We examine the reach of a Beta-beam experiment with two detectors at carefully chosen baselines for exploring neutrino mass parameters. Locating the source at CERN, the two detectors and baselines are: (a) a 50 kton iron calorimeter (ICAL) at a baseline of around 7150 km which is roughly the magic baseline, e.g., ICAL@INO, and (b) a 50 kton Totally Active Scintillator Detector at a distance of 730 km, e.g., at Gran Sasso. We choose ⁸B and ⁸Li source ions with a boost factor γ of 650 for the magic baseline while for the closer detector we consider ¹⁸Ne and ⁶He ions with a range of Lorentz boosts. We find that the locations of the two detectors complement each other leading to an exceptional high sensitivity. With γ=650 for ⁸B/⁸Li and γ=575 for ¹⁸Ne/⁶He and total luminosity corresponding to 5×(1.1×10¹⁸) and 5×(2.9×10¹⁸) useful ion decays in neutrino and antineutrino modes respectively, we find that the two-detector set-up can probe maximal CP violation and establish the neutrino mass ordering if sin²2θ₁₃ is 1.4×10⁻⁴ and 2.7×10⁻⁴, respectively, or more. The sensitivity reach for sin²2θ₁₃ itself is 5.5×10⁻⁴. With a factor of 10 higher luminosity, the corresponding sin²2θ₁₃ reach of this set-up would be 1.8×10⁻⁵, 4.6×10⁻⁵ and 5.3×10⁻⁵ respectively for the above three performance indicators. CP violation can be discovered for 64% of the possible δ_CP values for sin²2θ₁₃10⁻³ (8×10⁻⁵), for the standard luminosity (10 times enhanced luminosity). Comparable physics performance can be achieved in a set-up where data from CERN to INO@ICAL is combined with that from CERN to the Boulby mine in United Kingdom, a baseline of 1050 km.     

Effect of oxygen partial pressure on the structural and optical properties of dc reactive magnetron sputtered molybdenum oxide films

Molybdenum oxide films (MoO₃) were deposited on glass and crystalline silicon substrates by sputtering of molybdenum target under various oxygen partial pressures in the range 8 × 10⁻⁵–8 × 10⁻⁴ mbar and at a fixed substrate temperature of 473 K employing dc magnetron sputtering technique. The influence of oxygen partial pressure on the composition stoichiometry, chemical binding configuration, crystallographic structure and electrical and optical properties was systematically studied. X-ray photoelectron spectra of the films formed at 8 × 10⁻⁵ mbar showed the presence of Mo⁶⁺ and Mo⁵⁺ oxidation states of MoO₃ and MoO_3−x. The films deposited at oxygen partial pressure of 2 × 10⁻⁴ mbar showed Mo⁶⁺ oxidation state indicating the films were nearly stoichiometric. It was also confirmed by the Fourier transform infrared spectroscopic studies. X-ray diffraction studies revealed that the films formed at oxygen partial pressure of 2 × 10⁻⁴ mbar showed the presence of (0 k 0) reflections indicated the layered structure of α-phase MoO₃. The electrical conductivity of the films decreased from 3.6 × 10⁻⁵ to 1.6 × 10⁻⁶ Ω⁻¹ cm⁻¹, the optical band gap of the films increased from 2.93 to 3.26 eV and the refractive index increased from 2.02 to 2.13 with the increase of oxygen partial pressure from 8 × 10⁻⁵ to 8 × 10⁻⁴ mbar, respectively.     

Search for supermassive magnetic monopoles with the MACRO detector at the gran sasso laboratory

We present the results of the search for supermassive magnetic monopoles with the MACRO experiment. Our detector is equipped with three independent subdetectors (liquid scintillation counters, limited streamer tubes and nuclear track detectors), operating in different ranges of monopole velocity. In several years of data taking no candidates were found; the present flux upper limits are the level of half the Parker Bound for β > 10⁻⁴; for 10⁻⁴ < β < 5 × 10⁻² the limit is the best existing.     

