Sol-gel growth of Gd2MoO6:Eu nanocrystalline layers on SiO2 spheres (SiO2@Gd2MoO6:Eu) and their luminescent properties

SiO₂@Gd₂MoO₆:Eu³⁺ core-shell phosphors were prepared by the sol-gel process. X-ray diffraction (XRD), Fourier transform infrared spectroscopy (FT-IR), field emission scanning electron microscopy (FESEM), energy-dispersive X-ray spectra (EDS), transmission electron microscopy (TEM), photoluminescence (PL) spectra as well as kinetic decays were used to characterize the resulting SiO₂@Gd₂MoO₆:Eu³⁺ core-shell phosphors. The XRD results demonstrate that the Gd₂MoO₆:Eu³⁺ layers on the SiO₂ spheres begin to crystallize after annealing at 600 °C and the crystallinity increases with raising the annealing temperature. The obtained core-shell phosphors have a near perfect spherical shape with narrow size distribution (average size ca. 600 nm), are not agglomerated, and have a smooth surface. The thickness of the Gd₂MoO₆:Eu³⁺ shells on the SiO₂ cores could be easily tailored by varying the number of deposition cycles (50 nm for four deposition cycles). The Eu³⁺ shows a strong PL luminescence (dominated by ⁵D₀-⁷F₂ red emission at 613 nm) under the excitation of 307 nm UV light. The PL intensity of Eu³⁺ increases with increasing the annealing temperature and the number of coating cycles.     

Optical properties of In2O3 oxidized from InN deposited by reactive magnetron sputtering

Unintentionally doped and zinc-doped indium nitride (U-InN and InN:Zn) films were deposited on (0 0 0 1) sapphire substrates by radio-frequency reactive magnetron sputtering, and all samples were then treated by annealing to form In₂O₃ films. U-InN and InN:Zn films have similar photon absorption characteristics. The as-deposited U-InN and InN:Zn film show the absorption edge, ∼1.8-1.9 eV. After the annealing process at 500 °C for 20 min, the absorption coefficient at the visible range apparently decreases, and the absorption edge is about 3.5 eV. Two emission peaks at 3.342 eV (371 nm) and 3.238 eV (383 nm) in the 20 K photoluminescence (PL) spectrum of In₂O₃:Zn films were identified as the free-exciton (FE) or the near band-to-band (B-B) and conduction-band-to-acceptor (C-A) recombination, respectively.     

Modified thermal evaporation process using GeO2 for growing ZnO structures

In the current work, zinc oxide (ZnO) nano/microstructures are synthesized using a modified thermal-evaporation process by introducing germanium oxide (GeO₂) powder mixed with metallic Zn powder as the raw material. Without the use of any catalyst and oxygen flow in the furnace system, GeO₂ is utilized to provide an oxygen source for the growth of ZnO structure. The samples are treated by different temperatures ranging from 500 to 900 °C. Morphology, phase structure, and photoluminescence properties are investigated by scanning electron microscopy (SEM), X-ray diffractometer (XRD) and photoluminescence (PL) spectrometer. The structures and morphologies of the samples were found to vary with growth temperature. The XRD diffraction peaks show that the films grown at temperature from 600 to 800 °C consist of hexagonal wurtzite ZnO structures. Room-temperature PL measurement revealed ZnO spectra representing two bands: near-band-edge emission in the ultraviolet (UV) region and broad deep-level emission centered at about 500 nm. The strong UV emission in the PL spectra indicates that the GeO₂ supplies sufficient oxygen for formation of ZnO structures with few oxygen vacancies. The growth mechanism and the roles of GeO₂ for formation of ZnO structures are discussed in detail.     

Synthesis of In-doped Ga2O3 zigzag-shaped nanowires and optical properties

In-doped Ga₂O₃ zigzag-shaped nanowires and undoped Ga₂O₃ nanowires have been synthesized on Si substrate by thermal evaporation of mixed powders of Ga, In₂O₃ and graphite at 1000 °C without using any catalyst via a vapor-solid growth mechanism. The morphologies and microstructures of the products were characterized by field-emission scanning electron microscopy (FE-SEM), X-ray diffraction (XRD), transmission electron microscopy (TEM), energy-dispersive X-ray spectroscopy (EDS) and photoluminescence spectroscopy (PL). The nanowires range from 100 nm to several hundreds of nanometers in diameter and several tens of micrometers in length. A broad emission band from 400 to 700 nm is obtained in the PL spectrum of these nanowires at room temperature. There are two blue-emission peaks centering at 450 and 500 nm, which originate from the oxygen vacancies, gallium vacancies and gallium-oxygen vacancy pairs.     

