Influence of Al-doping on the structure and optical properties of ZnO films

Al-doped ZnO (ZnO:Al) thin films with c-axis preferred orientation were deposited on glass substrates using the radio frequency reactive magnetron sputtering technique. The effect of Al concentrations on the microstructure and the luminescence properties of the ZnO:Al thin films were studied by atomic force microscopy (AFM), X-ray diffraction (XRD), and fluorescence spectrophotometer. The results showed that the crystallization of the films was promoted by appropriate Al concentrations; the photoluminescence spectra (PL) of the samples were measured at room temperature. Strong blue peak located at 437 nm (2.84 eV) and two weak green peaks located at about 492 nm (2.53 eV) and 524 nm (2.37 eV) were observed from the PL spectra of the four samples. The origin of these emissions was discussed. In addition, absorption and transmittance properties of the samples were researched by UV spectrophotometer; the UV absorption edge shifted to a shorter wavelength first as Al was incorporated, and then to a longer wavelength with the increasing Al concentrations. The optical band gaps calculated based on the quantum confinement model are in good agreement with the experimental values.     

Properties of ZnO thin films deposited on (glass,ITO and ZnO:Al) substrates

ZnO thin films were deposited on glass, ITO (In₂O₃; Sn) and on ZnO:Al coated glass by spray pyrolysis. The substrates were heated at 350 °C. Structural characterization by X-ray diffraction (XRD) measurements shows that films crystallize in hexagonal structure with a preferential orientation along (0 0 2) direction. XRD peak-shift analysis revealed that films deposited on glass substrate (−0.173) were compressive, however, films deposited onto ITO (0.691) and on ZnO:Al (0.345) were tensile. Scanning electron microscopies (SEM) show that the morphologies of surface are porous in the form of nanopillars. The transmittance spectra indicated that the films of ZnO/ITO/glass and ZnO/ZnO:Al/glass exhibit a transmittance around 80% in the visible region. An empirical relationship modeled by theoretical numerical models has been presented for estimating refractive indices (n) relative to energy gap. All models indicate that the refractive index deceases with increasing energy band gap (E_g).     

Growth characteristics and properties of ZnO:Ga thin films prepared by pulsed DC magnetron sputtering

Transparent conductive ZnO:Ga thin films were deposited on Corning 1737 glass substrate by pulsed direct current (DC) magnetron sputtering. The effects of process parameters, namely pulse frequency and film thickness on the structural and optoelectronic properties of ZnO:Ga thin films are evaluated. It shows that highly c-axis (0 0 2) oriented polycrystalline films with good visible transparency and electrical conductivity were prepared at a pulsed frequency of 10 kHz. Increasing the film thickness also enlarged the grain size and carrier mobility which will subsequently lead to the decrease in resistivity. In summary, ZnO:Ga thin film with the lowest electrical resistivity of 2.01 × 10⁻⁴ Ω cm was obtained at a pulse frequency of 10 kHz with 500 nm in thickness. The surface RMS (root mean square) roughness of the film is 2.9 nm with visible transmittance around 86% and optical band gap of 3.83 eV.     

Aluminium-induced crystallization of amorphous silicon films deposited by DC magnetron sputtering on glasses

Amorphous silicon (a-Si) and hydrogenated amorphous silicon (a-Si:H) films were deposited by DC magnetron sputtering technique with argon and hydrogen plasma mixture on Al deposited by thermal evaporation on glass substrates. The a-Si/Al and a-Si:H/Al thin films were annealed at different temperatures ranging from 250 to 550 °C during 4 h in vacuum-sealed bulb. The effects of annealing temperature on optical, structural and morphological properties of as-grown as well as the vacuum-annealed a-Si/Al and a-Si:H/Al thin films are presented in this contribution. The averaged transmittance of a-Si:H/Al film increases upon increasing the annealing temperature. XRD measurements clearly evidence that crystallization is initiated at 450 °C. The number and intensity of diffraction peaks appearing in the diffraction patterns are more important in a-Si:H/Al than that in a-Si/Al layers. Results show that a-Si:H films deposited on Al/glass crystallize above 450 °C and present better crystallization than the a-Si layers. The presence of hydrogen induces an improvement of structural properties of poly-Si prepared by aluminium-induced crystallization (AIC).     

