Comparative evaluation of performance of percolated perpendicular media using FePt–MgO/Pt/Cr trilayer and FePt–MgO/MgO bilayer

(Fe₄₈Pt₅₂)_100−x–(MgO)_x films were used to examine the performance of a perpendicular percolated medium. Two underlayers, Pt(0 0 1)/Cr(0 0 2) and MgO(0 0 2), were used for comparison. The (Fe₄₈Pt₅₂)_100−x–(MgO)_x film with the MgO underlayer exhibits a strong preference to segregate at FePt grain boundaries. The microstructure with small closely packed MgO particles (2–4 nm) dispersed uniformly in the L1₀ FePt matrix was achieved in the Pt/Cr underlayered sample. Structural data reveal that the precipitate is crystallographically coherent with the surrounding L1₀ FePt phase and preserves good lattice alignment. Magnetic results indicate significant pinning behavior for those introduced non-magnetic columns with an enhanced coercivity of about 70%—much greater than that of the MgO underlayered samples. Percolated perpendicular medium can be realized in the FePt system and a Pt(0 0 1)/Cr(0 0 2) underlayer promotes the formation of pinning sites within the FePt grains.     

Microstructural and magnetic studies of L10 FePt–SiO2 nano-composite thin film with columnar structure for perpendicular magnetic recording

(Fe₅₀Pt₅₀)_100−x-(SiO₂)_x films (x=0–30 vol%) were grown on a textured Pt(0 0 1)/CrRu(0 0 2) bilayer at 420 °C using glass substrates. FePt(0 0 1) preferred orientation was obtained in the films. Interconnected microstructure with an average grain size of about 30 nm is observed in the binary FePt film. As SiO₂ is incorporated, it precipitates as particles are dispersed at FePt grain boundaries. When the content of SiO₂ is increased to 13 vol%, columnar FePt with (0 0 1) texture separated by SiO₂ is attained. The FePt columns have a length/radius ratio of 2:1. Additionally, the mean grain size is reduced to about 13 nm. The development of this well-isolated columnar structure leads to an enhancement in coercivity by about 44% from 210 to 315 kA/m. As the SiO₂ content exceeds 20 vol%, a significant ordering reduction is found accompanied by a transformation of preferred orientation from (0 0 1) to (2 0 0) and the columnar structure disappears, resulting in a drastic degradation in magnetism. The results of our study suggest that isolated columnar, grain refined, (0 0 1)-textured FePt film can be achieved via the fine control of SiO₂ content. This may provide useful information for the design of FePt perpendicular recording media.     

Texture development and magnetic properties of [ZrO2/CoPt]n/Ag nanocomposite films

The L1₀ CoPt films with (0 0 1) preferred orientation are achieved by fabricating on the glass substrates and post annealing at 600° C for 30 min. The preferred orientation of [ZrO₂/CoPt]_n/Ag films dependence of the Ag underlayer thickness, ZrO₂ and CoPt interlayer thickness is investigated. A large perpendicular magnetic anisotropy and a nearly perfect L1₀ CoPt (0 0 1) texture are obtained in the [ZrO₂ (3 nm)/CoPt (5 nm)]₃/Ag (10 nm) film. The existence of ZrO₂ plays an important role in reducing the intergranular interactions and in determining the size of CoPt grains. Magnetic reversal in textured CoPt films are close to a Stoner-Wolfarth rotation.     

High temperature ferromagnetism of the vacuum-annealed (In1−xFex)2O3 powders

(In_1−xFe_x)₂O₃ (x = 0.02, 0.05, 0.2) powders were prepared by a solid state reaction method and a vacuum annealing process. A systematic study was done on the structural and magnetic properties of (In_1−xFe_x)₂O₃ powders as a function of Fe concentration and annealing temperature. The X-ray diffraction and high-resolution transmission electron microscopy results confirmed that there were not any Fe or Fe oxide secondary phases in vacuum-annealed (In_1−xFe_x)₂O₃ samples and the Fe element was incorporated into the indium oxide lattice by substituting the position of indium atoms. The X-ray photoelectron spectroscopy revealed that both Fe²⁺ and Fe³⁺ ions existed in the samples. Magnetic measurements indicated that all samples were ferromagnetic with the magnetic moment of 0.49-1.73 μ_B/Fe and the Curie temperature around 783 K. The appearance of ferromagnetism was attributed to the ferromagnetic coupling of Fe²⁺ and Fe³⁺ ions via an electron trapped in a bridging oxygen vacancy.     

Structural transformations and magnetic properties of Fe60Pt15B25 and Fe60Pt25B15 nanocomposite alloys

Structural and magnetic properties of two rapidly solidified and post-annealed Fe₆₀Pt₁₅B₂₅ and Fe₆₀Pt₂₅B₁₅ alloys are compared. The as-quenched Fe₆₀Pt₁₅B₂₅ ribbon was fully amorphous whereas in the Fe₆₀Pt₂₅B₁₅ alloy the amorphous phase coexists with an fcc FePt disordered solid solution. Differential scanning calorimetry curves of both alloys reveal a single exothermal peak with onset temperatures of 873 and 847 K for Fe₆₀Pt₁₅B₂₅ and Fe₆₀Pt₂₅B₁₅, respectively. Magnetically hard, tetragonal ordered L1₀ FePt and magnetically soft Fe₂B nanocrystalline phases were formed due to the annealing of the alloys, as indicated by X-ray diffraction and Mössbauer spectroscopy measurements. Two-phase behavior was detected in the temperature dependence of magnetization of the annealed samples. A magnetic hardening was observed for all annealed ribbons. Magnetic properties of the annealed alloys, studied by hysteresis loop measurements, were related to the differences in the relative fractions of the hard and soft magnetic phases calculated from Mössbauer spectra. The alloy with 25 at% Pt exhibits better hard magnetic properties (H_c=437 kA/m, M_r/M_s=0.74) than the alloy with smaller Pt content (H_c=270 kA/m, M_r/M_s=0.73) mainly due to the larger abundance of the ordered tetragonal FePt phase.     

