LiNi1/3Co1/3Mn1/3O2 cathode materials for LIB prepared by spray pyrolysis I: the spectral, structural, and electro-chemical properties

Layered lithium ion battery cathode material LiNi_1/3Co_1/3Mn_1/3O₂ with uniform particle size of about 6 μm was synthesized by a spray pyrolysis method. Infrared and X-ray diffraction analyses show that the pyrolysis at 1,000 °C for 2 s in the tube furnace eliminates nearly all the organic components but is still not enough for the complete crystallization of LiNi_1/3Co_1/3Mn_1/3O₂ materials. Therefore, further annealing at 850 °C is needed. The prepared LiNi_1/3Co_1/3Mn_1/3O₂ cathode materials show excellent electrochemical performances. By increasing the C-rates, the cell shows discharge capacities of 159.3, 148.2, 133.7, and 125.7 mAh g^?1 at 0.1, 0.2, 0.5, and 1C rates, respectively. Only 2.1 mAh g^?1 capacity loss is observed when back to 0.1C rate. Moreover, LiNi_1/3Co_1/3Mn_1/3O₂ cathode retains 96, 97.7, 97.1, 94.5, and 97.1 % of its initial discharge capacities after 20 cycles at 0.1, 0.2, 0.5, 1, and back to 0.1C rates, respectively. More than 97 % coulombic efficiencies are observed at all the current densities in 20 cycles.     

Structural and electrochemical properties of LiNi1/3Co1/3Mn1/3O2 material prepared by a two-step synthesis via oxalate precursor

LiNi_1/3Co_1/3Mn_1/3O₂ (LNMCO) powders were formed by a two-step synthesis including preparation of an oxalate precursor by ??chimie douce?? followed by a solid-state reaction with lithium hydroxide. The product was characterized by TG-DTA, X-ray diffraction (XRD), scanning electron microscopy (SEM), transmission electron microscopy (TEM), Fourier transform infrared (FTIR), Raman spectroscopy, electron spin resonance (ESR), and SQUID magnetometry. XRD data revealed well-crystallized layered LNMCO with ??-NaFeO₂-type structure (R-3?m space group). Morphology studied by SEM and TEM shows submicronic particles of 400?C800?nm with a tendency to agglomerate. The local structure investigated by vibrational spectroscopy (FTIR, Raman), ESR, and SQUID measurements confirms the well-crystallized lattice with a cation disorder of 2.6% Ni²⁺ ions in Li(3b) sites. Electrochemical tests were carried out in the potential range 2.5?C4.5?V vs. lithium metal on samples heated at 900?°C for 12?h. Initial discharge capacity is 154 mAh/g at C/5, while a capacity of 82 mAh/g is still delivered at 10 C by the two-step synthesized LiNi_1/3Co_1/3Mn_1/3O₂ as cathode material.     

Studies of the electrochemical properties and thermal stability of LiNi1/3Co1/3Mn1/3O2/LiFePO4 composite cathodes for lithium ion batteries

A series of LiNi_1/3Co_1/3Mn_1/3O₂/LiFePO₄ composite cathodes with the LiFePO₄ mass content ranging from 10 to 30 wt% were prepared by ball milling in order to combine the merits of layered LiNi_1/3Co_1/3Mn_1/3O₂ and olivine LiFePO₄. The structure and morphology of the samples were characterized by X-ray diffraction and scanning electron microscope. The composite cathodes exhibited improved electrochemical performance compared with pristine LiNi_1/3Co_1/3Mn_1/3O₂. Among all the composite cathodes, the one with 20 wt% of LiFePO₄ showed the best electrochemical performance in terms of discharge capacity, cycle stability, and rate capability. Electrochemical impedance spectroscopy showed that mixing of LiFePO₄ in LiNi_1/3Co_1/3Mn_1/3O₂ decreased the internal resistance of the electrode, retarded the formation of SEI film, and facilitated the charge transfer reaction. Differential scanning calorimetry showed that the composite cathode had better thermal stability than pristine LiNi_1/3Co_1/3Mn_1/3O₂.     