Fabrication and electrical characterization of nanocrystalline ZnO/Si heterojunctions

Nanocrystalline zinc oxide (nc-ZnO) films were prepared by a sol-gel process on p-type single-crystalline Si substrates to fabricate nc-ZnO/p-Si heterojunctions. The structure and morphology of ZnO films on Si substrates, which were analyzed by X-ray diffraction (XRD) spectroscopy and atomic force microscopy (AFM), showed that ZnO films consisted of 50-100 nm polycrystalline nanograins with hexagonal wurtzite structure. The electrical transport properties of the nc-ZnO/p-Si heterojunctions were investigated by temperature-dependent current-voltage (I-V) measurements and room temperature capacitance-voltage measurements. The temperature-dependent I-V characteristics revealed that the forward conduction was determined by multi-step tunneling current, and the activation energy of saturation current was about 0.26 eV. The 1/C²-V plots indicated the junction was abrupt and the junction built-in potential was 1.49 V at room temperature.     

Ultraviolet photoconductive detector based on Al doped ZnO films prepared by sol-gel method

We report a study on the fabrication and characterization of ultraviolet photodetectors based on ZnO:Al films. Using sol-gel technique, highly c-axis oriented ZnO films with 5 mol% Al doping were deposited on Si(1 1 1) substrates. The photoconductive UV detectors based on ZnO:Al thin films, having a metal-semiconductor-metal (MSM) structure with interdigital (IDT) configuration, were fabricated by using Au as a contact metal. The characteristics of dark and photocurrent of the UV detector and the UV photoresponse of the detector were investigated. The linear current-voltage (I-V) characteristics under both forward and reverse bias exhibit ohmic metal-semiconductor contacts. Under illumination using monochromatic light with a wavelength of 350 nm, photo-generated current was measured at 58.05 μA at a bias of 6 V. The detector exhibits an evident wide-range spectral responsivity and shows a trend similar to that in transmittance and photoluminescence spectrum.     

Room temperature transparent conducting oxides based on zinc oxide thin films

Doped zinc oxide thin films are grown on glass substrate at room temperature under oxygen atmosphere, using pulsed laser deposition (PLD). O₂ pressure below 1 Pa leads to conductive films. A careful characterization of the film stoichiometry and microstructure using X-ray diffraction (XRD), X-ray photoelectron spectroscopy (XPS) and scanning electron microscopy (SEM) concludes on a decrease in crystallinity with Al and Ga additions (≤3%). The progressive loss of the (0 0 2) orientation is associated with a variation of the c parameter value as a function of the film thickness and substrate nature. ZnO:Al and ZnO:Ga thin films show a high optical transmittance (>80%) with an increase in band gap from 3.27 eV (pure ZnO) to 3.88 eV and 3.61 eV for Al and Ga doping, respectively. Optical carrier concentration, optical mobility and optical resistivity are deduced from simulation of the optical data.     

Effect of doping concentration on the structural and optical properties of pure and tin doped zinc oxide thin films by nebulizer spray pyrolysis (NSP) technique

Pure and tin doped zinc oxide (Sn:ZnO) thin films were prepared for the first time by NSP technique using aqueous solutions of zinc acetate dehydrate, tin (IV) chloride fendahydrate and methanol. X-ray diffraction patterns confirm that the films are polycrystalline in nature exhibiting hexagonal wurtzite type, with (0 0 2) as preferred orientation. The structural parameters such as lattice constant (‘a’ and ‘c’), crystallite size, dislocation density, micro strain, stress and texture coefficient were calculated from X-ray diffraction studies. Surface morphology was found to be modified with increasing Sn doping concentration. The ZnO films have high transmittance 85% in the visible region, and the transmittance is found to be decreased with the increase of Sn doping concentration. The corresponding optical band gap decreases from 3.25 to 3.08 eV. Room temperature photoluminescence reveals the sharp emission of strong UV peak at 400 nm (3.10 eV) and a strong sharp green luminescence at 528 nm (2.34 eV) in the Sn doped ZnO films. The electrical resistivity is found to be 10⁶ Ω-cm at higher temperature and 10⁵ Ω-cm at lower temperature.     

Effect of substrate and annealing on the structural and optical properties of ZnO:Al films

ZnO:Al thin films with c-axis preferred orientation were deposited on glass and Si substrates using RF magnetron sputtering technique. The effect of substrate on the structural and optical properties of ZnO:Al films were investigated. The results showed a strong blue peak from glass-substrate ZnO:Al film whose intensity became weak when deposited on Si substrate. However, the full width at half maxima (FWHM) of the Si-substrate ZnO:Al (0 0 2) peaks decreased evidently and the grain size increased. Finally, we discussed the influence of annealing temperature on the structural and optical properties of Si-substrate ZnO:Al films. After annealing, the crystal quality of Si-substrate ZnO:Al thin films was markedly improved and the intensity of blue peak (∼445 nm) increased noticeably. This observation may indicate that the visible emission properties of the ZnO:Al films are dependent more on the film crystallinity than on the film stoichiometry.     

