The single crystal of the new ternary compound Sm₁₂Fe₁₄Al₅ was grown and its crystallographic and magnetic properties were investigated. Sm₁₂Fe₁₄Al₅ has a hexagonal structure of the space group p-3m1 and shows ferromagnetism with a Curie temperature of 245 K. The easy direction of magnetization is parallel to the c-axis at temperatures between 245 and 85 K; however, it changes to the c-plane below 85 K through a first-order-like phase transition. No saturation is observed in the magnetization curve even under the applied field of 55 kOe at 5 K. Sm₁₂Fe₁₄Al₅ seems to have a large coercive field at very low temperatures. The anisotropy field was estimated at 5 and 120 K and the saturation magnetization of low temperature phase is explained assuming a ferromagnetic coupling between Fe and Sm sublattices.     

Magnetic and magneto-transport investigations of Co37Ni34Al29 alloy

Ferromagnetic shape memory alloy with nominal composition Co₃₇Ni₃₄Al₂₉ is investigated by transport and magnetic measurements. The anomaly due to the martensitic transition is observed around 130-210 K. The thermal hysteresis, observed due to martensitic transition in the dc magnetization versus temperature data, gets suppressed at higher applied field. Below 50 K, magnetization varies with temperature perfectly as T^3/2, which signifies that spin wave excitations are largely responsible for thermal demagnetization. The sample shows small negative magneto-resistance, which varies non-monotonically with temperature showing largest value at around 200 K.     

The effect of different temperature annealing on phase relation of LaFe11.5Si1.5 and the magnetocaloric effects of La0.8Ce0.2Fe11.5−xCoxSi1.5 alloys

The phase relation of LaFe_11.5Si_1.5 alloys annealed at different high-temperature from 1223 K (5 h) to 1673 K (0.5 h) has been studied. The powder X-ray diffraction (XRD) patterns show that large amount of 1:13 phase begins to form in the matrix alloy consisting of α-Fe and LaFeSi phases when the annealing temperature is 1423 K. In the temperature range from 1423  to 1523 K, α-Fe and LaFeSi phases rapidly decrease to form 1:13 phase, and LaFeSi phase is rarely observed in the XRD pattern of LaFe_11.5Si_1.5 alloy annealed at 1523 K. With annealing temperature increasing from 1573  to 1673 K, the LaFeSi phase is detected again in the LaFe_11.5Si_1.5 alloy, and there is La₅Si₃ phase when the annealing temperature reaches 1673 K. There almost is no change in the XRD patterns of LaFe_11.5Si_1.5 alloys annealed at 1523 K for 3-5 h. According to this result, the La_0.8Ce_0.2Fe_11.5−xCo_xSi_1.5 (0≤×≤0.7) alloys are annealed at 1523 K (3 h). The analysis of XRD patterns shows that La_0.8Ce_0.2Fe_11.5xCo_xSi_1.5 alloys consist of the NaZn₁₃-type main phase and α-Fe impurity phase. With the increase of Co content from x=0 to 0.7, the Curie temperature T_C increases from 180 to 266 K. Because the increase of Co content can weaken the itinerant electron metamagnetic transition, the order of the magnetic transition at T_C changes from first to second-order between x=0.3 and 0.5. Although the magnetic entropy change decreases from 34.9 to 6.8 J/kg K with increasing Co concentration at a low magnetic field of 0-2 T, the thermal and magnetic hysteresis loss reduces remarkably, which is very important for the magnetic refrigerant near room temperature.     

Low temperature magnetization behavior in Co36Fe36Si3Al1Nb4B20 (at%) nanostructured alloy

The investigation addresses low temperature magnetization behavior in Co₃₆Fe₃₆Si₃Al₁Nb₄B₂₀ alloy ribbons in their as-spun as well as annealed state. Optimum heat treatment at 875 K led to nanocrystallization whereby bcc-(FeCo)SiAl nanoparticles were dispersed in an amorphous matrix as evidenced from transmission electron microscopy. Low temperature magnetization studies were carried out in the range 77-300 K. Using the method of mathematical fittings, magnetization extrapolated to 0 K was obtained. The dependence of the magnetization with respect to temperature of BT^3/2 was used to determine the Bloch coefficient “B” and spin wave stiffness constant “D”. Magnetic softening revealed by lowering in the coercivity in the optimum nanostructured state was also the cause of a drop in the stiffness constant. The range of exchange interaction given by D/T_C was higher in the nanostructured state compared to the as-spun amorphous state. The effect of nanocrystallization and the resulting ferromagnetic coupling was further evidenced by low temperature magnetization studies.     

