Mn3O4包覆对LiNi0.5Mn1.5O4正极材料界面电化学性能的提高

本文采用化学湿磨法，首次将金属氧化物Mn₃O₄包覆于LiNi_0.5Mn_1.5O₄颗粒表面，使得电极材料的电子电导率从1.53×10^-7 S/cm 提高到3.15×10^-5 S/cm. 电化学测试结果表明Mn₃O₄包覆大大提高LiNi_0.5Mn_1.5O₄正极材料的倍率性能和高温循环稳定性. 最佳包覆样品为2.6wt% Mn₃O₄包覆的LiNi_0.5Mn_1.5O₄，在10 C倍率下具有108 mAh/g的高放电容并且在55 °C下100次循环后仍有78%的容量保持率，远大于未包覆样品67%的容量保持率.     

Ba0.98Ce0.8Tm0.2O3-α的离子导电性及其燃料电池性能

用高温固相反应法制备了Ba_0.98Ce_0.8Tm_0.2O_3-α钙钛矿型氧化物固溶体,粉末X射线衍射表明该固溶体为单相. 用交流阻抗谱技术和气体浓差电池方法研究了样品在500～900 oC、不同气体气氛中的导电性,以及该样品为固体电解质的氢-空气燃料电池性能. 该电池能稳定地工作,在900 oC时,电池的最大功率密度为110.2 mW/cm²,高于以Ba_xCe_0.8RE_0.2O₃^- (x≤1, RE=Y, Eu, Ho)为固体电解质的氢-空气燃料电池的功率密度     

聚对苯撑/LiNi0.5Fe2O4纳米复合热电材料的制备及其性能研究

本文以流变相反应法原位合成了聚对苯撑/LiNi_0.5Fe₂O₄纳米复合热电材料,并对其热电性能进行表征,研究了放电等离子烧结时保温时间对其热电性能的影响.结果发现,复合材料铁氧体颗粒粒径为100---300nm,其外部被一层聚对苯撑膜包覆.电子在Fe²⁺和Fe³⁺之间的跳跃机理在铁氧体电导中占主导作用,因此聚对苯撑/LiNi_0.5Fe₂O₄复合材料具有n型导电特性.随着保温时间增加,复合材料电导率基本不变,但热导率逐渐增大且Seebeck系数逐渐减小,导致热电优值系数降低.由于结合了有机物高电导率和低热导率以及无机材料高赛贝克系数的优点,所制备的复合材料热电性能较单一材料有较大提高.     

氧化还原可逆Nb2TiO7复合阴极电解池高温水蒸气电解研究

系统地研究Nb₂TiO₇与Nb_1.33Ti_0.67O₄材料相互转变的氧化还原循环可逆性能,同时研究Nb2TiO7和Nb_1.33Ti_0.67O₄样品随温度和氧分压变化的电导率,并与复合电极对称电池和电解池的电化学性能相关联. 在830 oC下,对Nb_1.33Ti_0.67O₄复合电极电解池进行水蒸气的电解研究测试. 电流电压曲线和电解池短期性能测试表明在低电压下主要为电极的还原和活化过程;而在高电压下主要为水蒸气的电解. 当3%H₂O/Ar/4%H_{2气体通入阴极时电解池水蒸气电解的法拉第效率为98.9%;而当通入气体转换为3%H2O/Ar时效率为89%.}     

针状纳米MnxNi0.5-xZn0.5Fe2O4的共沉淀法制备及表征

通过在碱液中共沉淀Mn²⁺、Ni²⁺和Fe²⁺后制备了棒状的前躯体,前躯体于不同温度煅烧后制得了Mn_xNi_0:5-xZn_0:5Fe₂O₄棒状体. 利用X射线衍射仪和透射电镜对棒状体的物相、形貌及粒径进行了表征,并利用振动样品磁强计对磁性能进行研究. 结果表明长径比大于15的棒状,随着x值的增加,Mn_xNi_0:5-xZn_0:5Fe₂O₄样品的直径增加,长度下降,长径比变小,当x=0.5时其直径在50 nm左右而长径比减小到7～8. 随着x值的增加,样品的矫顽力先增加后减少,x值达到0.4时样品的矫顽力再次增加,当煅烧温度为600 oC,x=0.5时样品的矫顽力最大为134.3 Oe. 饱和磁化强度随着x值的增加先增加后减少,当煅烧温度为800 oC和x=0.2时达到最大为68.5 Oe.     

