Dyand Mn emission in KMgSO4Cl phosphor

In the present paper, KMgSO₄Cl:Ce³⁺, KMgSO₄Cl:Ce³⁺,Dy³⁺, and KMgSO₄Cl:Ce³⁺,Mn²⁺, new halosulphate phosphors were synthesized by wet chemical method. X-ray powder diffraction (XRD) and photoluminescence (PL) characterization of phosphors have been reported in this paper. The effects of Dy³⁺ co-doping on the PL characteristics of KMgSO₄Cl:Ce phosphor were studied. Energy transfer from Ce³⁺→Dy³⁺and Ce³⁺→Mn²⁺ results in increase in PL peak intensity suggesting that Ce³⁺ plays an important role in PL emission in the present matrix. The PL emission spectra have two peaks (482 and 571 nm) and a single peak (564 nm), which could be attributed to the Ce³⁺→Dy³⁺and Ce³⁺→Mn²⁺ emissions, respectively.     

Luminescence in trivalent rare earth activated Sr4Al2O7 phosphor

In this paper we report the combustion synthesis of trivalent rare-earth (RE³⁺ = Dy, Eu and Ce) activated Sr₄Al₂O₇ phosphor. The prepared phosphors were characterized by the X-ray powder diffraction (XRD) and photoluminescence (PL) techniques. Photoluminescence emission peaks of Sr₄Al₂O₇:Dy³⁺ phosphor at 474 nm and 578 nm in the blue and yellow region of the spectrum. The prepared Eu³⁺ doped phosphors were excited by 395 nm then we found that the characteristics emission of europium ions at 615 nm (⁵D₀?⁷F₂) and 592 nm (⁵D₀?⁷F₁). Photoluminescence (PL) peaks situated at wavelengths of 363 and 378 nm in the UV region under excitation at around 326 nm in the Sr₄Al₂O₇:Ce³⁺ phosphor.     

Luminescent properties of Dy doped SrMoO4 phosphor

Trivalent dysprosium ions (Dy³⁺) doped strontium molybdate (SrMoO₄) phosphors were synthesized by solid-state reaction and their photoluminescence (PL) properties were investigated. X-ray powder diffraction (XRD) analysis confirmed the formation of SrMoO₄:Dy³⁺. PL measurements indicated that the phosphor exhibited intense emission at 482, 490 (⁴F_9/2→⁶H_15/2) and 575 nm (⁴F_9/2→⁶H_13/2) under UV excitation. The effect of the doping concentration of Dy³⁺in SrMoO₄:Dy³⁺ on the PL was investigated in detail. Na⁺ ion was a good charge compensator for SrMoO₄:Dy³⁺.     

Luminescence of KCaSO4Cl:X, Y (X=Eu or Ce; Y=Dy or Mn) halosulfate material

Polycrystalline KCaSO₄Cl:Eu, Dy, KCaSO₄Cl:Ce, Dy and KCaSO₄Cl:Ce, Mn phosphors prepared by a solid state diffusion method have been studied for its photoluminescence (PL) characteristics. The presence of two overlapping bands at around 400 and 450 nm in the PL emission spectra of the phosphor suggests the presence of Eu²⁺ in the host compound occupying two different lattice sites. The effects of co-doping on the photoluminescence (PL) characteristics of KCaSO₄Cl:Eu or Ce phosphors have been studied. The decrease in peak intensity of the phosphor on co-doping it with Dy gives an insight into the emission mechanism of the phosphors, which involves energy transfer from Eu²⁺→Dy³⁺, Ce³⁺→Dy³⁺ and Ce³⁺→Mn²⁺.     