Magnetic properties of RPd5Al2 (R=Y, Ce, Pr, Nd, Sm, Gd)

Polycrystalline samples of a new rare-earth series RPd₅Al₂ crystallizing in the tetragonal ZrNi₂Al₅-type structure have been prepared. Their physical properties by electrical resistivity ρ, magnetic susceptibility χ, magnetization M and specific heat C_p measurements are reported. The ingots are composed of elongated grains preferentially aligned in the c direction; therefore, measurements were conducted parallel and perpendicular to the grains. Antiferromagnetic ordering appears in R=Ce, Nd, Gd, and Sm at low temperatures. CePd₅Al₂ has two AFM transitions at 4.1 and 2.9 K and ρ(T) indicates a Kondo metal behavior with large anisotropy. In PrPd₅Al₂ no magnetic transition was observed down to 0.4 K. The C_p(T) shows a broad peak around 13 K due to the CEF effect, suggesting a non-magnetic singlet ground state. In NdPd₅Al₂, χ(T) shows anisotropy and the C_p(T) shows a sharp peak at 1.2 K. The magnetic entropy at 3 K is very close to Rln2, indicating a Kramers doublet ground state. In SmPd₅Al₂, C_p(T) shows a magnetic transition at 1.7 K. C_p(T) for GdPd₅Al₂ shows a peak at 6 K, followed by a broad anomaly around 3 K. Within this series, T_N's for CePd₅Al₂ and NdPd₅Al₂ clearly deviate from the relation predicted by de Gennes scaling, which is ascribed to the CEF effect.     

Crystal structure and structural transition caused by charge-transfer phase transition for iron mixed-valence complex (n-C3H7)4N[FeFe(dto)3] (dto=C2O2S2)

(n-C₃H₇)₄N[Fe^IIFe^III(dto)₃] shows a new type of first order phase transition called charge-transfer phase transition around 120 K, where the charge transfer between Fe^II and Fe^III occurs reversibly. Recently, we have succeeded in obtaining single crystals of the title complex and determined the crystal structure at room temperature. Crystal data: space group P6₃, Z=2. Moreover, we have investigated the structural transition caused by the charge-transfer phase transition by means of powder X-ray diffraction measurement. When the temperature is decreased, the a-axis, which corresponds to the hexagonal ring size in two-dimensional honeycomb network structure of [Fe^IIFe^III(dto)₃]_∞, contracts by 0.1 Å at the charge-transfer transition temperature (T_CT), while the c-axis, perpendicular to the honeycomb network layer, elongates by 0.1 Å at T_CT. Consequently, when the temperature is decreased, the unit cell volume decreases without noticeable anomaly around T_CT, which is responsible for the quite small vibrational contribution to the entropy change, compared with usual spin crossover transition. Thus, the charge-transfer phase transition around 120 K for (n-C₃H₇)₄N[Fe^IIFe^III(dto)₃] is regarded as spin entropy driven phase transition.     

Mössbauer study of antiferromagnetic CuFeO2

We have studied the magnetic spin structure of antiferromagnetic CuFeO₂ by X-ray diffraction (XRD) and Mössbauer spectroscopy. Its crystal structure determined by XRD analysis was a rhombohedral structure (space group R-3m) and lattice constants a₀ and c₀ were 3.0333 and 17.1595 Å, respectively. In spite of 4-Fe sublattices in a delafossite CuFeO₂, its Mössbauer spectra were analyzed with 1-set (6-Lorentzian lines) below 10 K due to the collinear-commensurate spin structure, but the spectra were fitted with 4-sextet above 10 K due to the incommensurate spin structure. This phenomenon was attributed to the spin–lattice relaxation effect. Magnetic Néel temperature was also determined at 18 K, which corresponded to the high-spin Fe³⁺ valance state. On the other hand, CuFe_0.98Al_0.02O₂ powder with a noncollinear spin structure was fitted with 4-sextet at 4.2 K.     

