Er3+单掺及Er3+/Yb3+共掺SiO2-Al2O3-La2O3玻璃光谱性质研究

研究了单掺Er³⁺及Er³⁺/Yb³⁺共掺SiO₂-Al₂O₃-La₂O₃玻璃的光谱性质随稀土离子浓度变化规律,应用McCumber理论计算了玻璃在1.53 μm的发射截面及积分吸收截面.结果表明:在Er³⁺离子掺杂浓度相同时,玻璃在980 nm吸收截面与Yb³⁺掺杂浓度成反比;当样品中Yb³⁺离子掺杂浓度为3.94×10²⁰ cm^-3时,玻璃在1.53 μm的吸收截面和发射截面最大,在1.40～1.60 μm积分吸收截面也最大;Er³⁺/Yb³⁺共掺SiO₂-Al₂O₃-La₂O₃玻璃在1.53 μm的荧光半高宽随Er³⁺掺杂浓度升高而增加,当Er³⁺离子掺杂浓度为2.41×10²⁰ cm^-3时,玻璃的荧光半高宽(FWHM)达到52.5 nm.     

Er3+/Ce3+共掺碲铋酸盐玻璃的制备及光谱特性提高研究

采用高温熔融退火法制备了系列 80TeO₂-10Bi₂O₃-10TiO₂-0.5Er₂O₃-xCe₂O₃ (x=0,0.25, 0.5,0.75,1.0 mol%)和(80-y) TeO₂-10Bi₂O₃-10TiO₂-yWO₃-0.5Er₂O₃-0.75Ce₂O₃ (y=3,6,9,12 mol%)的碲铋酸盐玻璃.测试了玻璃样品400-1700 nm范围内的吸收光谱, 975 nm抽运下的上转换发光谱和1.53 μm波段荧光谱, 以及808 nm激励下的Er³⁺离子荧光寿命和无掺杂玻璃样品的Raman光谱, 并结合Judd-Ofelt理论和McCumber理论计算了Er³⁺离子光谱参数.结果表明, 在掺Er³⁺碲铋酸盐玻璃中引入Ce³⁺离子进行Er³⁺/Ce³⁺共掺, 通过Er³⁺离子⁴I_11/2能级与Ce³⁺离子²F_5/2 能级间基于声子辅助的能量传递过程,可以有效抑制Er³⁺离子上转换发光并明显增强其 1.53 μm波段荧光;同时,在现有Er³⁺/Ce³⁺共掺玻璃组分基础上引入WO₃, 可进一步提高1.53 μm波段荧光并展宽其荧光发射谱. 研究结果对于获取优异光谱特性的宽带掺Er³⁺光纤放大器玻璃基质具有实际意义.     

Er3+/Ce3+共掺TeO2-Bi2O3-TiO2玻璃的热稳定性和光谱特性研究

用高温熔融法制备了Er³⁺/Ce³⁺共掺新型碲酸盐玻璃(TeO₂-Bi₂O₃-TiO₂).采用差热分析方法研究了玻璃的热稳定性,测试并分析了不同Ce³⁺离子掺杂浓度下Er³⁺离子的吸收光谱、上转换光谱和荧光光谱特性.研究结果表明,制备的碲酸盐玻璃具有很好的热稳定性,玻璃析晶温度Tx与玻璃转变温度Tg之差(ΔT=Tx-Tg)达到了185 ℃,高于其它文献的报道|同时,Ce3+离子共掺引入的能量转移(Ce³⁺∶2F5/2+Er³⁺∶4I11/2→Ce³⁺∶2F7/2+Er³⁺∶4I13/2)有效地抑制了Er³⁺离子上转换发光并显著增强了1.53 μm波段荧光强度,而发射截面随着Ce³⁺离子掺杂浓度相应增大.优异的热稳定性以及光谱性能揭示Er³⁺/Ce³⁺共掺碲酸盐玻璃是一种潜在的制备宽带掺铒光纤放大器的理想增益介质.     

掺杂浓度和烧结温度对CaWO4:Eu3+发光性能的影响

采用微乳液法合成掺杂浓度不同和烧结温度不同的CaWO₄:Eu³⁺系列荧光体, 这些荧光体都具有Eu³⁺离子的特征荧光发射. 在不同温度烧结后, 高浓度掺杂的样品(Eu³⁺掺杂30或50 mol%)可获得最大的发光强度, 低浓度掺杂的样品(掺杂0.5—2 mol%)在800 ℃烧结时也可获得优异的发光强度. 实验结果表明, Eu³⁺离子高浓度掺杂的CaWO₄:Eu³⁺在紫外光激发下可成为高效发光的荧光粉.     

