Development of a novel high speed (electron-mobility) epi-n-ZnO thin films by L-MBE for III–V opto-electronic devices

Intrinsic epitaxial zinc oxide (epi-ZnO) thin films were grown by laser-molecular beam epitaxy (L-MBE), i.e., pulsed laser deposition (PLD) technique using Johnson Matthey “specpure”-grade ZnO pellets. The effects of substrate temperatures on ZnO thin film growth, electrical conductivity (σ), mobility (μ) and carrier concentration (n) were studied. As well as the feasibility of developing high quality conducting oxide thin films was also studied simultaneously. The highest conductivity was found for optimized epi-ZnO thin films is σ=0.06×10³ ohm⁻¹ cm⁻¹ (n-type) (which is almost at the edge of semiconductivity range), carrier density n=0.316×10¹⁹ cm⁻³ and mobility μ=98 cm²/V s. The electrical studies further confirmed the semiconductor characteristics of epi-n-ZnO thin films. The relationship between the optical and electrical properties were also graphically enumerated. The electrical parameter values for the films were calculated, graphically enumerated and tabulated. As a novelty point of view, we have concluded that without doping and annealing, we have obtained optimum electrical conductivity with high optical transparency (95%) for as deposited ZnO thin films using PLD. Also, this is the first time that we have applied PLD made ZnO thin films to iso-, hetero-semiconductor–insulator–semiconductor (SIS) type solar cells as transparent conducting oxide (TCO) window layer. We hope that surely these data be helpful either as a scientific or technical basis in the semiconductor processing.     

The effect on the annealing temperature of Li doped ZnO thin film for a film bulk acoustic resonator

We investigated the material and electrical properties of Li doped ZnO thin film (ZLO) with variation of the annealing temperature. In the 500 C sample, ZLO film showed well defined (002) c-axis orientation and a full width half-maximum property of 0.25. The electrical properties of ZLO thin films showed the excellent specific resistance of 1.5×10¹¹ Ω cm. Finally, the frequency characteristics of the ZLO thin film FBAR, according to the annealing temperature, showed improvement of the return loss from 24.48 to 30.02 dB at a resonant frequency of 1.17 GHz.     

Preparation and characterization of ZnO thin films prepared by thermal oxidation of evaporated Zn thin films

In this paper, the experimental results regarding some structural, electrical and optical properties of ZnO thin films prepared by thermal oxidation of metallic Zn thin films are presented.Zn thin films (d=200–400 nm) were deposited by thermal evaporation under vacuum, onto unheated glass substrates, using the quasi-closed volume technique. In order to obtain ZnO films, zinc-coated glass substrates were isochronally heated in air in the 300–660 K temperature range, for thermal oxidation.X-ray diffraction (XRD) studies revealed that the ZnO films obtained present a randomly oriented hexagonal nanocrystalline structure. Depending on the heating temperature of the Zn films, the optical transmittance of the ZnO films in the visible wavelength range varied from 85% to 95%. The optical band gap of the ZnO films was found to be about 3.2 eV. By in situ studying of the temperature dependence of the electrical conductivity during the oxidation process, the value of about 2×10⁻² Ω⁻¹ m⁻¹ was found for the conductivity of completely oxidized ZnO films.     

Atomic layer deposition and characterization of Ga-doped ZnO thin films

Low-resistivity n-type ZnO thin films were grown by atomic layer deposition (ALD) using diethylzinc (DEZ) and H₂O as Zn and O precursors. ZnO thin films were grown on c-plane sapphire (c- Al₂O₃) substrates at 300 C. For undoped ZnO thin films, it was found that the intensity of ZnO () reflection peak increased and the electron concentration increased from 6.8×10¹⁸ to 1.1×10²⁰ cm⁻³ with the increase of DEZ flow rate, which indicates the increase of O vacancies () and/or Zn interstitials (Zn_i). Ga-doping was performed under Zn-rich growth conditions using triethylgallium (TEG) as Ga precursor. The resistivity of 8.0×10⁻⁴ Ω cm was achieved at the TEG flow rate of 0.24 μmol/min.     