ZrO2 coating of LiNi1/3Co1/3Mn1/3O2 cathode materials for Li-ion batteries

ZrO₂-coated LiNi_1/3Co_1/3Mn_1/3O₂ materials were prepared by hydroxide precipitation. The structure and electrochemical properties of the ZrO₂-coated LiNi_1/3Co_1/3Mn_1/3O₂ were investigated using X-ray diffraction, scanning electron microscope, and charge–discharge tests, indicating that the lattice structure of LiNi_1/3Co_1/3Mn_1/3O₂ were unchanged after the coating but the cycling stability was improved. As the coating amount increased from 0.0 to 0.5 mol.%, the initial capacity of the coated LiNi_1/3Co_1/3Mn_1/3O₂ decreased slightly; however, the cycling stability increased remarkably over the cut-off voltages of 2.5~4.3 V and the capacity retention reached 99.5% after 30 cycles at the coating amount of 0.5 mol.%. ZrO₂ coating also improved the cycling stability of LiNi_1/3Co_1/3Mn_1/3O₂ over wider cut-off voltage of 2.5~4.6 V.     

Hydrothermal synthesis and electrochemical performance studies of Al2O3-coated LiNi1/3Co1/3Mn1/3O2 for lithium-ion batteries

LiNi_1/3Co_1/3Mn_1/3O₂ nanocrystallites were synthesized by a one-step hydrothermal method, and uniform second particles were formed by a subsequent calcination process. X-ray diffraction results indicate that the as-synthesized material can be indexed by α-NaFeO₂ layered structure with R-3 m space group. The results of Rietveld refinements show the I ₀₀₃/I ₁₀₄ value of the material is 2.032, and the nanostructured material presents low cation mixing, small cell volume, and a consequent suppression of lattice strain. The rate performances of the as-synthesized material can be further improved by coating Al₂O₃. The discharging capacity of Al₂O₃-coated material reaches 154.4 mAh g^?1, and the capacity retention maintains 80.3 % after 50 cycles at 5 C in the voltage range of 2.5 to 4.5 V, while those of the bare one is only 139.0 mAh g^?1 and 71.6 %, respectively. The transmission electron microcopy observation shows no zigzag layer exists on the surface of particle after cycles for Al₂O₃-coated LiNi_1/3Co_1/3Mn_1/3O₂. Compared to bare LiNi_1/3Co_1/3Mn_1/3O₂, the de-intercalation potential difference before and after cycles of Al₂O₃-coated one is smaller. This indicates that Al₂O₃ coating can reduce the electrochemistry polarization in the electrode bulk.     

Synthesis of spherical LiNi1/3Co1/3Mn1/3O2 cathode materials for Li-ion batteries

Spherical LiNi_1/3Co_1/3Mn_1/3O₂ was successfully prepared by controlled crystallization. The preparation started with the spherical coprecipitate of Ni_1/3Co_1/3Mn_1/3CO₃ from NiSO₄, CoSO₄, MnSO₄, NH₄HCO₃, and NH₃·H₂O, followed by pyrolysis of Ni_1/3Co_1/3Mn_1/3CO₃ at 600°C for 3 h. The X-ray diffraction analysis showed that the homogeneous cubic (Ni_1/3Co_1/3Mn_1/3)₃O₄ was obtained after the pyrolysis. Spherical LiNi_1/3Co_1/3Mn_1/3O₂ was obtained by sintering of the mixture of as-obtained (Ni_1/3Co_1/3Mn_1/3)₃O₄ and LiOH·H₂O at 900°C for 6 h in air. As-prepared spherical LiNi_1/3Co_1/3Mn_1/3O₂ presented initial discharge capacity of 162.9 mA h g⁻¹ and capacity retention of 98% at 50th cycle.     

TiO2 coating of LiNi1/3Co1/3Mn1/3O2 cathode materials for Li-ion batteries

TiO₂-coated LiNi_1/3Co_1/3Mn_1/3O₂ materials were prepared by the hydrolyzation of Ti(OBu)₄. The impact of TiO₂ coating on the structure and electrochemical properties of LiNi_1/3Co_1/3Mn_1/3O₂ was investigated using X-ray diffraction, scanning electron microscope, and charge–discharge tests. The results indicated that TiO₂ coating did not affect the lattice of LiNi_1/3Co_1/3Mn_1/3O₂, but exhibited obvious effects on its discharge capacity and cycling stability. As coated TiO₂ increased from 0.0 to 2.0 mol%, the initial capacity of samples decreased slightly, but the cycling stability over 2.5∼4.3 V increased remarkably. The capacity retention reached 99.5% at the 50th cycle at a coating amount of 2.0 mol%.     

