A novel strategy to synthesize cobalt hydroxide and Co3O4 nanowires

Cobalt hydroxide ultra fine nanowires were prepared by a facile hydrothermal route using hydrogen peroxide. This method provides a simple, low cost, and large-scale route to produce β-cobalt hydroxide nanowires with an average diameter of 5 nm and a length of ca. 10 μm, which show a predominant well-crystalline hexagonal brucite-like phase. Their thermal decomposition produced highly uniform nanowires of cobalt oxide (Co₃O₄) under temperature 500 °C in the presence of oxygen gas. The produced cobalt oxide was characterized by X-ray diffraction, transmission electronic microscopy, and selected-area electron diffraction. The results indicated that cobalt oxide nanowires with an average diameter of 10 nm and a length of ca. 600 nm have been formed, which show a predominant well-crystalline cubic face-centered like phase.     

Mesoporous TiO2-B nanowires synthesized from tetrabutyl titanate

Ultralong mesoporous TiO₂-B nanowires were synthesized via a hybrid hydrothermal-ion exchanging-thermal treatment using tetrabutyl titanate (TBOT) as a raw material. The phase transformations and porous structures of TiO₂-B nanowires were characterized and studied by X-ray diffraction (XRD), transmission electron microscopy (TEM) and N₂ adsorption-desorption measurement. Mesoporous TiO₂-B nanowires showed a length of several micrometers and diameter of about 25 nm. The porous structures of obtained TiO₂-B nanowires were demonstrated by BJH pore distribution measurement. The wirelike morphologies and porous structures of monodisperse nanowires calcined at 600 °C showed little change, which indicated that such nanowires possessed high thermal stability. The formation mechanism of TiO₂-B nanowires with mesoporous structures were also discussed based on our experimental results.     

Synthesis of In-doped Ga2O3 zigzag-shaped nanowires and optical properties

In-doped Ga₂O₃ zigzag-shaped nanowires and undoped Ga₂O₃ nanowires have been synthesized on Si substrate by thermal evaporation of mixed powders of Ga, In₂O₃ and graphite at 1000 °C without using any catalyst via a vapor-solid growth mechanism. The morphologies and microstructures of the products were characterized by field-emission scanning electron microscopy (FE-SEM), X-ray diffraction (XRD), transmission electron microscopy (TEM), energy-dispersive X-ray spectroscopy (EDS) and photoluminescence spectroscopy (PL). The nanowires range from 100 nm to several hundreds of nanometers in diameter and several tens of micrometers in length. A broad emission band from 400 to 700 nm is obtained in the PL spectrum of these nanowires at room temperature. There are two blue-emission peaks centering at 450 and 500 nm, which originate from the oxygen vacancies, gallium vacancies and gallium-oxygen vacancy pairs.     

Synthesis and magnetic properties of spinel CoFe2O4 nanowire arrays

Spinel CoFe₂O₄ nanowire arrays were synthesized in nanopores of anodic aluminum oxide (AAO) template using aqueous solution of cobalt and iron nitrates as precursor. The precursor was filled into the nanopores by vacuum impregnation. After heat treatment, it transformed to spinel CoFe₂O₄ nanowires. The structure, morphology and magnetic properties of the sample were studied by X-ray diffraction (XRD), scanning electron microscopy (SEM), transmission electron microscopy (TEM) and vibrating sample magnetometer (VSM). The results indicate that the nanowire arrays are compact. And the individual nanowires have a high aspect ratio, which are about 80 nm in diameter and 10 μm in length. The nanowires are polycrystalline spinel phase. Magnetic measurements indicate that the nanowire arrays are nearly magnetic isotropic. The reason is briefly discussed. Moreover, the temperature dependence of the coercive force of the nanowire arrays was studied.     

Synthesis of β-Ga2O3 nanowires through microwave plasma chemical vapor deposition

In this study, we demonstrate the large-scale synthesis of beta gallium oxide (β-Ga₂O₃) nanowires through microwave plasma chemical vapor deposition (MPCVD) of a Ga droplet in the H₂O and Ar atmosphere at 600 W. Unlike the commonly used MPCVD method, the H₂O, not mixture of gas, was employed to synthesize the nanowires. The ultra-long β-Ga₂O₃ nanowires with diameters of about 20-30 nm were several tens of micrometers long. The morphology and structure of products were analyzed by scanning electron microscopy (SEM), X-ray diffraction (XRD), transmission electron microscopy (TEM) and high-resolution transmission electron microscope (HRTEM). The growth of β-Ga₂O₃ nanowires was controlled by vapor-solid (VS) crystal growth mechanism.     

