End group effect on surface and interfacial segregation in PS-PMMA blend thin films

Thin films of polystyrene (PS)/poly (methyl methacrylate) (PMMA) blends with different end groups were investigated using ToF-SIMS and AFM. PS with -OH and -NH₂ end groups were blended in toluene solvent with pure PMMA homopolymer, and PMMA having anhydride end group. The ToF-SIMS spectra of PS-OH/PMMA resembled that of pure PS-PMMA blends showing an increase of PMMA intensity after annealing. On the contrary, the PS-NH₂ blended with PMMA showed an increase in PS intensity on the surface after annealing. The ToF-SIMS spectra were similar to that of a pure PS-PMMA di-block copolymer. These results indicate copolymer formation at the surface. The PS-NH₂ with PMMA-anhydride blend spectra showed very slight changes in spectra before and after annealing and the AFM images revealed spinodal bi-continuous structures on the surface before and after annealing. The copolymer formation is found to occur in the as-cast film itself and not after thermal treatment.     

Influence of Blend Composition on Crystallization of Poly(L-Lactic Acid)/Poly (Ethylene Oxide) Crystalline/Crystalline Blends

The effect of blend composition on crystallization morphology and behavior of a crystalline/crystalline blend, poly(l-lactic acid) (PLLA)/poly(ethylene oxide) (PEO), during slow, non-isothermal crystallization was studied by polarized light microscopy (PLM) connected with a hot-stage and differential scanning calorimetry (DSC). The results showed that all of the PLLA/PEO blends produced spherulites which gradually became bigger and looser, as well as coarser, with the increment of the PEO content, indicating that the PEO crystals was resided in the interlamellar or interfibrillar (between clusters of commonly oriented lamellae) regions of the PLLA spherulites. In the (25/75) and (10/90) blends, the nucleation and growth processes of the PEO spherulites could be clearly observed in the pre-existing PLLA spherulites. The onset crystallization temperature and the melting point of one component decreased with increasing the content of the other one owing to the good miscibility of the two components in the non-crystalline state and the interaction between their macromolecules, indicating that the crystallization of each component was influenced by the other one.     

Quantitative ToF-SIMS studies of protein drug release from biodegradable polymer drug delivery membranes

Biodegradable polymers are of interest in developing strategies to control protein drug delivery. The protein that was used in this study is Keratinocyte Growth Factor (KGF) which is a protein involved in the re-epithelialization process. The protein is stabilized in the biodegradable polymer matrix during formulation and over the course of polymer degradation with the use of an ionic surfactant Aerosol-OT (AOT) which will encapsulate the protein in an aqueous environment. The release kinetics of the protein from the surface of these materials requires precise timing which is a crucial factor in the efficacy of this drug delivery system.Time-of-flight secondary ion mass spectrometry (ToF-SIMS) was used in the same capacity to identify the molecular ion peak of the surfactant and polymer and use this to determine surface concentration. In the polymer matrix, the surfactant molecular ion peak was observed in the positive and negative mode at m/z 467 and 421, respectively. These peaks were determined to be [AOT + Na⁺] and [AOT − Na⁺]. These methods are used to identify the surfactant and protein from the polymer matrix and are used to measure the rate of surface accumulation. The second step was to compare this accumulation rate with the release rate of the protein into an aqueous solution during the degradation of the biodegradable film. This rate is compared to that from fluorescence spectroscopy measurements using the protein autofluorescence from that released into aqueous solution [C.M. Mahoney, J. Yu, A. Fahey, J.A.J. Gardella, SIMS depth profiling of polymer blends with protein based drugs, Appl. Surf. Sci. 252 (2006), 6609-6614.].     

The Effect of Poly(Ethylene Succinate) on Mechanical Properties of PLLA/PES Blend Prepared by Melt-Blending

Fully biodegradable poly(L-lactide) and poly(ethylene succinate) (PLLA/PES) blends were prepared via melt-blending using PLLA and PES as reactants in a stainless steel chamber. The prepared PLLA/PES blend, as well as neat PLLA and PES, was characterized by Fourier transform infrared spectra (FTIR) and X-ray diffraction (XRD) to confirm the structure and the crystallization of PLLA in the blend. The mechanical properties of PLLA/PES blends were determined by bending and tensile tests and the effects of PES content on the mechanical properties of PLLA/PES blends were investigated. It was found that blending some amount of PES could significantly improve the elongation at break while still keeping considerably high strength and modulus. With increasing PES content, both strength and modulus gradually decreased; however the elongation at break significantly increased. SEM was used to examine the morphology of fracture surfaces of PLLA/PES blends.     