The influence of using different substrates on the structural and optical characteristics of ZnO thin films

ZnO thin films with thikness d = 100 nm were deposited onto different substrates such as glass, kapton, and silicon by radio frequency magnetron sputtering. The structural analyses of the films indicate they are polycrystalline and have a wurtzite (hexagonal) structure.The ZnO layer deposited on kapton substrate shows a stronger orientation of the crystallites with (0 0 2) plane parallel to the substrate surface, as compared with the other two samples of ZnO deposited on glass and silicon, respectively.All three layers have nanometer-scale values for roughness, namely 1.7 nm for ZnO/glass, 2.4 nm for ZnO/silicon, and 6.8 nm for ZnO/kapton. The higher value for the ZnO layer deposited on kapton substrate makes this sample suitable for solar cells applications. Transmission spectra of these thin films are strongly influenced by deposition conditions. With our deposition conditions the transparent conducting ZnO layer has a good transmission (78-88%) in VIS and NIR domains. The values of the energy gap calculated from the absorption spectra are 3.23 eV for ZnO sample deposited onto glass substrate and 3.30 eV for the ZnO sample deposited onto kapton polymer foil substrate. The influence of deposition arrangement and oxidation conditions on the structural, morphological, and optical properties of the ZnO films is discussed in the present paper.     

Effects of the substrate and oxygen partial pressure on the microstructures and optical properties of Ti-doped ZnO thin films

Ti-doped ZnO (ZnO:Ti) thin films were deposited on the glass and Si substrates using radio frequency reactive magnetron sputtering. The effects of substrate on the microstructures and optical properties of ZnO:Ti thin films were investigated by X-ray diffraction (XRD), scanning electron microscopy (SEM) and a fluorescence spectrophotometer. The structural analyses of the films indicated that they were polycrystalline and had a hexagonal wurtzite structure on different substrates. When ZnO:Ti thin film was deposited on Si substrate, the film had a c-axis preferred orientation, while preferred orientation of ZnO:Ti thin film deposited on glass substrate changed towards (1 0 0). Finally, we discussed the influence of the oxygen partial pressures on the structural and optical properties of glass-substrate ZnO:Ti thin films. At a high ratio of O₂:Ar of 18:10 sccm, the intensity of (0 0 2) diffraction peak was stronger than that of (1 0 0) diffraction peak, which indicated that preferred orientation changed with the increase of O₂:Ar ratios. The average optical transmittance with over 93% in the visible range was obtained independent of the O₂:Ar ratio. The photoluminescence (PL) spectra measured at room temperature revealed four main emission peaks located at 428, 444, 476 and 527 nm. Intense blue-green luminescence was obtained from the sample deposited at a ratio of O₂:Ar of 14:10 sccm. The results showed that the oxygen partial pressures had an important influence for PL spectra and the origin of these emissions was discussed.     

A comparative study on structural and optical properties of ZnO and Al-doped ZnO thin films obtained by ultrasonic spray method using different solvents

Transparent conducting ZnO and Al doped ZnO thin films were deposited on glass substrate by ultrasonic spray method. The thin films with concentration of 0.1 M were deposited at 350 °C with 2 min of deposition time. The effects of ethanol and methanol solution before and after doping on the structural, optical and electrical properties were examined. The DRX analyses indicated that ZnO films have nanocrystalline nature and hexagonal wurtzite structure with (1 0 0) and (0 0 2) preferential orientation corresponding to ZnO films resulting from methanol and ethanol solution, respectively. The crystallinity of the thin films improved with methanol solution after doping to (0 0 2) oriented. All films exhibit an average optical transparency about 90%, in the visible range. The band gaps values of ZnO thin films are increased after doping from 3.10 to 3.26 eV and 3.27 to 3.30 eV upon Al doping obtained by ethanol and methanol solution, respectively. The electrical conductivity increase from 7.5 to 15.2 (Ω cm)⁻¹ of undoped to Al doped ZnO thin films prepared by using ethanol solution. However, for the methanol solution; the electrical conductivity of the film is stabilized after doping.     