Sol-gel growth of Gd2MoO6:Eu nanocrystalline layers on SiO2 spheres (SiO2@Gd2MoO6:Eu) and their luminescent properties

SiO₂@Gd₂MoO₆:Eu³⁺ core-shell phosphors were prepared by the sol-gel process. X-ray diffraction (XRD), Fourier transform infrared spectroscopy (FT-IR), field emission scanning electron microscopy (FESEM), energy-dispersive X-ray spectra (EDS), transmission electron microscopy (TEM), photoluminescence (PL) spectra as well as kinetic decays were used to characterize the resulting SiO₂@Gd₂MoO₆:Eu³⁺ core-shell phosphors. The XRD results demonstrate that the Gd₂MoO₆:Eu³⁺ layers on the SiO₂ spheres begin to crystallize after annealing at 600 °C and the crystallinity increases with raising the annealing temperature. The obtained core-shell phosphors have a near perfect spherical shape with narrow size distribution (average size ca. 600 nm), are not agglomerated, and have a smooth surface. The thickness of the Gd₂MoO₆:Eu³⁺ shells on the SiO₂ cores could be easily tailored by varying the number of deposition cycles (50 nm for four deposition cycles). The Eu³⁺ shows a strong PL luminescence (dominated by ⁵D₀-⁷F₂ red emission at 613 nm) under the excitation of 307 nm UV light. The PL intensity of Eu³⁺ increases with increasing the annealing temperature and the number of coating cycles.     

Enhanced luminescence of Ca3B2O6:Dy phosphors by Na-codoping for LED applications

The Ca_2.95−yDy_0.05B₂O₆:yNa⁺ (0≤y≤0.20) phosphors were synthesized at 1100 °C in air by the solid-state reaction route. The as-synthesized phosphors were characterized by X-ray powder diffraction (XRD), scanning electron microscopy (SEM), photoluminescence excitation (PLE), photoluminescence (PL) spectra and thermoluminescence (TL) spectra. The PLE spectra show the excitation peaks from 300 to 400 nm due to the 4f-4f transitions of Dy³⁺. This mercury-free excitation is useful for solid-state lighting and light-emitting diodes (LEDs). The emission of Dy³⁺ ions on 350 nm excitation was observed at 480 nm (blue) due to the ⁴F_9/2→⁶H_15/2 transitions, 575 nm (yellow) due to ⁴F_9/2→⁶H_13/2 transitions and 660 nm (red) due to weak ⁴F_9/2→⁶H_11/2 emissions. The PL results from the investigated Ca_2.95−yDy_0.05B₂O₆:yNa⁺ phosphors show that Dy³⁺ emissions increase with the increase of the Na⁺ codoping ions. The integral intensity of yellow to blue (Y/B) can be tuned by controlling Na⁺ content. By the simulation of white light, the optimal CIE value (0.328, 0.334) can be achieved when the content of Na⁺-codoping ions is y=0.2. The results imply that the Ca_2.95−yDy_0.05B₂O₆:yNa⁺ phosphors could be potentially used as white LEDs.     

Sol-gel synthesis, structural and optical properties of rare earth ions (Sm or Dy) activated Ca3Ga2Si3O12 powder phosphors

Structural, morphological and optical properties of rare earth ions (RE³⁺=Sm³⁺ or Dy³⁺) activated Ca₃Ga₂Si₃O₁₂ (CaGaSi) phosphors synthesized by the sol-gel method are reported. XRD results confirmed the cubic phase structure of RE³⁺:CaGaSi phosphors. From the SEM images of RE³⁺:CaGaSi phosphors, it is observed that the particles are agglomerated. Photoluminescence spectra of Sm³⁺:CaGaSi phosphors have shown bright orange red emission at 598 nm (⁴G_5/2→⁶H_7/2) with an excitation wavelength of λ_exci=401 nm. In the case of Dy³⁺:CaGaSi phosphors bright yellow emission has been observed at 574 nm (⁴F_9/2→ ⁶H_13/2) with λ_exci=451 nm. From the PL spectral results, the rare earth ion concentration of CaGaSi phosphors is optimized.     

