SiC过渡层对氟化类金刚石薄膜附着特性的影响

采用射频反应磁控溅射法在316L不锈钢基片上分别沉积了两种薄膜:一种是氟化类金刚石薄膜(F-DLC),另一种是先镀上一定厚度的SiC过渡层再沉积F-DLC.着重研究了薄膜的附着力随过渡层制备条件的变化规律.结果显示,增加SiC过渡层后薄膜的附着力明显增加,且附着力随SiC过渡层的制备条件有所变化,在射频输入功率为200 W,沉积时间5min制备出的SiC过渡层上再沉积F-DLC时,附着力可达8.7 N,远高于未加过渡层时F-DLC膜的附着力(4 N).通过研究SiC的沉积速率曲线、表面形貌和红外光谱,探讨了SiC过渡层及其制备条件影响薄膜附着力的相关机制.     

射频反应磁控溅射法制备的氟化类金刚石薄膜摩擦特性研究

以高纯石墨做靶,CHF3和Ar气为源气体,采用射频反应磁控溅射法在不同流量比条件下制备了氟化类金刚石(F-DLC)薄膜.利用原子力显微镜、纳米压痕仪、拉曼光谱和红外光谱、摩擦磨损测试仪对薄膜的表面形貌、硬度、键结构以及摩擦性能做了具体分析.表面形貌测试结果表明,制备的薄膜整体均匀致密,表现出了良好的减摩性能.当CHF3与Ar气流量比r为1:6时,所得薄膜的摩擦系数减小至0.42,而纳米压痕结果显示,此时薄膜的硬度也最高.拉曼和红外光谱显示,随着r的增加,薄膜中的F浓度呈上升趋势,薄膜中的芳香环比例减小.研究表明,F原子的键入方式是影响F-DLC薄膜摩擦系数的一个重要因素,CF2反对称伸缩振动强度的减弱和CC中适量碳氢氟键的形成都能导致薄膜具有相对较低的摩擦系数.     

源气体流量比对氟化类金刚石薄膜蛋白吸附能力的影响

用316L不锈钢(SU316L)作基片,以高纯石墨作靶、CHF₃和Ar作源气体,采用反应磁控溅射法在不同流量比R (CHF₃／Ar)下制备了氟化类金刚石(F-DLC)薄膜. 利用双蒸水液滴法、BCA(二喹啉甲酸)法和傅里叶红外光谱(FTIR)探讨了影响薄膜蛋白吸附能力的因素. 结果表明,镀有F-DLC薄膜的SU316L表面的血小板黏附量明显减少,血小板的变形程度显著减轻,相应的白蛋白与纤维蛋白原的吸附比普遍高于未镀膜的SU316L表面的相应值,说明镀上F-DLC薄膜可以改善样品的血液相容性. 流量比为2 ∶1左右时制备出的F-DLC薄膜,其白蛋白与纤维蛋白原的吸附比值达到最大,相应的血液相容性最佳. 对薄膜的接触角和表面能以及FTIR光谱分析研究表明,SU316L表面的F-DLC薄膜的白蛋白与纤维蛋白原的吸附比及血液相容性与薄膜的中的-CF_x键的含量(F/C比)和表面能(疏水性)直接相关,控制源气体流量比可以实现对薄膜的血液相容性的调制. 关键词： 反应磁控溅射 氟化类金刚石薄膜 蛋白吸附     

Cu/TiOx复合薄膜的电子态分析及其对亲水性的影响

在室温下,采用射频磁控溅射法制备了Cu/TiO_x纳米晶复合薄膜.利用X射线粉末衍射（XRD）、X射线光电子能谱（XPS）对其结构进行表征,并研究了Cu/TiO_x复合薄膜的UV-vis吸收谱和亲水性.结果表明,退火前后薄膜中钛元素皆以Ti³⁺形式存在.薄膜在可见区有吸收,吸收限为600 nm左右.Cu/TiO_x复合薄膜具有良好的亲水性.这主要是由于Cu的掺杂,使得薄膜的性能的亲水性变好. 关键词： x复合薄膜')" href="#">Cu/TiO_x复合薄膜 射频磁控溅射 XPS 亲水性     

