PL Properties of Sr<Subscript>2</Subscript>CeO<Subscript>4</Subscript> With Eu<Superscript>3+</Superscript> and Dy<Superscript>3+</Superscript> for Solid State Lighting Prepared by Precipitation Method

Photoluminescence studies of pure and Dy³⁺, Eu³⁺ doped Sr₂CeO₄ compounds are presented by oxalate precipitation method for solid state lighting. The prepared samples also characterized by XRD, SEM (EDS) and FTIR spectroscopy. The pure Sr₂CeO₄ compound displays a broad band in its emission spectrum when excited with 280 nm wavelength, which peaks centered at 488 nm, which is due to the energy transfer between the molecular orbital of the ligand and charge transfer state of the Ce⁴⁺ ions. Emission spectra of Sr₂CeO₄ with different concentration of Dy³⁺ ions under near UV radiation excitation, shows that intensity of luminescence spectra is found to be affected by Dy³⁺ ions, and it increases with adding some percentages of Dy³⁺ ions. The maximum doping concentration for quenching is found to be Dy³⁺?=?0.2 mol % to Sr²⁺ions. The observed broad spectrum from 400 to 560 nm is mainly due to CT transitions in Sr₂CeO₄ matrix and some fractional contribution of transitions between ⁴F_9/2 → ⁶H_15/2 of Dy³⁺ ions. Secondly the effect of Eu³⁺ doping at the Sr²⁺ site in Sr₂CeO₄, have been studied. The results obtained by doping Eu³⁺ concentrations (0.2 mol% to 1.5 mol%), the observed excitation and emission spectra reveal excellent energy transfer between Ce⁴⁺ and Eu³⁺. The phenomena of concentration quenching are explained on the basis of electron phonon coupling and multipolar interaction. This energy transfer generates white light with a color tuning from blue to red, the tuning being dependent on the Eu³⁺ concentration. The results establish that the compound Sr₂CeO₄ with Eu³⁺?=?1 mol% is an efficient “single host lattice” for the generation of white lights under near UV-LED and blue LED irradiation. The commission internationale de I’Eclairage (CIE) coordinates were calculated by Spectrophotometric method using the spectral energy distribution of prepared phosphors.     

Synthesis and Optical Properties of Novel Red-Emitting PbNb<Subscript>2</Subscript>O<Subscript>6</Subscript>: Eu<Superscript>3+</Superscript> Phosphors

Undoped and PbNb₂O_6:Eu³⁺ (1.0 ≤ x ≤ 6.0 mol%) phosphors were synthesized at 1100 °C for 3.5 h by the conventional solid state reaction method. Synthesized PbNb₂O₆:Eu³⁺ phosphors were characterized by X-ray diffraction (XRD), Scanning electron microscopy (SEM), Energy dispersive spectroscopy (EDS) and Photoluminescence (PL) analyses. The PL spectra showed series of excitation peaks between 350 and 430 nm due to the 4f–4f transitions of Eu³⁺. For 395.0 nm excitation, emission spectra of Eu³⁺ doped samples were observed at 591 nm (orange) and 614 nm (red) due to the ⁵D₀ → ⁷F₁ transitions and ⁵D₀ → ⁷F₂ transitions, respectively. PL analysis results also showed that the emission intensity increased by increasing Eu³⁺ ion content. No concentration quenching effect was observed. The CIE chromaticity color coordinates (x,y) of the PbNb₂O₆:Eu³⁺ phosphors were found to be in the red region of the chromaticity diagram.     

Synthesis and Optical Characterization of Red-Emitting BaTa<Subscript>2</Subscript>O<Subscript>6</Subscript>:Eu<Superscript>3+</Superscript> Phosphors

Undoped and Eu³⁺ doped BaTa₂O₆ phosphors were synthesized via solid state reaction method and characterized by using XRD, SEM-EDS and photoluminescence (PL) analyses. The XRD results revealed that the crystal structure of BaTa₂O₆ allowed up to 10 mol% levels of Eu³⁺ ions due to the TTB characteristic network of adjacent octahedrals. SEM-EDS analyses confirmed the formation of BaTa₂O₆ structure and EuTaO₄ secondary phase. BaTa₂O_6:Eu³⁺ phosphors exhibited orange and red emissions at 592.2 nm and 615.7 nm in the visible region respectively. The Commission Internationale d’Eclairage (CIE) chromaticity coordinates of the BaTa₂O_6:Eu³⁺ phosphors that excited at λ _ex = 400 nm ranged from orangish-red to pinkish-red depending on increasing Eu³⁺ concentration.     