Luminescence in trivalent rare earth activated Sr4Al2O7 phosphor

In this paper we report the combustion synthesis of trivalent rare-earth (RE³⁺ = Dy, Eu and Ce) activated Sr₄Al₂O₇ phosphor. The prepared phosphors were characterized by the X-ray powder diffraction (XRD) and photoluminescence (PL) techniques. Photoluminescence emission peaks of Sr₄Al₂O₇:Dy³⁺ phosphor at 474 nm and 578 nm in the blue and yellow region of the spectrum. The prepared Eu³⁺ doped phosphors were excited by 395 nm then we found that the characteristics emission of europium ions at 615 nm (⁵D₀?⁷F₂) and 592 nm (⁵D₀?⁷F₁). Photoluminescence (PL) peaks situated at wavelengths of 363 and 378 nm in the UV region under excitation at around 326 nm in the Sr₄Al₂O₇:Ce³⁺ phosphor.     

Preparation and characterization of multi-functional CoFe2O4-ZnO nanocomposites

Multi-functional magnetic, photoluminescent and photocatalytic CoFe₂O₄-ZnO nanocomposites were successfully synthesized by a collosol method. The average diameter of the prepared CoFe₂O₄-ZnO nanocomposites was 30±5 nm, and a diffusion layer was formed to link CoFe₂O₄ and ZnO. The saturation magnetization of the CoFe₂O₄-ZnO nanocomposites was 8.99 emu/g. Generation of ZnO from Zn(OH)₂ collosol was nearly complete after thermal decomposition at about 380 °C. A photoluminescence emission peak was observed at 443 nm when excitated at 350 nm. Degradation of methyl orange is performed by CoFe₂O₄-ZnO nanocomposites under ultraviolet radiation, with a degradation rate of up to 93.9%.     

Synthesis and characterization of TiO2/Fe2O3 core-shell nanocomposition film and their photoelectrochemical property

TiO₂/Fe₂O₃ core-shell nanocomposition film has been fabricated via two-step method. TiO₂ nanorod arrays are synthesized by a facile hydrothermal method, and followed by Fe₂O₃ nanoparticles deposited on TiO₂ nanorod arrays through an ordinary chemical bath deposition. The phase structures, morphologies, particle size, chemical compositions of the composites have been characterized by X-ray diffraction (XRD), field emission scanning electron microscope (FESEM) and ultraviolet-visible (UV-vis) spectrophotometer. The results confirm that Fe₂O₃ nanoparticles of mean size ca. 10 nm coated on the surface of TiO2 NRs. After depositing Fe₂O₃, UV-vis absorption property is induces the shift to the visible-light range, the annealing temperature of 600 °C is the best condition for UV-vis absorption property of TiO₂/Fe₂O₃ nanocomposite film, and increasing Fe content, optical activity are enhanced one by one. The photoelectrochemical (PEC) performances of the as-prepared composite nanorods are determined by measuring the photo-generated currents under illumination of UV-vis light. The TiO₂ NRs modified by Fe₂O₃ show the photocurrent value of 1.36 mA/cm² at 0 V vs Ag/AgCl, which is higher than those of unmodified TiO₂ NRs.     

The effect of different gas atmospheres on luminescent properties of pulsed laser ablated SrAl2O4:Eu,Dy thinfilms