Thermomagnetic transitions and coercivity mechanism in bulk composite Nd60Fe30Al10 alloys

The thermomagnetic behaviour (within the temperature range 553-300 K) for the bulk composite Nd₆₀Fe₃₀Al₁₀ alloy is described in terms of a transition from paramagnetic to superferromagnetic state at T=553 K, followed by a ferromagnetic ordering for T<473 K. For the superferromagnetic regime, the alloy thermomagnetic response was associated to a homogeneous distribution of magnetic clusters with mean magnetic moment and size of 1072 μ_B and 2.5 nm, respectively. For T<473 K, a pinning model of domain walls described properly the alloy coercivity dependence with temperature, from which the domain wall width and the magnetic anisotropy constant were estimated as being of ≈8 nm and ≈10⁵ J/m³, typical values of hard magnetic phases. Results are supported by microstructural and magnetic domain observations.     

Magnetic dynamics of charge ordered Nd0.80Na0.20MnO3 compound

The magnetic dynamics of charge ordered Nd_0.8Na_0.2MnO₃ compound was studied by measuring the temperature variation of magnetization for different magnetic fields up to 7 T and, the field variation of magnetization at different temperatures down to 5 K. This sample exhibits a charge-ordering transition at 180 K, followed by a weak ferromagnetic (FM) transition at around 100 K and a spin glass like transition below 40 K. Suppression of charge-ordering and spin glass like transition and increase in FM T_C were observed with an increase in magnetic field. A reversible metamagnetic transition above a threshold field (H_f) of 4.5 T was observed at 130 K, followed by a saturation magnetization of 3.2 μ_B/f.u. However at 5 K, an irreversible field induced first order phase transition from charge ordered state to FM state was observed at H_f=5 T. For comparison, the temperature and field variations of magnetization were studied on a FM compound from the same series with the composition Nd_0.90Na_0.10MnO₃. A clear FM transition with a T_C of 113 K and a saturation magnetization of 4.3 μ_B/f.u was observed.     

Low temperature study of micrometric powder of melted Fe50Mn10Al40 alloy

Melted Fe₅₀Mn₁₀Al₄₀ alloy powder with particle size less than 40 μm was characterized at room temperature by XRD, SEM and XPS; and at low temperatures by Mössbauer spectrometry, ac susceptibility, and magnetization analysis. The results show that the sample is BCC ferromagnetic but with a big contribution of paramagnetic sites, and presents super-paramagnetic and re-entrant spin-glass phases with critical temperatures of 265 and 35 K, respectively. The presence of the different phases detected is due to the disordered character of the sample and the competitive magnetic interactions. The obtained values of the saturation magnetization and the coercive field as a function of temperature present a behavior which indicates a ferromagnetic phase. However, the behavior of the FC curve and that of the coercive field as a function of temperature suggest that the dipolar magnetic interaction between particles contributes to the internal magnetic field in the same way as was reported for nanoparticulate powders.     

Magnetoelastic properties of GdMn6Sn6 intermetallic compound

We studied the thermal expansion and magnetostriction of polycrystalline samples of GdMn₆Sn₆ intermetallic compound with hexagonal HfGe₆Fe₆-type structure in the temperature range of 77-520 K. The thermal expansion measurement of the sample shows anomalous behavior around its T_C=434 K and T_M=309 K, possibly the point of collapse-like reduction of Mn moments. In addition, the isofield curves of anisotropic and volume magnetostriction reveal anomalies around paramagnetic to ferrimagnetic phase transition. The obtained experimental results are discussed in the framework of two-magnetic sublattices by bearing in mind the lattice parameter dependence of interlayer Mn-Mn exchange interaction in this layered compound. From the temperature dependence of magnetostriction values and considering the magnetostriction relation of a hexagonal structure, we attempt to determine the signs of some of the magnetostriction constants as well as a comparison of their orders of magnitude for this compound.     

Influence of boron on the giant magnetocaloric effect of La(Fe0.9Si0.1)13

The influences of boron addition on the phase formation, Curie temperature and magnetic entropy change of the NaZn₁₃-type La(Fe_0.9Si_0.1)₁₃ compound have been investigated. Eight boron containing La(Fe_0.9Si_0.1)₁₃B_x samples were prepared with x=0, 0.03, 0.06, 0.1, 0.2, 0.3, 0.5 and 0.6, respectively. Experimental results show that a small amount of B addition in La(Fe_0.9Si_0.1)₁₃ forms the solid solution NaZn₁₃-type structure phase by substituting B for Si or doping B into interstitial position of the lattice, preserves its giant magnetocaloric effects due to their first-order structural/magnetic transition, as well as increase its Curie temperature T_c slightly. The maximum magnetic entropy changes in the magnetic field change of 0–1.6 T are around 20 J kg^–1 K^–1 for the samples with Boron addition less than 0.3, while improving the Curie temperatures by 2 K.     