Effect of excimer laser annealing on the properties of ZnO thin film prepared by sol-gel method

Pristine ZnO thin films have been deposited with zinc acetate [Zn(CH₃COO)₂], mono-ethanolamine (stabilizer), and isopropanol solutions by sol-gel method. After deposition, pristine ZnO thin films have been irradiated by excimer laser (λ = 248, KrF) source with energy density of 50 mJ/cm² for 30 sec. The effect of excimer laser annealing on the optical and structural properties of ZnO thin films are investigated by photoluminescence and field emission scanning electron microscope. As-grown ZnO thin films show a huge peak of visible region and a wide full width at half maximum (FWHM) of UV region due to low quality with amorphous ZnO thin films. After KrF excimer laser annealing, ZnO thin films show intense near-band-edge (NBE) emission and weak deep-level emission. The optically improved pristine ZnO thin films have demonstrated that excimer laser annealing is novel treatment process at room temperature.     

Characteristics of ZnO:In thin films prepared by RF magnetron sputtering

In-doped ZnO (ZnO:In) transparent conductive thin films were deposited on glass substrates by RF magnetron sputtering. The effect of substrate temperature on the structural, electrical and optical properties of the ZnO:In thin films was investigated. It was found that higher temperature improves the crystallinity of the films and promotes In substitution easily. ZnO:In thin films with the best crystal quality were fabricated at 300 °C, which exhibit a larger grain size of 29 nm and small tensile strain of 0.9%. The transmittance of all the films was revealed to be over 85% in the visible range independence of the substrate temperatures and the lowest resistivity of ZnO:In thin films is 2.4×10⁻³ Ω cm.     

Epitaxial growth of highly transparent and conducting Sc-doped ZnO films on c-plane sapphire by sol–gel process without buffer

Highly transparent and conductive scandium doped zinc oxide (ZnO:Sc) films were deposited on c-plane sapphire substrates by sol–gel technique using zinc acetate dihydrate [Zn(CH₃COO)₂·2H₂O] as precursor, 2-methoxyethanol as solvent and monoethanolamine as a stabilizer. The doping with scandium is achieved by adding 0.5 wt% of scandium nitrate hexahydrate [(ScNO₃·6H₂O)] in the solution. The influence of annealing temperature (300–550 °C) on the structural, optical and electrical properties was investigated. X-ray Diffraction study revealed that highly c-axis oriented films with full-width half maximum of 0.16° are obtained at an annealing temperature of 400 °C. The surface morphology of the films was judged by SEM and AFM images which indicated formation of grains. The average transmittance was found to be above 92% in the visible region. ZnO:Sc film, annealed at 400 °C exhibited minimum resistivity of 1.91 × 10⁻⁴ Ω cm. Room-temperature photoluminescence measurements of the ZnO:Sc films annealed at 400 °C showed ultraviolet peak at 3.31eV with a FWHM of 11.2 meV, which are comparable to those found in high-quality ZnO films. Reflection high-energy electron diffraction pattern confirmed the epitaxial nature of the films even without introducing any buffer layer.     

Structural and optical characterisation of InN layers grown by MOCVD

In the following, we report investigations of the dependencies of the structural, optical and electrical characteristics of InN thin films grown by MOCVD on the growth temperature. The layer thicknesses range from 70 to 400 nm. Their carrier concentrations range from 7×10¹⁸ to 4×10¹⁹ cm⁻³. Hall mobility values from 150 to 1300 cm²/V/s were determined in these films. The variation of the growth temperature and V/III ratio brought about different growth modes and rates. Using TEM, in addition to measuring layer thickness, we also determined the growth mode along with the structural quality of the InN layers. The surface roughness was obtained from AFM measurements. The layer crystalline quality was also investigated by means of X-ray diffraction in the rocking mode. Photoluminescence measurements performed at room temperature and at 7 K gave emission at around 0.7 eV.     

The effects of thermal annealing in NH3 -ambient on the p-type ZnO films

Thermal annealing in NH₃-ambient was carried out to form p-type ZnO films. The properties were examined by X-ray diffraction (XRD), Hall-effect measurement, photoluminescence (PL), and secondary ion mass spectrometry (SIMS). Electron concentrations in ZnO films were in the range of 10¹⁵–10¹⁷/cm³ with thermal annealing in NH₃-ambient. The activation thermal annealing process was needed at 800 C under N₂-ambient to obtain p-type ZnO. The electrical properties of the p-type ZnO showed a hole concentration of 1.06×10¹⁶/cm³, a mobility of 15.8 cm²/V s, and a resistivity of 40.18 Ω cm. The N-doped ZnO films showed a strong photoluminescence peak at 3.306 eV at 13 K, which is closely related to neutral acceptor bound excitons of the p-type ZnO. The incorporation of nitrogen was confirmed in the SIMS spectra.     

