La1－xPrxMnO3(x=0.1，0.2)薄膜庞磁电阻性质的研究

一种新的庞磁电阻氧化物薄膜La_1-xPr_xMnO₃(x=0.1，0 .2)薄膜用脉冲激光沉积(PLD)方法生长在(100)SrTiO₃单晶基底上.XRD结果显示 薄膜具有很好的外延单晶取向.电输运和磁性质的研究表明薄膜具有显著的庞磁电阻效应(CM R)效应，其中磁电阻比率达95％(在5T的磁场下).X射线光电子能谱(XPS)的结果表明薄膜体 系中Pr离子的价态为+4价，因此该薄膜很可能是电子掺杂的庞磁电阻体系. 关键词： 脉冲激光沉积 1-xPr_xMnO₃')" href="#">La_1-xPr_xMnO₃ 电子 掺杂 庞磁电阻     

La0.33Pr0.34Ca0.33MnO3薄膜的应变效应

采用脉冲激光沉积法分别在(100)LaAlO₃和(100)SrTiO₃基片上生长了La_0.33Pr_0.34Ca_0.33MnO₃薄膜,并通过磁测量和电输运测量对生长在不同基片上的La_0.33Pr_0.34Ca_0.33MnO₃薄膜的物性进行了研究.结果表明,基片和薄膜之间的压应力导致La_{关键词： 钙钛矿锰氧化物 相分离 电荷有序}     

Ti/Pr0.7Ca0.3MnO3/La0.67Sr0.33MnO3/Pt异质结电致电阻效应的改善

采用脉冲激光沉积技术制备了Ti/Pr_0.7Ca_0.3MnO₃/Pt和Ti/Pr_0.7Ca_0.3MnO₃/La_0.67Sr_0.33MnO₃/Pt异质结并研究了La_0.67Sr_0.33MnO₃功能插层对异质结电致电阻特性的影响. 实验结果表明La_0.67Sr_0.33MnO₃功能层的引入有效提高了器件的电阻转变特性,尤其是电阻转变率和疲劳性得到了极大的改善. 对La_0.67Sr_0.33MnO₃插层改善电致电阻转变特性的机理进行了定性的分析. 关键词： 电致电阻效应 电阻转变比率 疲劳特性     

La0.67Ba0.33MnO3薄膜的激光辐照效应研究

利用脉冲激光沉积技术在LaAlO₃（00l）单晶衬底上制备了La_067Ba_033MnO₃薄膜,研究了CO₂激光辐照对La_067Ba_033MnO₃薄膜的微结构和磁电性能的影响.结果表明,经激光辐照后,La_067Ba_033MnO₃薄膜的结晶性增强,薄膜应变减小;薄膜表面形貌由“岛状”结构变为“平原"结构,且粗糙度大大降低;同时,薄膜的饱和磁化强度、铁磁居里温度、金属—绝缘态转变温度和磁电阻增大,而矫顽场和电阻率减小.根据对传统退火效应的分析和理论计算,认为激光辐照导致的表面微结构的变化以及薄膜的氧含量和均匀性的提高对La_067Ba_033MnO₃薄膜的磁电性能的改善与优化密切相关. 关键词： 庞磁电阻 激光辐照 脉冲激光溅射沉积     

LaCaMnO/LaNdCaMnO/LaCaMnO三层膜中巨磁电阻增强效应

通过直流磁控溅射方法在SrTiO₃(001)衬底上制备了一系列La_0.67Ca_0.33MnO₃/(La_0.35Nd_0.65)_2/3Ca_1/3MnO₃/La_0.67Ca_0.33MnO₃(以下简写为LCMO/LNCMO/LCMO)外延三层膜，其中间层 关键词：     