Electron stimulated desorption of CO from

The electron impact behavior of CO adsorbed on was investigated. The desorption products observed were neutral CO, CO⁺, and O⁺. After massive electron impact residual carbon, C/W = 0.15, but not oxygen was also found, suggesting that energetic neutral O, not detected in a mass analyzer must also have been formed. Formation of β-CO, i.e., dissociated CO with C and O on the surface was not seen. The total disappearance cross section varies only slightly with coverage, ranging from 9 × 10 ⁻¹⁸ cm² at low to 5 × 10⁻¹⁸ cm² at saturation (CO/W = 0.75). The cross section for CO⁺ formation varies from 4 × 10⁻²² cm² at satura to 2 × 10⁻²¹ cm² at low coverage. That for O⁺ formation is 1.4 × 10⁻²² cm² at saturation and 2 × 10⁻²¹ cm² Threshold energies are similar to those found previously [J.C. Lin and R. Gomer, Surf. Sci. 218 (1989) 406] for and CO/Cu₁/W(110) which suggests similar mechanisms for product formation, with the exception of β-CO on clean W(110). It is argued that the absence or presence of β-CO in ESD hinges on its formation or absence in thermal desorption, since electron impact is likely to present the surface with vibrationally and rotationally activated CO in all cases; β-CO formation only occurs on surfaces which can dissociate such CO. It was also found that ESD of CO led to a work function increase of the remaining Pd₁/W(110) surface of 500 meV, which could be annealed out only at 900 K. This is attributed to surface roughness, caused by recoil momentum of energetic desorbing entities.     

Analysis of the 2ν3 band of CD3F at 5.06 μm recorded under high resolution

The 2ν₃(A₁) band of ¹²CD₃F near 5.06 μm has been recorded with a resolution of 20–24 × 10⁻³ cm⁻¹. The value of the parameter (α^B − α^A) for this band was found to be very small and, therefore, the K structure of the R(J) and P(J) manifolds was unresolved for J < 15 and only partially resolved for larger J values. The band was analyzed using standard techniques and values for the following constants determined: ν₀ = 1977.178(3) cm⁻¹, B″ = 0.68216(9) cm⁻¹, D″_J = 1.10(30) × 10⁻⁶ cm⁻¹, α^B = (B″ − B′) = 3.086(7) × 10⁻³ cm⁻¹, and β^J = (D″_J − D′_J) = −3.24(11) × 10⁻⁷ cm⁻¹. A value of α^A = (A″ − A′) = 2.90(5) × 10⁻³ cm⁻¹ has been obtained through band contour simulations of the R(J) and P(J) multiplets.     

Volatile metal β-diketonates — new precursors for the sonochemical synthesis of nanosized materials — sonolysis of thorium(IV) β-diketonates

Ultrasonic irradiation (22 kHz, Ar atmosphere) of Th(IV) β-diketonates Th(HFAA)₄ and Th(DBM)₄, where HFAA and DBM are hexafluoroacetylacetone and dibenzoylmethane respectively, causes them to decompose in hexadecane solutions, forming solid thorium compounds. The first-order rate constants for Th(IV) β-diketonate degradation were found to be (9.3±0.8)×10⁻³ for Th(HFAA)₄ and (3.8±0.4)×10⁻³ min⁻¹ for Th(DBM)₄, (T=92°C, I=3 W cm⁻²). The rate of the sonochemical reaction increased with the rising β-diketonate volatility and decreased with the rising hydrocarbon solvent vapor pressure. Solid sonication products consisted of a mixture of thorium carbide ThC₂ and Th(IV) β-diketonate partial degradation products. The average ThC₂ particle size was estimated to be about 2 nm. ThC₂ formation was attributed to the high-temperature reaction occurring within the cavitating bubble. The thorium β-diketonate partial degradation products formed in the liquid reaction zones surrounding the cavitating bubbles.     

