Er3+及Er3+/Yb3+掺杂ZrO2-Al2O3的制备及发光性质

采用共沉淀法制备了纳米晶ZrO₂-Al₂O₃∶Er³⁺发光粉体.所制备的粉体室温下具有Er3+离子特征荧光发射,主发射在绿光,其中位于547 nm、560 nm的绿光最强,并得出稀土离子与基质之间有能量传递.对不同煅烧温度下的样品研究表明:因不同温度下所制得的样品晶相不同.研究了纳米晶ZrO2-Al2O3∶Er3+及ZrO₂-Al₂O₃∶Er³⁺/Yb³⁺的上转换发光,并分析了上转换的跃迁机制.发现ZrO₂-Al₂O₃∶Er³⁺的绿光为双光子过程,而ZrO₂-Al₂O₃∶Er³⁺、Yb³⁺的上转换光谱中,红光和绿光也为双光子过程,而极弱的蓝光为三光子过程.讨论了Er³⁺的浓度猝灭现象.最适宜掺杂浓度的原子分数为2%（Er³⁺/Zr⁴⁺）.     

Gd2O3:Eu3+纳米晶的燃烧合成及光致发光性质

采用柠檬酸作燃烧剂用燃烧合成法制备了Gd₂O₃:Eu³⁺纳米晶.用X射线衍射仪(XRD)、高分辨透射电子显微镜(HRTEM)和荧光分光光度计等对Gd₂O₃:Eu³⁺纳米晶的结构、形貌和发光性能进行了分析.结果表明：不同柠檬酸与稀土离子配比(C/M)制备的样品经800℃ 退火1 h后，均得到了纯立方相的Gd₂O₃:Eu³⁺纳米晶，晶粒尺寸约为30 nm，尺寸分布较窄，其中以C/M=1.0时制备的纳米晶结晶性最好，发光强度最大.Gd₂O₃:Eu³⁺纳米晶主发射峰位置均在612 nm处 (⁵D₀→⁷F₂跃迁)，激发光谱中电荷迁移态发生红移，观察到Gd³⁺向Eu³⁺的有效能量传递.对柠檬酸与稀土离子配比(C/M)对结晶度、发光性质等的影响也进行了分析和讨论.     

Er3+/Yb3+共掺Gd3Sc2Ga3O12晶体的上转换发光

研究了提拉法生长的Er³⁺/Yb³⁺:Gd₃Sc₂Ga₃O₁₂和Er³⁺:Gd₃Sc₂Ga₃O₁₂晶体在室温下320—1700nm范围的吸收光谱和500—750nm范围内的上转换荧光谱，同时对其上转换荧光的可能发生机制、途径以及上转换过程可能对Er^{3+相似文献}   

Er3+/Yb3+共掺碲钨酸盐玻璃的光谱性质和热稳定性的研究

制备了Er³⁺和Yb³⁺共掺的碲钨酸盐玻璃样品65TeO₂-25 WO₃-10R_mO_n(R_mO_n=PbO,BaO),(65+x)TeO₂-(25-x)WO ₃-10La₂O₃ (x=0,5,10), (60+x)TeO₂-(30 -x)WO₃-10Bi₂O₃ (x=0,5,10).测试了玻璃样品的吸收光谱、荧光光谱、能级寿命及热稳定性能.结果表明除含Bi ₂O₃的碲钨酸盐玻璃外，其余玻璃样品均没出现析晶开始温度(T_x)，说明碲钨酸盐 是一种适合于光纤拉制的玻璃基质材料.应用Judd-Ofelt理论计算了强度参数Ω_t(t=2, 4,6)，研究表明Ω₂在碲钨酸盐玻璃中主要受到Er-O键的共价性的影响，而Er^{3 +} 离子周围配位场的非对称性影响可以忽略.测得了Er³⁺在15 μm发射谱的荧光 半高宽 (FWHM=71—77nm)和Er³⁺的⁴I_13/2能级寿命 (τ^m=3—34 ms).应用McCumber理论计算了Er³⁺在15 μm处的受激发射截面(σ^peak=068—103×10^-20 cm²).比较了Er³⁺在不同玻璃基质里 的15 μm荧光带宽和发射截面，研究结果表明碲钨酸盐玻璃是一种制备宽带光纤放大器的理想基质材料.     

