Correlation between the surface chemistry and the atmospheric corrosion of AZ31, AZ80 and AZ91D magnesium alloys

X-ray photoelectron spectroscopy (XPS) was used in order to investigate the correlation between the surface chemistry and the atmospheric corrosion of AZ31, AZ80 and AZ91D magnesium alloys exposed to 98% relative humidity at 50 °C. Commercially pure magnesium, used as the reference material, revealed MgO, Mg(OH)₂ and tracers of magnesium carbonate in the air-formed film. For the AZ80 and AZ91D alloys, the amount of magnesium carbonate formed on the surface reached similar values to those of MgO and Mg(OH)₂. A linear relation between the amount of magnesium carbonate formed on the surface and the subsequent corrosion behaviour in the humid environment was found. The AZ80 alloy revealed the highest amount of magnesium carbonate in the air-formed film and the highest atmospheric corrosion resistance, even higher than the AZ91D alloy, indicating that aluminium distribution in the alloy microstructure influenced the amount of magnesium carbonate formed.     

Characterization of ceramic PVD thin films on AZ31 magnesium alloys

Ceramic thin films have been widely used to protect the metal substrate as coatings in the past years. In order to improve the poor corrosion resistance of AZ31 magnesium alloy, the study in this paper used the electron beam evaporation method to prepare ceramic PVD films on its surface with TiO₂ and Al₂O₃ as donors, respectively. Atomic force microscopy (AFM), scanning electron microscope (SEM), energy dispersive X-ray spectrometer (EDS), Auger electron spectroscopy (AES) and X-ray diffraction (XRD) were used to investigate the surface morphology, composition and microstructure of the thin films. Both films deposited on AZ31 took on compact top surface morphologies and grew as amorphous structures on substrate. AES test not only showed that films compositions deviated the standard stoichiometric ratios, but also found that element Mg diffused into films and existed as magnesium oxide in the TiO_x film as well as the AlO_x film. In the electrochemical corrosion test, the AlO_x coating on AZ31 exhibited the largest electrochemical impedance in a 3.5% NaCl solution. But it did not show better corrosion resistance than others for the poorer adhesion. Even if its thickness was small, the TiO_x coating on AZ31 exhibited the best corrosion resistance in this study. According to the observation and analysis, the damage of these films on AZ31 in aggressive solutions was mainly due to the existence of pores, microcracks, vacancies and poor adhesion between coating and substrate.     

Studies on influence of zinc immersion and fluoride on nickel electroplating on magnesium alloy AZ91D

The effect of zinc immersion and the role of fluoride in nickel plating bath were mainly investigated in nickel electroplating on magnesium alloy AZ91D. The state of zinc immersion, the composition of zinc film and the role of fluoride in nickel plating bath were explored from the curves of open circuit potential (OCP) and potentiodynamic polarization, the images of scanning electron microscopy (SEM) and the patterns of energy dispersive X-ray (EDX). Results show that the optimum zinc film mixing small amount of Mg(OH)₂ and MgF₂ is obtained by zinc immersion for 30-90 s. The corrosion potential of magnesium alloy substrate attached zinc film will be increased in nickel plating bath and the quantity of MgF₂ sandwiched between magnesium alloy substrate and nickel coating will be reduced, which contributed to produce nickel coating with good performance. Fluoride in nickel plating bath serves as an activator of nickel anodic dissolution and corrosion inhibitor of magnesium alloy substrate. 1.0-1.5 mol dm⁻³ of F⁻ is the optimum concentration range for dissolving nickel anode and protecting magnesium alloy substrate from over-corrosion in nickel plating bath. The nickel coating with good adhesion and high corrosion resistance on magnesium alloy AZ91D is obtained by the developed process of nickel electroplating. This nickel layer can be used as the rendering coating for further plating on magnesium alloys.     

