Improvement of erosion and erosion-corrosion resistance of AISI420 stainless steel by low temperature plasma nitriding

Plasma nitriding experiments were carried out with DC-pulsed plasma in 25% N₂ + 75% H₂ atmosphere at low temperature (350 °C) and normal temperature (550 °C) for 15 h. The composition, microstructure, microhardness profiles, residual stress profiles and electrochemical impedance spectrum analyses of the nitrided samples were examined. The influence of plasma nitriding on the erosion and erosion-corrosion resistance of AISI 420 martensitic stainless steel was investigated using a jet solid particle erosion tester and a slurry erosion-corrosion tester.Results showed that the 350 °C nitriding layer was dominated by ?-Fe₃N and α_N phase, a supersaturated nitrogen solid solution. However, nitrogen would react with Cr in the steel to form CrN precipitates directly during 550 °C nitriding, which would lead to the depletion of Cr in the solid solution phase of the nitrided layer. Both 350 and 550 °C plasma nitriding could improve the erosion resistance of AISI420 stainless steel under dry erosion, but the former showed better results. In both neutral and acid environment, while the erosion-corrosion resistance of AISI 420 was improved by means of 350 °C nitriding, it was decreased through 550 °C nitriding.     

Improvement of corrosion resistance of nitrided low alloy steel by plasma post-oxidation

Post-oxidizing treatments can be performed to improve the corrosion resistance of nitrided steel samples. In this paper, plasma nitriding treatments were performed at 540 °C for 4 h using ammonia as the working gas, and plasma post-oxidizing treatments were carried out at temperatures ranging from 350 °C to 500 °C for 2 h in oxygen gas. The treated samples were characterized by using optical microscopy, SEM, XRD, and electrochemical polarization. The X-ray analysis revealed the formation of iron-nitride phases of ?-Fe_2-3N and γ′-Fe₄N during plasma nitriding and iron oxide phases of hematite (Fe₂O₃) and magnetite (Fe₃O₄) through the post-oxidizing treatment. In particular, it was found that the very thin magnetite layer 0.8-1.5 μm in thickness on top of the compound layer was obtained by plasma post-oxidized at 400 °C and 450 °C. It was also demonstrated that the corrosion characteristics of the nitrided compound layer were further improved by post-oxidation treatment.     

Surface improvement and biocompatibility of TiAl24Nb10 intermetallic alloy using rf plasma nitriding

The present work describes the surface improvement and biocompatibility of TiAl₂₄Nb₁₀ intermetallic alloy using rf plasma nitriding. The nitriding process was carried out at different plasma power from 400 W to 650 W where the other plasma conditions were fixed. Grazing incidence X-ray diffractometry (GIXRD), Auger electron spectroscopy (AES), tribometer and a nanohardness tester were employed to characterize the nitrided layer. Further potentiodynamic polarization method was used to describe the corrosion behavior of the un-nitrided and nitrided alloy. It has been found that the Vickers hardness (HV) and corrosion resistance values of the nitrided layers increase with increasing plasma power while the wear rates of the nitrided layers reduce by two orders of magnitude as compared to those of the un-nitrided layer. This improvement in surface properties of the intermetallic alloy is due to formation of a thin modified layer which is composed of titanium nitride in the alloy surface. Moreover, all modified layers were tested for their sustainability as a biocompatible material. Concerning the application area of biocompatibility, the present treated alloy show good surface properties especially for the nitrided alloy at low plasma power of 400 W.     

The effect of surface nanocrystallization on plasma nitriding behaviour of AISI 4140 steel

A plastic deformation surface layer with nanocrystalline grains was produced on AISI 4140 steel by means of surface mechanical attrition treatment (SMAT). Plasma nitriding of SMAT and un-SMAT AISI 4140 steel was carried out by a low-frequency pulse excited plasma unit. A series of nitriding experiments has been conducted at temperatures ranging from 380 to 500 °C for 8 h in an NH₃ gas. The samples were characterized using X-ray diffraction, scanning electron microscopy, optical microscopy and Vickers microhardness tester. The results showed that a much thicker compound layer with higher hardness was obtained for the SMAT samples when compared with un-SMAT samples after nitriding at the low temperature. In particular, plasma nitriding SMAT AISI 4140 steel at 380 °C for 8 h can produced a compound layer of 2.5 μm thickness with very high hardness on the surface, which is similar to un-SMAT samples were plasma nitrided at approximately 430 °C within the same time.     