Temperature dependence of thermoelectric properties of Ni-doped CoSb3

Temperature dependences of the Hall coefficient, Hall mobility and thermoelectric properties of Ni-doped CoSb₃ have been characterized over the temperature range from 20 to 773 K. Ni-doped CoSb₃ is an n-type semiconductor and the conduction type changes from n-type to p-type at around 450 K. The temperature for the transition from n-type to p-type increased with increasing Ni content x. The Seebeck coefficient reaches a maximum value near the transition temperature. The electrical resistivity indicates that Co_1−xNi_xSb₃ is a typical semiconductor when x≤0.03 and a degenerate semiconductor when x>0.03. Thermal conductivity analyses show that the lattice component is predominant at lower temperatures and carrier and bipolar components become large at temperatures higher than the transition temperature. The thermoelectric figure of merit reaches a maximum value close to the transition temperature and the largest value, 4.67×10⁻⁴ K⁻¹ at 600 K, was obtained for x=0.05.     

Effect of pressure and magnetic field on bilayer La1.25Sr1.75Mn2O7 single crystal

We report the temperature dependence of susceptibility for various pressures, magnetic fields and constant magnetic field of 5 T with various pressures on La_2−2xSr_1+2xMn₂O₇ single crystal to understand the effectiveness of pressure and magnetic field in altering the magnetic properties. We find that the Curie temperature, T_c, increases under pressure (dT_c/dP=10.9 K/GPa) and it indicates the enhancement of ferromagnetic phase under pressure up to 2 GPa. The magnetic field dependence of T_c is about 26 K for 3 T. The combined effect of pressure and constant magnetic field (5 T) shows dT_c/dP=11.3 K/GPa and the peak structure is suppressed and broadened. The application of magnetic field of 5 T realizes 3D spin ordered state below T_c at atmospheric pressure. Both peak structure in χ_c and 3D spin ordered state are suppressed, and changes to 2D-like spin ordered state by increase of pressure. These results reveal that the pressure and the magnetic field are more competitive in altering the magnetic properties of bilayer manganite La_1.25Sr_1.75Mn₂O₇ single crystal.     

Magnetic and transport properties of Pr2Pd3Si5

We have investigated the magnetic and transport properties of a new ternary intermetallic compound Pr₂Pd₃Si₅ which forms in U₂Co₃Si₅-type orthorhombic structure (space group Ibam). At low field (0.01 T) magnetic susceptibility exhibits an abrupt increase below 7 K and peaks at 5 K, revealing a magnetic phase transition. The onset of magnetic order is also confirmed by well defined anomalies in the specific heat and electrical resistivity data. Apart from the sharp λ-type anomaly, magnetic part of specific heat also shows a broad Schottky-type hump due to crystal field effect. Magnetoresistance data as a function of temperature exhibits a pronounced peak in paramagnetic state which could be interpreted in terms of crystal field effect and short-range ferromagnetic correlations.     

Nanocrystalline FeAl intermetallics obtained in mechanically alloyed Fe50Al40Ni10 powder

B2-Fe₄₇Al₅₃ intermetallics has been produced by mechanical alloying in a planetary ball mill, using elemental Fe, Al and Ni powder mixture. The microstructural and magnetic properties of the mechanically alloyed Fe₅₀Al₄₀Ni₁₀ powdered samples were investigated by X-ray diffraction and ⁵⁷Fe Mössbauer spectrometry at 300 and 77 K. As resulted from the X-ray diffraction studies, the ordered B2 structure was formed in the Fe₅₀Al₄₀Ni₁₀ powder, together with the bcc α_i-Fe(Al, Ni) (i = 1, 2) solid solutions. Further milling led to a partial disordering of B2-Fe₄₇Al₅₃; it has undergone an order–disorder transition which is characterized by an expansion of the volume Δa₀ (lattice disorder) and a magnetic transition from the paramagnetic to ferromagnetic state which is characterized by strong ferromagnetic interactions in the alloy. The nanocrystalline bcc α_i-Fe(Al, Ni) solid solution was ferromagnetic with a mean crystallite size of 6 nm.     