Photoluminescence spectra of thenardite Na2SO4 activated with rare-earth ions, Ce, Sm, Tb, Dy and Tm

Five Na₂SO₄:RE³⁺ phosphors activated with rare-earth (RE) ions (RE³⁺=Ce³⁺, Sm³⁺, Tb³⁺, Dy³⁺ and Tm³⁺) were synthesized by heating natural thenardite Na₂SO₄ from Ai-Ding Salt Lake, Xinjiang, China with small amounts of rare-earth fluorides, CeF₃, SmF₃, TbF₃, DyF₃ and TmF₃, at 920 °C in air. The photoluminescence (PL) and optical excitation spectra of the obtained phosphors were measured at 300 and 10 K. In the PL spectrum of Na₂SO₄:Ce³⁺ at 300 K, two overlapping bands with peaks at 335 and 356 nm due to Ce³⁺ were first observed. Narrow bands observed in PL and excitation spectra of Na₂SO₄:RE³⁺ (RE³⁺=Sm³⁺, Tb³⁺, Dy³⁺ and Tm³⁺) phosphors were well identified with the electronic transitions within the 4fⁿ (n=5, 8, 9 and 12) configurations of RE³⁺. The existence of excitation bands with high luminescence efficiency at wavelengths shorter than 230 nm is characteristic of Na₂SO₄:RE³⁺ (RE³⁺=Sm³⁺, Tb³⁺, Dy³⁺ and Tm³⁺) phosphors. The obtained results suggest that these phosphors are unfavorable as the phosphor for usual fluorescence tubes, i.e., mercury discharge tubes, but may be favorable as the phosphor for UV-LED fluorescent tubes and as cathodoluminescence, X-ray luminescence and thermoluminescence phosphors.     

Correlation of photoluminescence of (Y, Ln)VO4:Eu (Ln=Gd and La) phosphors with their crystal structures

We have studied the photoluminescence (PL) of (Y, Ln)VO₄:Eu³⁺ (Ln=La and Gd) phosphors and the correlation of the PL of those phosphor with their crystal structure. It is found that (Y, Gd)VO₄:Eu³⁺ phosphors have the same crystal structure as YVO₄:Eu³⁺, which is tetragonal with a little different lattice parameters. In the case of (Y, La)VO₄:Eu³⁺ phosphors, however, the gradual change from tetragonal to monoclinic structure of host lattice was observed as the amount of La ion increased. To investigate the PL property of (Y, Ln)VO₄:Eu³⁺ (Ln=La and Gd) phosphors, vacuum ultraviolet (VUV) and ultraviolet (UV) excitation were used. The favorable crystal structure for the PL intensity of orthovanadate phosphor under 147 and 254 nm excitation was tetragonal containing Gd ion and under 365 nm excitation was monoclinic containing La ion which might have the lowest site symmetry for Eu³⁺ ion.     

VUV-UV excited luminescent properties of LnCa4O(BO3)3:RE (Ln=Y, La, Gd; Re=Eu, Tb, Dy, Ce)

Calcium lanthanide oxyborate doped with rare-earth ions LnCa₄O(BO₃)₃:RE³⁺ (LnCOB:RE, Ln=Y, La, Gd, RE=Eu, Tb, Dy, Ce) was synthesized by the method of solid-state reaction at high temperature. Their fluorescent spectra were measured from vacuum ultraviolet (VUV) to visible region at room temperature. Their excitation spectra all have a broadband center at about 188 nm, which is ascribed to host absorption. Using Dorenbos’ and Jφrgensen's work [P. Dorenbos, J. Lumin. 91 (2000) 91, R. Resfeld, C.K. Jφrgensen, Lasers and Excite States of Rare Earth [M], Springer, Berlin, 1977, p. 45], the position of the lowest 5d levels E(Ln,A) and charge transfer band E_ct were calculated and compared with their excitation spectra.Eu³⁺ and Tb³⁺ ions doped into LnCOB show efficient luminescence under VUV and UV irradiation. In this system, Ce³⁺ ions do not show efficient luminescence and quench the luminescence of Tb³⁺ ions when Tb³⁺ and Ce³⁺ ions are co-doped into LnCOB. GdCOB doped with Dy³⁺ shows yellowish white light under irradiation of 254 nm light for the reason that Gd³⁺ ions transfer the energy from itself to Dy³⁺. Because of the existence of Gd³⁺, the samples of GdCOB:RE³⁺ show higher excitation efficiency than LaCOB:RE³⁺ and YCOB:RE³⁺, around 188 nm, which indicates that the Gd³⁺ ions have an effect on the host absorption and can transfer the excitation energy to the luminescent center such as Tb³⁺, Dy³⁺ and Eu³⁺.     