Microstructure and antibacterial properties of microwave plasma nitrided layers on biomedical stainless steels

Nitriding of AISI 303 austenitic stainless steel using microwave plasma system at various temperatures was conducted in the present study. The nitrided layers were characterized via scanning electron microscopy, glancing angle X-ray diffraction, transmission electron microscopy and Vickers microhardness tester. The antibacterial properties of this nitrided layer were evaluated. During nitriding treatment between 350 °C and 550 °C, the phase transformation sequence on the nitrided layers of the alloys was found to be γ → (γ + γ_N) → (γ + α + CrN). The analytical results revealed that the surface hardness of AISI 303 stainless steel could be enhanced with the formation of γ_N phase in nitriding process. Antibacterial test also demonstrated the nitrided layer processed the excellent antibacterial properties. The enhanced surface hardness and antibacterial properties make the nitrided AISI 303 austenitic stainless steel to be one of the essential materials in the biomedical applications.     

Plasticity and ab initio characterizations on Fe4N produced on the surface of nanocrystallized 18Ni-maraging steel plasma nitrided at lower temperature

18Ni-maraging steel has been entirely nanocrystallized by a series of processes including solution treatment, hot-rolling deformation, cold-drawn deformation and direct electric heating. The plasma nitriding of nanocrystallized 18Ni-maraging steel was carried out at 410 °C for 3 h and 6 h in a mixture gas of 20% N₂ + 80% H₂ with a pressure of 400 Pa. The surface phase constructions and nitrogen concentration profile in surface layer were analyzed using an X-ray diffractometer (XRD) and the glow discharge spectrometry (GDS), respectively. The results show that an about 2 μm thick compound layer (mono-phase γ′-Fe₄N) can be produced on the top of the surface layer of nanocrystallized 18Ni-maraging steel plasma nitrided at 410 °C for 6 h. The measured hardness value of the nitrided surface is 11.6 GPa. More importantly, the γ′-Fe₄N phase has better plasticity, i.e., its plastic deformation energy calculated from the load-displacement curve obtained by nano-indentation tester is close to that of nanocrystallized 18Ni-maraging steel. Additionally, the mechanical properties of γ′-Fe₄N phase were also characterized by first-principles calculations. The calculated results indicate that the hardness value and the ratio of bulk to shear modulus (B/G) of the γ′-Fe₄N phase are 10.15 GPa and 3.12 (>1.75), respectively. This demonstrates that the γ′-Fe₄N phase has higher hardness and better ductility.     

Surface engineering of biomedical metallic materials by plasma-based low-energy ion implantation

Plasma-based low-energy ion implantation, including plasma source ion nitriding/carburizing and plasma source low-energy ion enhanced deposition of thin films, for surface engineering of metallic materials was emerged as low-temperature, low-pressure surface modification technique. Plasma source ion nitriding onto AISI 316L austenitic stainless steel produced a high nitrogen face-centered-cubic phase (γ_N) layer about 10 μm thick at the temperature of 380 °C during 4 h with the high microhardness of HK_0.1 N 22.0 GPa. The microhardness of the nitrided surface from the titanium nitride phase [(Ti, Al, V)N] layer on Ti6Al4V alloy at 750 °C during 4 h achieved up to about HK_0.1 N 15.5 GPa. No pitting corrosion in the Ringer’s solution at 37 °C was detected by electrochemical polarization measurement for the nitrided AISI 316L stainless steel and Ti6Al4V alloy, respectively. Plasma source ion nitriding of the metallic materials provided the engineering surfaces with combined improvement in hardness and corrosion resistance.     

Effect of nitriding time on secondary recrystallization behaviors and magnetic properties of grain-oriented electrical steel

The effect on secondary recrystallization behaviors and magnetic properties of grain-oriented electrical steel of nitriding time from 0 to 240 s in the acquired-inhibitor method has been studied. It was found that the volume fraction of nitride precipitates increased with increasing nitriding time. However, the average diameter of the nitride precipitates decreased with increasing nitriding time. Two kinds of nitride precipitates were found to have formed after primary recrystallization annealing. A fine rod-shaped precipitate was found to be Si₃N₄ and and a coarse, lozenge-shaped precipitate was MnSiN₂. Moreover, primary grain size decreased with increasing nitriding time due to retarding of the grain growth by precipitates. After secondary recrystallization annealing, the specimen that was nitrided for 30 s obtained the largest volume fraction of abnormal growth grains and largest area percentage of Goss grains. Conversely, specimens that were nitrided more or less than 30 s demonstrated poor secondary recrystallization and obtained low area percentage of Goss grains. Furthermore, the optimum nitriding time to obtain the best magnetic properties was 30 s. In addition, the optimum nitrogen content was 150 ppm.     

