La2Zr2O7:Eu3+纳米棒的合成、表征及其荧光性能

采用传统固相法和水热法成功地制备出棒状La₂Zr₂O₇:Eu³⁺荧光粉. 利用X射线粉末衍射仪、透射电镜和荧光光谱仪等分析了产物的结构、形貌和发光特性. 结果表明红色荧光粉La₂Zr₂O₇:Eu³⁺有良好的晶相,属于立方结构,空间点群为Fd3m; 其形貌主要为纳米棒, 平均直径约47 nm, 长度为50～700 nm. 并对纳米棒的生长机理进行了探讨. 在466 nm蓝光激发下,La₂Zr₂O₇:Eu³⁺荧光粉能发射出Eu³⁺的特征红色荧光,发射主峰位于616 nm处,归属于Eu³⁺的⁵DO_→⁷F2_{超灵敏电偶极跃迁.此外,在产物的发射光谱中能够观察到⁵D}1_→⁷FJ _{(J=0, 1, 2)跃迁和⁵D}1_→⁷FJ _{(J=1, 2, 4)跃迁的劈裂峰,这说明Eu³⁺处在低对称性的晶体场格位中.}     

Tm3+/Yb3 :LiYF4单晶的高效近红外量子剪裁及其在光伏电池中的应用

采用改进的坩埚下降法成功地生长了Tm/Yb共掺氟化钇锂单晶. 该单晶体具有每吸收一个蓝色光子并能发射出2个1000 nm近红外光子的下转换发光效应. 测定了样品的激发光谱、发射光谱和荧光衰减曲线. 在465 nm蓝光激发下观察到由Yb³⁺：²F_5/2→²F_7/2能级跃迁所致的960～1050 nm 波段的发射带,此发光带源于Tm³ 对Yb³ 离子的能量下转换过程. 应用Inokuti-Hirayama模型,研究了晶体的能量转换过程,结果表明Tm³ 向Yb³ 的能量传递是一个电偶极子相互作用机制过程. 当Tm³ 与Yb³ 离子的掺杂浓度为0.49mol%与5.99mol%时,单晶的量子剪裁效率达到最大值167.5%.     

Er3+：GdVO4中Er3+离子的光谱参数计算和晶场中能级分裂的讨论

对Er³⁺：GdVO₄样品的光谱参数以及Er³⁺在晶场中能级的分裂情况进行了研究. 首先对样品进行了吸收光谱的测量，接着用Judd-Ofelt理论拟合出了Er³⁺在GdVO₄晶体中的强度参量Ω_t，并由此计算了跃迁的振子强度、自发辐射跃迁速率、荧光分支比和积分发射截面. 通过计算结果可以发现有较多能级之间的跃迁都有大于10^-6的振子强度和大于10^-18cm的积分发射截面，并且具有较高的荧光分支比，特别是²H_11/2→⁴I_15/2，⁴S_3/2→⁴I_15/2，⁴F_9/2→⁴I_15/2和⁴I_13/2→⁴I_15/2等几个强发光能级除了具有较大的振子强度和积分发射截面外还有很好的应用前景，因此也更加值得关注. 最后还利用群论讨论了Er³⁺离子在GdVO₄晶场中各能级的分裂情况并对各Stark子能级的J_z混杂情况进行了分析.     

Gd2O3:Eu3+纳米晶的燃烧合成及光致发光性质

采用柠檬酸作燃烧剂用燃烧合成法制备了Gd₂O₃:Eu³⁺纳米晶.用X射线衍射仪(XRD)、高分辨透射电子显微镜(HRTEM)和荧光分光光度计等对Gd₂O₃:Eu³⁺纳米晶的结构、形貌和发光性能进行了分析.结果表明：不同柠檬酸与稀土离子配比(C/M)制备的样品经800℃ 退火1 h后，均得到了纯立方相的Gd₂O₃:Eu³⁺纳米晶，晶粒尺寸约为30 nm，尺寸分布较窄，其中以C/M=1.0时制备的纳米晶结晶性最好，发光强度最大.Gd₂O₃:Eu³⁺纳米晶主发射峰位置均在612 nm处 (⁵D₀→⁷F₂跃迁)，激发光谱中电荷迁移态发生红移，观察到Gd³⁺向Eu³⁺的有效能量传递.对柠檬酸与稀土离子配比(C/M)对结晶度、发光性质等的影响也进行了分析和讨论.     

