     

Na4Ca3(AlO2)10∶Eu2+,Mn2+荧光粉的发光特性

采用高温固相法,制得一种新型荧光粉Na₄Ca₃(AlO₂)₁₀∶Eu²⁺,Mn²⁺。样品的结构和发光性质分别由X射线衍射谱和荧光光谱来表征。在Na₄Ca₃(AlO₂)₁₀∶Eu²⁺的激发光谱中出现了Eu²⁺的f-d跃迁吸收带;在发射光谱中,出现蓝光发射,峰值位于441 nm。当在Na₄Ca₃(AlO₂)₁₀∶Eu²⁺中掺杂Mn²⁺时,发生了Eu²⁺→Mn²⁺的能量传递,在542 nm处出现了Mn²⁺的发射峰。在Na₄Ca₃(AlO₂)₁₀∶Eu²⁺,Mn²⁺中,随着Mn²⁺浓度的增加,Eu²⁺粒子的发射强度减弱,而Mn²⁺粒子的发射强度增强,且Eu²⁺离子发射的衰减时间缩短,同时色度由蓝光移向白光。     

绿色K2-xNaxZn0.94SiO4∶0.06Mn2+荧光粉晶体相变对光致发光性能的影响

采用高温固相法,通过阳离子替代的实验策略,制备出系列窄带发射且颜色可由深黄色调至绿色的K_2-xNa_xZn_0.94SiO₄∶0.06Mn²⁺(0≤x≤2)荧光粉。用X射线粉末衍射仪对样品的物相进行表征,通过扫描电子显微镜和能量色散谱测试对样品的形貌和元素分布进行分析。结果表明,成功地合成了纯相且元素分布均匀的K_2-xNa_xZn_0.94SiO₄∶0.06Mn²⁺(0≤x≤2)荧光粉。在蓝光激发下,随着Na⁺离子逐渐代替K⁺离子,K_2-xNa_xZn_0.94SiO₄∶0.06Mn²⁺(0≤x≤2)荧光粉的发光强度逐渐增强,原荧光粉的发光强度得到有效提高的同时发光颜色由深黄色调至绿色。在427 nm激光的激发下：当x=0.8时,...     

BaCl2中Eu2+的电子自旋共振研究

制备和用X射线分析BaCl₂:Eu微晶的结构,并测量它的电子自旋共振(ESR)谱,结构分析和ESR谱都表明,替代Ba²⁺的Eu²⁺离子是处在轴对称的正交晶场中;并用抽对称的自旋哈密顿量和晶场哈密顿量对ESR实验数据进行拟合,求得在正交对称的BaCl₂中的Eu²⁺的自旋哈密顿参数;还发现Eu替代Ba²⁺的掺杂浓度的饱和值为0.34mol％。 关键词：     

Impurity levels of iron-group ions in TiO2(II)

Photocurrent measurements on oxidized, single-crystal TiO₂ undoped and doped with V, Cr, Mn or Fe were made both before and after exposure to white light from a tungsten lamp; they revealed a band of states centered at 2.0 eV below the conduction-band edge E_c that appears to be the band of surface states active in the photoelectrolysis of water. They also revealed a band of bulk states extending from near the valence-band edge E_v to about 1.9 eV below E_c. The ESR signals from V⁴⁺, Cr³⁺ and Fe³⁺ ions in oxidized samples and from Mn³⁺ ions in reduced samples were measured before and after exposure to white and monochromatic light; changes in the ESR signal intensities allow placement of the V⁴⁺: d¹ level about 2.1 eV below E_c, the Cr³⁺: d³ level about 2.7 eV belo E_c, the Fe³⁺ level at or just below the valence band edge E_v which is 3.0 eV below E_c, the Fe²⁺ level approximately at E_c, the Mn³⁺ level about 1.9 eV below E_c. Comparison of experiments on oxidized and reduced samples suggests that the bulk states are associated with cation vacancies, and measurements with polarized light gave anisotropies that are qualitatively interpretable with a cation-vacancy model for the oxidized samples.     

磺化乙丙三元胶离聚体溶液的ESR波谱研究

考察了磺化乙丙三元胶锰盐离聚体在二甲苯/正己醇混合溶剂中的ESR谱,结果表明醇对金属离子的溶剂化作用破坏了溶液中Mn²⁺的聚集,出现超精细分裂的ESR谱线,溶剂化程度与醇含量、醇分子体积、温度和Mn²⁺浓度有关,这些结果与离聚体溶液粘性行为得到的结论相一致。     

