TeO2-ZnO-Na2O-K2O玻璃中Er3+离子掺杂浓度对其发光及荧光寿命的影响

测量了不同掺杂浓度下Er³⁺离子在碲酸盐玻璃中的吸收光谱、发射光谱和Er3+离子的荧光寿命，计算了Er³⁺离子的发射截面σ_e,分析 了Er ³⁺离子掺杂浓度对其发光强度和荧光寿命的影响.结果表明，Er³⁺离子掺 杂浓度较低时，对其荧光强度和荧光寿命没有显著的影响；掺杂浓度高时，出现了浓度猝灭 效应，使Er³⁺离 子荧光光强度降低，荧光寿命下降.实验确定了掺杂浓度最优值，同时对浓度猝灭机制进行 了分析. 关键词： 碲锌碱玻璃 3+离子')" href="#">Er³⁺离子 掺杂浓度 发光和荧光寿命     

铋酸盐铒玻璃在1.54 μm处的荧光特性研究

用高温熔融法制备了Er3+单掺和Er3+ /Yb3+共掺铋酸盐玻璃,测量了上述玻璃样品的吸收光谱、荧光光谱、荧光半高宽和荧光寿命.对高浓度掺杂Er3+时的浓度猝灭现象给出了解释.分析了Er3+ /Yb3+双掺样品中Yb3+对Er3+的敏化过程.在对Er3+ /Yb3+共掺时的研究结果发现, Er3+浓度的变化对荧光半高宽和荧光寿命有显著影响,而Yb3+浓度的变化则对吸收光谱和荧光光谱的强度影响显著.实验获得了Er3+ /Yb3+共掺铋酸盐玻璃在1. 54μm处荧光半高宽达76nm,荧光寿命为0. 55ms.     

Yb3+离子掺杂浓度对Yb∶YAG晶体发光及荧光寿命的影响

研究了不同掺杂浓度Yb∶YAG晶体的发光特性和荧光寿命.Yb3+在YAG晶体中的掺杂浓度分别为5at%、10at%、20at%、30at%.Yb3+离子掺杂浓度越高，Yb∶YAG晶体的吸收系数越大.采用940 nm波长的LD泵浦源和TRIA X550荧光谱仪，对这一系列掺有不同浓度Yb3+的Yb∶YAG晶体进行了荧光光谱的测定.结果表明:在1030 nm主发光波段的荧光强度以10at%Yb∶YAG的为最强.同时发现它在450 nm-680 nm波段有明显的可见发光，其强度随Yb3+掺杂浓度的增加而迅速地增强.Yb∶YAG晶体的荧光寿命存在浓度猝灭现象，对猝灭机制进行了分析研究，指出浓度猝灭的主要原因是合作发光和痕量稀土离子的上转换发光.     

Er3+单掺及Yb3+/Er3+双掺LaLiP4O12玻璃光谱性质研究

制备了Er3 +单掺杂及Yb3+/Er3+双掺杂四磷酸盐玻璃 ,测量了吸收光谱、荧光光谱 ,用McCumber理论计算Er3 +的发射截面 ,研究了其荧光特性、浓度猝灭及其机制、以及OH基对荧光强度和能量传递的影响 ,研究发现对四磷酸盐玻璃Yb3+的最佳浓度约为 1.82× 10 2 1ions/cm3,Er3+最佳浓度约为 0 .96× 10 2 0 ions/cm3。     

稀土离子掺杂的AlF3基氟化物玻璃

在800和970!nm LD激发下,分别研究了Er3+单掺和Yb3+,Tm3+共掺的AlF3基(AYF,AZF)玻璃中上转换发光、能量传递和浓度猝灭.在Er3+掺杂的AlF3基玻璃,随着Er3+掺杂量的增加,红光与绿光上转换发光强度比(Ired/Igreen)增加,这被认为与两个Er3+离子(一个在4I9/2态、另一个在4S3/2态)的交叉弛豫过程有关.在Tm3+-Yb3+共掺的AlF3基玻璃中,发现对于Tm3+的浓度猝灭,蓝光跃迁比近红外荧光跃迁表现更明显,研究还发现Yb3+-Tm3+共掺AYF和AZF玻璃存在Yb3+离子对上转换发光的猝灭现象,这被认为可能是Tm3+(3F4)→Yb(3F5/2)反向能量传递的结果.     