Er3+/Ce3+共掺TeO2-Bi2O3-TiO2玻璃的热稳定性和光谱特性研究

用高温熔融法制备了Er³⁺/Ce³⁺共掺新型碲酸盐玻璃(TeO₂-Bi₂O₃-TiO₂).采用差热分析方法研究了玻璃的热稳定性,测试并分析了不同Ce³⁺离子掺杂浓度下Er³⁺离子的吸收光谱、上转换光谱和荧光光谱特性.研究结果表明,制备的碲酸盐玻璃具有很好的热稳定性,玻璃析晶温度Tx与玻璃转变温度Tg之差(ΔT=Tx-Tg)达到了185 ℃,高于其它文献的报道|同时,Ce3+离子共掺引入的能量转移(Ce³⁺∶2F5/2+Er³⁺∶4I11/2→Ce³⁺∶2F7/2+Er³⁺∶4I13/2)有效地抑制了Er³⁺离子上转换发光并显著增强了1.53 μm波段荧光强度,而发射截面随着Ce³⁺离子掺杂浓度相应增大.优异的热稳定性以及光谱性能揭示Er³⁺/Ce³⁺共掺碲酸盐玻璃是一种潜在的制备宽带掺铒光纤放大器的理想增益介质.     

Er3+单掺及Er3+/Yb3+共掺SiO2-Al2O3-La2O3玻璃光谱性质研究

研究了单掺Er³⁺及Er³⁺/Yb³⁺共掺SiO₂-Al₂O₃-La₂O₃玻璃的光谱性质随稀土离子浓度变化规律,应用McCumber理论计算了玻璃在1.53 μm的发射截面及积分吸收截面.结果表明:在Er³⁺离子掺杂浓度相同时,玻璃在980 nm吸收截面与Yb³⁺掺杂浓度成反比;当样品中Yb³⁺离子掺杂浓度为3.94×10²⁰ cm^-3时,玻璃在1.53 μm的吸收截面和发射截面最大,在1.40～1.60 μm积分吸收截面也最大;Er³⁺/Yb³⁺共掺SiO₂-Al₂O₃-La₂O₃玻璃在1.53 μm的荧光半高宽随Er³⁺掺杂浓度升高而增加,当Er³⁺离子掺杂浓度为2.41×10²⁰ cm^-3时,玻璃的荧光半高宽(FWHM)达到52.5 nm.     

Tm3+/Yb3+ ∶LaF3纳米体系中掺杂Yb3+ 离子对Tm3+ 离子荧光发射的影响

为研究Yb³⁺离子浓度变化对Tm³⁺离子在蓝色波段荧光强度的影响,以NaF和La(NO₃)₃为原料,采用水热法制备了Tm³⁺和Yb³⁺共掺的Tm³⁺/ Yb³⁺∶LaF₃纳米颗粒.用X射线衍射对LaF₃纳米颗粒进行表征的结果显示,纳米晶体结构呈六方相.透射电镜的观测结果显示,纳米颗粒样品大小均匀、分散性良好.在波长为800 nm的激光激发下,观测到了上转换蓝光发射,其中包括波长为474 nm和479 nm的较强的荧光辐射(相应的跃迁为1G4→3H6)和波长位于450 nm的强度较弱的荧光发射(相应的跃迁为1D2→3F4).通过观测不同Yb³⁺离子浓度条件下共掺Tm³⁺/Yb³⁺∶LaF₃样品的荧光光谱,研究了Yb³⁺离子掺杂浓度对于Tm³⁺离子的荧光发射的影响,并探讨了产生这种现象的原因.研究结果显示,对于1G4→3H6跃迁产生的荧光发射(474 nm),当Yb³⁺离子浓度增大时,反向能量传递速率的增加导致了荧光强度的增大.然而,当Yb³⁺离子浓度增大到一定程度时,Yb³⁺离子激发态能级寿命的减少将引发荧光强度的下降.相比较而言,Yb³⁺离子的浓度的变化对于1D2→3F4跃迁产生的位于450 nm处荧光强度的影响较弱.     