Ho3+/Yb3+→α-NaYF4单晶的上转换荧光光谱特性

以KF作为助熔剂,采用固液界面温度梯度(70～90 oC/cm),通过改进的助熔剂-坩埚下降法从NaF-YF₃熔体系统中生长出了Ho³⁺/Yb³⁺离子双掺杂的α-NaYF₄单晶体. 在980 nm激光泵浦下可以观察到544 nm的上转换绿光和657和751 nm的上转换红光. 上转换的绿光强度明显强于上转换红光. 通过测量泵浦功率和上转换光的强度之间的关系研究了上转换发光的机理. 当Ho³⁺的掺杂浓度保持为1.0 mol%的情况下,Yb³⁺的浓度为8.08 mol%时上转换强度最强.     

85MeV19F重离子辐照α–Al2O3的空洞研究

5.28×10¹⁶cm^－2 85MeV¹⁹F辐照的αAl₂O₃中,在其热退火过程中采用正电子湮没方法首次观察到了空洞.450℃退火开始产生空洞,550℃到750℃空洞半径约为0.29nm不随温度变化,但浓度随温度增加而增加;高于750℃,空洞半径随温度升高迅速增大,1050℃时空洞的半径达1.10nm.     

脉冲激光沉积温度及氧压对Bi2Sr2Co2Oy热电薄膜晶体结构与电输运性能的影响

利用脉冲激光沉积技术在c-Al₂O₃单晶基片上制备了Bi₂Sr₂Co₂O_y热电薄膜并研究了沉积温度和氧压对薄膜晶体结构及电输运性能的影响.在最佳沉积条件下制备的单相、c轴取向的Bi₂Sr₂Co₂O_y薄膜的室温电阻率ρ和塞贝克系数S分别为2.9mΩ/cm和110μupV/K,其功率因子S²/ρ好于在单晶样品上得到的值.此外,该薄膜在低温下表现出较强的负磁阻效应,在2K,9T时达到了40%.     

掺杂Cs2O的12CaO·7Al2O3型发射材料的制备与特性

研究了掺杂Cs₂O的12CaO·7Al₂O₃(C12A7)型负离子存储发射材料的发射特性、离子发射分支比以及温度对发射强度的影响,同时对该材料的X射线衍射和电子顺磁共振的表征结果进行了分析. C12A7中Cs₂O的掺入不仅降低了发射温度,同时还增强了发射强度. 掺杂Cs₂O后,在800 V/cm的引出场下,发射温度由570 oC降低至500 oC,在700 oC时,发射强度由0.23 μA/cm<     

CO2对Ba0.5Sr0.5Co0.8Fe0.2O3−δ表面氧交换的影响

采 用 了 一 种 新 的 脉 冲 同 位 素 交 换 技 术 , 研 究了CO₂对Ba_0.5Sr_0.5Co_0.8Fe_0.2O_3?δ(BSCF)的表面氧交换动力学的毒害作用．当BSCF暴露于CO₂时,由于在材料表面形成了碳酸盐,其表面交换率严重降低．在低CO₂浓度(1%)时,毒害作用从375 oC开始,并且随着温度的上升而变得更加明显．同时,表面交换动力学的下降导致BSCF在CO₂条件下氧渗透性能快速下降．     

Theoretical analysis and simulation of conjugate heights for dual-conjugate AO system in lidar

A multi-conjugate adaptive optics （MCAO） can offer a possibility of widening field of view （FOV） characterized by the isoplanatic angle, and the choose of conjugate height becomes a basic problem for MCAO, which influences the size of iosplanatic angle. Considering the application of lidar, the isoplanatic angle＇s expressions of two deformable mirrors （DMs） MCAO for uplink and downlink are deduced. The effects of conjugate heights for dual-conjugate AO are thoughtfully discussed, and the isoplanatic angles are further analyzed. The results show that the isopanatic angle varies with the conjugate height and reaches the maximum as the conjugate height is at the optimal altitude. Moreover, the optimal conjugate height changes with the propagation distance.     

Quick single-photon detector with many avalanche photo diodes working on the time division

Due to the limit of response speed of the present single-photon detector, the code rate is still too low to come into practical use for the present quantum key distribution (QKD) system.A new idea is put up to design a quick single-photon detector.This quick single-photon detector is composed of a multi-port optic-fiber splitter and many avalanche photo diodes (APDs).Au of the ports with APDs work on the time division and cooperate with a logic discriminating and deciding unit driven by the clock signal.The operation frequency lies on the number N of ports, and can reach N times of the conventional single-photon detector.The single-photon prompt detection can come true for high repetition-rate pulses.The applying of this detector will largely raise the code rate of the QKD, and boost the commercial use.     