Red,Yellow, Blue and Green Emission from Eu<Superscript>3+</Superscript>, Dy<Superscript>3+</Superscript> and Bi<Superscript>3+</Superscript> Doped Y<Subscript>2</Subscript>O<Subscript>3</Subscript>nano-Phosphors

Rare earth elements (RE = Eu³⁺& Dy³⁺)and Bi³⁺ doped Y₂O₃ nanoparticles were synthesized by urea hydrolysis method in ethylene glycol, which acts as reaction medium as well as a capping agent, at a low temperature of 140 °C,followed by calcination of the obtained product. Transmission electron microscope (TEM) images reveals that ovoid shaped Y₂O₃ nanoparticles of around 22–24 nm size range were obtained in this method. The respective RE and Bi³⁺ doped Y₂O₃ precursor nanoparticles when heated at 600 and 750 °C, retains the same shape as that of the as-synthesized Y₂O₃ precursor samples. From EDAX spectra, the incorporation of RE ions into the host has been studied. XRD pattern reveals the crystalline nature of the heated nanoparticles and indicate the absence of any impurity phase other than cubic Y₂O₃.However, the as-synthesized nanoparticles were highly amorphous without the presence of any sharp XRD peaks. Photoluminescence study suggests that the synthesized samples could be used as red (Eu³⁺), yellow (Dy³⁺), blue and green (Bi³⁺)emitting phosphors.     

Re-dispersible Li<Superscript>+</Superscript> and Eu<Superscript>3+</Superscript> co-doped CdS nanoparticles: Luminescence studies

Re-dispersible CdS, 5 at.% Eu³⁺-doped CdS, 2 at.% Li⁺ and 5 at.% Eu³⁺ co-doped CdS nanoparticles in organic solvent are prepared by urea hydrolysis in ethylene glycol medium at a low temperature of 170°C. CdS nanoparticles have spherical shape with a diameter of ∼80 nm. The asymmetric ratio (A ₂₁) of the integrated intensities of the electrical dipole transition to the magnetic dipole transition for 5 at.% Eu³⁺-doped CdS is found to be 3.8 and this ratio is significantly decreased for 2 at.% Li⁺ and 5 at.% Eu³⁺ co-doped CdS (A ₂₁ = 2.6). It establishes that the symmetry environment of Eu³⁺ ion is more favored by Li-doping. Extra peak at 550 nm (green emission) could be seen for 2 and 5 at.% Eu³⁺ co-doped CdS. Also, the significant energy transfer from host CdS to Eu³⁺ is found for 5 at.% Eu³⁺-doped CdS compared to that for 2 at.% Li⁺ and 5 at.% Eu³⁺ co-doped CdS.      

Sol-gel method and luminescence properties of the ZrO<Subscript>2</Subscript>:Eu<Superscript>3+</Superscript> phosphors with different charge compensation

Eu³⁺-doped ZrO₂ phosphors with different charge compensators (Li⁺, Na⁺, K⁺) were prepared by the sol-gel method. The properties of the as-obtained samples are characterized by X-ray diffraction, scanning electron microscope, photoluminescence spectra, and decay curve. The results show that ZrO₂:Eu³⁺ phosphors with different charge compensation are mixed phase of tetragonal and monoclinic phase, and the volume fraction of tetragonal phase of ZrO₂:Eu³⁺/Na⁺ phosphor is bigger than the other phosphors. The phosphors can emit strong red light at 606~616 nm (⁵D₀ → ⁷F₂) excited by ultraviolet light (395 nm). Compared with two charge compensation patterns in the ZrO₂:Eu³⁺, it has been found that ZrO₂:Eu³⁺ phosphors used Na⁺ as charge compensator show greatly enhanced red emission under 395 nm excitation and longer luminescence lifetime.     