Non-vacuum, single-step conductive transparent ZnO patterning by ultra-short pulsed laser annealing of solution-deposited nanoparticles

A solution-processable, high-concentration transparent ZnO nanoparticle (NP) solution was successfully synthesized in a new process. A highly transparent ZnO thin film was fabricated by spin coating without vacuum deposition. Subsequent ultra-short-pulsed laser annealing at room temperature was performed to change the film properties without using a blanket high temperature heating process. Although the as-deposited NP thin film was not electrically conductive, laser annealing imparted a large conductivity increase and furthermore enabled selective annealing to write conductive patterns directly on the NP thin film without a photolithographic process. Conductivity enhancement could be obtained by altering the laser annealing parameters. Parametric studies including the sheet resistance and optical transmittance of the annealed ZnO NP thin film were conducted for various laser powers, scanning speeds and background gas conditions. The lowest resistivity from laser-annealed ZnO thin film was about 4.75×10⁻² Ω cm, exhibiting a factor of 10⁵ higher conductivity than the previously reported furnace-annealed ZnO NP film and is even comparable to that of vacuum-deposited, impurity-doped ZnO films within a factor of 10. The process developed in this work was applied to the fabrication of a thin film transistor (TFT) device that showed enhanced performance compared with furnace-annealed devices. A ZnO TFT performance test revealed that by just changing the laser parameters, the solution-deposited ZnO thin film can also perform as a semiconductor, demonstrating that laser annealing offers tunability of ZnO thin film properties for both transparent conductors and semiconductors.     

Effect of different annealing temperature on Sb-doped ZnO thin films prepared by pulsed laser deposition on sapphire substrates

Influence of annealing temperature on the properties of Sb-doped ZnO thin films were studied. Hall measurement results indicated that the Sb-doped ZnO annealed at 950 °C was p-type conductivity. X-ray diffraction (XRD) results indicated that the Sb-doped ZnO thin films prepared at the experiments are high c-axis oriented. It was worth noting that p-type sample had the worst crystallinity. The measurements of low-temperature photoluminescence (PL) spectra indicate that the sample annealed at the temperatures of 950 °C showed strong acceptor-bound exciton (A⁰X) emission, and confirmed that it is related to Sb-doping by comparing with the undoped ZnO low-temperature PL spectrum.     

The Effects of Thermal Treatments on Microstructure Phosphorus-Doped ZnO Layers Grown by Thermal Evaporation

The ZnO films doped with 3 wt% phosphorus (P) were produced by activating phosphorus doped ZnO (ZnO:P) thin films in oxygen (O₂) ambient at 600°C for 30, 60, 90 and 120 min, respectively. As-deposited films doped with phosphorus are highly conductive and n type. All the films showed p-type conduction after annealing, in an O₂ ambient atmosphere. The activation energies of the phosphorus dopant in the p-type ZnO under O₂ ambient gases indicate that phosphorus substitution on the O site yielded a deep level in the gap. With a further increase of the annealed durations, the crystalline quality of the ZnO:P sample is degraded. The best p-type ZnO:P film deposited at 600°C for 30 min shows a resistivity of 1.85 Ω cm and a relatively high hole concentration of 5.1 × 10¹⁷cm^–3 at room temperature. The films exhibit a polycrystalline hexagonal wurtzite structure without preferred orientation. The mean grain sizes are calculated to be about 60, 72, 78, 85 and 90 nm for the p-type ZnO films prepared at 600°C for 30, 60, 90 and 120 min, respectively. Room temperature photoluminescence (PL) spectra of the ZnO film exhibit two emission bands — paramount excitonic ultraviolet (UV) emission and weak deep level visible emission. The excellent emission from the film annealed at 600°C for 30 min is attributed to the good crystalline quality of the p-type ZnO film and the low rate of formation of intrinsic defects at such short duration. The visible emission consists of two components in the green range.     