Behavior of N atoms in atomic-order nitrided Si0.5Ge0.5(1 0 0)

Behavior of N atoms in atomic-order nitrided Si_0.5Ge_0.5(1 0 0) by heat treatment in Ar at 600 °C was investigated by X-ray photoelectron spectroscopy (XPS). For thermal nitridation by NH₃ at 400 °C, nitridation of surface Si atoms tends to proceed preferentially over nitridation of surface Ge atoms. It is also clear that, with the heat treatment, nitridation of Si atoms proceeds by transfer of N atoms from Ge atoms. Angle-resolved XPS results show that Ge fraction beneath the surface nitrided layer increases significantly at 600 °C compared to the initial surface. These results indicate that preferential nitridation of Si atoms at surface over Ge atoms induces Ge segregation beneath the surface nitrided layer at higher temperatures above 400 °C.     

Surface modification of 30CrNiMo8 low-alloy steel by active screen setup and conventional plasma nitriding methods

In this paper, we report on a comparative study of active screen plasma nitriding (ASPN) and conventional dc plasma nitriding (CPN) behavior of 30CrNiMo8 low-alloy steel that has been examined under various process conditions. The process variables included active screen setup parameters (screen and iron plate top lids placed on the screen setup with 8 mm of hole size), treatment temperature (550 and 580 °C), gas mixture (75/25 and 25/75 of N₂/H₂) and treatment time (5 and 10 h) in 500 Pa pressure. The structure and phases composition of the diffusion zone and compound layer were studied by X-ray diffraction (XRD), microhardness tests, light optical microscopy and scanning electron microscopy (SEM). It was observed that treated sample surfaces in both CPN and ASPN methods consist of γ′ and ? phases, and while the nitriding time and/or temperature increases, the intensity of ? phase in the compound layer will increase for ASPN and decrease for CPN method. Results show that the amount of nitrogen transferred from holes of screen toward the sample surface via sputtering and re-condensation mechanism can be affected due to the hardness and thickness of the layer.     

Influence of treating frequency on microstructure and properties of Al2O3 coating on 304 stainless steel by cathodic plasma electrolytic deposition

Alumina ceramic coatings were fabricated on 304 stainless steel by cathodic plasma electrolytic deposition (CPED). Influence of treating frequency of the power supply on the microstructure and properties of the coatings were studied. The results indicated that coatings obtained at various frequencies on 304 stainless steels were all composed of α-Al₂O₃ and γ-Al₂O₃, and α-Al₂O₃ was the dominant phase. The contents of α-Al₂O₃ decreased gradually in a very small rate with increasing the frequency and γ-Al₂O₃ gradually increased. The surface of alumina ceramic coating was porous. With increasing the frequency, the coating surface gradually became less rough and more compact, resulting in low surface roughness. The bonding strength of Al₂O₃ coating was higher than 22 MPa and was not strongly affected by treating frequency. With increasing the frequency, the alumina coated steels showed better and gradually increasing corrosion resistance than the uncoated one in 3.5% NaCl solution. The coating steel with desirable corrosion resistance was obtained at 800 Hz whose corrosion current potential and corrosion density were −0.237 V and 7.367 × 10⁻⁸ A/cm², respectively.     