Synthesis and luminescent properties of Eu<Superscript>3+</Superscript>- and Eu<Superscript>2+</Superscript>-activated sodium pyrophosphate Na<Subscript>4</Subscript>P<Subscript>2</Subscript>O<Subscript>7</Subscript>

The luminescent properties of Eu³⁺ and Eu²⁺ ions in sodium pyrophosphate, Na₄P₂O₇, have been studied. The excitation spectrum of the Eu³⁺ emission in Na₄P₂O₇ consists of several sets of bands in the range 280–535 nm due to 4f–4f transitions of Eu³⁺ ions and a broad band with a maximum at about 240 nm interpreted to be due to a charge transfer (CT) transition from oxygen 2p states to empty states of the Eu³⁺ 4f⁶-configuration. Although the CT band energy is large enough, the quantum efficiency (η) of the Eu³⁺ emission in Na₄P₂O₇ under CT excitation was estimated to be very low (η ≤ 0.01). In terms of a configurational coordinate model, this fact is interpreted as a result of the high efficiency of a radiationless relaxation from the CT state to the ⁷F₀ ground state of Eu³⁺ ions occupying sodium sites in Na₄P₂O₇. A strong reducing agent is required in order to stabilize Eu²⁺ ions in Na₄P₂O₇ during the synthesis. Several nonequivalent Eu²⁺ luminescence centers in Na₄P₂O₇ were found.     

Grain size effects on dynamics of Li-ions in Li<Subscript>3</Subscript>V<Subscript>2</Subscript>(PO<Subscript>4</Subscript>)<Subscript>3</Subscript> glass-ceramic nanocomposites

Li₃V₂(PO₄)₃ glass-ceramic nanocomposites, based on 37.5Li₂O-25V₂O₅-37.5P₂O₅ mol% glass, were successfully prepared via heat treatment (HT) process. The structure and morphology were investigated by X-ray diffraction (XRD) and scanning electron microscope (SEM). XRD patterns exhibit the formation of Li₃V₂(PO₄)₃ NASICON type with monoclinic structure. The grain sizes were found to be in the range 32–56 nm. The effect of grain size on the dynamics of Li⁺ ions in these glass-ceramic nanocomposites has been studied in the frequency range of 20 Hz–1 MHz and in the temperature range of 333–373 K and analyzed by using both the conductivity and modulus formalisms. The frequency exponent obtained from the power law decreases with the increase of temperature, suggesting a weaker correlation among the Li⁺ ions. Scaling of the conductivity spectra has also been performed in order to obtain insight into the relaxation mechanisms. The imaginary modulus spectra are broader than the Debye peak-width, but are asymmetric and distorted toward the high frequency region of the maxima. The electric modulus data have been fitted to the non-exponential Kohlrausch–Williams–Watts (KWW) function and the value of the stretched exponent β is fairly low, suggesting a higher ionic conductivity in the glass and its glass-ceramic nanocomposites. The advantages of these glass-ceramic nanocomposites as cathode materials in Li-ion batteries are shortened diffusion paths for Li⁺ ions/electrons and higher surface area of contact between cathode and electrolyte.     

Investigation on lithium ion conductivity and structural stability of yttrium-substituted Li<Subscript>7</Subscript>La<Subscript>3</Subscript>Zr<Subscript>2</Subscript>O<Subscript>12</Subscript>