Structure and magnetic properties of (Nd,Dy)16(Fe,Co)76−xTixB8 powders prepared by mechanical alloying

Nanocrystalline (Nd,Dy)₁₆(Fe,Co)_76−xTi_xB₈ magnets were prepared by mechanical alloying and respective heat treatment at 973–1073 K/30–60 min. An addition of 0.5 at % of Ti results in an increase of coercivity from 796 to 1115 kA m⁻¹. Partial substitution of Nd by Dy results in an additional increase of coercivity up to 1234 kA m⁻¹. Mössbauer investigations shows that for x?1 the (Nd,Dy)₁₆(Fe,Co)_76−xTi_xB₈ powders are single phase. For higher Ti contents (x>1) the mechanically alloyed powders heat treated at 973 K are no more single phase, and the coercivity decreases due to the presence of an amorphous phase. A heat treatment at a higher temperature (1073 K) for longer time (1 h) results in the full recrystallisation of powders. The mean hyperfine field of the Nd₂Fe₁₄B phase decreases for titanium contents of 0?x?1, and remains constant for x>1. This indicates that the Ti content in the Nd₂Fe₁₄B phase reaches its maximum value.     

Ferromagnetic-to-antiferromagnetic transition in (Hf1−xTix)Fe2 intermetallic compounds induced by geometrical frustration of the Fe(2a) sites

The ferromagnetic-to-antiferromagnetic transition in the hexagonal (Hf_1−xTi_x)Fe₂ (0?x?1) intermetallic compounds has been investigated by ⁵⁷Fe Mössbauer spectroscopy. At 10 K, the transition occurs within rather narrow concentration limits, around x=0.55–0.65. We found that the key factor governing the unexpected quick change of the magnetic structure is the magnetic frustration of the Fe(2a) sites. The magnetic frustration is caused by the noncollinearity of the Fe(6h) magnetic sublattice. The noncollinearity arises from the rotation of the magnetic moments due to the competition between the ferromagnetic exchange interactions and the antiferromagnetic Fe(6h)–Ti–Fe(6h) interaction. In the compounds with x=0.4–0.6, the temperature transitions to the antiferromagnetic state are observed. As an example, the Hf_0.4Ti_0.6Fe₂ compound is completely antiferromagnetic above 200 K.     

Effect of Cr100−xTix (x = 0-19 at.%) alloy underlayers on the high coercivity of FePt thin film below the substrate temperature of 250 °C

The effect of Cr_100−xTi_x underlayer on orderd-L1₀ FePt films was investigated. A low-temperature ordering of FePt films could be attained through changing the Ti content of Cr_100−xTi_x underlayer. The ordering temperature of the 30 nm FePt film grown on 20 nm Cr₉₀Ti₁₀ underlayer was reduced to 250 °C which is practical manufacture process temperature. An in-plane coercivity was very high to 6000 Oe and a ratio of remnant magnetization (M_r) to saturation magnetization (M_s) was as large as 0.85. This result indicates that the coercivity obtained at 250 °C by the effect of CrTi underlayer is significantly higher than those obtained at 250-275 °C by the effect of underlayers in other conventional studies. The prominent improvement of the magnetic properties of ordered FePt thin films at low temperature of 250 °C could be understood with considering the strain-induced ordering phase transformation associated with lattice mismatch between Cr underlayer and FePt magnetic layer due to an addition of Ti content.     

Structural and magnetic properties of sol-gel Co2xNi0.5−x Zn0.5−xFe2O4 thin films

Nanocrystalline Co_2xNi_0.5−xZn_0.5−xFe₂O₄ (x=0−0.5) thin films have been synthesized with various grain sizes by a sol-gel method on polycrystalline silicon substrates. The morphology as well as magnetic and microwave absorption properties of the films calcined at 1073 K were studied using X-ray diffraction, scanning electron microscopy, X-ray photoelectron spectroscopy, and vibrating sample magnetometry. All films were uniform without microcracks. The Co content in the Co-Ni-Zn films resulted in a grain size ranging from 15 to 32 nm while it ranged from 33 to 49 nm in the corresponding powders. Saturation and remnant magnetization increased with increase in grain size, while coercivity demonstrated a drop due to multidomain behavior of crystallites for a given value of x. Saturation magnetization increased and remnant magnetization had a maximum as a function of grain size independent of x. In turn, coercivity increased with x independent of grain size. Complex permittivity of the Co-Ni-Zn ferrite films was measured in the frequency range 2-15 GHz. The highest hysteretic heating rate in the temperature range 315-355 K was observed in CoFe₂O₄. The maximum absorption band shifted from 13 to 11 GHz as cobalt content increased from x=0.1 to 0.2.     

Positive exchange bias in a Ni80Fe20/NixFe1−xO thin-film bilayer

We have measured positive exchange bias in a Ni₈₀Fe₂₀/Ni_xFe_1−xO thin-film nanocrystallite system. A series of solid solution Ni_xFe_1−xO 40 nm thick films capped with 25 nm thick Ni₈₀Fe₂₀ were deposited using a range of %O₂/Ar bombardment energies (i.e. End-Hall voltages). Proper tuning of the deposition conditions results in a Ni₈₀Fe₂₀/Ni_xFe_1−xO (30%O₂/Ar) based bilayer that exhibits a positive exchange bias loop shift of H_ex∼60 Oe at 150 K.