Luminescent properties of (Y,Gd)BO3:Bi,RE (RE=Eu, Tb) phosphor under VUV/UV excitation

Bi³⁺- and RE³⁺-co-doped (Y,Gd)BO₃ phosphors were prepared and their luminescent properties under vacuum ultraviolet (VUV)/UV excitation were investigated. Strong red emission for (Y,Gd)BO₃:Bi³⁺,Eu³⁺ and strong green emission for (Y,Gd)BO₃:Bi³⁺,Tb³⁺ are observed under VUV excitation from 147 to 200 nm with a much broader excitation region than that of single Eu³⁺-doped or Tb³⁺-doped (Y,Gd)BO₃ phosphor. Strong emissions are also observed under UV excitation around 265 nm where as nearly no luminescence is observed for single Eu³⁺-doped or Tb³⁺-doped (Y,Gd)BO₃. The luminescence enhancement of Bi³⁺- and RE³⁺-co-doped (Y,Gd)BO₃ phosphors is due to energy transfer from Bi³⁺ ion to Eu³⁺ or Tb³⁺ ion not only in the VUV region but also in the UV region. Besides, host sensitization competition between Bi³⁺ and Eu³⁺ or Tb³⁺ is also observed. The investigated phosphors may be preferable for devices with a VUV light 147-200 nm as an excitation source such as PDP or mercury-free fluorescent lamp.     

Luminescence studies on SrMgAl10O17:Eu, Dy phosphor crystals

Using urea as fuel, SrMgAl₁₀O₁₇:Eu, Dy phosphor was prepared by a combustion method. Its luminescence properties under ultraviolet (UV) excitation were investigated. Pure SrMgAl₁₀O₁₇ phase was formed by urea-nitrate solution combustion synthesis at 550 °C. The results indicated that the emission spectra of SrMgAl₁₀O₁₇:Eu, Dy has one main peak at 460 nm and one shoulder peak near 516 nm, which are ascribed to two different types of luminescent Eu²⁺ centers existing in the SrMgAl₁₀O₁₇ matrix crystal. The blue luminescence emission of SrMgAl₁₀O₁₇:Eu phosphors was improved under UV excitation by codoping Dy³⁺ ions. The SrMgAl₁₀O₁₇:Eu phosphors showed green afterglow (λ=516 nm) when Dy³⁺ ions were doped. Dy³⁺ ions not only successfully play the role of sensitizer for energy transfer in the system, but also act as trap levels and capture the free holes in the spinel blocks.     

Synthesis and luminescence properties of needle-like SrAl2O4:Eu, Dy phosphor via a hydrothermal co-precipitation method

Needle-like SrAl₂O₄:Eu²⁺, Dy³⁺ phosphors had been prepared by calcining the precursors obtained from hydrothermal process at the temperature of 1100 °C in a weak reductive atmosphere of active carbon. The crystal structure, morphology and optical properties of the composites were characterized. X-ray diffraction (XRD) patterns illustrated that the single-phase SrAl₂O₄ was formed at 1100 °C, which is much lower than that prepared by the traditional method. The transmission electron microscope (TEM) observation revealed the precursors and the resulted SrAl₂O₄:Eu²⁺, Dy³⁺ phosphors had well-dispersed distribution and needle-like morphology with an average diameter about 150 nm at the center and the length up to 1 μm. After irradiation by ultraviolet radiation with 350 nm for 5 min, the phosphors emit green color long-lasting phosphorescence corresponding to the typical emission of Eu²⁺ ion, both the PL spectra and luminance decay revealed that the phosphors had efficient luminescent and long lasting properties.     