Advanced Li-air battery architecture demands a high Li⁺ conductive solid electrolyte membrane that is electrochemically stable against metallic lithium and aqueous electrolyte. In this work, an investigation has been carried out on the microstructure, Li⁺ conduction behaviour and structural stability of Li₇La_3-x Y _x Zr₂O₁₂ (x = 0.125, 0.25 and 0.50) prepared by conventional solid-state reaction technique. The phase analysis of Li₇La_3-x Y _x Zr₂O₁₂ (x = 0.125, 0.25 and 0.50) sintered at 1200 °C by powder X-ray diffraction (PXRD) and Raman confirms the formation of high Li⁺ conductive cubic phase (\( Ia\overline{3}d \)) lithium garnets. Among the investigated lithium garnets, Li₇La_2.75Y_0.25Zr₂O₁₂ sintered at 1200 °C exhibits a maximized room temperature total (bulk + grain boundary) Li⁺ conductivity of 3.21 × 10^?4 S cm^?1 along with improved relative density of 96 %. The preliminary investigation on the structural stability of Li₇La_2.75Y_0.25Zr₂O₁₂ in the solutions of 1 M LiCl, dist. H₂O and 1 M LiOH at 30 °C/50 °C indicates that the Li₇La_2.75Y_0.25Zr₂O₁₂ is relatively stable against 1 M LiCl and dist. H₂O. Further electrochemical investigation is essential for practical application of Li₇La_2.75Y_0.25Zr₂O₁₂ as protective solid electrolyte membrane in aqueous Li-air battery.     

Cr<Superscript>3+</Superscript> spectroscopy study in ZnO-codoped and Zn-in-diffused congruent LiNbO<Subscript>3</Subscript>:Cr crystals

This paper reports on the spectroscopy properties, absorption and luminescence, of Cr³⁺ ions in singly doped, ZnO-codoped, and Zn in-diffused LiNbO₃:Cr crystals. In addition to the broad absorption, inter-ionic transitions ascribed to Cr³⁺ ions located in Li⁺ and Nb⁵⁺ sites; [Cr]_Li and [Cr]_Nb centres two absorption bands at higher energy are reported and ascribed to the charge transfer transitions of the Cr³⁺ ions of the two defect centres. The charge transfer transitions are used as optical probe to study the role of the Zn ions in the Zn in-diffused LiNbO₃:Cr samples. It has been observed that the Zn-in-diffused processes created [Cr]_Nb centres in the diffusion zone. The location of the diffused Zn²⁺ ions is considered to be in Li⁺ site, displacing the Cr³⁺ ions from the Li⁺ sites, [Cr]_Li, to the Nb⁵⁺ positions, [Cr]_Nb.     

Microstructural and Radioluminescence Characteristics of Nd<Superscript>3+</Superscript> Doped Columbite-Type SrNb<Subscript>2</Subscript>O<Subscript>6</Subscript> Phosphor

Undoped and different concentration Nd³⁺ doped SrNb₂O₆ powders with columbite structure were synthesized by molten salt process using a mixture of strontium nitrate and niobium (V) oxide and NaCl-KCl salt mixture as a flux under relatively low calcining temperature. X-ray diffraction analysis results indicated that SrNb₂O₆ phases found to be orthorhombic columbite single phase for undoped, 0.5 and 3 mol% Nd³⁺ doping concentrations. Phase composition of the powders was examined by SEM-EDS analyses. Radioluminescence properties of Nd³⁺ doped samples from UV to near-IR spectral region were studied. The emissions increased with the doping concentration of up to 3 mol%, and then decreased due to concentration quenching effect. There is a sharp emission peak around 880 nm associated with ⁴F_5/2 → ⁴I_9/2 transition in the Nd³⁺ ion between 300 and 1100 nm. The broad emission band intensity was observed from 400 to 650 nm where the peak intensities increased by increasing Nd³⁺ doping concentration. All the measurements were taken under the room temperature.     

Enhanced Up-Conversion Emission in Al<Superscript>3+</Superscript> Co-Doped ZnGa<Subscript>2</Subscript>O<Subscript>4</Subscript>:Yb<Superscript>3+</Superscript>,Tm<Superscript>3+</Superscript> Powder Phosphors