OH-对磷酸盐铒玻璃光谱性质的影响

本文系统研究了Yb³⁺、Er³⁺共掺磷酸盐铒玻璃中OH^-含量与铒玻璃荧光寿命和光谱性质的关系.结果表明OH^-基团的存在使得Er³⁺离子的荧光强度显著降低,荧光寿命大大缩短.比较了三种不同Al₂O₃含量(5mol%,8mol%和13mol%)的铒玻璃在2.9μm波长处的红外吸收系数与铒离子荧光寿命的关系,发现玻璃中OH^-在2.9μm的吸收系数和Er³⁺的⁴Ⅰ_13/2能级离子衰减速率成线性关系,不同Al₂O₃含量的玻璃具有不同Er³⁺和OH^-基团的相互作用参量和不同的荧光寿命值及量子效率.并从玻璃结构上解释了Al₂O₃含量对除水机制和光谱性质的影响.经过充分除水后的铒玻璃荧光寿命可达到9.1ms.     

超声喷雾共沉淀法制备的Lu3Al5O12∶Eu3+ 纳米粉体发光特性

采用新型超声喷雾共沉淀法技术,以Lu₂O₃、Eu₂O₃、Al(NO₃)₃·9H₂O为原料,制备了不同浓度Eu³⁺离子掺杂的Lu₃Al₅O₁₂纳米粉体.用X射线粉末衍射表征了获得纳米粉体的相,用扫描电镜观察了纳米粒子的形貌.测定了粉体的激发光谱、⁷F₀-⁵D₂声子边带谱与发射光谱.研究了不同高温烧结温度与Eu³⁺掺杂浓度对纳米粒子的发光强度与粒子形貌的影响规律.研究表明,当烧结温度高于900 ℃时,粉体发光强度明显增强,并且随着煅烧温度的增加,发光强度有所增强.Eu³⁺离子的最佳掺杂浓度为5~7 mol%.根据稀土离子Eu³⁺光学跃起矩阵元的特点,从发射光谱获得Eu³⁺光学跃起的J-O参量Ω₂与Ω₄.在Eu³⁺掺杂浓度均为5 mol%时,其强度参量达最小,电-声子耦合最强.然后随着掺杂浓度的进一步提高,强度参量略有增加,电-声子耦合减弱.说明Eu-O键强增加,共价性增强,Eu³⁺的局域环境对称性降低.Ω₂值低于Eu³⁺在玻璃与晶体基质中的情况,这是由于纳米粒子中存在着大量的缺陷以及晶体的结构畸变导致纳米粒子的对称性下降所致.     

Gd2O3:Eu3+纳米晶的燃烧合成及光致发光性质

采用柠檬酸作燃烧剂用燃烧合成法制备了Gd₂O₃:Eu³⁺纳米晶.用X射线衍射仪(XRD)、高分辨透射电子显微镜(HRTEM)和荧光分光光度计等对Gd₂O₃:Eu³⁺纳米晶的结构、形貌和发光性能进行了分析.结果表明：不同柠檬酸与稀土离子配比(C/M)制备的样品经800℃ 退火1 h后，均得到了纯立方相的Gd₂O₃:Eu³⁺纳米晶，晶粒尺寸约为30 nm，尺寸分布较窄，其中以C/M=1.0时制备的纳米晶结晶性最好，发光强度最大.Gd₂O₃:Eu³⁺纳米晶主发射峰位置均在612 nm处 (⁵D₀→⁷F₂跃迁)，激发光谱中电荷迁移态发生红移，观察到Gd³⁺向Eu³⁺的有效能量传递.对柠檬酸与稀土离子配比(C/M)对结晶度、发光性质等的影响也进行了分析和讨论.     

掺入Ni2+和V3+对α-Al2O3晶体光谱精细结构、晶体局域结构和零场分裂参量的影响

应用晶体场理论和不可约张量算符方法构造了3d2/3d8态离子在C3v对称晶场中包含自旋-轨道相互作用、自旋-自旋相互作用、自旋-其它轨道相互作用和其它轨道-其它轨道相互作用四种微观磁效应的45阶可完全对角化的能量哈密顿矩阵.利用该矩阵,计算了V³⁺∶α-Al₂O₃和Ni²⁺∶α-Al₂O₃晶体的光谱精细结构、晶体局域结构和零场分裂参量,研究了掺入两种互补态离子Ni²⁺和V³⁺对同种晶体的光谱精细结构、晶体局域结构和零场分裂参量的影响,理论计算值和实验值相符.研究发现：掺杂没有改变晶体的光谱精细结构和能级分裂条数,但改变了能级间距|掺杂也没有改变晶体的对称性,但使晶体局域结构发生了一定程度的畸变| Ni²⁺∶α-Al₂O₃晶体局域结构的伸长畸变量大于V³⁺∶α-Al₂O₃晶体,键角的变化量小于V³⁺∶α-Al₂O₃晶体.     