La2/3Sr1/3MnO3/BaTiO3复合薄膜的制备及其电致磁电效应研究

使用脉冲激光沉积技术,在LaAlO₃(001)单晶基片上制备了La_2/3Sr_1/3MnO₃(LSMO)/BaTiO₃(BTO)双层薄膜.X射线衍射分析显示,LSMO层和BTO层呈现纯(001)取向.原子力显微镜研究表明,薄膜表面晶粒大小均匀,排列致密,表面均方根粗糙度为1.4 nm.复合薄膜的磁学、电学性能研究表明,其具有良好的磁学和介电性能.电输运测试显示,与在BTO层上施加正方向 关键词： 磁电效应 铁电/铁磁异质结构 脉冲激光沉积     

Pr0.5Ca0.5MnO3/Si异质结输运特性和整流特性研究

利用固相反应法制备Pr_0.5Ca_0.5MnO₃(PCMO)靶材,并采用脉冲激光沉积法(PLD)在n型Si(111)基片上沉积PCMO外延薄膜,研究了薄膜的输运特性及薄膜与Si衬底形成异质结的整流特性.结果表明:在80—300 K温度范围内,PCMO薄膜的阻温关系符合变程跳跃模型,随着温度的升高表现出从一维到二维再到三维的转变,分析认为可能源于轨道自由度对电子输运特性的影响.PCMO/Si异质结在磁场作用下整流特性得到改善,且在正向电流方向出 关键词： 0.5Ca_0.5MnO₃')" href="#">Pr_0.5Ca_0.5MnO₃ Si 整流 正磁电阻     

二元掺杂镧锰氧化物La-Ca-Ba-Mn-O的庞磁电阻特性

用固相反应法制备了二元掺杂的镧锰氧化物La_0.67(Ca_0.6Ba_0.4)_0.33MnO_z(LCBMO)立方多晶体材料,研究了其磁特性和庞磁电阻特性,并与用类似方法制备的一元掺杂的La_0.67Ca_0.33MnO_z(LCMO)及La_0.67Ba_0.33MnO_z(LBMO)的庞磁电阻特性进行了比较.研究表明,LCBMO的居里温度T_C为312K,介于LCMO和LBMO的T_C（分别为280,362K）之间,其金属-半导体转变温度T_p和μ₀H=0.6T下的磁电阻（MR）峰值温度T_m分别为306,298K,接近于其T_C,也介于LCMO和LBMO的T_p和T_m之间.μ₀H=0.6T下,在各自的T_m处,LCMO,LCBMO和LBMO的庞磁电阻值分别达到41%,24.7%和8%,但在室温（300K）处,LCBMO的MR值仍达到20％,远大于LCMO和LBMO的值（分别为2.0％和2.4％）.研究还发现,在温度远低于T_m时,LCMO仍保持一定的磁电阻效应,而LCBMO和LBMO的磁电阻温度降低而增加,这些低温磁电阻特性与材料的结构特征（如晶界和致密度）有关. 关键词：     

La1-xCaxMnO3的巨磁电阻效应

通过测量La_2/3Ca_1/3MnO₃，La_0.6Ca_0.4MnO₃单相多晶样品的磁电阻、电阻与温度的依赖关系，发现在La_1-xCa_xMnO₃体系中随x的变化，其磁电阻峰和电阻峰都发生了位移．作者认为体系中Mn⁴⁺含量是受Ca含量调制的，正是Mn⁴⁺含量的变化，导致磁性 关键词：     

钙钛矿结构La0.9Sb0.1MnO3的庞磁电阻性质

一种新的钙钛矿结构的庞磁电阻氧化物La_0.9Sb_0.1MnO₃已用固态反应方法制 成，通过超导量子干涉器件(SQUID)装置测量研究了它的电输运性质和磁性质.x射线光电子 能谱分析证明，该氧化物中Sb的价态是+5价，因此该氧化物是一种新的电子掺杂型庞磁电阻 材料. 关键词： 钙钛矿结构 0.9Sb_0.1MnO₃')" href="#">La_0.9Sb_0.1MnO₃ 电子掺杂 庞磁电阻     

Electrical transport behavior of La0.67Ca0.33MnO3/Fe3O4 composites

The influence of Fe₃O₄ contents on the electrical transport properties (resistivity and ac susceptibility) of a series of composite samples of La_0.67Ca_0.33MnO₃/Fe₃O₄ is studied. Results show that the Fe₃O₄ phase not only shifts the intrinsic insulator-metal (I-M) transition temperature T_P1 to a lower temperature, but also causes a new I-M transition at a lower temperature T_P2 (T_P2<T_P1). On the basis of an analysis by scanning electron microscopy and X-ray diffraction, we suggest that the decrease of the I-M transition temperature and the formation of the new I-M transition are caused by the segregation of a new phases related to the Fe₃O₄ at grain boundaries or surfaces of the La_0.67Ca_0.33MnO₃ grains.     