Yb³⁺-Tm³⁺ co-doped up-conversion powder phosphors using Zn(Al_xGa_1-x)₂O₄ (ZAGO) as the host materials were synthesized via solid-state reaction successfully. In addition, the morphology, structural characterization and up-conversion luminescent properties were all investigated by scanning electron microscope (SEM), x-ray diffraction (XRD) and fluorescence spectrophotometer (F-7000), respectively. Under the excitation of a 980 nm laser, all as-prepared powders can carry out blue emission at about 477 nm (corresponding to ¹G₄ → ³H₆ transition of Tm³⁺ ions), and red emission at about 691 nm (attributed to ³F₃ → ³H₆ transition of Tm³⁺ ions). Also, the influence of doping Al³⁺ ions were investigated. In brief, the doping of Al³⁺ ions has no effect on the position of emission peak. Howbeit the up-conversion efficiency and intensity of ZAGO:Yb,Tm phosphors are stronger than ZGO:Yb,Tm and ZAO:Yb,Tm phosphors, while the crystallinity is the opposite. More particularly, all as-prepared powder phosphors emit strong luminescence, which is observable by the naked eye, demonstrating the potential applications in luminous paint, luminescent dye, etc.     

Luminescence and energy transfer mechanism in Eu<Superscript>3+</Superscript>/Tb<Superscript>3+</Superscript>-co-doped ZrO<Subscript>2</Subscript> nanocrystal rods

Nanocrystal rods of Eu³⁺/Tb³⁺-co-doped ZrO₂ were synthesized using a simple chemical precipitation technique. Both ions were successfully doped into the Zr⁴⁺ ion site in a mixed structure containing both monoclinic and tetragonal phases. The Eu³⁺ or Tb³⁺ singly doped zirconia produced red and green luminescence which are characteristics of Eu³⁺ and Tb³⁺ ions, respectively. The co-doped zirconia samples produced blue emission from defect states transitions in the host ZrO₂, red and green luminescence from dopant ions giving cool to warm white light emissions. The phosphors were efficiently excited by ultraviolet and near-ultraviolet/blue radiations giving white and red light, respectively. The decay lifetime was found to increase with increasing donor ion concentration contrary to conventional observations reported by previous researchers. Weak quadrupole–quatdrupole multipolar process was responsible for energy transfer from Tb³⁺ (donor) ion to Eu³⁺ ion. No energy back-transfer from Eu³⁺ to Tb³⁺ ion was observed from the excitation spectra. Temperature-dependent photoluminescence shows the presence of defects at low temperature, but these defects vanished at room temperature and beyond. The Eu³⁺/Tb³⁺-co-doped ZrO₂ nanocrystal rod is a potential phosphor for white light application using UV as an excitation source. Thermoluminescence measurements show that the inclusion of Tb³⁺ ion increases trap depths in the host zirconia.     

On the Luminescence of Ce<Superscript>3+</Superscript>, Eu<Superscript>3+</Superscript>, and Tb<Superscript>3+</Superscript> in Novel Borate LiSr<Subscript>4</Subscript>(BO<Subscript>3</Subscript>)<Subscript>3</Subscript>

This paper reports on the photoluminescence (PL) and time-resolved properties of Ce³⁺, Eu³⁺, and Tb³⁺ in novel LiSr₄(BO₃)₃ powder phosphors. Ce³⁺ shows an emission band peaking at 420 nm under 350-nm UV excitation. Energy transfer from Ce³⁺ to Mn²⁺ takes place in the co-doped samples. Eu³⁺ shows red emission under near UV excitation. LiSr₄(BO₃)₃:Eu³⁺ phosphor could be a suitable candidate for phosphor-converted solid state lighting. The luminescence lifetime is 2.13 ms for Eu³⁺ in LiSr₄(BO₃)₃:0.001Eu³⁺. As Eu³⁺ concentration increasing, the decay curves deviate from exponential behavior. Tb³⁺ shows the strongest ⁵D₄→⁷ F₅ emission line at 540 nm. Decay curves of ⁵D₄→⁷ F₅ and ⁵D₃→⁷ F₅ emission with different Tb³⁺ concentrations were also measured. Cross-relaxation process is discussed based on the decay curves.     