Ce3+和Mn2+掺杂的Ba9(Y2-xScx)(SiO4)6光谱特性和温度特性研究

采用高温固相法制备了Ba₉(Y_2-xSc_x)(SiO₄)₆:Ce³⁺,Mn²⁺(x=0,0.5,1.0,1.5,2.0)样品。在该体系中,当Sc³⁺含量从x=0逐渐增加至x=2时,Ce³⁺的蓝光发射强度提高了1.7倍;同时,Mn²⁺的红光发射强度提高了1.9倍,显示了优良的红光特性。样品的发射光谱和漫反射光谱表明,Ce³⁺、Mn²⁺发射强度的增加与Ce³⁺吸收能力和Ce³⁺向Mn²⁺能量传递的提升有直接关系。研究了样品Ba₉Sc₂(SiO₄)₆:Ce³⁺,Mn²⁺的热稳定性。随着温度的升高,Mn²⁺的红光发射呈现先升后降的态势。当温度从室温升至488 K时,Mn²⁺发射强度仅下降至室温时的84%,表现出优良的热稳定性。高亮的红光发射和优良的热稳定性表明该荧光材料可为紫外基白光LED提供良好的红色光源。     

红色长余辉材料Mg2SiO4：Dy3+,Mn2+的制备及发光特性

用高温固相法制备了长余辉发光材料Mg₂SiO₄:Dy³⁺,Mn²⁺,对这种材料的红色长余辉性质进行了研究.对以不同掺杂浓度单掺杂Mn²⁺、单掺杂Dy³⁺以及双掺杂Dy³⁺,Mn²⁺的Mg₂SiO₄体系,通过在紫外激发下的发射光谱及其激发光谱的研究,确认了在双掺杂体系中,峰值为660nm的发光带对应着Mn²⁺的⁴T₁(⁴G)→⁶A₁(⁶S)跃迁,Mn²⁺为主要发光中心.Mn²⁺的660nm发射的激发谱分布很宽,样品在近紫外和可见光区都有良好的吸收,长波边可达600nm,是这种材料的一个显著优点.还研究了双掺杂体系中Dy³⁺对Mn²⁺的660nm发光带的敏化作用.另外,通过对单掺杂、双掺杂体系热释光曲线的比较,揭示了双掺杂体系中Dy³⁺的陷阱作用.     

共沉淀法制备暖白光LED用Na2TiF6:Mn4+红色荧光粉及其发光性能研究

采用简便的共沉淀法制备了不同Mn⁴⁺ 掺杂摩尔分数的Na₂TiF₆:Mn⁴⁺ 红色荧光粉。通过X射线衍射仪、扫描电子显微镜、红外光谱仪、荧光光谱仪对荧光粉的结构、形貌、傅立叶红外光谱、激发和发射光谱及荧光寿命曲线进行了表征。结果表明,Mn⁴⁺的掺杂没有改变Na₂TiF₆的晶格结构,样品具有六方结构。Mn⁴⁺最佳掺杂摩尔分数为4.77%,量子效率为74%。在460 nm激发下,最强窄带发射峰位于628 nm处(²E_g-⁴A₂),色坐标为(0.681,0.317)。²E_g能级的荧光寿命曲线遵循双指数衰减,其荧光寿命值为3.148 ms。     

煅烧温度对Ba1.2Ca0.64SiO4：0.10Eu，0.06Mn粉体发光性能的影响

以MCM-41为硅源,在800~1 100℃下合成了Ba_1.2Ca_0.64SiO₄：0.10Eu,0.06Mn荧光粉,研究了煅烧温度对荧光粉发光性能的影响。实验结果表明,Eu²⁺的蓝绿光发射带的强度与宽度随煅烧温度的升高先增大后减小,在1 000℃时强度达到最大。最大发射峰位随温度的升高而发生红移,由800℃和900℃时的450 nm移至1 000℃和1 100℃时的480 nm。Mn²⁺的红光发射起源于Eu²⁺发射光的激发,其强度随温度的升高而增大。与Mn²⁺发生能量传递作用的Eu²⁺主要位于10配位的M（1）格位。     

红色长余辉材料Zn3(PO4)2：Mn2+,Ga3+的合成及光谱性质

采用高温固相法合成α、β和γ-Zn₃(PO₃)₂:Mn²⁺,Ga³⁺(ZPMG),XRD分析表明,高温合成过程中淬火条件有利于β相的形成,退火条件有利于γ相的形成。三种磷光粉的激发光谱分别位于246nm(α)、234nm(β和γ)的宽带谱。α相的发射光谱为位于508nm的锐线谱,β和γ相的发射光谱均存在两个谱带,分别位于508nm的绿色光谱区和616nm的红色光谱区。两种发射均归属为Mn²⁺的⁴T₁(⁴G)→⁶A_1g(⁶S)跃迁,但是由于Mn²⁺在Zn₃(PO₃)₂结构中的配位数不同,故发光颜色及强度均不同。对于余辉发射,只能观察到红色余辉光谱。