SrAl₂O₄:Eu²⁺,Dy³⁺ thin films were grown on Si (1 0 0) substrates using the pulsed laser deposition (PLD) technique to investigate the effect of vacuum, oxygen (O₂) and argon (Ar) deposition atmospheres on the structural, morphological, photoluminescence (PL) and cathodoluminescence (CL) properties of the films. The films were ablated using a 248 nm KrF excimer laser. Atomic force microscopy (AFM), scanning electron microscopy (SEM), X-ray diffraction (XRD), energy dispersive X-ray spectroscopy (EDS) and fluorescence spectrophotometry were used to characterize the thin films. Auger electron spectroscopy (AES) combined with CL spectroscopy were employed for the surface characterization and electron-beam induced degradation of the films. Better PL intensities were obtained from the unannealed films prepared in Ar and O₂ atmospheres with respect to those prepared in vacuum. A stable green emission peak at 515 nm, attributed to 4f⁶5d¹→4f⁷ Eu²⁺ transitions were obtained with less intense peaks at 619 nm, which were attributed to transitions in Eu³⁺. After annealing the films prepared in vacuum at 800 °C for 2 h, the intensity of the green emission (520 nm) of the thin film increased considerably. The amorphous thin film was crystalline after the annealing process. The CL intensity increased under prolonged electron bombardment during the removal of C due to electron stimulated surface chemical reactions (ESSCRs) on the surface of the SrAl₂O₄:Eu²⁺, Dy³⁺ thin films. The CL stabilized and stayed constant thereafter.     

Role of Ti in the luminescence process of Al2O3:Si,Ti

Al₂O₃:Si,Ti, prepared under oxidizing condition at high temperature, gives PL emission around 430 nm when excited with 240 nm. The Al₂O₃:C, TL/OSL phosphor, also shows emission around 430 nm, which corresponds to characteristic emission of F-center. Thus, to identify the exact nature of luminescent center in Al₂O₃:Si,Ti, fluorescence lifetime measurement studies were carried out along with the PL,TL and OSL studies. The PL and TL in Al₂O₃:Si,Ti show emission around 430 nm and the time-resolved fluorescence studies show lifetime of about 43 μs for the 430 nm emission, which is much smaller than the reported lifetime of ∼35 ms for the 430 nm emission (F-center emission) in Al₂O₃:C phosphor. Therefore, the emission observed in Al₂O₃:Si,Ti phosphor was assigned to Ti⁴⁺ charge transfer transition. Fluorescence studies of Al₂O₃:Si,Ti do not show any traces of F and F⁺ centers. Also, Ti⁴⁺ does not show any change in the charge state after gamma-irradiation. On the basis of the above studies, a mechanism for TSL/OSL process in Al₂O₃:Si,Ti is proposed.     

Structural, optical and electrical properties of ZnO/Zn2GeO4 porous-like thin film and wires

Zinc oxide/zinc germanium oxide (ZnO/Zn₂GeO₄) porous-like thin film and wires has been fabricated by simple thermal evaporation method at temperature about 1120 °C for 2.5 h. The structural and optical properties of the porous-like-thin film and wires have been investigated by scanning electron microscopy (SEM), energy-dispersive X-ray spectroscopy (EDX), X-ray diffraction (XRD) and photoluminescence (PL) spectroscopy. Metal semiconductor metal (MSM) photodetector structure was used to evaluate the electrical characteristics by using current-voltage (I-V) measurements. Room temperature photoluminescence spectrum of the sample shows one prominent ultraviolet peak at 378 nm and a shoulder at 370 nm. In addition, broad visible blue emission peak at wavelength 480 nm and green emission peak at 500 nm are also observed. Strong photoelectric properties of the MSM in the UV demonstrated that the porous-like-thin film and wires contribute to its photosensitivity and therefore making ZnO/Zn₂GeO₄ wires potential photodetector in the shorter wavelength applications.     

Green synthesis of soya bean sprouts-mediated superparamagnetic Fe3O4 nanoparticles

Superparamagnetic Fe₃O₄ nanoparticles were first synthesized via soya bean sprouts (SBS) templates under ambient temperature and normal atmosphere. The reaction process was simple, eco-friendly, and convenient to handle. The morphology and crystalline phase of the nanoparticles were determined from scanning electron microscopy (SEM), transmission electron microscopy (TEM), selected area electron diffraction (SAED), and X-ray diffraction (XRD) spectra. The effect of SBS template on the formation of Fe₃O₄ nanoparticles was investigated using X-ray photoemission spectroscopy (XPS) and Fourier-transform infrared spectroscopy (FT-IR). The results indicate that spherical Fe₃O₄ nanoparticles with an average diameter of 8 nm simultaneously formed on the epidermal surface and the interior stem wall of SBS. The SBS are responsible for size and morphology control during the whole formation of Fe₃O₄ nanoparticles. In addition, the superconducting quantum interference device (SQUID) results indicate the products are superparamagnetic at room temperature, with blocking temperature (T_B) of 150 K and saturation magnetization of 37.1 emu/g.     

