Spectroscopic studies of interfacial structures of CeO2-TiO2 mixed oxides

We have investigated the geometric and electronic structures of the cerium oxide (CeO₂)-titanium dioxide (TiO₂) mixed oxides with various Ce/TiO₂ weight ratios prepared by the sol-gel method in detail by means of X-ray diffraction (XRD), high-resolution X-ray photoelectron spectroscopy (XPS), Raman spectroscopy excited by 325 and 514.5 nm lasers, and scanning electron microscope (SEM). Existence of cerium effectively inhibits the phase transition of TiO₂ from the anatase phase to the rutile phase. XRD peaks of TiO₂ anatase attenuate continuously with the increasing amount of CeO₂ in the mixed oxide, but the XRD peaks of cubic CeO₂ appear only after the weight ratio of Ce/TiO₂ reaches 0.50. The average crystalline sizes of TiO₂ anatase and cubic CeO₂ in CeO₂-TiO₂ mixed oxides are smaller than those in the corresponding individual TiO₂ anatase and cubic CeO₂. Raman spectroscopy excited by the 514.5 nm laser detects CeO₂ after the weight ratio of Ce/TiO₂ reaches 0.70 whereas Raman spectroscopy excited by the 325 nm laser detects CeO₂ after the weight ratio of Ce/TiO₂ reaches 0.90. XPS results demonstrate that Ti exists in the form of Ti⁴⁺ in the CeO₂-TiO₂ mixed oxide. Ce is completely in the form of Ce³⁺ in the mixed oxides with a 0.05 weight ratio of Ce/TiO₂. With the increasing weight ratio of Ce/TiO₂, Ce⁴⁺ dominates. On basis of these results, we proposed that CeO₂ initially nucleates at the defects (oxygen vacancies) within TiO₂ anatase, forming an interface bridged with oxygen between CeO₂ and TiO₂ anatase. At the interface, Ce species cannot substitute Ti⁴⁺ in the lattice of TiO₂ anatase whereas Ti⁴⁺ can substitute Ce⁴⁺ in the lattice of cubic CeO₂. The decreasing concentration of oxygen vacancies, the Ti-O-Ce interface, and the decreasing average crystalline size of TiO₂ anatase act to inhibit the phase transformation of TiO₂ anatase. With the increasing amounts of CeO₂, the CeO₂ clusters continuously grow and form cubic CeO₂ nanocrystals. Spectroscopic results strongly demonstrate that the surface region of CeO₂-TiO₂ mixed oxide is enriched with TiO₂.     

Reactivity and XAFS study on (1−x)CeO2-xNiO (x=0.025-0.3) system in the two-step water-splitting reaction for solar H2 production

The redox reaction of Ce⁴⁺-Ce³⁺ promoted by the catalytic function of nickel ions in a (1−x)CeO₂-xNiO solid solution was investigated for solar H₂ production by the two-step water-splitting reaction. By irradiation using an infrared imaging lamp as a solar simulator, the O₂-releasing reaction with (1−x)CeO₂-xNiO solid solution proceeded at 1673-1873 K, and its reduced form was produced. The amounts of H₂ gas evolved by the reduced form were 1.2-2.5 cm³/g and the evolved gases amounts ratio of H₂/O₂ was nearly 2, which is equal to the stoichiometric value of the water-splitting reaction (H₂O=H₂+1/2O₂). The maximum amounts of evolved H₂ and O₂ gases were obtained at the Ce:Ni mole ratio of 0.95:0.05 (x=0.05) in the (1−x)CeO₂-xNiO system. The X-ray absorption fine structure (XAFS) measurement showed that the O₂-releasing and H₂-generation reactions with (1−x)CeO₂-xNiO solid solution were repeatable with the redox system of Ce⁴⁺-Ce³⁺, which was enhanced by the catalytic function of Ni²⁺-Ni⁰.     