Possibility of adjusting photoluminescence spectra of Ca scheelites (CaMoO<Subscript>4</Subscript>: Eu<Superscript>3+</Superscript> and CaWO<Subscript>4</Subscript>: Eu<Superscript>3+</Superscript>) to the emission spectrum of incandescent lamps

The peculiarities of the photoluminescence of compounds CaMoO₄: Eu³⁺ and CaWO₄: Eu³⁺ with the scheelite structure associated with a change in the short- and long-range orders of the crystal lattice upon a change in the activator (Eu³⁺) of the photoluminescence range in the interval 1–4 mol %, in which the photoluminescence of the matrix is preserved in the range 484–557 nm, are investigated using X-ray phase analysis as well as photoluminescence, Raman, and diffuse reflection spectroscopies. The introduction of Eu³⁺ ions leads to the reconstruction of the lattice so that up to 10% of these ions stimulate the formation of centrosymmetric localization upon the substitution of Ca²⁺ ions in the noncentrosymmetric positions. It is found that the spectral radiant emittance of the more effective luminophore CaMoO₄: Eu³⁺ can be adjusted to this parameter for an incandescent lamp for the Eu³⁺ concentration of 1–2 mol %.     

luminescence of BaGa<Subscript>2</Subscript>Se<Subscript>4</Subscript> crystals activated by Eu<Superscript>2+</Superscript> and Ce<Superscript>3+</Superscript> ions

We have studied the effect of doping with Eu²⁺ and Ce³⁺ ions on the photoluminescence (PL) of BaGa₂Se₄ crystals in the temperature range 77–300 K. We have established that the broad bands with maxima at wavelengths 456 nm and 506 nm observed in the photoluminescence spectra of BaGa₂Se₄:Ce³⁺ crystals are due to intracenter transitions 5d → ²F_7/2 and 5d →²F_5/2 of the Ce³⁺ ions, while the broad photoluminescence band with maximum at 521 nm in the spectrum of BaGa₂Se₄:Eu²⁺ is associated with 4f⁶ 5d → 4f⁷ (⁸S_7/2) transitions of the Eu²⁺ ion. We show that in BaGa₂Se₄:Eu²⁺,Ce³⁺ crystals, excitation energy is transferred from the Ce³⁺ ions to the Eu²⁺ ions.     

The upconversion luminescence and magnetism in Yb<Superscript>3+</Superscript>/Ho<Superscript>3+</Superscript> co-doped LaF<Subscript>3</Subscript> nanocrystals for potential bimodal imaging

Biocompatible upconversion nanoparticles with multifunctional properties can serve as potential nanoprobes for multimodal imaging. Herein, we report an upconversion nanocrystal based on lanthanum fluoride which is developed to address the imaging modalities, upconversion luminescence imaging and magnetic resonance imaging (MRI). Lanthanide ions (Yb³⁺ and Ho³⁺) doped LaF₃ nanocrystals (LaF₃ Yb³⁺/Ho³⁺) are fabricated through a rapid microwave-assisted synthesis. The hexagonal phase LaF₃ nanocrystals exhibit nearly spherical morphology with average diameter of 9.8 nm. The inductively coupled plasma mass spectrometry (ICP-MS) analysis estimated the doping concentration of Yb³⁺ and Ho³⁺ as 3.99 and 0.41%, respectively. The nanocrystals show upconversion luminescence when irradiated with near-infrared (NIR) photons of wavelength 980 nm. The emission spectrum consists of bands centred at 542, 645 and 658 nm. The stronger green emission at 542 nm and the weak red emissions at 645 and 658 nm are assigned to ⁵S₂ → ⁵I₈ and ⁵F₅ → ⁵I₈ transitions of Ho³⁺, respectively. The pump power dependence of luminescence intensity confirmed the two-photon upconversion process. The nanocrystals exhibit paramagnetism due to the presence of lanthanide ion dopant Ho³⁺ and the magnetization is 19.81 emu/g at room temperature. The nanocrystals exhibit a longitudinal relaxivity (r ₁) of 0.12 s^?1 mM^?1 and transverse relaxivity (r ₂) of 28.18 s^?1 mM^?1, which makes the system suitable for developing T2 MRI contrast agents based on holmium. The LaF₃ Yb³⁺/Ho³⁺ nanocrystals are surface modified by PEGylation to improve biocompatibility and enhance further functionalisation. The PEGylated nanocrystals are found to be non-toxic up to 50 μg/mL for 48 h of incubation, which is confirmed by the MTT assay as well as morphological studies in HeLa cells. The upconversion luminescence and magnetism together with biocompatibility enables the adaptability of the present system as a nanoprobe for potential bimodal imaging.     