Er3+及Er3+/Yb3+掺杂ZrO2-Al2O3的制备及发光性质

采用共沉淀法制备了纳米晶ZrO₂-Al₂O₃∶Er³⁺发光粉体.所制备的粉体室温下具有Er3+离子特征荧光发射,主发射在绿光,其中位于547 nm、560 nm的绿光最强,并得出稀土离子与基质之间有能量传递.对不同煅烧温度下的样品研究表明:因不同温度下所制得的样品晶相不同.研究了纳米晶ZrO2-Al2O3∶Er3+及ZrO₂-Al₂O₃∶Er³⁺/Yb³⁺的上转换发光,并分析了上转换的跃迁机制.发现ZrO₂-Al₂O₃∶Er³⁺的绿光为双光子过程,而ZrO₂-Al₂O₃∶Er³⁺、Yb³⁺的上转换光谱中,红光和绿光也为双光子过程,而极弱的蓝光为三光子过程.讨论了Er³⁺的浓度猝灭现象.最适宜掺杂浓度的原子分数为2%（Er³⁺/Zr⁴⁺）.     

Tm3+/Yb3+共掺碲酸盐玻璃的近红外发光及能量传递机理

采用高温熔融法制备了组分为TeO₂-ZnO-Na₂O的Tm³⁺离子单掺和Tm³⁺/Yb³⁺共掺碲酸盐玻璃,应用Judd-Ofelt理论计算分析了玻璃样品的强度参量Ω_t(t=2, 4, 6),自发辐射跃迁几率A,荧光分支比β和荧光辐射寿命τ_rad等光谱参量,测量得到了不同Yb³⁺离子掺杂浓度下玻璃样品的Tm³⁺离子上转换发光谱.结果显示,在980 nm泵浦光激励下玻璃样品发射出强烈的近红外上转换荧光.对Tm³⁺离子上转换发光分析表明,强烈的Tm³⁺离子近红外上转换发光主要来自于Yb³⁺/Yb³⁺离子间的共振能量传递以及基于单声子和双声子辅助的Yb³⁺/Tm³⁺离子间的非共振能量传递过程,并进一步计算得到了声子贡献比和能量传递系数.最后,计算分析了Tm³⁺:³F₄→³H₆能级间跃迁的1.8 μm波段吸收截面、受激发射截面和增益系数.研究表明,Yb³⁺/Tm³⁺共掺TeO₂-ZnO-Na₂O玻璃可以作为近红外波段固体激光器的潜在增益基质.     

Observation of green emission from Ce-doped gadolinium oxide nanoparticles

Green emission at around 500 nm is observed in Gd₂O₃:Ce³⁺ nanoparticles and the intensity is highly dependent on the concentration of Ce³⁺ in the nanoparticles. The luminescence of this emission displays both picosecond (ps) and millisecond (ms) lifetimes. The ms lifetime is over four orders of magnitude longer than typical luminescence lifetimes (10-40 ns) of Ce³⁺ in traditional Ce³⁺ doped phosphors and therefore likely originates from defect states. The picosecond lifetime is shorter than the typical Ce³⁺ value and is also likely due to defect or surface states. When the samples are annealed at 700 °C, this emission disappears possibly due to changes in the defect moieties or concentration. In addition, a blue emission at around 430 nm is observed in freshly prepared Gd₂O₃ undoped nanoparticles, which is attributed to the stabilizer, polyethylene glycol biscarboxymethyl ether. On aging, the undoped particles show similar emission to the doped particles with similar luminescence lifetimes. When Eu³⁺ ions are co-doped in Gd₂O₃:Ce nanoparticles, both the green emission and the emission at 612 nm from Eu³⁺ are observed.     

Luminescence properties of Ce3+ doped gadolinium-calcium-silicaborate glass scintillator

In this work, the Ce³⁺ doped gadolinium-calcium-silicaborate glass scintillators of the composition ratio 25Gd₂O₃:10CaO:10SiO₂:(55−x)B₂O₃:xCeF₃, have been fabricated by using the melt-quenching technique. The doping concentration of the Ce³⁺ was varied from 0.05 mol% to 2.5 mol%. The 4f-5d transition of the Ce³⁺ allowed scintillation with a fast decay time. The absorption spectrum, X-ray induced emission spectrum, photo luminescence spectrum, laser luminescence spectrum and decay time of the scintillators were measured for studying the luminescence properties. From the X-ray induced emission spectrum result, we checked the trend between doping concentration and light yield. The laser induced luminescence spectrum was measured while changing the temperature from 300 K to 10 K. We also measured the decay time by using the laser excitation of the 0.15 mol% Ce³⁺ doped glass scintillator.     