反应磁控溅射法制备的氟化类金刚石薄膜的XPS结构研究

采用射频反应磁控溅射法用高纯石墨作靶、三氟甲烷(CHF₃)和氩气(Ar)作源气体制 备了氟化类金刚石（FDLC）薄膜，通过XPS光谱结合拉曼光谱、红外透射光谱和紫外 可见光光谱研究了源气体流量比等工艺条件对薄膜中键结构、sp2/sp3杂化比以及光学带隙等性能的影响.结果表明在低功率(60W)、高气压(2.0Pa)和适当的流量比(Ar/CHF₃=2∶ 1)下利用射频反应磁控溅射法可制备出氟含量高且具有较宽光学带隙和超低介电常数的FDLC薄膜. 关键词： 反应磁控溅射 氟化类金刚石薄膜 红外透射光谱 XPS光谱     

氮气流量对磁控溅射制备类金刚石薄膜性能的影响

采用磁控溅射法以石墨为靶材在玻璃衬底上沉积了类金刚石(DLC)薄膜,用原子力显微镜表征了不同氮气流量条件下生长薄膜的形貌,用拉曼光谱仪、X射线光电子能谱仪和分光光度计分析了样品的微结构、元素的价态和透光性能.结果表明:沉积的薄膜均为非晶结构.通入2sccm氮气时,薄膜的光学透过率大大提高,此时DLC薄膜内的氮元素含量为5.88%,sp3键百分比为64.65%,ID/IG值为1.81;掺氮DLC薄膜在可见光范围内光学透过率达到95.69%.随着氮气流量增加,DLC薄膜光学透过率呈现出下降的趋势.退火2h后不掺氮DLC薄膜光学透过率呈小幅度下降,而掺氮DLC薄膜的光学透过率几乎没有变化.     

氟化类金刚石薄膜的拉曼和红外光谱结构研究

关键词：     

W过渡层结合界面对金刚石薄膜在WC-6%Co上的附着力的影响

 在微波等离子体化学气相沉积装置中,采用负偏压形核等方法,研究两种不同的W过渡层/基体结合界面对金刚石薄膜与WC-6%Co附着力的影响。采用氢等离子体脱碳、磁控溅射镀W、高偏压碳化等方法,在YG6衬底表面形成化学反应型界面,W膜在碳化时和基体WC连为一体,极大地增加了W膜与基体的附着力,明显优于直接镀钨、碳化形成的物理吸附界面。在高负偏压下碳化,能提高表面粗糙度,增加膜与基体机械钳合,而负偏压形核增加核密度,从而增加膜与基体的接触面积,结果极大地提高了金刚石薄膜的附着力。     

Au/SiO2纳米多层薄膜的制备及其性质表征

利用多靶磁控溅射技术制备了Au/SiO2纳米颗粒分散氧化物多层复合薄膜.研究了在保持Au单层颗粒膜沉积时间一定时薄膜厚度一定、变化SiO2的沉积时间及SiO2的沉积时间一定而改变薄膜厚度时,多层薄膜在薄膜厚度方向的微观结构对吸收光谱的影响.研究结果表明:具有纳米层状结构的Au/SiO2多层薄膜在560nm波长附近有明显的表面等离子共振吸收峰,吸收峰的强度随Au颗粒的浓度增加而增强,在Au颗粒浓度相同的情况下,复合薄膜光学吸收强度随薄膜厚度的增加而增强.但当金属颗粒的浓度增加到一定程度时,金属颗粒相互接触,没有观察到纳米层状结构,薄膜不显示共振吸收峰特征.用修正后的M-G(Maxwell-Garnett)理论对吸收光谱进行了模拟,得到了与实验一致的结果.     

Au/SiO2纳米多层薄膜的制备及其性质表征

利用多靶磁控溅射技术制备了Au/SiO₂纳米颗粒分散氧化物多层复合薄膜.研究了在保持Au单层颗粒膜沉积时间一定时薄膜厚度一定、变化SiO₂的沉积时间及SiO₂的沉积时间一定而改变薄膜厚度时，多层薄膜在薄膜厚度方向的微观结构对吸收光谱的影响.研究结果表明：具有纳米层状结构的Au/SiO₂多层薄膜在560 nm波长附近有明显的表面等离子共振吸收峰，吸收峰的强度随Au颗粒的浓度增加而增强，在Au颗粒浓度相同的情况下，复合薄膜 关键词： 2纳米复合薄膜')" href="#">Au/SiO₂纳米复合薄膜 多靶磁控溅射 吸收光谱 有效介质理论     