掺Yb3+氧化镧钇透明激光陶瓷的光谱特性

采用传统陶瓷烧结工艺,在无压还原气氛下低温制备出透明性良好的掺Yb3+氧化镧钇透明激光陶瓷,测试了其在室温下的吸收光谱、发射光谱和荧光寿命.结果表明,掺Yb3+氧化镧钇透明激光陶瓷的吸收系数随着Yb3+掺杂浓度的增加而增大,最强吸收峰974nm处的吸收截面为0.90～1.12×10－20 cm2;主发射峰1 032 nm和1 075 nm处的发射截面分别为1.05×10－20 cm2和0.87×10－20 cm2; Yb3+掺杂浓度为5at.%时荧光寿命为1.38 ms,并随Yb3+掺杂浓度的增加而减小;当Yb3+掺杂浓度超过10at.%时,样品中存在严重的浓度猝灭.产生浓度猝灭的原因是高掺杂时离子间存在合作上转换和能量转移.     

Yb3+掺杂浓度对Er3+/Yb3+共掺SiO2-Al2O3-La2O3玻璃光谱性质的影响

测量了不同Yb3+ 离子掺杂浓度下 ,Er3+ /Yb3+ 共掺SiO2 Al2 O3 La2O3玻璃的吸收光谱、荧光光谱和Yb3+离子2 F5/ 2 的能级寿命 ,应用迈克康伯 (McCumber)理论计算了Er3+ 的受激发射截面σemi,讨论了Yb3+ 离子浓度对其自身吸收性质、Er3+ 离子发光性质 ,以及Yb3+ →Er3+ 能量传递效率 (η)的影响 ,初步探明该基质玻璃中Yb3+ 离子掺杂数浓度的最佳范围为 3 .94× 1 0 2 0 cm- 3至 5 .92× 1 0 2 0 cm- 3,在此掺杂范围内 ,Yb3+ 离子的最大吸收系数为9.8cm- 1 ,Er3+ 的峰值发射截面和Yb3+ →Er3+ 能量传递效率 (η)分别为 0 64× 1 0 - 2 4 m2 和 92 %。     

Er~(3+)及Er~(3+)/Yb~(3+)掺杂纳米晶CaWO_4的发光性质

利用共沉淀法制备了Er3+掺杂及Er3+/Yb3+共掺杂纳米晶CaWO4发光粉体,室温下观察到Er3+的下转换和上转换特征发射。研究了不同煅烧温度、不同掺杂浓度对Er3+离子特征发射的影响。结果表明:随着煅烧温度的升高,发射强度增强;掺杂浓度的改变,导致了Er3+的浓度猝灭现象,其适宜的掺杂原子数分数为0.6%。同时观测到O-W的电荷迁移态与稀土离子之间的能量传递现象,并给出了能量传递的模型。对Er3+的上转换研究观察到:在976nm激光激发下Yb3+对Er3+的上转换发射起到了很好的敏化作用,两个Yb3+同时将能量以共振方式传递给一个Er3+离子,Er3+、Yb3+共掺杂样品的绿光上转换过程展示了双光子过程。     