Er3+/Ce3+共掺碲铋酸盐玻璃的制备及光谱特性提高研究

采用高温熔融退火法制备了系列 80TeO₂-10Bi₂O₃-10TiO₂-0.5Er₂O₃-xCe₂O₃ (x=0,0.25, 0.5,0.75,1.0 mol%)和(80-y) TeO₂-10Bi₂O₃-10TiO₂-yWO₃-0.5Er₂O₃-0.75Ce₂O₃ (y=3,6,9,12 mol%)的碲铋酸盐玻璃.测试了玻璃样品400-1700 nm范围内的吸收光谱, 975 nm抽运下的上转换发光谱和1.53 μm波段荧光谱, 以及808 nm激励下的Er³⁺离子荧光寿命和无掺杂玻璃样品的Raman光谱, 并结合Judd-Ofelt理论和McCumber理论计算了Er³⁺离子光谱参数.结果表明, 在掺Er³⁺碲铋酸盐玻璃中引入Ce³⁺离子进行Er³⁺/Ce³⁺共掺, 通过Er³⁺离子⁴I_11/2能级与Ce³⁺离子²F_5/2 能级间基于声子辅助的能量传递过程,可以有效抑制Er³⁺离子上转换发光并明显增强其 1.53 μm波段荧光;同时,在现有Er³⁺/Ce³⁺共掺玻璃组分基础上引入WO₃, 可进一步提高1.53 μm波段荧光并展宽其荧光发射谱. 研究结果对于获取优异光谱特性的宽带掺Er³⁺光纤放大器玻璃基质具有实际意义.     

LD抽运Er3+，Yb3+共掺磷酸盐玻璃被动调Q激光器的理论分析和数值计算

研究了以Co²⁺:MgAl₂O₄晶体为饱和吸收体的LD抽运Er³⁺,Yb³⁺共掺磷酸盐玻璃激光器.针对双掺离子之间的能量传递和Er³⁺的多种跃迁过程，结合Co²⁺:MgAl₂O₄晶体中Co²⁺离子的饱和吸收特性，给出了详尽的速率方程，在其基础上进行了数值分析，分析了输出镜透过率、激光介质长度、谐振腔长度、腔内往返损耗、饱和吸收体长度对激光阈值、峰值功率、单脉冲能量以及脉冲宽度的影响.     

Superacid Catalyst SO42-/ZrO2-La2O3 Prepared by Ultrasonic Co-precipitation and Low Temperature Aging

低温陈化超声波共沉淀法制得SO₄^2-/ZrO^2-La₂O₃前驱体， 经H₂SO₄处理， 在不同温度下焙烧得到纳米晶催化剂SO₄^2-/ZrO^2-La₂O₃；用Hammett指示剂法测定其酸性. 用XRD、BET、TEM、IR和XPS对样品进行表征，其催化活性用醋酸和甘油的酯化反应进行了评价. 结果表明经超声波搅拌和低温(-15 ºC)陈化，650 ºC焙烧4 h得到的固体超强酸表现出较高催化活性.     

980 nm激发下Er3+/Yb3+共掺杂ZrO2-Al2O3粉末的上转换发光特性

通过固相反应法制备了Er³⁺/Yb³⁺共掺杂ZrO₂-Al₂O₃粉末的样品，并对样品在980nm激光激发下的上转换发光特性进行了研究.从发射光谱可以发现，在可见光范围内有3个强的发光带，一个位于654nm附近的红光带和两个分别位于545nm、525nm附近的绿光带，分别对应于Er³⁺离子的以下辐射跃迁：⁴F_9/2→⁴I_15/2、⁴S_3/2→⁴I_15/2、 ²H_11/2→⁴I_15/2.其中又以Er³⁺离子的⁴F_9/2→⁴I_15/2跃迁产生的红色荧光辐射最强.对其上转换发光机制进行了分析，发现这三个发光过程都是双光子过程.对样品粉末进行了XRD检测，发现ZrO₂主要以立方相为主，并且计算得到了这种立方结构的晶格常数.Al₂O₃固溶于ZrO₂中，Al³⁺嵌入ZrO₂后产生氧空位，导致ZrO₂晶体的对称性降低，这种结构变化更有利于提高上转换效率，即上转换发光强度增强. 关键词： 3+/Yb³⁺')" href="#">Er³⁺/Yb³⁺ 上转换 2-Al₂O₃')" href="#">ZrO₂-Al₂O₃ 荧光 稀土     