Electrical transport of (1−x)La0.7Ca0.3MnO3+xAl2O3 composites

We report the resistivity (ρ)-temperature (T) patterns in (1-x)La_0,7Ca_0,3MnO₃+xAl₂O₃ composites (0≤x≤0.05) over a temperature regime of 50-300 K. Al₂O₃ addition has increased the resistivity of these composites. The Curie temperature (T_C) is almost independent on the Al₂O₃ content and is about 250 K for all the samples, while the metal-insulator transition temperature (T_MI) decreases with increasing Al₂O₃ content. Based on the phenomenological equation for conductivity under a percolation approach, which is dependent on the phase segregation of ferromagnetic metallic clusters and paramagnetic insulating regions, we fitted the experimental data (ρ−T) from 50 to 300 K and find that the activation barrier increases as Al₂O₃ content increases.     

Evidence of glassy ferromagnetic phase and kinetic arrest of electronic phase in Sm0.35Pr0.15Sr0.5MnO3 manganites

The effect of doping of rare earth Pr³⁺ ion as a replacement of Sm³⁺ in Sm_0.5Sr_0.5MnO₃ is investigated. Temperature dependent dc and ac magnetic susceptibility, resistivity, magnetoresistance measurements on chemically synthesized (Sm_0.5−xPr_x)Sr_0.5MnO₃ show various unusual features with doping level x=0.15. The frequency independent ferromagnetic to paramagnetic transition at higher temperature (∼191 K) followed by a frequency dependent reentrant magnetic transition at lower temperature (∼31 K) has been observed. The nature of this frequency dependent reentrant magnetic transition is described by a critical slowing down model of spin glasses. From non-linear ac susceptibility measurements it has been confirmed that the finite size ferromagnetic clusters are formed as a consequence of intrinsic phase separation, and undergo spin glass-like freezing below a certain temperature. There is an unusual observation of a 2nd harmonic peak in the non-linear ac susceptibility around this reentrant magnetic transition at low temperature (∼31 K). Arrott plots at 10 and 30 K confirm the existence of glassy ferromagnetism below this low temperature reentrant transition. Electronic- and magneto-transport measurements show a strong magnetic field—temperature history dependence and strong irreversibility with respect to the sweeping of magnetic field. These results are attributed to the effect of phase separation and kinetic arrest of the electronic phase in this phase separated manganite at low temperatures.     

Low temperature magnetoresistance in La1.32Sr1.68Mn2O7 layered manganite under hydrostatic pressure

The La_1.32Sr_1.68Mn₂O₇ layered manganite system has been studied by the low temperature electrical resistance and magnetoresistance under hydrostatic pressure up to 25 kbar. We have observe both, a Curie temperature (T_C) and a metal-insulator transition (T_MI) at 118 K in the ambient pressure. The applied pressure shifts the T_MI to higher temperature values and induces a second metal-insulator transition (T²_MI) at 90 K, in the temperature dependence of resistivity measurements. Also, the pressure suppresses the peak resistance abruptly at T_C. When an external field of 5 T is applied, we have observed a large negative magnetoresistance of 300% at the transition temperature and a 128% at 4.5 K. However, the increased pressure decreases the magnetoresistance ratio gradually. When the pressure reaches its maximum available value of 25 kbar, the magnetoresistance ratio decreases at a rate of 1.3%/kbar. From our experimental results, the decrease of magnetoresistance ratio with pressure is explained by the pressure induced canted spin state which is not favor for the spin polarized intergrain tunneling in layered manganites.     

Effect of magnetic annealing on phonon behaviors of nanocrystalline BiFeO3

Influence of magnetic annealing at 823 K up to 10 T (T) on the phonon behaviors of nanocrystalline BiFeO₃ was investigated by Raman spectroscopy. The frequencies of fundamental Raman modes increase obviously with increasing annealing magnetic field, and the intensity of the 1260 cm⁻¹ two-phonon mode decreases. The pronounced anomalies of Raman phonon modes under magnetic annealing are attributed to the change of the spin-phonon coupling due to the modulation of spiral spin order. Furthermore, the temperature dependence of Raman peak positions, for the two prominent modes (147 and 176 cm⁻¹), show no notable anomaly around T_N except the sample annealed under 10 T magnetic field; meanwhile, in this sample, another obvious phonon anomaly occurs at ∼150 K (another magnetic phase transition point), which indicate that stronger magnetic annealing with 10 T intensely enhances the spin-phonon coupling, and possibly increases magnetoelectric coupling of nanocrystalline BiFeO₃ due to severely modulation of spiral spin order.