Synthesis, characterization and optical properties of water-soluble ZnS:Mn nanoparticles

ZnS nanoparticles with Mn²⁺ doping (0.5-20%) have been prepared through a simple chemical method, namely the chemical precipitation method. The structure of the nanoparticles has been analyzed using X-ray diffraction (XRD), scanning electron microscope (SEM), transmission electron microscope (TEM) and UV-vis spectrometer. The size of the particles is found to be 3-5 nm range. Photoluminescence spectra were recorded for undoped ZnS nanoparticles using an excitation wavelength of 320 nm, exhibiting an emission peak centered at around 445 nm. However, from the Mn²⁺-doped samples, a yellow-orange emission from the Mn²⁺⁴T₁-⁶A₁ transition is observed along with the blue emission. The prepared Mn²⁺-doped sample shows efficient emission of yellow-orange light with the peak emission 580 nm with the blue emission suppressed. The maximum PL intensity is observed only at the excitation energy of 3.88 eV (320 nm). Increase in stabilizing time up to 48 h in de-ionized water yields the enhancement of emission intensity of doped (4% Mn²⁺) ZnS. The correlation made through the concentration of Mn²⁺ versus PL intensity resulted in opposite trend (mirror image) of blue and yellow emissions.     

Photoluminescence and phosphorescence properties of MAl2O4:Eu, Dy (M=Ca, Ba, Sr) phosphors prepared at an initiating combustion temperature of 500 °C

Eu²⁺ and Dy³⁺ co-doped calcium aluminate, barium aluminate and strontium aluminate phosphors were synthesized at an initiating combustion temperature of 500 °C using urea as an organic fuel. The crystallinity of the phosphors was investigated by using X-ray diffraction (XRD) and the morphology was determined by a scanning electron microscope (SEM). The low temperature monoclinic structure for both CaAl₂O₄ and SrAl₂O₄ and the hexagonal structure of BaAl₂O₄ were observed. The effect of the host materials on the photoluminescence (PL) and phosphorescence properties were investigated by using a He-Cd Laser and a Cary Eclipse fluorescence spectrophotometer, respectively. The broad band emission spectra observed at 449 nm for CaAl₂O₄:Eu²⁺, Dy³⁺, 450 nm (with a shoulder-peak at 500 nm) for BaAl₂O₄:Eu²⁺, Dy³⁺ and 528 nm for SrAl₂O₄:Eu²⁺, Dy³⁺ are attributed to the 4f⁶5d¹ to 4f⁷ transition in the Eu²⁺ ion in the different hosts.     

Synthesis and luminescent properties of a new red-emitting phosphor for solid-state lighting: Eu0.1GdxLa1.9−xTeO6 (0.02?x?0.1)

The photoluminescence (PL) emission and excitation behavior of red-emitting Eu_0.1Gd_xLa_1.9−xTeO₆ (0.02?x?0.1) powder phosphors is reported. Three dominant bands centered at 395, 466 and 534 nm characterized the excitation spectrum. Under the excitation of 395 nm UV light, the emission spectrum exhibits an intense peak centered at 616 nm corresponding to the ⁵D₀→⁷F₂ transition of Eu³⁺. Because the f→f transitions are located in the wavelength range of blue or near-UV range, optimized phosphor, Eu_0.10Gd_0.08La_1.82TeO₆, is a promising material for solid-state lighting based on GaN LEDs applications.     