Yb~(3 )离子掺杂浓度对Yb∶YAG晶体发光及荧光寿命的影响

研究了不同掺杂浓度Yb∶YAG晶体的发光特性和荧光寿命·Yb3 在YAG晶体中的掺杂浓度分别为5at%、10at%、20at%、30at%·Yb3 离子掺杂浓度越高,Yb∶YAG晶体的吸收系数越大·采用940nm波长的LD泵浦源和TRIAX550荧光谱仪,对这一系列掺有不同浓度Yb3 的Yb∶YAG晶体进行了荧光光谱的测定.结果表明:在1030nm主发光波段的荧光强度以10at%Yb∶YAG的为最强·同时发现它在450nm~680nm波段有明显的可见发光,其强度随Yb3 掺杂浓度的增加而迅速地增强·Yb∶YAG晶体的荧光寿命存在浓度猝灭现象,对猝灭机制进行了分析研究,指出浓度猝灭的主要原因是合作发光和痕量稀土离子的上转换发光·     

纳米晶ZrO2：Dy3+的光致发光和能量传递性质

研究了Dy³⁺离子掺杂的ZrO₂纳米粉体的光致发光性质。观测到Dy³⁺离子的室温强特征发射和浓度猝灭现象以及基质ZrO₂与Dy³⁺离子之间的能量传递过程。发现了煅烧温度对样品的晶相有明显的影响,随着煅烧温度的变化,晶相也随之改变。晶相的改变使样品的荧光发射产生较大的差异,并观测到两个发射中心。通过对荧光强度与激活离子Dy³⁺离子浓度的关系研究发现,Dy³⁺离子在纳米ZrO₂基质中存在浓度猝灭现象,最佳掺杂浓度取决于ZrO₂基质的晶相,不同晶相导致不同的猝灭浓度,当基质晶相表现为四方相时,猝灭浓度为0.5%,而基质晶相为混合相时,猝灭浓度为1%。能量传递也依赖于样品的晶相。当煅烧温度为950℃时能量传递效果最好,并且从微观结构上给出了解释基质与Dy³⁺离子之间的能量传递的模型。     

μ+SR study of LaNi2As2, URh2Si2 and CeRh2Si2

Muon spin relaxation experiments have been carried out in the paramagnetic and magnetically ordered states of URh₂Si₂ and CeRh₂Si₂. As the magnetic structure of these compounds is well known, these measurements can help to characterise their magnetic properties probed by μSR and to understand the μSR results of the heavy fermion compounds of the same crystallographic family. Our measurements show that the muons occupy two different crystallographic sites. The spectra of URh₂Si₂ and CeRh₂Si₂ in the magnetically ordered states are very different, probably reflecting their different magnetic structures. The spectra obtained on CeRh₂Si₂ are similar to the published spectra of the heavy fermion compound CeCu_2.1 Si₂. Muon spin rotation measurements on LaNi₂As₂ indicate that the muon is diffusing at 150 K.     

13C-selective IRMPD of CBr2F2/Cl2 and CCl2F2/Br2 systems

The CO₂ TEA laser irradiation of CBr₂F₂ in the presence of Cl₂ yielded ¹³C-enriched CBrClF₂ and ¹³C-enriched CCl₂F₂ under selected experimental conditions. As the photolysis proceeded, the ¹³C concentration of CBrClF₂ decreased gradually and that of CCl₂F₂ increased up to 90% or higher. These results can be explained by the mechanism involving the secondary ¹³C-selective IRMPD of the primary product CBrClF₂. On the other hand, the carbon-containing product for a CCl₂F₂/Br₂ system was only CBrClF₂; the further IRMPD of which probably regenerated CBrClF₂ in the presence of Br₂. The decomposition probabilities of ¹²C- and ¹³C-containing molecules in both systems were measured as functions of laser line, laser fluence, and reactant pressures.     

Magnetostriction of SmMn2Ge2 and GdMn2Ge2 intermetallic compounds

Longitudinal and transverse magnetostrictions of polycrystalline samples of intermetallic compounds RMn₂Ge₂ (R=Sm or Gd) are measured in pulsed magnetic fields up to 250 kOe. It is found that linear magnetostrictive strains of about 10^?3 arise in a temperature range in which the magnetic field causes a change in the magnetic state of a manganese magnetic subsystem. The results obtained are described within the model of a two-sublattice ferrimagnet with a negative exchange interaction in the manganese subsystem in terms of a strong dependence of this interaction on interatomic distances.     