Ce3+对Er3+/Yb3+共掺TeO2-WO3-ZnO玻璃发光性能的影响

在Er³⁺/Yb³⁺共掺TeO₂-WO₃-ZnO玻璃中引入Ce³⁺，研究了Ce³⁺对Er³⁺1.5μm发射性能及其上转换发光性能的影响。结果表明，随Ce³⁺浓度的增加Er³⁺1.5μm波段的荧光强度先增强后降低，优化的Ce³⁺掺杂浓度在2.07×10²⁰/cm³左右；1.5μm波段的荧光寿命则随Ce³⁺浓度的增加有轻微降低，从3.4ms降到3.0ms，但Ce³⁺浓度的增加对1.5μm波段的荧光半高宽基本无影响；Er³⁺/Ce³⁺间的交叉弛豫Er³⁺(⁴I_11/2)+Ce³⁺(²F_5/2)→Er³⁺(⁴I_13/2)+Ce³⁺(²F_7/2)使玻璃的上转换发光强度大大降低，但在过高的Ce³⁺浓度下，Er³⁺/Ce³⁺间的另一交叉弛豫Er³⁺(⁴I_13/2)+Ce³⁺(²F_5/2)→Er³⁺(⁴I_15/2)+Ce³⁺(²F_7/2)则使Er³⁺⁴I_13/2能级粒子数减少，导致1.5μm波段荧光强度和荧光寿命降低. 关键词： 碲钨酸盐玻璃 发光性能 3+离子')" href="#">Er³⁺离子 3+离子')" href="#">Ce³⁺离子 交叉弛豫     

Up-conversion photoluminescence characteristics of Yb3+:Er3+:Tm3+ co-doped borosilicate glasses

Yb3+:Er3+:Tm3+ co-doped borosilicate glasses are prepared.Their strong up-conversion photoluminescence spectra in a range from ultra-violet to near-infrared,which are excited by a 978-nm laser diode,are measured,and the mechanisms of energy transfer among Yb3+,Er3+ and Tm3+ ions are discussed.The results show that there is an unexpected wavelength at 900-nm emission from Yb3+ Stark splitting levels to pump Tm3+ ions and there exists an optimum pump power.The concentration of the Tm3+ dopant gives rise to a prominent effect on the intensity of visible and near-infrared emissions for the Yb3+:Er3+:Tm3+ co-doped borosilicate glasses.     

Upconversion luminescence of Tm^3＋/Yb^3＋ codoped oxyfluoride glasses

Novel oxyfluoride glasses are developed with the composition of 30SiO2-15Al2O3-28PbF2-22CdF2-0.1TmF3 - xYbF3 - （4.9 - x） AlF3（x=0, 0.5, 1.0, 1.5, 2.0） in tool fraction, Furthermore, the upconversion luminescence characteristics under a 970nm excitation are investigated. Intense blue, red and near infrared luminescences peaked at 453nm, 476nm, 647nm and 789nm, which correspond to the transitions of Tm^3＋： ^1D2 →^3F4, ^1G4 →^3H6, ^1G4 →^3F4, and ^3H4 →^3H6, respectively, are observed. Due to the sensitization of Yb^3＋ ions, all the upconversion luminescence intensities are enhanced considerably with Yb^3＋ concentration increasing. The upconversion mechanisms are discussed based on the energy matching rule and quadratic dependence on excitation power. The results indicate that the dominant mechanism is the excited state absorption for those upconversion emissions.     