Synthesis of (Ca,Ce,Ce)2Ti2O7: a pyrochlore with mixed-valence cerium

Pyrochlore with mixed-valence Ce was synthesized by firing and annealing Ce(NO₃)₄, TiO₂, and Ca(OH)₂ with a stoichiometry of CaCeTi₂O₇ at 1300 °C. The product contains Ce-pyrochlore, Ce-rich perovskite, CeO₂ (cerianite), and minor CaO. Electron energy-loss spectroscopy (EELS) revealed both Ce⁴⁺ and Ce³⁺ in the Ce-pyrochlore with a Ce⁴⁺ to total Ce (Ce⁴⁺/ΣCe) of 0.80 giving . Cerium in the perovskite and cerianite is dominated by Ce³⁺ and Ce⁴⁺, respectively. High-resolution transmission electron microscope (HRTEM) images show that the boundary between Ce-pyrochlore and Ce-rich perovskite is semi-coherently bonded. The orientational relationship between the neighboring Ce-pyrochlore and Ce-rich perovskite is not random. Ce-pyrochlore (CaCeTi₂O₇) is a chemical analogue for CaPuTi₂O₇, which is a proposed ceramic waste form for deposition of excess weapons-usable Pu in geological repositories. It is postulated, based on the presence of Ce³⁺ in the Ce-pyrochlore, that neutron poisons such as Gd can be incorporated into the CaPuTi₂O₇ phase.     

Variations in the structural, optical and electrochemical properties of CeO2-TiO2 films as a function of TiO2 content

Alcohol based sols of cerium chloride (CeCl₃·7H₂O) and titanium propoxide (Ti(OPr)₄) in ethanol mixed in different mole ratios have yielded mixed oxide films on densification at 500 °C. The reversibility of the intercalation/deintercalation reactions has shown electrochemical stability of the films. Addition of TiO₂ in an equivalent mole ratio manifests in producing highly transparent films with appreciable ion storage capacity. The electrochemical studies have revealed the significant role of TiO₂ in controlling the ion storage capacity of the films, as it tends to induce the disorder. In addition, the films prepared from an aged sol are observed to exhibit a much higher ion storage capacity than the films deposited using the as-prepared sol. The X-ray photoelectron spectroscopic studies have provided information on the variation of Ce⁴⁺/Ce³⁺ ratio as a function of increased TiO₂ content in the films. This study has led to a better understanding of the increased ion storage capacity with the increased TiO₂ proportion. The transmission electron microscopic study has demonstrated the presence of CeO₂ nanograins even in films, which are amorphous to X-rays. Elucidation of the structural, optical and electrochemical features of the films has yielded information on aspects relevant to their usage in transmissive electrochromic devices. The films have been found to exhibit properties that can find application as counter electrode in electrochromic smart windows in which they are able to retain their transparency under charge insertion, high enough for practical uses. Also, the fastest coloration-bleaching kinetics for the primary electrochromic electrode (WO₃) working in combination with Ce/Ti (1:1) electrode stimulates the use of latter in electrochromic windows (ECWs).     

Electrical conductivity of (Er,U)O2+x and (Ce,U)O2+x

The electrical conductivity (σ) of (Er_yU_1−y)O_2+x (y=0.06, 0.20) and (Ce_yU_1−y)O_2+x (y=0.05, 0.15, 0.25) has been measured as a function of oxygen partial pressure in the temperature range of 1100≤T/°C≤1300 by a d.c. 4-probe method. Both of the oxides exhibited Po₂-regions where the electrical conductivity is independent of oxygen partial pressure, which indicates that doped Er and Ce exist as trivalent cations on uranium sites and fix the hole concentration by acting as electron acceptors, i.e. [h]=[Er′_U] and [h]=[Ce′_U], respectively. It is considered that strong oxidization tendency of uranium and reduction tendency of cerium simultaneously render the cerium ions exist exclusively as Ce³⁺ in the uranium dioxide. The electron-hole mobility of (Er_yU_1−y)O_2+x and (Ce_yU_1−y)O_2+x in the Po₂ region where σ is constant has been calculated by the combination of the electrical conductivity and charge carrier concentration; the activation energy (E_H) of each oxide has been obtained from the temperature dependence of the mobility. Small polaron hopping conduction mechanism was confirmed by small magnitude of the mobility (0.018-0.052 cm² V⁻¹ s⁻¹) and the activation energy (0.12-0.22 eV).     