A novel scheme to acquire enhanced up-conversion emissions of Ho3+ and Yb3+ co-doped Sc2O3

A detailed investigation about the effect of Sc₂O₃: 1 mol%Ho³⁺/5 mol%Yb³⁺ co-doped with Ce⁴⁺ ions prepared by sol-gel methods was performed systematically. Under the excitation of 980 nm laser diode, both green emission (553 nm, ⁵F₄/⁵S₂→⁵I₈) and red emission (672 nm, ⁵F₅→⁵I₈) were both observed in the emission spectra of the samples, which were found to be two-photon process and sensitized by Yb³⁺ ions. With the increasing of Ce⁴⁺ ions, the up-conversion green emission intensity are increased by 6.52, 8.69, 10.85, 13.92 and 16.66 fold, corresponding to the Ce⁴⁺ ions concentrations from 5 mol% to 13 mol%, respectively. The number of photons are necessary to populate the upper emitting state decreases to 2 and the infrared absorption coefficient is reduced, when the Ce⁴⁺ ions concentration increase to 13 mol%. Ce⁴⁺ ions play an important role in tailoring the local crystal field around Ho³⁺ ions, lowering the highest phonon cut-off energy of matrix and reducing the infrared absorption coefficient, thus hindering the non-radiative processes, which contribute to the increased emission intensity. The excellent enhancement makes it a promising multifunctional optical luminescence material.     

Synthesis and luminescence properties of nanocrystalline Gd2O3:Eu by combustion process

The nanocrystalline Gd₂O₃:Eu³⁺ powders with cubic phase were prepared by a combustion method in the presence of urea and glycol. The effects of the annealing temperature on the crystallization and luminescence properties were studied. The results of XRD show pure phase can be obtained, the average crystallite size could be calculated as 7, 8, 15, and 23 nm for the precursor and samples annealed at 600, 700 and 800 °C, respectively, which coincided with the results from TEM images. The emission intensity, host absorption and charge transfer band intensity increased with increasing the temperature. The slightly broad emission peak at 610 nm for smaller particles can be observed. The ratio of host absorption to O²⁻-Eu³⁺ charge transfer band of smaller nanoparticles is much stronger compared with that for larger nanoparticles, furthermore, the luminescence lifetimes of nanoparticles increased with increasing particles size. The effects of doping concentration of Eu³⁺ on luminescence lifetimes and intensities were also discussed. The samples exhibited a higher quenching concentration of Eu³⁺, and luminescence lifetimes of nanoparticles are related to annealing temperature of samples and the doping concentration of Eu³⁺ ions.     

The effect of Mg ions on the photoluminescence of Ce-doped silica

In this paper, we report enhanced luminescence of Mg-co-doped silica gels, which were prepared by a sol-gel method. The total amount of Ce³⁺ ions was kept constant in this experiment at 0.5 mol% total doping. Structural, morphological, thermal, optical absorption and photoluminescence studies were employed. The XRD spectra show that all the samples are non-crystalline. Scanning electron microscopy (SEM) images show that the particles were in nano-range and spherical in shape. Differential scanning calorimetry (DSC) and thermal gravimetric analysis (TGA) of samples depict that the presence of dopant and co-dopant decreases the endothermic peak temperature; while Ce³⁺ increase the yield, Mg²⁺ reduces it. UV analyses revealed that the presence of Ce³⁺ ions increases transmittance but lowers absorbance of annealed silica xerogels, while that of Mg²⁺ ions reduces transmittance but increases absorbance. Luminescence intensities were compared for different gels with and without Mg particles by varying the different concentrations of Mg. Silica containing Mg²⁺ ions had broad blue emission due to energy transfer from Mg²⁺ to Ce³⁺, which is due to radiative recombination. An increase in luminescence intensity was observed as the Mg²⁺ to Ce³⁺ ratio increased for the range investigated.     