Electrodeposition and characterization of thermoelectric Bi2Te2Se/Te multilayer nanowire arrays

Multilayer nanowire arrays of a new heterogeneous thermoelectric material, Bi₂Te₂Se/Te, were successfully fabricated by a template-assisted pulsed electrodeposition method. The nanowires were characterized by X-ray diffraction, field emission scanning electron microscopy, transmission electron microscopy, high resolution transmission electron microscopy, and energy dispersive X-ray spectroscopy, respectively. The diameter of the nanowires is in the range of 60–85 nm. By adjusting the concentration of Te precursor, the length of the Te segment can be modulated. At sufficient low concentration of Te precursor, the phase composition of the other segment can even be changed from Bi₂Te₂Se to Bi₂Se₂Te. The formation and growth mechanisms of the nanowires were proposed.     

Raman spectroscopic and photoluminescence study of single-crystalline SnO2 nanowires

Single-crystalline SnO₂ nanowires with sizes of 4-14 nm in diameter and 100-500 nm in length were produced in a molten salt approach by using hydrothermal synthesized precursor. Structural characters of the nanowires were examined by X-ray diffraction and high-resolution electron transmission microscopy. Raman, photoluminescence and X-ray photoelectron spectra of the samples were examined under heat treatments. Three new Raman modes at 691, 514 and 358 cm⁻¹ were recorded and assigned. The former two are attributed to activation of original Raman-forbidden A_2uLO mode and the third is attributed to defects in small-sized nanowires. A strong photoluminescence is observed at about 600 nm, the temperature effects is examined and the origin of the PL process is discussed via X-ray photoelectron spectra.     

Fabrication and characterization of CuO-core/TiO2-shell one-dimensional nanostructures

We have fabricated CuO-core/TiO₂-shell one-dimensional nanostructures by coating the CuO nanowires with MOCVD-TiO₂. The structure of the core/shell nanowires has been investigated by using scanning electron microscopy, transmission electron microscopy, and X-ray diffraction analysis techniques. The CuO-cores and the TiO₂-shells of the as-synthesized nanowires have been found to have crystalline monoclinic CuO and crystalline tetragonal anatase TiO₂ structures, respectively. The CuO-core/TiO₂-shell nanowires are winding and has rougher surface, whereas the CuO nanowires are straight and have smoother surface.Influence of the substrate temperature and the growth time on the structure such as the morphology, size, and crystallographic orientation of CuO nanowires synthesized by thermal oxidation of Cu foils have also been investigated. All the nanowires have only the CuO phase synthesized at 600 °C, whereas those synthesized at 400 °C have both CuO and Cu₂O phases. The highest density of CuO nanowires with long thin straight morphologies can be obtained at 600 °C. In addition, the growth mechanism of the CuO nanowires has been discussed.     

Fabrication and characterization of GaN/amorphous Ga2O3 nanocables through thermal oxidation

In an effort to obtain one-dimensional core/shell nanostructures, thermal oxidation behavior of GaN nanowires in O₂ with N₂ ambients was investigated by x-ray diffraction, transmission electron microscopy, and x-ray photoelectron spectroscopy. Crystallinity and chemical bonding states of the oxidized surface in the GaN nanowires were strongly dependent on the oxidation temperature. Chemical oxidation reaction occurred upon increasing the temperature, accompanied by the formation of an amorphous Ga₂O₃ layer at the GaN nanowire surface at 900 ^°C. The XPS analyses provided further evidence supporting the change in the chemical bonding states with increasing oxidation temperature.     

Alumina template-assisted electrodeposition of Bi2Te2.7Se0.3 nanowire arrays

Bi₂Te_2.7Se_0.3 nanowire arrays have been fabricated by electrodeposition into the pores of an anodic aluminum oxide (AAO) template followed by annealing at 300 °C under Ar atmosphere. The as-prepared nanowires were characterized by X-ray diffraction, field emission scanning electron microscopy, transmission electron microscopy and energy dispersive X-ray spectroscopy. The nanowires are uniform single crystalline with diameter of ∼14 nm.