Laser diffusion nitriding of Ti-6Al-4V for improving hardness and wear resistance

Owing to poor tribological properties, titanium (Ti) alloys are usually surface-treated to enhance their surface properties. Laser surface nitriding, among others, is a common method employed to increase hardness and wear resistance for Ti alloys. Conventional laser nitriding involves surface melting of Ti alloys in a nitrogen atmosphere. This inevitably results in a roughened surface and post-treatment might be required. The present study aims at laser diffusion nitriding Ti alloys without surface melting via carefully selecting the laser processing parameters. The nitrided surface was characterized by X-ray diffractometry (XRD), optical microscopy (OM), scanning-electron microscopy (SEM), and profilometry. The nitride layer formed was about 1.62 μm upon repeated passes. The change in surface roughness resulting from laser diffusion nitriding was only minimal. Nanoindentation measurements revealed that the hardness of the nitride layer was around 11.3 GPa, being about 2.3 times that of Ti-6Al-4V. Ball-on-slab sliding wear test recorded a reduction in wear volume by about 8 times. The results of the present work thus demonstrate the feasibility of diffusion nitriding of Ti-6Al-4V by laser treatment for enhancing its surface properties and performance.     

MicroRaman study of the effect of oxide layer on nitriding of Ti-6Al-4V

Ti-6Al-4V samples were subjected to nitrogen ion implantation and low pressure RF plasma nitriding in a PIII equipment after chemical etching in Kroll's reagent. The samples were characterized by optical microscopy, AFM, microRaman, XRD and micro hardness measurements. From microRaman, oxides of titanium were found in the inter-granular β region whereas the oxide on the α region was extremely thin. The oxide on the β region was found to be amorphous and from intensity dependent Raman spectra, it was found to have a layered structure. The top layer was rutile and the inner layer anastase. Presence of Ti₂O₃ was also found. After PIII treatment at 600 °C, microRaman showed the presence of nitride in both the regions and the oxide was absent in the β regions. Also, from intensity dependent Raman spectra, it was found that in-take of nitrogen by β regions was higher. The oxide layer remained unaffected after plasma nitriding. Nitride presence in the α was established by microRaman. Even though Raman spectra from β regions were nearly the same as that of oxide, presence of nitrogen was indicated by the spectra. XRD studies of implanted and nitrided samples showed the prsence of TiN and Ti₂N in implanted sample and presence of Ti₂N in the nitrided sample. The β regions were found to have higher microhardness values after PIII and nitriding treatments. This is attributed to the deeper diffusion of nitrogen in these regions.     

Effect of surface nanocrystallization induced by fast multiple rotation rolling on hardness and corrosion behavior of 316L stainless steel

A nanostructured layer was fabricated by using fast multiple rotation rolling (FMRR) on the surface of 316L stainless steel. The microstructure in the surface was characterized by transmission electron microscopy and X-ray diffraction. The effects of FMRR on the microhardness, surface roughness and corrosion behavior of the stainless steel were investigated by microhardness measurements, surface roughness measurements, potentiodynamic polarization curves and pitting corrosion tests. The surface morphologies of pitting corrosion specimens were characterized by scanning electron microscopy. The results show that FMRR can cause surface nanocrystallization with the grain size ranges from 6 to 24 nm in the top surface layer of the sample. The microhardness of FMRR specimen in the top surface layer remarkably increases from 190 to 530 HV. However, the surface roughness slightly rises after FMRR treatment. The potentiodynamic polarization curves and pitting corrosion tests indicated that the FMRR treated 316L stainless steel with a surface nanocrystallized layer reduced the corrosion resistance in a 3.5% NaCl solution and enhanced the pitting corrosion rate in a FeCl₃ solution. Possible reasons leading to the decrease in corrosion resistance were discussed.     

Corrosion behavior of boride layers evaluated by the EIS technique

The corrosion behavior of boride layers at the AISI 304 steel surface is evaluated in the present study. Electrochemical impedance spectroscopy (EIS) technique was used for the evaluation of the polarization resistance at the steel surface, with the aid of AUTOLAB potentiostat. Samples were treated with boron paste thickness of 4 and 5 mm, in the range of temperatures 1123 ≤ T ≤ 1273 K and exposed time of 4 and 6 h. The electrochemical technique employed 10 mV AC with a frequency scan range from 8 kHz to 3 mHz in deaerated 0.1 M NaCl solution. Nyquist diagrams show that the highest values of corrosion resistance are present in the samples borided at the temperature of 1273 K, with treatment time of 4 h and 4 mm of boron paste thickness. The values of corrosion resistance on borided steels are compared with the porosity exhibited in the layers.     