Electrodeposition of Al-Mn alloy on AZ31B magnesium alloy in molten salts

The Al-Mn alloy coatings were electrodeposited on AZ31B Mg alloy in AlCl₃-NaCl-KCl-MnCl₂ molten salts at 170 °C aiming to improve the corrosion resistance. However, in order to prevent AZ31B Mg alloy from corrosion during electrodeposition in molten salts and to ensure excellent adhesion of coatings to the substrate, AZ31B Mg alloy should be pre-plated with a thin zinc layer as intermediate layer. Then the microstructure, composition and phase constituents of the coatings were investigated by scanning electron microscopy (SEM), energy-dispersive X-ray spectrometry (EDX), and X-ray diffraction (XRD). It was indicated that, by adjusting the MnCl₂ content in the molten salts from 0.5 wt% to 2 wt%, the Mn content in the alloy coating was increased and the phase constituents were changed from f.c.c Al-Mn solid solution to amorphous phase. The corrosion resistance of the coatings was evaluated by potentiodynamic polarization measurements in 3.5% NaCl solution. It was confirmed that the Al-Mn alloy coatings exhibited good corrosion resistance with a chear passive region and significantly reduced corrosion current density at anodic potentiodynamic polarization. The corrosion resistance of the alloy coatings was also related with the microstructure and Mn content of the coatings.     

镁合金阳极氧化膜腐蚀特性的红外显微成像分析

采用显微红外成像技术对镁合金阳极氧化膜表面的腐蚀特性进行了研究。镁合金在7.3 Wt% Na₂SO₄溶液中浸泡后,表面氧化层中的部分MgO逐渐转化为Mg(OH)₂,进而发生溶解和脱落,使得镁合金失去保护作用。当浸泡时间达到2 h时,显微红外成像结果表明阳极氧化膜中Mg(OH)₂的红外吸收信号最强,Mg(OH)₂的含量最多。而4 h后Mg(OH)₂的红外吸收信号开始减弱,Mg(OH)₂开始减少,镁合金不断被腐蚀。氧化膜中另一成分Al₂O₃随浸泡时间的显微红外成像信息与Mg(OH)₂的变化规律相同。采用电化学阻抗谱技术对阳极氧化膜的阻抗进行测试,其阻抗随时间的变化特点基本符合氧化膜腐蚀规律。本研究对于镁合金阳极氧化膜的表征具有很好的指导作用和推广应用价值。     

Corrosion behaviors in physiological solution of cerium conversion coatings on AZ31 magnesium alloy

In this paper, a non-toxic Ce-based conversion coating was obtained on the surface of bio-medical AZ31 magnesium alloys. The micro-morphology of the coating prepared with optimal technical parameters and immersed in physiological solution (Hank's solution) in different time was observed by scanning electron microscopy (SEM), composition of the cerium conversion coating and corrosion products in Hank's solution were characterized by X-ray photoelectron spectroscopy (XPS) and energy dispersive spectroscopy (EDS), respectively. In addition, the corrosion property in Hank's solution was studied by electrochemical experiment and immersion test. The results show that the dense Ce-based conversion coating is obtained on the surface of AZ31 magnesium alloys in optimal technical parameters and the conversion coating consists of a mass of trivalent and tetravalent cerium oxides. The cerium conversion coating can provide obvious protection of magnesium alloys and can effectively reduce the degradation speed in Hank's solution. Also the degradation products have little influence on human body.     

Adsorption orientation of sodium of polyaspartic acid effect on anodic films formed on magnesium alloy

We previously reported organic addition agent in improving the performance of anodic film formed on magnesium alloy. Here we report that the environment-friendly electrolyte with sodium of polyaspartic acid (PASP) affects the anodizing process including the microstructure, phase constituents and corrosion performance. We have used SEM, XRD, XPS and polarization curve to study in detail the electrolyte impact. Our results show that the anodic film in electrolyte with 19.2-28.8 g/L PASP is compact, smooth and high corrosion resistant. And also, increasing the PASP concentration ranging from 9.6 to 28.8 g/L results in enhancing the cell voltage, thickness and the content of compound including MgO and Mg₂SiO₄ in anodic film. Interestingly, the anodic film is non-stoichiometric oxide. Comparing with Tafel curves of the anodic film to the addition of PASP or not to, the corrosion current density is 1-2 magnitudes less than the later. Furthermore, a plausible model we propose that the anodizing process is regulated by two main plausible adsorption orientations of PASP at the surface anode. With the increasing of PASP content, the adsorption orientation may transit from “end-on” to “flat-on”. This research using organic addition agent PASP may further broaden applications of organic additive in the anti-corrosion engineering and electrochemical surface treatment of magnesium alloy.     