Characterization of Na-substituted LiNi1/3Co1/3Mn1/3O2 cathode materials for lithium-ion battery

Highly crystalline layered Li_1?xNa_xNi_1/3Co_1/3Mn_1/3O₂ (x?=?0, 0.001, 0.01, 0.03, 0.05) materials are synthesized by molten salts method and characterized by scanning electron microscopy, inductively coupled plasma (ICP), X-ray diffraction, Rietveld refinement, and electrochemical measurement, respectively. ICP, SEM, and EDS results show that Na ions are incorporated in LiNi_1/3Co_1/3Mn_1/3O₂. Rietveld refinement results show that suitable Na substitution leads to stable layered structure by full Na occupying in Li layer and further attributes to low cation mixing. Electrochemical studies demonstrate that the Na-substituted LiNi_1/3Co_1/3Mn_1/3O₂ shows improved rate capability and cycling performance compared to that of pure LiNi_1/3Co_1/3Mn_1/3O₂.     

Improving the rate performance and stability of LiNi<Subscript>0.6</Subscript>Co<Subscript>0.2</Subscript>Mn<Subscript>0.2</Subscript>O<Subscript>2</Subscript> in high voltage lithium-ion battery by using fluoroethylene carbonate as electrolyte additive

Fluoroethylene carbonate (FEC) is investigated as the electrolyte additive to improve the electrochemical performance of high voltage LiNi_0.6Co_0.2Mn_0.2O₂ cathode material. Compared to LiNi_0.6Co_0.2Mn_0.2O₂/Li cells in blank electrolyte, the capacity retention of the cells with 5 wt% FEC in electrolytes after 80 times charge-discharge cycle between 3.0 and 4.5 V significantly improve from 82.0 to 89.7%. Besides, the capacity of LiNi_0.6Co_0.2Mn_0.2O₂/Li only obtains 12.6 mAh g^?1 at 5 C in base electrolyte, while the 5 wt% FEC in electrolyte can reach a high capacity of 71.3 mAh g^?1 at the same rate. The oxidative stability of the electrolyte with 5 wt% FEC is evaluated by linear sweep voltammetry and potentiostatic data. The LSV results show that the oxidation potential of the electrolytes with FEC is higher than 4.5 V vs. Li/Li⁺, while the oxidation peaks begin to appear near 4.3 V in the electrolyte without FEC. In addition, the effect of FEC on surface of LiNi_0.6Co_0.2Mn_0.2O₂ is elucidated by scanning electron microscopy (SEM), transmission electron microscopy (TEM), and X-ray photoelectron spectroscopy (XPS). The analysis result indicates that FEC facilitates the formation of a more stable surface film on the LiNi_0.6Co_0.2Mn_0.2O₂ cathode. The electrochemical impedance spectroscopy (EIS) result evidences that the stable surface film could improve cathode electrolyte interfacial resistance. These results demonstrate that the FEC can apply as an additive for 4.5 V high voltage electrolyte system in LiNi_0.6Co_0.2Mn_0.2O₂/Li cells.     

Enhanced electrochemical performances of LiNi0.5Co0.2Mn0.3O2 cathode material co-coated by graphene/TiO2

The electrochemical performances of LiNi_0.5Co_0.2Mn_0.3O₂ (NCM523) layered cathode material, such as poor rate capacity and cycling stability caused by undesirable intrinsic conductivity and low rate of lithium ion transportation, are not fairly good especially at elevated rate and cut-off voltage. To improve these properties, in this study, the co-coating layer of graphene and TiO₂ was constructed on NCM523 surface. The graphene/TiO₂ coating layer could effectively prevent hydrofluoric acid (HF) attacks, suppress the side reaction, accelerate the lithium ion diffusion and facilitate the electron migration. The enhancement of cycle performance and rate capacity was contributed to the uniform co-modified surface, interacting each other and thus exhibiting synergistic effects.