Tm3+/Yb3+ ∶LaF3纳米体系中掺杂Yb3+ 离子对Tm3+ 离子荧光发射的影响

为研究Yb³⁺离子浓度变化对Tm³⁺离子在蓝色波段荧光强度的影响,以NaF和La(NO₃)₃为原料,采用水热法制备了Tm³⁺和Yb³⁺共掺的Tm³⁺/ Yb³⁺∶LaF₃纳米颗粒.用X射线衍射对LaF₃纳米颗粒进行表征的结果显示,纳米晶体结构呈六方相.透射电镜的观测结果显示,纳米颗粒样品大小均匀、分散性良好.在波长为800 nm的激光激发下,观测到了上转换蓝光发射,其中包括波长为474 nm和479 nm的较强的荧光辐射(相应的跃迁为1G4→3H6)和波长位于450 nm的强度较弱的荧光发射(相应的跃迁为1D2→3F4).通过观测不同Yb³⁺离子浓度条件下共掺Tm³⁺/Yb³⁺∶LaF₃样品的荧光光谱,研究了Yb³⁺离子掺杂浓度对于Tm³⁺离子的荧光发射的影响,并探讨了产生这种现象的原因.研究结果显示,对于1G4→3H6跃迁产生的荧光发射(474 nm),当Yb³⁺离子浓度增大时,反向能量传递速率的增加导致了荧光强度的增大.然而,当Yb³⁺离子浓度增大到一定程度时,Yb³⁺离子激发态能级寿命的减少将引发荧光强度的下降.相比较而言,Yb³⁺离子的浓度的变化对于1D2→3F4跃迁产生的位于450 nm处荧光强度的影响较弱.     

N2O+离子A2Σ+电子态高振动能级的转动结构分析

利用一束波长为36055nm的激光，通过(3+1)共振多光子电离方法制备纯净的且处于X²Π_1/2，3/2(000)态的N₂O⁺离子，用另一束激光激发所制备的离子到第一电子激发态A²Σ⁺的不同振动能级，然后解离，通过检测解离碎片NO⁺强度随光解光波长的变化，得到了转动分辨的N₂     

Tm3+/Yb3+共掺碲酸盐玻璃的近红外发光及能量传递机理

采用高温熔融法制备了组分为TeO₂-ZnO-Na₂O的Tm³⁺离子单掺和Tm³⁺/Yb³⁺共掺碲酸盐玻璃,应用Judd-Ofelt理论计算分析了玻璃样品的强度参量Ω_t(t=2, 4, 6),自发辐射跃迁几率A,荧光分支比β和荧光辐射寿命τ_rad等光谱参量,测量得到了不同Yb³⁺离子掺杂浓度下玻璃样品的Tm³⁺离子上转换发光谱.结果显示,在980 nm泵浦光激励下玻璃样品发射出强烈的近红外上转换荧光.对Tm³⁺离子上转换发光分析表明,强烈的Tm³⁺离子近红外上转换发光主要来自于Yb³⁺/Yb³⁺离子间的共振能量传递以及基于单声子和双声子辅助的Yb³⁺/Tm³⁺离子间的非共振能量传递过程,并进一步计算得到了声子贡献比和能量传递系数.最后,计算分析了Tm³⁺:³F₄→³H₆能级间跃迁的1.8 μm波段吸收截面、受激发射截面和增益系数.研究表明,Yb³⁺/Tm³⁺共掺TeO₂-ZnO-Na₂O玻璃可以作为近红外波段固体激光器的潜在增益基质.     