Study of molybdenum/lanthanum-based composite conversion coatings on AZ31 magnesium alloy

The molybdenum/lanthanum-based (Mo/La) composite conversion coating on AZ31 magnesium alloy was investigated and the corrosion resistance was evaluated as well. The morphology, composition and corrosion resistance of the coating were studied by scanning electron microscopy (SEM), X-ray photoelectron spectroscopy (XPS), and potentiodynamic polarization analysis, respectively. The results revealed that the conversion coating consisted of spherical nodular particles, which was mainly composed of Mo, La, O and Mg. After conversion treatment the corrosion potential shifts about 500 mV positively, and the corrosion current density decreases two orders of magnitude. The corrosion resistance of AZ31 alloy is remarkably improved by Mo/La composite conversion coating.     

XPS study of the surface chemistry on AZ31 and AZ91 magnesium alloys in dilute NaCl solution

The surface chemistry on AZ31 and AZ91 magnesium alloys was characterized by X-ray photoelectron spectroscopy (XPS) in the corrosion and the passivation zones. In the corrosion zone, the presence of Mg(OH)₂ and MgCO₃ species was found in the outer surface, whereas, in the inner layer, the co-existence of Mg(OH)₂, MgO and MgCO₃ species was observed for both alloys. The presence of Al³⁺ in the surface electrolyte to form Al₂O₃/Al(OH)₃ and the formation of carbonate product provide a better passivation on the surfaces and retard the chloride-induced corrosion on the materials in the passivation zone.     

Enhanced corrosion resistance of Zr coating on biomedical TiNi alloy prepared by plasma immersion ion implantation and deposition

Zirconium film was prepared on TiNi alloy by plasma immersion ion implantation and deposition (PIIID) technique to enhance its corrosion resistance and prolong its working lifetime. The atomic force microscopy (AFM) results show that the film was relatively smooth with the root mean square roughness being 9.166 nm. The X-ray photoelectron spectroscopy (XPS) and X-ray diffraction (XRD) results indicate that the implant element of Zr was oxidation partialness. The potentiodynamic polarization measurements in the Hank's solution at 37 °C show that the corrosion resistance of the alloy was improved by the Zr coating film and the atomic absorption spectrometry (AAS) tests also indicate that Ni ion concentration released from the substrate in the Hank's solution after the polarization test was reduced greatly, in comparison to the unmodified TiNi alloy sample.     

In vitro corrosion and biocompatibility study of phytic acid modified WE43 magnesium alloy

Phytic acid (PA) conversion coating on WE43 magnesium alloy was prepared by the method of immersion. The influences of phytic acid solution with different pH on the microstructure, properties of the conversion coating and the corrosion resistance were investigated by SEM, FTIR and potentiodynamic polarization method. Furthermore, the biocompatibility of different pH phytic acid solution modified WE43 magnesium alloys was evaluated by MTT and hemolysis test. The results show that PA can enhance the corrosion resistance of WE43 magnesium especially when the pH value of modified solution is 5 and the cytotoxicity of the PA coated WE43 magnesium alloy is much better than that of the bare WE43 magnesium alloy. Moreover, all the hemolysis rates of the PA coated WE43 Mg alloy were lower than 5%, indicating that the modified Mg alloy met the hemolysis standard of biomaterials. Therefore, PA coating is a good candidate to improve the biocompatibility of WE43 magnesium alloy.     