Synthesis and photoluminescence properties of aqueous CdWO4 quantum dots with WO6 luminescence center

Aqueous CdWO₄ QDs were synthesized by the reaction of CdCl₂ and Na₂WO₄ in the presence of mercaptoacetic acid (TGA) as capping reagent. The crystal morphology, particle size and its distribution of as-prepared products were characterized by transmission electron microscopy (TEM, SAED) atomic force microscopy (AFM), high-resolution transmission electron microscopy (HRTEM), and photon correlation spectroscopy (PCS), respectively. Qualitative assays for functional groups on the QDs’ surface were measured by fourier transform infrared spectroscopy (FTIR). Photoluminescence properties of QDs were studied by photoluminescence spectroscopy (PL). The results showed that the single QD with diameter of about 8 ± 2 nm was single-crystal. The particle size distribution of QDs was normal. Infrared absorption bands of carboxylic group on the surface of CdWO₄ QDs were observed around 1610-1550 cm⁻¹ (nonsymmetrical vibration of -COO⁻) and 1400 cm⁻¹ (symmetric vibration of C-O). With reaction-time going, PL peak position shifted from 498 to 549 nm and intensity of PL increased first and then decreased. PL peak position of QDs was blue-shift compared with 570 nm WO₆⁶⁻ luminescence center of bulk CdWO₄.     

Synthesis of Y2Si2O7:Eu nanocrystal and its optical properties

Nanocrystalline Y₂Si₂O₇:Eu phosphor with an average size about 60 nm is easily prepared using silica aerogel as raw material under ultrasonic irradiation and annealing temperature at 300-600 °C and this nanocrystalline decomposes into Y₂O₃:Eu and silica by heat treatment at 700-900 °C. The excitation broad band centered at 283 and 254 nm results from Eu³⁺ substituting for Y³⁺ in Y₂Si₂O₇ and Y₂O₃/SiO₂, respectively. Compared with Y₂O₃:Eu/SiO₂ crystalline, the PL excitation and emission peaks of Y₂Si₂O₇:Eu nanocrystalline red-shift and lead to the enhance of its luminescence intensity due to the different chemical surroundings of Eu³⁺ in above nanocrystallines. The decrease of PL intensity may be ascribed to quenching effect resulting from more defects in Y₂O₃:Eu/SiO₂ crystalline.     

Photoluminescence from ZnO-SiO2 opals with different sphere diameters and thicknesses

We systematically investigated the photoluminescence (PL) and transmittance characteristics of ZnO-SiO₂ opals with varied positions of the stop-band and film thicknesses. An improved ultraviolet (UV) luminescence was observed from ZnO-SiO₂ composites over pure ZnO nanocrystals under 325 nm He-Cd laser excitation at room temperature. The UV PL of ZnO nanocrystals in SiO₂ opals with stop-bands center of 410 nm is sensitive to the thickness of opal films, and the UV PL intensity increases with the film thickness increasing. The PL spectra of ZnO nanocrystals in SiO₂ opals with stop-bands center of 570 nm show a suppression of the weak visible band. The experimental results are discussed based on the scattering and/or absorbance in opal crystals.     

Towards anode with low indium content as effective anode in organic solar cells

In₂O₃ thin films (100 nm thick) have been deposited by reactive evaporation of indium, in an oxygen partial atmosphere. Conductive (σ = 3.5 × 10³ S/cm) and transparent films are obtained using the following experimental conditions: oxygen partial pressure = 1 × 10⁻¹ Pa, substrate temperature = 300 °C and deposition rate = 0.02 nm/s. Layers of this In₂O₃ thick of 5 nm have been introduced in AZO/In₂O₃ and FTO/In₂O₃ multilayer anode structures. The performances of organic photovoltaic cells, based on the couple CuPc/C₆₀, are studied using the anode as parameter. In addition to these bilayers, other structures have been used as anode: AZO, FTO, AZO/In₂O₃/MoO₃, FTO/In₂O₃/MoO₃ and FTO/MoO₃. It is shown that the use of the In₂O₃ film in the bilayer structures improves significantly the cell performances. However the open circuit voltage is quite small while better efficiencies are achieved when MoO₃ is present. These results are discussed in the light of surface roughness and surface work function of the different anodes.     