Magnetoresistance and transport properties of different impurity doped La0.67Ca0.33MnO3 composite

An enhanced magnetoresistance and a two-fold effect result from impurity dopant were observed in composites of La_0.67Ca_0.33MnO₃/YSZ and La_0.67Ca_0.33MnO₃/Fe₃O₄. Where YSZ represents yttria-stabilized zirconia and the doping level of both YSZ and Fe₃O₄ is 1 mol%. Different electrical and magnetic transport properties, in particular a lower field magnetization behavior, were observed between pure La_0.67Ca_0.33MnO₃ and the impurity doped La_0.67Ca_0.33MnO₃ composites. Compared with pure La_0.67Ca_0.33MnO₃, a possible interpretation is presented by considering the influences of YSZ and Fe₃O₄ on the structure of grain boundaries and/or surfaces of La_0.67Ca_0.33MnO₃grains.     

Enhancing low-field magnetoresistance of La0.67Ca0.33MnO3 films deposited on anodized aluminium-oxide membranes

In this paper we report a new method to fabricate nanostructured films, La0.67Ca0.33MnO3 （LCMO） nanostructured films have been fabricated by using pulsed electron beam deposition （PED） on anodized aluminium oxide （AAO） membranes, The magnetic and electronic transport properties are investigated by using the Quantum Design physics properties measurement system （PPMS） and magnetic properties measurement system （MPMS）. The resistance peak temperature （Tp） is about 85 K and the Curie temperature （To） is about 250 K for the LCMO film on an AAO membrane with a pore diameter of 20nm. Large magnetoresistance ratio （MR） is observed near Tp. The MR is as high as 85% under 1 T magnetic field. The great enhancement of MR at low magnetic fields could be attributed to the lattice distortion and the grain boundary that are induced by the nanopores on the AAO membrane.     

Search for high temperature coefficient of resistance La2/3Ca1/3MnO3 polycrystalline ceramics

La_2/3Ca_1/3MnO₃ polycrystalline ceramics were synthesized by sol–gel method. Sharp temperature coefficient of resistance (TCR) variation (with peak value up to 22 %) has been observed near the metal-insulator transition temperature T _MI (273 K) for the sample sintered at 1,450 °C. This TCR value is much higher than the previously reported values for the undoped and Ag-doped La_0.67Ca_0.33MnO₃ samples and is comparable to the optimized thin films. It was concluded that the improved physical properties of the La_0.67Ca_0.33MnO₃ material are due to its improved microstructure and homogeneity.     

La0.67Ca0.33MnO3单晶中Fe的掺杂提高本征磁电阻率和激活能的研究

La_0.67Ca_0.33MnO₃ and La_0.67Ca_0.33Mn_0.96Fe0.04O₃单晶的磁性和磁电阻特性。由于缺少晶粒间界，磁场对于自旋涨落的抑制作用更加明显，所以单晶中的磁电阻率比多晶的提高了两个数量级。通过Fe的掺杂，在40×10⁵A/m的磁场下，磁电阻率从3400%进一步提高到了17600%。通过对居里温度以上电阻率的小极化子模型拟和的结果，我们看到随着Fe的掺杂，激活能被提高。磁极化子激活能的增大可以更加局域电子，这可能是在Fe掺杂单晶中本征磁电阻率进一步提高的主要原因。     

Prediction of thermomagnetic properties of La0.67Ca0.33MnO3 and La0.67Sr0.33MnO3

The dependence of magnetization on the variation of temperature for La_0.67Ca_0.33MnO₃ and La_0.67Sr_0.33MnO₃ perovskite-type ceramic materials under an external magnetic field was modelled. Application of phenomenological model was performed, showing a good agreement with the experimental data. Temperature dependence of change of both magnetic entropy and specific heat under magnetic field 0.05?T was predicted for La_0.67Ca_0.33MnO₃ and La_0.67Sr_0.33MnO₃. Predicted values of maximum magnetic entropy change, full-width at half-maximum, relative cooling power and maximum specific heat under 0.05 T were evaluated.     