Reaction of water with Ce-Au(1 1 1) and CeOx/Au(1 1 1) surfaces: Photoemission and STM studies

This article reports photoemission and STM studies for the adsorption and dissociation of water on Ce-Au(1 1 1) alloys and CeO_x/Au(1 1 1) surfaces. In general, the adsorption of water at 300 K on disordered Ce-Au(1 1 1) alloys led to O-H bond breaking and the formation of Ce(OH)_x species. Heating to 500-600 K induced the decomposition or disproportionation of the adsorbed OH groups, with the evolution of H₂ and H₂O into gas phase and the formation of Ce₂O₃ islands on the gold substrate. The intrinsic Ce ↔ H₂O interactions were explored by depositing Ce atoms on water multilayers supported on Au(1 1 1). After adsorbing Ce on ice layers at 100 K, the admetal was oxidized immediately to yield Ce³⁺. Heating to room temperature produced finger-like islands of Ce(OH)_x on the gold substrate. The hydroxyl groups dissociated upon additional heating to 500-600 K, leaving Ce₂O₃ particles over the surface. On these systems, water was not able to fully oxidize Ce into CeO₂ under UHV conditions. A complete Ce₂O₃ → CeO₂ transformation was seen upon reaction with O₂. The particles of CeO₂ dispersed on Au(1 1 1) did not interact with water at 300 K or higher temperatures. In this respect, they exhibited the same reactivity as does a periodic CeO₂(1 1 1) surface. On the other hand, the Ce₂O₃/Au(1 1 1) and CeO_2−x/Au(1 1 1) surfaces readily dissociated H₂O at 300-500 K. These systems showed an interesting reactivity for H₂O decomposition. Water decomposed into OH groups on Ce₂O₃/Au(1 1 1) or CeO_2−x/Au(1 1 1) without completely oxidizing Ce³⁺ into Ce⁴⁺. Annealing over 500 K removed the hydroxyl groups leaving behind CeO_2−x/Au(1 1 1) surfaces. In other words, the activity of CeO_x/Au(1 1 1) for water dissociation can be easily recovered. The behavior of gold-ceria catalysts during the water-gas shift reaction is discussed in light of these results.     

A resonant photoemission study of the Ce and Ce-oxide/Pd(1 1 1) interfaces

We have investigated the Ce 4f electronic states in the Ce/Pd(1 1 1) and Ce-oxide/Pd(1 1 1) systems, using resonant photoemission (Ce 4d → 4f transitions), and XPS to understand Pd-Ce interactions in ultra thin layers of cerium and ceria deposited on Pd(1 1 1). Cerium deposited on Pd(1 1 1) at room temperature forms surface Ce-Pd alloys with Ce rich character, while a Pd rich Ce-Pd alloy is formed by heating to 700 °C. A modification of the chemical state of Ce can also be seen after oxygen exposure. RPES provides evidence that Ce-oxide layers deposited on Pd(1 1 1) have a CeO₂ (Ce⁴⁺) character, however a net contribution of the Ce³⁺ states is also revealed. The Ce³⁺ states have surface character and are accompanied by oxygen vacancies. Heating to 600 °C causes Ce-oxide reduction. A significant shift of Pd 4d-derived states, induced by Pd 4d and Ce 4f hybridization, was observed. The resonant features in the valence band corresponding to Ce⁴⁺, Ce³⁺ and Ce⁰ states have been investigated for various Pd−Ce(CeO_x) coverages.     