Surface characterization and luminescent properties of SrAl2O4:Eu,Dy nano thin films

SrAl₂O₄:Eu²⁺, Dy³⁺ thin films were grown on Si (1 0 0) substrates in different atmospheres using the pulsed laser deposition (PLD) technique. The effects of vacuum, oxygen (O₂) and argon (Ar) deposition atmospheres on the structural, morphological and photoluminescence (PL) properties of the films were investigated. The films were ablated using a 248 nm KrF excimer laser. Improved PL intensities were obtained from the unannealed films prepared in Ar and O₂ atmospheres compared to those prepared in vacuum. A stable green emission peak at 520 nm, attributed to 4f⁶5d¹→4f⁷ Eu²⁺ transitions was obtained. After annealing the films prepared in vacuum at 800 °C for 2 h, the intensity of the green emission (520 nm) of the thin film increased considerably. The amorphous thin film was crystalline after the annealing process. The diffusion of adventitious C into the nanostructured layers deposited in the Ar and O₂ atmospheres was most probably responsible for the quenching of the PL intensity after annealing.     

Excitonic photoluminescence properties of nanocrystalline GaSb and Ga0.62In0.38Sb embedded in silica films

The GaSb and Ga_0.62In_0.38Sb nanocrystals were embedded in the SiO₂ films by radio-frequency magnetron co-sputtering and were grown on GaSb and Si substrates at different temperatures. We present results on the 10 K excitonic photoluminescence (PL) properties of nanocrystalline GaSb and Ga_0.62In_0.38Sb as a function of their size. The measurements show that the PL of the GaSb and Ga_0.62In_0.38Sb nanocrystallites follows the quantum confinement model very closely. By using deconvolution of PL spectra, origins of structures in PL were identified.     

Characterization of single-crystalline In2O3 films deposited on Y-stabilized ZrO2 (1 0 0) substrates by MOCVD

Epitaxial In₂O₃ films have been deposited on Y-stabilized ZrO₂ (YSZ) (1 0 0) substrates by metalorganic chemical vapor deposition (MOCVD). The films were deposited at different substrate temperatures (450-750 °C). The film deposited at 650 °C has the best crystalline quality, and observation of the interface area shows a clear cube-on-cube epitaxial relationship of In₂O₃(1 0 0)||YSZ(1 0 0) with In₂O₃[0 0 1]||YSZ[0 0 1]. The Hall mobility of the single-crystalline In₂O₃ film deposited at 650 °C is as high as 66.5 cm² V⁻¹ s⁻¹ with carrier concentration of 1.5 × 10¹⁹ cm⁻³ and resistivity of 6.3 × 10⁻³ Ω cm. The absolute average transmittance of the obtained films in the visible range exceeds 95%.     

Preparation and luminescent characteristic of Li3NbO4 nanophosphor

Synthesis and luminescence properties of Li₃NbO₄ oxides by the sol-gel process were investigated. The products were characterized by the X-ray diffraction (XRD), scanning electron microscopy (SEM), photoluminescence (PL) spectroscopy and absorption spectra. The PL spectra excited at 247 nm have a broad and strong blue emission band maximum at 376 nm, corresponding to the self-activated luminescence of the niobate octahedra group [NbO₆]⁷⁻. The optical absorption spectra of the samples sintered at temperatures of 600 and 700 °C exhibited the band-gap energies of 4.0 and 4.08 eV.     

Preparation and photoluminescence characteristics of Eu-doped MgAl1.8Y0.2O4 nanocrystals

A simple combustion route was employed for the preparation of Eu³⁺-doped MgAl_1.8Y_0.2−xO₄ nanocrystals using metal nitrates as precursors and urea as a fuel in a preheated furnace at 500 °C. The powders thus obtained were then fired at 1000 °C for 3 h to get better luminescent properties. The incorporation of Eu³⁺ activator in these nanocrystals was checked by luminescence characteristics. These nanocrystals displayed bright red color on excitation under 254 nm UV source. The main emission peak was assigned to the transition [⁵D₀→⁷F₂] at 615 nm. Scanning electron microscopy (SEM) and transmission electron microscopy (TEM) studies were carried out to understand surface morphological features and the particle size. Crystal structures of the nanocrystals were investigated by the X-ray diffraction (XRD) technique. The crystallite size of the as-prepared nanocrystals was around 29 nm, which was evaluated from the broad XRD peaks. The crystallite size increased to ∼45 nm on further heat treatment at 1000 °C.