Elementary reactions of formyl (HCO) radical studied by laser photolysis—transient absorption spectroscopy

Several elementary reactions of formyl radical of combustion importance were studied using pulsed laser photolysis coupled to transient UV–Vis absorption spectroscopy: HCO → H + CO (1), HCO + HCO → products (2), and HCO + CH₃ → products (3). One-pass UV absorption, multi-pass UV absorption as well as cavity ring-down spectroscopy in the red spectral region were used to monitor temporal profiles of HCO radical. Reaction (1) was studied over the buffer gas (He) pressure range 0.8–100 bar and the temperature range 498–769 K. Reactions (2a), (2b), (2c), (3a) and (3b) as well as the UV absorption spectrum of HCO, were studied at 298 and 588 K, and the buffer gas (He) pressure of 1 bar. Pulsed laser photolysis (308, 320, and 193 nm) of acetaldehyde, propionaldehyde, and acetone was used to prepare mixtures of free radicals. The second-order rate constant of reaction (1) obtained from the data at 1 bar is: k₁(He) = (0.8 ± 0.4) × 10⁻¹⁰exp(−(66.0 ± 3.4) kJ mol⁻¹/RT) cm³ molecule⁻¹ s⁻¹. The HCO dissociation rate constants measured in this work are lower than those reported in the previous direct work. The difference is a factor of 2.2 at the highest temperature of the experiments and a factor of 3.5 at the low end. The experimental data indicate pressure dependence of the rate constant of dissociation of formyl radical 1, which was attributed to the early pressure fall-off expected based on the theory of isolated resonances. The UV absorption spectrum of HCO was revised. The maximum absorption cross-section of HCO is (7.3 ± 1.2) × 10⁻¹⁸ cm² molecule⁻¹ at 230 nm (temperature independent within the experimental error). The measured rate constants for reactions (2a), (2b), (2c), (3a) and (3b) are: k₂ = (3.6 ± 0.8) × 10⁻¹¹ cm³ molecule⁻¹ s⁻¹ (298 K); k₃ = (9.3 ± 2.3) × 10⁻¹¹ cm³ molecule⁻¹ s⁻¹(298 and 588 K).     

Rotational absorption spectrum of methylene fluoride in the 20–100 cm region

The pure rotational spectrum of CH₂F₂ was recorded in the 20–100 cm⁻¹ spectral range and analyzed to obtain rotation and centrifugal distortion constants. Analysis of the data yielded rotation constants: A = 1.6392173 ± 0.0000015, B = 0.3537342 ± 0.00000033, C = 0.3085387 ± 0.00000027, τ_aaaa = −(7.64 ± 0.46) × 10⁻⁵, τ_bbbb = −(2.076 ± 0.016) × 10⁻⁶, τ_cccc = −(9.29 ± 0.12) × 10⁻⁷, T₁ = (4.89 ± 0.20) × 10⁻⁶, and T₂ = −(1.281 ± 0.016) × 10⁻⁶cm⁻¹.     

Fourier Transform Spectroscopy of theYΣ–XΠiTransition of CuO

TheY²Σ⁺–X²Π_inear-infrared electronic transition of CuO was observed at high resolution for the first time. The spectrum was recorded with the Fourier transform spectrometer associated with the McMath–Pierce Solar Telescope at Kitt Peak. The excited CuO molecules were produced in a low pressure copper hollow cathode sputter with a slow flow of oxygen. Constants for theY²Σ⁺states of CuO are:T₀= 7715.47765(54) cm⁻¹,B= 0.4735780(28) cm⁻¹,D= 0.822(12) × 10⁻⁶cm⁻¹,H= 0.46(10) × 10⁻¹⁰cm⁻¹, γ = −0.089587(42) cm⁻¹, γ_D= 0.1272(79) × 10⁻⁶cm⁻¹,b_F= 0.12347(22) cm⁻¹, andc= 0.0550(74) cm⁻¹. ImprovedX²Π_iconstants are also presented.     