In-situ XAS study on the Cu and Ce local structural changes in a CuO-CeO2/Al2O3 catalyst under propane reduction and re-oxidation

The redox behaviour of a CuO-CeO₂/Al₂O₃ catalyst is studied under propane reduction and re-oxidation. The evolution of the local Cu and Ce structure is studied with in-situ transmission X-ray absorption spectroscopy (XAS) at the Cu K and Ce L₃ absorption edges.CuO and CeO₂ structures are present in the catalyst as such. No structural effect on the local Cu structure is observed upon heating in He up to 873 K or after pre-oxidation at 423 K.Exposure to propane at reaction temperature (600-763 K) fully reduces the Cu²⁺ cations towards metallic Cu⁰. Quick EXAFS spectra taken during reduction show a small amount of intermediate Cu¹⁺ species. Parallel to the CuO reduction, CeO₂ is also reduced in the same temperature range. About 25% of the Ce⁴⁺ reduces rapidly to Ce³⁺ in the 610-640 K temperature interval, while beyond 640 K a further slower reduction of Ce⁴⁺ to Ce³⁺ occurs. At 763 K, Ce reduction is still incomplete with 32% of Ce³⁺.Re-oxidation of Cu and Ce is fast and brings back the original oxides.The propane reduction of the CuO-CeO₂/Al₂O₃ catalyst involves both CuO and CeO₂ reduction at similar temperatures, which is ascribed to an interaction between the two compounds.     

The surface properties and the activities in catalytic wet air oxidation over CeO2-TiO2 catalysts

No-noble metal CeO₂-TiO₂ catalysts prepared by sol-gel method were developed and examined for catalytic wet air oxidation (CWAO) of acetic acid. The structure of the catalysts was measured by BET, SEM, XRD, XPS and DTA-TG. We investigated the effect of the interactions of Ce and Ti on the structure of CeO₂-TiO₂ catalysts. The mechanisms of the relationships between the different content of Ti and the activity of CeO₂-TiO₂ catalysts were discussed. The results showed that the average crystal size of CeO₂ decreased and the surface areas increased; the low valence of Ce³⁺ increase, and the chemisorbed oxygen slightly decreased with the increase of Ti content on the surface of CeO₂-TiO₂ catalysts. The order of the activity in CWAO of acetic acid followed: Ce/Ti 1/1 > Ce/Ti 3/1 > Ce/Ti 1/3 > Ce/Ti 5/1 > CeO₂ > TiO₂ > no catalyst. In CWAO of acetic acid, the optimal atomic ratio of Ce and Ti was 1, and the highest COD removal was over 64% at 230 °C, 5 MPa and 180 min reaction time over Ce/Ti 1/1 catalyst. The excellent activity and stability of CeO₂-TiO₂ catalysts was observed in our study.     

Synthesis,characterization, and ecotoxicity of CeO<Subscript>2</Subscript> nanoparticles with differing properties

CeO₂ nanoparticles with various characteristics find an increasing number of applications in the electronic, medical, and other industries and are therefore likely released in the environment. This calls for investigations linking the physicochemical properties of these particles with their potential environmental impacts. In this study, CeO₂ nanoparticle powders were prepared using three different precursors [Ce(NO₃)₃, CeCl₃, and Ce(CH₃COO)₃] and annealing temperatures (300, 500, and 700 °C). This procedure resulted in nine different types of nanoparticles with differing size (5–90 nm), morphology, surface Ce³⁺/Ce⁴⁺ ratio, and slightly different crystal structures as characterized using transmission electron microscopy, dynamic light scattering, X-ray photoelectron spectroscopy, and X-ray diffraction measurements with Rietveld refinement. These CeO₂ nanoparticles underwent toxicity testing at concentrations up to 64 mg L^?1 using Daphnia magna. Toxic effects were observed for three particle types with EC50 values between 5 and 64 mg L^?1. No clear correlation was observed between the physicochemical properties (size, shape, oxygen occupancy, Ce³⁺/Ce⁴⁺ ratio) of the nanoparticles and their toxicity. However, toxicity was correlated with the amount of Ce remaining suspended in the test medium after 24 h. This indicated that toxic effects may depend on the colloidal stability of CeO₂ nanoparticles during the first day of exposure. Therefore, being readily suspended and remaining stable for several days in the aquatic media increases the likelihood that CeO₂ nanoparticles will cause unwanted adverse effects.     