Er3+/Yb3+共掺Gd3Sc2Ga3O12晶体的上转换发光

研究了提拉法生长的Er³⁺/Yb³⁺:Gd₃Sc₂Ga₃O₁₂和Er³⁺:Gd₃Sc₂Ga₃O₁₂晶体在室温下320—1700nm范围的吸收光谱和500—750nm范围内的上转换荧光谱，同时对其上转换荧光的可能发生机制、途径以及上转换过程可能对Er^{3+相似文献}   

NaF晶体中电荷补偿掺杂Ce3+离子光谱性质的从头算

用从头算研究NaF晶体中Ce³⁺占据Na⁺格位时的光谱性质,电荷补偿由占据格位第一配位壳层的两个氟原子被氧取代 (O_F^') 或第二配位壳层的两个Na空位(_Na^') 来提供. 首先采用基于DFT的超单胞模型方法优化了Ce³⁺的局域结构,并构造以Ce为中心的镶嵌团簇,对其进行基于波函数理论的CASSCF/CASPT2/RASSI-SO计算,获得Ce³⁺的4f¹和5d¹组态分裂能级能量. 通过将4f→5d跃迁能量计算值与低温实验激发光谱比较,发现实验观测到的最低4f→5d跃迁谱带(390 nm)来自于两个最近邻O_F^'补偿的Ce³⁺离子,并不是文献中的两个次近邻V_Na^' 补偿的Ce³⁺. 最后从5d¹组态能级重心位移和晶场分裂两方面分析了由两个最近邻O_F^'取代造成最低4f→5d 跃迁红移约8000 cm^-1的原因.     

Cl2+离子R支跃迁光谱的理论研究

从双原子分子能级的物理表达式出发进行多次微分,建立了预测双原子分子体系R支高振转跃迁谱线的新解析公式. 使用新解析公式预测双原子体系R支高阶跃迁谱线的数据时,最多只需15条精确的实验跃迁谱线和该跃迁带中对应的上下 振动态的转动光谱常数B′_v 和 B″_v.将该解析公式用于预测Cl₂⁺ 离子 A²∏_u---X²∏_g跃迁系(3,7)带和(4,8)带的跃迁谱线,不仅精确的重复了实验给出的较低阶的跃迁光谱数据值, 而且正确预言了所研究体系中缺失的振转跃迁谱线,尤其是高阶的跃迁谱线数据.     

Synthesis and luminescent properties of nanoparticles LaSrAl3O7:Eu, Tb

Phosphors of nanoparticles LaSrAl₃O₇:RE³⁺(REEu, Tb) have been prepared by a sol–gel method. The structure and luminescent properties of LaSrAl₃O₇:Eu³⁺ and LaSrAl₃O₇:Tb³⁺ phosphors were characterized by X-ray diffraction and atomic force microscopy (AFM), photoluminescence excitation and emission spectra were utilized. From X-ray diffraction (XRD) patterns, it is indicated that the phosphor LaSrAl₃O₇ forms without impurity phase at 900 °C. From atomic force microscopy (AFM) images, it is shown that the crystal size of the phosphores are about 60–80 nm. Upon excitation with UV irradiation, it is shown that there is a strong emission at around 617 nm corresponding to the forced electric dipole ⁵D₀–⁷F₂ transition of Eu³⁺, and at around 545 nm corresponding to the ⁵D₄–⁷F₅ transition of Tb³⁺. The dependence of photoluminescence intensity on Eu³⁺(or Tb³⁺) concentration and annealing temperature were also studied in detail.     

Spectral characterization and energy levels of Cr:Sc2(MoO4)3 crystal

This paper reports the spectral properties and energy levels of Cr³⁺:Sc₂(MoO₄)₃ crystal. The crystal field strength Dq, Racah parameter B and C were calculated to be 1408 cm⁻¹, 608 cm⁻¹ and 3054 cm⁻¹, respectively. The absorption cross sections σ_α of ⁴A₂→⁴T₁ and ⁴A₂→⁴T₂ transitions were 3.74×10⁻¹⁹ cm² at 499 nm and 3.21×10⁻¹⁹ cm² at 710 nm, respectively. The emission cross section σ_e was 375×10⁻²⁰ cm² at 880 nm. Cr³⁺:Sc₂(MoO₄)₃ crystal has a broad emission band with a broad FWHM of 176 nm (2179 cm⁻¹). Therefore, Cr³⁺:Sc₂(MoO₄)₃ crystal may be regarded as a potential tunable laser gain medium.     