Al和Sb共掺对ZnO有序阵列薄膜的结构和光学性能的影响

采用水热合成法在预先生长的ZnO种子层的玻璃衬底上制备出Al和Sb共掺ZnO纳米棒有序阵列薄膜. 通过X射线衍射、扫描电镜、透射电镜和选区电子衍射分析表明:所制备的薄膜由垂直于ZnO种子层的纳米棒组成, 呈单晶六角纤锌矿ZnO结构, 且沿[001]方向择优生长, 纳米棒的平均直径和长度分别为27.8 nm和1.02 μm. Al和Sb共掺ZnO纳米棒有序阵列薄膜的拉曼散射分析表明:相对于未掺杂ZnO薄膜的拉曼振动峰(580 cm^-1), Al和Sb共掺ZnO阵列薄膜的E₁(LO)振动模式存在拉曼位移. 当Al和Sb的掺杂量为3.0at%,4.0at%,5.0at%,6.0at%时, Al和Sb共掺ZnO阵列薄膜的拉曼振动峰的位移量分别为3,10,14,12 cm^-1. E₁ (LO) 振动模式位移是由Al和Sb掺杂ZnO产生的缺陷引起的. 室温光致发光结果表明:掺杂Al和Sb后, ZnO薄膜在545 nm处的发光强度减小,在414 nm处的发光强度增加. 这是由于掺杂Al和Sb后, ZnO薄膜中Zn_i缺陷增加, O_i缺陷减少引起的. 关键词： Al和Sb共掺ZnO薄膜 纳米棒有序阵列 结构表征 拉曼散射     

Structural and electrical characterization of annealed Si1-xCx/SiC thin film prepared by magnetron sputtering

Si-rich Sil-xCx/SiC multilayer thin films are prepared using magnetron sputtering, subsequently followed by thermal annealing in the range of 800-1200 ℃. The influences of annealing temperature （Ta） on the formation of Si and/or SiC nanocrystals （NCs） and on the electrical characteristics of the multilayer film are investigated by using a variety of analytical techniques, including X-ray diffraction （XRD）, Raman spectroscopy and Fourier transform infrared spectrometry （FT-IR）, current-voltage （I-V） technique, and capacitance-voltage （C-V） technique. XRD and Raman analyses indicate that Si NCs begin to form in samples for Ta _ 800 ~C. At annealing temperatures of 1000 ℃ or higher, the formation of Si NCs is accompanied by the formation of SiC NCs. With the increase in the annealing temperature, the shift of FT-IR Si-C bond absorption spectra toward a higher wave number along with the change of band shape can be explained by a Si-C transitional phase between the loss of substitutional carbon and the formation of SiC precipitates and a precursor for the growth of SiC crystalline. The C-V and I-V results indicate that the interface quality of Si1-xCx/SiC multilayer film is improved significantly and the leakage current is reduced rapidly for Ta ≥ 1000 ℃, which can be ascribed to the formation of Si and SiC NCs.     

Comparison of fibre/matrix interface strength for a 3D woven SiC/SiC composite

The fibre/matrix interface shear strength, τ _P, was determined by analysis of fibre pullout length distributions for a 3D woven SiC/SiC-based composite that had undergone tensile testing between room temperature and 1300°C in vacuum and air. Data was compared with the fibre/matrix interface shear strength, τ _S, obtained previously for this system by analysis of in situ fibre strength distributions. τ _P was found to follow the same general trend as that of τ _S and this was explained in terms of the carbon-rich fibre/matrix interface region. However, τ _P was smaller than τ _S by a factor of 3-4 for all cases, but the reason for this remains unclear although several tentative suggestions have been put forward.     