PLA-PMMA blends: A study by XPS and ToF-SIMS

This paper reports which are the possibilities of quantification by time of flight secondary ion mass spectrometry (ToF-SIMS) for some polymer blends. In order to assess the composition of the mixtures, we studied first different poly(l-lactide)/polymethylmethacrylate (PLA/PMMA) blends by X-ray photoelectron spectroscopy (XPS), this technique being quantitative. By XPS fitting of the C 1s level, we found a very good agreement of the measured concentrations with the initial compositions. Concerning ToF-SIMS data treatment, we used principal component analysis (PCA) on negative spectra allowing to discriminate one polymer from the other one. By partial least square regression (PLS), we found also a good agreement between the ToF-SIMS predicted and initial compositions. This shows that ToF-SIMS, in a similar way to XPS, can lead to quantitative results. In addition, the observed agreement between XPS (60-100 Å depth analyzed) and ToF-SIMS (10 Å depth analyzed) measurements show that there is no segregation of one of the two polymers onto the surface.     

Interfacial morphology and friction properties of thin PEO and PEO/PAA blend films

The scanning force microscope (SFM) was used to investigate morphology of poly(ethylene oxide) (PEO) and poly(acrylic acid) (PAA) blend. The effect of solvent and dewetting in surface structure of PEO film was reported. The results manifested that the crystallization of PEO could be suppressed completely in ultrathin region via using chloroform as a solvent, and the branched-like crystallization was recovered after dewetting. Also, the effect of thickness, the ratio of PEO/PAA and dewetting in surface morphology of PEO-PAA blend films were investigated. These results showed that the crystallization was highly dependent on the ratio of PEO/PAA and the thickness of blend film. Furthermore, we assembled the PEO/PAA layer-by-layer film by spin-casting method for the first time, which exhibited highly efficiency. As a complementary tool, we also used lateral force microscopy (LFM) to explore surface information of these films. The result was indicative of interfacial constraints in ultrathin region, and also was supported by the results showing the spin-casting PEO/PAA blends rather than heterogeneous mixture.     

AFM lateral force imagining of modified polychloroprene: A study based on roughness analysis

Films of a binary polymer blends comprising polychloroprene (PCP) and piperylene-styrene copolymer (PSC) have been prepared by solution casting. The dependence of the surface morphology of the free blend films on PSC content was studied with both roughness and correlation analysis of lateral force microscopy (LFM) images. Significant changes in roughness and lateral parameter values of different blend film sides have been observed depending on the blend composition. It was shown that up to 15 wt.% PSC is distributed continuously in PCP bulk. The increase of roughness and lateral parameter values at the air/film surface shows the enrichment of PCP in the blends containing 25 wt.% or more PSC. The enrichment of PCP on the air/film surface favours the increase of PSC concentration at the backing/film surface. The films underside morphology becomes similar to that of PSC, when its content reaches 40 wt.%.     

用显微红外光谱法研究高分子共混物溶液自组织形成的相组成分布

本文制备了ＰＳ／ＰＣ（７／３）和ＰＳ／ＰＭＭＡ（５／５）的四氢呋喃（ＴＨＦ）溶液,通过缓慢蒸发溶剂制得ＰＳ／ＰＣ和ＰＳ／ＰＭＭＡ的共混物薄膜。利用不同的ＦＴＩＲ测试方法检测了制得薄膜中的组成分布。将ＰＳ／ＰＣ薄膜超薄切片,通过显微投射红外方法检测了其纵剖面的组成分布（测试步长为１６μｍ）。结果表明：ＰＳ含量从膜底面到表面缓慢增大呈梯度分布,在膜表面附近急剧增大,即ＰＳ组分在成膜过程中向表面（与空气     

衰减全反射傅里叶红外光谱在聚丙烯的表面改性的应用

应用衰减全反射傅里叶变换红外光谱法(ATR-FTIR)对聚丙烯共混薄膜的表面组成进行了测试.通过比尔定律的验证,确认1 103和1 733 cm-1可以分别用于含聚乙二醇和含羰基结构单元的改性剂共混体系的定量计算.利用ATR校正程序,以相应的特征峰峰面积比作为定量测定的基准,可以减少测试误差.通过工作曲线法,定量地分析了聚丙烯共混物薄膜表层中改性剂的含量.此外,利用变角全反射,通过改变入射光线的角度,可以测定不同深度的改性剂含量,剖析改性剂在PP共混薄膜的表层分布.     

Protein quantification on dendrimer-activated surfaces by using time-of-flight secondary ion mass spectrometry and principal component regression

Interaction between streptavidin and biotin on poly(amidoamine) (PAMAM) dendrimer-activated surfaces and on self-assembled monolayers (SAMs) was quantitatively studied by using time-of-flight secondary ion mass spectrometry (ToF-SIMS). The surface protein density was systematically varied as a function of protein concentration and independently quantified using the ellipsometry technique. Principal component analysis (PCA) and principal component regression (PCR) were used to identify a correlation between the intensities of the secondary ion peaks and the surface protein densities. From the ToF-SIMS and ellipsometry results, a good linear correlation of protein density was found. Our study shows that surface protein densities are higher on dendrimer-activated surfaces than on SAMs surfaces due to the spherical property of the dendrimer, and that these surface protein densities can be easily quantified with high sensitivity in a label-free manner by ToF-SIMS.