Intense green/yellow emission in Ca8Zn(SiO4)4Cl2:Eu, Mn through energy transfer for blue-LED lighting

Eu²⁺ and Mn²⁺ co-doped Ca₈Zn(SiO₄)₄Cl₂ phosphors have been synthesized by a high temperature solid state reaction. Energy transfer from Eu²⁺ to Mn²⁺ is observed. The emission spectra of the phosphors show a green band at 505 nm of Eu²⁺ and a yellow band at 550 nm of Mn²⁺. The excitation spectra corresponding to 4f⁷-4f⁶5d transition of Eu²⁺ cover the spectral range of 370-470 nm, well matching UV and/or blue LEDs. The shortening of fluorescent lifetimes of Eu²⁺ followed by simultaneous increase of fluorescent intensity of Mn²⁺ with increasing Mn²⁺ concentrations is studied based on energy transfer. Upon blue light excitation the present phosphor can emit intense green/yellow in comparison with other chlorosilicate phosphors such as Eu²⁺ and Mn²⁺ co-doped Ca₈Mg(SiO₄)₄Cl₂ and Ca₃SiO₄Cl₂, demonstrating a potential application in phosphor converted white LEDs.     

The effects of substrate temperature on the structure, morphology and photoluminescence properties of pulsed laser deposited SrAl2O4:Eu,Dy thin films

In this study, SrAl₂O₄:Eu²⁺,Dy³⁺ thin film phosphors were deposited on Si (1 0 0) substrates using the pulsed laser deposition (PLD) technique. The films were deposited at different substrate temperatures in the range of 40-700 °C. The structure, morphology and topography of the films were determined by using X-ray diffraction (XRD), atomic force microscopy (AFM), scanning electron microscopy (SEM) and high resolution transmission electron microscopy (HRTEM). Photoluminescence (PL) data was collected in air at room temperature using a 325 nm He-Cd laser as an excitation source. The PL spectra of all the films were characterized by green phosphorescent photoluminescence at ∼530 nm. This emission was attributed to 4f⁶5d¹→4f⁷ transition of Eu²⁺. The highest PL intensity was observed from the films deposited at a substrate temperature of 400 °C. The effects of varying substrate temperature on the PL intensity were discussed.     

Dy3+ emission in M5(PO4)3F (M = Ca, Ba) phosphor

Ultrafine M₅(PO₄)₃F:Dy³⁺ (M = Ca, Ba) phosphors were prepared via combustion process using metal nitrates as precursors. The formation of crystalline phosphate was confirmed by X-ray diffraction pattern. The PL excitation spectra show the excitation peaks observed at 250 to 400 nm due to f → f transition of Dy³⁺ ion, which are useful for solid-state lighting purpose (mercury free excitation). The PL emission of Dy³⁺ ion by 348 nm excitation gave an emission at 489 nm (blue), 582 nm (yellow) and 675 nm (red). All the characteristics of BYR emissions like BGR indicate that Dy doped Ca₅(PO₄)₃F and Ba₅(PO₄)₃F phosphors are good candidates that can be applied in solid-state lighting phosphor (mercury free excited lamp phosphor) and white light LED.      

Effect of RE as a co-dopant in long-lasting phosphorescence CdSiO3:Mn (RE=Y, La, Gd, Lu)

Effect of RE³⁺ as a co-dopant in long-lasting phosphorescence CdSiO₃:Mn²⁺ (RE=Y, La, Gd, Lu) has been investigated. A longer orange emitting phosphorescence phenomenon was observed in the co-doped CdSiO₃:Mn²⁺,RE³⁺ phosphors after exciting with ultraviolet (UV) light. The luminescence properties, including photoluminescence (PL) spectra and thermoluminescence (TL) spectra, as well as the afterglow decay curves, were studied. The results revealed that one of the origins of the improvement is due to nonequivalent substitution to produce more e-traps, and energy transfer from Gd³⁺ to Mn²⁺ to boost the performance of CdSiO₃:Mn²⁺,Gd³⁺. Role of RE³⁺ co-doped into CdSiO₃:Mn²⁺ matrix and the possible long-lasting phosphorescence process are discussed in this paper.