磁控溅射方法制备垂直取向FePt/BN颗粒膜

用磁控溅射在热单晶MgO(100)基片上制备了［FePt/BN］多层膜，经真空热处理后，得到具有垂直取向L1₀-FePt/BN颗粒膜.X射线衍射结果和磁性测量的结果表明，［FePt(2nm)/BN(0.5nm)］₁₀和［FePt(1nm)/BN(0.25nm)］₂₀多层膜经700℃热处理1h后，均具有较好的(001)取向.［FePt(1nm)/BN(0.25nm)］₂₀垂直矫顽力达到522kA/m，剩磁比达到0.99，开关场分布S达到0.94，FePt晶粒平均尺寸约15—20nm，适合用于将来超高密度的垂直磁记录介质. 关键词： 磁控溅射 垂直磁记录 0-FePt/BN纳米颗粒膜')" href="#">L1₀-FePt/BN纳米颗粒膜     

Effects of substrate temperature on the efficiency of hydrogen incorporation on the properties of Al-doped ZnO films

Al-doped ZnO (AZO) transparent conducting films were successfully prepared on glass substrates by RF magnetron sputtering at different substrate temperatures in Ar and H₂ + Ar sputtering ambient. The effects of substrate temperature on the effectiveness of hydrogen incorporation in Al-doped ZnO films were investigated. The microstructural, electrical and optical properties of AZO films were systematically analyzed by surface profiler, X-ray diffractometry, scanning electron microscope, four-point probe measurement and UV/vis spectrophotometer. The XRD patterns and SEM pictures indicate that the crystallinity of AZO thin films was markedly improved with hydrogen incorporation at low substrate temperature, while the improvement of crystallinity was not an obvious change at high substrate temperature. The results also indicate that hydrogen incorporation has the stronger effectiveness on the transparent conductive properties of AZO films with the substrate temperature decreasing. The resistivity of the films decreases, especially for lower substrate temperatures, due to the incorporation of hydrogen atoms. These results suggest that substrate temperature should be controlled to the lower level to effectively reduce resistivity without detriment to transmittance of AZO thin films when hydrogen is incorporated.     

退火温度对ZnO薄膜结构和发光特性的影响

采用反应射频磁控溅射法在 Si(100)基片上制备了高c轴择优取向的ZnO薄膜，研究了退火温度对ZnO薄膜的晶粒尺度、应力状态、成分和发光光谱的影响，探讨了ZnO薄膜的紫外发光光谱和可见发光光谱与薄膜的微观状态之间的关系.研究结果显示,在600—1000℃退火温度范围内，退火对薄膜的织构取向的影响较小，但薄膜的应力状态和成分有比较明显的变化.室温下光致发光光谱分析发现，薄膜的近紫外光谱特征与薄膜的晶粒尺度和缺陷状态之间存在着明显的对应关系；而近紫外光谱随退火温度升高所呈现的整体峰位红移是各激子峰相对比例变 关键词： ZnO薄膜 退火 光致发光 射频反应磁控溅射 可见光发射     

Characterization of a SiC/SiC composite by X-ray diffraction, atomic force microscopy and positron spectroscopies

A SiC/SiC composite is characterized by X-ray diffraction, atomic force microscopy and various positron spectroscopies (slow positron implantation, positron lifetime and re-emission). It is found that besides its main constituent 3C-SiC the composite still must contain some graphite. In order to better interpret the experimental findings of the composite, a pyrolytic graphite sample was also investigated by slow positron implantation and positron lifetime spectroscopies. In addition, theoretical calculations of positron properties of graphite are presented.     

Application of indium tin oxide (ITO) thin film as a low emissivity film on Ni-based alloy at high temperature

Indium tin oxide (ITO) films as the low emissivity coatings of Ni-based alloy at high temperature were studies. ITO films were deposited on the polished surface of alloy K424 by direct current magnetron sputtering. These ITO-coated samples were heat-treated in air at 600–900 °C for 150 h to explore the effect of high temperature environment on the emissivity. The samples were analyzed by X-ray diffraction (XRD), SEM and EDS. The results show that the surface of sample is integrity after heat processing at 700 °C and below it. A small amount of fine crack is observed on the surface of sample heated at 800 °C and Ti oxide appears. There are lots of fine cracks on the sample annealed at 900 °C and a large number of various oxides are detected. The average infrared emissivities at 3–5 μm and 8–14 μm wavebands were tested by an infrared emissivity measurement instrument. The results show the emissivity of the sample after annealed at 600 and 700 °C is still kept at a low value as the sample before annealed. The ITO film can be used as a low emissivity coating of super alloy K424 up to 700 °C.