Characterization of PolyA and PolyC mismatches by Raman spectroscopy

A.C mismatches are studied by Raman spectral characterization of PolyA, PolyC, and their equimolar complex in solution of 0.14 mol/L Na ,pH7.0.Experimental results show that A·C mismatches occur to be A/B (mainly A) conformers, and unlike Watson-Crick base pairing, this kind of mismatches is stabilized by only one hydrogen bond involving cytosine N4H2 and adenine N7.The formation of A·C complex makes the base stacking interactions much stronger, and conformation of the backbone more ordered, which leads to obvious Raman hypochromic effect with some shifts in corresponding bands.     

Improvement of four-wave mixing-based wavelength conversion efficiency in dispersion shifted fiber by 40-GHz clock pumping

40-GHz clock modulated signal as a pump to improve the efficiency of four-wave mixing (FWM)-based wavelength conversion in a 26.5-km dispersion shifted fiber (DSF) is investigated. The experimental results demonstrate that the conjugated FWM component has higher intensity with the clock pumping than that with the continuous-wave (CW) light pumping. The improvement of FWM-based wavelength conversion efficiency is negligible when the pump power is less than Brillouin threshold. But when the pump power is greater than Brillouin threshold, the improvement becomes significant and increases with the increment of pump power. The improvement can increase up to 9 dB if pump power reaches 17 dBm.     

Speech enhancement by array crosstalk resistant ANC and spectrum subtraction

Microphone array-based speech enhancement has great importance for speech communications and speech recognition. To reduce the aperture of the microphone array and to increase the effect of the speech enhancement will greatly broaden the application areas of the microphone array. An array crosstalk resistant adaptive noise cancellation method is therefore presented. And then an improved spectral subtraction algorithm is further cascaded to obtain better enhancement results. Theoretic analysis and experiments indicate that the proposed scheme needs only a very small microphone array while it simultaneously achieves a higher SNR improvement. Besides, the proposed scheme can be used in many noisy environments and is easy for real-time implementation.     

Multi-pulse operation of a Kerr-lens mode-locked femtosecond laser

Our experimental results show that the presence of a proper amount of negative group velocity dispersion is essential to multi-pulse operation of a Kerr-lens mode-locked femtosecond laser. We demonstrate that the pulse separations and the number of pulses contained within a cavity round trip are strongly dependent on the initial perturbations. The results allow us to get a better understanding on the influences of the convoluted self-phase modulation and intra-cavity dispersions on the stable multi-pulse oscillation in a Kerr-lens mode-locked femtosecond laser.     

Propagation of Helmholtz-Gauss beams in weak turbulent atmosphere

Based on the Rytov approximation of light propagation in weak turbulent atmosphere,the closed-form expressions of field and average irradiance of each one of the four fundamental families of Helmholtz-Gauss (HzG)beams:cosine-Gauss beams,stationary Mathieu-Gauss beams,stationary parabolic-Gauss beams,and Bessel-Gauss beams,which are propagating in weak turbulent atmosphere,are obtained.The results show that the field and average irradiance can be written as the product of four factors:complex amplitude depending on the z-coordinate only,a Ganssian beam.a factor of complex phase perturbation induced by atmospheric turbulence,and a complex scaled version of the transverse shape of the non-diffracting beam.The effect of weak atmospheric turbulence on irradiance distribution of the HzG beam can be ignored.     

An effective method for reducing speckle noise in digital holography

An effective method for reducing the speckle noise in digital holography is proposed in this paper.Different from the methods based on classical filtering technique,it utilizes the multiple holograms which are generated by rotating the illuminating light continuously.The intensity images reconstructed by a series of holograms generated by rotating the illuminating light possess different speckle patterns.Hence by properly averaging the reconstructed intensity fields,the speckle noises can be reduced greatly.Experimental results show that the proposed method is simple and effective to reduce speckle noise in digital holography.     

Influence of purity of HfO2 on reflectance of ultraviolet multilayer

The impurities in two kinds of HfO2 materials and in their corresponding single layer thin films were determined through glow discharge mass spectrum technology and secondary ion mass spectrometry(SIMS) equipment respectively.It was found that ZrO2 was the main impurity in the two kinds of HfO2 either in the original HfO2 materials or in the electron beam deposited films.In addition,the difference of Zr content in the two kinds of HfO2 single laver films was much laxger than that of the other impurities such as Ti and Fe.which showed that it was just ZrO2 that made the difference between the optical performance of the film products including the two kinds of HfO2.With these two kinds of HfO2 and the same kind of SiO2.we deposited HfO2/SiO2 multilayer reflective coatings at the wavelength of 266 nm.Experimental results showed that the reflectances of these two mirrors were about 99.85% and 99.15% respectively,which agreed well with the designed results what were based on the optical constants obtained from the corresponding single layer thin films.