Crystal field energy levels of the laser crystal Gd3Ga5O12: Nd

The crystal field energy levels of laser crystal Gd₃Ga₅O₁₂: Nd³⁺ are calculated using the diagonalization (of energy matrix) method. From the calculations, the 93 observed crystal field energy levels are explained reasonably and the root-mean-square (r.m.s.) deviation σ(≈25.6 cm⁻¹) and the scalar crystal-field strength parameter Nv (≈3847 cm⁻¹) are obtained. The results are discussed.     

Energy transfer and upconversion of Nd doped RbY2Cl7

Single crystals of Nd³⁺:RbY₂Cl₇ were grown by the Bridgman-Stockbarger method. The host crystal contains two slightly inequivalent Y³⁺ ions, each with an approximate C_2v site symmetry. Anti-Stokes emission from the ⁴G_7/2 and ⁴D_3/2 levels was observed after laser excitation of the ⁴F_3/2 and ⁴F_9/2 multiplets. Laser excitation at 413 cm⁻¹ or 453 cm⁻¹ above the ⁴F_3/2 multiplet resulted in emission from the ²P_1/2 level. Laser site-selective upconverted emission spectra have been measured, as well as their emission transients and power dependence. Possible excited state absorption and energy-transfer upconversion (ETU) mechanisms are proposed and discussed. Due to the smaller crystal field and a somewhat different energy level structure for the Nd³⁺ ions in RbY₂Cl₇ as compared with those observed for Nd³⁺ in fluoride or oxide hosts, the ⁴G_7/2 and ⁴D_3/2 multiplets are populated under ⁴F_3/2 excitation in a three and four step ETU process, respectively, instead of in a two and three step process as observed for the lighter hosts.     

Photoluminescence characterization of Ce and Dy doped Li2CaGeO4 phosphors

Ce³⁺ and Dy³⁺ activated Li₂CaGeO₄ phosphors were prepared by a solid-state reaction method, and characterized by XRD (X-ray diffraction) and photoluminescence techniques. The characteristic emission bands of Dy³⁺ due to ⁴F_9/2→⁶H_15/2 (blue) and ⁴F_9/2→⁶H_13/2 (yellow) transitions were detected in the emission spectra of Li₂CaGeO₄:Dy³⁺. Ce³⁺ broad band emission was observed in Li₂CaGeO₄:Ce³⁺ phosphors at 372 and 400 nm due to 5d→4f transition when excited at 353 nm. Co-doping of Ce³⁺ enhanced the luminescence of Dy³⁺ significantly and concentration quenching occurs when Dy³⁺ is beyond 0.04 mol%. White-light with different hues can be realized by tuning Dy³⁺ concentration in the phosphors.     

Structures and luminescence properties of Yb3＋ in the double perovskites Ba2YB＇O6 （B＇=Ta5＋, Nb5＋） phosphors

The Yb³⁺ doped Ba₂YB'O₆ (B'=Ta⁵⁺, Nb⁵⁺) were prepared by high temperature solid-state reaction method, their structures were determined by x-ray diffraction and refined by Rietveld method. The diffuse reflection absorption, excitation and emission spectra of Yb³⁺:Ba₂YB'O₆ (B'=,Ta⁵⁺, Nb⁵⁺) were measured at room temperature. Under the excitation of ultraviolet light, these phosphors exhibit broad charge transfer band emissions of TaO₆ or NbO₆ centre with large Stokes shift. The Yb³⁺ doped into these hosts are situated at Y³⁺ sites of cubic symmetry (O_h). The experimental energy levels of Yb³⁺ in Ba₂YTaO₆ and Ba₂YNbO₆ were determined by photoluminescence and diffuse reflection absorption spectra. Their wavefunctions and theoretical energy levels were obtained by diagonalising the Hamiltonian matrix. The experimental energy levels were fitted by Levenberg--Marquardt iteration algorithm to determine crystal field parameters. Then, the magnetic-pole transition line strengths of Yb³⁺:Ba₂YB'O₆(B'=Ta⁵⁺, Nb⁵⁺) from (²F_5/2)Γ₈^- to the low-energy states were calculated.     