Synthesis and properties of HgI2 intercalation of Bi2Sr2CaCu2Oy superconductor

Polycrystalline or single crystals of HgI₂ intercalated Bi₂Sr₂CaCu₂O_y (Bi2212) have been synthesized and their properties have been studied together with those of HgBr₂ intercalates. Single crystals of HgI₂ intercalated Bi2212 were synthesized by a stepwise intercalation method using iodine intercalate as a secondary host material. These could not be obtained through direct intercalation methods by which polycrystalline sample were obtained. From ac susceptibility and resistivity measurements, superconducting onset temperature (T_con) for polycrystalline HgI₂ intercalate was found to be 82 K which was higher than that of the host (75 K). On the other hand, T_con for single crystal HgI₂ intercalate was shown to be 79–80 K which is lower than that of host (95–97 K). The effect of HgI₂ or HgBr₂ intercalation on T_c tried discussion from the view point of hole doping and interblock coupling effect.     

Eu2+掺杂CaSi2O2N2荧光粉发光性能

采用固相反应法合成了组成为Ca_1-xEu_xSi₂O₂N₂的Eu²⁺掺杂CaSi₂O₂N₂荧光粉.通过荧光光谱对样品的发光性能进行了研究,发现Eu²⁺掺杂CaSi₂O₂N₂荧光粉发射光谱为宽波段的单峰结构,主要包含绿光和黄光区,发射峰在556~568 nm.从发射光谱的宽带特征来看,CaSi₂O₂N₂:Eu²⁺的发射主要对应着Eu²⁺离子4f⁶5d→4f⁷跃迁.从激发光谱所覆盖的范围还可以看到,样品可以有效的被UV蓝-光激发,这意味着该类荧光粉在白光LED方面有可能得到广泛的应用.另外,样品的发光性能与激发离子的浓度有着很大关系.激发离子浓度增大时,发射光谱会发生明显红移.利用这一性质,可以通过改变Eu²⁺浓度来调节荧光粉的发光范围,从而满足不同场合的需要.同时,Eu²⁺浓度提高,样品发射光谱的强度也会随之增强,在x=0.06时发射强度达到最大值,之后继续增加Eu²⁺浓度,强度不仅没有增加反而降低,即出现浓度猝灭现象.     

CO2-laser-induced multiphoton absorption of CF2Cl2

Energy absorption by CF₂Cl₂ from an intense TEA CO₂ laser pulse is measured as a function of the pressure of CF₂Cl₂ and the pressure of Ar bath gas for different laser energy fluences. The fraction of the molecules excited by the laser field and the average energy of the molecular ensemble are determined by a simple experimental method.     

X-ray photoemission spectra measurements of CeNi2Sb2 and CeCu2Sb2

X-ray photoemission spectra, resistivity and susceptibility of CeNi₂Sb₂ and CeCu₂Sb₂ were measured and are discussed. The results indicate that these alloys are Kondo systems. For comparison of the valence band properties, the spectra of the isostructural alloys of RT₂X₂-type with R = La, Gd, T = Cu, Ni and X = Sn, Sb were investigated, too.     

(NH_2CH_2COOH)_2CdCl_2晶体的拉曼光谱的研究

（ＮＨ２ＣＨ２ＣＯＯＨ）２ＣｄＣｌ２晶体的拉曼光谱的研究刘建军吴粤郑吉民扈士芬蓝国祥（南开大学天津３０００７１）ＲａｍａｎＳｐｅｃｔｒａｏｆ（ＮＨ２ＣＨ２ＣＯＯＨ）２ＣｄＣｌ２ＣｒｙｓｔａｌｓＬｉｕＪｉａｎｊｕｎ，ＷｕＹｕｅ，ＺｈｅｎｇＪｉｍｉｎ，Ｈ...