Characterization of nitrogen-doped ZnO thin films grown by plasma-assisted pulsed laser deposition on sapphire substrates

The crystalline, optical and electrical properties of N-doped ZnO thin films were measured using X-ray diffraction, photoluminescence and Hall effect apparatus, respectively. The samples were grown using pulsed laser deposition on sapphire substrates coated priorly with ZnO buffer layers. For the purpose of acceptor doping, an electron cyclotron resonance (ECR) plasma source operated as a low-energy ion source was used for nitrogen incorporation in the samples. The X-ray diffraction analyses indicated some deterioration of the ZnO thin film with nitrogen incorporation. Temperature-dependent Van der Pauw measurements showed consistent p-type behavior over the measured temperature range of 200–450 K, with typical room temperature hole concentrations and mobilities of 5×10¹⁵ cm⁻³ and 7 cm²/V s, respectively. Low temperature photoluminescence spectra consisted of a broad emission band centered around 3.2 eV. This emission is characterized by the absence of the green deep-defect band and the presence of a band around 3.32 eV.     

Low resistance nonalloyed Al-based ohmic contacts on n-ZnO:Al

We have investigated the electrical properties of nonalloyed Al, Al/Au, and Al/Pt ohmic contacts on n-type ZnO:Al (2×10¹⁸ cm⁻³). All Al-based nonalloyed ohmic contacts on the n-ZnO:Al reveal linear current–voltage behavior with low specific contact resistivity of 8.5×10⁻⁴ (Al), 8.0×10⁻⁵ (Al/Au) and 1.2×10⁻⁵ Ω cm² (Al/Pt), respectively. Using secondary ion mass spectroscopy (SIMS) and x-ray photoelectron spectroscopy (XPS) depth profiles, it was found that the O atoms in the ZnO:Al layer outdiffused to Al metal layer while the Al atoms indiffused to the surface region of ZnO:Al. This interdiffusion between Al and O atoms at room temperature results in an increase of doping concentration in the surface region of the ZnO:Al and reduces a specific contact resistivity of the Al-based ohmic contacts without thermal annealing process.     

Effect of annealing in N2 atmosphere on net acceptor concentration in ZnSe:N grown by MOCVD

Annealing effect on net acceptor concentration in ZnSe:N is investigated. ZnSe:N homo-epitaxial layer was grown at 823 K by MOCVD using ammonia (NH₃) as a dopant source. Photoluminescence (PL) spectra measured on as-grown layer exhibited the strong deep donor–acceptor pair (D^dAP) emission and the weak I₁^N emission line. In order to enhance the activation of nitrogen in ZnSe epitaxial layer, sample was annealed at the 823 K in nitrogen (N₂) and hydrogen (H₂) atmosphere. Only the annealing in nitrogen atmosphere increased I₁^N emission intensity indicate the activation of nitrogen acceptor. And net acceptor concentration was estimated to be 3 × 10¹⁷cm⁻³ by C–V measurements. This activation mechanism is interpreted as hydrogen is released from N–H bonds during annealing in nitrogen atmosphere.     

Dependences of structural and electrical properties on thickness of polycrystalline Ga-doped ZnO thin films prepared by reactive plasma deposition

Polycrystalline Ga-doped (Ga content: 4 wt%) ZnO (GZO) thin films were deposited on glass substrates at 200 C by a reactive plasma deposition with DC arc discharge technique. The dependences of structural and electrical properties of GZO films on thickness, ranging from 30 to 560 nm, were investigated. Carrier concentration, n, and Hall mobility, μ, increases with increasing film thickness below 100 nm, and then the n remains nearly constant and the μ gradually increases until the thickness reaches 560 nm. The resistivity obtained of the order of 10⁻⁴ Ω cm for these films decreases with increasing film thickness: The highest resistivity achieved is 4.4×10⁻⁴ Ω cm with n of 7.6×10²⁰ cm⁻³ and μ of 18.5 cm²/V s for GZO films with a thickness of 30 nm and the lowest one is 1.8×10⁻⁴ Ω cm with n of 1.1×10²¹ cm⁻³ and μ of 31.7 cm²/V s for the GZO film with a thickness of 560 nm. X-ray diffraction pattern for all the films shows a hexagonal wurtzite structure with its strongly preferred orientation along the c-axis. Full width at half maximum of the (002) preferred orientation diffraction peak of the films decreases with increasing film thickness below 100 nm.     