Improvement of thermal and spectroscopic behavior of Er<Superscript>3+</Superscript>/Ce<Superscript>3+</Superscript> co-doped tellurite glass for lasing materials

Tellurite glasses (TeO₂–ZnO–Nb₂O₅) mono-doped Er³⁺ and co-doped Er³⁺/Ce³⁺ have been prepared using the melt-quenching technique. To evaluate the effect of Ce³⁺ on the structural, thermal stability of glass hosts and fluorescence properties of Er³⁺, X-ray diffraction patterns, Ftir spectra, differential scanning calorimeter curves, absorption spectra, fluorescence emission spectra, fluorescence lifetimes, up-conversion emission spectra of glass samples were measured and investigated. Using Judd–Ofelt theory, we calculated intensity parameters (Ω₂, Ω₄ and Ω₆), spontaneous emission probabilities, the radiative lifetime, luminescence branching factors and the quantum yield of luminescence for ⁴I_13/2 → ⁴I_15/2 transition. The co-doping with Ce³⁺ was effective on the suppression of up-conversion emission of Er³⁺ owing to the phonon-assisted energy transfer: Er³⁺:⁴I_11/2 + Ce³⁺:²F_5/2 → Er³⁺:⁴I_13/2 + Ce³⁺:²F_7/2 which contributed the effective enhancement of 1.53 µm fluorescence emission. The change in optical properties with the addition of Ce³⁺ ions have been discussed and compared with other glasses. Using the Mc Cumber method for the ⁴I_13/2 → ⁴I_15/2 transition, absorption cross-section, calculated emission cross-section, and gain cross-section values support that TZNEr1Ce1 glass is a potential material for developing broad-band and high-gain erbium-doped fiber amplifiers applied for 1.53 µm.     

Structural and Near-Infrared Properties of Nd<Superscript>3+</Superscript> Activated Lu<Subscript>3</Subscript>NbO<Subscript>7</Subscript> Phosphor

Undoped and Nd³⁺ doped lutetium niobate phases have been prepared by a conventional solid state reaction method using lutetium acetate and niobium oxide at 1250 °C for 6 h. X-ray diffraction patterns of the 6 mol% Lu₃NbO₇ sample exhibited a cubic fluorite single phase. Phase structure exhibited interesting crystallization behaviour depending on increasing Nd³⁺ concentration which led to a Lu₃NbO₇ single phase formation during the heat treatment process. SEM investigations were also in agreement with the XRD results. Morphologies of Nd³⁺ doped lutetium niobate powders exhibited oval like shapes and grain sizes varied between 0.3 and 5 μm. Near-infrared luminescence properties of Nd³⁺ doped Lu₃NbO₇ were also studied. 1.06 μm laser transition characteristics of Nd³⁺ doped lutetium niobate have been observed. Concentration quenching phenomenon was not detected depending on increasing Nd³⁺ doping concentrations at room temperature.     

Luminescence in Dy<Superscript>3+</Superscript> and Eu<Superscript>3+</Superscript> Activated K<Subscript>3</Subscript>Al<Subscript>2</Subscript>(PO<Subscript>4</Subscript>)<Subscript>3</Subscript>

The Dy³⁺ and Eu³⁺ activated K₃Al₂ (PO₄)₃ phosphors were prepared by a combustion synthesis. From a powder X-ray diffraction (XRD) analysis the formation of K₃Al₂ (PO₄)₃ was confirmed. In the photoluminescence emission spectra, the K₃Al₂(PO₄)₃:Dy³⁺ phosphor emits two distinctive colors: blue and yellow whereas K₃Al₂(PO₄)₃:Eu³⁺ emits red color. Thus the combination of colors gives BYR (blue–yellow–red) emissions can produce white light. These phosphors exhibit a strong absorption between 340 and 400 nm which suggest that present phosphor is a promising candidate for producing white light-emitting diodes (LED).