One-step fabrication of oriented Mg/Al-layered double hydroxide film on magnesium substrate with urea hydrolysis and its corrosion resistance

This work presents a simple and direct method for synthesizing Mg/Al-layered double hydroxides (MgAl-LDHs) film on an Mg sheet by in situ hydrothermal crystallization with urea hydrolysis, and protecting the Mg sheet from corrosion. The morphology and structure of the LDHs film were characterized by scanning electron microscopy, X-ray diffraction (XRD), and Fourier transform infrared spectroscopy, respectively. A uniform and compact thin film was formed, of which the LDHs platelets were highly oriented with their ab-face perpendicular to the Mg substrate. XRD pattern and FT-IR spectrum show that MgAl-LDHs film was formed accompanied with Mg(OH)₂. Polarization measurements showed that the LDHs film exhibited a low corrosion current density value of 10^?6?A/cm². The strong adhesion between the film and the substrate was observed by cross-cutting method. These results indicated that the LDHs film can effectively protect Mg sheet from corrosion.     

Synthesis of MgB2 films by diffusion of magnesium into electrophoretically deposited boron films

The boron films were formed from the optimized stable suspension solution of boron particles using electrophoretic deposition technique. The magnesium film with optimized thickness was deposited onto boron films by vacuum evaporation technique. The heterogeneous structure was given heat treatment in ambient and vacuum atmosphere for diffusion of Mg into the boron films to form MgB₂ phase. XRD studies were carried out on both as deposited and heat treated heterostructure films to investigate their structure and phase. Surface morphological studies of these films were done by SEM.     

Growth mechanism of hydroxyapatite-coatings formed on pure magnesium and corrosion behavior of the coated magnesium

Hydroxyapatite (HAp) coatings were uniformly formed on pure Mg by a hydrothermal treatment using a C₁₀H₁₂N₂O₈Na₂Ca (Ca-EDTA) solution. The growth mechanism of the HAp coating was investigated with XRD, SEM and TEM. At the initial stage, dome-shape HAp precipitates were formed on the Mg. Subsequently, the precipitates grew and the coating became a dual-layer consisting of an inner dense HAp layer and outer course layer consisting of rod-like HAp crystals. The protectiveness of the coatings with different treatment times was investigated by a polarization test in a 3.5 wt.% NaCl solution. The corrosion current density decreased with the growth of the HAp coating.     

Effects of magnesium film thickness and annealing temperature on formation of Mg2Si films on silicon (1 1 1) substrate deposited by magnetron sputtering

Magnesium films of various thicknesses were first deposited on silicon (1 1 1) substrates by magnetron sputtering method and then annealed in annealing furnace filled with argon gas. The effects of the magnesium film thickness and the annealing temperature on the formation of Mg₂Si films were investigated by means of X-ray diffraction (XRD) and scanning electron microscopy (SEM). The Mg₂Si thin films thus obtained were found to be polycrystalline and the Mg₂Si (2 2 0) orientation is preferred regardless of the magnesium film thickness and annealing temperature. XRD results indicate that high quality magnesium silicide films are produced if the magnesium/silicon samples are annealed at 400 °C for 5 h. Otherwise, the synthesized films annealed at annealing temperatures lower than 350 °C or higher than 450 °C contain magnesium crystallites or magnesium oxide. SEM images have revealed that microstructure grains in the polycrystalline films are about 1-5 μm in dimensions, and the texture of the Mg₂Si films becomes denser and more homogeneous as the thickness of the magnesium film increases.     

The anodization of ZK60 magnesium alloy in alkaline solution containing silicate and the corrosion properties of the anodized films

The anodization of ZK60 magnesium alloy in an alkaline electrolyte of 100 g/l NaOH + 20 g/l Na₂B₄O₇·10H₂O + 50 g/l C₆H₅Na₃O₇·2H₂O + 60g/l Na₂SiO₃·9H₂O was studied in this paper. The corrosion resistance of the anodic films was studied by electrochemical impedance spectroscopy (EIS) and potentiodynamic polarization techniques and the microstructure and composition of films were examined by SEM and XRD. The influence of anodizing time was studied and the results show that the anodizing time of 60 min is suitable for acquiring films with good corrosion resistance. The influence of current density on the corrosion resistance of anodizing films was also studied and the results show that the film anodized at 20 mA/cm² has the optimum corrosion resistance. The film formed by anodizing in the alkaline solution with optimized parameters show superior corrosion resistance than that formed by the traditional HAE process. The XRD pattern shows that the components of the anodized film consist of MgO and Mg₂SiO₄.     