Structural properties of 10 μm thick InN grown on sapphire (0001)

The structural properties of a 10 μm thick In-face InN film, grown on Al₂O₃ (0001) by radio-frequency plasma-assisted molecular beam epitaxy, were investigated by transmission electron microscopy and high resolution x-ray diffraction. Electron microscopy revealed the presence of threading dislocations of edge, screw and mixed type, and the absence of planar defects. The dislocation density near the InN/sapphire interface was 1.55×10¹⁰ cm⁻², 4.82×10⁸ cm⁻² and 1.69×10⁹ cm⁻² for the edge, screw and mixed dislocation types, respectively. Towards the free surface of InN, the density of edge and mixed type dislocations decreased to 4.35×10⁹ cm⁻² and 1.20×10⁹ cm⁻², respectively, while the density of screw dislocations remained constant. Using x-ray diffraction, dislocations with screw component were found to be 1.2×10⁹ cm⁻², in good agreement with the electron microscopy results. Comparing electron microscopy results with x-ray diffraction ones, it is suggested that pure edge dislocations are neither completely randomly distributed nor completely piled up in grain boundaries within the InN film.     

Recrystallization of germanium surfaces by femtosecond laser pulses

The damage morphology of germanium surfaces using femtosecond laser pulses of various fluences and number of pulses is reported. The single pulse damage threshold in the present experiment was 9.7±4.0×10⁻¹³ W/cm². The experimental threshold value was compared with theory, considering the damage threshold as the melting threshold. The cooling rate calculated on the basis of present results is 2.4×10^15°C/s. Recrystallization was the common feature of the damage morphology. For fluences greater than the single pulse damage-threshold micropits and spherical grains of micron size were formed in the damaged surface. Ablation (surface removal) was also observed at higher fluences (at two or three times of damage threshold value). The damage morphology, induced by multiple pulses, was unaffected for linear and circular polarization.     

Nonlinear optical properties of Cu nanocluster composite fabricated by 180 keV ion implantation

Metal nanocluster composite glass prepared by 180 keV Cu ions into silica with dose of 5×10¹⁶ ions/cm² has been studied. The microstructural properties of the nanoclusters has been verified by optical absorption spectra and transmission electron microscopy (TEM). Third-order nonlinear optical properties of the nanoclusters were measured at 1064 and 532 nm excitations using Z-scan technique. The nonlinear refraction index, nonlinear absorption coefficient, and the real and imaginary parts of the third-order nonlinear susceptibility were deduced. Results of the investigation of nonlinear refraction by the off-axis Z-scan configuration were presented and the mechanisms responsible for the nonlinear response were discussed. Third-order nonlinear susceptibility χ⁽³⁾ of this kind of sample was determined to be 8.7×10⁻⁸ esu at 532 nm and 6.0×10⁻⁸ esu at 1064 nm, respectively.     

Effect of fluorine doping on highly transparent conductive spray deposited nanocrystalline tin oxide thin films

The undoped and fluorine doped thin films are synthesized by using cost-effective spray pyrolysis technique. The dependence of optical, structural and electrical properties of SnO₂ films, on the concentration of fluorine is reported. Optical absorption, X-ray diffraction, scanning electron microscope (SEM) and Hall effect studies have been performed on SnO₂:F (FTO) films coated on glass substrates. The film thickness varies from 800 to 1572 nm. X-ray diffraction pattern reveals the presence of cassiterite structure with (2 0 0) preferential orientation for FTO films. The crystallite size varies from 35 to 66 nm. SEM and AFM study reveals the surface of FTO to be made of nanocrystalline particles. The electrical study reveals that the films are degenerate and exhibit n-type electrical conductivity. The 20 wt% F doped film has a minimum resistivity of 3.8 × 10⁻⁴ Ω cm, carrier density of 24.9 × 10²⁰ cm⁻³ and mobility of 6.59 cm² V⁻¹ s⁻¹. The sprayed FTO film having minimum resistance of 3.42 Ω/cm², highest figure of merit of 6.18 × 10⁻² Ω⁻¹ at 550 nm and 96% IR reflectivity suggest, these films are useful as conducting layers in electrochromic and photovoltaic devices and also as the passive counter electrode.     

Experimental determination of CR-39 counting efficiency to α particles to design the holder of a new radon gas dosemeter

To design a new radon gas dosemeter, the knowledge of the SSNTD α counting efficiency is essential. It depends primarily on the energy and incidence angle into the detector, then on the etching conditions and finally on the track counting procedure. Therefore the elicited efficiency function represents all these factors. The detectors were exposed to α particles at different angles of incidence and energies, by using a ²⁴⁴Cm source; two alternative NaOH solution etching conditions were tested, 6.25 N 70°C at 6 and 12 h, respectively. The counting was performed with a light microscope, 267×, and with an automatic track analysis procedure. The critical incidence angle dependance on energy, in our standard condition (6 h), resulted θ_C(E)=380.0e^{(−0.286•(E−0.050))}(1−e^{(−0.186•(E−0.050))}), and it was used to design our new radon gas holder.     