Conductivity increase of ZnO:Ga films by rapid thermal annealing

Due to a constant increase in demands for transparent electronic devices the search for alternative transparent conducting oxides (TCO) is a major field of research now. New materials should be low-cost and have comparable or better optical and electrical characteristics in comparison to ITO. The use of n-type ZnO was proposed many years ago, but until now the best n-type dopant and its optimal concentration is still under discussion. Ga was proposed as the best dopant for ZnO due to similar atomic radius of Ga³⁺ compared to Zn²⁺ and its lower reactivity with oxygen. The resistivity ρ of ZnO:Ga/Si (100) films grown by PEMOCVD was found to be 3×10⁻² Ω cm. Rapid thermal annealing (RTA) was applied to increase the conductivity of ZnO:Ga (1 wt%) films and the optimal regime was determined to be 800  C in oxygen media for 35 s. The resistivity ratio before and after the annealing and the corresponding surface morphologies were investigated. The resistivity reduction () was observed after annealing at optimal regime and the final film resistivity was approximately ≈4×10⁻⁴ Ω cm, due to effective Ga dopant activation. The route mean square roughness (R_q) of the films was found to decrease with increasing annealing time and the grain size has been found to increase slightly for all annealed samples. These results allow us to prove that highly conductive ZnO films can be obtained by simple post-growth RTA in oxygen using only 1% of Ga precursor in the precursor mix.     

Room temperature soft chemical route for nanofibrous wurtzite ZnO thin film synthesis

Room temperature soft chemical deposition route has been utilized to grow thin films of ZnO on glass substrate. Annealing at 673 K removed zinc hydroxide phase and nanofibrous ZnO films with wurtzite crystal structure were obtained. Decrease in the room temperature electrical resistivity from 10⁷ to 10⁴ Ω cm was observed after annealing. The nanofibrous ZnO thin films were sensitive to the explosive liquefied petroleum gas (LPG) and the maximum response of 17% at 698 K under the exposure of 6500 ppm of LPG was obtained.     

Structure and properties of ZnO films grown on Si substrates with low temperature buffer layers

Zinc oxide (ZnO) thin films were grown on Si (1 0 0) substrates by pulsed laser deposition (PLD) using two-step epitaxial growth method. Low temperature buffer layer (LTBL) was initially deposited in order to obtain high quality ZnO thin film; the as-deposited films were then annealed in air at 700 °C. The effects of LTBL and annealing treatment on the structural and luminescent properties of ZnO thin film were investigated. It was found that tensile strain was remarkably relaxed by employing LTBL and the band-gap redshifted, correspondingly. The shift value was larger than that calculated from band-gap theories. After annealing treatment, it was found that the annealing temperature with 700 °C has little influence on strains of ZnO films with LTBLs other than directly deposited film in our experiments. Interestingly, the different behaviors in terms of the shift of ultraviolet (UV) emission after annealing between films with and without buffer were observed, and a tentative explanation was given in this paper.     

Effect of annealing temperature and annealing atmosphere on the structure and optical properties of ZnO thin films on sapphire (0 0 0 1) substrates by magnetron sputtering

ZnO thin films were epitaxially grown on sapphire (0 0 0 1) substrates by radio frequency magnetron sputtering. ZnO thin films were then annealed at different temperatures in air and in various atmospheres at 800 °C, respectively. The effect of the annealing temperature and annealing atmosphere on the structure and optical properties of ZnO thin films are investigated by X-ray diffraction (XRD), atomic force microscopy (AFM), photoluminescence (PL). A strong (0 0 2) diffraction peak of all ZnO thin films shows a polycrystalline hexagonal wurtzite structure and high preferential c-axis orientation. XRD and AFM results reveal that the better structural quality, relatively smaller tensile stress, smooth, uniform of ZnO thin films were obtained when annealed at 800 °C in N₂. Room temperature PL spectrum can be divided into the UV emission and the Visible broad band emission. The UV emission can be attributed to the near band edge emission (NBE) and the Visible broad band emission can be ascribed to the deep level emissions (DLE). By analyzing our experimental results, we recommend that the deep-level emission correspond to oxygen vacancy (V_O) and interstitial oxygen (O_i). The biggest ratio of the PL intensity of UV emission to that of visible emission (I_NBE/I_DLE) is observed from ZnO thin films annealed at 800 °C in N₂. Therefore, we suggest that annealing temperature of 800 °C and annealing atmosphere of N₂ are the most suitable annealing conditions for obtaining high quality ZnO thin films with good luminescence performance.