Corrosion behaviour of AISI 304 stainless steel with Cu coatings in H2SO4

The work addresses the influence of cementation and electrodeposition of copper coatings on the corrosion resistance of AISI 304 stainless steel immersed in 30 wt.% H₂SO₄ at temperatures of 25 and 50 °C. Corrosion process was evaluated by gravimetric tests, DC measurements and electrochemical impedance spectroscopy (EIS). The specimen surfaces were analysed by scanning electron microscopy, X-ray photoelectron spectroscopy (XPS) and X-ray diffraction. The corrosion performance of AISI 304 stainless steel in sulphuric acid solution was greatly improved by copper coatings. The amount of copper deposited by the cementation process was sufficient to protect the stainless steel of corrosion. A greater amount of copper obtained by electrodeposition treatments does not supply further improvement in the corrosion behaviour. The improved corrosion resistance is related to copper dissolution at the initial stages of immersion tests and the presence of Cu²⁺ in the solution, which makes the medium more oxidizing, increasing the stability of the passive layer. In addition, the presence of copper at the surface reduces the overpotential of cathodic reaction, enabling the transition from an active region to the passive one.     

Laser Nitriding of Iron,Stainless Steel,and Plain Carbon Steel Investigated by Mössbauer Spectroscopy

Nitriding is a common method for improving the hardness, mechanical properties, wear and corrosion resistance of metals. Laser nitriding of metals is an efficient process, where the irradiation of surfaces in air or nitrogen atmospheres with short laser pulses leads to a fast take-up of nitrogen into the irradiated surfaces. This process has been extensively investigated for pure iron, but usually, no tools or functional parts are made of pure iron. Mainly steel or cast iron is used as a base material. Therefore, when looking for technical applicability, also the influence of alloying elements on the laser nitriding process is of great interest. Besides the pure iron various carbon steels and an austenitic stainless steel were studied in laser nitriding experiments in order to investigate the influence of the material itself. Here, the process is investigated via Conversion Electron and X-ray Mössbauer Spectroscopy (CEMS and CXMS), Resonant Nuclear Reaction Analysis (RNRA), and X-Ray Diffraction (XRD). It appears that carbon steels are even better suited for the laser nitriding process than pure iron, and the laser nitriding also works efficiently for the stainless steel which is normally difficult to be nitrided.     

Growth and real time corrosion resistance monitoring of lead decanoate coatings

Lead is very susceptible to corrosion in the presence of organic acids and humidity. A potential countermeasure is to apply a lead carboxylate coating by immersing the metal in a sodium carboxylate solution/suspension. In this work we report on the degree of surface coverage and the corrosion resistance of a lead decanoate Pb(C₁₀)₂ coating as a function of treatment time. Results show that the surface coverage reaches 91% after 15 min and about 100% after 1 h in a 0.05 M sodium decanoate solution. The corrosion resistance, as indicated by electrochemical impedance spectroscopy, continues to increase even after 6 h of immersion. In addition, we show that in the case of planar transport, a diffusion layer of 17 mm thickness exists, wherein the sodium decanoate concentration drops linearly from its bulk value to almost zero at the solid/surface interface.     

Characterization of the nitrided layers of XC38 carbon steel obtained by R.F. plasma nitriding

XC38 carbon steel was nitrided in a low-pressure R.F. plasma using a mixture of 60% N₂-40% H₂ without cathodic bias on the samples. The experiments were carried out at different temperatures for various time durations. The generated nitride layers were characterized by SEM observations, XRD and GDOS analyses. These analyses indicate that the compound layer was composed of the γ′-Fe₄N phase with a surface content of N close to 6 wt%. An approach was used to study the growth kinetics of the compound layer at 500 °C. Furthermore, it was concluded that its kinetics follows a power law, which deviates from the classical parabolic growth.     

First stages of surface steel nitriding: X-ray photoelectron spectroscopy and electrical measurements

Quantitative and qualitative analysis techniques were employed to study the first stages of ultra-high vacuum plasma nitriding of the 42CrMo4 steel. At constant treatment temperature, maintained for all samples at about 360 °C, we have established the influence of treatment time on the chemical composition, thickness and electrical properties of the nitrided layer.In this purpose it was used a stacking atomic layer model describing the sample surface, which takes into account the attenuation depth of photoelectrons by the atomic monolayers. So, we have found that after 2 h of nitriding in laboratory conditions, 70% of the nitrided layer was composed of iron oxide. Also, I–V measurements indicate an influence of the nitride overlayer with increasing treatment time.