Low energy Ar-ion bombardment effects on the CeO2 surface

The structure and electronic properties of epitaxial grown CeO₂(1 1 1) thin films before and after Ar⁺ bombardment have been comprehensively studied with synchrotron radiation photoemission spectroscopy (SRPES). Ar⁺ bombardment of the surface causes a new emission appearing at 1.6 eV above the Fermi edge which is related to the localized Ce 4f¹ orbital in the reduced oxidation state Ce³⁺. Under the condition of the energy of Ar ions being 1 keV and a constant current density of 0.5 μA/cm², the intensity of the reduced state Ce³⁺ increases with increasing time of sputtering and reaches a constant value after 15 min sputtering, which corresponds to the surface being exposed to 2.8 × 10¹⁵ ions/cm². The reduction of CeO₂ is attributed to a preferential sputtering of oxygen from the surface. As a result, Ar⁺ bombardment leads to a gradual buildup of an, approximately 0.69 nm thick, sputtering altered layer. Our studies have demonstrated that Ar⁺ bombardment is an effective method for reducing CeO₂ to CeO_2−x and the degree of the reduction is related to the energy and amount of Ar ions been exposed to the CeO₂ surface.     

Formation of alumina-ceria mixed oxide in model systems

Interaction of aluminium with cerium oxide was studied by photoelectron spectroscopy of Al/CeO₂(1 1 1) and CeO₂/Al(1 1 1) model systems. It was found in both cases that metallic aluminium was immediately oxidized, CeO₂ was partially reduced and a mixed oxide with cerium present as Ce³⁺ was formed. The compound is probably cerium aluminate CeAlO₃ mixed with Al₂O₃ or Ce₂O₃. In both cases the intermixing was limited by the diffusion of aluminium into ceria. The excess of deposited material above this limit formed AlO_x and CeO₂ overlayers on the top of the mixed oxide + aluminate/CeO₂ and mixed oxide + aluminate/Al films, respectively.     

First-principles prediction of coexistence of magnetism and ferroelectricity in rhombohedral Bi2FeTiO6

First principles calculations based on the density functional theory within the local spin density approximation plus U(LSDA + U) scheme, show rhombohedral Bi₂FeTiO₆ is a potential multiferroic in which the magnetism and ferroelectricity coexist. A ferromagnetic configuration with magnetic moment of 4μB per formula unit has been reported with respect to the minimum total energy. Spontaneous polarization of 27.3 μC/cm², caused mainly by the ferroelectric distortions of Ti, was evaluated using the berry phase approach in the modern theory of polarization. The Bi-6s stereochemical activity of long-pair and the ‘d⁰-ness’ criterion in off-centring of Ti were coexisting in the predicted new system. In view of the oxidation state of Bi³⁺, Fe²⁺, Ti⁴⁺, and O²⁻ from the orbital-resolved density of states of the Bi-6p, Fe-3d, Ti-3d, and O-2p states, the valence state of Bi₂FeTiO₆ in the rhombohedral phase was found to be Bi³⁺₂Fe²⁺Ti⁴⁺O₆.     