Magnetoresistance and electrical conductivity of manganite bicrystal contacts

Magnetic bicrystal contacts in epitaxial films of manganite La_0.67Ca_0.33MnO₃ prepared on bicrystal substrates with a misorientation of the NdGaO₃(110) basal planes rotated through an angle of ±14° around the bicrystal boundary line were studied. The temperature dependence of the contact electrical resistance was studied, and the magnetoresistance was measured in fields of up to 1.5 kOe. It is shown that the suppression of ferromagnetic correlations near the boundary leads to the formation of a layer having a substantially lower Curie temperature. Magnetoresistance of 150%, which is record-braking for bicrystal contacts, was measured at T = 4.2 K in a weak magnetic field of about 500 Oe and at a characteristic electrical resistance of the boundary of 3 × 10⁻⁶ Ω cm². It is found that slight orthorhombic distortions of a La_0.67Ca_0.33MnO₃ film due to a lattice mismatch with the NdGaO₃(110) substrate crystal structure lead to the formation of biaxial magnetic anisotropy in the La_0.67Ca_0.33MnO₃ film.     

Preparation and study of silver added La0.67Ca0.33MnO3 film

La_0.67Ca_0.33MnO₃ (LCMO) and Ag admixed La_0.67Ca_0.33MnO₃ (Ag-LCMO) polycrystalline films have been prepared on SrTiO₃ single crystal (100) substrates by ultrasonic spray pyrolysis technique. These films are characterized using XRD, SEM, and temperature dependence of resistivity (ρ-T) and ac susceptibility (χ-T). The films are having cubic structure with lattice parameters as 3.890 and 3.885 Å for LCMO and Ag-LCMO films, respectively. The peek in ρ-T curve (T_p) and the ferromagnetic transition temperature (T_C) for the Ag-LCMO film is higher than that of LCMO film. The stability of both the films was tested by repeated measurements of its characteristics over a period of one week after several thermal cycling from room temperature to 77 K. In the LCMO film, the peak in the ρ-T curve (T_p) is found to shift towards lower value and conduction noise of the film increases in the subsequent measurements. In the case of Ag-LCMO the value of T_p, T_C and conduction noise of the film did not change even after several measurements. Silver segregating at the grain boundaries in Ag-LCMO polycrystalline film seems to be responsible for improving the characteristics of Ag-LCMO films.     

Transport parameters of granular La0.67Ca0.33MnO3 films grown on an R-plane sapphire

Precisely (100)-oriented, 200-nm thick La_0.67Ca_0.33MnO₃ films have been grown by laser ablation on a sapphire (R-plane) substrate covered by a (100)SrTiO₃/(001)Bi₂SrNb₂O₉/(001)CeO₂ trilayer buffer. The azimuthal misorientation of crystal grains (50–300 nm) in the La_0.67Ca_0.33MnO₃ films decreased by about 40% as the condensation temperature was increased ered from 760 to 810° C. The lattice parameter of the grown manganate films was reduced to 3.81–3.82 Å by enriching them with oxygen. The maximum in the temperature dependence of the electrical resistivity of the La_0.67Ca_0.33MnO₃ films grown was shifted toward lower temperatures by 20–50 K relative to its position for bulk ceramic samples of a stoichiometric composition. The largest magnetoresistance (MR=42% at H=0.4 T) was found in La_0.67Ca_0.33MnO₃ films with a Mn⁴⁺ concentration on the order of 50% (T=166 K).