The bending energy levels of C2H2

Absorption spectra of C₂H₂ have been recorded between 50 and 1450 cm⁻¹, with a resolution always better than 0.005 cm⁻¹, using two different Fourier transform spectrometers. Analysis of the data provided two sets of results. First, the bending levels with Σ_t V_t(t = 4, 5) ≤ 2 were characterized by a coherent set of 34 parameters derived from the simultaneous analysis of 15 bands, performed using a matrix Hamiltonian. The following main parameters were obtained (in cm⁻¹): ω₄⁰ = 608.985196(14), ω₅⁰ = 729.157564(10); B₀ = 1.17664632(18), α₄ = −1.353535(86) × 10⁻³, α₅ = −2.232075(40) × 10⁻³; q₄⁰ = 5.24858(12) × 10⁻³, and q₅⁰ = 4.66044(12) × 10⁻³, with the errors (1σ) on the last quoted digit. Second, a more complete set of bending levels with Σ_t V_t ≤ 4, some of which have never previously been reported, and also including V₂ = 1 have been fitted to 80 parameters. This simultaneous fit involved 43 bands and used the same full Hamiltonian matrix. Some perturbations which affect the higher excited levels are discussed.     

Electrical conductivity of Ag/Na ion-exchanged titanosilicate glasses

The Ag₂O–TiO₂–SiO₂ glasses were prepared by Ag⁺/Na⁺ ion-exchange method from Na₂O–TiO₂–SiO₂ glasses at 380–450 °C below their glass transition temperatures (T_g), and their electrical conductivities were investigated as functions of TiO₂ content and the ion-exchange ratio (Ag/(Ag+Na)). In a series of glasses 20R₂O·xTiO₂·(80−x)SiO₂ with x=10, 20, 30 and 40 in mol%, the electrical conductivities at 200 °C of the fully ion-exchanged glasses of R=Ag were in the order of 10⁻⁵ or 10⁻⁴ S cm⁻¹ and were 1 or 2 orders of magnitude higher than those of the initial glasses of R=Na. The glass of x=30 exhibited the highest increase of conductivity from 3.8×10⁻⁷ to 1.3×10⁻⁴ S cm⁻¹ at 200 °C by Ag⁺/Na⁺ ion exchange among them. When the ion-exchange ratio was changed in 20R₂O·30TiO₂·50SiO₂ system, the electrical conductivity at 200 °C exhibited a minimum value of 7.6×10⁻⁸ S cm⁻¹ around Ag/(Ag+Na)=0.3 and increased steeply in the region of Ag/(Ag+Na)=0.5–1.0. When the ion-exchange temperature was changed from 450 to 400 °C, the conductivity of the ion-exchanged glass of x=30 decreased. The infrared spectroscopy measurement revealed that the ion-exchange temperature of 450 °C induced a structural change in the glass of x=30. The T_g of the fully ion-exchanged glass of x=30 was 498 °C. It was suggested that the incorporated silver ions changed the average coordination number of titanium ions to form higher ion-conducting pathway and resulted in high conductivity in the titanosilicate glasses.     

Low resistance nonalloyed Al-based ohmic contacts on n-ZnO:Al

We have investigated the electrical properties of nonalloyed Al, Al/Au, and Al/Pt ohmic contacts on n-type ZnO:Al (2×10¹⁸ cm⁻³). All Al-based nonalloyed ohmic contacts on the n-ZnO:Al reveal linear current–voltage behavior with low specific contact resistivity of 8.5×10⁻⁴ (Al), 8.0×10⁻⁵ (Al/Au) and 1.2×10⁻⁵ Ω cm² (Al/Pt), respectively. Using secondary ion mass spectroscopy (SIMS) and x-ray photoelectron spectroscopy (XPS) depth profiles, it was found that the O atoms in the ZnO:Al layer outdiffused to Al metal layer while the Al atoms indiffused to the surface region of ZnO:Al. This interdiffusion between Al and O atoms at room temperature results in an increase of doping concentration in the surface region of the ZnO:Al and reduces a specific contact resistivity of the Al-based ohmic contacts without thermal annealing process.     