Structure and magnetic properties of (Nd,Dy)16(Fe,Co)76−xTixB8 powders prepared by mechanical alloying

Nanocrystalline (Nd,Dy)₁₆(Fe,Co)_76−xTi_xB₈ magnets were prepared by mechanical alloying and respective heat treatment at 973–1073 K/30–60 min. An addition of 0.5 at % of Ti results in an increase of coercivity from 796 to 1115 kA m⁻¹. Partial substitution of Nd by Dy results in an additional increase of coercivity up to 1234 kA m⁻¹. Mössbauer investigations shows that for x?1 the (Nd,Dy)₁₆(Fe,Co)_76−xTi_xB₈ powders are single phase. For higher Ti contents (x>1) the mechanically alloyed powders heat treated at 973 K are no more single phase, and the coercivity decreases due to the presence of an amorphous phase. A heat treatment at a higher temperature (1073 K) for longer time (1 h) results in the full recrystallisation of powders. The mean hyperfine field of the Nd₂Fe₁₄B phase decreases for titanium contents of 0?x?1, and remains constant for x>1. This indicates that the Ti content in the Nd₂Fe₁₄B phase reaches its maximum value.     

Reduction of thin-film ceria on Pt(111) by supported Pd nanoparticles probed with resonant photoemission

Local defects present in CeO_2 ? x films result in a mixture of Ce³⁺ and Ce⁴⁺ oxidation states. Previous studies of the Ce 3d region with XPS have shown that depositing metal nanoparticles on ceria films causes further reduction, with an increase in Ce³⁺ concentration. Here, we compare the use of XPS and resonant photoemission spectroscopy (RESPES) to estimate the concentration of Ce³⁺ and Ce⁴⁺ in CeO_2 ? x films grown on Pt (111), and the variation of this concentration as a function of Pd deposition. Due to the nature of the electronic structure of CeO_2 ? x, resonant peaks are observed for the 4d–4f transitions when the photon energy matches the resonant energy; (hν = 121.0 eV) for Ce³⁺ and (hν = 124.5 eV) for Ce⁴⁺. This results in two discrete resonant photoemission peaks in valence band spectra. The ratio of the difference of these peaks with off-resonance scans gives an indication of the relative contribution of Ce³⁺. Results from RESPES indicate reduction of CeO_2 ? x on deposition of Pd, confirming earlier findings from XPS studies.     

Investigation on mechanism of photocatalytic activity enhancement of nanometer cerium-doped titania

A series of Ce-TiO₂ are prepared by the sol-gel process with ammonium cerium(IV) nitrate and tetra-n-butyl titanium as raw materials and characterized with XRD, TEM, DRS, and XPS. The aberrance (0.355) of anatase(1 0 1) plane of 0.1% Ce/TiO₂ increases compared to that of TiO₂. Cerium is found to be present as a mixture of Ce^3+/4+ oxidation states, that is, the oxidation state of some cerium in Ce-TiO₂ has changed after calcination. Ce/TiO₂ yields a large red shift compared to TiO₂. Moreover, the reflectance decreases in the visible region after cerium doped on TiO₂, and the lower the reflectance the higher the activity. Cerium appears to enhance the photocatalytic activity of Ce/TiO₂ by suppressing electron-hole recombination with electron trapping at Ce⁴⁺. 0.1% Ce/TiO₂ shows highest activity for the degradation of aqueous suspension of formaldehyde.     

Sn interaction with the CeO2(1 1 1) system: Bimetallic bonding and ceria reduction

A tin layer 0.8 nm thick was deposited onto the CeO₂(1 1 1) surface by molecular beam deposition at a temperature of 520 K. The interaction of tin with cerium oxide (ceria) was investigated by X-ray photoelectron spectroscopy (XPS), ultra-violet photoelectron spectroscopy (UPS) and resonant photoelectron spectroscopy (RPES). The strong tin-ceria interaction led to the formation of a homogeneous bulk Ce-Sn-O mixed oxide system. The bulk compound formation is accompanied by partial Ce⁴⁺ → Ce³⁺ reduction, observed as a giant 4f resonance enhancement of the Ce³⁺ species. CeO₂ and SnO₂ oxides were formed after oxygen treatment at 520 K. The study proved the existence of strong Ce-Sn interaction and charge transfer from Sn to the Ce-O complex that lead to a weakening of the cerium-oxygen bond, and consequently, to the formation of oxygen deficient active sites on the ceria surface. This behavior can be a key for understanding the higher catalytic activity of the SnO_x/CeO_x mixed oxide catalysts as compared with the individual pure oxides.     