Growth and optical properties of Yb and Tb codoped BaB2O4 crystals

Optical absorption and luminescence spectra of ytterbium and terbium codoped BaB₂O₄ (β-BBO and α-BBO) crystals grown in different conditions have been studied. Low-temperature absorption peaks were observed in all samples. Features related to rare earth ions were observed in absorption and luminescence spectra. Absorption and emission in the range 860-1000 nm are caused by ²F_5/2↔²F_7/2 transitions in Yb³⁺ ions. Emission peaks at 500, 550, 590 and 630 nm correspond to ⁵D₄→⁷F₆, ⁷F₅, ⁷F₄, and ⁷F₃ transitions of Tb³⁺ ions, respectively. The probable reasons of variations in spectroscopic features related to Yb in BBO host are discussed. It has been shown that the replacement of Ва²⁺ by Yb³⁺ in the lattice of ВаВ₂О₄ results in the decrease in the symmetry of oxygen surrounding of Yb³⁺.     

超声喷雾共沉淀法制备的Lu3Al5O12∶Eu3+ 纳米粉体发光特性

采用新型超声喷雾共沉淀法技术,以Lu₂O₃、Eu₂O₃、Al(NO₃)₃·9H₂O为原料,制备了不同浓度Eu³⁺离子掺杂的Lu₃Al₅O₁₂纳米粉体.用X射线粉末衍射表征了获得纳米粉体的相,用扫描电镜观察了纳米粒子的形貌.测定了粉体的激发光谱、⁷F₀-⁵D₂声子边带谱与发射光谱.研究了不同高温烧结温度与Eu³⁺掺杂浓度对纳米粒子的发光强度与粒子形貌的影响规律.研究表明,当烧结温度高于900 ℃时,粉体发光强度明显增强,并且随着煅烧温度的增加,发光强度有所增强.Eu³⁺离子的最佳掺杂浓度为5~7 mol%.根据稀土离子Eu³⁺光学跃起矩阵元的特点,从发射光谱获得Eu³⁺光学跃起的J-O参量Ω₂与Ω₄.在Eu³⁺掺杂浓度均为5 mol%时,其强度参量达最小,电-声子耦合最强.然后随着掺杂浓度的进一步提高,强度参量略有增加,电-声子耦合减弱.说明Eu-O键强增加,共价性增强,Eu³⁺的局域环境对称性降低.Ω₂值低于Eu³⁺在玻璃与晶体基质中的情况,这是由于纳米粒子中存在着大量的缺陷以及晶体的结构畸变导致纳米粒子的对称性下降所致.     

共掺Na+的Yb3+∶CaF2晶体的荧光分析与低阈值激光运转

基于975nm激发的室温下荧光光谱测量，系统地研究了在新型钠、镱共掺的氟化钙晶体中钠离子的作用机理，分析了掺钠离子浓度与激光阈值的关系，获得了具有最低激光阈值的掺杂浓度优化配比. 激光实验表明对于2%Yb³⁺离子浓度的氟化钙，掺入3%的钠离子能够获得最低阈值的激光运转，这与理论和荧光分析完全一致. 关键词： 镱、钠共掺氟化钙 荧光光谱 激光阈值     

Luminescence of La3F3[Si3O9]:Ce

The luminescence properties of Ce³⁺ in La₃F₃[Si₃O₉] are reported. Excitation and emission bands corresponding to 4f¹→5d¹ transitions of Ce³⁺ were identified. The center of gravity of the 5d states lies at remarkable high energy (43.2×10³ cm⁻¹) for Ce³⁺ in a silicate compound. This high value is attributed to the combined oxygen/fluoride coordination of the Ce³⁺ ion. Emission from the lowest 4f5d level to the ²F_5/2 and ²F_7/2 levels was found at 32.4×10³ and 30.4×10³ cm⁻¹. These results are compared with literature data on silicates and fluorides. From the values found for Ce³⁺, predictions are made for the positions of the 4f5d bands of Pr³⁺ and Er³⁺ in La₃F₃[Si₃O₉]. For both ions, it is concluded that in this host lattice emission is expected from high lying 4fⁿ energy levels.