High Resolution Study of Deuterated Hydrogen Sulfide in the Region 2400-3000 cm

High resolution Fourier transform spectra of deuterated hydrogen sulfide have been recorded in the region 2400-3000 cm⁻¹. Rotational structures of the ν₁ + ν₂, ν₂ + ν₃ bands of D₂³²S, of the ν₃ and ν₁ + ν₂ bands of HD³²S, and of the ν₁ + ν₂ band of HD³⁴S were analyzed. Band centers and rotational, centrifugal distortion, and resonance parameters were obtained, which reproduce the initial values of the upper energy levels within a mean accuracy of 1.39 × 10⁻⁴ cm⁻¹ for the states (110) and (011) of D₂³²S, 1.61 × 10⁻⁴ cm⁻¹ and 1.82 × 10⁻⁴ cm⁻¹ for the states (001) and (110) of HD³²S, and 2.09 × 10⁻⁴ cm⁻¹ for the state (110) of HD³⁴S, respectively.     

Polarization spectroscopy of ion-pair states of ICl

Molecular constants for the E0⁺(³P₂) and 1(³P₂) ion-pair states of ICl vapor have been determined using sequential two-photon polarization-labeling spectroscopy. The two states are coupled by a heterogeneous perturbation which is analyzed in some detail for low-lying vibrational levels of 1(³P₂). The I³⁵Cl potential constants for the 1(³P₂) state and the rotation-vibration constants for the set of f sublevels—i.e., the constants unaffected by coupling with the E state—are (in cm⁻¹) 1(³P₂): Y_0,0= 39103.814(32), Y_1,0= 170.213(15), Y_2,0= −0.4528(22), Y_3,0= −7.0(12) × 10⁻⁴, Y_4,0= −1.48(24) × 10⁻⁵ and Y_5,0= −6.6(19) × 10⁻⁸, Y^(f)_0,1= 5.6878(17) × 10⁻² Y^(f)_1,1= −2.110(24) × 10⁻⁴, Y^(f)_2,1= −1.23(62) × 10⁻⁷, and Y^(f)_0,1= −3.08(22) × 10⁻⁸Likewise, the I³⁵Cl constants determined for the E 0⁺(³P₂) state are E 0⁺(³P₂: Y_0,0= 39054.38(61), Y_1,0= 166.96(10), Y_2,0 = −0.3995(42), Y_0,1= 5.738(31) × 10⁻², and Y_1,1= −1.67(26) × 10⁻⁴Practical constraints in pumping the sequence E 0⁺ ← B 0⁺ ← × 0⁺ restrict the analysis of the E state to levels v = 9–15. Given the long extrapolation to the equilibrium state the 3σ statistical uncertainties quoted for these constants should be treated with caution.     

Spectral characterization and energy levels of Cr:Sc2(MoO4)3 crystal

This paper reports the spectral properties and energy levels of Cr³⁺:Sc₂(MoO₄)₃ crystal. The crystal field strength Dq, Racah parameter B and C were calculated to be 1408 cm⁻¹, 608 cm⁻¹ and 3054 cm⁻¹, respectively. The absorption cross sections σ_α of ⁴A₂→⁴T₁ and ⁴A₂→⁴T₂ transitions were 3.74×10⁻¹⁹ cm² at 499 nm and 3.21×10⁻¹⁹ cm² at 710 nm, respectively. The emission cross section σ_e was 375×10⁻²⁰ cm² at 880 nm. Cr³⁺:Sc₂(MoO₄)₃ crystal has a broad emission band with a broad FWHM of 176 nm (2179 cm⁻¹). Therefore, Cr³⁺:Sc₂(MoO₄)₃ crystal may be regarded as a potential tunable laser gain medium.