Tb3+掺杂的氟氧碲酸盐玻璃发光性能

用高温熔融法制备了Tb³⁺掺杂的氟氧碲酸盐玻璃样品,测试了不同Tb³⁺和Gd³⁺浓度玻璃样品的密度、透过光谱、以及380 nm紫外光和X射线激发的发光光谱.着重研究了玻璃中不同Tb³⁺和Gd³⁺离子含量对玻璃性能的影响规律及机理.结果表明:氟氧碲酸盐玻璃具有较大的密度,ρ大于5 g/cm³;增加Tb³⁺离子的浓度,可以有效提高样品的闪烁发光 关键词： 铽离子 氟氧碲酸盐玻璃 闪烁玻璃 发光性能     

Terbium-activated heavy scintillating glasses

Tb-activated scintillating glasses with Ln₂O₃ (Ln=Y, Gd, Lu) concentrations up to 40 mol% have been prepared. The effects of Ln³⁺ ions on the density, thermal properties, transmission, and luminescence properties under both UV and X-ray excitation have been investigated. Glasses containing Gd₂O₃ or Lu₂O₃ exhibit a density of more than 6.0 g/cm³. Energy transfer from Gd³⁺ to Tb³⁺ takes place in Gd-containing glass and as a result the Gd-containing glass shows a light yield 2.5 times higher than the Y- or Lu-containing glass. The effect of the substitution of fluorine for oxygen on the optical properties was also investigated.     

Enhanced photoluminescence of Sm/Bi co-doped Gd2O3 phosphors by combustion synthesis

Gd₂O₃:Sm³⁺ and Gd₂O₃:Sm³⁺,Bi³⁺ powders were prepared by a combustion method. Their structures were determined using X-ray diffraction. UV-visible absorption and photoluminescence spectra were investigated for Gd₂O₃:Sm³⁺ and Gd₂O₃:Sm³⁺,Bi³⁺ at different annealing temperatures and different doping concentrations. The emission spectra of all samples presented the characteristic emission narrow lines arising from the ⁴G_5/2→⁶H_J transitions (J=5/2, 7/2, and 9/2) of Sm³⁺ ions upon excitation with UV irradiation. The emission intensity of Sm³⁺ ions was largely enhanced with introducing Bi³⁺ ions into Gd₂O₃:Sm³⁺ and the maximum occurred at a Bi³⁺ concentration of 0.5 mol%. The relevant mechanisms were discussed with the sensitization theory by Dexter and the aggregation behavior of Bi³⁺ ions.     

Processes of the excitation energy migration and transfer in Ce-doped alkali gadolinium phosphates studied with time-resolved photoluminescence spectroscopy technique

Spectral-kinetic characteristics of Gd³⁺ and Ce³⁺ luminescence from a series of Ce³⁺-doped alkali gadolinium phosphates of MGdP₄O₁₂ type (M=Li, Na, Cs) have been studied within 4.2-300 K temperature range using time-resolved luminescence spectroscopy techniques. The processes of energy migration along the Gd³⁺ sub-lattice and energy transfer between the Gd³⁺ and Ce³⁺ ions have been investigated. Peculiarities of these processes have been compared for MGdP₄O₁₂ phosphate hosts with different alkali metal ions. A contribution of different levels from the ⁶P_j multiplet of the lowest Gd³⁺ excited state into the energy migration and transfer processes has been clarified. The phonon-assisted occupation of high-energy ⁶P_{5/2, 3/2} levels by Gd³⁺ in the excited ⁶P_j state has been revealed as a shift of Gd³⁺⁶P_j→⁸S_7/2 emission into the short-wavelength spectral range upon the temperature increase. The relaxation of excited Gd³⁺ via phonon-assisted population of Gd³⁺⁶P_5/2 level (next higher one to the lowest excited ⁶P_7/2) is supposed to be responsible for the rise in probability of energy migration within the Gd³⁺ sub-lattice initiating the Gd³⁺→Ce³⁺ energy transfer at T<150 K, whereas further intensification of Gd³⁺→Ce³⁺ energy transfer at T>150 K is explained by the increase in probability of Gd³⁺ relaxation into the highest ⁶P_3/2 level of the ⁶P_j multiplet. An efficient reversed Ce³⁺→Gd³⁺ energy transfer has been revealed for the studied phosphates at 4.2 K.     

Ce3+对Er3+/Yb3+共掺氟磷酸盐玻璃光谱性质的影响

研究了能量接受离子Ce³⁺对Er³⁺上转换发光强度以及Er³⁺在1.5μm附近波段发光性能参数的影响，并从能量匹配及能级结构角度出发对Er³⁺/Ce³⁺间的能量转移机制进行了分析.分析认为，⁴I_11/2能级的Er³⁺通过无辐射能量转移把能量传递给²F_5/2能级的Ce³⁺关键词： 氟磷酸盐玻璃 光谱性质 光纤放大器 3+和Ce³⁺')" href="#">Er³⁺和Ce³⁺