Surface treatment of magnesium hydroxide to improve its dispersion in organic phase by the ultrasonic technique

Micron magnesium hydroxide [Mg(OH)₂] was modified by means of ultrasonic method with stearic acid (SA) as modifier in water. The Fourier transform infrared spectroscopy (FT-IR) and element analysis showed all SA was bonded upon the surface of the Mg(OH)₂ forming a coating layer and no free SA was detected after the modifying process. The thickness of coating SA on the Mg(OH)₂ was determined by X-ray photoelectron spectroscopy (XPS). Compared with the unmodified Mg(OH)₂, the modified Mg(OH)₂ had better dispersion property in xylene, slower sedimentation velocity of dilute suspension in xylene and lower viscosity of suspension in paraffin liquid. The results showed that the modified Mg(OH)₂ could be dispersed much better than the unmodified Mg(OH)₂ in organic phase.     

Preparation and properties of super-hydrophobic coating on magnesium alloy

The super-hydrophobic coating was successfully fabricated on the surface of magnesium alloy AZ31 by chemical etching and surface modification. The surface morphologies, compositions, wettability and corrosion resistance of the coating were investigated with SEM, XPS, contact angle measurement and electrochemical method, respectively. It shows that the rough and porous micro-nano-structure was presented on the surface of magnesium alloy, and the contact angle could reach up to 157.3 ± 0.5° with sliding angle smaller than 10°. The super-hydrophobic coating showed a long service life. The results of electrochemical measurements showed that anticorrosion property of magnesium alloy was improved. The super-hydrophobic phenomenon of the prepared surface was analyzed with Cassie theory, and it finds that only about 10% of the water surface is contacted with the metal substrate and the rest 90% is contacted with the air cushion.     

Characterization of microarc oxidation coatings formed on AM60B magnesium alloy in silicate and phosphate electrolytes

Microarc oxidation coatings on AM60B magnesium alloy were prepared in silicate and phosphate electrolytes. Structure, composition, mechanical property, tribological, and corrosion resistant characteristics of the coatings was studied by scanning electron microscope (SEM), X-ray diffraction (XRD) and microhardness analyses, and by ball-on-disc friction and potentiodynamic corrosion testing. It is found that the coating produced from the silicate electrolyte is compact and uniform and is mainly composed of MgO and forsterite Mg₂SiO₄ phases, while the one formed in phosphate electrolyte is relatively porous and is mainly composed of MgO phase. The thick coating produced from a silicate electrolyte possesses a high hardness and provides a low wear rate (3.55 × 10⁻⁵ mm³/Nm) but a high friction coefficient against Si₃N₄ ball. A relatively low hardness and friction coefficient while a high wear rate (8.65 × 10⁻⁵ mm³/Nm) is recorded during the testing of the thick coating produced from a phosphate electrolyte. Both of these types of coatings provide effective protection for the corrosion resistance compared with the uncoated magnesium alloy. The coating prepared from the silicate electrolyte demonstrates better corrosion behavior due to the compacter microstructure.     

Broad-beam laser cladding of Al-Cu alloy coating on AZ91HP magnesium alloy

The resistance to wear and corrosion of AZ91HP Mg alloy was improved by laser cladding Al-Cu alloy. It was found that the clad layer was characterized by AlCu₄ and Mg₁₇Al₁₂ grains embedded in a AlMg matrix. The bonding zone exhibited a white-light planar crystal band with thickness of 10-13 μm. The heat-affected zone formed a eutectic structure due to the Mg diffusion. The microhardness and wear resistance of the coating were improved due to the formation of the hard phases AlCu₄ and Mg₁₇Al₁₂. Owing to the formation of dense Al₂O₃ oxide film, the coating exhibited better corrosion resistance in 3.5 wt.% NaCl solution.