Synthesis, structure and luminescence of LaSi3N5:Ce phosphor

In this work, new LaSi₃N₅:Ce³⁺ phosphors have been synthesized by solid-state reaction. Rietveld refinement of the crystal structure of La_1−xCe_xSi₃N₅ reveals that Ce atoms substituted for La atoms occupy 4a crystallographic positions. Broad emission and excitation bands observed were attributed to the transitions between the doublet ground state of the 4f¹ configuration and the crystal field components of the 5d¹ excited state. At 77 K, the centroid and crystal field splitting ε_cfs of the 5d levels of Ce³⁺ in LaSi₃N₅:Ce³⁺ compounds were valuated at 33.4×10³ and 11.3×10³ cm⁻¹, respectively. The zero-phonon line and the Stokes shift were measured to be 26.0×10³ and 5.0×10³ cm⁻¹, respectively.     

Thermodynamic properties of titanium dioxide,niobium dioxide and their solid solutions at high temperature

By means of thermogravimetric measurements, it has been possible to obtain information on the nature of the intrinsic and extrinsic defects of TiO₂, NbO₂ and solid solutions Nb_yTi_1?yO_2±x Pure TiO₂ is an oxygen-deficient oxide The main defects are oxygen vacancies, doubly ionized V^.._o or singly ionized V^._o, and interstitial titanium Ti³_i NbO₂ is a metal-deficient oxide The main defects are neutral niobium vacancies. The solid solutions Nb_yTi_1?yO_2±x may be divided into two groups If y > 0 04, the behavior is analogous to that of NbO₂; with the same defects, but the width of the homogeneity range decreases with the titanium content and Nb_{0 04}Ti_{0 96}O₂ is a stoichiometnc oxide If y < 004, the oxides are both metal deficient and oxygen deficient according to the oxygen partial pressure. We have particularly studied the solution Ti_{0 995}Nb_{0 005}O₂ In the oxygen-deficient domain, the main defects are assumed to be neutral or singly ionized oxygen vacancies In the metal-deficient domain, the main defects are metal vacancies V⁴_Ti From these results we have deduced the nature of intrinsic defects in TiO₂ to be Schottky defects: 2V^.._O + V⁴_T1.     

Spinel-type solid solutions involving Mn and Ti:Crystal chemistry, magnetic and electrochemical properties

This study reports the structural and magnetic properties of spinel systems Li₄Mn_5−xTi_xO₁₂ (“4-5-12” series) and LiNi_0.5Mn_1.5−xTi_xO₄ (“LNMTO” series), both based on Mn⁴⁺ substitution by Ti⁴⁺. Intermediate compositions covering the whole range of compositions (0≤x≤5 and 0≤x≤1.5, respectively) were prepared by solid state reaction. The 4-5-12 system forms a continuous spinel solid solution, whereas the spinel phase range in LNMTO stops before the end member “LiNi_0.5Ti_1.5O₄”, which is multi-phased with a major hexagonal phase component. Cell parameters and (Mn,Ti)-O distances increase monotonically with titanium content in both series. In the LNMTO series, the end member LiNi_0.5Mn_1.5O₄ is known to form a superstructure with Ni/Mn cation ordering. Neutron diffraction and Raman spectroscopy show that this order is lost when Ti is substituted, even at low level (x=0.15). The LNMTO crystal chemistry is also complicated by the presence of partial cation inversion, and the presence of a secondary rocksalt-type phase that modifies the spinel stoichiometry. Magnetic properties are characterized by a competition between ferromagnetic and antiferromagnetic interactions; no magnetic ordering is achieved, in agreement with B-site cation frustration and disorder. Electrochemical measurements show that the Ti^3+/4+ and Mn^3+/4+ redox couples behave independently in the 4-5-12 series, and that titanium decreases the high-potential electrochemical redox activity of LNMTO because of its blocking character for electron transfer to and from the nickel sites in the spinel structure.