Nano-star formation in Al-doped ZnO thin film deposited by dip-dry method and its characterization using atomic force microscopy, electron probe microscopy, photoluminescence and laser Raman spectroscopy

Zinc oxide doped with Al (AZO) thin films were prepared on borosilicate glass substrates by dip and dry technique using sodium zincate bath. Effects of doping on the structural and optical properties of ZnO film were investigated by XRD, EPMA, AFM, optical transmittance, PL and Raman spectroscopy. The band gap for ZnO:Al (5.0 at. wt.%) film was found to be 3.29 eV compared with 3.25 eV band gap for pure ZnO film. Doping with Al introduces aggregation of crystallites to form micro-size clusters affecting the smoothness of the film surface. Al³⁺ ion was found to promote chemisorption of oxygen into the film, which in turn affects the roughness of the sample. Six photoluminescence bands were observed at 390, 419, 449, 480, 525 and 574 nm in the emission spectra. Excitation spectra of ZnO film showed bands at 200, 217, 232 and 328 nm, whereas bands at 200, 235, 257 and 267 nm were observed for ZnO:Al film. On the basis of transitions from conduction band or deep donors (CB, Zn_i or V_OZn_i) to valence band and/or deep acceptor states (VB, V_Zn or O_i or O_Zn), a tentative model has been proposed to explain the PL spectra. Doping with Al³⁺ ions reduced the polar character of the film. This has been confirmed from laser Raman studies.     

Highly conductive and transparent laser ablated nanostructured Al: ZnO thin films

Al doped ZnO thin films are prepared by pulsed laser deposition on quartz substrate at substrate temperature 873 K under a background oxygen pressure of 0.02 mbar. The films are systematically analyzed using X-ray diffraction, atomic force microscopy, micro-Raman spectroscopy, UV-vis spectroscopy, photoluminescence spectroscopy, z-scan and temperature-dependent electrical resistivity measurements in the temperature range 70-300 K. XRD patterns show that all the films are well crystallized with hexagonal wurtzite structure with preferred orientation along (0 0 2) plane. Particle size calculations based on XRD analysis show that all the films are nanocrystalline in nature with the size of the quantum dots ranging from 8 to 17 nm. The presence of high frequency E₂ mode and longitudinal optical A₁ (LO) modes in the Raman spectra suggest a hexagonal wurtzite structure for the films. AFM analysis reveals the agglomerated growth mode in the doped films and it reduces the nucleation barrier of ZnO by Al doping. The 1% Al doped ZnO film presents high transmittance of ∼75% in the visible and near infrared region and low dc electrical resistivity of 5.94 × 10⁻⁶ Ω m. PL spectra show emissions corresponding to the near band edge (NBE) ultra violet emission and deep level emission in the visible region. Nonlinear optical measurements using the z-scan technique shows optical limiting behavior for the 5% Al doped ZnO film.     

Effects of Ti-doped concentration on the microstructures and optical properties of ZnO thin films

The Ti-doped ZnO (ZnO:Ti) thin films have been deposited on glass substrates by radio frequency (RF) reactive magnetron sputtering technique with different Ti doping concentrations. The effect of Ti contents on the crystalline structure and optical properties of the as-deposited ZnO:Ti films was systematically investigated by X-ray diffraction (XRD), scanning electronic microscopy (SEM) and fluorescence spectrophotometer. The XRD measurements revealed that all the films had hexagonal wurtzite type structure with a strong (100) preferential orientation and relatively weak (002), (101), and (110) peaks. It was found that the intensity of the (100) diffraction peaks was strongly dependent on the Ti doping concentration. And the full width at half-maximum (FWHM) of (002) diffraction peaks constantly changed at various Ti contents, which decreased first and then increased, reaching a minimum of about 0.378° at 1.43 at.% Ti. The morphologies of ZnO:Ti films with 1.43 at.% Ti showed a denser texture and better smooth surface. All the films were found to be highly transparent in the visible wavelength region with an average transmittance over 90%. Compared with E_g = 3.219 eV for pure ZnO film, all the doping samples exhibited a blue-shift of E_g. It can be attributed to the incorporation of Ti atoms and raising the concentration of carriers. Five emission peaks located at 412, 448, 486, 520, and 550 nm were observed from the photoluminescence spectra measured at room temperature and the origin of these emissions was discussed.     

Oxygen influence on sputtered high rate ZnO:Al films from dual rotatable ceramic targets

In this study, the influence of oxygen on high rate (up to 110 nm m/min) sputtered aluminum doped zinc oxide films (ZnO:Al) was systematically investigated. Different oxygen gas flows from 0 sccm to 8 sccm were inputted into the chamber during the preparation of ZnO:Al films from dual rotatable ceramic targets under high discharge power (14 kW). The resistivity increases from 4.2 × 10⁻⁴ Ω cm to 4.3 × 10⁻² Ω cm with the rising oxygen gas flow. While both the carrier concentration and mobility drop by one order of magnitude from 3.4 × 10²⁰ cm⁻³ to 2.5 × 10¹⁹ cm⁻³ and from 43.5 cm²/V s to 5.6 cm²/V s, respectively. The as-grown ZnO:Al films and after-etched ZnO:Al films after a chemical wet etching step in diluted HCl solution (0.5%) exhibit different surface structures. All films show high light transmission and low light absorption but different light scattering properties (diffusion and haze) because of different surface structures. Moreover, ZnO:Al films display different optical bandgaps between 3.51 eV and 3.27 eV, which are corresponding to different carrier concentrations. The variation of mobility and morphology is related with chemisorption of oxygen in the grain boundaries as well as high energetic oxygen ions bombardment.     