Doping effects of Nb5+ on red long afterglow phosphor CaTiO3:Pr3+

A series of Nb5+ codoped red long afterglow phosphors CaTi1 xNbxO3:Pr03.+002 (0 ≤ x ≤ 0.05) is prepared by a solid state reaction method. Their photoluminescence, phosphorescence and thermoluminescence are investigated. The results indicate that codoping Nb5+ can improve the photoluminescence and phosphorescence property of CaTiO3:Pr3+ significantly. When 3-mol% Nb5+ is codoped, the emission intensity of CaTiO3:Pr3+ is enhanced twice, while the afterglow time is extended from 10 min to about 40 min. Thermoluminescence results reveal that the trapping level of CaTiO3:Pr3+ is reduced from 0.82 eV to 0.62 eV by codoping Nb5+. The effect of Nb5+ doping on enhancing the photoluminescence intensity and afterglow time of CaTiO3:Pr3+ is discussed.     

Cr3+,Yb3+,Er3+共掺磷酸盐铒玻璃转镜调Q激光性质研究

研究了Cr³⁺,Yb³⁺,Er³⁺共掺磷酸盐铒玻 璃转镜调Q激光性质.三种Er₂O₃掺杂浓度的激光实验结果表明，在Er₂O₃名义掺杂浓 度为0.5wt％时，玻璃的综合激 光性质最好，重复频率为0.1Hz时，它的激光阈值功率为14.5mJ，最大输出能量为9.6mJ ，斜率效率为0.55％.在同种实验条件下，比较了Cr14和Kigre公司生产的QE-7S激光性质参数，实验表明，前者激光阈值功率稍低，而后者的斜率效率和最大输出功率略高. 关键词： 3+-Yb³⁺-Er³⁺共掺')" href="#">Cr³⁺-Yb³⁺-Er³⁺共掺 磷酸 盐玻璃 光谱性质 激光性质     

Upconversion properties of Er^3＋/Yb^3＋ co-doped TeO2-Nb2O5-Li2O glasses

The Er^3＋/Yb^3＋ co-doped TeO2-Nb2O5-Li2O glass is prepared by conventional melting method, and its upconversion spectra are measured. The intense green upconversion luminescence upon excitation with a 976 nm laser diode is observed with the naked eyes. The dependence of luminescence intensity on the ratio of Yb^3＋/Er^3＋ is discussed in detail, and the relationship between the ratio of green luminescence intensity to red luminescence intensity and the ratio of Yb^3＋/Er^3＋ is also studied, The luminescence intensity increases with the ratio of Yb^3＋/Er^3＋ increasing. The ratio of Yb^3＋/Er^3＋ plays a more important role than the concentration of Er^3＋ in determining the upconversion luminescence intensity. The ratio of green luminescence intensity to red luminescence intensity reaches a maximum when ratio of Yb^3＋/Er^3＋ is 3. Thus the glass could be one of the potential candidates for LD pumping solid-state lasers.     

Synthesis and characterization of Sr3Al2O6：Eu2＋, Dy3＋ phosphors prepared by sol-gel-combustion processing

A type of red luminescent Sr3Al2O6:Eu2+, Dy3+ phosphor powder is synthesised by sol-gel-combustion processing, with metal nitrates used as the source of metal ions and citric acid as a chelating agent of metal ions. By tracing the formation process of the sol-gel, it is found that it is necessary to reduce the amount of NO3- by dropping ethanol into the solution for forming a stable and homogeneous sol-gel. Thermogravimetric and Differential Scanning Calorimeter Analysis, x-ray diffractionmeter, scanning electron microscopy and photoluminescence spectroscopy are used to investigate the luminescent properties of the as-synthesised Sr3Al2O6:Eu2+, Dy3+. The results reveal that the Sr3Al2O6 crystallises completely when the combustion ash is sintered at 1250 C. The excitation and the emission spectra indicate that the excitation broadband lies mainly in a visible range and the phosphors emit a strong light at 618 nm under the excitation of 472 nm. The afterglow of (Sr0.94Eu0.03Dy0.03)3Al2O6 phosphors sintered at 1250 ℃ lasts for over 1000 s when the excited source is cut off.