Influence of substrate temperature and Cobalt concentration on structural and optical properties of ZnO thin films prepared by Ultrasonic spray technique

Pure and Cobalt doped zinc oxide were deposited on glass substrate by Ultrasonic spray method. Zinc acetate dehydrate, Cobalt chloride, 4-methoxyethanol and monoethanolamine were used as a starting materials, dopant source, solvent and stabilizer, respectively. The ZnO samples and ZnO:Co with Cobalt concentration of 2 wt.% were deposited at 300, 350 and 400 °C. The effects of substrate temperature and presence of Co as doping element on the structural, electrical and optical properties were examined. Both pure and Co doped ZnO samples are (0 0 2) preferentially oriented. The X-ray diffraction results indicate that the samples have polycrystalline nature and hexagonal wurtzite structure with the maximum average crystallite size of ZnO and ZnO:Co were 33.28 and 55.46 nm. An increase in the substrate temperature and presence doping the crystallinity of the thin films increased. The optical transmittance spectra showed transmittance higher than 80% within the visible wavelength region. The band gap energy of the thin films increased after doping from 3.25 to 3.36 eV at 350 °C.     

Low-temperature deposited ZnO thin films on the flexible substrate by cathodic vacuum arc technology

In this paper, un-doped zinc oxide (ZnO) films with various thicknesses (150, 250, 350, 450 and 550 nm) were successfully prepared onto PET substrates using cathodic vacuum arc technique at low-temperature (<40 °C). Their microstructure, optical and electrical properties were investigated and discussed. The films showed (0 0 2) peaks, an average transmittance over 80% in the visible region. Calculated values of the band gap are around 3.29-3.33 eV when the film thickness increased, indicating a slight blue shift of optical transmission spectra. The lowest resistivity about 5.26 × 10⁻³ Ω cm could be achieved for the un-doped ZnO film with thickness of 550 nm.     

Relationship between the photoluminescence and conductivity of undoped ZnO thin films grown with various oxygen pressures

The pulsed laser deposition (PLD) technique is used to deposit undoped ZnO thin films on glass substrates at 150 °C with different oxygen pressures of 40, 80, 100 and 150 mTorr. X-ray diffraction (XRD) and atomic force microscopy (AFM) studies indicated that the obtained ZnO thin films were hexagonal wurtzite-type structures with strong (0 0 2) c-axis orientation. The relationship between photoluminescence and the conductivity of the ZnO thin films grown by pulsed laser deposition at various oxygen pressures was also discussed. The intensity of the deep-level-emission (DLE) and conductivity generally increased as the oxygen pressure decreased. The intensity of DLE peak was generally proportional to the conductivity. The band gap energy values, determined from transmittance spectra, were around 3.30-3.34 eV, and decreased when the oxygen pressure increased.     

Preparation and characterization of Mg-doped ZnO thin films by sol-gel method

Undoped and Mg-doped ZnO thin films were deposited on Si(1 0 0) and quartz substrates by the sol-gel method. The thin films were annealed at 873 K for 60 min. Microstructure, surface topography and optical properties of the thin films have been measured by X-ray diffraction (XRD), atomic force microscope (AFM), UV-vis spectrophotometer, and fluorophotometer (FL), respectively. The XRD results show that the polycrystalline with hexagonal wurtzite structure are observed for the ZnO thin film with Mg:Zn = 0.0, 0.02, and 0.04, while a secondary phase of MgO is evolved for the thin film with Mg:Zn = 0.08. The ZnO:Mg-2% thin film exhibits high c-axis preferred orientation. AFM studies reveal that rms roughness of the thin films changes from 7.89 nm to 16.9 nm with increasing Mg concentrations. PL spectra show that the UV-violet emission band around 386-402 nm and the blue emission peak about 460 nm are observed. The optical band gap calculated from absorption spectra and the resistivity of the ZnO thin films increase with increasing Mg concentration. In addition, the effects of Mg concentrations on microstructure, surface topography, PL spectra and electrical properties are discussed.